“Inhomogeneous superconductivity and quasilinear magnetoresistance at amorphous LaTiO₃/SrTiO₃, interfaces”. Lebedev N, Stehno M, Rana A, Gauquelin N, Verbeeck J, Brinkman A, Aarts J, Journal Of Physics-Condensed Matter 33, 055001 (2020). http://doi.org/10.1088/1361-648X/ABC102
Abstract: We have studied the transport properties of LaTiO3/SrTiO3 (LTO/STO) heterostructures. In spite of 2D growth observed in reflection high energy electron diffraction, transmission electron microscopy images revealed that the samples tend to amorphize. Still, we observe that the structures are conducting, and some of them exhibit high conductance and/or superconductivity. We established that conductivity arises mainly on the STO side of the interface, and shows all the signs of the two-dimensional electron gas usually observed at interfaces between STO and LTO or LaAlO3, including the presence of two electron bands and tunability with a gate voltage. Analysis of magnetoresistance (MR) and superconductivity indicates the presence of spatial fluctuations of the electronic properties in our samples. That can explain the observed quasilinear out-of-plane MR, as well as various features of the in-plane MR and the observed superconductivity.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.7
Times cited: 1
DOI: 10.1088/1361-648X/ABC102
|
|
|
“Coupled anion and cation ordering in Sr3RFe4O10.5 (R=Y, Ho, Dy) anion-deficientperovskites”. Abakumov AM, d' Hondt H, Rossell MD, Tsirlin AA, Gutnikova O, Filimonov DS, Schnelle W, Rosner H, Hadermann J, Van Tendeloo G, Antipov EV, Journal of solid state chemistry 183, 2845 (2010). http://doi.org/10.1016/j.jssc.2010.09.039
Abstract: The Sr3RFe4O10.5 (R=Y, Ho, Dy) anion-deficient perovskites were prepared using a solid-state reaction in evacuated sealed silica tubes. Transmission electron microscopy and 57Fe Mössbauer spectroscopy evidenced a complete A-cations and oxygen vacancies ordering. The structure model was further refined by ab initio structure relaxation, based on density functional theory calculations. The compounds crystallize in a tetragonal a≈2√2ap≈11.3 Å, с≈4сp≈16 Å unit cell (ap: parameter of the perovskite subcell) with the P42/mnm space group. Oxygen vacancies reside in the (FeO5/4□3/4) layers, comprising corner-sharing FeO4 tetrahedra and FeO5 tetragonal pyramids, which are sandwiched between the layers of the FeO6 octahedra. Smaller R atoms occupy the 9-fold coordinated position, whereas the 10-fold coordinated positions are occupied by larger Sr atoms. The Fe sublattice is ordered aniferromagnetically up to at least 500 K, while the rare-earth sublattice remains disordered down to 2 K.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 8
DOI: 10.1016/j.jssc.2010.09.039
|
|
|
“Crystal structure and properties of the new vanadyl(IV)phosphates Na2MVO(PO4)2 M=Ca and Sr”. Chernaya VV, Tsirlin AA, Shpanchenko RV, Antipov EV, Gippius AA, Morozova EN, Dyakov V, Hadermann J, Kaul EE, Geibel C, Journal of solid state chemistry 177, 2875 (2004). http://doi.org/10.1016/j.jssc.2004.04.035
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 6
DOI: 10.1016/j.jssc.2004.04.035
|
|
|
“New germanates RCrGeO5 (R=NdEr, Y): synthesis, structure, and properties”. Shpanchenko RV, Tsirlin AA, Kondakova ES, Antipov EV, Bougerol C, Hadermann J, Van Tendeloo G, Sakurai H, Takayama-Muromachi E, Journal of solid state chemistry 181, 2433 (2008). http://doi.org/10.1016/j.jssc.2008.05.043
Abstract: The new complex germanates RCrGeO5 (R=NdEr, Y) have been synthesized and investigated by means of X-ray powder diffraction, electron microscopy, magnetic susceptibility and specific heat measurements. All the compounds are isostructural and crystallize in the orthorhombic symmetry, space group Pbam, and Z=4. The crystal structure of RCrGeO5, as refined using X-ray powder diffraction data, includes infinite chains built by edge-sharing Cr+3O6 octahedra with two alternating Cr−Cr distances. The chains are combined into a three-dimensional framework by Ge2O8 groups consisting of two edge-linked square pyramids oriented in opposite directions. The resulting framework contains pentagonal channels where rare-earth elements are located. Thus, RCrGeO5 germanates present new examples of RMn2O5-type compounds and show ordering of Cr+3 and Ge+4 cations. Electron diffraction as well as high-resolution electron microscopy confirm the structure solution. Magnetic susceptibility data for R=Nd, Sm, and Eu are qualitatively consistent with the presence of isolated 3d (antiferromagnetically coupled Cr+3 cations) and 4f (R+3) spin subsystems in the RCrGeO5 compounds. NdCrGeO5 undergoes long-range magnetic ordering at 2.6 K, while SmCrGeO5 and EuCrGeO5 do not show any phase transitions down to 2 K.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 6
DOI: 10.1016/j.jssc.2008.05.043
|
|
|
“Original close-packed structure and magnetic properties of the Pb4Mn9O20 manganite”. Abakumov AM, Hadermann J, Tsirlin AA, Tan H, Verbeeck J, Zhang H, Dikarev EV, Shpanchenko RV, Antipov EV, Journal of solid state chemistry 182, 2231 (2009). http://doi.org/10.1016/j.jssc.2009.06.003
Abstract: The crystal structure of the Pb4Mn9O20 compound (previously known as Pb0.43MnO2.18) was solved from powder X-ray diffraction, electron diffraction, and high resolution electron microscopy data (S.G. Pnma, a=13.8888(2) Å, b=11.2665(2) Å, c=9.9867(1) Å, RI=0.016, RP=0.047). The structure is based on a 6H (cch)2 close packing of pure oxygen h-type (O16) layers alternating with mixed c-type (Pb4O12) layers. The Mn atoms occupy octahedral interstices formed by the oxygen atoms of the close-packed layers. The MnO6 octahedra share edges within the layers, whereas the octahedra in neighboring layers are linked through corner sharing. The relationship with the closely related Pb3Mn7O15 structure is discussed. Magnetization measurements reveal a peculiar magnetic behavior with a phase transition at 52 K, a small net magnetization below the transition temperature, and a tendency towards spin freezing.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 5
DOI: 10.1016/j.jssc.2009.06.003
|
|
|
“Oxygen exchange on nanocrystalline tin dioxide modified by palladium”. Frolov DD, Kotovshchikov YN, Morozov IV, Boltalin AI, Fedorova AA, Marikutsa AV, Rumyantseva MN, Gaskov AM, Sadovskaya EM, Abakumov AM, Journal of solid state chemistry 186, 1 (2012). http://doi.org/10.1016/j.jssc.2011.11.028
Abstract: Temperature-programmed oxygen isotopic exchange study was performed on nanocrystalline tin dioxide-based materials synthesized via sol-gel route and modified by palladium. Such materials are widely used as resistive gas sensors. The experiments were carried out in a flow-reactor up to complete isotopic substitution of oxygen. Substantial rates of isotopic exchange for SnO2 were observed from about 700 K. The distribution of isotopic molecules O-16(2). (OO)-O-16-O-18 and O-18(2) corresponds to simple dioxygen heteroexchange mechanism with single lattice oxygen atom. The modification of SnO2 by Pd introduced multiple heteroexchange mechanism with preliminary O-2 dissociation on the clusters surface. Spill-over of atomic oxygen from Pd to the surface of SnO2 and fast exchange with lattice oxygen result in more than 100% increase of apparent heteroexchange rate. The exchange on SnO2/Pd was shown to be a complex process involving partial deactivation of the catalytic centers at temperature higher than 750 K. (C) 2011 Elsevier Inc. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 34
DOI: 10.1016/j.jssc.2011.11.028
|
|
|
“Synthesis and characterization of new phases: Sr3.75K1.75Bi3O12 and Sr3.1Na2.9Bi3O12”. Pshirkov JS, Kazakov SM, Abakumov AM, Putilin SN, Antipov EV, Bougerol-Chaillout C, Lebedev OI, Van Tendeloo G, Journal of solid state chemistry 152, 492 (2000). http://doi.org/10.1006/jssc.2000.8718
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 2
DOI: 10.1006/jssc.2000.8718
|
|
|
“Synthesis, crystal structure and magnetic properties of the Sr2Al0.78Mn1.22O5.2 anion-deficient layered perovskite”. d' Hondt H, Hadermann J, Abakumov AM, Kalyuzhnaya AS, Rozova MG, Tsirlin AA, Tan H, Verbeeck J, Antipov EV, Van Tendeloo G, Journal of solid state chemistry 182, 356 (2009). http://doi.org/10.1016/j.jssc.2008.11.002
Abstract: A new layered perovskite Sr2Al0.78Mn1.22O5.2 has been synthesized by solid state reaction in a sealed evacuated silica tube. The crystal structure has been determined using electron diffraction, high-resolution electron microscopy, and high-angle annular dark field imaging and refined from X-ray powder diffraction data (space group P4/mmm, a=3.89023(5) Å, c=7.8034(1) Å, RI=0.023, RP=0.015). The structure is characterized by an alternation of MnO2 and (Al0.78Mn0.22)O1.2 layers. Oxygen atoms and vacancies, as well as the Al and Mn atoms in the (Al0.78Mn0.22)O1.2 layers are disordered. The local atomic arrangement in these layers is suggested to consist of short fragments of brownmillerite-type tetrahedral chains of corner-sharing AlO4 tetrahedra interrupted by MnO6 octahedra, at which the chain fragments rotate over 90°. This results in an averaged tetragonal symmetry. This is confirmed by the valence state of Mn measured by EELS. The relationship between the Sr2Al0.78Mn1.22O5.2 tetragonal perovskite and the parent Sr2Al1.07Mn0.93O5 brownmillerite is discussed. Magnetic susceptibility measurements indicate spin glass behavior of Sr2Al0.78Mn1.22O5.2. The lack of long-range magnetic ordering contrasts with Mn-containing brownmillerites and is likely caused by the frustration of interlayer interactions due to presence of the Mn atoms in the (Al0.78Mn0.22)O1.2 layers.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 12
DOI: 10.1016/j.jssc.2008.11.002
|
|
|
“Multiparametric tumor organoid drug screening using widefield live-cell imaging for bulk and single-organoid analysis”. Le Compte M, Cardenas De La Hoz E, Peeters S, Smits E, Lardon F, Roeyen G, Vanlanduit S, Prenen H, Peeters M, Lin A, Deben C, Jove-Journal Of Visualized Experiments , 1 (2022). http://doi.org/10.3791/64434
Abstract: Patient-derived tumor organoids (PDTOs) hold great promise for preclinical and translational research and predicting the patient therapy response from ex vivo drug screenings. However, current adenosine triphosphate (ATP)-based drug screening assays do not capture the complexity of a drug response (cytostatic or cytotoxic) and intratumor heterogeneity that has been shown to be retained in PDTOs due to a bulk readout. Live-cell imaging is a powerful tool to overcome this issue and visualize drug responses more in-depth. However, image analysis software is often not adapted to the three-dimensionality of PDTOs, requires fluorescent viability dyes, or is not compatible with a 384-well microplate format. This paper describes a semi-automated methodology to seed, treat, and image PDTOs in a high-throughput, 384-well format using conventional, widefield, live-cell imaging systems. In addition, we developed viability marker-free image analysis software to quantify growth rate-based drug response metrics that improve reproducibility and correct growth rate variations between different PDTO lines. Using the normalized drug response metric, which scores drug response based on the growth rate normalized to a positive and negative control condition, and a fluorescent cell death dye, cytotoxic and cytostatic drug responses can be easily distinguished, profoundly improving the classification of responders and non-responders. In addition, drug-response heterogeneity can by quantified from single-organoid drug response analysis to identify potential, resistant clones. Ultimately, this method aims to improve the prediction of clinical therapy response by capturing a multiparametric drug response signature, which includes kinetic growth arrest and cell death quantification. ,
Keywords: A1 Journal article; Engineering sciences. Technology; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT); Antwerp Surgical Training, Anatomy and Research Centre (ASTARC); Center for Oncological Research (CORE)
Impact Factor: 1.2
DOI: 10.3791/64434
|
|
|
“Enhancement of toughness of Al-to-steel Friction Melt Bonded welds via metallic interlayers”. Jimenez-Mena N, Jacques PJ, Ding L, Gauquelin N, Schryvers D, Idrissi H, Delannay F, Simar A, Materials science and engineering: part A: structural materials: properties, microstructure and processing 740-741, 274 (2019). http://doi.org/10.1016/j.msea.2018.10.101
Abstract: The toughness of Al-to-steel welds decreases with increasing thickness of the intermetallic (IM) layer formed at the interface. Co plating has been added as interlayer in Al-to-steel Friction Melt Bonded (FMB) welds to control the nature and thickness of the IM layer. In comparison to a weld without interlayer, Co plating brings about a reduction of the thickness of the IM layer by 70%. The critical energy release rate of the crack propagating in the weld is used as an indicator of toughness. It is evaluated via an adapted crack propagation test using an energy conservation criterion. For a weld without interlayer, critical energy release rate is found to increase when the thickness of the intermetallic layer decreases. When the intermetallic layer is thick, the crack propagates in a brittle manner through the intermetallic whereas, at low layer thickness, the crack deviates and partially propagates through the Al plate, which causes an increase of toughness. The use of a Co interlayer brings about an increase of toughness by causing full deviation of the crack towards the Al plate.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 4
DOI: 10.1016/j.msea.2018.10.101
|
|
|
“Crystal structure and magnetic properties of the Cr-doped spiral antiferromagnet BiMnFe2O6”. Batuk D, de Dobbelaere C, Tsirlin AA, Abakumov AM, Hardy A, van Bael MK, Greenblatt M, Hadermann J, Materials research bulletin 48, 2993 (2013). http://doi.org/10.1016/j.materresbull.2013.04.038
Abstract: We report the Cr3+ for Mn3+ substitution in the BiMnFe2O6 structure. The BiCrxMn1-xFe2O6 solid solution is obtained by the solution-gel synthesis technique for the x values up to 0.3. The crystal structure investigation using a combination of X-ray powder diffraction and transmission electron microscopy demonstrates that the compounds retain the parent BiMnFe2O6 structure (for x = 0.3, a = 5.02010(6)angstrom, b = 7.06594(7)angstrom, c = 12.6174(1)angstrom, S.G. Pbcm, R-1 = 0.036, R-p = 0.011) with only a slight decrease in the cell parameters associated with the Cr3+ for Mn3+ substitution. Magnetic susceptibility measurements suggest strong similarities in the magnetic behavior of BiCrxMn1-xFe2O6 (x = 0.2; 0.3) and parent BiMnFe2O6. Only T-N slightly decreases upon Cr doping that indicates a very subtle influence of Cr3+ cations on the magnetic properties at the available substitution rates. (C) 2013 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.446
Times cited: 3
DOI: 10.1016/j.materresbull.2013.04.038
|
|
|
“Crystal structure and properties of the new complex vanadium oxide K2SrV3O9”. Tsirlin AA, Chernaya VV, Shpanchenko RV, Antipov EV, Hadermann J, Materials research bulletin 40, 800 (2005). http://doi.org/10.1016/j.materresbull.2005.02.004
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.446
Times cited: 9
DOI: 10.1016/j.materresbull.2005.02.004
|
|
|
“Structure and magnetic properties of a new anion-deficient perovskite Pb2Ba2BiFe4ScO13 with crystallographic shear structure”. Batuk M, Tyablikov OA, Tsirlin AA, Kazakov SM, Rozova MG, Pokholok KV, Filimonov DS, Antipov EV, Abakumov AM, Hadermann J, Materials research bulletin 48, 3459 (2013). http://doi.org/10.1016/j.materresbull.2013.05.028
Abstract: Pb2Ba2BiFe4ScO13, a new n = 5 member of the oxygen-deficient perovskite-based A(n)B(n)O(3n-2) homologous series, was synthesized using a solid-state method. The crystal structure of Pb2Ba2BiFe4ScO13 was investigated by a combination of synchrotron X-ray powder diffraction, electron diffraction, high-angle annular dark-field scanning transmission electron microscopy and Mossbauer spectroscopy. At 900 K, it crystallizes in the Ammm space group with the unit cell parameters a = 5.8459(1) angstrom, b = 4.0426(1) angstrom, and c=27.3435(1) angstrom. In the Pb2Ba2BiFe4ScO13 structure, quasi-two-dimensional perovskite blocks are periodically interleaved with 1/2[1 1 0] ((1) over bar 0 1)(p) crystallographic shear (CS) planes. At the CS planes, the corner-sharing FeO6 octahedra are transformed into chains of edge-sharing FeO5 distorted tetragonal pyramids. B-positions of the perovskite blocks between the CS planes are jointly occupied by Fe3+ and Sc3+. The chains of the FeO5 pyramids and (Fe,Sc)O-6 octahedra delimit six-sided tunnels that are occupied by double columns of cations with a lone electron pair (Pb2+). The remaining A-cations (Bi3+, Ba2+) occupy positions in the perovskite block. According to the magnetic susceptibility measurements, Pb2Ba2BiFe4ScO13 is antiferromagnetically ordered below T-N approximate to 350 K. (C) 2013 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.446
Times cited: 2
DOI: 10.1016/j.materresbull.2013.05.028
|
|
|
“Strain mapping of semiconductor specimens with nm-scale resolution in a transmission electron microscope”. Cooper D, Denneulin T, Bernier N, Béché, A, Rouvière J-L, Micron 80, 145 (2016). http://doi.org/10.1016/J.MICRON.2015.09.001
Abstract: The last few years have seen a great deal of progress in the development of transmission electron microscopy based techniques for strain mapping. New techniques have appeared such as dark field electron holography and nanobeam diffraction and better known ones such as geometrical phase analysis have been improved by using aberration corrected ultra-stable modern electron microscopes. In this paper we apply dark field electron holography, the geometrical phase analysis of high angle annular dark field scanning transmission electron microscopy images, nanobeam diffraction and precession diffraction, all performed at the state-of-the-art to five different types of semiconductor samples. These include a simple calibration structure comprising 10-nm-thick SiGe layers to benchmark the techniques. A SiGe recessed source and drain device has been examined in order to test their capabilities on 2D structures. Devices that have been strained using a nitride stressor have been examined to test the sensitivity of the different techniques when applied to systems containing low values of deformation. To test the techniques on modern semiconductors, an electrically tested device grown on a SOI wafer has been examined. Finally a GaN/AlN superlattice was tested in order to assess the different methods of measuring deformation on specimens that do not have a perfect crystalline structure. The different deformation mapping techniques have been compared to one another and the strengths and weaknesses of each are discussed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.98
Times cited: 50
DOI: 10.1016/J.MICRON.2015.09.001
|
|
|
“Nanoscale investigation by TEM and STEM-EELS of the laser induced yellowing”. Godet M, Vergès-Belmin V, Gauquelin N, Saheb M, Monnier J, Leroy E, Bourgon J, Verbeeck J, Andraud C, Micron 115, 25 (2018). http://doi.org/10.1016/j.micron.2018.08.006
Abstract: Nd-YAG QS laser cleaning of soiled stone at 1064 nm can sometimes result in a more yellow appearance compared to other cleaning techniques. Especially in France, this yellowing effect is still considered as a major aesthetic issue by the architects and conservators. One explanation states that the yellowing is linked to the formation of iron-rich nanophase(s) through the laser beam interaction with black crusts that would re-deposit on the cleaned substrate after irradiation. To characterize these nanophases, a model crust containing hematite was elaborated and laser irradiated using a Nd-YAG QS laser. The color of the sample shifted instantaneously from red to a bright yellow and numerous particles were ablated in a visible smoke. Transmission electron microscopy (TEM) was used to examine the morphology and the crystallinity of the neo-formed compounds, both on the surface of the samples and in the ablated materials. In addition, an investigation of the chemical and structural properties of the nanophases was conducted by X-ray dispersive energy (EDX) and electron energy loss (EELS) spectroscopies. It was found that both the surface of the sample and the ablated materials are covered by crystallized nano-spheres and nano-residues, all containing iron and oxygen, sometimes along with calcium and sulfur. In particular an interfacial area containing the four elements was evidenced between some nanostructures and the substrate. Magnetite Fe3O4 was also identified at the nanoscale. This study demonstrates that the laser yellowing of a model crust is linked to the presence of iron-rich nanophases including CaxFeySzOδ nanostructures and magnetite Fe3O4 at the surface after irradiation.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.98
Times cited: 9
DOI: 10.1016/j.micron.2018.08.006
|
|
|
“Non-ionic surfactant (C13EOm, m=6, 12 and 18) for large pore mesoporous molecular sieves preparation”. Blin JL, Becue A, Pauwels B, Van Tendeloo G, Su BL, Microporous and mesoporous materials 44/45, 41 (2001). http://doi.org/10.1016/S1387-1811(01)00167-6
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.615
Times cited: 27
DOI: 10.1016/S1387-1811(01)00167-6
|
|
|
“Novel method to synthesize highly ordered ethane-bridged PMOs under mild acidic conditions : taking advantages of phosphoric acid”. Lin F, Meng X, Kukueva E, Kus M, Mertens M, Bals S, Van Doorslaer S, Cool P, Microporous and mesoporous materials: zeolites, clays, carbons and related materials 207, 61 (2015). http://doi.org/10.1016/j.micromeso.2014.12.029
Abstract: Highly ordered SBA-15-type ethane-bridged PMOs have been obtained by employing H3PO4 as acid to tune the pH in the presence of copolymer surfactant P123. The effects of the acidity and the addition of inorganic salt on the formation of the mesostructure are investigated. It is found that, compared with HCl, the polyprotic weak acid H3PO4 is preferable for the synthesis of highly ordered SBA-15-type ethane-bridged PMOs with larger pore size and surface areas under mild acidic conditions. Moreover, taking the advantages of the mild acidic condition, vanadium-containing SBA-15-type ethane-bridged PMOs were successfully prepared through a direct synthesis approach. The XRD, N2-sorption, UVVis and CW-EPR studies of the V-PMO show that part of the vanadium species are present in polymeric (VOV)n clusters, while part of the vanadium centers are well-dispersed and immobilized on the inner surface of the mesopores.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 3.615
Times cited: 5
DOI: 10.1016/j.micromeso.2014.12.029
|
|
|
“Fabrication, microstructure, and enhanced thermionic electron emission properties of vertically aligned nitrogen-doped nanocrystalline diamond nanorods”. Sankaran KJ, Deshmukh S, Korneychuk S, Yeh C-J, Thomas JP, Drijkoningen S, Pobedinskas P, Van Bael MK, Verbeeck J, Leou K-C, Leung K-T, Roy SS, Lin I-N, Haenen K, MRS communications 8, 1311 (2018). http://doi.org/10.1557/MRC.2018.158
Abstract: Vertically aligned nitrogen-doped nanocrystalline diamond nanorods are fabricated from nitrogen-doped nanocrystalline diamond films using reactive ion etching in oxygen plasma. These nanorods show enhanced thermionic electron emission (TEE) characteristics, viz.. a high current density of 12.0 mA/cm(2) and a work function value of 4.5 eV with an applied voltage of 3 Vat 923 K. The enhanced TEE characteristics of these nanorods are ascribed to the induction of nanographitic phases at the grain boundaries and the field penetration effect through the local field enhancement from nanorods owing to a high aspect ratio and an excellent field enhancement factor.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.01
Times cited: 1
DOI: 10.1557/MRC.2018.158
|
|
|
“Spatially controlled octahedral rotations and metal-insulator transitions in nickelate superlattices”. Chen B, Gauquelin N, Green RJ, Lee JH, Piamonteze C, Spreitzer M, Jannis D, Verbeeck J, Bibes M, Huijben M, Rijnders G, Koster G, Nano Letters 21, 1295 (2021). http://doi.org/10.1021/ACS.NANOLETT.0C03850
Abstract: The properties of correlated oxides can be manipulated by forming short-period superlattices since the layer thicknesses are comparable with the typical length scales of the involved correlations and interface effects. Herein, we studied the metal-insulator transitions (MITs) in tetragonal NdNiO3/SrTiO3 superlattices by controlling the NdNiO3 layer thickness, n in the unit cell, spanning the length scale of the interfacial octahedral coupling. Scanning transmission electron microscopy reveals a crossover from a modulated octahedral superstructure at n = 8 to a uniform nontilt pattern at n = 4, accompanied by a drastically weakened insulating ground state. Upon further reducing n the predominant dimensionality effect continuously raises the MIT temperature, while leaving the antiferromagnetic transition temperature unaltered down to n = 2. Remarkably, the MIT can be enhanced by imposing a sufficiently large strain even with strongly suppressed octahedral rotations. Our results demonstrate the relevance for the control of oxide functionalities at reduced dimensions.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.712
Times cited: 19
DOI: 10.1021/ACS.NANOLETT.0C03850
|
|
|
“Breakdown of universal scaling for nanometer-sized bubbles in graphene”. Villarreal R, Lin P-C, Faraji F, Hassani N, Bana H, Zarkua Z, Nair MN, Tsai H-C, Auge M, Junge F, Hofsaess HC, De Gendt S, De Feyter S, Brems S, Ahlgren EH, Neyts EC, Covaci L, Peeters FM, Neek-Amal M, Pereira LMC, Nano Letters 21, 8103 (2021). http://doi.org/10.1021/ACS.NANOLETT.1C02470
Abstract: We report the formation of nanobubbles on graphene with a radius of the order of 1 nm, using ultralow energy implantation of noble gas ions (He, Ne, Ar) into graphene grown on a Pt(111) surface. We show that the universal scaling of the aspect ratio, which has previously been established for larger bubbles, breaks down when the bubble radius approaches 1 nm, resulting in much larger aspect ratios. Moreover, we observe that the bubble stability and aspect ratio depend on the substrate onto which the graphene is grown (bubbles are stable for Pt but not for Cu) and trapped element. We interpret these dependencies in terms of the atomic compressibility of the noble gas as well as of the adhesion energies between graphene, the substrate, and trapped atoms.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Condensed Matter Theory (CMT); Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 12.712
Times cited: 24
DOI: 10.1021/ACS.NANOLETT.1C02470
|
|
|
“Alternating superconducting and charge density wave monolayers within bulk 6R-TaS₂”. Achari A, Bekaert J, Sreepal V, Orekhov A, Kumaravadivel P, Kim M, Gauquelin N, Pillai PB, Verbeeck J, Peeters FM, Geim AK, Milošević, MV, Nair RR, Nano letters 22, 6268 (2022). http://doi.org/10.1021/ACS.NANOLETT.2C01851
Abstract: Van der Waals (vdW) heterostructures continue to attract intense interest as a route of designing materials with novel properties that cannot be found in nature. Unfortunately, this approach is currently limited to only a few layers that can be stacked on top of each other. Here, we report a bulk vdW material consisting of superconducting 1H TaS2 monolayers interlayered with 1T TaS2 monolayers displaying charge density waves (CDW). This bulk vdW heterostructure is created by phase transition of 1T-TaS2 to 6R at 800 degrees C in an inert atmosphere. Its superconducting transition (T-c) is found at 2.6 K, exceeding the T-c of the bulk 2H phase. Using first-principles calculations, we argue that the coexistence of superconductivity and CDW within 6R-TaS2 stems from amalgamation of the properties of adjacent 1H and 1T monolayers, where the former dominates the superconducting state and the latter the CDW behavior.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Condensed Matter Theory (CMT)
Impact Factor: 10.8
Times cited: 12
DOI: 10.1021/ACS.NANOLETT.2C01851
|
|
|
“Insights into the Photoelectrocatalytic Behavior of gCN-Based Anode Materials Supported on Ni Foams”. Benedoue S, Benedet M, Gasparotto A, Gauquelin N, Orekhov A, Verbeeck J, Seraglia R, Pagot G, Rizzi GA, Balzano V, Gavioli L, Noto VD, Barreca D, Maccato C, Nanomaterials 13, 1035 (2023). http://doi.org/10.3390/nano13061035
Abstract: Graphitic carbon nitride (gCN) is a promising n-type semiconductor widely investigated for photo-assisted water splitting, but less studied for the (photo)electrochemical degradation of aqueous organic pollutants. In these fields, attractive perspectives for advancements are offered by a proper engineering of the material properties, e.g., by depositing gCN onto conductive and porous scaffolds, tailoring its nanoscale morphology, and functionalizing it with suitable cocatalysts. The present study reports on a simple and easily controllable synthesis of gCN flakes on Ni foam substrates by electrophoretic deposition (EPD), and on their eventual decoration with Co-based cocatalysts [CoO, CoFe2O4, cobalt phosphate (CoPi)] via radio frequency (RF)-sputtering or electrodeposition. After examining the influence of processing conditions on the material characteristics, the developed systems are comparatively investigated as (photo)anodes for water splitting and photoelectrocatalysts for the degradation of a recalcitrant water pollutant [potassium hydrogen phthalate (KHP)]. The obtained results highlight that while gCN decoration with Co-based cocatalysts boosts water splitting performances, bare gCN as such is more efficient in KHP abatement, due to the occurrence of a different reaction mechanism. The related insights, provided by a multi-technique characterization, may provide valuable guidelines for the implementation of active nanomaterials in environmental remediation and sustainable solar-to-chemical energy conversion.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 5.3
Times cited: 3
DOI: 10.3390/nano13061035
|
|
|
“Phase problem in the B-site ordering of La2CoMnO6 : impact on structure and magnetism”. Egoavil R, Huehn S, Jungbauer M, Gauquelin N, Béché, A, Van Tendeloo G, Verbeeck, Moshnyaga V, Nanoscale 7, 9835 (2015). http://doi.org/10.1039/c5nr01642h
Abstract: Epitaxial double perovskite La2CoMnO6 (LCMO) films were grown by metalorganic aerosol deposition on SrTiO3(111) substrates. A high Curie temperature, T-C = 226 K, and large magnetization close to saturation, M-S(5 K) = 5.8 mu(B)/f.u., indicate a 97% degree of B-site (Co,Mn) ordering within the film. The Co/Mn ordering was directly imaged at the atomic scale by scanning transmission electron microscopy with energy-dispersive X-ray spectroscopy (STEM-EDX). Local electron-energy-loss spectroscopy (EELS) measurements reveal that the B-sites are predominantly occupied by Co2+ and Mn4+ ions in quantitative agreement with magnetic data. Relatively small values of the (1/2 1/2 1/2) superstructure peak intensity, obtained by X-ray diffraction (XRD), point out the existence of ordered domains with an arbitrary phase relationship across the domain boundary. The size of these domains is estimated to be in the range 35-170 nm according to TEM observations and modelling the magnetization data. These observations provide important information towards the complexity of the cation ordering phenomenon and its implications on magnetism in double perovskites, and similar materials.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 7.367
Times cited: 37
DOI: 10.1039/c5nr01642h
|
|
|
“Films of filled single-wall carbon nanotubes as a new material for high-performance air-sustainable transparent conductive electrodes operating in a wide spectral range”. Tonkikh AA, Tsebro VI, Obraztsova EA, Rybkovskiy DV, Orekhov AS, Kondrashov II, Kauppinen EI, Chuvilin AL, Obraztsova ED, Nanoscale 11, 6755 (2019). http://doi.org/10.1039/C8NR10238D
Abstract: In this paper we show the advantages of transparent high conductive films based on filled single-wall carbon nanotubes. The nanotubes with internal channels filled with acceptor molecules (copper chloride or iodine) form networks demonstrating significantly improved characteristics. Due to the charge transfer between the nanotubes and filler, the doped-nanotube films exhibit a drop in electrical sheet resistance of an order of magnitude together with a noticeable increase of film transparency in the visible and near-infrared spectral range. The thermoelectric power measurements show a significant improvement of air-stability of the nanotube network in the course of the filling procedure. For the nanotube films with an initial transparency of 87% at 514 nm and electrical sheet resistance of 862 Ohm sq(-1) we observed an improvement of transparency up to 91% and a decrease of sheet resistance down to 98 Ohm sq(-1). The combination of the nanotube synthesis technique and molecules for encapsulation has been optimized for applications in optoelectronics.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 7.367
Times cited: 2
DOI: 10.1039/C8NR10238D
|
|
|
“Interplay of strain and indium incorporation in InGaN/GaN dot-in-a-wire nanostructures by scanning transmission electron microscopy”. Woo SY, Gauquelin N, Nguyen HPT, Mi Z, Botton GA, Nanotechnology 26, 344002 (2015). http://doi.org/10.1088/0957-4484/26/34/344002
Abstract: The interplay between strain and composition is at the basis of heterostructure design to engineer new properties. The influence of the strain distribution on the incorporation of indium during the formation of multiple InGaN/GaN quantum dots (QDs) in nanowire (NW) heterostructures has been investigated, using the combined techniques of geometric phase analysis of atomic-resolution images and quantitative elemental mapping from core-loss electron energy-loss spectroscopy within scanning transmission electron microscopy. The variation in In-content between successive QDs within individual NWs shows a dependence on the magnitude of compressive strain along the growth direction within the underlying GaN barrier layer, which affects the incorporation of In-atoms to minimize the local effective strain energy. Observations suggest that the interfacial misfit between InGaN/GaN within the embedded QDs is mitigated by strain partitioning into both materials, and results in normal stresses inflicted by the presence of the surrounding GaN shell. These experimental measurements are linked to the local piezoelectric polarization fields for individual QDs, and are discussed in terms of the photoluminescence from an ensemble of NWs.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.44
Times cited: 19
DOI: 10.1088/0957-4484/26/34/344002
|
|
|
“Unravelling stacking order in epitaxial bilayer MX₂, using 4D-STEM with unsupervised learning”. Mehta AN, Gauquelin N, Nord M, Orekhov A, Bender H, Cerbu D, Verbeeck J, Vandervorst W, Nanotechnology 31, 445702 (2020). http://doi.org/10.1088/1361-6528/ABA5B6
Abstract: Following an extensive investigation of various monolayer transition metal dichalcogenides (MX2), research interest has expanded to include multilayer systems. In bilayer MX2, the stacking order strongly impacts the local band structure as it dictates the local confinement and symmetry. Determination of stacking order in multilayer MX(2)domains usually relies on prior knowledge of in-plane orientations of constituent layers. This is only feasible in case of growth resulting in well-defined triangular domains and not useful in-case of closed layers with hexagonal or irregularly shaped islands. Stacking order can be discerned in the reciprocal space by measuring changes in diffraction peak intensities. Advances in detector technology allow fast acquisition of high-quality four-dimensional datasets which can later be processed to extract useful information such as thickness, orientation, twist and strain. Here, we use 4D scanning transmission electron microscopy combined with multislice diffraction simulations to unravel stacking order in epitaxially grown bilayer MoS2. Machine learning based data segmentation is employed to obtain useful statistics on grain orientation of monolayer and stacking in bilayer MoS2.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.5
Times cited: 13
DOI: 10.1088/1361-6528/ABA5B6
|
|
|
“Charge-ordering transition in iron oxide Fe4O5 involving competing dimer and trimer formation”. Ovsyannikov SV, Bykov M, Bykova E, Kozlenko DP, Tsirlin AA, Karkin AE, Shchennikov VV, Kichanov SE, Gou H, Abakumov AM, Egoavil R, Verbeeck J, McCammon C, Dyadkin V, Chernyshov D, van Smaalen S, Dubrovinsky LS, Nature chemistry 8, 501 (2016). http://doi.org/10.1038/nchem.2478
Abstract: Phase transitions that occur in materials, driven, for instance, by changes in temperature or pressure, can dramatically change the materials' properties. Discovering new types of transitions and understanding their mechanisms is important not only from a fundamental perspective, but also for practical applications. Here we investigate a recently discovered Fe4O5 that adopts an orthorhombic CaFe3O5-type crystal structure that features linear chains of Fe ions. On cooling below approximately 150 K, Fe4O5 undergoes an unusual charge-ordering transition that involves competing dimeric and trimeric ordering within the chains of Fe ions. This transition is concurrent with a significant increase in electrical resistivity. Magnetic-susceptibility measurements and neutron diffraction establish the formation of a collinear antiferromagnetic order above room temperature and a spin canting at 85 K that gives rise to spontaneous magnetization. We discuss possible mechanisms of this transition and compare it with the trimeronic charge ordering observed in magnetite below the Verwey transition temperature.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 25.87
Times cited: 51
DOI: 10.1038/nchem.2478
|
|
|
“Nematic superconducting state in iron pnictide superconductors”. Li J, Pereira PJ, Yuan J, Lv Y-Y, Jiang M-P, Lu D, Lin Z-Q, Liu Y-J, Wang J-F, Li L, Ke X, Van Tendeloo G, Li M-Y, Feng H-L, Hatano T, Wang H-B, Wu P-H, Yamaura K, Takayama-Muromachi E, Vanacken J, Chibotaru LF, Moshchalkov VV, Nature communications 8, 1880 (2017). http://doi.org/10.1038/s41467-017-02016-y
Abstract: Nematic order often breaks the tetragonal symmetry of iron-based superconductors. It arises from regular structural transition or electronic instability in the normal phase. Here, we report the observation of a nematic superconducting state, by measuring the angular dependence of the in-plane and out-of-plane magnetoresistivity of Ba 0.5 K 0.5 Fe 2 As 2 single crystals. We find large twofold oscillations in the vicinity of the superconducting transition, when the direction of applied magnetic field is rotated within the basal plane. To avoid the influences from sample geometry or current flow direction, the sample was designed as Corbino-shape for in-plane and mesa-shape for out-of-plane measurements. Theoretical analysis shows that the nematic superconductivity arises from the weak mixture of the quasi-degenerate s-wave and d-wave components of the superconducting condensate, most probably induced by a weak anisotropy of stresses inherent to single crystals.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.124
Times cited: 8
DOI: 10.1038/s41467-017-02016-y
|
|
|
“Signatures of enhanced out-of-plane polarization in asymmetric BaTiO3 superlattices integrated on silicon”. Chen B, Gauquelin N, Strkalj N, Huang S, Halisdemir U, Nguyen MD, Jannis D, Sarott MF, Eltes F, Abel S, Spreitzer M, Fiebig M, Trassin M, Fompeyrine J, Verbeeck J, Huijben M, Rijnders G, Koster G, Nature communications 13, 265 (2022). http://doi.org/10.1038/s41467-021-27898-x
Abstract: In order to bring the diverse functionalities of transition metal oxides into modern electronics, it is imperative to integrate oxide films with controllable properties onto the silicon platform. Here, we present asymmetric LaMnO<sub>3</sub>/BaTiO<sub>3</sub>/SrTiO<sub>3</sub>superlattices fabricated on silicon with layer thickness control at the unit-cell level. By harnessing the coherent strain between the constituent layers, we overcome the biaxial thermal tension from silicon and stabilize<italic>c</italic>-axis oriented BaTiO<sub>3</sub>layers with substantially enhanced tetragonality, as revealed by atomically resolved scanning transmission electron microscopy. Optical second harmonic generation measurements signify a predominant out-of-plane polarized state with strongly enhanced net polarization in the tricolor superlattices, as compared to the BaTiO<sub>3</sub>single film and conventional BaTiO<sub>3</sub>/SrTiO<sub>3</sub>superlattice grown on silicon. Meanwhile, this coherent strain in turn suppresses the magnetism of LaMnO<sub>3</sub>as the thickness of BaTiO<sub>3</sub>increases. Our study raises the prospect of designing artificial oxide superlattices on silicon with tailored functionalities.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 16.6
Times cited: 11
DOI: 10.1038/s41467-021-27898-x
|
|
|
“Extreme mobility enhancement of two-dimensional electron gases at oxide interfaces by charge-transfer-induced modulation doping”. Chen YZ, Trier F, Wijnands T, Green RJ, Gauquelin N, Egoavil R, Christensen DV, Koster G, Huijben M, Bovet N, Macke S, He F, Sutarto R, Andersen NH, Sulpizio JA, Honig M, Prawiroatmodjo GEDK, Jespersen TS, Linderoth S, Ilani S, Verbeeck J, Van Tendeloo G, Rijnders G, Sawatzky GA, Pryds N, Nature materials 14, 801 (2015). http://doi.org/10.1038/nmat4303
Abstract: Two-dimensional electron gases (2DEGs) formed at the interface of insulating complex oxides promise the development of all-oxide electronic devices. These 2DEGs involve many-body interactions that give rise to a variety of physical phenomena such as superconductivity, magnetism, tunable metalinsulator transitions and phase separation. Increasing the mobility of the 2DEG, however, remains a major challenge. Here, we show that the electron mobility is enhanced by more than two orders of magnitude by inserting a single-unit-cell insulating layer of polar La1−xSrxMnO3 (x = 0, 1/8, and 1/3) at the interface between disordered LaAlO3 and crystalline SrTiO3 produced at room temperature. Resonant X-ray spectroscopy and transmission electron microscopy show that the manganite layer undergoes unambiguous electronic reconstruction, leading to modulation doping of such atomically engineered complex oxide heterointerfaces. At low temperatures, the modulation-doped 2DEG exhibits Shubnikovde Haas oscillations and fingerprints of the quantum Hall effect, demonstrating unprecedented high mobility and low electron density.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 39.737
Times cited: 170
DOI: 10.1038/nmat4303
|
|