Abstract: Simple methods for producing noble metal catalysts with well-defined active sites and improved performance are highly desired in the chemical industry. However, the development of such methods still presents a formidable synthetic challenge. Here, we demonstrate a one-pot synthesis route for the controlled production of bimetallic Pt–In catalysts based on the single-step formation of Mg,Al,Pt,In-containing layered double hydroxides (LDHs). Besides their simple synthesis, these Pt–In catalysts exhibit superior propane dehydrogenation activity compared to their multi-step synthesized analogs. The presented material serves as a showcase for the one-pot synthesis of a broader class of LDH-derived mono- and multimetallic Pt catalysts. The compositional flexibility provided by LDH materials can pave the way towards highperforming Pt-based catalysts with tunable physicochemical properties.

Abstract: The one-step preparation of capped PbS nanoparticles in an inorganic matrix via UV-induced decomposition of lead thiosulfate complexes intercalated into a hydrotalcite-type layered double hydroxide is reported.

Abstract: The influence of the amount of catalyst and the reaction time on the quantity and quality of catalytically grown single wall carbon nanotubes (SWNT) was investigated. The aim was to optimize some of the SWNT growth parameters using TEM and HRTEM. The thickness of catalyst layer influences the synthesis of the nanotube because the gas composition can differ between top and bottom. Microscopic investigation of the grown SWNT samples showed that the thicker the catalyst layer the lower relative nanotube content, so the deeper parts of the catalyst layer are less effective: The optimum time for the reaction was found to be 10 minutes. This may be understood assuming that nanotube growth needs an initial incubation time while the activity of the catalyst decreases steadily until the nariotube growth stops.

Abstract: Er3+Yb3+ co-doped transparent glass-ceramics with varying Er/Yb content and ratio have been prepared. High quantum yields for up- and down-conversion luminescence by energy transfer from Yb3+ to Er3+ and from Er3+ to Yb3+, respectively, have been detected and optimized with respect to the Er/Yb content and ratio, and proposed in particular for up- and down-conversion of solar spectrum for enhancement of the efficiency of solar cells. The rise and decay kinetics for the population of the excited levels of Er3+ and Yb3+ have been studied and fit. Based on these experimental data, the mechanisms for the energy transfers have been suggested with emphasis on the optimized Er/Yb content and ratio for enhancement of the efficiency of the Er3+↔Yb3+ energy transfers.

Abstract: ZSM-48 and related zeolites are considered to be highly disordered structures. Different polytypes can be clearly distinguished by simulation of high-resolution electron microscopy images. Synthesis of phase-pure polytypes was attempted. One of the investigated samples crystallized via seeding designated as COK-8 consisted of nanoscopic, needlelike crystals with a very large length/width ratio, growing along the pore direction. These specimens are phase-pure polytype 6 (PT6, numbering according to Lobo and van Koningsveld). Aggregates of these nanoneedles occasionally contained a second polytype: PT1. The latter polytype occurred more abundantly in larger crystal rods in an IZM-1 sample crystallized in ethylene glycol. Here too, the isolated crystallites mainly consist of large, defect-free regions of PT6. A simulation of polytype lattice energies offers a rational explanation for the observed polytypical intergrowth formation.

Abstract: A new potassium palladate KPd2O3 was synthesized by the reaction of KO2 and PdO at elevated oxygen pressure. Its crystal structure was solved from powder X-ray diffraction data in the space group Rm (a = 6.0730(1) Å, c = 18.7770(7) Å, and Z = 6). KPd2O3 represents a new structure type, consisting of an alternating sequence of K+ and Pd2O3− layers with ordered Pd2+ and Pd4+ ions. The presence of palladium ions in di- and tetravalent low-spin states was confirmed by magnetic susceptibility measurements.

Abstract: The new families of superconducting compounds ''1201'' (Hg0.4Pr0.6Sr2CuO4+delta), ''1212'' (Hg0.4Pr0.6Sr2(Ca1-x-ySrxPry) Cu2O6+delta), and ''1222'' (Hg0.4Pr0.6Sr2(Pr1.7Sr0.3)(2)Cu2O8+delta) all show ordering between praseodymium and mercury in the (Hg,Pr)O-delta plane, reducing the symmetry from tetragonal to orthorhombic or even to monoclinic. In the 1201 compound the ordered superstructure can be described as O-I (a(I) approximate to 2a(p), b(I), approximate to a(p), c(I) approximate to c(1201)). In the 1212 compound two distinct superstructures are identified, O-I (a(I) approximate to 2a(p), b(II) approximate to a(p), c(I) approximate to c(1212)) and O-II (a(II) approximate to 2a(p), b(II) approximate to a(p), c(II) approximate to 2c(1212)). In some compounds, such as Hg0.4Pr0.6Sr2(Ca0.4Sr0.4Pr0.2) Cu2O6+delta, the Hg-Pr ordering is only present in microdomains, but due to an ordering between Sr layers and Ca layers, the c-axis doubles and one obtains a tetragonal superstructure T-III (a(III) approximate to a(p), c(III) approximate to 2c(1212)). In the 1222 compound, ordering in the (Pr,Hg)O-delta plane is very defective; a large number of translation defects actually reduce the symmetry to triclinic. (C) 1995 Academic Press, Inc.

Abstract: Pd particles supported on SnO2 and GeO2 have been structurally investigated by X-ray diffraction, (High-Resolution) transmission and scanning electron microscopy after different reductive treatments to monitor the eventual formation of bimetallic phases and catalytically tested in methanol dehydrogenation/ reforming. For both oxides this included a thin film sample with well-defined Pd particles and a powder catalyst prepared by incipient wetness impregnation. The hexagonal and the tetragonal polymorph were studied for powder GeO2. Pd2Ge formation was observed on all GeO2-supported catalysts, strongly depending on the specific sample used. Reduction of the thin film at 573K resulted in full transformation into the bimetallic state. The partial solubility of hexagonal GeO2 in water and its thermal structural instability yielded Pd2Ge formation at 473 K, at the cost of a structurally inhomogeneous support and Ge metal formation at higher reduction temperatures. Pd on tetragonal GeO2 entered a state of strong metalsupport interaction after reduction at 573673 K, resulting in coalescing Pd2Ge particles on a sintered and re-crystallized support, apparently partially covering the bimetallic particles and decreasing the catalytic activity. Pd2Ge on amorphous thin film and hexagonal GeO2 converted methanol primarily via dehydrogenation to CO and H2. At 573 K, formation of Pd2Sn and also PdSn occurred on the Pd/SnO2 thin film. Pd3Sn2 (and to some extent Pd2Sn) were predominantly obtained on the respective powder catalyst. Strong deactivation with increasing reduction temperature was observed, likely not based on the classical strong metalsupport interaction effect, but rather on a combination of missing active structural ensembles on Sn-enriched bimetallic phases and the formation of metallic -Sn. Correlations to Pd and its bimetallics supported on ZnO, Ga2O3 and In2O3 were also discussed.

Abstract: Although Li-rich layered oxides (Li1+xNiyCozMn1−x−y−zO2 > 250 mAh g−1) are attractive electrode materials providing energy densities more than 15% higher than todays commercial Li-ion cells, they suffer from voltage decay on cycling. To elucidate the origin of this phenomenon, we employ chemical substitution in structurally related Li2RuO3 compounds. Li-rich layered Li2Ru1−yTiyO3 phases with capacities of ~240 mAh g−1 exhibit the characteristic voltage decay on cycling. A combination of transmission electron microscopy and X-ray photoelectron spectroscopy studies reveals that the migration of cations between metal layers and Li layers is an intrinsic feature of the chargedischarge process that increases the trapping of metal ions in interstitial tetrahedral sites. A correlation between these trapped ions and the voltage decay is established by expanding the study to both Li2Ru1−ySnyO3 and Li2RuO3; the slowest decay occurs for the cations with the largest ionic radii. This effect is robust, and the finding provides insights into new chemistry to be explored for developing high-capacity layered electrodes that evade voltage decay.

Abstract: Oxygen ordering has been investigated in superconducting ABa2Cu3O7-delta ceramic materials with A = Er, Nd, Sm and Yb, as well as in samples of this type with the rate earth A partially substituted by Pr. The critical temperature T(c) was determined as a function of the oxygen deficiency-delta of the compound and the corresponding microstructures were investigated by electron diffraction and electron microscopy. A distinct relationship exists between the width of the 60 K plateau and the ortho II ordering. Our results show that the ortho II ordered phase is the superconducting phase with a characteristic T(c) of 60 K.

Abstract: Transition metal L2,3 electron energy-loss spectra for a wide range of V-, Mn- and Fe-based oxides were recorded and carefully analyzed for their correlation with the formal oxidation states of the transition metal ions. Special attention is paid to obtain an accurate energy scale which provides absolute energy positions for all core-loss edges. The white-line ratio method, chemical shift method, ELNES fitting method, two-parameter method and other methods are compared and their validity is discussed. Both the ELNES fitting method and the chemical shift method have the advantage of a wide application range and good consistency but require special attention to accurately measure the core-loss edge position. The obtained conclusions are of fundamental importance, e.g., for obtaining atomic resolution oxidation state information in modern experiments.

Abstract: Two different Pd/In2O3 samples including a thin film model catalyst with well-defined Pd particles grown on NaCl(0 0 1) supports and a powder catalyst prepared by an impregnation technique are examined by electron microscopy, X-ray diffraction and catalytic measurements in methanol steam reforming in order to correlate the formation of different oxide-supported bimetallic PdIn phases with catalytic activity and selectivity. A PdIn shell around the Pd particles is observed on the thin film catalyst after embedding the Pd particles in In2O3 at 300 K, likely because alloying to PdIn and oxidation to In2O3 are competing processes. Increased PdIn bimetallic formation is observed up to 573 K reduction temperature until at 623 K the film stability limit in hydrogen is reached. Oxidative treatments at 573 K lead to decomposition of PdIn and to the formation of an In2O3 shell covering the Pd particles, which irreversibly changes the activity and selectivity pattern to clean In2O3. PdIn and Pd2In3 phases are obtained on the powder catalyst after reduction at 573 K and 673 K, respectively. Only CO2-selective methanol steam reforming is observed in the reduction temperature range between 473 K and 573 K. After reduction at 673 K encapsulation of the bimetallic particles by crystalline In2O3 suppresses CO2 formation and only activity and selectivity of clean In2O3 are measured.