“Barrier efficiency of sponge-like La2Zr2O7 buffer layers for YBCO-coated conductors”. Molina L, Tan H, Biermans E, Batenburg KJ, Verbeeck J, Bals S, Van Tendeloo G, Superconductor science and technology 24, 065019 (2011). http://doi.org/10.1088/0953-2048/24/6/065019
Abstract: Solution derived La2Zr2O7 films have drawn much attention for potential applications as thermal barriers or low-cost buffer layers for coated conductor technology. Annealing and coating parameters strongly affect the microstructure of La2Zr2O7, but different film processing methods can yield similar microstructural features such as nanovoids and nanometer-sized La2Zr2O7 grains. Nanoporosity is a typical feature found in such films and the implications for the functionality of the films are investigated by a combination of scanning transmission electron microscopy (STEM), electron energy-loss spectroscopy (EELS) and quantitative electron tomography. Chemical solution based La2Zr2O7 films deposited on flexible Ni5 at.%W substrates with a {100}lang001rang biaxial texture were prepared for an in-depth characterization. A sponge-like structure composed of nanometer-sized voids is revealed by high-angle annular dark-field scanning transmission electron microscopy in combination with electron tomography. A three-dimensional quantification of nanovoids in the La2Zr2O7 film is obtained on a local scale. Mostly non-interconnected highly faceted nanovoids compromise more than one-fifth of the investigated sample volume. The diffusion barrier efficiency of a 170 nm thick La2Zr2O7 film is investigated by STEM-EELS, yielding a 1.8 ± 0.2 nm oxide layer beyond which no significant nickel diffusion can be detected and intermixing is observed. This is of particular significance for the functionality of YBa2Cu3O7 − δ coated conductor architectures based on solution derived La2Zr2O7 films as diffusion barriers.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 2.878
Times cited: 31
DOI: 10.1088/0953-2048/24/6/065019
|
|
|
“Catalytic and molecular separation properties of Zeogrids and Zeotiles”. Martens JA, Thybaut JW, Denayer JFM, Sree SP, Aerts A, Reyniers M-F, van Speybroeck V, Waroquier M, Buekenhoudt A, Vankelecom I, Buijs W, Persoons J, Baron GV, Bals S, Van Tendeloo G, Marin GB, Jacobs PA, Kirschhock CEA, Catalysis today 168, 17 (2011). http://doi.org/10.1016/j.cattod.2011.01.036
Abstract: Zeogrids and Zeotiles are hierarchical materials built from assembled MFI zeolite precursor units. Permanent secondary porosity in these materials is obtained through self assembly of nanoparticles encountered in MFI zeolite synthesis in the presence of supramolecular templates. Hereon, the aggregated species are termed nanoslabs. Zeogrids are layered materials with lateral spacings between nanoslabs creating galleries qualifying as supermicropores. Zeotiles present a diversity of tridimensional nanoslab assemblies with mesopores. Zeotile-1, -4 and -6 are hexagonal mesostructures. Zeotile-1 has triangular and hexagonal channels; Zeotile-4 has hexagonal channels interconnected via slits. Zeotile-2 has a cubic structure with gyroid type mesoporosity. The behavior of Zeogrids and Zeotiles in adsorption, membrane and chromatographic separation and catalysis has been characterized and compared with zeolites and mesoporous materials derived from unstructured silica sources. Shape selectivity was detected via adsorption of n- and iso-alkanes. The mesoporosity of Zeotiles can be exploited in chromatographic separation of biomolecules. Zeotiles present attractive separation properties relevant to CO2 sequestration. Because of its facile synthesis procedure without hydrothermal steps Zeogrid is convenient for membrane synthesis. The performance of Zeogrid membrane in gas separation, nanofiltration and pervaporation is reported. In the Beckmann rearrangement of cyclohexanone oxime Zeogrids and Zeotiles display a catalytic activity characteristic of silicalite-1 zeolites. Introduction of acidity and redox catalytic activity can be achieved via incorporation of Al and Ti atoms in the nanoslabs during synthesis. Zeogrids are active in hydrocracking, catalytic cracking, alkylation and epoxidation reactions. Zeogrids and Zeotiles often behave differently from ordered mesoporous materials as well as from zeolites and present a valuable extension of the family of hierarchical silicate based materials.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.636
Times cited: 13
DOI: 10.1016/j.cattod.2011.01.036
|
|
|
“Cation ordering within the perovskite block of a six-layer Ruddlesden-Popper oxide from layer-by-layer growth artificial interfaces in complex unit cells”. Yan L, Niu HJ, Duong GV, Suchomel MR, Bacsa J, Chalker PR, Hadermann J, Van Tendeloo G, Rosseinsky MJ, Chemical science 2, 261 (2011). http://doi.org/10.1039/c0sc00482k
Abstract: The (AO)(ABO3)n Ruddlesden-Popper structure is an archetypal complex oxide consisting of two distinct structural units, an (AO) rock salt layer separating an n-octahedra thick perovskite block. Conventional high-temperature oxide synthesis methods cannot access members with n > 3, but low-temperature layer-by-layer thin film methods allow the preparation of materials with thicker perovskite blocks, exploiting high surface mobility and lattice matching with the substrate. This paper describes the growth of an n = 6 member CaO[(CSMO)2(LCMO)2 (CSMO)2] in which the six unit cell perovskite block is sub-divided into two central La0.67Ca0.33MnO3 (LCMO) and two terminal Ca0.85Sm0.15MnO3 (CSMO) layers to allow stabilization of the rock salt layer and variation of the transition metal charge.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 8.668
Times cited: 16
DOI: 10.1039/c0sc00482k
|
|
|
d' Hondt H (2011) Characterization of anion deficient perovskites. Antwerpen
Keywords: Doctoral thesis; Electron microscopy for materials research (EMAT)
|
|
|
“Characterization of NbC and (Nb, Ti)N nanoprecipitates in TRIP assisted multiphase steels”. Tirumalasetty GK, van Huis MA, Fang CM, Xu Q, Tichelaar FD, Hanlon DN, Sietsma J, Zandbergen HW, Acta materialia 59, 7406 (2011). http://doi.org/10.1016/j.actamat.2011.08.012
Abstract: Multiphase steels utilising composite strengthening may be further strengthened via grain refinement or precipitation by the addition of microalloying elements. In this study a Nb microalloyed steel comprising martensite, bainite and retained austenite has been studied. By means of transmission electron microscopy (TEM) we have investigated the size distribution and the structural properties of (Nb, Ti)N and NbC precipitates, their occurrence in the various steel phases, and their relationship with the Fe matrix. (Nb, Ti)N precipitates were found in ferrite, martensite, and bainite, while NbC precipitates were found only in ferrite. All NbC precipitates were found to be small (520 nm in size) and to have a face centred cubic (fcc) crystal structure with lattice parameter a = 4.36 ± 0.05 Å. In contrast, the (Nb, Ti)N precipitates were found to have a broader size range (5150 nm) and to have a fcc crystal structure with lattice parameter a = 8.09 ± 0.05 Å. While the NbC precipitates were found to be randomly oriented, the (Nb, Ti)N precipitates have a well-defined NishiyamaWasserman orientation relationship with the ferrite matrix. An analysis of the lattice mismatch suggests that the latter precipitates have a high potential for effective strengthening. Density functional theory calculations were performed for various stoichiometries of NbCx and NbxTiyNz phases and the comparison with experimental data indicates that both the carbides and nitrides are deficient in C and N content.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.301
Times cited: 58
DOI: 10.1016/j.actamat.2011.08.012
|
|
|
“The chemical vapor infiltration of exfoliated graphite to produce carbon/carbon composites”. Tikhomirov AS, Sorokina NE, Shornikova ON, Morozov VA, Van Tendeloo G, Avdeev VV, Carbon 49, 147 (2011). http://doi.org/10.1016/j.carbon.2010.08.054
Abstract: Chemical vapor infiltration was used for the production of carbon/carbon composites based on exfoliated graphite and pyrolytic carbon Two different exfoliated graphites compacted to densities of 0 05-0 4 g/cm(3) were used as a preform The influence of the synthesis conditions (temperature, pressure, time etc) on the degree of infiltration, the pyrolytic carbon morphology and the C/C composite characteristics was examined using Raman spectroscopy, scanning electron microscopy and low-temperature nitrogen adsorption (C) 2010 Elsevier Ltd All rights reserved
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.337
Times cited: 7
DOI: 10.1016/j.carbon.2010.08.054
|
|
|
“Community structure and feeding preference of nematodes associated with methane seepage at the Darwin mud volcano (Gulf of Cádiz)”. Pape E, Bezerra TN, Vanneste H, Heeschen K, Moodley L, Leroux F, van Breugel P, Vanreusel A, Marine ecology progress series 438, 71 (2011). http://doi.org/10.3354/meps09278
Abstract: We sampled the Darwin mud volcano (MV) for meiofaunal community and trophic structure in relation to pore-water geochemistry along a 10 m transect from a seep site on the rim of the crater towards the MV slope. Pore-water profiles indicated considerable variation in upward methane (CH4) flow among sediment cores taken along the transect, with highest flux in the seep sediment core, gradually decreasing along the transect, to no CH4 flux in the core taken at a 5 m distance. Low sulphate concentrations and high levels of total alkalinity and sulphide (H2S) suggested that anaerobic oxidation of methane (AOM) occurred close to the sediment surface in the seep sediment core. High H2S levels had a genus- and species-specific impact on meiofaunal densities. Nematode genus composition varied gradually between sediment cores, with the genus Sabatieria dominating almost all sediment cores. However, genus diversity increased with increasing distance from the seep site. These limited data suggest that the community structure of seep meiofauna is highly dependent on local (a)biotic habitat characteristics, and a typical seep meiofaunal community cannot be delineated. Stable isotope values suggested the nematode diet up to 10 m from the seep site included thiotrophic carbon. The thicker hemipelagic sediment layer (photosynthetic carbon), the increased trophic diversity, and the heavier nematode δ13C farther from the seep site suggest a decrease in thiotrophy and an increase in photosynthetic carbon in the nematode diet.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.292
Times cited: 18
DOI: 10.3354/meps09278
|
|
|
“Compositional characterization of nickel silicides by HAADF-STEM imaging”. Verleysen E, Bender H, Richard O, Schryvers D, Vandervorst W, Journal of materials science 46, 2001 (2011). http://doi.org/10.1007/s10853-010-5191-z
Abstract: A methodology for the quantitative compositional characterization of nickel silicides by high angle annular dark field scanning transmission electron microscopy (HAADF-STEM) imaging is presented. HAADF-STEM images of a set of nickel silicide reference samples Ni3Si, Ni31Si12, Ni2Si, NiSi and NiSi2 are taken at identical experimental conditions. The correlation between sample thickness and HAADF-STEM intensity is discussed. In order to quantify the relationship between the experimental Z-contrast intensities and the composition of the analysed layers, the ratio of the HAADF-STEM intensity to the sample thickness or to the intensity of the silicon substrate is determined for each nickel silicide reference sample. Diffraction contrast is still detected on the HAADF-STEM images, even though the detector is set at the largest possible detection angle. The influence on the quantification results of intensity fluctuations caused by diffraction contrast and channelling is examined. The methodology is applied to FUSI gate devices and to horizontal TFET devices with different nickel silicides formed on source, gate and drain. It is shown that, if the elements which are present are known, this methodology allows a fast quantitative 2-dimensional compositional analysis.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.599
Times cited: 1
DOI: 10.1007/s10853-010-5191-z
|
|
|
“A comprehensive modelling approach for the neutral atmospheric boundary layer : consistent inflow conditions, wall function and turbulence model”. Parente A, Gorlé, C, van Beeck J, Benocci C, Boundary-layer meteorology 140, 411 (2011). http://doi.org/10.1007/s10546-011-9621-5
Abstract: We report on a novel approach for the Reynolds-averaged Navier-Stokes (RANS) modelling of the neutral atmospheric boundary layer (ABL), using the standard k− turbulence model. A new inlet condition for turbulent kinetic energy is analytically derived from the solution of the k− model transport equations, resulting in a consistent set of fully developed inlet conditions for the neutral ABL. A modification of the standard k− model is also employed to ensure consistency between the inlet conditions and the turbulence model. In particular, the turbulence model constant C μ is generalized as a location-dependent parameter, and a source term is introduced in the transport equation for the turbulent dissipation rate. The application of the proposed methodology to cases involving obstacles in the flow is made possible through the implementation of an algorithm, which automatically switches the turbulence model formulation when going from the region where the ABL is undisturbed to the region directly affected by the building. Finally, the model is completed with a slightly modified version of the Richards and Hoxey rough-wall boundary condition. The methodology is implemented and tested in the commercial code Ansys Fluent 12.1. Results are presented for a neutral boundary layer over flat terrain and for the flow around a single building immersed in an ABL.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.573
Times cited: 54
DOI: 10.1007/s10546-011-9621-5
|
|
|
“Crystal fields, disorder, and antiferromagnetic short-range order in Yb0.24Sn0.76Ru”. Klimczuk T, Wang CH, Lawrence JM, Xu Q, Durakiewicz T, Ronning F, Llobet A, Trouw F, Kurita N, Tokiwa Y, Lee Ho, Booth CH, Gardner JS, Bauer ED, Joyce JJ, Zandbergen HW, Movshovich R, Cava RJ, Thompson JD;, Physical review : B : condensed matter and materials physics 84, 075152 (2011). http://doi.org/10.1103/PhysRevB.84.075152
Abstract: We report extensive measurements on a new compound (Yb0.24Sn0.76)Ru that crystallizes in the cubic CsCl structure. Valence-band photoemission (PES) and L3 x-ray absorption show no divalent component in the 4f configuration of Yb. Inelastic neutron scattering (INS) indicates that the eight-fold degenerate J-multiplet of Yb3+ is split by the crystalline electric field (CEF) into a Γ7-doublet ground state and a Γ8 quartet at an excitation energy 20 meV. The magnetic susceptibility can be fit very well by this CEF scheme under the assumption that a Γ6-excited state resides at 32 meV; however, the Γ8/Γ6 transition expected at 12 meV was not observed in the INS. The resistivity follows a Bloch-Grüneisen law shunted by a parallel resistor, as is typical of systems subject to phonon scattering with no apparent magnetic scattering. All of these properties can be understood as representing simple local moment behavior of the trivalent Yb ion. At 1 K there is a peak in specific heat that is too broad to represent a magnetic-phase transition, consistent with absence of magnetic reflections in neutron diffraction. On the other hand this peak also is too narrow to represent the Kondo effect in the Γ7-doublet ground state. On the basis of the field dependence of the specific heat, we argue that antiferromagnetic (AF) short-range order (SRO) (possibly coexisting with Kondo physics) occurs at low temperatures. The long-range magnetic order is suppressed because the Yb site occupancy is below the percolation threshold for this disordered compound.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 8
DOI: 10.1103/PhysRevB.84.075152
|
|
|
“Crystal growth of CsCl-type Yb0.24Sn0.76Ru”. Klimczuk T, Wang CH, Xu Q, Lawrence J, Durakiewicz T, Ronning F, Llobet A, Bauer ED, Griveau J-C, Sadowski W, Zandbergen HW, Thompson JD, Cava RJ, Journal of crystal growth 318, 1005 (2011). http://doi.org/10.1016/j.jcrysgro.2010.10.045
Abstract: The YbRuSn ternary system was investigated and a new material, Yb0.24Sn0.76Ru, with a simple cubic crystal structure, was discovered. Yb0.24Sn0.76Ru has a smaller lattice parameter a=3.217(4) Å, than its isostructural YbRu analogue (a=3.360 Å). Both X-ray diffraction and electron microscopy techniques were used to refine the crystal structure of Yb0.24Sn0.76Ru. It was found that a new compound forms in the CsCl structure, with Ru on the 1a site and a (Yb, Sn) mixture on site 1b. The XRD Rietveld analysis provides the occupation of Yb equal to 0.24, in agreement with the single crystal nano-electron diffraction refinement, which gives the occupation 0.21.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.751
Times cited: 1
DOI: 10.1016/j.jcrysgro.2010.10.045
|
|
|
“Crystallographic and magnetic characterisation of the brownmillerite Sr2Co2O5”. Sullivan E, Hadermann J, Greaves C, Journal of solid state chemistry 184, 649 (2011). http://doi.org/10.1016/j.jssc.2011.01.026
Abstract: Sr2Co2O5 with the perovskite-related brownmillerite structure has been synthesised via quenching, with the orthorhombic unit cell parameters a=5.4639(3) Å, b=15.6486(8) Å and c=5.5667(3) Å based on refinement of neutron powder diffraction data collected at 4 K. Electron microscopy revealed LRLR-intralayer ordering of chain orientations, which require a doubling of the unit cell along the c-parameter, consistent with the assignment of the space group Pcmb. However, on the length scale pertinent to NPD, no long-range order is observed and the disordered space group Imma appears more appropriate. The magnetic structure corresponds to G-type order with a moment of 3.00(4) μB directed along [1 0 0].
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 19
DOI: 10.1016/j.jssc.2011.01.026
|
|
|
“A cyclic catalyst pretreatment in CO2 for high yield production of Carbon nanofibers with narrow diameter distribution”. Corthals S, van Noyen J, Liang D, Ke X, Van Tendeloo G, Jacobs P, Sels B, Catalysis letters 141, 1621 (2011). http://doi.org/10.1007/s10562-011-0690-3
Abstract: This paper presents a cyclic catalyst pretreatment process to improve the CNF yield with narrow size distribution by sequentially feeding the CVD reactor with CH4/CO2 mixtures (carbon deposition) and CO2 (carbon removal) prior to the actual growth process. A mechanism based on a break-up of large Ni particles tentatively explains the beneficial effect of the cyclic carbon deposition/removal CVD procedure.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.799
Times cited: 1
DOI: 10.1007/s10562-011-0690-3
|
|
|
“Degradation process of lead chromate in paintings by Vincent van Gogh studied by means of synchrotron X-ray spectromicroscopy and related methods : 1 : artificially aged model samples”. Monico L, van der Snickt G, Janssens K, de Nolf W, Miliani C, Verbeeck J, Tian H, Tan H, Dik J, Radepont M, Cotte M, Analytical chemistry 83, 1214 (2011). http://doi.org/10.1021/ac102424h
Abstract: On several paintings by artists of the end of the 19th century and the beginning of the 20th Century a darkening of the original yellow areas, painted with the chrome yellow pigment (PbCrO4, PbCrO4·xPbSO4, or PbCrO4·xPbO) is observed. The most famous of these are the various Sunflowers paintings Vincent van Gogh made during his career. In the first part of this work, we attempt to elucidate the degradation process of chrome yellow by studying artificially aged model samples. In view of the very thin (1−3 μm) alteration layers that are formed, high lateral resolution spectroscopic methods such as microscopic X-ray absorption near edge (μ-XANES), X-ray fluorescence spectrometry (μ-XRF), and electron energy loss spectrometry (EELS) were employed. Some of these use synchrotron radiation (SR). Additionally, microscopic SR X-ray diffraction (SR μ-XRD), μ-Raman, and mid-FTIR spectroscopy were employed to completely characterize the samples. The formation of Cr(III) compounds at the surface of the chrome yellow paint layers is particularly observed in one aged model sample taken from a historic paint tube (ca. 1914). About two-thirds of the chromium that is present at the surface has reduced from the hexavalent to the trivalent state. The EELS and μ-XANES spectra are consistent with the presence of Cr2O3·2H2O (viridian). Moreover, as demonstrated by μ-XANES, the presence of another Cr(III) compound, such as either Cr2(SO4)3·H2O or (CH3CO2)7Cr3(OH)2 [chromium(III) acetate hydroxide], is likely.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 6.32
Times cited: 113
DOI: 10.1021/ac102424h
|
|
|
“Design of Ru-zeolites for hydrogen-free production of conjugated linoleic acid”. Philippaerts A, Goossens S, Vermandel W, Tromp M, Turner S, Geboers J, Van Tendeloo G, Jacobs PA, Sels BF, Chemsuschem 4, 757 (2011). http://doi.org/10.1002/cssc.201100015
Abstract: While conjugated vegetable oils are currently used as additives in the drying agents of oils and paints, they are also attractive molecules for making bio-plastics. Moreover, conjugated oils will soon be accepted as nutritional additives for functional food products. While current manufacture of conjugated vegetable oils or conjugated linoleic acids (CLAs) uses a homogeneous base as isomerisation catalyst, a heterogeneous alternative is not available today. This contribution presents the direct production of CLAs over Ru supported on different zeolites, varying in topology (ZSM-5, BETA, Y), Si/Al ratio and countercation (H+, Na+, Cs+). Ru/Cs-USY, with a Si/Al ratio of 40, was identified as the most active and selective catalyst for isomerisation of methyl linoleate (cis-9,cis-12 (C18:2)) to CLA at 165 °C. Interestingly, no hydrogen pre-treatment of the catalyst or addition of hydrogen donors is required to achieve industrially relevant isomerisation productivities, namely, 0.7 g of CLA per litre of solvent per minute. Moreover, the biologically most active CLA isomers, namely, cis-9,trans-11, trans-10,cis-12 and trans-9,trans-11, were the main products, especially at low catalyst concentrations. Ex situ physicochemical characterisation with CO chemisorption, extended X-ray absorption fine structure measurements, transmission electron microscopy analysis, and temperature-programmed oxidation reveals the presence of highly dispersed RuO2 species in Ru/Cs-USY(40).
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 7.226
Times cited: 24
DOI: 10.1002/cssc.201100015
|
|
|
“Diagnostic mirrors with transparent protection layer for ITER”. Razdobarin AG, Mukhin EE, Semenov VV, Tolstyakov SY, Kochergin MM, Kurskiev GS, Podushnikova KA, Kirilenko DA, Sitnikova AA, Konovalov VG, Solodovchenko SI, Nekhaieva OM, Skorik OA, Bondarenko VN, Voitsenya VS;, Fusion engineering and design 86, 1341 (2011). http://doi.org/10.1016/j.fusengdes.2011.02.052
Abstract: Fast degradation of in-vessel optics is one of the most serious problems for all optical diagnostics in ITER. To provide the resistance to mechanical and thermal stresses along with a high stability of optical characteristics under deposition-dominated conditions we suggest using high-reflective metallic (Ag or Al) film mirrors coated on silicon substrate and protected with thin oxide film in the divertor Thomson Scattering (TS) diagnostics. The mirrors coated with Al2O3 and ZrO2 films were tested under irradiation by deuterium ions. The experimental results on the oxide films sputtering are discussed in the context of their applicability for the first mirror protection in ITER.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 1.319
Times cited: 6
DOI: 10.1016/j.fusengdes.2011.02.052
|
|
|
“Dynamic shear localization in Ti6Al4V”. Peirs J, Verleysen P, Tirry W, Rabet L, Schryvers D, Degrieck J, Procedia Engineering
T2 –, 11th International Conference on the Mechanical Behavior of Materials, (ICM), 2011, Como, ITALY (ICM11) , 1 (2011). http://doi.org/10.1016/j.proeng.2011.04.386
Abstract: The alloy Ti6Al4V is known to be prone to the formation of adiabatic shear bands when dynamically loaded in shear. This causes a catastrophic decrease of the load carrying capacity and is usually followed by fracture. Although, the main mechanism is recognized to be the competition between strain hardening and thermal softening, a detailed understanding of the role of microstructural plasticity mechanisms and macroscopic loading conditions does not exist yet. To study strain localization and shear fracture, different high strain rate shear tests have been carried out: compression of hat-shaped specimens, torsion of thin walled tubular specimens and in-plane shear tests. The value of the three techniques in studying shear localization is evaluated. Post-mortem analysis of the fracture surface and the materials' microstructure is performed with optical and electron microscopy. In all cases a ductile fracture is observed. SEM and TEM techniques are used to study the local microstructure and composition in the shear band and as such the driving mechanism for the ASB formation. (C) 2011 Published by Elsevier Ltd. Selection and/or peer-review under responsibility of ICM11
Keywords: P1 Proceeding; Electron microscopy for materials research (EMAT)
Times cited: 4
DOI: 10.1016/j.proeng.2011.04.386
|
|
|
“Effect of mold hardness on microstructure and contraction porosity in ductile cast iron”. Khalil-Allafi J, Amin-Ahmadi B, Journal of iron and steel research international 18, 44 (2011). http://doi.org/10.1016/S1006-706X(11)60048-4
Abstract: The effect of mold hardness on the microstructure of ductile iron and the contraction porosity was investigated. Molds with different hardnesses (0.41, 0.48, 0.55, 0.62 MPa) and a sand mold prepared by Co2 method were used. The influence of silicon content on the induced expansion pressure owing to the formation of graphite was also investigated. The contraction during solidification can be compensated by an induced expansion owing to the graphite relief when the hardness of mold increases; therefore, the possibility of achieving a sound product without using any riser increases.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.836
Times cited: 1
DOI: 10.1016/S1006-706X(11)60048-4
|
|
|
“Effect of PbZr0.52Ti0.48O3 thin layer on structure, electronic and magnetic properties of La0.65Sr0.35MnO3 and La0.65Ca0.30MnO3 thin-films”. Hezareh T, Razavi FS, Kremer RK, Habermeier H-U, Lebedev OI, Kirilenko D, Van Tendeloo G, Journal of applied physics 109, 113707 (2011). http://doi.org/10.1063/1.3592660
Abstract: Epitaxial thin film heterostructures of high dielectric PbZr<sub>1-x</sub>Ti<sub>x</sub>O<sub>3</sub> (PZT) and La<sub>1-x</sub>A<sub>x</sub>MnO<sub>3</sub> (A-divalent alkaline earth metals such as Sr (LSMO) and Ca (LCMO)) were grown on SrTiO<sub>3</sub> substrates and their structure, temperature dependence of electrical resistivity, and magnetization were investigated as a function of the thickness of the LSMO(LCMO) layer. The microstructures of the samples were analyzed by TEM. By applying an electric field across the PZT layer, we applied a ferrodistortive pressure on the manganite layer and studied the correlations between lattice distortion and electric transport and magnetic properties of the CMR materials.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.068
Times cited: 4
DOI: 10.1063/1.3592660
|
|
|
“Electronic structure and band gap of zinc spinel oxides beyond LDA : ZnAl2O4, ZnGa2O4 and ZnIn2O4”. Dixit H, Tandon N, Cottenier S, Saniz R, Lamoen D, Partoens B, van Speybroeck V, Waroquier M, New journal of physics 13, 063002 (2011). http://doi.org/10.1088/1367-2630/13/6/063002
Abstract: We examine the electronic structure of the family of ternary zinc spinel oxides ZnX2O4 (X=Al, Ga and In). The band gap of ZnAl2O4 calculated using density functional theory (DFT) is 4.25 eV and is overestimated compared with the experimental value of 3.83.9 eV. The DFT band gap of ZnGa2O4 is 2.82 eV and is underestimated compared with the experimental value of 4.45.0 eV. Since DFT typically underestimates the band gap in the oxide system, the experimental measurements for ZnAl2O4 probably require a correction. We use two first-principles techniques capable of describing accurately the excited states of semiconductors, namely the GW approximation and the modified BeckeJohnson (MBJ) potential approximation, to calculate the band gap of ZnX2O4. The GW and MBJ band gaps are in good agreement with each other. In the case of ZnAl2O4, the predicted band gap values are >6 eV, i.e. ~2 eV larger than the only reported experimental value. We expect future experimental work to confirm our results. Our calculations of the electron effective masses and the second band gap indicate that these compounds are very good candidates to act as transparent conducting host materials.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Condensed Matter Theory (CMT)
Impact Factor: 3.786
Times cited: 98
DOI: 10.1088/1367-2630/13/6/063002
|
|
|
“Existence of superstructures due to large amounts of Fe vacancies in the LiFePO4-type framework”. Hamelet S, Casas-Cabanas M, Dupont L, Davoisne C, Tarascon JM, Masquelier C, Chemistry of materials 23, 32 (2011). http://doi.org/10.1021/cm102511m
Abstract: LiFePO4 has been under intense scrutiny over the past decade because it stands as an attractive positive electrode material for the next generation of Li-ion batteries to power electric vehicles and hybrid electric vehicles, hence the importance of its thermal behavior. The reactivity of LiFePO4 with air at moderate temperatures is shown to be dependent on its particle size. For nanosized materials, a progressive displacement of Fe from the core structure leading to a composite made of nanosize Fe2O3 and highly defective, oxidized LixFeyPO4 compositions, among which the “ideal” formula LiFe2/3PO4. Herein we report, from both temperature-controlled X-ray diffraction and electronic diffraction microscopy, that these off-stoichiometry olivine-type compounds show a defect ordering resulting in the formation of a superstructure. Such a finding shows striking similarities with the temperature-driven oxidation of fayalite Fe2SiO4 (another olivine) to structurally defective laihunite, reported in the literature three decades ago.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 30
DOI: 10.1021/cm102511m
|
|
|
“Exploring different inelastic projection mechanisms for electron tomography”. Goris B, Bals S, van den Broek W, Verbeeck J, Van Tendeloo G, Ultramicroscopy 111, 1262 (2011). http://doi.org/10.1016/j.ultramic.2011.02.007
Abstract: Several different projection mechanisms that all make use of inelastically scattered electrons are used for electron tomography. The advantages and the disadvantages of these methods are compared to HAADFSTEM tomography, which is considered as the standard electron tomography technique in materials science. The different inelastic setups used are energy filtered transmission electron microscopy (EFTEM), thickness mapping based on the log-ratio method and bulk plasmon mapping. We present a comparison that can be used to select the best inelastic signal for tomography, depending on different parameters such as the beam stability and nature of the sample. The appropriate signal will obviously also depend on the exact information which is requested.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 2.843
Times cited: 21
DOI: 10.1016/j.ultramic.2011.02.007
|
|
|
“Extension of the clathrate family : the type X clathrate Ge79P29S18Te6”. Kirsanova MA, Olenev AV, Abakumov AM, Bykov MA, Shevelkov AV, Angewandte Chemie: international edition in English 50, 2371 (2011). http://doi.org/10.1002/anie.201007483
Abstract: Now they are 10! The title compound displays a new type of crystal structure and is labeled clathrate X according to the general classification of clathrate structures. In contrast to typical clathrates, this compound has three-coordinate atoms within the framework and combines distorted 24-vertex polyhedra (see picture, green) centered around tellurium guest atoms with very irregular 10-vertex polyhedra around sulfur atoms (yellow).
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 11.994
Times cited: 23
DOI: 10.1002/anie.201007483
|
|
|
“F-doped Co3O4 photocatalysts for sustainable H2 generation from water/ethanol”. Gasparotto A, Barreca D, Bekermann D, Devi A, Fischer RA, Fornasiero P, Gombac V, Lebedev OI, Maccato C, Montini T, Van Tendeloo G, Tondello E, Journal of the American Chemical Society 133, 19362 (2011). http://doi.org/10.1021/ja210078d
Abstract: p-Type Co3O4 nanostructured films are synthesized by a plasma-assisted process and tested in the photocatalytic production of H2 from water/ethanol solutions under both near-UV and solar irradiation. It is demonstrated that the introduction of fluorine into p-type Co3O4 results in a remarkable performance improvement with respect to the corresponding undoped oxide, highlighting F-doped Co3O4 films as highly promising systems for hydrogen generation. Notably, the obtained yields were among the best ever reported for similar semiconductor-based photocatalytic processes.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 13.858
Times cited: 114
DOI: 10.1021/ja210078d
|
|
|
“FIB/SEM applied to quantitative 3D analysis of precipitates in Ni-Ti”. Cao S, Nishida M, Schryvers D, Diffusion and defect data : solid state data : part B : solid state phenomena 172/174, 1284 (2011). http://doi.org/10.4028/www.scientific.net/SSP.172-174.1284
Abstract: Ni4Ti3 precipitates with a heterogeneous distribution growing in a polycrystalline Ni50.8Ti49.2 alloy have been investigated in a Dual-Beam FIB/SEM system. The volume ratio, mean volume, central plane diameter, thickness, aspect ratio and sphericity of the precipitates in the grain interior as well as near to the grain boundary were measured or calculated. The morphology of the precipitates was classified according to the Zingg scheme. The multistage martensitic transformation occurring in these kinds of samples is interpreted in view of the data of this heterogeneous microstructure of matrix and precipitates.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
DOI: 10.4028/www.scientific.net/SSP.172-174.1284
|
|
|
“Fitting the momentum dependent loss function in EELS”. Bertoni G, Verbeeck J, Brosens F, Microscopy research and technique 74, 212 (2011). http://doi.org/10.1002/jemt.20894
Abstract: Momentum dependent inelastic plasmon scattering can be measured by electron energy loss in a transmission electron microscope. From energy filtered diffraction, the characteristic angle of scattering and the cutoff angle are measured, using a thin film of aluminum as a model test. Rather than deconvolving the data (as done in previous works), a fitting technique is used to extract the loss function from angular resolved spectra, starting from a simple model simulation.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Theory of quantum systems and complex systems
Impact Factor: 1.147
Times cited: 6
DOI: 10.1002/jemt.20894
|
|
|
“Fluorinated heterometallic \beta-diketonates as volatile single-source precursors for the synthesis of low-valent mixed-metal fluorides”. Navulla A, Tsirlin AA, Abakumov AM, Shpanchenko RV, Zhang H, Dikarev EV, Journal of the American Chemical Society 133, 692 (2011). http://doi.org/10.1021/ja109128r
Abstract: Hexafluoroacetylacetonates that contain lead and divalent first-row transition metals, PbM(hfac)4 (M = Ni (1), Co (2), Mn (3), Fe (4), and Zn (5)), have been synthesized. Their heterometallic structures are held together by strong Lewis acid−base interactions between metal atoms and diketonate ligands acting in chelating−bridging fashion. Compounds 1−5 are highly volatile and decompose below 350 °C. Fluorinated heterometallic β-diketonates have been used for the first time as volatile single-source precursors for the preparation of mixed-metal fluorides. Complex fluorides of composition Pb2MF6 have been obtained by decomposition of 1−5 in a two-zone furnace under low-pressure nitrogen flow. Lead−transition metal fluorides conform to orthorhombically distorted Aurivillius-type structure with layers of corner-sharing [MF6] octahedra separated by α-PbO-type (Pb2F2) blocks. Pb2NiF6 and Pb2CoF6 were found to exhibit magnetic ordering below 80 and 43 K, respectively. The ordering is antiferromagnetic, with a weak, uncompensated moment due to the canting of spins. The Pb2MF6 fluorides represent a new class of prospective magnetoelectric materials combining transition metals and lone-pair main-group cations.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 13.858
Times cited: 28
DOI: 10.1021/ja109128r
|
|
|
“GaN@ZIF-8 : selective formation of gallium nitride quantum dots inside a zinc methylimidazolate framework”. Esken D, Turner S, Wiktor C, Kalidindi SB, Van Tendeloo G, Fischer RA, Journal of the American Chemical Society 133, 16370 (2011). http://doi.org/10.1021/ja207077u
Abstract: The microporous zeolitic imidazolate framework [Zn(MeIM)2; ZIF-8; MeIM = imidazolate-2-methyl] was quantitatively loaded with trimethylamine gallane [(CH3)3NGaH3]. The obtained inclusion compound [(CH3)3NGaH3]@ZIF-8 reveals three precursor molecules per host cavity. Treatment with ammonia selectively yields the caged cyclotrigallazane intermediate (H2GaNH2)3@ZIF-8, and further annealing gives GaN@ZIF-8. This new composite material was characterized with FT-IR spectroscopy, solid-state NMR spectroscopy, powder X-ray diffraction, elemental analysis, (scanning) transmission electron microscopy combined with electron energy-loss spectroscopy, photoluminescence (PL) spectroscopy, and N2 sorption measurements. The data give evidence for the presence of GaN nanoparticles (13 nm) embedded in the cavities of ZIF-8, including a blue-shift of the PL emission band caused by the quantum size effect.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 13.858
Times cited: 82
DOI: 10.1021/ja207077u
|
|
|
“Graphitic nanocrystals inside the pores of mesoporous silica : synthesis, characterization and an adsorption study”. de Clippel F, Harkiolakis A, Vosch T, Ke X, Giebeler L, Oswald S, Houthoofd K, Jammaer J, Van Tendeloo G, Martens JA, Jacobs PA, Baron GV, Sels BF, Denayer JFM, Microporous and mesoporous materials: zeolites, clays, carbons and related materials 144, 120 (2011). http://doi.org/10.1016/j.micromeso.2011.04.003
Abstract: This work presents a new carbonsilica hybrid material, denoted as CSM, with remarkable sorption properties. It consists of intraporous graphitic nanocrystals grown in the pores of mesoporous silica. CSM is obtained by a subtle incipient wetness impregnation of Al-containing mesoporous silica with furfuryl alcohol (FA)/hemelitol solutions. Both the volume match of the impregnation solution with that of the silica template pore volume, and the presence of Al3+ in the silica, are crucial to polymerize FA selectively inside the mesopores. Carbonization of the intraporous polymer was then performed by pyrolysis under He up to 1273 K. The resulting CSMs were examined by SEM, HRTEM, 27Al MAS NMR, N2 adsorption, XRD, TGA, TPD, XPS, pycnometry and Raman spectroscopy. Mildly oxidized graphitic-like carbon nanoblocks, consisting of a few graphene-like sheets, were thus identified inside the template mesopores. Random stacking of these carbon crystallites generates microporosity resulting in biporous materials at low carbon content and microporous materials at high carbon loadings. Very narrow pore distributions were obtained when pyrolysis was carried out under slow heating rate, viz. 1 K min−1. Adsorption and shape selective properties of the carbon filled mesoporous silica were studied by performing pulse chromatography and breakthrough experiments, and by measuring adsorption isotherms of linear and branched alkanes. Whereas the parent mesoporous silica shows unselective adsorption, their CSM analogues preferentially adsorb linear alkanes. The sorption capacity and selectivity can be adjusted by changing the pore size of the template or by varying the synthesis conditions. A relation between the carbon crystallites size and the shape selective behaviour of the corresponding CSM for instance is demonstrated. Most interestingly, CSM shows separation factors for linear and branched alkanes up to values comparable to those of zeolitic molecular sieves.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.615
Times cited: 15
DOI: 10.1016/j.micromeso.2011.04.003
|
|
|
“High precision measurements of atom column positions using model-based exit wave reconstruction”. de Backer A, Van Aert S, van Dyck D, Ultramicroscopy 111, 1475 (2011). http://doi.org/10.1016/j.ultramic.2011.07.002
Abstract: In this paper, it has been investigated how to measure atom column positions as accurately and precisely as possible using a focal series of images. In theory, it is expected that the precision would considerably improve using a maximum likelihood estimator based on the full series of focal images. As such, the theoretical lower bound on the variances of the unknown atom column positions can be attained. However, this approach is numerically demanding. Therefore, maximum likelihood estimation has been compared with the results obtained by fitting a model to a reconstructed exit wave rather than to the full series of focal images. Hence, a real space model-based exit wave reconstruction technique based on the channelling theory is introduced. Simulations show that the reconstructed complex exit wave contains the same amount of information concerning the atom column positions as the full series of focal images. Only for thin samples, which act as weak phase objects, this information can be retrieved from the phase of the reconstructed complex exit wave.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 2.843
Times cited: 8
DOI: 10.1016/j.ultramic.2011.07.002
|
|