Abstract: Since 1995 when the first of metal−organic frameworks was crystallized with the strong bond approach, where metal ions are joined by charged organic linkers exemplified by carboxylates, followed by proof of their porosity in 1998 and ultrahigh porosity in 1999, a revolution in the development of their chemistry has ensued. This is being reinforced by the discovery of two- and three-dimensional covalent organic frameworks in 2005 and 2007. Currently, the chemistry of such porous, crystalline frameworks is collectively referred to as reticular chemistry, which is being practiced in over 100 countries. The involvement of researchers from various backgrounds and fields, and the vast scope of this chemistry and its societal applications, necessitate articulating the “Standard Practices of Reticular Chemistry”.

Abstract: Synthetic and naturally occurring forms of tricopper orthotellurate, (Cu3TeO6)-Te-II-O-IV (the mineral mcalpineite) have been investigated by 3D electron diffraction (3D ED), X-ray powder diffraction (XRPD), Raman and infrared (IR) spectroscopic measurements. As a result of the diffraction analyses, (Cu3TeO6)-Te-II-O-IV is shown to occur in two polytypes. The higher-symmetric (Cu3TeO6)-Te-II-O-IV-1C polytype is cubic, space group 1a (3) over bar, with a = 9.537 (1) angstrom and V = 867.4 (3) angstrom(3) as reported in previous studies. The 1C polytype is a well characterized structure consisting of alternating layers of (CuO6)-O-II octahedra and both (CuO6)-O-II and (TeO6)-O-VI octahedra in a patchwork arrangement. The structure of the lower-symmetric orthorhombic (Cu3TeO6)-Te-II-O-IV-2O polytype was determined for the first time in this study by 3D ED and verified by Rietveld refinement. The 2O polytype crystallizes in space group Pcca, with a = 9.745 (3) angstrom, b = 9.749 (2) angstrom, c = 9.771 (2) angstrom and V = 928.3 (4) angstrom(3) . High-precision XRPD data were also collected on (Cu3TeO6)-Te-II-O-IV-2O to verify the lower-symmetric structure by performing a Rietveld refinement. The resultant structure is identical to that determined by 3D ED, with unit-cell parameters a = 9.56157 (19) angstrom, b = 9.55853 (11) angstrom, c = 9.62891 (15) angstrom and V = 880.03 (2) angstrom(3) . The lower symmetry of the 2O polytype is a consequence of a different cation ordering arrangement, which involves the movement of every second (CuO6)-O-II and (TeO6)-O-VI octahedral layer by (1/4, 1/4, 0), leading to an offset of (TeO6)-O-VI and (CuO6)-O-II octahedra in every second layer giving an ABAB* stacking arrangement. Syntheses of (Cu3TeO6)-Te-II-O-IV showed that low-temperature (473 K) hydrothermal conditions generally produce the 2O polytype. XRPD measurements in combination with Raman spectroscopic analysis showed that most natural mcalpineite is the orthorhombic 2O polytype. Both XRPD and Raman spectroscopy measurements may be used to differentiate between the two polytypes of (Cu3TeO6)-Te-II-O-IV. In Raman spectroscopy, (Cu3TeO6)-Te-II-O-IV-1C has a single strong band around 730 cm(-1), whereas (Cu3TeO6)-Te-II-O-IV-2O shows a broad double maximum with bands centred around 692 and 742 cm(-1).

Abstract: The crystal structure solution of modulated compounds is often very challenging, even using the well established methodology of single-crystal X-ray crystallography. This task becomes even more difficult for materials that cannot be prepared in a single-crystal form, so that only polycrystalline powders are available. This paper illustrates that the combined application of transmission electron microscopy (TEM) and powder diffraction is a possible solution to the problem. Using examples of anion-deficient perovskites modulated by periodic crystallographic shear planes, it is demonstrated what kind of local structural information can be obtained using various TEM techniques and how this information can be implemented in the crystal structure refinement against the powder diffraction data. The following TEM methods are discussed: electron diffraction (selected area electron diffraction, precession electron diffraction), imaging (conventional high-resolution TEM imaging, high-angle annular dark-field and annular bright-field scanning transmission electron microscopy) and state-of-the-art spectroscopic techniques (atomic resolution mapping using energy-dispersive X-ray analysis and electron energy loss spectroscopy).

Abstract: Cold atmospheric plasma (CAP) is a partially ionized gas that gains attention
as a well-tolerated cancer treatment that can enhance anti-tumor immune
responses, which are important for durable therapeutic effects. This review
offers a comprehensive and critical summary on the current understanding of
mechanisms in which CAP can assist anti-tumor immunity: induction of
immunogenic cell death, oxidative post-translational modifications of the
tumor and its microenvironment, epigenetic regulation of aberrant gene
expression, and enhancement of immune cell functions. This should provide
a rationale for the effective and meaningful clinical implementation of CAP. As
discussed here, despite its potential, CAP faces different clinical limitations
associated with the current CAP treatment modalities: direct exposure of
cancerous cells to plasma, and indirect treatment through injection of
plasma-treated liquids in the tumor. To this end, a novel modality is proposed:
plasma-treated hydrogels (PTHs) that can not only help overcome some of the
clinical limitations but also offer a convenient platform for combining CAP
with existing drugs to improve therapeutic responses and contribute to the
clinical translation of CAP. Finally, by integrating expertise in biomaterials and
plasma medicine, practical considerations and prospective for the
development of PTHs are offered.

Abstract: The recently discovered superconducting mercury-based cuprates HgBa2Can-1CunO2n+2+delta have proved difficult to synthesize as single phases and are sensitive to environment (CO2, moisture). The present paper gives an overview of new series mercury based superconductors, whose stabilisation is based on the fact that a foreign cation with a higher valency than Hg(II) must be introduced in the mercury layers, in order to fill up partially the oxygen vacancies of these layers. By this method, several new series of superconductors involving strontium instead of barium with critical temperatures ranging from 27 K to 95 K have been isolated : Hg0.5Bi0.5Sr2-xLaxCuO4+delta, Hg(0.5)Bi(0.5)Sr(2)Ca(1-x)R(x)Cu(2)O(6+delta) (R Y, Nd, Pr), Pb0.7Hg0.3Sr2-xLaxCuO4+delta, Pb(0.7)Hg(0.3)Sr(2)Ca(1-x)R(x)Cu(2)O(6+delta) (R = Y, Nd) Hg(1-x)Pr(x)Sr(2)A(1-x')Pr(x') Cu2O6+delta (A = Sr, Ca), Pb0.7Hg0.3Sr2Cu2CO3O7 and Hg1-xCrxSr2CuO4+delta. The behaviour of the praseodymium cuprates that exhibit a rather sharp transition and reach a Tc of 85 K is especially discussed. A method to synthesize new ''Ba-Hg'' superconducting cuprates with the 1212 structure at normal pressure with a Tc up to 110 K is also presented.

Abstract: Recently, a universal equation by Narushin, Romanov, and Griffin (hereafter, the NRGE) was proposed to describe the shape of avian eggs. While NRGE can simulate the shape of spherical, ellipsoidal, ovoidal, and pyriform eggs, its predictions were not tested against actual data. Here, we tested the validity of the NRGE by fitting actual data of egg shapes and compared this with the predictions of our simpler model for egg shape (hereafter, the SGE). The eggs of nine bird species were sampled for this purpose. NRGE was found to fit the empirical data of egg shape well, but it did not define the egg length axis (i.e., the rotational symmetric axis), which significantly affected the prediction accuracy. The egg length axis under the NRGE is defined as the maximum distance between two points on the scanned perimeter of the egg's shape. In contrast, the SGE fitted the empirical data better, and had a smaller root-mean-square error than the NRGE for each of the nine eggs. Based on its mathematical simplicity and goodness-of-fit, the SGE appears to be a reliable and useful model for describing egg shape.

Abstract: The post-growth modification of diamond-like amorphous hydrogenated carbon a-C:H films by laser treatment has been studied by transmission electron microscopy and Raman spectroscopy. a-C:H films grown on Si substrates by benzene decomposition in a rf glow discharge were irradiated with 15 ns pulses of a KrF-excimer laser with fluences in the ran e of E = 50-700 mJ/cm(2). At fluences below 100 mJ/cm(2) an increase in the number of graphitic clusters and in their ordering was evidenced from Raman spectra, while the film structure remained amorphous according to electron microscopy and electron diffraction observations. At higher fluences the appearance of diamond particles of 2-7 nm size, embedded into the lower crystallized graphitic matrix, was observed and simultaneously a progressive growth of graphite nanocrystals with dimensions from 2 nm to 4 nm was deduced from Raman measurements. The maximum thickness of the crystallized surface layer (approximate to 400 nm) and the degree of laser annealing are limited by the film ablation which starts at E > 250 mJ/cm(2). The laser-treated areas lose their chemical inertness. In particular, chemical etching in chromium acid becomes possible, which may be used for patterning the highly inert carbon films.

Abstract: In this study the usefulness of micro-Computed Tomography (µ-CT) for the in-depth analysis of enamelled metal objects was tested. Usually investigations of enamelled metal artefacts are restricted to non-destructive surface analysis or analysis of cross sections after destructive sampling. Radiography, a commonly used technique in the field of cultural heritage studies, is limited to providing two-dimensional information about a three-dimensional object (Lang and Middleton, Radiography of Cultural Material, pp. 6061, Elsevier-Butterworth-Heinemann, Amsterdam-Stoneham-London, 2005). Obtaining virtual slices and information about the internal structure of these objects was made possible by CT analysis. With this technique the underlying metal work was studied without removing the decorative enamel layer. Moreover visible defects such as cracks were measured in both width and depth and as of yet invisible defects and weaker areas are visualised. All these features are of great interest to restorers and conservators as they allow a view inside these objects without so much as touching them.

Abstract: Samples of cretaceous limestone have been treated with three application methods (poultice, immersion and brushing) using different concentrations of ammonium oxalate solution (AmOx) and varying treatment time in order to test the efficiency of surface and in-depth formation of a protective layer of calcium oxalate (CaOx). Synchrotron-based microanalytical techniques (SR-mu XRD with 12.5 mu mx7.5 mu m (HxV) probe size, SR-mu FTIR with 10 mu mx10 mu m and 8 mu mx20 mu m probe sizes) and laboratory mu FTIR, XRD and SEM have been employed for analysis of the treated samples. Synchrotron-based techniques showed variations in the CaOx distribution along the surface on a micrometer scale. All treatments resulted in the development of a CaOx layer with a maximum thickness of approximately 40 mu m. Application by the brushing method with 10 1-min applications with 5-min breaks during one hour showed a development of the calcium oxalate layer equivalent to the poultice treatment taking 10 h. This treatment could be preferred for large marble or limestone surfaces where poultice usage is economically not feasible.

Abstract: For the non-destructive identification of pigments and colorants in works of art, in archaeological and in forensic materials, a wide range of analytical techniques can be used. Bearing in mind that every method holds particular limitations, two complementary spectroscopic techniques, namely confocal ì-Raman spectroscopy (ì-RS) and ì-X-ray fluorescence spectroscopy (ì-XRF), were joined in one instrument. The combined ì-XRF and ì-RS device, called PRAXIS unites both complementary techniques in one mobile setup, which allows ì- and in situ analysis. ì-XRF allows one to collect elemental and spatially-resolved information in a non-destructive way on major and minor constituents of a variety of materials. However, the main disadvantages of ì-XRF are the penetration depth of the X-rays and the fact that only elements and not specific molecular combinations of elements can be detected. As a result ì-XRF is often not specific enough to identify the pigments within complex mixtures. Confocal Raman microscopy (ì-RS) can offer a surplus as molecular information can be obtained from single pigment grains. However, in some cases the presence of a strong fluorescence background limits the applicability. In this paper, the concrete analytical possibilities of the combined PRAXIS device are evaluated by comparing the results on an illuminated sheet of parchment with the analytical information supplied by synchrotron radiation ì-X-ray diffraction (SR ì-XRD), a highly specific technique.

Abstract: Imaging methods with elemental contrast are of great value for the investigation of historical paintings, as they allow for study of sub-surface layers that provide insight into a painting's creation process. Two of the most important methods are neutron activation autoradiography (NAAR) and scanning macro-XRF (MA-XRF). Given the differences between these methods in the fundamental physical phenomena exploited, a theoretical comparison of their capabilities is difficult and until now a critical comparison of their use on the same painting is missing. In this paper, we present a study of Rembrandt van Rijn's painting Susanna and the Elders from the Gemaldegalerie in Berlin employing both techniques. The painting features a considerable number of overpainted features and a wide range of pigments with different elemental tracers, including earth pigments (Mn/Fe), Azurite (Cu), lead white (Pb), vermilion (Hg) and smalt (Co, As). MA-XRF can detect all elements above Si (Z = 14), suffers from few spectral overlaps and can be performed in a few tens of hours in situ, i.e. in a museum. NAAR requires the stay of the painting at a research facility for several weeks, and inter-element interferences can be difficult to resolve. Also, only a limited number of elements contribute to the acquired autoradiographs, most notably Mn, Cu, As, Co, Hg and P. However, NAAR provides a higher lateral resolution and is less hindered by absorption in covering layers, which makes it the only method capable of visualizing P in lower paint layers.