“Selectivity in sorption and hydrogenation of methyl oleate and elaidate on MFI zeolites”. Philippaerts A, Paulussen S, Turner S, Lebedev OI, Van Tendeloo G, Poelman H, Bulut M, de Clippel F, Smeets P, Sels B, Jacobs P, Journal of catalysis 270, 172 (2010). http://doi.org/10.1016/j.jcat.2009.12.022
Abstract: Different zeolites were tested for selective removal of methyl elaidate (trans isomer) from an equimolar mixture with methyl oleate (cis isomer). Sorption experiments of the geometric isomers show that only ZSM-5 samples with reduced Al content in the framework are able to discriminate among the bent cis and the linear trans fatty acid methyl esters. Hydrogenation experiments of equimolar methyl oleate and elaidate mixtures at low temperature (65 °C) and high hydrogen pressure (6.0 MPa), using Pt catalysts, confirm this result. Only with a Pt/NaZSM-5 catalyst outspoken selectivity for the hydrogenation of the trans isomer is obtained. In order to prepare a selective Pt/ZSM-5 catalyst, the influence of Pt addition (impregnation, ion-exchange and competitive ion-exchange) and Pt activation (different calcination and reduction temperatures) on the Pt-distribution and Pt particle size was investigated using SEM, bright-field and HR TEM, EDX, electron tomography, CO-chemisorption, XPS, XRD, and UVvis measurements. The best result in terms of hydrogenation activity and selectivity is obtained with a Pt/ZSM-5 catalyst, which is prepared via competitive ion-exchange, followed by slow calcination up to 350 °C under high O2 flow and a reduction up to 500 °C under H2. This preparation method leads to a Pt/ZSM-5 catalyst with the best Pt distribution and the smallest Pt clusters occluded in the zeolite structure. Finally, the influence of zeolite crystal size, morphology, and elemental composition of ZSM-5 on hydrogenation activity and selectivity was investigated in detail.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 6.844
Times cited: 24
DOI: 10.1016/j.jcat.2009.12.022
|
|
|
“Modeling the single-gate, double-gate, and gate-all-around tunnel field-effect transistor”. Verhulst A, Sorée B, Leonelli D, Vandenberghe WG, Groeseneken G, Journal Of Applied Physics 107, 024518 (2010). http://doi.org/10.1063/1.3277044
Abstract: Tunnel field-effect transistors (TFETs) are potential successors of metal-oxide-semiconductor FETs because scaling the supply voltage below 1 V is possible due to the absence of a subthreshold-swing limit of 60 mV/decade. The modeling of the TFET performance, however, is still preliminary. We have developed models allowing a direct comparison between the single-gate, double-gate, and gate-all-around configuration at high drain voltage, when the drain-voltage dependence is negligible, and we provide improved insight in the TFET physics. The dependence of the tunnel current on device parameters is analyzed, in particular, the scaling with gate-dielectric thickness, channel thickness, and dielectric constants of gate dielectric and channel material. We show that scaling the gate-dielectric thickness improves the TFET performance more than scaling the channel thickness and that improvements are often overestimated. There is qualitative agreement between our model and our experimental data.
Keywords: A1 Journal article; Electron Microscopy for Materials Science (EMAT);
Impact Factor: 2.068
Times cited: 150
DOI: 10.1063/1.3277044
|
|
|
“Speciation and diurnal variation of thoracic, fine thoracic and sub-micrometer airborne particulate matter at naturally ventilated office environments”. Horemans B, Van Grieken R, Atmospheric environment : an international journal 44, 1497 (2010). http://doi.org/10.1016/J.ATMOSENV.2010.01.010
Abstract: Thoracic (PM10), fine thoracic (PM2.5) and sub-micrometer (PM1) airborne particulate matter was sampled during day and night. In total, about 100 indoor and outdoor samples were collected for each fraction at ten different office environments. Energy-dispersive X-ray fluorescence spectrometry and ion chromatography were applied for the quantification of some major and minor elements and ions in the collected aerosols. During daytime, mass concentrations were in the ranges: 1129, 8.124, and 6.618 μg m−3, with averages of 20 ± 1, 15.0 ± 0.9, and 11.0 ± 0.8 μg m−3, respectively. At night, mass concentrations were found to be significantly lower for all fractions. Indoor PM1 concentrations exceeded the corresponding outdoor levels during office hours and were thought to be elevated by office printers. Particles with diameters between 1 and 2.5 μm and 2.5 and 10 μm were mainly associated with soil dust elements and were clearly subjected to distinct periods of settling/resuspension. Indoor NO3 − levels were found to follow specific microclimatic conditions at the office environments, while daytime levels of sub-micrometer Cl− were possibly elevated by the use of Cl-containing cleaning products. Indoor carbon black concentrations were sometimes as high as 22 μg m−3 and were strongly correlated with outdoor traffic conditions.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
DOI: 10.1016/J.ATMOSENV.2010.01.010
|
|
|
“Nitrogen and luminescent nitrogen-vacancy defects in detonation nanodiamond”. Vlasov II, Shenderova O, Turner S, Lebedev OI, Basov AA, Sildos I, Rähn M, Shiryaev AA, Van Tendeloo G, Small 6, 687 (2010). http://doi.org/10.1002/smll.200901587
Abstract: An efficient method to investigate the microstructure and spatial distribution of nitrogen and nitrogen-vacancy (N-V) defects in detonation nanodiamond (DND) with primary particle sizes ranging from approximately 3 to 50 nm is presented. Detailed analysis reveals atomic nitrogen concentrations as high as 3 at% in 50% of diamond primary particles with sizes smaller than 6 nm. A non-uniform distribution of nitrogen within larger primary DND particles is also presented, indicating a preference for location within the defective central part or at twin boundaries. A photoluminescence (PL) spectrum with well-pronounced zero-phonon lines related to the N-V centers is demonstrated for the first time for electron-irradiated and annealed DND particles at continuous laser excitation. Combined Raman and PL analysis of DND crystallites dispersed on a Si substrate leads to the conclusion that the observed N-V luminescence originates from primary particles with sizes exceeding 30 nm. These findings demonstrate that by manipulation of the size/nitrogen content in DND there are prospects for mass production of nanodiamond photoemitters based on bright and stable luminescence from nitrogen-related defects.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 8.643
Times cited: 84
DOI: 10.1002/smll.200901587
|
|
|
“Effect of neutron irradiation on the characteristics of laser-produced plasma”. Khaydarov RT, Beisinbaeva HB, Sabitov NM, Terentev VB, Berdiyorov GR, Nuclear fusion 50, 025024 (2010). http://doi.org/10.1088/0029-5515/50/2/025024
Abstract: Using the mass-spectrometric method we studied the formation of multi-charged plasma ions during the interaction of laser radiation with solid targets irradiated by neutron beams. We found that structural defects, caused by the neutron irradiation, influence not only the efficiency of the process of material evaporation and emission of plasma, but also the ionization and recombination processes taking place at the initial stage of plasma formation and expansion. We also show the effect of the dose of neutron irradiation on the threshold of plasma formation from the surface of the target.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 3.307
Times cited: 3
DOI: 10.1088/0029-5515/50/2/025024
|
|
|
“Investigation of inclusions trapped inside Libyan desert glass by Raman microscopy”. Swaenen M, Stefaniak EA, Frost R, Worobiec A, Van Grieken R, Analytical and bioanalytical chemistry 397, 2659 (2010). http://doi.org/10.1007/S00216-009-3351-2
Abstract: Several specimens of Libyan desert glass (LDG), an enigmatic natural glass from Egypt, were subjected to investigation by micro-Raman spectroscopy. The spectra of inclusions inside the LDG samples were successfully measured through the layers of glass and the mineral species were identified on this basis. The presence of cristobalite as typical for high-temperature melt products was confirmed, together with co-existing quartz. TiO2 was determined in two polymorphic species rutile and anatase. Micro-Raman spectroscopy proved also the presence of minerals unusual for high-temperature glasses such as anhydrite and aragonite.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation); Laboratory Experimental Medicine and Pediatrics (LEMP)
DOI: 10.1007/S00216-009-3351-2
|
|
|
“Combined molecular dynamics: continuum study of phase transitions in bulk metals under ultrashort pulsed laser irradiation”. Wendelen W, Dzhurakhalov AA, Peeters FM, Bogaerts A, The journal of physical chemistry: C : nanomaterials and interfaces 114, 5652 (2010). http://doi.org/10.1021/jp907385n
Abstract: The phase transition processes induced by ultrashort, 100 fs pulsed laser irradiation of Au, Cu, and Ni are studied by means of a combined atomistic-continuum approach. A moderately low absorbed laser fluence range, from 200 to 600 J/m2 is considered to study phase transitions by means of a local and a nonlocal order parameter. At low laser fluences, the occurrence of layer-by-layer evaporation has been observed, which suggests a direct solid to vapor transition. The calculated amount of molten material remains very limited under the conditions studied, especially for Ni. Therefore, our results show that a kinetic equation that describes a direct solid to vapor transition might be the best approach to model laser-induced phase transitions by continuum models. Furthermore, the results provide more insight into the applicability of analytical superheating theories that were implemented in continuum models and help the understanding of nonequilibrium phase transitions.
Keywords: A1 Journal article; Integrated Molecular Plant Physiology Research (IMPRES); Condensed Matter Theory (CMT); Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 4.536
Times cited: 2
DOI: 10.1021/jp907385n
|
|
|
“On the mechanism of twin formation in FeMnC TWIP steels”. Idrissi H, Renard K, Ryelandt L, Schryvers D, Jacques PJ, Acta materialia 58, 2464 (2010). http://doi.org/10.1016/j.actamat.2009.12.032
Abstract: Although it is well known that FeMnC TWIP steels exhibit high work-hardening rates, the elementary twinning mechanisms controlling the plastic deformation of these steels have still not been characterized. The aim of the present study is to analyse the extended defects related to the twinning occurrence using transmission electron microscopy. Based on these observations, the very early stage of twin nucleation can be attributed to the pole mechanism with deviation proposed by Cohen and Weertman or to the model of Miura, Takamura and Narita, while the twin growth is controlled by the pole mechanism proposed by Venables. High densities of sessile Frank dislocations are observed within the twins at the early stage of deformation, which can affect the growth and the stability of the twins, but also the strength of these twins and their interactions with the gliding dislocations present in the matrix. This experimental evidence is discussed and compared to recent results in order to relate the defects analysis to the macroscopic behaviour of this category of material.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.301
Times cited: 244
DOI: 10.1016/j.actamat.2009.12.032
|
|
|
“Guided nucleation of superconductivity on a graded magnetic substrate”. Milošević, MV, Gillijns W, Silhanek AV, Libál A, Peeters FM, Moshchalkov VV, Applied physics letters 96, 032503 (2010). http://doi.org/10.1063/1.3293300
Abstract: We demonstrate the controlled spatial nucleation of superconductivity in a thin film deposited on periodic arrays of ferromagnetic dots with gradually increasing diameter. The perpendicular magnetization of the dots induces vortex-antivortex molecules in the sample, with the number of (anti)vortices increasing with magnet size. The resulting gradient of antivortex density between the dots predetermines local nucleation of superconductivity in the sample as a function of the applied external field and temperature. In addition, the compensation between the applied magnetic field and the antivortices results in an unprecedented enhancement of the critical temperature.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 3.411
Times cited: 15
DOI: 10.1063/1.3293300
|
|
|
“Structure and defect characterization of multiferroic <tex>ReMnO$3 films and multilayers by TEM”. Jehanathan N, Lebedev O, Gélard I, Dubourdieu C, Van Tendeloo G, Nanotechnology 21, 075705 (2010). http://doi.org/10.1088/0957-4484/21/7/075705
Abstract: Epitaxial rare earth manganite thin films (ReMnO3; Re = Tb, Ho, Er, and Y) and multilayers were grown by liquid injection metal organic chemical vapor deposition (MOCVD) on YSZ(111) and the same systems were grown c-oriented on Pt(111) buffered Si substrates. They have been structurally investigated by electron diffraction (ED) and high resolution transmission electron microscopy (HRTEM). Nanodomains of secondary orientation are observed in the hexagonal YMnO3 films. They are related to a YSZ(111) and Pt(111) misorientation. The epitaxial film thickness has an influence on the defect formation. TbO2 and Er2O3 inclusions are observed in the TbMnO3 and ErMnO3 films respectively. The structure and orientation of these inclusions are correlated to the resembling symmetry and structure of film and substrate. The type of defect formed in the YMnO3/HoMnO3 and YMnO3/ErMnO3 multilayers is also influenced by the type of substrate they are grown on. In our work, atomic growth models for the interface between the film/substrate are proposed and verified by comparison with observed and computer simulated images.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.44
Times cited: 15
DOI: 10.1088/0957-4484/21/7/075705
|
|
|
“Kink-antikink vortex transfer in periodic-plus-random pinning potential : theoretical analysis and numerical experiments”. Pogosov WV, Zhao HJ, Misko VR, Peeters FM, Physical review : B : condensed matter and materials physics 81 (2010). http://doi.org/10.1103/PhysRevB.81.024513
Abstract: The influence of random pinning on the vortex dynamics in a periodic square potential under an external drive is investigated. Using numerical experiments and theoretical approach, we found several dynamical regimes of vortex motion that are different from the ones for a regular pinning potential. Vortex transfer is controlled by kinks and antikinks, which either pre-exist in the system or appear spontaneously in pairs and then propagate. When kinks and antikinks collide, they annihilate. We provide clear physical interpretations of the observed features.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 3.836
Times cited: 10
DOI: 10.1103/PhysRevB.81.024513
|
|
|
“Incommensurate crystallographic shear structures and magnetic properties of the cation deficient perovskite (Sr0.61Pb0.18)(Fe0.75Mn0.25)O2.29”. Malo S, Lepoittevin C, Pérez O, Hébert S, Van Tendeloo G, Hervieu M, Chemistry of materials 22, 1788 (2010). http://doi.org/10.1021/cm903288s
Abstract: The origin of the incommensurability in the crystallographic shear (CS) structure of the ferri-Manganite (Sr0.61Pb0.18)(Fe0.75Mn0.25)O2.29, related to the cation deficient perovskite, has been determined by careful analysis of the boundaries between the two variants constituting the phasoid. High Resolution Electron Microscopy/HAADF-STEM images allow the structural mechanisms to be understood through the presence of structural units common to both phases, responsible of the incommensurate character observed in the electron diffraction patterns. The structural analysis allows for identifying different types of CS phases in the Pb−Sr−Fe(Mn)−O diagram and shows that the stabilization of the six-sided tunnels requires a higher A/B cationic ratio. A description of these phases is proposed through simple structural building units (SBU), based on chains of octahedra bordered by two pyramids. The (Sr0.61Pb0.18)(Fe0.75Mn0.25)O2.29 CS compound exhibits a strong antiferromagnetic and insulating behavior, similar to the Fe-2201 and terrace ferrites but differs by the presence of a hysteresis, with a small coercive field.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 6
DOI: 10.1021/cm903288s
|
|
|
“Continuous structural transitions in quasi-one-dimensional classical Wigner crystals”. Piacente G, Hai GQ, Peeters FM, Physical review : B : condensed matter and materials physics 81 (2010). http://doi.org/10.1103/PhysRevB.81.024108
Abstract: We study the structural phase transitions in confined systems of strongly interacting particles. We consider infinite quasi-one-dimensional systems with different pairwise repulsive interactions in the presence of an external confinement following a power law. Within the framework of Landaus theory, we find the necessary conditions to observe continuous transitions and demonstrate that the only allowed continuous transition is between the single- and the double-chain configurations and that it only takes place when the confinement is parabolic. We determine analytically the behavior of the system at the transition point and calculate the critical exponents. Furthermore, we perform Monte Carlo simulations and find a perfect agreement between theory and numerics.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 3.836
Times cited: 37
DOI: 10.1103/PhysRevB.81.024108
|
|
|
“Transmission electron microscopy study of phase compatibility in low hysteresis shape memory alloys”. Delville R, Kasinathan S, Zhang Z, van Humbeeck J, James RD, Schryvers D, Philosophical magazine 90, 177 (2010). http://doi.org/10.1080/14786430903074755
Abstract: Recent findings have linked low hysteresis in shape memory alloys with phase compatibility between austenite and martensite. To investigate the evolution of microstructure as phase compatibility increases and hysteresis is reduced, transmission electron microscopy was used to study the alloy system Ti50Ni50xPdx, where the composition is systemically tuned to approach perfect compatibility. Changes in morphology, twinning density and twinning modes are reported, along with special microstructures occurring when compatibility is achieved. In addition, the interface between austenite and a single variant of martensite was studied by high-resolution and conventional electron microscopy. The low energy configuration of the interface detailed in this article suggests that it plays an important role in the lowering of hysteresis compared to classical habit plane interfaces.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 1.505
Times cited: 70
DOI: 10.1080/14786430903074755
|
|
|
“Catalytic characterization of pure SnO2 and GeO2 in methanol steam reforming”. Zhao Q, Lorenz H, Turner S, Lebedev OI, Van Tendeloo G, Rameshan C, Klötzer B, Konzett J, Penner S, Applied catalysis : A : general 375, 188 (2010). http://doi.org/10.1016/j.apcata.2009.12.027
Abstract: Structural changes of a variety of different SnO, SnO2 and GeO2 catalysts upon reduction in hydrogen were correlated with associated catalytic changes in methanol steam reforming. Studied systems include SnO, SnO2 and GeO2 thin film model catalysts prepared by vapour phase deposition and growth on polycrystalline NaCl surfaces and, for comparison, the corresponding pure oxide powder catalysts. Reduction of both the SnO2 thin film and powder at around 673 K in 1 bar hydrogen leads to a substantial reduction of the bulk structure and yields a mixture of SnO2 and metallic β-Sn. On the powder catalyst this transformation is fully reversible upon oxidation in 1 bar O2 at 673 K. Strongly reduced thin films, however, can only be re-transformed to SnO2 if the reduction temperature did not exceed 573 K. For GeO2, the situation is more complex due to its polymorphism. Whereas the tetragonal phase is structurally stable during reduction, oxidation or catalytic reaction, a small part of the hexagonal phase is always transformed into the tetragonal at 673 K independent of the gas phase used. SnO2 is highly active and CO2 selective in methanol steam reforming, but the initial high activity drops considerably upon reduction between 373 and 573 K and almost complete catalyst deactivation is observed after reduction at 673 K, which is associated with the parallel formation of β-Sn. In close correlation to the structural results, the catalytic activity and selectivity can be restored upon an oxidative catalyst regeneration at 673 K. Tetragonal GeO2 exhibits only a small activity and no pronounced selectivity to either CO or CO2, at least after reduction. In its fully oxidized state release of surface/lattice oxygen results in a non-catalytic formation of CO2 by oxidation of CO originating from catalytic dehydrogenation.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.339
Times cited: 20
DOI: 10.1016/j.apcata.2009.12.027
|
|
|
“Branch current behavior at two level anti-crossings in vertical quantum dot single-particle spectra”. Payette C, Austing DG, Yu G, Gupta JA, Nair SV, Partoens B, Amaha S, Tarucha S, AIP conference proceedings 1199, 271 (2010). http://doi.org/10.1063/1.3295404
Abstract: We study single-electron-elastic-resonant-tunneling through two weakly coupled vertical quantum dots and investigate the branch current behavior at anti-crossings between two single-particle energy levels in the constituent dot spectra that are induced to approach each other by application of an out-of-dot-plane magnetic field. We observe both the familiar case of monotonic transfer of the resonant current strengths between the two branches as well as the less familiar case of concurrent enhancement and suppression (ideally complete cancellation) of the resonant current in the two branches. These two situations can be explained in terms of a simple coherent tunneling model. ©2009 American Institute of Physics
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
DOI: 10.1063/1.3295404
|
|
|
“Ordering of Pd2+ and Pd4+ in the mixed-valent palladate KPd2O3”. Panin RV, Khasanova NR, Bougerol C, Schnelle W, Van Tendeloo G, Antipov EV, Inorganic chemistry 49, 1295 (2010). http://doi.org/10.1021/ic902187a
Abstract: A new potassium palladate KPd2O3 was synthesized by the reaction of KO2 and PdO at elevated oxygen pressure. Its crystal structure was solved from powder X-ray diffraction data in the space group Rm (a = 6.0730(1) Å, c = 18.7770(7) Å, and Z = 6). KPd2O3 represents a new structure type, consisting of an alternating sequence of K+ and Pd2O3− layers with ordered Pd2+ and Pd4+ ions. The presence of palladium ions in di- and tetravalent low-spin states was confirmed by magnetic susceptibility measurements.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 9
DOI: 10.1021/ic902187a
|
|
|
“Synchrotron-based X-ray absorption spectroscopy for art conservation: looking back and looking forward”. Cotte M, Susini J, Dik J, Janssens K, Accounts of chemical research 43, 705 (2010). http://doi.org/10.1021/AR900199M
Abstract: A variety of analytical techniques augmented by the use of synchrotron radiation (SR), such as X-ray fluorescence (SR-XRF) and X-ray diffraction (SR-XRD), are now readily available, and they differ little, conceptually, from their common laboratory counterparts. Because of numerous advantages afforded by SR-based techniques over benchtop versions, however, SR methods have become popular with archaeologists, art historians, curators, and other researchers in the field of cultural heritage (CH). Although the CH community now commonly uses both SR-XRF and SR-XRD, the use of synchrotron-based X-ray absorption spectroscopy (SR-XAS) techniques remains marginal, mostly because CH specialists rarely interact with SR physicists. In this Account, we examine the basic principles and capabilities of XAS techniques in art preservation. XAS techniques offer a combination of features particularly well-suited for the chemical analysis of works of art. The methods are noninvasive, have low detection limits, afford high lateral resolution, and provide exceptional chemical sensitivity. These characteristics are highly desirable for the chemical characterization of precious, heterogeneous, and complex materials. In particular, the chemical mapping capability, with high spatial resolution that provides information about local composition and chemical states, even for trace elements, is a unique asset. The chemistry involved in both the objects history (that is, during fabrication) and future (that is, during preservation and restoration treatments) can be addressed by XAS. On the one hand, many studies seek to explain optical effects occurring in historical glasses or ceramics by probing the molecular environment of relevant chromophores. Hence, XAS can provide insight into craft skills that were mastered years, decades, or centuries ago but were lost over the course of time. On the other hand, XAS can also be used to characterize unwanted reactions, which are then considered alteration phenomena and can dramatically alter the objects original visual properties. In such cases, the bulk elemental composition is usually unchanged. Hence, monitoring oxidation state (or, more generally, other chemical modifications) can be of great importance. Recent applications of XAS in art conservation are reviewed and new trends are discussed, highlighting the value (and future possibilities) of XAS, which remains, given its potential, underutilized in the CH community.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 20.268
Times cited: 74
DOI: 10.1021/AR900199M
|
|
|
“Model-based determination of dielectric function by STEM low-loss EELS”. Zhang L, Turner S, Brosens F, Verbeeck J, Physical review : B : condensed matter and materials physics 81, 035102 (2010). http://doi.org/10.1103/PhysRevB.81.035102
Abstract: Dielectric properties of materials are crucial in describing the electromagnetic response of materials. As devices are becoming considerably smaller than the optical wavelength, the conventional measuring methods based on optical response are limited by their spatial resolution. Electron energy loss spectroscopy performed in a scanning transmission electron microscope is a good alternative to obtain the dielectric properties with excellent spatial resolution. Due to the overlap of diffraction discs in scanning transmission electron microscopy, it is difficult to apply conventional experimental settings to suppress retardation losses. In this contribution, a relativistic dielectric model for the loss function is presented which is used in a model based optimization scheme to estimate the complex dielectric function of a material. The method is applied to experiments on bulk diamond and SrTiO3 and shows a good agreement with optical reference data when retardation effects are included. Application of this technique to nanoparticles is possible but several theoretical assumptions made in the model of the loss function are violated and interpretation becomes problematic.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Theory of quantum systems and complex systems
Impact Factor: 3.836
Times cited: 9
DOI: 10.1103/PhysRevB.81.035102
|
|
|
“Formation of stripelike flux patterns obtained by freezing kinematic vortices in a superconducting Pb film”. Silhanek AV, Milošević, MV, Kramer RBG, Berdiyorov GR, Vondel van de J, Luccas RF, Puig T, Peeters FM, Moshchalkov VV, Physical review letters 104 (2010). http://doi.org/10.1103/PhysRevLett.104.017001
Abstract: We demonstrate experimentally and theoretically that the dissipative state of superconducting samples with a periodic array of holes at high current densities consists of flux rivers resulting from a short-range attractive interaction between vortices. This dynamically induced vortex-vortex attraction results from the migration of quasiparticles out of the vortex core (kinematic vortices). We have directly visualized the formation of vortex chains by scanning Hall probe microscopy after freezing the dynamic state by a field cooling procedure at a constant bias current. Similar experiments carried out in a sample without holes show no hint of flux river formation. We shed light on this nonequilibrium phenomena modeled by time-dependent Ginzburg-Landau simulations.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 8.462
Times cited: 60
DOI: 10.1103/PhysRevLett.104.017001
|
|
|
“Molecular dynamics simulation of oxide thin film growth: importance of the inter-atomic interaction potential”. Georgieva V, Todorov IT, Bogaerts A, Chemical physics letters 485, 315 (2010). http://doi.org/10.1016/j.cplett.2009.12.067
Abstract: A molecular dynamics (MD) study of MgxAlyOz thin films grown by magnetron sputtering is presented using an ionic model and comparing two potential sets with formal and partial charges. The applicability of the model and the reliability of the potential sets for the simulation of thin film growth are discussed. The formal charge potential set was found to reproduce the thin film structure in close agreement with the structure of the experimentally grown thin films. Graphical abstract A molecular dynamics study of growth of MgxAlyOz thin films is presented using an ionic model and comparing two potential sets with formal and partial charges. The simulation results with the formal charge potential set showed a transition in the film from a crystalline to an amorphous structure, when the Mg metal content decreases below 50% in very close agreement with the structure of the experimentally deposited films.
Keywords: A1 Journal article; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 1.815
Times cited: 16
DOI: 10.1016/j.cplett.2009.12.067
|
|
|
“Pd-In2O3 interaction due to reduction in hydrogen: consequences for methanol steam reforming”. Lorenz H, Turner S, Lebedev OI, Van Tendeloo G, Klötzer B, Rameshan C, Pfaller K, Penner S, Applied catalysis : A : general 374, 180 (2010). http://doi.org/10.1016/j.apcata.2009.12.007
Abstract: Two different Pd/In2O3 samples including a thin film model catalyst with well-defined Pd particles grown on NaCl(0 0 1) supports and a powder catalyst prepared by an impregnation technique are examined by electron microscopy, X-ray diffraction and catalytic measurements in methanol steam reforming in order to correlate the formation of different oxide-supported bimetallic PdIn phases with catalytic activity and selectivity. A PdIn shell around the Pd particles is observed on the thin film catalyst after embedding the Pd particles in In2O3 at 300 K, likely because alloying to PdIn and oxidation to In2O3 are competing processes. Increased PdIn bimetallic formation is observed up to 573 K reduction temperature until at 623 K the film stability limit in hydrogen is reached. Oxidative treatments at 573 K lead to decomposition of PdIn and to the formation of an In2O3 shell covering the Pd particles, which irreversibly changes the activity and selectivity pattern to clean In2O3. PdIn and Pd2In3 phases are obtained on the powder catalyst after reduction at 573 K and 673 K, respectively. Only CO2-selective methanol steam reforming is observed in the reduction temperature range between 473 K and 573 K. After reduction at 673 K encapsulation of the bimetallic particles by crystalline In2O3 suppresses CO2 formation and only activity and selectivity of clean In2O3 are measured.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.339
Times cited: 55
DOI: 10.1016/j.apcata.2009.12.007
|
|
|
“LiZnNb4O11.5 : a novel oxygen deficient compound in the Nb-rich part of the Li2O-ZnO-Nb2O5 system”. Morozov VA, Arakcheeva AV, Konovalova VV, Pattison P, Chapuis G, Lebedev OI, Fomichev VV, Van Tendeloo G, Journal of solid state chemistry 183, 408 (2010). http://doi.org/10.1016/j.jssc.2009.12.008
Abstract: A novel lithium zinc niobium oxide LiZnNb(4)O(11.5) (LZNO) has been found in the Nb-rich part of Li(2)O-ZnO-Nb(2)O(5) system. LZNO, with an original alpha-PbO(2) related structure, has been synthesized by the routine ceramic technique and characterized by X-ray diffraction and transmission electron microscopy (TEM). Reflections belonging to the LZNO phase, observed in X-ray powder diffraction (XRPD) and electron diffraction, have been indexed as monoclinic with unit cell parameters a=17.8358(9)angstrom, b=15.2924(7)angstrom, c=5.0363(3)angstrom and gamma=96.607(5)degrees or as alpha-PbO(2)-like with lattice constants a=4.72420(3)angstrom, b=5.72780(3)angstrom, c=5.03320(3)angstrom, gamma=90.048(16)degrees and modulation vector q=0.3a*+1.1b* indicating a commensurately modulated alpha-PbO(2) related structure. The monoclinic cell is a supercell related to the latter. Using synchrotron powder diffraction data, the structure has been solved and refined as a commensurate modulation (superspace group P112(1)/n(alpha beta 0)00) as well as a supercell (space group P2(1)/b). The superspace description allows us to consider the LZNO structure as a member of the proposed alpha-PbO(2)-Z (3 + 1)D structure type, which unifies both incommensurately and commensurately modulated structures. HRTEM reveals several types of defects in LZNO and structural models for these defects are proposed. Two new phases in Li(2)O-ZnO-Nb(2)O(5) system are predicted on the basis of this detailed HRTEM analysis. (C) 2009 Elsevier Inc. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 9
DOI: 10.1016/j.jssc.2009.12.008
|
|
|
“James Ensor's pigment use: artistic and material evolution studied by means of portable X-ray fluorescence spectrometry”. van der Snickt G, Janssens K, Schalm O, Aibéo C, Kloust H, Alfeld M, X-ray spectrometry 39, 103 (2010). http://doi.org/10.1002/XRS.1235
Abstract: In this paper, portable X-ray fluorescence spectrometry (PXRF) was employed as a screening tool for determining and comparing the pigment use in a large series of paintings by the Belgian artist James Ensor (1860-1949). Benefits and drawbacks of PXRF as a method, and the instrument employed, are discussed from a practical, conservation and instrumental perspective. Regardless of several restrictions due to the set-up and/or the analytical method, it appeared feasible to document the evolution with time in Ensor's use of inorganic pigments and to correlate this technical evolution with stylistic developments, Nevertheless, it became clear that a full identification of all materials present can only be done by means of the analysis of (cross-sectioned) samples.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 1.298
Times cited: 25
DOI: 10.1002/XRS.1235
|
|
|
“Direct structure inversion from exit waves: part 1: theory and simulations”. Wang A, Chen FR, Van Aert S, van Dyck D, Ultramicroscopy 110, 527 (2010). http://doi.org/10.1016/j.ultramic.2009.11.024
Abstract: In order to interpret the amplitude and phase of the exit wave in terms of mass and position of the atoms, one has to invert the dynamic scattering of the electrons in the object so as to obtain a starting structure which can then be used as a seed for further quantitative structure refinement. This is especially challenging in case of a zone axis condition when the interaction of the electrons with the atom column is very strong. Based on the channelling theory we will show that the channelling map not only yields a circle on the Argand plot but also a circular defocus curve for every column. The former gives the number of atoms in each column, while the latter provides the defocus value for each column, which reveals the surface roughness at the exit plane with single atom sensitivity.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 2.843
Times cited: 25
DOI: 10.1016/j.ultramic.2009.11.024
|
|
|
“Real space maps of magnetic moments on the atomic scale: theory and feasibility”. Schattschneider P, Ennen I, Stoger-Pollach M, Verbeeck J, Mauchamp V, Jaouen M, Ultramicroscopy 110, 1038 (2010). http://doi.org/10.1016/j.ultramic.2009.11.020
Abstract: The recently discovered EMCD technique (energy loss magnetic chiral dichroism) can detect atom specific magnetic moments with nanometer resolution, exploiting the spin selectivity of electronic transitions in energy loss spectroscopy. Yet, direct imaging of magnetic moments on the atomic scale is not possible. In this paper we present an extension of EMCD that can overcome this limit. As a model system we chose bcc Fe. We present image simulations of the L3 white line signal, based on the kinetic equation for the density matrix of the 200 kV probe electron. With actual progress in instrumentation (high brightness sources, aberration corrected lenses) this technique should allow direct imaging of spin moments on the atomic scale.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.843
Times cited: 10
DOI: 10.1016/j.ultramic.2009.11.020
|
|
|
“Molecular sieve properties of mesoporous silica with intraporous nanocarbon”. de Clippel F, Harkiolakis A, Ke X, Vosch T, Van Tendeloo G, Baron GV, Jacobs PA, Denayer JFM, Sels BF, Chemical communications 46, 928 (2010). http://doi.org/10.1039/b918864a
Abstract: Biporous carbonsilica materials (CSM) with molecular sieve properties and high sorption capacity were developed by synthesizing nano-sized carbon crystallites in the mesopores of Al-MCM-41.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.319
Times cited: 21
DOI: 10.1039/b918864a
|
|
|
“Focused ion beam/scanning electron microscopy tomography and conventional transmission electron microscopy assessment of Ni4Ti3 morphology in compression-aged Ni-rich Ni-Ti single crystals”. Cao S, Somsen C, Croitoru M, Schryvers D, Eggeler G, Scripta materialia 62, 399 (2010). http://doi.org/10.1016/j.scriptamat.2009.11.040
Abstract: The size, morphology and configuration of Ni4Ti3 precipitates in a single-crystal NiTi alloy have been investigated by two-dimensional transmission electron microscopy-based image analysis and three-dimensional reconstruction from slice-and-view images obtained in a focused ion beam/scanning electron microscopy (FIB/SEM) dual-beam system. Average distances between the precipitates measured along the compression direction correlate well between both techniques, while particle shape and configuration data is best obtained from FIB/SEM. Precipitates form pockets of B2 of 0.54 ìm in the compression direction and 1 ìm perpendicular to the compression direction.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Condensed Matter Theory (CMT)
Impact Factor: 3.747
Times cited: 16
DOI: 10.1016/j.scriptamat.2009.11.040
|
|
|
“Photo-excited carriers and optical conductance and transmission in graphene in the presence of phonon scattering”. Dong HM, Xu W, Zhang J, Peeters FM, Vasilopoulos P, Physica. E: Low-dimensional systems and nanostructures 42, 748 (2010). http://doi.org/10.1016/j.physe.2009.11.048
Abstract: We present a theoretical study of the optoelectronic properties of monolayer graphene. Including the effect of the electron-photon-phonon scattering, we employ the mass- and energy-balance equations derived from the Boltzmann equation to evaluate self-consistently the carrier densities, optical conductance and transmission coefficient in graphene in the presence of linearly polarized radiation field. We find that the photo-excited carrier density can be increased under infrared radiation and depend strongly on radiation intensity and frequency. For short wavelengths (lambda <3 mu m), the universal optical conductance sigma(0) = e(2)/4h is obtained and the light transmittance is about 0.97-0.98. Interestingly, there is an optical absorption window in the range 4-100 mu m which is induced by different transition energies required for inter- and intra-band optical absorption. The position and width of this absorption window depend sensitively on temperature and carrier density of the system. These results are relevant for applications of recently developed graphene devices in advanced optoelectronics such as the infrared photodetectors. Crown Copyright (C) 2009 Published by Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Condensed Matter Theory (CMT)
Impact Factor: 2.221
Times cited: 7
DOI: 10.1016/j.physe.2009.11.048
|
|
|
“Radiation dose estimation and mass attenuation coefficients of cement samples used in Turkey”. Damla N, Čevik U, Kobya AI, Celik A, Celik N, Van Grieken R, Journal of hazardous materials 176, 644 (2010). http://doi.org/10.1016/J.JHAZMAT.2009.11.080
Abstract: Different cement samples commonly used in building construction in Turkey have been analyzed for natural radioactivity using gamma-ray spectrometry. The mean activity concentrations observed in the cement samples were 52, 40 and 324 Bq kg−1 for 226Ra, 232Th and 40K, respectively. The measured activity concentrations for these radionuclides were compared with the reported data of other countries and world average limits. The radiological hazard parameters such as radium equivalent activities (Raeq), gamma index (Iγ) and alpha index (Iα) indices as well as terrestrial absorbed dose and annual effective dose rate were calculated and compared with the international data. The Raeq values of cement are lower than the limit of 370 Bq kg−1, equivalent to a gamma dose of 1.5 mSv y−1. Moreover, the mass attenuation coefficients were determined experimentally and calculated theoretically using XCOM in some cement samples. Also, chemical compositions analyses of the cement samples were investigated.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
DOI: 10.1016/J.JHAZMAT.2009.11.080
|
|