Abstract: Multiwall carbon nanotubes are produced by decomposition of acetylene at 600 degreesC on metal catalysts supported on NaY zeolite. The support and the metal are eliminated by dissolving them in aqueous hydrofluoric acid (HF). Two methods were used to eliminate the pyrolitic carbon: oxidation in air at 500 degreesC and oxidation by potassium permanganate in acidic solution at 70 degreesC. The progress and efficacy of the purification methods are verified by TEM. The properties of the purified multiwalled carbon nanotubes are probed using C-13 and Xe-129 NMR spectroscopy under continuous-flow optical-pumping conditions. Xenon is shown to penetrate the interior of the nanotubes. A distribution of inner tube diameters gives rise to chemical shift dispersion. When the temperature is lowered, an increasing fraction of xenon resides inside the nanotubes and is not capable of exchanging with xenon in the interparticle space. In the case of the permanganate-oxidized sample, rapid xenon relaxation is attributed to interaction with residual MnO2 nanoparticles in the interior of the tubes.

Abstract: The microstructure of a Fe-Mn-Si-Al twinning-induced plasticity (TWIP) steel exhibiting remarkable work hardening rate under uniaxial tensile deformation was investigated using transmission electron microscopy to uncover the mechanism(s) controlling the nucleation and growth of the mechanically induced twins. The results show that the stair-rod cross-slip deviation mechanism is necessary for the formation of the twins, while large extrinsic stacking faults homogenously distributed within the grains could act as preferential sources for the activation of the deviation process. The influence of such features on the thickness and strength of the twins and the resulting mechanical behaviour is discussed and compared to similar works recently performed on Fe-Mn-C TWIP steels.

Abstract: In the last few decades, nanostructuring has driven significant attention towards the development of novel metallic materials with advanced mechanical properties. Nanocrystalline (nc) metals are a class of nanostructured materials with grain sizes smaller than about 100 nm. These exhibit outstanding mechanical strength and fatigue properties compared to their coarse-grained (cg) counterparts. These are promising candidates for application as structural or functional materials. Nc metals in the form of thin films are employed as hard coatings on bulk components, structural components, and conductive layers in various micro-/nanoscale devices. These structural components and devices are often subjected to cyclic stresses or fatigue loading. Under these cyclic stresses, nc metals tend to exhibit the Bauschinger effect (BE). The strength loss during the BE is of great importance concerning the strength-ductility trade-off in nc metals. Furthermore, contact surfaces of the engineering components in service often undergo relative motion and are subject to both friction and wear. These extreme loading conditions demand nc metals with tailored interfacial characteristics for improved tribological performance. Aiming at ensuring high reliability and mechanical robustness for optimum performance of these components, there has been a strong motivation for understanding the mechanical properties and governing deformation mechanisms in nc metallic materials. This thesis aimed at in-depth investigation of microstructures at micro-/nanoscales using state-of-the-art in situ and ex situ transmission electron microscopy (TEM) to develop a closer link between the deformation structure and underlying deformation mechanisms in some nc metallic materials. The thesis has primarily focused on the in situ TEM nanomechanics of the BE and rotational deformation of grains in nc palladium thin films. A sputtered thin film of nc Pd was deformed inside TEM by cyclic loading-unloading experiments and the evolving microstructure was studied in real-time under different TEM imaging modes. The stress-strain response of the film exhibited a characteristic non-linear unloading behavior confirming the BE in the film. The corresponding bright-field TEM imaging revealed evidence of partially reversible dislocation activity. Towards a quantitative understanding of the deformation structure in real-time, in situ nanomechanical testing was coupled with precession-assisted automated crystal orientation mapping in scanning TEM (ACOM-STEM). Global ACOM-STEM analysis offered crystal orientation of a large number of grains at different states of deformation and confirmed partially reversible rotations of nanosized grains fitting to the observed BE during loading and unloading. Analysis of intragranular rotations showed substantial changes in the sub-structure within most of these grains indicating a dominant role of dislocation-based processes in driving these rotations. Globally, an unusually random evolution of texture was seen that demonstrated the influence of deformation heterogeneity and grain interactions on the resulting texture characteristics in nc metals. In the quest of understanding the grain interactions, local investigations based on annular dark-field STEM imaging during loading-unloading showed reversible changes in the contrast of grains with sets of adjoining grains exhibiting a unique cooperative rotation. Local analysis of the density of geometrically necessary dislocations (GNDs) showed the formation of dislocation pile-up at grain boundaries due to the generation of back-stresses during unloading. Critical observations of the evolution of GND density offered greater insights into the mechanism of cooperative grain rotations and these rotations were related to grain structure and grain boundary characteristics. In addition to understanding the influence of grain structure and grain boundaries, the thesis has further investigated the role of heterointerfaces in sputtered Au-Cu and Cu-Cr nanocrystalline multilayered composites (NMCs) deformed under cyclic sliding contact. The microstructural evolution in the NMCs was investigated at different deformation states by classical TEM imaging, ACOM-STEM as well as energy-filtered TEM (EFTEM). Au-Cu NMC with an initial high density of twin boundaries deformed by stress-driven detwinning with a concurrent change in grain structure in both Au and Cu. The formation of a vortex structure was observed due to plastic flow instabilities at Au-Cu interfaces that led to codeformation and mechanical intermixing. Cu-Cr NMC showed a preferential grain growth in Cu layers whereas no noticeable change in the grain sizes was seen in Cr layers. The phase maps revealed sharp interfaces between Cu and Cr layers indicating no intermixing between the immiscible phases. EFTEM results exposed the cracking processes in Cr layers with a concurrent migration of Cu in the cracks. Overall, the thesis has attempted to analyze the competing deformation processes and relate these with the microstructural heterogeneity in terms of grain structure and GB and interfacial characteristics in nc metallic materials.

Abstract: Using pulsed laser deposition ultra-thin DyBa2Cu3O7-x films were deposited on a single terminated (0 0 1) SrTiOr(3) substrate. The initial growth was studied by high-resolution electron microscopy. Two different types of interface arrangements occur and were determined as: bulk-SrO-TiO2-BaO-CuO-BaO-CuO2-Dy-CuO2-BaO bulk and bulk-SrO-TiO2-BaO-CuO2-Dy-CuO2-BaO-CuO-BaO-bulk This variable growth sequence causes structural shifts, resulting in antiphase boundaries with displacement vector R = [0 0 1/3]. as well as local chemical variations. (C) 2001 Elsevier Science B.V. All rights reserved.

Abstract: Recent developments in the field of TEM characterisation of Si device materials are discussed and illustrated by a few case studies of material in different stages of various kinds of processing. Important challenges are the ever decreasing defect densities and device feature sizes. Defect delineation techniques using large area inspection tools yielding accurate coordinates of the defects to be studied have therefore become an essential part of the TEM analysis procedure. The possibility to transfer these defect coordinates without loss of accuracy to tools for local TEM specimen preparation is also a conditio sine qua non for a successful analysis. Insitu TEM remains important as dynamic processes can be observed and analysed under well defined experimental conditions. As case studies illustrating new developments, results are presented on defects in as-grown Ct silicon, on in-situ studies in processed silicon, on problem sites in advanced integrated circuit structures and on assessment of localised strain fields in the nm size scale.

Abstract: Laser induced phase transition from b.c.c.(alpha) to f.c.c.(gamma) iron thin films is studied by high resolution TEM. The iron film has been covered on both sides with carbon layers to protect it against oxidation. Single pulse, tau FWHM = 20ns KrF (lambda = 248nm) excimer laser irradiation was performed in air with the film on the substrate. The laser pulse acts like a heat pulse followed by a rapid quenching revealing sequential aspects of the phase transition process. The presence of a fine mixture of the alpha + gamma phases between the alpha and gamma regions of the film has been interpreted as an incomplet transformation. The results are explained by assuming that the transformation took place via a phonon drag mechanism.

Abstract: The surface of commercial Nitinol wires with original oxides and a thickness in the 30-190 nm range was investigated by different state of art TEM techniques. The oxide surface layer was identified as a combination of TiO and TiO2 depending on the processing of the wire. Between the core of the wires and the oxidized surface, an interfacial Ni3Ti nanolayer was observed while Ni nanoparticles are found inside the original oxide. The particle sizes, their distribution in the surface and the Ti-O stoichiometry were deduced from the analysis of the obtained data. Molecular dynamics calculations performed for evaluation of the stability of Ni particles relative to the atomic state revealed that a pure Ni particle has a lower energy than free Ni atoms inside the TiO2 lattice. The obtained results are discussed with respect to surface stability and Ni release in the human body.

Abstract: Noble metal nanoparticles are widely used as probes or substrates for surface-enhanced Raman scattering (SERS), due to their characteristic plasmon resonances in the visible and NIR spectral ranges. Aiming at obtaining a versatile system with high SERS performance we developed the synthesis of quasi-monodisperse, non-aggregated gold nanoparticles protected by radial mesoporous silica shells. The radial channels of such shells were used as templates for the growth of gold tips branching from the cores, thereby improving the plasmonic performance of the particles while favoring the localization of analyte molecules at high electric field regions: close to the tips, inside the pores. The method, which allows control over tip length, was successfully applied to various gold nanoparticle shapes, leading to materials with highly efficient SERS performance. The obtained nanoparticles are stable in ethanol and water upon thermal consolidation and can be safely stored as a powder.