“Dimethylformamide-mediated synthesis of water-soluble platinum nanodendrites for ethanol oxidation electrocatalysis”. Mourdikoudis S, Chirea M, Altantzis T, Pastoriza-Santos I, Perez-Juste J, Silva F, Bals S, Liz-Marzan LM, Nanoscale 5, 4776 (2013). http://doi.org/10.1039/c3nr00924f
Abstract: Herein we describe the synthesis of water-soluble platinum nanodendrites in dimethylformamide (DMF), in the presence of polyethyleneimine (PEI) as a stabilizing agent. The average size of the dendrites is in the range of 20-25 nm while their porosity can be tuned by modifying the concentration of the metal precursor. Electron tomography revealed different crystalline orientations of nanocrystallites in the nanodendrites and allowed a better understanding of their peculiar branching and porosity. The high surface area of the dendrites (up to 22 m(2) g(-1)) was confirmed by BET measurements, while X-ray diffraction confirmed the abundance of high-index facets in the face-centered-cubic crystal structure of Pt. The prepared nanodendrites exhibit excellent performance in the electrocatalytic oxidation of ethanol in alkaline solution. Sensing, selectivity, cycleability and great tolerance toward poisoning were demonstrated by cyclic voltammetry measurements.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 7.367
Times cited: 50
DOI: 10.1039/c3nr00924f
|
|
|
“Direct correlation of nanoscale morphology and device performance to study photocurrent generation in donor-enriched phases of polymer solar cells”. Ben Dkhil S, Perkhun P, Luo C, Mueller D, Alkarsifi R, Barulina E, Quiroz YAA, Margeat O, Dubas ST, Koganezawa T, Kuzuhara D, Yoshimoto N, Caddeo C, Mattoni A, Zimmermann B, Wuerfel U, Pfannmöller M, Bals S, Ackermann J, Videlot-Ackermann C, Acs Applied Materials &, Interfaces 12, 28404 (2020). http://doi.org/10.1021/ACSAMI.0C05884
Abstract: The nanoscale morphology of polymer blends is a key parameter to reach high efficiency in bulk heterojunction solar cells. Thereby, research typically focusing on optimal blend morphologies while studying nonoptimized blends may give insight into blend designs that can prove more robust against morphology defects. Here, we focus on the direct correlation of morphology and device performance of thieno[3,4-b]-thiophene-alt-benzodithiophene (PTB7):[6,6]phenyl C-71 butyric acid methyl ester (PC71BM) bulk heterojunction (BHJ) blends processed without additives in different donor/acceptor weight ratios. We show that while blends of a 1:1.5 ratio are composed of large donor-enriched and fullerene domains beyond the exciton diffusion length, reducing the ratio below 1:0.5 leads to blends composed purely of polymer-enriched domains. Importantly, the photocurrent density in such blends can reach values between 45 and 60% of those reached for fully optimized blends using additives. We provide here direct visual evidence that fullerenes in the donor-enriched domains are not distributed homogeneously but fluctuate locally. To this end, we performed compositional nanoscale morphology analysis of the blend using spectroscopic imaging of low-energy-loss electrons using a transmission electron microscope. Charge transport measurement in combination with molecular dynamics simulations shows that the fullerene substructures inside the polymer phase generate efficient electron transport in the polymer-enriched phase. Furthermore, we show that the formation of densely packed regions of fullerene inside the polymer phase is driven by the PTB7:PC71BM enthalpy of mixing. The occurrence of such a nanoscale network of fullerene clusters leads to a reduction of electron trap states and thus efficient extraction of photocurrent inside the polymer domain. Suitable tuning of the polymer-acceptor interaction can thus introduce acceptor subnetworks in polymer-enriched phases, improving the tolerance for high-efficiency BHJ toward morphological defects such as donor-enriched domains exceeding the exciton diffusion length.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 9.5
Times cited: 7
DOI: 10.1021/ACSAMI.0C05884
|
|
|
“Direct determination of polarity, faceting, and core location in colloidal core/shell wurtzite semiconductor nanocrystals”. Bertoni G, Grillo V, Brescia R, Ke X, Bals S, Catellani A, Li H, Manna L, ACS nano 6, 6453 (2012). http://doi.org/10.1021/nn302085t
Abstract: The ability to determine the atomic arrangement and termination of various facets of surfactant-coated nanocrystals is of great importance for understanding their growth mechanism and their surface properties and represents a critical piece of information that can be coupled to other experimental techniques and to calculations. This is especially appealing in the study of nanocrystals that can be grown in strongly anisotropic shapes, for which the relative growth rates of various facets can be influenced under varying reaction conditions. Here we show that in two representative cases of rod-shaped nanocrystals in the wurtzite phase (CdSe(core)/CdS(shell) and ZnSe(core)/ZnS(shell) nanorods) the terminations of the polar facets can be resolved unambiguously by combining advanced electron microscopy techniques, such as aberration-corrected HRTEM with exit wave reconstruction or aberration-corrected HAADF-STEM. The [0001] and [000-1] polar directions of these rods, which grow preferentially along their c-axis, are revealed clearly, with one side consisting of the Cd (or Zn)-terminated (0001) facet and the other side with a pronounced faceting due to Cd (or Zn)-terminated {10-1-1} facets. The lateral faceting of the rods is instead dominated by three nonpolar {10-10} facets. The core buried in the nanostructure can be localized in both the exit wave phase and HAADF-STEM images.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 13.942
Times cited: 63
DOI: 10.1021/nn302085t
|
|
|
“Direct evidence for the existence of multi-walled carbon nanotubes with hexagonal cross-sections”. He Z, Ke X, Bals S, Van Tendeloo G, Carbon 50, 2524 (2012). http://doi.org/10.1016/j.carbon.2012.01.075
Abstract: Carbon nanotubes (CNTs) with a polygonal cross-section have been paid increasing attention since their three-dimensional structure is related to specific physical properties, which are found to be different in comparison to CNTs with a circular cross-section. Here, we report the existence of novel multi-walled CNTs yielding walls with a rounded-hexagonal configuration. This structure was directly confirmed for the first time by both cross-sectional transmission electron microscopy and electron tomography. The morphology of the Fe catalytic particle also exhibits hexagonal characteristics, and is proposed as the origin of the formation of the rounded-hexagonal walls of the CNT. This observation is of great importance with respect to the design of polygonal (such as pentagonal or hexagonal) cross-sectional CNTs. By controlling the morphology of the catalytic nanoparticles it will be possible to grow CNTs with desired electronic and mechanical properties.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.337
Times cited: 8
DOI: 10.1016/j.carbon.2012.01.075
|
|
|
“Direct evidence of spontaneous quantum dot formation in a thick InGaN epilayer”. Nistor L, Bender H, Vantomme A, Wu MF, van Landuyt J, O'Donnell KP, Martin R, Jacobs K, Moerman I, Applied physics letters 77, 507 (2000). http://doi.org/10.1063/1.127026
Abstract: We report a direct observation of quantum dots formed spontaneously in a thick InGaN epilayer by high resolution transmission electron microscopy. Investigation of a (280 nm thick) In0.22Ga0.78N single layer, emitting in the blue/green spectral region, reveals quantum dots with estimated sizes in the range of 1.5-3 nm. Such sizes are in very good agreement with calculations based on the luminescence spectra of this specimen. (C) 2000 American Institute of Physics. [S0003-6951(00)00930-X].
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 44
DOI: 10.1063/1.127026
|
|
|
“Direct evidence of stacking disorder in the mixed ionic-electronic conductor Sr4Fe6O12+\delta”. Rossell MD, Abakumov AM, Ramasse QM, Erni R, ACS nano 7, 3078 (2013). http://doi.org/10.1021/nn3058449
Abstract: Determining the structure-to-property relationship of materials becomes particularly challenging when the material under investigation is dominated by defects and structural disorder. Knowledge on the exact atomic arrangement at the defective structure is required to understand its influence on the functional properties. However, standard diffraction techniques deliver structural information that is averaged over many unit cells. In particular, information about defects and order-disorder phenomena is contained in the coherent diffuse scattering intensity which often is difficult to uniquely interpret. Thus, the examination of the local disorder in materials requires a direct method to study their structure on the atomic level with chemical sensitivity. Using aberration-corrected scanning transmission electron microscopy in combination with atomic-resolution electron energy-loss spectroscopy, we show that the controversial structural arrangement of the Fe2O2+delta layers in the mixed ionic-electronic conducting Sr4Fe6O12+delta perovskite can be unambiguously resolved. Our results provide direct experimental evidence for the presence of a nanomixture of “ordered” and “disordered” domains in an epitaxial Sr4Fe6O12+delta thin film. The most favorable arrangement is the disordered structure and is interpreted as a randomly occurring but well-defined local shift of the Fe-O chains in the Fe2O2+delta layers. By analyzing the electron energy-loss near-edge structure of the different building blocks in the Sr4Fe6O12+delta unit cell we find that the mobile holes in this mixed ionic-electronic conducting oxide are highly localized in the Fe2O2+delta layers, which are responsible for the oxide-ion conductivity. A possible link between disorder and oxygen-ion transport along the Fe2O2+delta layers is proposed by arguing that the disorder can effectively break the oxygen diffusion pathways.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 13.942
Times cited: 4
DOI: 10.1021/nn3058449
|
|
|
“Direct Imaging of ALD Deposited Pt Nanoclusters inside the Giant Pores of MIL-101”. Meledina M, Turner S, Filippousi M, Leus K, Lobato I, Ramachandran RK, Dendooven J, Detavernier C, Van Der Voort P, Van Tendeloo G, Particle and particle systems characterization 33, 382 (2016). http://doi.org/10.1002/ppsc.201500252
Abstract: MIL-101 giant-pore metal-organic framework (MOF) materials have been loaded with Pt nanoparticles using atomic layer deposition. The final structure has been investigated by aberration-corrected annular dark-field scanning transmission electron microscopy under strictly controlled low dose conditions. By combining the acquired experimental data with image simulations, the position of the small clusters within the individual pores of a metal-organic framework has been determined. The embedding of the Pt nanoparticles is confirmed by electron tomography, which shows a distinct ordering of the highly uniform Pt nanoparticles. The results show that atomic layer deposition is particularly well-suited for the deposition of individual nanoparticles inside MOF framework pores and that, upon proper regulation of the incident electron dose, annular dark-field scanning transmission electron microscopy is a powerful tool for the characterization of this type of materials at a local scale.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.474
Times cited: 11
DOI: 10.1002/ppsc.201500252
|
|
|
“Direct imaging of boron segregation at dislocations in B:diamond heteroepitaxial films”. Turner S, Idrissi H, Sartori AF, Korneychuck S, Lu Y-G, Verbeeck J, Schreck M, Van Tendeloo G, Nanoscale 8, 2212 (2016). http://doi.org/10.1039/c5nr07535a
Abstract: A thin film of heavily B-doped diamond has been grown epitaxially by microwave plasma chemical vapor deposition on an undoped diamond layer, on top of a Ir/YSZ/Si(001) substrate stack, to study the boron segregation and boron environment at the dislocations present in the film. The density and nature of the dislocations were investigated by conventional and weak-beam dark-field transmission electron microscopy techniques, revealing the presence of two types of dislocations: edge and mixed-type 45 degrees dislocations. The presence and distribution of B in the sample was studied using annular dark-field scanning transmission electron microscopy and spatially resolved electron energy-loss spectroscopy. Using these techniques, a segregation of B at the dislocations in the film is evidenced, which is shown to be intermittent along the dislocation. A single edge-type dislocation was selected to study the distribution of the boron surrounding the dislocation core. By imaging this defect at atomic resolution, the boron is revealed to segregate towards the tensile strain field surrounding the edge-type dislocations. An investigation of the fine structure of the B-K edge at the dislocation core shows that the boron is partially substitutionally incorporated into the diamond lattice and partially present in a lower coordination (sp(2)-like hybridization).
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 7.367
Times cited: 15
DOI: 10.1039/c5nr07535a
|
|
|
“Direct imaging of loaded metal-organic framework materials (metal@MOF-5)”. Turner S, Lebedev OI, Schroeder F, Fischer RA, Van Tendeloo G, Chemistry of materials 20, 5622 (2008). http://doi.org/10.1021/cm801165s
Abstract: We illustrate the potential of advanced transmission electron microscopy for the characterization of a new class of soft porous materials: metal@Zn4O(bdc)3 (metal@MOF-5; bdc = 1,4-benzenedicarboxylate). By combining several electron microscopy techniques (transmission electron microscopy (TEM), high-resolution transmission electron microscopy (HRTEM), electron diffraction (ED), high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM), and electron tomography) and by carefully reducing the electron dose to avoid beam damage, it is possible to simultaneously characterize the MOF-5 framework material and the loaded metal nanoparticles. We also demonstrate that electron tomography can be used to accurately determine the position and distribution of the particles within the MOF-5 framework. To demonstrate the implementation of these microscopy techniques and what kind of results can be expected, measurements on gas-phase-loaded metal−organic framework materials Ru@MOF-5 and Pd@MOF-5 are presented.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 112
DOI: 10.1021/cm801165s
|
|
|
“Direct nucleation of hexagonal boron nitride on diamond : crystalline properties of hBN nanowalls”. Hoang D-Q, Korneychuk S, Sankaran KJ, Pobedinskas P, Drijkoningen S, Turner S, Van Bael MK, Verbeeck J, Nicley SS, Haenen K, Acta materialia 127, 17 (2017). http://doi.org/10.1016/J.ACTAMAT2017.01.002
Abstract: Hexagonal boron nitride (hBN) nanowalls were deposited by unbalanced radio frequency sputtering on (100)-oriented silicon, nanocrystalline diamond films, and amorphous silicon nitride (Si3N4) membranes. The hBN nanowall structures were found to grow vertically with respect to the surface of all of the substrates. To provide further insight into the nucleation phase and possible lattice distortion of the deposited films, the structural properties of the different interfaces were characterized by transmission electron microscopy. For Si and Si3N4 substrates, turbostratic and amorphous BN phases form a clear transition zone between the substrate and the actual hBN phase of the bulk nanowalls. However, surprisingly, the presence of these phases was suppressed at the interface with a nanocrystalline diamond film, leading to a direct coupling of hBN with the diamond surface, independent of the vertical orientation of the diamond grain. To explain these observations, a growth mechanism is proposed in which the hydrogen terminated surface of the nanocrystalline diamond film leads to a rapid formation of the hBN phase during the initial stages of growth, contrary to the case of Si and Si3N4 substrates. (C) 2017 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 5.301
DOI: 10.1016/J.ACTAMAT2017.01.002
|
|
|
“Direct observation and structural characterization of natural and metal ion-exchanged HEU-type zeolites”. Filippousi M, Turner S, Katsikini M, Pinakidou F, Zamboulis D, Pavlidou E, Van Tendeloo G, Microporous and mesoporous materials: zeolites, clays, carbons and related materials 210, 185 (2015). http://doi.org/10.1016/j.micromeso.2015.01.043
Abstract: The atomic structure of natural HEU-type zeolite and two ion-exchanged variants of the zeolite, Ag+ (Ag-HEU) and Zn2+ (Zn-HEU) ion exchanged HEU-type zeolites, are investigated using advanced transmission electron microscopy techniques in combination with X-ray powder diffraction and X-ray absorption fine structure measurements. In both ion-exchanged materials, loading of the natural HEU zeolite is confirmed. Using low-voltage, aberration-corrected transmission electron microscopy at low-dose conditions, the local crystal structure of natural HEU-type zeolite is determined and the interaction of the ion-exchanged natural zeolites with the Ag+ and Zn2+ ions is studied. In the case of Ag-HEU, the presence of Ag+ ions and clusters at extra-framework sites as well as Ag nanoparticles has been confirmed. The Ag nanoparticles are preferentially positioned at the zeolite surface. For Zn-HEU, no large Zn(O) nanopartides are present, instead, the HEU channels are evidenced to be decorated by small Zn(O) clusters. (c) 2015 Elsevier Inc. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.615
Times cited: 5
DOI: 10.1016/j.micromeso.2015.01.043
|
|
|
“Direct observation of cation diffusion driven surface reconstruction at van der Waals gaps”. Cui W, Lin W, Lu W, Liu C, Gao Z, Ma H, Zhao W, Van Tendeloo G, Zhao W, Zhang Q, Sang X, Nature communications 14, 554 (2023). http://doi.org/10.1038/S41467-023-35972-9
Abstract: Weak interlayer van der Waals (vdW) bonding has significant impact on the surface/interface structure, electronic properties, and transport properties of vdW layered materials. Unraveling the complex atomistic dynamics and structural evolution at vdW surfaces is therefore critical for the design and synthesis of the next-generation vdW layered materials. Here, we show that Ge/Bi cation diffusion along the vdW gap in layered GeBi2Te4 (GBT) can be directly observed using in situ heating scanning transmission electron microscopy (STEM). The cation concentration variation during diffusion was correlated with the local Te-6 octahedron distortion based on a quantitative analysis of the atomic column intensity and position in time-elapsed STEM images. The in-plane cation diffusion leads to out-of-plane surface etching through complex structural evolutions involving the formation and propagation of a non-centrosymmetric GeTe2 triple layer surface reconstruction on fresh vdW surfaces, and GBT subsurface reconstruction from a septuple layer to a quintuple layer. Our results provide atomistic insight into the cation diffusion and surface reconstruction in vdW layered materials. Weak interlayer van der Waals (vdW) bonding has significant impact on the structure and properties of vdW layered materials. Here authors use in-situ aberration-corrected ADF-STEM for an atomistic insight into the cation diffusion in the vdW gaps and the etching of vdW surfaces at high temperatures.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
DOI: 10.1038/S41467-023-35972-9
|
|
|
“Direct observation of clusters in some FCC alloys by HREM”. De Meulenaere P, Van Tendeloo G, van Landuyt J, Icem 13, 447 (1994)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
|
|
|
“Direct observation of enhanced magnetism in individual size- and shape-selected 3d transition metal nanoparticles”. Kleibert A, Balan A, Yanes R, Derlet PM, Vaz CAF, Timm M, Fraile Rodríguez A, Béché, A, Verbeeck J, Dhaka RS, Radovic M, Nowak U, Nolting F, Physical review B 95, 195404 (2017). http://doi.org/10.1103/PhysRevB.95.195404
Abstract: Magnetic nanoparticles are critical building blocks for future technologies ranging from nanomedicine to spintronics. Many related applications require nanoparticles with tailored magnetic properties. However, despite significant efforts undertaken towards this goal, a broad and poorly understood dispersion of magnetic properties is reported, even within monodisperse samples of the canonical ferromagnetic 3d transition metals. We address this issue by investigating the magnetism of a large number of size- and shape-selected, individual nanoparticles of Fe, Co, and Ni using a unique set of complementary characterization techniques. At room temperature, only superparamagnetic behavior is observed in our experiments for all Ni nanoparticles within the investigated sizes, which range from 8 to 20 nm. However, Fe and Co nanoparticles can exist in two distinct magnetic states at any size in this range: (i) a superparamagnetic state, as expected from the bulk and surface anisotropies known for the respective materials and as observed for Ni, and (ii) a state with unexpected stable magnetization at room temperature. This striking state is assigned to significant modifications of the magnetic properties arising from metastable lattice defects in the core of the nanoparticles, as concluded by calculations and atomic structural characterization. Also related with the structural defects, we find that the magnetic state of Fe and Co nanoparticles can be tuned by thermal treatment enabling one to tailor their magnetic properties for applications. This paper demonstrates the importance of complementary single particle investigations for a better understanding of nanoparticle magnetism and for full exploration of their potential for applications.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 21
DOI: 10.1103/PhysRevB.95.195404
|
|
|
“Direct observation of ferrielectricity at ferroelastic domain boundaries in CaTiO3 by electron microscopy”. Van Aert S, Turner S, Delville R, Schryvers D, Van Tendeloo G, Salje EKH, Advanced materials 24, 523 (2012). http://doi.org/10.1002/adma.201103717
Abstract: High-resolution aberration-corrected transmission electron microscopy aided by statistical parameter estimation theory is used to quantify localized displacements at a (110) twin boundary in orthorhombic CaTiO3. The displacements are 36 pm for the Ti atoms and confined to a thin layer. This is the first direct observation of the generation of ferroelectricity by interfaces inside this material which opens the door for domain boundary engineering.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 19.791
Times cited: 150
DOI: 10.1002/adma.201103717
|
|
|
“Direct Observation of Ferroelectric Domain Walls in LiNbO3: Wall-Meanders, Kinks, and Local Electric Charges”. Gonnissen J, Batuk D, Nataf GF, Jones L, Abakumov AM, Van Aert S, Schryvers D, Salje EKH, Advanced functional materials 26, 7599 (2016). http://doi.org/10.1002/adfm.201603489
Abstract: Direct observations of the ferroelectric domain boundaries in LiNbO3 are performed using high-resolution high-angle annular dark field scanning transmission electron microscopy imaging, revealing a very narrow width of the domain wall between the 180° domains. The domain walls demonstrate local side-way meandering, which results in inclinations even when the overall wall orientation follows the ferroelectric polarization. These local meanders contain kinks with “head-to-head” and “tail-to-tail” dipolar configurations and are therefore locally charged. The charged meanders are confined to a few cation layers along the polarization direction and are separated by longer stretches of straight domain walls.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.124
Times cited: 23
DOI: 10.1002/adfm.201603489
|
|
|
“Direct observation of laser-induced crystallization of a-C : H films”. Nistor LC, van Landuyt J, Ralchenko VG, Kononenko TV, Obraztsova ED, Strelnitsky VE, Applied physics A : materials science &, processing 58, 137 (1994). http://doi.org/10.1007/BF00332170
Abstract: The post-growth modification of diamond-like amorphous hydrogenated carbon a-C:H films by laser treatment has been studied by transmission electron microscopy and Raman spectroscopy. a-C:H films grown on Si substrates by benzene decomposition in a rf glow discharge were irradiated with 15 ns pulses of a KrF-excimer laser with fluences in the ran e of E = 50-700 mJ/cm(2). At fluences below 100 mJ/cm(2) an increase in the number of graphitic clusters and in their ordering was evidenced from Raman spectra, while the film structure remained amorphous according to electron microscopy and electron diffraction observations. At higher fluences the appearance of diamond particles of 2-7 nm size, embedded into the lower crystallized graphitic matrix, was observed and simultaneously a progressive growth of graphite nanocrystals with dimensions from 2 nm to 4 nm was deduced from Raman measurements. The maximum thickness of the crystallized surface layer (approximate to 400 nm) and the degree of laser annealing are limited by the film ablation which starts at E > 250 mJ/cm(2). The laser-treated areas lose their chemical inertness. In particular, chemical etching in chromium acid becomes possible, which may be used for patterning the highly inert carbon films.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 73
DOI: 10.1007/BF00332170
|
|
|
“Direct observation of layer-stacking and oriented wrinkles in multilayer hexagonal boron nitride”. Chen L, Elibol K, Cai H, Jiang C, Shi W, Chen C, Wang HS, Wang X, Mu X, Li C, Watanabe K, Taniguchi T, Guo Y, Meyer JC, Wang H, 2d Materials 8, 024001 (2021). http://doi.org/10.1088/2053-1583/ABD41E
Abstract: Hexagonal boron nitride (h-BN) has long been recognized as an ideal substrate for electronic devices due to its dangling-bond-free surface, insulating nature and thermal/chemical stability. These properties of the h-BN multilayer are mainly determined by its lattice structure. Therefore, to analyse the lattice structure and orientation of h-BN crystals becomes important. Here, the stacking order and wrinkles of h-BN are investigated by transmission electron microscopy. It is experimentally confirmed that the layers in the h-BN flakes are arranged in the AA ' stacking. The wrinkles in a form of threefold network throughout the h-BN crystal are oriented along the armchair direction, and their formation mechanism was further explored by molecular dynamics simulations. Our findings provide a deep insight about the microstructure of h-BN and shed light on the structural design/electronic modulations of two-dimensional crystals.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.937
DOI: 10.1088/2053-1583/ABD41E
|
|
|
“Direct Observation of Luminescent Silver Clusters Confined in Faujasite Zeolites”. Altantzis T, Coutino-Gonzalez E, Baekelant W, Martinez GT, Abakumov AM, Van Tendeloo G, Roeffaers MBJ, Bals S, Hofkens J, ACS nano 10, 7604 (2016). http://doi.org/10.1021/acsnano.6b02834
Abstract: One of the ultimate goals in the study of metal clusters is the correlation between the atomic-scale organization and their physicochemical properties. However, direct observation of the atomic organization of such minuscule metal clusters is heavily hindered by radiation damage imposed by the different characterization techniques. We present direct evidence of the structural arrangement, at an atomic level, of luminescent silver species stabilized in faujasite (FAU) zeolites using aberration-corrected scanning transmission electron microscopy. Two different silver clusters were identified in Ag-FAU zeolites, a trinuclear silver species associated with green emission and a tetranuclear silver species related to yellow emission. By combining direct imaging with complementary information obtained from X-ray powder diffraction and Rietveld analysis, we were able to elucidate the main differences at an atomic scale between luminescent (heat-treated) and nonluminescent (cation-exchanged) Ag-FAU zeolites. It is expected that such insights will trigger the directed synthesis of functional metal nanocluster-zeolite composites with tailored luminescent properties.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 13.942
Times cited: 57
DOI: 10.1021/acsnano.6b02834
|
|
|
“Direct observation of nanometer-scale pinning sites in (Nd0.33Eu0.20Gd0.47)Ba2Cu3O7-\delta single crystals”. Das P, Koblischka MR, Turner S, Van Tendeloo G, Wolf T, Jirsa M, Hartmann U, Europhysics letters 83, 37005 (2008). http://doi.org/10.1209/0295-5075/83/37005
Abstract: We report on the observation of self-organized stripe-like structures on the as-grown surface and in the bulk of (Nd,Eu,Gd)Ba2Cu3Oy single crystals. The periodicity of the stripes on the surface lies between 500800 nm. These are possibly the growth steps of the crystal. Transmission electron microscopy investigations revealed stripes of periodicity in the range of 2040 nm in the bulk. From electron back scattered diffraction investigations, no crystallographic misorientation due to the nanostripes has been found. Scanning tunneling spectroscopic experiments revealed nonsuperconducting regions, running along twin directions, which presumably constitute strong pinning sites.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.957
Times cited: 5
DOI: 10.1209/0295-5075/83/37005
|
|
|
“Direct operando visualization of metal support interactions induced by hydrogen spillover during CO₂, hydrogenation”. Jenkinson K, Spadaro MC, Golovanova V, Andreu T, Morante JR, Arbiol J, Bals S, Advanced materials 35, 2306447 (2023). http://doi.org/10.1002/ADMA.202306447
Abstract: The understanding of catalyst active sites is a fundamental challenge for the future rational design of optimized and bespoke catalysts. For instance, the partial reduction of Ce4+ surface sites to Ce3+ and the formation of oxygen vacancies are critical for CO2 hydrogenation, CO oxidation, and the water gas shift reaction. Furthermore, metal nanoparticles, the reducible support, and metal support interactions are prone to evolve under reaction conditions; therefore a catalyst structure must be characterized under operando conditions to identify active states and deduce structure-activity relationships. In the present work, temperature-induced morphological and chemical changes in Ni nanoparticle-decorated mesoporous CeO2 by means of in situ quantitative multimode electron tomography and in situ heating electron energy loss spectroscopy, respectively, are investigated. Moreover, operando electron energy loss spectroscopy is employed using a windowed gas cell and reveals the role of Ni-induced hydrogen spillover on active Ce3+ site formation and enhancement of the overall catalytic performance.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
DOI: 10.1002/ADMA.202306447
|
|
|
“Direct room-temperature synthesis of methyl-functionalized Ti-MCM-41 nanoparticles and their catalytic performance in epoxidation”. Lin K, Pescarmona PP, Houthoofd K, Liang D, Van Tendeloo G, Jacobs PA, Journal of catalysis 263, 75 (2009). http://doi.org/10.1016/j.jcat.2009.01.013
Abstract: Methyl-functionalized Ti-MCM-41 nanoparticles with a size of 80 to 160 nm (Me-Ti-MCM-41 NP) were directly prepared via a dilute solution route by the co-condensation of tetraethoxysilane and methylalkoxysilanes in sodium hydroxide medium at room temperature. The characterization results showed the existence of ordered hexagonal mesoporous structure and tetrahedral Ti species in the nanoparticles. In the epoxidation of cyclohexene with tert-butyl hydroperoxide and aqueous H2O2, Me-Ti-MCM-41 NP samples displayed higher turnover frequencies (TOFs) for cyclohexene and initial reaction rates compared to Ti-MCM-41 and methyl-functionalized Ti-MCM-41 with normal particle size and to non-functionalized Ti-MCM-41 nanoparticles. Simultaneously, a higher selectivity for cyclohexene epoxide was observed in the case of aqueous H2O2, suggesting that the hydrolysis of cyclohexene epoxide with water is reduced on Me-Ti-MCM-41 NP samples. The improved catalytic behavior of Me-Ti-MCM-41 NP is discussed both in terms of the nanosize and methylation of the surface of the catalyst particles. The regeneration of Me-Ti-MCM-41 NP with tert-butyl hydroperoxide solution was evaluated via washing and calcination approaches.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.844
Times cited: 89
DOI: 10.1016/j.jcat.2009.01.013
|
|
|
“Direct Solar Energy-Mediated Synthesis of Tertiary Benzylic Alcohols Using a Metal-Free Heterogeneous Photocatalyst”. Zhang Y, Qin S, Claes N, Schilling W, Sahoo PK, Ching HYV, Jaworski A, Lemière F, Slabon A, Van Doorslaer S, Bals S, Das S, ACS Sustainable Chemistry and Engineering 10, 530 (2022). http://doi.org/10.1021/acssuschemeng.1c07026
Abstract: Direct hydroxylation via the functionalization of tertiary benzylic C(sp3)-H bond is of great significance for obtaining tertiary alcohols which find wide applications in pharmaceuticals as well as in fine chemical industries. However, current synthetic procedures use toxic reagents and therefore, the development of a sustainable strategy for the synthesis of tertiary benzyl alcohols is highly desirable. To solve this problem, herein, we report a metal-free
heterogeneous photocatalyst to synthesize the hydroxylated products using oxygen as the key reagent. Various benzylic substrates were employed into our mild reaction conditions to afford the desirable products in good to excellent yields. More importantly, gram-scale reaction was achieved via harvesting direct solar energy and exhibited high quantity of the product. The high stability of the catalyst was proved via recycling the catalyst and spectroscopic analyses. Finally, a possible mechanism was proposed based on the EPR and other experimental
evidence.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Organic synthesis (ORSY)
Impact Factor: 8.4
Times cited: 24
DOI: 10.1021/acssuschemeng.1c07026
|
|
|
“Direct space structure solution from precession electron diffraction data: resolving heavy and light scatterers in Pb13Mn9O25”. Hadermann J, Abakumov AM, Tsirlin AA, Filonenko VP, Gonnissen J, Tan H, Verbeeck J, Gemmi M, Antipov EV, Rosner H, Ultramicroscopy 110, 881 (2010). http://doi.org/10.1016/j.ultramic.2010.03.012
Abstract: The crystal structure of a novel compound Pb13Mn9O25 has been determined through a direct space structure solution with a Monte-Carlo-based global optimization using precession electron diffraction data (a=14.177(3) Å, c=3.9320(7) Å, SG P4/m, RF=0.239) and compositional information obtained from energy dispersive X-ray analysis and electron energy loss spectroscopy. This allowed to obtain a reliable structural model even despite the simultaneous presence of both heavy (Pb) and light (O) scattering elements and to validate the accuracy of the electron diffraction-based structure refinement. This provides an important benchmark for further studies of complex structural problems with electron diffraction techniques. Pb13Mn9O25 has an anion- and cation-deficient perovskite-based structure with the A-positions filled by the Pb atoms and 9/13 of the B positions filled by the Mn atoms in an ordered manner. MnO6 octahedra and MnO5 tetragonal pyramids form a network by sharing common corners. Tunnels are formed in the network due to an ordered arrangement of vacancies at the B-sublattice. These tunnels provide sufficient space for localization of the lone 6s2 electron pairs of the Pb2+ cations, suggested as the driving force for the structural difference between Pb13Mn9O25 and the manganites of alkali-earth elements with similar compositions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.843
Times cited: 24
DOI: 10.1016/j.ultramic.2010.03.012
|
|
|
“Direct structural and spectroscopic investigation of ultrathin films of tetragonal CuO: Six-fold coordinated copper”. Samal D, Tan H, Takamura Y, Siemons W, Verbeeck J, Van Tendeloo G, Arenholz E, Jenkins CA, Rijnders G, Koster G, Europhysics letters 105, 17003 (2014). http://doi.org/10.1209/0295-5075/105/17003
Abstract: Unlike other 3d transition metal monoxides (MnO, FeO, CoO, and NiO), CuO is found in a low-symmetry distorted monoclinic structure rather than the rocksalt structure. We report here of the growth of ultrathin CuO films on SrTiO3 substrates; scanning transmission electron microscopy was used to show the stabilization of a tetragonal rocksalt structure with an elongated c-axis such that c/a similar to 1.34 and the Cu-O-Cu bond angle similar to 180 degrees, pointing to metastable six-fold coordinated Cu. X-ray absorption spectroscopy demonstrates that the hole at the Cu site for the CuO is localized in 3d(x2-y2) orbital unlike the well-studied monoclinic CuO phase. The experimental confirmation of the tetragonal structure of CuO opens up new avenues to explore electronic and magnetic properties of six-fold coordinated Cu. Copyright (C) EPLA, 2014
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.957
Times cited: 15
DOI: 10.1209/0295-5075/105/17003
|
|
|
“Direct structure inversion from exit waves : part 2 : a practical example”. Wang A, Chen FR, Van Aert S, van Dyck D, Ultramicroscopy 116, 77 (2012). http://doi.org/10.1016/j.ultramic.2012.03.011
Abstract: This paper is the second part of a two-part paper on direct structure inversion from exit waves. In the first part, a method has been proposed to quantitatively determine structure parameters with atomic resolution such as atom column positions, surface profile and the number of atoms in the atom columns. In this part, the theory will be demonstrated by means of a Au[110] exit wave reconstructed from a set of focal-series images. The procedures to analyze the experimentally reconstructed exit wave in terms of quantitative structure information are described in detail.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 2.843
Times cited: 8
DOI: 10.1016/j.ultramic.2012.03.011
|
|
|
“Direct structure inversion from exit waves: part 1: theory and simulations”. Wang A, Chen FR, Van Aert S, van Dyck D, Ultramicroscopy 110, 527 (2010). http://doi.org/10.1016/j.ultramic.2009.11.024
Abstract: In order to interpret the amplitude and phase of the exit wave in terms of mass and position of the atoms, one has to invert the dynamic scattering of the electrons in the object so as to obtain a starting structure which can then be used as a seed for further quantitative structure refinement. This is especially challenging in case of a zone axis condition when the interaction of the electrons with the atom column is very strong. Based on the channelling theory we will show that the channelling map not only yields a circle on the Argand plot but also a circular defocus curve for every column. The former gives the number of atoms in each column, while the latter provides the defocus value for each column, which reveals the surface roughness at the exit plane with single atom sensitivity.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 2.843
Times cited: 25
DOI: 10.1016/j.ultramic.2009.11.024
|
|
|
“Direct synthesis of antimicrobial coatings based on tailored bi-elemental nanoparticles”. Benetti G, Cavaliere E, Canteri A, Landini G, Rossolini GM, Pallecchi L, Chiodi M, Van Bael MJ, Winckelmans N, Bals S, Gavioli L, APL materials 5, 036105 (2017). http://doi.org/10.1063/1.4978772
Abstract: Ultrathin coatings based on bi-elemental nanoparticles (NPs) are very promising to limit the surface-related spread of bacterial pathogens, particularly in nosocomial environments. However, tailoring the synthesis, composition, adhesion to substrate, and antimicrobial spectrum of the coating is an open challenge. Herein, we report on a radically new nanostructured coating, obtained by a one-step gas-phase deposition technique, and composed of bi-elemental Janus type Ag/Ti NPs. The NPs are characterized by a cluster-in-cluster mixing phase with metallic Ag nano-crystals embedded in amorphous TiO2 and present a promising antimicrobial activity including also multidrug resistant strains. We demonstrate the flexibility of the method to tune the embedded Ag nano-crystals dimension, the total relative composition of the coating, and the substrate type, opening the possibility of tailoring the dimension, composition, antimicrobial spectrum, and other physical/chemical properties of such multi-elemental systems. This work is expected to significantly spread the range of applications of NPs coatings, not only as an effective tool in the prevention of healthcare-associated infections but also in other technologically relevant fields like sensors or nano-/micro joining.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.335
Times cited: 21
DOI: 10.1063/1.4978772
|
|
|
“Direct visualization of atomic-scale heterogeneous structure dynamics in MnO₂, nanowires”. Peng X, Peng H, Zhao K, Zhang Y, Xia F, Lyu J, Van Tendeloo G, Sun C, Wu J, Acs Applied Materials &, Interfaces 13, 33644 (2021). http://doi.org/10.1021/ACSAMI.1C07929
Abstract: Manganese oxides are attracting great interest owing to their rich polymorphism and multiple valent states, which give rise to a wide range of applications in catalysis, capacitors, ion batteries, and so forth. Most of their functionalities are connected to transitions among the various polymorphisms and Mn valences. However, their atomic-scale dynamics is still a great challenge. Herein, we discovered a strong heterogeneity in the crystalline structure and defects, as well as in the Mn valence state. The transitions are studied by in situ transmission electron microscopy (TEM), and they involve a complex ordering of [MnO6] octahedra as the basic building tunnels. MnO2 nanowires synthesized using solution-based hydrothermal methods usually exhibit a large number of multiple polymorphism impurities with different tunnel sizes. Upon heating, MnO2 nanowires undergo a series of stoichiometric polymorphism changes, followed by oxygen release toward an oxygen-deficient spinel and rock-salt phase. The impurity polymorphism exhibits an abnormally high stability with interesting small-large-small tunnel size transition, which is attributed to a preferential stabilizer (K+) concentration, as well as a strong competition of kinetics and thermodynamics. Our results unveil the complicated intergrowth of polymorphism impurities in MnO2, which provide insights into the heterogeneous kinetics, thermodynamics, and transport properties of the tunnel-based building blocks.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 7.504
DOI: 10.1021/ACSAMI.1C07929
|
|
|
“Direct visualization of boron dopant distribution and coordination in individual chemical vapor deposition nanocrystalline B-doped diamond grains”. Lu Y-G, Turner S, Verbeeck J, Janssens SD, Wagner P, Haenen K, Van Tendeloo G, Applied physics letters 101, 041907 (2012). http://doi.org/10.1063/1.4738885
Abstract: The boron dopant distribution in individual heavily boron-doped nanocrystalline diamond film grains, with sizes ranging from 100 to 350nm in diameter, has been studied using a combination of high resolution annular dark field scanning transmission electron microscopy and spatially resolved electron energy-loss spectroscopy. Using these tools, the boron distribution and local boron coordination have been determined. Quantification results reveal embedding of B dopants in the diamond lattice, and a preferential enrichment of boron at defective areas and twin boundaries. Coordination mapping reveals a distinct difference in coordination of the B dopants in “pristine” diamond areas and in defective regions. (C) 2012 American Institute of Physics. [http://dx.doi.org/10.1063/1.4738885]
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 59
DOI: 10.1063/1.4738885
|
|