“Process development for hydrometallurgical recovery of valuable metals from sulfide-rich residue generated in a secondary lead smelter”. Kim E, Roosen J, Horckmans L, Spooren J, Broos K, Binnemans K, Vrancken KCM, Quaghebeur M, Hydrometallurgy 169, 589 (2017). http://doi.org/10.1016/J.HYDROMET.2017.04.002
Abstract: Two routes were investigated to selectively recover lead and minor metals (Cu, Ni, Zn) from a sulfide-rich lead smelter residue, matte. The first route comprises a two-step leaching process that combines Fe(III)-HNO3 leaching with roasting, followed by water leaching. In the first step, the efficiency of Pb leaching was 90% at the optimum condition (L/S ratio 8, 0.5 mol.L-1 HNO3, 0.15 mol.L-1 Fe(III), 25 degrees C). In the second step, roasting at 600 degrees C followed by water leaching at 50 degrees C selectively leached Ni, Cu, and Zn while fully converting iron sulfides to oxides. One-step oxidative pressure leaching in HNO3 was investigated as an alternative to simultaneously leach Pb, Cu, Ni and Zn. At the optimal conditions (130 degrees C, 60 min, 0.3 mol.L-1 HNO3, 0.07 mol.L-1 Fe(III), L/S ratio 20), Pb, Cu, Zn and Ni leaching were 92, 60, 70 and 66%, respectively, while Fe leaching remained low (2%). The leachates obtained from both leaching routes were treated by ion-exchange adsorption with diethylenetriaminepentaacetic acid (DTPA) functionalized chitosan-silica hybrid materials to investigate the selective recovery of Cu, Zn and Ni. The adsorption order appeared to be in the same order as the corresponding stability constants for complexes between the respective metal ions and free DTPA: Ca(II) < Zn(II) < Pb (II) approximate to Ni(II) < Cu(II). This allows not only to selectively recover Cu, Zn and Ni from the leachates, but also to mutually separate them by using the functionalized resin as a stationary phase in column chromatography. To avoid adsorbent contamination, Fe(III) and Pb(II) may be removed from the leachates in a pre-treatment step. Based on these results, the investigated methods can be combined as process steps of two possible routes for the selective recovery of valuable metals from the studied secondary lead smelting residue. The two-step leaching process seems to be superior since a more concentrated solution of Cu, Ni, and Zn is produced in the 2nd leaching step with low capital cost.
Keywords: A1 Journal article; Engineering sciences. Technology; Sustainable Energy, Air and Water Technology (DuEL)
DOI: 10.1016/J.HYDROMET.2017.04.002
|
|
|
“Recycling of a secondary lead smelting matte by selective citrate leaching of valuable metals and simultaneous recovery of hematite as a secondary resource”. Kim E, Horckmans L, Spooren J, Broos K, Vrancken KCM, Quaghebeur M, Hydrometallurgy 169, 290 (2017). http://doi.org/10.1016/J.HYDROMET.2017.02.007
Abstract: Anew recycling process, according to the zero-waste concept, was investigated for an iron rich waste stream, more specifically a secondary lead smelting matte. The process consists of a selective citrate leaching of Pb, Cu, Ni and Zn in combination with a roasting step, leading to a simultaneous recovery of hematite as a secondary iron resource. The parameters, such as leaching time, leaching temperature, H2O2 concentration and roasting temperature, were experimentally optimized. The maximum Pb leaching efficiency was 93% and the leachability of Cu (33%) and Zn (11%) increased slightly in the presence of 0.5 M H2O2 in 1 M citrate at 25 degrees C and pH 5.5. Importantly, almost no Fe was leached (< 0.6%) from the iron rich matrix material at this condition allowing for a maximal recovery of hematite as a secondary resource after further treatment (i.e. roasting or sulfur removal). The leachability of Pb, Cu, Ni and Zn was strongly affected by the roasting temperature. Maximum leaching efficiency in 1 M citrate (25 degrees C, L/S ratio 10, pH 6.5) was 93% for Pb, 80% for Cu and 60% for Zn at a roasting temperature of 600 degrees C, while for Ni the maximum leaching efficiency of 53% was reached after roasting at 650 degrees C. Furthermore, when oxidative roasting was applied, the leaching residue consists dominantly of hematite (Fe2O3) with minor quantities of PbSO4, which can be used as pig iron ore (Fe > 60 wt%). (C) 2017 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Sustainable Energy, Air and Water Technology (DuEL)
DOI: 10.1016/J.HYDROMET.2017.02.007
|
|
|
“Selective leaching of Pb, Cu, Ni and Zn from secondary lead smelting residues”. Kim E, Horckmans L, Spooren J, Vrancken KC, Quaghebeur M, Broos K, Hydrometallurgy 169, 372 (2017). http://doi.org/10.1016/J.HYDROMET.2017.02.027
Abstract: Several HNO3-based leaching approaches were tested and optimized to selectively recover Pb and other minor metals (Cu, Ni, Zn) from secondary lead smelter residues (i.e., slag and matte). Firstly, the leaching behaviors of Pb and the matrix element Fe were studied at atmospheric pressure in the temperature range 25-70 degrees C. These elements were present in both materials studied as sulfide and oxide phases. For the sulfur-rich matte residue, the Pb leaching increased from 63% to 69% upon increasing the HNO3 concentration from 0.2 M to 0.5 M. However, by adding Fe(III) as an oxidation agent, Pb leaching from the matte amounted to 90% at 25 degrees C. At a higher temperature, Pb leaching was reduced due to PbSO4 precipitation. In this process, Cu, Zn and Ni leaching was insignificant. For the slag residue, HNO3 could not leach Pb (0.03% Pb leached), while Fe leaching was 19.8% due to a galvanic effect. However, Pb leaching of the slag was 82% in the presence of additional Fe(III). Secondly, to enhance leaching of the other base metals (Cu, Zn and Ni) from the matte, roasting followed by water leaching and (microwave assisted or autoclave) pressurized leaching in 0.5 M HNO3 were applied. During roasting, the FeS phase converted to Fe2O3 above 500 degrees C, and PbS and Pb phases were transformed into insoluble PbSO4 above 400 degrees C. Cu, Ni and Zn leaching was drastically enhanced by a roasting step at 600 degrees C followed by leaching with 0.5 M HNO3 at 50 degrees C, or by pressurized HNO3 leaching above 130 degrees C, whereby Pb leaching almost ceased due to PbSO4 precipitation. During the roasting above 600 degrees C, or microwave assisted extraction (MAE) at 160 degrees C for 15 min, FeS was completely converted to iron oxides that can be used as raw material for pig iron production. Based on the results, the methods investigated can be combined as process steps of two possible routes for the selective recovery of valuable metals and the production of a clean source of Fe oxides from the secondary lead smelting residues studied. (C) 2017 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Sustainable Energy, Air and Water Technology (DuEL)
DOI: 10.1016/J.HYDROMET.2017.02.027
|
|
|
“P-N Junction Passivation in Kesterite Solar Cells by Use of Solution-Processed TiO2 Layer”. Ranjbar S, Hadipour A, Vermang B, Batuk M, Hadermann J, Garud S, Sahayaraj S, Meuris M, Brammertz G, da Cunha AF, Poortmans J, IEEE journal of photovoltaics 7, 1130 (2017). http://doi.org/10.1109/JPHOTOV.2017.2692208
Abstract: In this work, we used a solution-processed TiO2 layer between Cu2ZnSnSe4 and CdS buffer layer to reduce the recombination at the p–n junction. Introducing the TiO2 layer showed a positive impact on VOC but fill factor and efficiency decreased. Using a KCN treatment, we could create openings in the TiO2 layer, as confirmed by transmission electron microscopy measurements. Formation of these openings in the TiO2 layer led to the improvement of the short-circuit current, fill factor, and the efficiency of the modified solar cells.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.712
Times cited: 2
DOI: 10.1109/JPHOTOV.2017.2692208
|
|
|
“Tailoring microstructure and superconducting properties in thick BaHfO3 and Ba2YNb/Ta)O-6 doped YBCO films on technical templates”. Sieger M, Pahlke P, Lao M, Eisterer M, Meledin A, Van Tendeloo G, Ottolinger R, Haenisch J, Holzapfel B, Usoskin A, Kursumovic A, MacManus-Driscoll JL, Stafford BH, Bauer M, Nielsch K, Schultz L, Huehne R, IEEE transactions on applied superconductivity 27, 6601407 (2017). http://doi.org/10.1109/TASC.2016.2644858
Abstract: The current transport capability of YBa2Cu3O7-x(YBCO) based coated conductors (CCs) is mainly limited by two features: the grain boundaries of the used textured template, which are transferred into the superconducting film through the buffer layers, and the ability to pin magnetic flux lines by incorporation of defined defects in the crystal lattice. By adjusting the deposition conditions, it is possible to tailor the pinning landscape in doped YBCO in order to meet specific working conditions (T, B) for CC applications. To study these effects, we deposited YBCO layers with a thickness of about 1-2 mu m using pulsed laser deposition on buffered rolling-assisted biaxially textured Ni-W substrates as well as on metal tapes having either an ion-beam-texturedYSZbuffer or an MgO layer textured by inclined substrate deposition. BaHfO3 and the mixed double-perovskite Ba2Y(Nb/Ta)O-6 were incorporated as artificial pinning centers in these YBCO layers. X-ray diffraction confirmed the epitaxial growth of the superconductor on these templates as well as the biaxially oriented incorporation of the secondary phase additions in the YBCO matrix. A critical current density J(c) of more than 2 MA/cm(2) was achieved at 77 K in self-field for 1-2 mu m thick films. Detailed TEM (transmission electron microscopy) studies revealed that the structure of the secondary phase can be tuned, forming c-axis aligned nanocolumns, ab-oriented platelets, or a combination of both. Transport measurements show that the J(c) anisotropy in magnetic fields is reduced by doping and the peak in the J(c) (theta) curves can be correlated to the microstructural features.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 12
DOI: 10.1109/TASC.2016.2644858
|
|
|
“Synthesis of MAX Phases in the Zr-Ti-Al-C System”. Tunca B, Lapauw T, Karakulina OM, Batuk M, Cabioc’h T, Hadermann J, Delville R, Lambrinou K, Vleugels J, Inorganic chemistry 56, 3489 (2017). http://doi.org/10.1021/acs.inorgchem.6b03057
Abstract: This study reports on the synthesis and characterization of MAX phases in the (Zr,Ti)n+1AlCn system. The MAX phases were synthesized by reactive hot pressing and pressureless sintering in the 1350–1700 °C temperature range. The produced ceramics contained large fractions of 211 and 312 (n = 1, 2) MAX phases, while strong evidence of a 413 (n = 3) stacking was found. Moreover, (Zr,Ti)C, ZrAl2, ZrAl3, and Zr2Al3 were present as secondary phases. In general, the lattice parameters of the hexagonal 211 and 312 phases followed Vegard’s law over the complete Zr-Ti solid solution range, but the 312 phase showed a non-negligible deviation from Vegard’s law around the (Zr0.33,Ti0.67)3Al1.2C1.6 stoichiometry. High-resolution scanning transmission electron microscopy combined with X-ray diffraction demonstrated ordering of the Zr and Ti atoms in the 312 phase, whereby Zr atoms occupied preferentially the central position in the close-packed M6X octahedral layers. The same ordering was also observed in 413 stackings present within the 312 phase. The decomposition of the secondary (Zr,Ti)C phase was attributed to the miscibility gap in the ZrC-TiC system.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 26
DOI: 10.1021/acs.inorgchem.6b03057
|
|
|
“Crystal Structure, Defects, Magnetic and Dielectric Properties of the Layered Bi3n+1Ti7Fe3n-3,O9n+11 Perovskite-Anatase lntergrowths”. Batuk D, Batuk M, Filimonov DS, Zakharov KV, Volkova OS, Vasiliev AN, Tyablikov OA, Hadermann J, Abakumov AM, Inorganic chemistry 56, 931 (2017). http://doi.org/10.1021/ACS.INORGCHEM.6B02559
Abstract: The Bi3n+1Ti7Fe3n-3,O9n+11 materials are built of (001)(p) plane parallel perovskite blocks with a thickness of n (Ti,Fe)O-6 octahedra, separated by periodic translational interfaces. The interfaces are based on anatase-like chains of edge -sharing (Ti,Fe)O-6 octahedra. Together with the octahedra of the perovskite blocks, they create S-shaped tunnels stabilized by lone pair Bi3+ cations. In this work, the structure of the n = 4-6 Bi3n+1Ti7Fe3n-3,O9n+11 homologues is analyzed in detail using advanced transmission electron microscopy, powder X-ray diffraction, and Mossbauer spectroscopy. The connectivity of the anatase-like chains to the perovskite blocks results in,a 3ap periodicity along the interfaces, so that they can be located either on top of each other or with shifts of +/- a(p) along [100](p). The ordered arrangement of the interfaces gives rise to orthorhombic Immm and monoclinic A2/m polymorphs with the unit cell parameters a = 3a(p), b = b(p), c = 2(n + 1)c(p) and a = 3a(p), b = b(p), c = 2(n + 1)c(p) – a(p), respectively. While the n = 3 compound is orthorhombic, the monoclinic modification is more favorable in higher homologues. The Bi3n+1Ti7Fe3n-3,O9n+11 structures demonstrate intricate patterns of atomic displacements in the perovskite blocks, which are supported by the stereochemical activity of the Bi3+ cations. These patterns are coupled to the cationic coordination of the oxygen atoms in the (Ti,Fe)O-2 layers at the border of the perovskite blocks. The coupling is strong in the 1/ = 3, 4 homologues, but gradually reduces with the increasing thickness of the perovskite blocks, so that, in the n = 6 compound, the dominant mode of atomic displacements is aligned along the interface planes. The displacements in the adjacent perovskite blocks tend to order antiparallel, resulting in an overall antipolar structure. The Bi3n+1Ti7Fe3n-3,O9n+11 materials demonstrate an unusual diversity of structure defects. The n = 4-6 homologues are robust antiferromagnets below T-N = 135, 220, and 295 K, respectively. They show a high dielectric constant that weakly increases with temperature and is relatively insensitive to the Ti/Fe ratio.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 3
DOI: 10.1021/ACS.INORGCHEM.6B02559
|
|
|
“Crystal growth and structure analysis of Ce-18-W-10-O-57 : a complex oxide containing tungsten in an unusual trigonal prismatic coordination environment”. Abeysinghe D, Smith MD, Yeon J, Tran TT, Sena RP, Hadermann J, Halasyamani PS, zur Loye H-C, Inorganic chemistry 56, 2566 (2017). http://doi.org/10.1021/ACS.INORGCHEM.6B02710
Abstract: The noncentrosymmetric tungstate oxide, Ce18W10O57) was synthesized for the first time as high-quality single crystals via the molten chloride flux method and structurally characterized by single-crystal X-ray diffraction. The compound is a structural analogue to the previously reported La18W10O57, which crystallizes in the hexagonal space group P (6) over bar 2c. The +3 oxidation state of cerium in Ce18W10O57 was achieved via the in situ reduction of Ce(IV) to Ce(III) using Zn metal. The structure consists of both isolated and face-shared WO6 octahedra and, surprisingly, isolated WO6 trigonal prisms. A careful analysis of the packing arrangement in the structure makes it possible to explain the unusual structural architecture of Ce18W10O57, which is described in detail. The temperature-dependent magnetic susceptibility of Ce18W10O57 indicates that the cerium(III) f(1) cations do not order magnetically and exhibit simple paramagnetic behavior. The SHG efficiency of Ln(18)W(10)O(57) (Ln = La, Ce) was measured as a function of particle size, and both compounds were found to be SHG active with efficiency approximately equal to that of alpha-SiO2.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 9
DOI: 10.1021/ACS.INORGCHEM.6B02710
|
|
|
“Synthesis, structure, and electrochemical properties of k-based sulfates K2M2(SO4)3) with M = Fe and Cu”. Lander L, Rousse G, Batuk D, Colin CV, Dalla Corte DA, Tarascon J-M, Inorganic chemistry 56, 2013 (2017). http://doi.org/10.1021/ACS.INORGCHEM.6B02526
Abstract: Stabilizing new host structures through potassium extraction from K-based polyanionic materials has been proven to be an interesting approach to develop new Li+/Na+ insertion materials. Pursuing the same trend, we here report the feasibility of preparing langbeinite “Fe-2(SO4)(3)” via electrochemical and chemical oxidation of K2Fe2(SO4)(3). Additionally, we succeeded in stabilizing a new K2Cu2(SO4)(3) phase via a solid-state synthesis approach. This novel compound crystallizes in a complex orthorhombic structure that differs from that of langbeinite as deduced from synchrotron X-ray and neutron powder diffraction. Electrochemically, the performance of this new phase is limited, which we explain in terms of sluggish diffusion kinetics. We further show that K2Cu2(SO4)(3) decomposes into K2Cu3O(SO4)(3) on heating, and we report for the first time the synthesis of fedotovite K2Cu3O(SO4)(3). Finally, the fundamental attractiveness of these S = 1/2 systems for physicists is examined by neutron magnetic diffraction, which reveals the absence of a long-range ordering of Cu2+ magnetic moments down to 1.5 K.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 13
DOI: 10.1021/ACS.INORGCHEM.6B02526
|
|
|
“Molybdenum oxide nitrides of the Mo2(O,N,\square)5 type : on the way to Mo2O5”. Weber D, Huber M, Gorelik TE, Abakumov AM, Becker N, Niehaus O, Schwickert C, Culver SP, Boysen H, Senyshyn A, Poettgen R, Dronskowski R, Ressler T, Kolb U, Lerch M, Inorganic chemistry 56, 8782 (2017). http://doi.org/10.1021/ACS.INORGCHEM.7B00551
Abstract: Blue-colored molybdenum oxide nitrides of the Mo-2(O,N,square)(5) type were synthesized by direct nitridation of commercially available molybdenum trioxide with a mixture of gaseous ammonia and oxygen. Chemical composition, crystal structure, and stability of the obtained and hitherto unknown compounds are studied extensively. The average oxidation state of +5 for molybdenum is proven by Mo K near-edge X-ray absorption spectroscopy; the magnetic behavior is in agreement with compounds exhibiting (MoO6)-O-v units. The new materials are stable up to similar to 773 K in an inert gas atmosphere. At higher temperatures, decomposition is observed. X-ray and neutron powder diffraction, electron diffraction, and high-resolution transmission electron microscopy reveal the structure to be related to VNb9O24.9-type phases, however, with severe disorder hampering full structure determination. Still, the results demonstrate the possibility of a future synthesis of the potential binary oxide Mo2O5. On the basis of these findings, a tentative suggestion on the crystal structure of the potential compound Mo2O5, backed by electronic-structure and phonon calculations from first principles, is given.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 3
DOI: 10.1021/ACS.INORGCHEM.7B00551
|
|
|
“Nanosecond-pulsed DBD plasma-generated reactive oxygen species trigger immunogenic cell death in A549 lung carcinoma cells through intracellular oxidative stress”. Lin A, Truong B, Patel S, Kaushik N, Choi EH, Fridman G, Fridman A, Miller V, International journal of molecular sciences 18, 966 (2017). http://doi.org/10.3390/IJMS18050966
Abstract: A novel application for non-thermal plasma is the induction of immunogenic cancer cell death for cancer immunotherapy. Cells undergoing immunogenic death emit danger signals which facilitate anti-tumor immune responses. Although pathways leading to immunogenic cell death are not fully understood; oxidative stress is considered to be part of the underlying mechanism. Here; we studied the interaction between dielectric barrier discharge plasma and cancer cells for oxidative stress-mediated immunogenic cell death. We assessed changes to the intracellular oxidative environment after plasma treatment and correlated it to emission of two danger signals: surface-exposed calreticulin and secreted adenosine triphosphate. Plasma-generated reactive oxygen and charged species were recognized as the major effectors of immunogenic cell death. Chemical attenuators of intracellular reactive oxygen species successfully abrogated oxidative stress following plasma treatment and modulated the emission of surface-exposed calreticulin. Secreted danger signals from cells undergoing immunogenic death enhanced the anti-tumor activity of macrophages. This study demonstrated that plasma triggers immunogenic cell death through oxidative stress pathways and highlights its potential development for cancer immunotherapy.
Keywords: A1 Journal article; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
DOI: 10.3390/IJMS18050966
|
|
|
“Land-use suitability in Northeast Iran : application of AHP-GIS hybrid model”. Memarbashi E, Azadi H, Barati AA, Mohajeri F, Van Passel S, Witlox F, Isprs International Journal Of Geo-Information 6, 396 (2017). http://doi.org/10.3390/IJGI6120396
Abstract: Land-use suitability is the ability of a given type of land to support a defined use. Analysis of land-use suitability requires the consideration of a variety of criteria, not only the natural/physical capacity of a land unit, but also its socioeconomic and environmental impact implications. As land suitability is assessed within a Geographic Information System (GIS) environment, it is formulated as a multi-criteria decision making (MCDM) problem. The study was conducted in the Sangab Plain in northeast Iran. We investigated the study areas suitability for grassland and agricultural uses. A hybrid method of the analytic hierarchy process (AHP) and GIS methodology was applied to evaluate land suitability based on a set of criteria and sub-criteria. Results showed that 20% of the study area had high (rich), 65% had medium (fair), and 15% had low (poor) suitability for agriculture. In terms of grassland use, the comparable amounts were, respectively, about 7%, 23%, and 70%. The lands of the Sangab Plain have medium potential for agricultural use and low potential for grassland use. This paper used both qualitative and quantitative techniques.
Keywords: A1 Journal article; Economics; Engineering Management (ENM); Government and Law
Impact Factor: 0.371
Times cited: 7
DOI: 10.3390/IJGI6120396
|
|
|
“Progress and prospects in nanoscale dry processes: How can we control atomic layer reactions?”.Ishikawa K, Karahashi K, Ichiki T, Chang JP, George SM, Kessels WMM, Lee HJ, Tinck S, Um JH, Kinoshita K, Japanese journal of applied physics 56, 06HA02 (2017). http://doi.org/10.7567/JJAP.56.06HA02
Abstract: In this review, we discuss the progress of emerging dry processes for nanoscale fabrication. Experts in the fields of plasma processing have contributed to addressing the increasingly challenging demands in achieving atomic-level control of material selectivity and physicochemical reactions involving ion bombardment. The discussion encompasses major challenges shared across the plasma science and technology community. Focus is placed on advances in the development of fabrication technologies for emerging materials, especially metallic and intermetallic compounds and multiferroic, and two-dimensional (2D) materials, as well as state-of-the-art techniques used in nanoscale semiconductor manufacturing with a brief summary of future challenges.
Keywords: A1 Journal article; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 1.384
Times cited: 18
DOI: 10.7567/JJAP.56.06HA02
|
|
|
“CVD growth of monolayer MoS2: Role of growth zone configuration and precursors ratio”. Ozden A, Ay F, Sevik C, Perkgoz NK, Japanese journal of applied physics 56, 06gg05 (2017). http://doi.org/10.7567/JJAP.56.06GG05
Abstract: Single-layer, large-scale two-dimensional material growth is still a challenge for their wide-range usage. Therefore, we carried out a comprehensive study of monolayer MoS2 growth by CVD investigating the influence of growth zone configuration and precursors ratio. We first compared the two commonly used approaches regarding the relative substrate and precursor positions, namely, horizontal and face-down configurations where facedown approach is found to be more favorable to obtain larger flakes under identical growth conditions. Secondly, we used different types of substrate holders to investigate the influence of the Mo and S vapor confinement on the resulting diffusion environment. We suggest that local changes of the S to Mo vapor ratio in the growth zone is a key factor for the change of shape, size and uniformity of the resulting MoS2 formations, which is also confirmed by performing depositions under different precursor ratios. Therefore, to obtain continuous monolayer films, the S to Mo vapor ratio is needed to be kept within a certain range throughout the substrate. As a conclusion, we obtained monolayer triangles with a side length of 90 mu m and circles with a diameter of 500 mu m and continuous films with an area of 85 0 mu m x 1 cm when the S-to-Mo vapor ratio is optimized. (C) 2017 The Japan Society of Applied Physics
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
DOI: 10.7567/JJAP.56.06GG05
|
|
|
“Canola adoption enhancement in Western Iran”. Zarafshani K, Ghasemi S, Houshyar E, Ghanbari R, Van Passel S, Azadi H, Journal Of Agricultural Science And Technology 19, 47 (2017)
Abstract: Canola production is an important alternative for agricultural policy-makers in Iran to reduce dependency on the imported vegetable oils. Nevertheless, the canola planted area is only increasing at a slow pace, indicating a low willingness-to-accept of farmers. The general aim of this study was to determine the factors influencing the canola adoption in the Kermanshah Province in Western Iran. Employing stratified random sampling method, 106 farmers from each adopter and non-adopter group were selected. Helping to reach a suitable extensional program, two main categories of variables were defined; i.e. farmers personal characteristics and extension parameters. The analysis of farmers personal characteristics variables revealed that the adopters had larger farms and were younger. The results also show that 80% of the adopters were highly to very highly willing to cultivate canola. Furthermore, a logistic regression model estimated the influence of extensional parameters variables on the canola adoption. According to the regression model, the most effective factors are contact with extension agents and participating in extension classes. As a conclusion, it is suggested that the focus of extension services should be to reduce the distance to agricultural service centers in combination with more contact with extension agents and classes.
Keywords: A1 Journal article; Economics; Engineering Management (ENM)
Impact Factor: 0.813
|
|
|
“Structure and magnetic properties of Sm(Fe,Si)(9)C/alpha-Fe nanocomposite magnets”. Bez R, Zehani K, Batuk M, Van Tendeloo G, Mliki N, Bessais L, Journal of alloys and compounds 695, 810 (2017). http://doi.org/10.1016/J.JALLCOM.2016.10.122
Abstract: SmFe8.75 Si-0.25 C/alpha-Fe nanocomposites have been successfully synthesized using high energy milling, followed by annealing at 750 degrees C. The crystal structure of these compounds was characterized by the Rietveld method using powder X-ray diffraction data. By increasing the concentration of Sm, we observed a decrease in the amount of alpha-Fe phase. The morphology of the samples was determined by scanning and transmission electron microscopy. The average grain size is about 20 nm. The magnetic properties were investigated at room temperature and at 10 K. A ferromagnetic behavior was observed in all samples at both temperatures. An increase of the soft magnetic phase alpha-Fe induced an increase in the magnetization and a decrease in coercivity. (C) 2016 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.133
Times cited: 1
DOI: 10.1016/J.JALLCOM.2016.10.122
|
|
|
“Effect of cation vacancies on the crystal structure and luminescent properties of Ca(0.85-1.5x)Gd(x)Eu(0.1)_(0.05+0.5x)WO(4) (0<x<0.567) scheelite-based red phosphors”. Batuk D, Batuk M, Morozov VA, Meert KW, Smet PF, Poelman D, Abakumov AM, Hadermann J, Journal of alloys and compounds 706, 358 (2017). http://doi.org/10.1016/j.jallcom.2017.02.154
Abstract: The Ca0.85-1.5xGdxEu0.1_0.05-0.5xWO4 (0 < x < 0.567) series of cation-deficient scheelites is investigated to unveil the influence of the cation vacancies on the crystal structure and luminescent properties. The concentration of the vacancies is varied by the heterovalent substitution of Gd3+ for Ca2+, keeping the concentration of the Eu3+ luminescent centers constant in all compounds of the series. The crystal structure of the materials is studied using a combination of transmission electron microscopy and synchrotron X-ray powder diffraction. At low vacancy concentration (x = 0.1, 0.2), cations and cation vacancies are randomly distributed in the structure, and the materials preserve the I41/a symmetry of the parent scheelite structure [x = 0.1: a = 5.25151(1) Å, c = 11.39479(2) Å; x = 0.2: a = 5.25042(1) Å, c = 11.41335(2) Å]. At higher concentration, the cation-vacancy ordering gives rise to incommensurately modulated structures. The x = 0.3 structure has a (3 + 2)D tetragonal symmetry [superspace group I41/a(a,b,0)00(-b,a,0)00, a = 5.24700(1) Å, c = 11.45514(3) Å, q1 = 0.51637(14)a* + 0.80761(13)b*, q2 = -0.80761a* + 0.51637b*]. At x = 0.4, the scheelite basic cell undergoes a monoclinic distortion with the formation of the (3 + 1)D structure [superspace group I2/b(a,b,0)00, a = 5.23757(1) Å, b = 5.25035(1) Å, c = 11.45750(2) Å, g = 90.5120(2) o, q = 0.54206(8)a* + 0.79330(8)b*]. In both structures, the antiphase Ca and (Gd,Eu) occupancy modulations indicate that the ordering between the A cations and vacancies also induces partial Ca/(Gd,Eu) cation ordering. Further increase of the Gd3þ content up to x = 0.567 leads to the formation of a monoclinic phase (space group C2/c) with the Eu2/3WO4-type structure. Despite the difference in the cation-vacancy ordering patterns, all materials in the series demonstrate very similar quantum efficiency and luminescence decay lifetimes. However, the difference in the local coordination environment of the A cation species noticeably affects the line width and the multiplet splitting of the 4f6-4f6 transitions.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.133
Times cited: 2
DOI: 10.1016/j.jallcom.2017.02.154
|
|
|
“Cobalt location in p -CoO x / n -SnO 2 nanocomposites: Correlation with gas sensor performances”. Vladimirova SA, Rumyantseva MN, Filatova DG, Chizhov AS, Khmelevsky NO, Konstantinova EA, Kozlovsky VF, Marchevsky AV, Karakulina OM, Hadermann J, Gaskov AM, Journal Of Alloys And Compounds 721, 249 (2017). http://doi.org/10.1016/j.jallcom.2017.05.332
Abstract: Nanocomposites CoOx/SnO2 based on tin oxide powders with different crystallinity have been prepared by wet chemical synthesis and characterized in detail by ICP-MS, XPS, EPR, XRD, HAADF-STEM imaging and EDX-STEM mapping. It was shown that cobalt is distributed differently between the bulk and surface of SnO2 nanocrystals, which depends on the crystallinity of the SnO2 matrix. The measurements of gas sensor properties have been carried out during exposure to CO (10 ppm), and H2S (2 ppm) in dry air. The decrease of sensor signal toward CO was attributed to high catalytic activity of Co3O4 leading to oxidation of carbon monoxide entirely on the surface of catalyst particles. The formation of a p-CoOx/n-SnO2 heterojunction results in high sensitivity of nanocomposites in H2S detection. The conductance significantly changed in the presence of H2S, which was attributed to the formation of metallic cobalt sulfide and removal of the p – n junction.
Keywords: A1 Journal Article; Electron Microscopy for Materials Science (EMAT) ;
Impact Factor: 3.133
DOI: 10.1016/j.jallcom.2017.05.332
|
|
|
“Cobalt location in p-CoOxIn-SnO2 nanocomposites : correlation with gas sensor performances”. Vladimirova SA, Rumyantseva MN, Filatova DG, Chizhov AS, Khmelevsky NO, Konstantinova EA, Kozlovsky VF, Marchevsky AV, Karakulina OM, Hadermann J, Gaskov AM, Journal of alloys and compounds 721, 249 (2017). http://doi.org/10.1016/JJALLCOM.2017.05.332
Abstract: Nanocomposites CoOx/SnO2 based on tin oxide powders with different crystallinity have been prepared by wet chemical synthesis and characterized in detail by ICP-MS, XPS, EPR, XRD, HAADF-STEM imaging and EDX-STEM mapping. It was shown that cobalt is distributed differently between the bulk and surface of SnO2 nanocrystals, which depends on the crystallinity of the SnO2 matrix. The measurements of gas sensor properties have been carried out during exposure to CO (10 ppm), and H2S (2 ppm) in dry air. The decrease of sensor signal toward CO was attributed to high catalytic activity of Co3O4 leading to oxidation of carbon monoxide entirely on the surface of catalyst particles. The formation of a p-CoOx/n-SnO2 heterojunction results in high sensitivity of nanocomposites in H2S detection. The conductance significantly changed in the presence of H2S, which was attributed to the formation of metallic cobalt sulfide and removal of the p – n junction. (C) 2017 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.133
DOI: 10.1016/JJALLCOM.2017.05.332
|
|
|
“Antiferroelectric properties and site occupations ofR3+ cations in Ca8MgR(PO4)7 luminescent host materials”. Belik AA, Morozov VA, Deyneko DV, Savon AE, Baryshnikova OV, Zhukovskaya ES, Dorbakov NG, Katsuya Y, Tanaka M, Stefanovich SY, Hadermann J, Lazoryak BI, Journal of alloys and compounds 699, 928 (2017). http://doi.org/10.1016/J.JALLCOM.2016.12.288
Abstract: Ca8MgR(PO4)(7) = La, Pr, Nd, Sm-Lu, and Y) phosphates with a beta-Ca-3(PO4)(2) related structure were prepared by a standard solid-state method in air. Second-harmonic generation, differential scanning calorimetry, and dielectric measurements led to the conclusion that all Ca8MgR(PO4)(7) are centrosymmetric and go to another centrosymmetric phase in the course of a first-order antiferroelectric phase transition well above room temperature (RT). High-temperature electron diffraction showed that the symmetry changes from R (3) over barc to R (3) over barm during the phase transition. Structures of Ca8MgR(PO4)(7) at RT were refined by the Rietveld method in centrosymmetric space group R (3) over barc. Mg2+ cations occupy the M5 site; the occupancy of the M1 site by R3+ cations increases monotonically from 0.0389 for R = La to 0.1667 for R = Er-Lu, whereas the occupancy of the M3 site by R3+ cations decreases monotonically from 0.1278 for R = La to 0 for R = Er-Lu. In the case of R = Er-Lu, the M3 site is occupied only by Ca2+ cations. P1O(4) tetrahedra and cations at the M3 site are disordered in the R (3) over barc structure of Ca8MgEu(PO4)(7). Using synchrotron X-ray powder diffraction, we found that annealing conditions do not significantly affect the distribution of Ca2+ and Eu3+ cations between the structure positions of Ca8MgEu(PO4)(7). Luminescent properties of CasMgEu(PO4)(7) powder samples were investigated under near-ultraviolet (n-UV) light. Excitation spectra of CasMgEu(PO4)(7) show the strongest absorption at about 395 nm that matches with commercially available n-UV-emitting GaN-based LED chips. Emission spectra show an intense red emission due to the D-5(0) -> F-7(2) transition of Eu3+. (C) 2016 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
DOI: 10.1016/J.JALLCOM.2016.12.288
|
|
|
“Inductively coupled plasma-mass spectrometry: insights through computer modeling”. Bogaerts A, Aghaei M, Journal of analytical atomic spectrometry 32, 233 (2017). http://doi.org/10.1039/C6JA00408C
Abstract: In this tutorial review paper, we illustrate how computer modeling can contribute to a better insight in inductively coupled plasma-mass spectrometry (ICP-MS). We start with a brief overview on previous efforts, studying the fundamentals of the ICP and ICP-MS, with main focus on previous modeling activities. Subsequently, we explain in detail the model that we developed in previous years, and we show typical calculation results, illustrating the plasma characteristics, gas flow patterns and the sample transport, evaporation and ionization. We also present the effect of various experimental parameters, such as operating conditions, geometrical aspects and sample characteristics, to illustrate how modeling can help to elucidate the optimal conditions for improved analytical performance.
Keywords: A1 Journal article; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 3.379
Times cited: 14
DOI: 10.1039/C6JA00408C
|
|
|
“The darkening of copper- or lead-based pigments explained by a structural modification of natural orpiment : a spectroscopic and electrochemical study”. Vermeulen M, Sanyova J, Janssens K, Nuyts G, De Meyer S, De Wael K, Journal of analytical atomic spectrometry 32, 1331 (2017). http://doi.org/10.1039/C7JA00047B
Abstract: A combined Raman and electrochemical study of natural orpiment (As2S3), an arsenic sulfide pigment, was used to assess the quick formation of oxidized species such as arsenic oxide (As2O3) upon exposing the pigment to 405 nm or 532 nm monochromatic light while simultaneously recording the Raman spectra of the exposed sample. During this process, a distortion of the main band at 355 cm−1, associated with the stretching of the AsS3/2 pyramids of natural orpiment, was observed as well as an increased intensity of the 359 cm−1 band, corresponding to covalent AsAs bonds in natural orpiment. The distortion was accompanied by an overall decrease of the global Raman signal for natural orpiment, which could be explained by a loss in the crystal structure. The same phenomena were recorded in reference natural orpiment model paint samples stored for a long time together with verdigris (Cu(OH)2·(CH3COO)2·5H2O) and minium (Pb3O4) paints, the latter two appearing darkened on their sides closest to the orpiment sample as well as in several historical samples containing natural orpiment mixed with various blue pigments. By SEM-EDX and XRPD analysis, respectively on loose material and cast thin-sections of model paint samples, the darkening was identified as dark sulfide species such as chalcocite (Cu2S) and galena (PbS), suggesting the release of volatile sulfide or related species by the natural orpiment paint. XANES analyses of paint samples presenting AsAs bond increase indicated the presence of sulfur species most likely identified as organosulfur compounds formed upon the AsAs bond formation and explained the darkening of the Cu- and Pb-based pigments. To the best of our knowledge, this article reports for the first time the light-induced formation of AsAs bonds in natural orpiment used as an artists' pigment and objectively demonstrates the incompatibility between orpiment and (arsenic) sulfide-sensitive pigments.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 3.379
Times cited: 10
DOI: 10.1039/C7JA00047B
|
|
|
“The ID21 X-ray and infrared microscopy beamline at the ESRF: status and recent applications to artistic materials”. Cotte M, Pouyet E, Salome M, Rivard C, De Nolf W, Castillo-Michel H, Fabris T, Monico L, Janssens K, Wang T, Sciau P, Verger L, Cormier L, Dargaud O, Brun E, Bugnazet D, Fayard B, Hesse B, del Real AEP, Veronesi G, Langlois J, Balcar N, Vandenberghe Y, Sole VA, Kieffer J, Barrett R, Cohen C, Cornu C, Baker R, Gagliardini E, Papillon E, Susini J, Journal of analytical atomic spectrometry 32, 477 (2017). http://doi.org/10.1039/C6JA00356G
Abstract: The ID21 beamline (European Synchrotron Radiation facility, France) is a multi micro-analytical platform combining X-ray and infrared micro-probes, for characterization of elements, species, molecular groups and crystalline structures in complex materials. Applications are mainly in the fields of cultural heritage, life science, environmental and earth sciences, materials sciences. Here, we first present the status of instruments: (i) the scanning micro-spectroscopy end-station, operating from 2.0 to 9.2 keV, under vacuum and offering cryo conditions, for the acquisition of 2D micro X-ray fluorescence (mu XRF) maps, single point micro X-ray Absorption Near Edge Structure (mu XANES) spectra and speciation maps with sub-micrometric resolution; (ii) the XANES full-field end-station, operating in the same vacuum and energy conditions, for the acquisition of hyper-spectral radiographs of thin concentrated samples, resulting in speciation maps with micrometric resolution and millimetric field of view; (iii) the scanning micro-X-ray diffraction (mu XRD)/mu XRF end-station, operating at 8.5 keV, in air, for the acquisition of 2D crystalline phase maps, with micrometric resolution; and (iv) the scanning infrared microscope, operating in the mid-infrared range for the acquisition of molecular maps and some structural maps with micrometric resolution. Recent hardware and software developments are presented, as well as new protocols for improved sample preparation of thin sections. Secondly, a review of recent applications for the study of cultural heritage is presented, illustrated by various examples: determination of the origin of the color in blue Chinese porcelains and in brown Sevres porcelains; detection of lead in ink on Herculaneum papyri; identification and degradation of modeling materials used by Auguste Rodin and of chrome yellow pigments used by Vincent van Gogh. Cryo capabilities are illustrated by the analysis of plants exposed to chromate solutions. These examples show the variety of materials analyzed, of questions tackled, and particularly the multiple advantages of the ID21 analytical platform for the analysis of ancient and artistic materials.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 3.379
Times cited: 39
DOI: 10.1039/C6JA00356G
|
|
|
“Thickness dependence of the resistivity of platinum-group metal thin films”. Dutta S, Sankaran K, Moors K, Pourtois G, Van Elshocht S, Bommels J, Vandervorst W, Tokei Z, Adelmann C, Journal of applied physics 122, 025107 (2017). http://doi.org/10.1063/1.4992089
Abstract: We report on the thin film resistivity of several platinum-group metals (Ru, Pd, Ir, and Pt). Platinum-group thin films show comparable or lower resistivities than Cu for film thicknesses below about 5 nm due to a weaker thickness dependence of the resistivity. Based on experimentally determined mean linear distances between grain boundaries as well as ab initio calculations of the electron mean free path, the data for Ru, Ir, and Cu were modeled within the semiclassical Mayadas-Shatzkes model [Phys. Rev. B 1, 1382 (1970)] to assess the combined contributions of surface and grain boundary scattering to the resistivity. For Ru, the modeling results indicated that surface scattering was strongly dependent on the surrounding material with nearly specular scattering at interfaces with SiO2 or air but with diffuse scattering at interfaces with TaN. The dependence of the thin film resistivity on the mean free path is also discussed within the Mayadas-Shatzkes model in consideration of the experimental findings. Published by AIP Publishing.
Keywords: A1 Journal article; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 2.068
Times cited: 42
DOI: 10.1063/1.4992089
|
|
|
“On the electrostatic control achieved in transistors based on multilayered MoS2 : a first-principles study”. Lu AKA, Pourtois G, Luisier M, Radu IP, Houssa M, Journal of applied physics 121, 044505 (2017). http://doi.org/10.1063/1.4974960
Abstract: In this work, the electrostatic control in metal-oxide-semiconductor field-effect transistors based on MoS2 is studied, with respect to the number of MoS2 layers in the channel and to the equivalent oxide thickness of the gate dielectric, using first-principles calculations combined with a quantum transport formalism. Our simulations show that a compromise exists between the drive current and the electrostatic control on the channel. When increasing the number of MoS2 layers, a degradation of the device performances in terms of subthreshold swing and OFF currents arises due to the screening of the MoS2 layers constituting the transistor channel. Published by AIP Publishing.
Keywords: A1 Journal article; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
DOI: 10.1063/1.4974960
|
|
|
“Characterization of 18th century Portuguese glass from Real Fábrica de Vidros de Coina”. Lopes F, Lima A, Pires de Matos A, Custódio J, Cagno S, Schalm O, Janssens K, Journal of Archaeological Science: Reports 14, 137 (2017). http://doi.org/10.1016/J.JASREP.2017.05.020
Abstract: This work reports the first systematic chemical characterization of Portuguese 18th century glassware. 28 selected glass fragments, recovered from an archaeological excavation carried out in the site where King D. João V of Portugal established an important glass manufacture, Real Fábrica de Vidros de Coina (Coina Royal Glass Factory), were studied. This factory operated from 1719 until 1747, the year in which the factory was transferred to Marinha Grande. The fragments were analysed by micro-energy dispersive X-ray fluorescence (micro-EDXRF), using a portable spectrometer ArtTAX, and scanning electron microscopy (SEM-EDX). The analytical data showed that a large variety of glass types was manufactured in that factory, namely soda-lime glass, mixed-alkali glass, high lime-low alkali glass, potash glass and lead glass. In general, the composition of the glass varies according to the function of the objects. It was demonstrated that micro-EDXRF can be an important tool to characterize museum glass objects when only in situ non-invasive analytical methods are allowed.
Keywords: A1 Journal article; Engineering sciences. Technology; Art; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation); Antwerp Cultural Heritage Sciences (ARCHES)
Times cited: 3
DOI: 10.1016/J.JASREP.2017.05.020
|
|
|
“Quantitative determination of residual silver distribution in nanoporous gold and its influence on structure and catalytic performance”. Mahr C, Kundu P, Lackmann A, Zanaga D, Thiel K, Schowalter M, Schwan M, Bals S, Wittstock A, Rosenauer A, Journal of catalysis 352, 52 (2017). http://doi.org/10.1016/j.jcat.2017.05.002
Abstract: Large efforts have been made trying to understand the origin of the high catalytic activity of dealloyed nanoporous gold as a green catalyst for the selective promotion of chemical reactions at low temperatures. Residual silver, left in the sample after dealloying of a gold-silver alloy, has been shown to have a strong influence on the activity of the catalyst. But the question of how the silver is distributed within the porous structure has not finally been answered yet. We show by quantitative energy dispersive X-ray tomography measurements that silver forms clusters that are distributed irregularly, both on the surface and inside the ligaments building up the porous structure. Furthermore, we find that the role of the residual silver is ambiguous. Whereas CO oxidation is supported by more residual silver, methanol oxidation to methyl formate is hindered. Structural characterisation reveals larger ligaments and pores for decreasing residual silver concentration.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.844
Times cited: 42
DOI: 10.1016/j.jcat.2017.05.002
|
|
|
“Enhancing immobilization of arsenic in groundwater: A model-based evaluation”. Peng L, Liu Y, Sun J, Wang D, Dai X, Ni B-J, Journal of cleaner production 166, 449 (2017). http://doi.org/10.1016/J.JCLEPRO.2017.08.051
Abstract: The mobilization of arsenic (As) in aquatic environment (groundwater) can cause severe environmental and healthy issues. To develop remediation strategies, we proposed a comprehensive mathematical model to describe the As removal in a arsenite (As (III)) oxidizing and ferrous iron (Fe (II)) oxidizing denitrifying granular biofilm system. In the model framework, the growth-linked microbial oxidation of As (III) and Fe (II) was coupled to chemolithotrophic denitrification of one-step reduction of nitrate to nitrogen gas. Meanwhile, the precipitation of ferric iron (Fe (III)) and adsorption of arsenate (As (V)) onto the biogenic Fe (III) (hydr)oxides were also considered. The model was calibrated by comparing the model predictions against experimental data from batch experiments. The validity of the model was further demonstrated through testing against long-term experimental results from five independent bioreactors with different reactor configurations and operational conditions. Modeling results revealed that the granule size would exert a limited impact on arsenic and iron removal. Nevertheless, their removal efficiencies increased rapidly with the increase of hydraulic retention time (HRT) from 1 h to 12 h, but became independent of HRT as it further increased. The established model framework enables interpretation of a range of experimental observations on As and Fe removal and helps to identify the optimal conditions for enhanced arsenic remediation. (C) 2017 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Sustainable Energy, Air and Water Technology (DuEL)
DOI: 10.1016/J.JCLEPRO.2017.08.051
|
|
|
“CO2 conversion in a gliding arc plasma: Performance improvement based on chemical reaction modeling”. Sun SR, Wang HX, Mei DH, Tu X, Bogaerts A, Journal of CO2 utilization 17, 220 (2017). http://doi.org/10.1016/j.jcou.2016.12.009
Abstract: CO2 conversion into value-added chemicals is gaining increasing interest in recent years, and a gliding arc plasma has great potential for this purpose, because of its high energy efficiency. In this study, a chemical reaction kinetics model is presented to study the CO2 splitting in a gliding arc discharge. The calculated
conversion and energy efficiency are in good agreement with experimental data in a range of different operating conditions. Therefore, this reaction kinetics model can be used to elucidate the dominant chemical reactions contributing to CO2 destruction and formation. Based on this reaction pathway analysis, the restricting factors for CO2 conversion are figured out, i.e., the reverse reactions and the small treated gas fraction. This allows us to propose some solutions in order to improve the CO2 conversion, such as decreasing the gas temperature, by using a high frequency discharge, or increasing the power
density, by using a micro-scale gliding arc reactor, or by removing the reverse reactions, which could be realized in practice by adding possible scavengers for O atoms, such as CH4. Finally, we compare our results with other types of plasmas in terms of conversion and energy efficiency, and the results illustrate that gliding arc discharges are indeed quite promising for CO2 conversion, certainly when keeping in mind the possible solutions for further performance improvement.
Keywords: A1 Journal article; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 4.292
Times cited: 41
DOI: 10.1016/j.jcou.2016.12.009
|
|
|
“Kinetic and thermodynamic heterogeneity : an intrinsic source of variability in Cu-based RRAM memories”. Clima S, Belmonte A, Degraeve R, Fantini A, Goux L, Govoreanu B, Jurczak M, Ota K, Redolfi A, Kar GS, Pourtois G, Journal of computational electronics 16, 1011 (2017). http://doi.org/10.1007/S10825-017-1042-3
Abstract: <script type='text/javascript'>document.write(unpmarked('The resistive random-access memory (RRAM) device concept is close to enabling the development of a new generation of non-volatile memories, provided that their reliability issues are properly understood. The design of a RRAM operating with extrinsic defects based on metallic inclusions, also called conductive bridge RAM, allows the use of a large spectrum of solid electrolytes. However, when scaled to device dimensions that meet the requirements of the latest technological nodes, the discrete nature of the atomic structure of the materials impacts the device operation. Using density functional theory simulations, we evaluated the migration kinetics of Cu conducting species in amorphous and solid electrolyte materials, and established that atomic disorder leads to a large variability in terms of defect stability and kinetic barriers. This variability has a significant impact on the filament resistance and its dynamics, as evidenced during the formation step of the resistive filament. Also, the atomic configuration of the formed filament can age/relax to another metastable atomic configuration, and lead to a modulation of the resistivity of the filament. All these observations are qualitatively explained on the basis of the computed statistical distributions of the defect stability and on the kinetic barriers encountered in RRAM materials.'));
Keywords: A1 Journal article; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 1.526
Times cited: 2
DOI: 10.1007/S10825-017-1042-3
|
|