“Kinetic regulation of the synthesis of pentatwinned gold nanorods below room temperature”. Sanchez-Iglesias A, Jenkinson K, Bals S, Liz-Marzan LM, Journal Of Physical Chemistry C 125, 23937 (2021). http://doi.org/10.1021/ACS.JPCC.1C07284
Abstract: The synthesis of gold nanorods requires the presence of symmetry-breaking and shape-directing additives, among which bromide ions and quaternary ammonium surfactants have been reported as essential. As a result, hexadecyltrimethylammonium bromide (CTAB) has been selected as the most efficient surfactant to direct anisotropic growth. One of the difficulties arising from this selection is the low solubility of CTAB in water at room temperature, and therefore the seeded growth of gold nanorods is usually performed at 25 degrees C or above, which has restricted so far the analysis of kinetic effects derived from lower temperatures. We report a systematic study of the synthesis of gold nanorods from pentatwinned seeds using hexadecyltrimethylammonium chloride (CTAC) as the principal surfactant and a low concentration of bromide as shape-directing agent. Under these conditions, the synthesis can be performed at temperatures as low as 8 degrees C, and the corresponding kinetic effects can be studied, resulting in temperature-controlled aspect ratio tunability.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.536
Times cited: 6
DOI: 10.1021/ACS.JPCC.1C07284
|
|
|
“Interface Pattern Engineering in Core‐Shell Upconverting Nanocrystals: Shedding Light on Critical Parameters and Consequences for the Photoluminescence Properties”. Hudry D, De Backer A, Popescu R, Busko D, Howard IA, Bals S, Zhang Y, Pedrazo‐Tardajos A, Van Aert S, Gerthsen D, Altantzis T, Richards BS, Small , 2104441 (2021). http://doi.org/10.1002/smll.202104441
Abstract: Advances in controlling energy migration pathways in core-shell lanthanide (Ln)-based hetero-nanocrystals (HNCs) have relied heavily on assumptions about how optically active centers are distributed within individual HNCs. In this article, it is demonstrated that different types of interface patterns can be formed depending on shell growth conditions. Such interface patterns are not only identified but also characterized with spatial resolution ranging from the nanometer- to the atomic-scale. In the most favorable cases, atomic-scale resolved maps of individual particles are obtained. It is also demonstrated that, for the same type of core-shell architecture, the interface pattern can be engineered with thicknesses of just 1 nm up to several tens of nanometers. Total alloying between the core and shell domains is also possible when using ultra-small particles as seeds. Finally, with different types of interface patterns (same architecture and chemical composition of the core and shell domains) it is possible to modify the output color (yellow, red, and green-yellow) or change (improvement or degradation) the absolute upconversion quantum yield. The results presented in this article introduce an important paradigm shift and pave the way toward the emergence of a new generation of core-shell Ln-based HNCs with better control over their atomic-scale organization.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Applied Electrochemistry & Catalysis (ELCAT)
Impact Factor: 8.643
Times cited: 17
DOI: 10.1002/smll.202104441
|
|
|
“Optical encoding of luminescent carbon nanodots in confined spaces”. Bartholomeeusen E, De Cremer G, Kennes K, Hammond C, Hermans I, Lu J-B, Schryvers D, Jacobs PA, Roeffaers MBJ, Hofkens J, Sels BF, Coutino-Gonzalez E, Chemical Communications 57, 11952 (2021). http://doi.org/10.1039/D1CC04777A
Abstract: Stable emissive carbon nanodots were generated in zeolite crystals using near infrared photon irradiation gradually converting the occluded organic template, originally used to synthesize the zeolite crystals, into discrete luminescent species consisting of nano-sized carbogenic fluorophores, as ascertained using Raman microscopy, and steady-state and time-resolved spectroscopic techniques. Photoactivation in a confocal laser fluorescence microscope allows 3D resolved writing of luminescent carbon nanodot patterns inside zeolites providing a cost-effective and non-toxic alternative to previously reported metal-based nanoclusters confined in zeolites, and opens up opportunities in bio-labelling and sensing applications.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.319
DOI: 10.1039/D1CC04777A
|
|
|
“3D Atomic Structure of Supported Metallic Nanoparticles Estimated from 2D ADF STEM Images: A Combination of Atom –, Counting and a Local Minima Search Algorithm”. Arslan Irmak E, Liu P, Bals S, Van Aert S, Small methods , 2101150 (2021). http://doi.org/10.1002/smtd.202101150
Abstract: Determining the three-dimensional (3D) atomic structure of nanoparticles (NPs) is critical to understand their structure-dependent properties. It is hereby important to perform such analyses under conditions relevant for the envisioned application. Here, we investigate the 3D structure of supported Au NPs at high temperature, which is of importance to understand their behavior during catalytic reactions. To overcome limitations related to conventional high-resolution electron tomography at high temperature, 3D characterization of NPs with atomic resolution has been performed by applying atom-counting using atomic resolution annular darkfield scanning transmission electron microscopy (ADF STEM) images followed by structural relaxation. However, at high temperatures, thermal displacements, which affect the ADF STEM intensities, should be taken into account. Moreover, it is very likely that the structure of a NP investigated at elevated temperature deviates from a ground state configuration, which is difficult to determine using purely computational energy minimization approaches. In this paper, we therefore propose an optimized approach using an iterative local minima search algorithm followed by molecular dynamics (MD) structural relaxation of candidate structures associated with each local minimum. In this manner, it becomes possible to investigate the 3D atomic structure of supported NPs, which may deviate from their ground state configuration.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Times cited: 12
DOI: 10.1002/smtd.202101150
|
|
|
“Event driven 4D STEM acquisition with a Timepix3 detector: Microsecond dwell time and faster scans for high precision and low dose applications”. Jannis D, Hofer C, Gao C, Xie X, Béché, A, Pennycook Tj, Verbeeck J, Ultramicroscopy 233, 113423 (2022). http://doi.org/10.1016/j.ultramic.2021.113423
Abstract: Four dimensional scanning transmission electron microscopy (4D STEM) records the scattering of electrons in a material in great detail. The benefits offered by 4D STEM are substantial, with the wealth of data it provides facilitating for instance high precision, high electron dose efficiency phase imaging via centre of mass or ptychography based analysis. However the requirement for a 2D image of the scattering to be recorded at each probe position has long placed a severe bottleneck on the speed at which 4D STEM can be performed. Recent advances in camera technology have greatly reduced this bottleneck, with the detection efficiency of direct electron detectors being especially well suited to the technique. However even the fastest frame driven pixelated detectors still significantly limit the scan speed which can be used in 4D STEM, making the resulting data susceptible to drift and hampering its use for low dose beam sensitive applications. Here we report the development of the use of an event driven Timepix3 direct electron camera that allows us to overcome this bottleneck and achieve 4D STEM dwell times down to 100 ns; orders of magnitude faster than what has been possible with frame based readout. We characterize the detector for different acceleration voltages and show that the method is especially well suited for low dose imaging and promises rich datasets without compromising dwell time when compared to conventional STEM imaging.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 2.2
Times cited: 31
DOI: 10.1016/j.ultramic.2021.113423
|
|
|
“Dynamical diffraction of high-energy electrons investigated by focal series momentum-resolved scanning transmission electron microscopy at atomic resolution”. Robert Hl, Lobato I, Lyu Fj, Chen Q, Van Aert S, Van Dyck D, Müller-Caspary K, Ultramicroscopy 233, 113425 (2022). http://doi.org/10.1016/j.ultramic.2021.113425
Abstract: We report a study of scattering dynamics in crystals employing momentum-resolved scanning transmission
electron microscopy under varying illumination conditions. As we perform successive changes of the probe
focus, multiple real-space signals are obtained in dependence of the shape of the incident electron wave.
With support from extensive simulations, each signal is shown to be characterised by an optimum focus for
which the contrast is maximum and which differs among different signals. For instance, a systematic focus
mismatch is found between images formed by high-angle scattering, being sensitive to thickness and chemical
composition, and the first moment in diffraction space, being sensitive to electric fields. It follows that a single
recording at one specific probe focus is usually insufficient to characterise materials comprehensively. Most
importantly, we demonstrate in experiment and simulation that the second moment (
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 2.2
DOI: 10.1016/j.ultramic.2021.113425
|
|
|
“Third-Order Nonlinear Optical Properties and Saturation of Two-Photon Absorption in Lead-Free Double Perovskite Nanocrystals under Femtosecond Excitation”. Mushtaq A, Pradhan B, Kushavah D, Zhang Y, Wolf M, Schrenker N, Fron E, Bals S, Hofkens J, Debroye E, Pal SK, Acs Photonics 8, 3365 (2021). http://doi.org/10.1021/acsphotonics.1c01351
Abstract: Lead halide perovskites have been widely explored
in the field of photovoltaics, light-emitting diodes, and lasers due to
their outstanding linear and nonlinear optical (NLO) properties.
But, the presence of lead toxicity and low chemical stability remain
serious concerns. Lead-free double perovskite with excellent
optical properties and chemical stability could be an alternative.
However, proper examination of the NLO properties of such a
material is crucial to identify their utility for future nonlinear device
applications. Herein, we have made use of femtosecond (fs) Z-scan
technique to explore the NLO properties of Cs2AgIn0.9Bi0.1Cl6
nanocrystals (NCs). Our measurements suggest that under
nonresonant fs excitation, perovskite NCs exhibit strong twophoton
absorption (TPA). The observed saturation of TPA at high
light intensities has been explained by a customized model. Furthermore, we have demonstrated a change in the nonlinear refractive
index of the NCs under varying input intensities. The strong TPA absorption of lead-free double perovskite NCs could be used for
Kerr nonlinearity-based nonlinear applications such as optical shutters for picosecond lasers.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 6.756
Times cited: 25
DOI: 10.1021/acsphotonics.1c01351
|
|
|
“Nanoparticle-MediatedIn SituMolecular Reprogramming of Immune Checkpoint Interactions for Cancer Immunotherapy”. Walters AA, Santacana-Font G, Li J, Routabi N, Qin Y, Claes N, Bals S, Tzu-Wen Wang J, Al-Jamal KT, Acs Nano 15, 17549 (2021). http://doi.org/10.1021/acsnano.1c04456
Abstract: Immune checkpoint blockade involves targeting immune
regulatory molecules with antibodies. Preclinically, complex multiantibody
regimes of both inhibitory and stimulatory targets are a promising
candidate for the next generation of immunotherapy. However, in this
setting, the antibody platform may be limited due to excessive toxicity
caused by off target effects as a result of systemic administration. RNA
can be used as an alternate to antibodies as it can both downregulate
immunosuppressive checkpoints (siRNA) or induce expression of
immunostimulatory checkpoints (mRNA). In this study, we demonstrate
that the combination of both siRNA and mRNA in a single
formulation can simultaneously knockdown and induce expression of
immune checkpoint targets, thereby reprogramming the tumor
microenvironment from immunosuppressive to immunostimulatory
phenotype. To achieve this, RNA constructs were synthesized and
formulated into stable nucleic acid lipid nanoparticles (SNALPs); the SNALPs produced were 140−150 nm in size with >80%
loading efficiency. SNALPs could transfect macrophages and B16F10 cells in vitro resulting in 75% knockdown of inhibitory
checkpoint (PDL1) expression and simultaneously express high levels of stimulatory checkpoint (OX40L) with minimal
toxicity. Intratumoral treatment with the proposed formulation resulted in statistically reduced tumor growth, a greater
density of CD4+ and CD8+ infiltrates in the tumor, and immune activation within tumor-draining lymph nodes. These data
suggest that a single RNA-based formulation can successfully reprogram multiple immune checkpoint interactions on a
cellular level. Such a candidate may be able to replace future immune checkpoint therapeutic regimes composed of both
stimulatory- and inhibitory-receptor-targeting antibodies.
Keywords: A1 Journal article; Pharmacology. Therapy; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 13.942
Times cited: 11
DOI: 10.1021/acsnano.1c04456
|
|
|
“&alpha, phase growth and branching in titanium alloys”. Shi R, Choudhuri D, Kashiwar A, Dasari S, Wang Y, Banerjee R, Banerjee D, Philosophical magazine (2021). http://doi.org/10.1080/14786435.2021.1998693
Abstract: The morphology and spatial distribution of alpha (α) precipitates have been mapped as a function of Mo content in Ti-Mo binary alloys employing a combinatorial approach. Heat-treatments were carried out on compositionally graded Ti-xMo samples processed using a rapid throughput laser engineered net shape (LENS) process. The composition space spans 1.5 at% to 6 at% Mo with ageing at 750°C, 650°C and 600°C following a β solution treatment. Three distinct regimes of α morphology and distribution were observed. These are colony-dominated microstructures originating from grain boundary α allotriomorphs, bundles of intragranular α laths, and homogeneously distributed individual fine-scale α laths. Branching of the α precipitates was observed in all these domains in a manner reminiscent of solid-state dendritic growth. The phenomenon is particularly apparent at low volume fractions of α. Similar features are present in a wide variety of alloy compositions. 3-dimensional features of such branched structures have been analysed. Simulation of the branching process by phase field methods incorporating anisotropy in the α/β interface energy and elasticity suggests that it can be initiated at growth ledges present at broad faces of the α laths, driven by the enhancement of the diffusion flux at these steps. The dependence of branching on various parameters such as supersaturation and diffusivity, and microstructural features like ledge height and distribution and the presence of adjacent α variants has been evaluated.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 1.505
DOI: 10.1080/14786435.2021.1998693
|
|
|
“Catalytic upcycling of PVC waste-derived phthalate esters into safe, hydrogenated plasticizers”. Windels S, Diefenhardt T, Jain N, Marquez C, Bals S, Schlummer M, De Vos DE, Green chemistry : cutting-edge research for a greener sustainable future 24, 754 (2022). http://doi.org/10.1039/D1GC03864H
Abstract: Recycling of end-of-life polyvinyl chloride (PVC) calls for solutions to deal with the vast amounts of harmful phthalate plasticizers that have historically been incorporated in PVC. Here, we report on the upcycling of such waste-extracted phthalate esters into analogues of the much safer diisononyl 1,2-cyclohexanedicarboxylate plasticizer (DINCH), via a catalytic one-pot (trans)esterification-hydrogenation process. For most of the virgin phthalates, Ru/Al2O3 is a highly effective hydrogenation catalyst, yielding >99% ring-hydrogenated products under mild reaction conditions (0.1 mol% Ru, 80 degrees C, 50 bar H-2). However, applying this reaction to PVC-extracted phthalates proved problematic, (1) as benzyl phthalates are hydrogenolyzed to benzoic acids that inhibit the Ru-catalyst, and (2) because impurities in the plasticizer extract (PVC, sulfur) further retard the hydrogenation. These complications were solved by coupling the hydrogenation to an in situ (trans)esterification with a higher alcohol, and by pretreating the extract with an activated carbon adsorbent. In this way, a real phthalate extract obtained from post-consumer PVC waste was eventually completely (>99%) hydrogenated to phthalate-free, cycloaliphatic plasticizers.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 9.8
Times cited: 8
DOI: 10.1039/D1GC03864H
|
|
|
“Optimized 3D Reconstruction of Large, Compact Assemblies of Metallic Nanoparticles”. Altantzis T, Wang D, Kadu A, van Blaaderen A, Bals S, Journal Of Physical Chemistry C 125, 26240 (2021). http://doi.org/10.1021/acs.jpcc.1c08478
Abstract: 3D characterization of assemblies of nanoparticles is of great importance to determine their structure-property connection. Such investigations become increasingly more challenging when the assemblies become larger and more compact. In this paper, we propose an optimized approach for electron tomography to minimize artefacts related to beam broadening in High Angle Annular Dark-Field Scanning Transmission Electron Microscopy mode. These artefacts are typically present at one side of the reconstructed 3D data set for thick nanoparticle assemblies. To overcome this problem, we propose a procedure in which two tomographic tilt series of the same sample are acquired. After acquiring the first series, the sample is flipped over 180o, and a second tilt series is acquired. By merging the two reconstructions, blurring in the reconstructed volume is minimized. Next, this approach is combined with an advanced three-dimensional reconstruction algorithm yielding quantitative structural information. Here, the approach is applied to a thick and compact assembly of spherical Au nanoparticles, but the methodology can we used to investigate a broad range of samples.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Applied Electrochemistry & Catalysis (ELCAT)
Impact Factor: 4.536
Times cited: 4
DOI: 10.1021/acs.jpcc.1c08478
|
|
|
“Creation of Exclusive Artificial Cluster Defects by Selective Metal Removal in the (Zn, Zr) Mixed-Metal UiO-66”. Feng X, Jena HS, Krishnaraj C, Arenas-Esteban D, Leus K, Wang G, Sun J, Rüscher M, Timoshenko J, Roldan Cuenya B, Bals S, Voort PVD, Journal Of The American Chemical Society , jacs.1c05357 (2021). http://doi.org/10.1021/jacs.1c05357
Abstract: The differentiation between missing linker defects
and missing cluster defects in MOFs is difficult, thereby limiting the
ability to correlate materials properties to a specific type of defects.
Herein, we present a novel and easy synthesis strategy for the
creation of solely “missing cluster defects” by preparing mixed-metal
(Zn, Zr)-UiO-66 followed by a gentle acid wash to remove the Zn
nodes. The resulting material has the reo UiO-66 structure, typical
for well-defined missing cluster defects. The missing clusters are
thoroughly characterized, including low-pressure Ar-sorption, iDPCSTEM
at a low dose (1.5 pA), and XANES/EXAFS analysis. We
show that the missing cluster UiO-66 has a negligible number of missing linkers. We show the performance of the missing cluster
UiO-66 in CO2 sorption and heterogeneous catalysis.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 13.858
Times cited: 29
DOI: 10.1021/jacs.1c05357
|
|
|
“Towards Exotic Layered Materials: 2D Cuprous Iodide”. Mustonen K, Hofer C, Kotrusz P, Markevich A, Hulman M, Mangler C, Susi T, Pennycook TJ, Hricovini K, Richter CM, Meyer JC, Kotakoski J, Skákalová, V, Advanced materials , 2106922 (2021). http://doi.org/10.1002/adma.202106922
Abstract: Heterostructures composed of two-dimensional (2D) materials are already opening many new possibilities in such fields of technology as electronics and magnonics, but far more could be achieved if the number and diversity of 2D materials is increased. So far, only a few dozen 2D crystals have been extracted from materials that exhibit a layered phase in ambient conditions, omitting entirely the large number of layered materials that may exist in other temperatures and pressures. Here, we demonstrate how these structures can be stabilized in 2D van der Waals stacks under room temperature via growing them directly in graphene encapsulation by using graphene oxide as the template material. Specifically, we produce an ambient stable 2D structure of copper and iodine, a material that normally only occurs in layered form at elevated temperatures between 645 and 675 K. Our results establish a simple route to the production of more exotic phases of materials that would otherwise be difficult or impossible to stabilize for experiments in ambient.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 19.791
DOI: 10.1002/adma.202106922
|
|
|
“Monitoring oxygen production on mass-selected iridium–tantalum oxide electrocatalysts”. Zheng Y-R, Vernieres J, Wang Z, Zhang K, Hochfilzer D, Krempl K, Liao T-W, Presel F, Altantzis T, Fatermans J, Scott SB, Secher NM, Moon C, Liu P, Bals S, Van Aert S, Cao A, Anand M, Nørskov JK, Kibsgaard J, Chorkendorff I, Nature Energy (2021). http://doi.org/10.1038/s41560-021-00948-w
Abstract: Development of low-cost and high-performance oxygen evolution reaction catalysts is key to implementing polymer electrolyte membrane water electrolyzers for hydrogen production. Iridium-based oxides are the state-of-the-art acidic oxygen evolution reactio catalysts but still suffer from inadequate activity and stability, and iridium's scarcity motivates the discovery of catalysts with lower iridium loadings. Here we report a mass-selected iridium-tantalum oxide catalyst prepared by a magnetron-based cluster source with considerably reduced noble-metal loadings beyond a commercial IrO2 catalyst. A sensitive electrochemistry/mass-spectrometry instrument coupled with isotope labelling was employed to investigate the oxygen production rate under dynamic operating conditions to account for the occurrence of side reactions and quantify the number of surface active sites. Iridium-tantalum oxide nanoparticles smaller than 2 nm exhibit a mass activity of 1.2 ± 0.5 kA “g” _“Ir” ^“-1” and a turnover frequency of 2.3 ± 0.9 s-1 at 320 mV overpotential, which are two and four times higher than those of mass-selected IrO2, respectively. Density functional theory calculations reveal that special iridium coordinations and the lowered aqueous decomposition free energy might be responsible for the enhanced performance.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Applied Electrochemistry & Catalysis (ELCAT)
Times cited: 95
DOI: 10.1038/s41560-021-00948-w
|
|
|
“Asymmetric Interfacial Intermixing Associated Magnetic Coupling in LaMnO3/LaFeO3 Heterostructures”. Chen B, Gauquelin N, Green RJ, Verbeeck J, Rijnders G, Koster G, Frontiers in physics 9 (2021). http://doi.org/10.3389/fphy.2021.698154
Abstract: The structural and magnetic properties of LaMnO<sub>3</sub>/LaFeO<sub>3</sub>(LMO/LFO) heterostructures are characterized using a combination of scanning transmission electron microscopy, electron energy-loss spectroscopy, bulk magnetometry, and resonant x-ray reflectivity. Unlike the relatively abrupt interface when LMO is deposited on top of LFO, the interface with reversed growth order shows significant cation intermixing of Mn<sup>3+</sup>and Fe<sup>3+</sup>, spreading ∼8 unit cells across the interface. The asymmetric interfacial chemical profiles result in distinct magnetic properties. The bilayer with abrupt interface shows a single magnetic hysteresis loop with strongly enhanced coercivity, as compared to the LMO plain film. However, the bilayer with intermixed interface shows a step-like hysteresis loop, associated with the separate switching of the “clean” and intermixed LMO sublayers. Our study illustrates the key role of interfacial chemical profile in determining the functional properties of oxide heterostructures.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 1
DOI: 10.3389/fphy.2021.698154
|
|
|
“3D arrangement of epitaxial graphene conformally grown on porousified crystalline SiC”. Veronesi S, Pfusterschmied G, Fabbri F, Leitgeb M, Arif O, Esteban DA, Bals S, Schmid U, Heun S, Carbon 189, 210 (2022). http://doi.org/10.1016/j.carbon.2021.12.042
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 10.9
Times cited: 3
DOI: 10.1016/j.carbon.2021.12.042
|
|
|
“Interfacial gliding-driven lattice oxygen release in layered cathodes”. Sun C, Liao X, Peng H, Zhang C, Van Tendeloo G, Zhao Y, Wu J, Cell reports physical science 3 (2022). http://doi.org/10.1016/J.XCRP.2021.100695
Abstract: The oxygen release of layered cathodes causes many battery failures, but the underlying mechanism in an actual working cathode is still elusive as it involves secondary agglomerates that introduce complicated boundary structures. Here, we report a general structure instability on the mismatch boundaries driven by interfacial gliding-it introduces a shear stress causing a distortion of the metal-oxygen octahedra framework that reduces its kinetic stability. The migration of cations and diffusion of oxygen vacancies continue to degrade the whole particle from the boundary to the interior, followed by the formation of nano-sized cracks on the fast-degrading interfaces. This work reveals a robust chemical and mechanical interplay on the oxygen release inherent to the intergranular boundaries of layered cathodes. It also suggests that radially patterned columnar grains with low-angle planar boundaries would be an efficient approach to mitigate the boundary oxygen release.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
DOI: 10.1016/J.XCRP.2021.100695
|
|
|
“ZnAl layered double hydroxide based catalysts (with Cu, Mn, Ti) used as noble metal-free three-way catalysts”. Van Everbroeck T, Wu J, Arenas-Esteban D, Ciocarlan R-G, Mertens M, Bals S, Dujardin C, Granger P, Seftel EM, Cool P, Applied clay science 217, 106390 (2022). http://doi.org/10.1016/j.clay.2021.106390
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 5.6
Times cited: 6
DOI: 10.1016/j.clay.2021.106390
|
|
|
“The crystal and defect structures of polar KBiNb2O7”. Mallick S, Zhang W, Batuk M, Gibbs AS, Hadermann J, Halasyamani PS, Hayward MA, Journal of the Chemical Society : Dalton transactions 51, 1866 (2022). http://doi.org/10.1039/D1DT04064B
Abstract: KBiNb2O7 was prepared from RbBiNb2O7 by a sequence of cation exchange reactions which first convert RbBiNb2O7 to LiBiNb2O7, before KBiNb2O7 is formed by a further K-for-Li cation exchange. A combination of neutron, synchrotron X-ray and electron diffraction data reveal that KBiNb2O7 adopts a polar, layered, perovskite structure (space group A11m) in which the BiNb2O7 layers are stacked in a (0, ½, z) arrangement, with the K+ cations located in half of the available 10-coordinate interlayer cation sites. The inversion symmetry of the phase is broken by a large displacement of the Bi3+ cations parallel to the y-axis. HAADF-STEM images reveal that KBiNb2O7 exhibits frequent stacking faults which convert the (0. ½, z) layer stacking to (½, 0, z) stacking and vice versa, essentially switching the x- and y-axes of the material. By fitting the complex diffraction peak shape of the SXRD data collected from KBiNb2O7 it is estimated that each layer has approximately an ~11% chance of being defective – a high level which is attributed to the lack of cooperative NbO6 tilting in the material, which limits the lattice strain associated with each fault.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4
DOI: 10.1039/D1DT04064B
|
|
|
“Direct Solar Energy-Mediated Synthesis of Tertiary Benzylic Alcohols Using a Metal-Free Heterogeneous Photocatalyst”. Zhang Y, Qin S, Claes N, Schilling W, Sahoo PK, Ching HYV, Jaworski A, Lemière F, Slabon A, Van Doorslaer S, Bals S, Das S, ACS Sustainable Chemistry and Engineering 10, 530 (2022). http://doi.org/10.1021/acssuschemeng.1c07026
Abstract: Direct hydroxylation via the functionalization of tertiary benzylic C(sp3)-H bond is of great significance for obtaining tertiary alcohols which find wide applications in pharmaceuticals as well as in fine chemical industries. However, current synthetic procedures use toxic reagents and therefore, the development of a sustainable strategy for the synthesis of tertiary benzyl alcohols is highly desirable. To solve this problem, herein, we report a metal-free
heterogeneous photocatalyst to synthesize the hydroxylated products using oxygen as the key reagent. Various benzylic substrates were employed into our mild reaction conditions to afford the desirable products in good to excellent yields. More importantly, gram-scale reaction was achieved via harvesting direct solar energy and exhibited high quantity of the product. The high stability of the catalyst was proved via recycling the catalyst and spectroscopic analyses. Finally, a possible mechanism was proposed based on the EPR and other experimental
evidence.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Organic synthesis (ORSY)
Impact Factor: 8.4
Times cited: 24
DOI: 10.1021/acssuschemeng.1c07026
|
|
|
“Signatures of enhanced out-of-plane polarization in asymmetric BaTiO3 superlattices integrated on silicon”. Chen B, Gauquelin N, Strkalj N, Huang S, Halisdemir U, Nguyen MD, Jannis D, Sarott MF, Eltes F, Abel S, Spreitzer M, Fiebig M, Trassin M, Fompeyrine J, Verbeeck J, Huijben M, Rijnders G, Koster G, Nature communications 13, 265 (2022). http://doi.org/10.1038/s41467-021-27898-x
Abstract: In order to bring the diverse functionalities of transition metal oxides into modern electronics, it is imperative to integrate oxide films with controllable properties onto the silicon platform. Here, we present asymmetric LaMnO<sub>3</sub>/BaTiO<sub>3</sub>/SrTiO<sub>3</sub>superlattices fabricated on silicon with layer thickness control at the unit-cell level. By harnessing the coherent strain between the constituent layers, we overcome the biaxial thermal tension from silicon and stabilize<italic>c</italic>-axis oriented BaTiO<sub>3</sub>layers with substantially enhanced tetragonality, as revealed by atomically resolved scanning transmission electron microscopy. Optical second harmonic generation measurements signify a predominant out-of-plane polarized state with strongly enhanced net polarization in the tricolor superlattices, as compared to the BaTiO<sub>3</sub>single film and conventional BaTiO<sub>3</sub>/SrTiO<sub>3</sub>superlattice grown on silicon. Meanwhile, this coherent strain in turn suppresses the magnetism of LaMnO<sub>3</sub>as the thickness of BaTiO<sub>3</sub>increases. Our study raises the prospect of designing artificial oxide superlattices on silicon with tailored functionalities.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 16.6
Times cited: 11
DOI: 10.1038/s41467-021-27898-x
|
|
|
“On amorphization as a deformation mechanism under high stresses”. Idrissi H, Carrez P, Cordier P, Current opinion in solid state and materials science 26, 100976 (2022). http://doi.org/10.1016/J.COSSMS.2021.100976
Abstract: In this paper we review the work related to amorphization under mechanical stress. Beyond pressure, we highlight the role of deviatoric or shear stresses. We show that the most recent works make amorphization appear as a deformation mechanism in its own right, in particular under extreme conditions (shocks, deformations under high stresses, high strain-rates).
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 11
DOI: 10.1016/J.COSSMS.2021.100976
|
|
|
“Polytypism in mcalpineite : a study of natural and synthetic Cu₃TeO₆”. Missen OP, Mills SJ, Canossa S, Hadermann J, Nenert G, Weil M, Libowitzky E, Housley RM, Artner W, Kampf AR, Rumsey MS, Spratt J, Momma K, Dunstan MA, Acta Crystallographica. Section B: Structural Science, Crystal Engineering and Materials (Online) 78 (2022). http://doi.org/10.1107/S2052520621013032
Abstract: Synthetic and naturally occurring forms of tricopper orthotellurate, (Cu3TeO6)-Te-II-O-IV (the mineral mcalpineite) have been investigated by 3D electron diffraction (3D ED), X-ray powder diffraction (XRPD), Raman and infrared (IR) spectroscopic measurements. As a result of the diffraction analyses, (Cu3TeO6)-Te-II-O-IV is shown to occur in two polytypes. The higher-symmetric (Cu3TeO6)-Te-II-O-IV-1C polytype is cubic, space group 1a (3) over bar, with a = 9.537 (1) angstrom and V = 867.4 (3) angstrom(3) as reported in previous studies. The 1C polytype is a well characterized structure consisting of alternating layers of (CuO6)-O-II octahedra and both (CuO6)-O-II and (TeO6)-O-VI octahedra in a patchwork arrangement. The structure of the lower-symmetric orthorhombic (Cu3TeO6)-Te-II-O-IV-2O polytype was determined for the first time in this study by 3D ED and verified by Rietveld refinement. The 2O polytype crystallizes in space group Pcca, with a = 9.745 (3) angstrom, b = 9.749 (2) angstrom, c = 9.771 (2) angstrom and V = 928.3 (4) angstrom(3) . High-precision XRPD data were also collected on (Cu3TeO6)-Te-II-O-IV-2O to verify the lower-symmetric structure by performing a Rietveld refinement. The resultant structure is identical to that determined by 3D ED, with unit-cell parameters a = 9.56157 (19) angstrom, b = 9.55853 (11) angstrom, c = 9.62891 (15) angstrom and V = 880.03 (2) angstrom(3) . The lower symmetry of the 2O polytype is a consequence of a different cation ordering arrangement, which involves the movement of every second (CuO6)-O-II and (TeO6)-O-VI octahedral layer by (1/4, 1/4, 0), leading to an offset of (TeO6)-O-VI and (CuO6)-O-II octahedra in every second layer giving an ABAB* stacking arrangement. Syntheses of (Cu3TeO6)-Te-II-O-IV showed that low-temperature (473 K) hydrothermal conditions generally produce the 2O polytype. XRPD measurements in combination with Raman spectroscopic analysis showed that most natural mcalpineite is the orthorhombic 2O polytype. Both XRPD and Raman spectroscopy measurements may be used to differentiate between the two polytypes of (Cu3TeO6)-Te-II-O-IV. In Raman spectroscopy, (Cu3TeO6)-Te-II-O-IV-1C has a single strong band around 730 cm(-1), whereas (Cu3TeO6)-Te-II-O-IV-2O shows a broad double maximum with bands centred around 692 and 742 cm(-1).
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.9
DOI: 10.1107/S2052520621013032
|
|
|
“Two-Dimensional CdSe-PbSe Heterostructures and PbSe Nanoplatelets: Formation, Atomic Structure, and Optical Properties”. Salzmann BBV, Wit J de, Li C, Arenas-Esteban D, Bals S, Meijerink A, Vanmaekelbergh D, The journal of physical chemistry: C : nanomaterials and interfaces 126, 1513 (2022). http://doi.org/10.1021/acs.jpcc.1c09412
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.7
Times cited: 12
DOI: 10.1021/acs.jpcc.1c09412
|
|
|
“Ferroelectric engineering : enhanced thermoelectric performance by local structural heterogeneity”. Meng X, Chen S, Peng H, Bai H, Zhang S, Su X, Tan G, Van Tendeloo G, Sun Z, Zhang Q, Tang X, Wu J, Science China : materials (2022). http://doi.org/10.1007/S40843-021-1927-9
Abstract: Although traditional ferroelectric materials are usually dielectric and nonconductive, GeTe is a typical ferroelectric semiconductor, possessing both ferroelectric and semiconducting properties. GeTe is also a widely studied thermoelectric material, whose performance has been optimized by doping with various elements. However, the impact of the ferroelectric domains on the thermoelectric properties remains unclear due to the difficulty to directly observe the ferroelectric domains and their evolutions under actual working conditions where the material is exposed to high temperatures and electric currents. Herein, based on in-situ investigations of the ferroelectric domains and domain walls in both pure and Sb-doped GeTe crystals, we have been able to analyze the dynamic evolution of the ferroelectric domains and domain walls, exposed to an electric field and temperature. Local structural heterogeneities and nano-sized ferroelectric domains are generated due to the interplay of the Sb3+ dopant and the Ge-vacancies, leading to the increased number of charged domain walls and a much improved thermoelectric performance. This work reveals the fundamental mechanism of ferroelectric thermoelectrics and provides insights into the decoupling of previously interdependent properties such as thermo-power and electrical conductivity.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 8.1
DOI: 10.1007/S40843-021-1927-9
|
|
|
“In situ atomistic insight into magnetic metal diffusion across Bi0.5Sb1.5Te3 quintuple layers”. Lu W, Cui W, Zhao W, Lin W, Liu C, Van Tendeloo G, Sang X, Zhao W, Zhang Q, Advanced Materials Interfaces , 2102161 (2022). http://doi.org/10.1002/ADMI.202102161
Abstract: Diffusion and occupancy of magnetic atoms in van der Waals (VDW) layered materials have significant impact on applications such as energy storage, thermoelectrics, catalysis, and topological phenomena. However, due to the weak VDW bonding, most research focus on in-plane diffusion within the VDW gap, while out-of-plane diffusion has rarely been reported. Here, to investigate out-of-plane diffusion in VDW-layered Bi2Te3-based alloys, a Ni/Bi0.5Sb1.5Te3 heterointerface is synthesized by depositing magnetic Ni metal on a mechanically exfoliated Bi0.5Sb1.5Te3 (0001) substrate. Diffusion of Ni atoms across the Bi0.5Sb1.5Te3 quintuple layers is directly observed at elevated temperatures using spherical-aberration-corrected scanning transmission electron microscopy (STEM). Density functional theory calculations demonstrate that the diffusion energy barrier of Ni atoms is only 0.31-0.45 eV when they diffuse through Te-3(Bi, Sb)(3) octahedron chains. Atomic-resolution in situ STEM reveals that the distortion of the Te-3(Bi, Sb)(3) octahedron, induced by the Ni occupancy, drives the formation of coherent NiM (M = Bi, Sb, Te) at the heterointerfaces. This work can lead to new strategies to design novel thermoelectric and topological materials by introducing magnetic dopants to VDW-layered materials.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.4
DOI: 10.1002/ADMI.202102161
|
|
|
“Induced giant piezoelectricity in centrosymmetric oxides”. Park D-s, Hadad M, Riemer LM, Ignatans R, Spirito D, Esposito V, Tileli V, Gauquelin N, Chezganov D, Jannis D, Verbeeck J, Gorfman S, Pryds N, Muralt P, Damjanovic D, Science 375, 653 (2022). http://doi.org/10.1126/science.abm7497
Abstract: Giant piezoelectricity can be induced in centrosymmetric oxides by controlling the long-range motion of oxygen vacancies.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 56.9
Times cited: 51
DOI: 10.1126/science.abm7497
|
|
|
“Sustainable formation of tricarballylic acid from citric acid over highly stable Pd/Nb2O5.nH2O catalysts”. Stuyck W, Bugaev AL, Nelis T, de Oliveira-Silva R, Smolders S, Usoltsev OA, Arenas Esteban D, Bals S, Sakellariou D, De Vos D, Journal of catalysis (2022). http://doi.org/10.1016/j.jcat.2022.02.013
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 7.3
Times cited: 5
DOI: 10.1016/j.jcat.2022.02.013
|
|
|
“From 2D to 3D : bridging self-assembled monolayers to a substrate-induced polymorph in a molecular semiconductor”. Hao Y, Velpula G, Kaltenegger M, Bodlos WR, Vibert F, Mali KS, De Feyter S, Resel R, Geerts YH, Van Aert S, Beljonne D, Lazzaroni R, Chemistry of materials 34, 2238 (2022). http://doi.org/10.1021/ACS.CHEMMATER.1C04038
Abstract: In this study, a new bottom-up approach is proposed to predict the crystal structure of the substrate-induced polymorph (SIP) of an archetypal molecular semiconductor. In spite of intense efforts, the formation mechanism of SIPs is still not fully understood, and predicting their crystal structure is a very delicate task. Here, we selected lead phthalocyanine (PbPc) as a prototypical molecular material because it is a highly symmetrical yet nonplanar molecule and we demonstrate that the growth and crystal structure of the PbPc SIPs can be templated by the corresponding physisorbed self-assembled molecular networks (SAMNs). Starting from SAMNs of PbPc formed at the solution/graphite interface, the structural and energetic aspects of the assembly were studied by a combination of in situ scanning tunneling microscopy and multiscale computational chemistry approach. Then, the growth of a PbPc SIP on top of the physisorbed monolayer was modeled without prior experimental knowledge, from which the crystal structure of the SIP was predicted. The theoretical prediction of the SIP was verified by determining the crystal structure of PbPc thin films using X-ray diffraction techniques, revealing the formation of a new polymorph of PbPc on the graphite substrate. This study clearly illustrates the correlation between the SAMNs and SIPs, which are traditionally considered as two separate but conceptually connected research areas. This approach is applicable to molecular materials in general to predict the crystal structure of their SIPs.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 8.6
DOI: 10.1021/ACS.CHEMMATER.1C04038
|
|
|
“Quantification of the Helical Morphology of Chiral Gold Nanorods”. Heyvaert W, Pedrazo-Tardajos A, Kadu A, Claes N, González-Rubio G, Liz-Marzán LM, Albrecht W, Bals S, ACS materials letters 4, 642 (2022). http://doi.org/10.1021/acsmaterialslett.2c00055
Abstract: Chirality in inorganic nanoparticles and nanostructures has gained increasing scientific interest, because of the possibility to tune their ability to interact differently with left- and right-handed circularly polarized light. In some cases, the optical activity is hypothesized to originate from a chiral morphology of the nanomaterial. However, quantifying the degree of chirality in objects with sizes of tens of nanometers is far from straightforward. Electron tomography offers the possibility to faithfully retrieve the three-dimensional morphology of nanomaterials, but only a qualitative interpretation of the morphology of chiral nanoparticles has been possible so far. We introduce herein a methodology that enables us to quantify the helicity of complex chiral nanomaterials, based on the geometrical properties of a helix. We demonstrate that an analysis at the single particle level can provide significant insights into the origin of chiroptical properties.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 11
DOI: 10.1021/acsmaterialslett.2c00055
|
|