“Ba2Y(Nb/Ta)O6–Doped YBCO Films on Biaxially Textured Ni–5at.% W Substrates”. Sieger M, Pahlke P, Hanisch J, Sparing M, Bianchetti M, MacManus-Driscoll J, Lao M, Eisterer M, Meledin A, Van Tendeloo G, Nast R, Schultz L, Holzapfel B, Huhne R, IEEE transactions on applied superconductivity 26, 1 (2016). http://doi.org/10.1109/TASC.2016.2539254
Abstract: The incorporation of nanoscaled pinning centers in superconducting YBa2Cu3O7-d (YBCO) films is one of the core topics to enhance the critical current density Jc(B, Q) of coated conductors. The mixed double-perovskite Ba2Y(Nb/Ta)O6 (BYNTO) can be grown in nanosized columns parallel the YBCO c-axis and in step-like patterns, making it customizable to meet specific working conditions (T, B, Q). We compare a 1.6 μm thick film of pure YBCO and a similar film with additional 5 mol% of BYNTO, grown by pulsed laser deposition with a growth rate of 1.6 nm/s on buffered biaxially textured Ni-5at.% W tape. Our doped sample shows nanosized BYNTO columns parallel cYBCO and plates in the ab-plane containing Y, Nb and Ta. An improved homogeneity of the critical current density Jc over the sample was evaluated from trapped field profiles measured with a scanning Hall probe microscope. The mean Jc in rolling direction of the tape is 1.8 MA/cm² (77 K, self-field) and doubles the value of the undoped sample. Angular dependent measurements of the critical current density, Jc(Q), show a decreased anisotropy of the doped film for various magnetic fields at 77 K as well as 64 K.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 6
DOI: 10.1109/TASC.2016.2539254
|
|
|
“Determinants of commercial bank loan and advance disbursement : the case of private Ethiopian commercial banks”. Birhanu T, Deressa SB, Azadi H, Viira A-H, Van Passel S, Witlox F, International journal of bank marketing 39, 1227 (2021). http://doi.org/10.1108/IJBM-05-2021-0166
Abstract: Purpose This paper aimed to investigate the determinants of loans and advances from commercial banks in the case of Ethiopian private commercial banks. Design/methodology/approach The study randomly selected seven commercial banks to represent the population stratified on their asset, deposit and paid-up capital amounts. The study utilized an unbalanced panel data model as each bank started operation at a different period of time and considered the period 1995-2016 for secondary details. Findings The findings showed that the deposit size, credit risk, portfolio investment, average lending rate, real gross domestic product (GDP) and inflation rate had significant and optimistic effects on the lending and advancement of private commercial banks. On the contrary, liquidity ratio had significant and negative effects on private commercial bank loans and advances. Finally, the study forwarded a feasible recommendation for concerned organs to focus on deposit size, credit risk, portfolio investment, average lending rate, real GDP, inflation rate and liquidity ratio. The results of this study will help banking industry policymakers and planners understand how to minimize inflation and unemployment by improving development and sustainable economic growth. Originality/value The findings of this study can also affect the general attitudes of a society by increasing knowledge and improve the quality of life for the general public.
Keywords: A1 Journal article; Economics; Engineering Management (ENM)
DOI: 10.1108/IJBM-05-2021-0166
|
|
|
“An accurate parameterization for scattering factors, electron densities and electrostatic potentials for neutral atoms that obey all physical constraints”. Lobato Hoyos IP, van Dyck D, Acta crystallographica: section A: foundations of crystallography 70, 636 (2014). http://doi.org/10.1107/S205327331401643X
Abstract: An efficient procedure and computer program are outlined for fitting numerical X-ray and electron scattering factors with the correct inclusion of all physical constraints. The numerical electron scattering factors have been parameterized using five analytic non-relativistic hydrogen electron scattering factors as basis functions for 103 neutral atoms of the periodic table. The inclusion of the correct physical constraints in the electron scattering factor and its derived quantities allows the use of the new parameterization in different fields. In terms of quality of the fit, the proposed parameterization of the electron scattering factor is one order of magnitude better than the previous analytic fittings.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 5.725
Times cited: 19
DOI: 10.1107/S205327331401643X
|
|
|
“Polytypism in mcalpineite : a study of natural and synthetic Cu₃TeO₆”. Missen OP, Mills SJ, Canossa S, Hadermann J, Nenert G, Weil M, Libowitzky E, Housley RM, Artner W, Kampf AR, Rumsey MS, Spratt J, Momma K, Dunstan MA, Acta Crystallographica. Section B: Structural Science, Crystal Engineering and Materials (Online) 78 (2022). http://doi.org/10.1107/S2052520621013032
Abstract: Synthetic and naturally occurring forms of tricopper orthotellurate, (Cu3TeO6)-Te-II-O-IV (the mineral mcalpineite) have been investigated by 3D electron diffraction (3D ED), X-ray powder diffraction (XRPD), Raman and infrared (IR) spectroscopic measurements. As a result of the diffraction analyses, (Cu3TeO6)-Te-II-O-IV is shown to occur in two polytypes. The higher-symmetric (Cu3TeO6)-Te-II-O-IV-1C polytype is cubic, space group 1a (3) over bar, with a = 9.537 (1) angstrom and V = 867.4 (3) angstrom(3) as reported in previous studies. The 1C polytype is a well characterized structure consisting of alternating layers of (CuO6)-O-II octahedra and both (CuO6)-O-II and (TeO6)-O-VI octahedra in a patchwork arrangement. The structure of the lower-symmetric orthorhombic (Cu3TeO6)-Te-II-O-IV-2O polytype was determined for the first time in this study by 3D ED and verified by Rietveld refinement. The 2O polytype crystallizes in space group Pcca, with a = 9.745 (3) angstrom, b = 9.749 (2) angstrom, c = 9.771 (2) angstrom and V = 928.3 (4) angstrom(3) . High-precision XRPD data were also collected on (Cu3TeO6)-Te-II-O-IV-2O to verify the lower-symmetric structure by performing a Rietveld refinement. The resultant structure is identical to that determined by 3D ED, with unit-cell parameters a = 9.56157 (19) angstrom, b = 9.55853 (11) angstrom, c = 9.62891 (15) angstrom and V = 880.03 (2) angstrom(3) . The lower symmetry of the 2O polytype is a consequence of a different cation ordering arrangement, which involves the movement of every second (CuO6)-O-II and (TeO6)-O-VI octahedral layer by (1/4, 1/4, 0), leading to an offset of (TeO6)-O-VI and (CuO6)-O-II octahedra in every second layer giving an ABAB* stacking arrangement. Syntheses of (Cu3TeO6)-Te-II-O-IV showed that low-temperature (473 K) hydrothermal conditions generally produce the 2O polytype. XRPD measurements in combination with Raman spectroscopic analysis showed that most natural mcalpineite is the orthorhombic 2O polytype. Both XRPD and Raman spectroscopy measurements may be used to differentiate between the two polytypes of (Cu3TeO6)-Te-II-O-IV. In Raman spectroscopy, (Cu3TeO6)-Te-II-O-IV-1C has a single strong band around 730 cm(-1), whereas (Cu3TeO6)-Te-II-O-IV-2O shows a broad double maximum with bands centred around 692 and 742 cm(-1).
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.9
DOI: 10.1107/S2052520621013032
|
|
|
“Introducton to the special issue on electron crystallography”. Hadermann J, Palatinus L, And Materials 75, 462 (2019). http://doi.org/10.1107/S2052520619010783
Keywords: Editorial; Electron microscopy for materials research (EMAT)
Times cited: 2
DOI: 10.1107/S2052520619010783
|
|
|
“Interstitial defects in the van der Waals gap of Bi2Se3”. Callaert C, Bercx M, Lamoen D, Hadermann J, Acta Crystallographica. Section B: Structural Science, Crystal Engineering and Materials (Online) 75, 717 (2019). http://doi.org/10.1107/S2052520619008357
Abstract: Bi<sub>2</sub>Se<sub>3</sub>is a thermoelectric material and a topological insulator. It is slightly conducting in its bulk due to the presence of defects and by controlling the defects different physical properties can be fine tuned. However, studies of the defects in this material are often contradicting or inconclusive. Here, the defect structure of Bi<sub>2</sub>Se<sub>3</sub>is studied with a combination of techniques: high-resolution scanning transmission electron microscopy (HR-STEM), high-resolution energy-dispersive X-ray (HR-EDX) spectroscopy, precession electron diffraction tomography (PEDT), X-ray diffraction (XRD) and first-principles calculations using density functional theory (DFT). Based on these results, not only the observed defects are discussed, but also the discrepancies in results or possibilities across the techniques. STEM and EDX revealed interstitial defects with mainly Bi character in an octahedral coordination in the van der Waals gap, independent of the applied sample preparation method (focused ion beam milling or cryo-crushing). The inherent character of these defects is supported by their observation in the structure refinement of the EDT data. Moreover, the occupancy probability of the defects determined by EDT is inversely proportional to their corresponding DFT calculated formation energies. STEM also showed the migration of some atoms across and along the van der Waals gap. The kinetic barriers calculated using DFT suggest that some paths are possible at room temperature, while others are most probably beam induced.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.032
DOI: 10.1107/S2052520619008357
|
|
|
“Synergy between transmission electron microscopy and powder diffraction : application to modulated structures”. Batuk D, Batuk M, Abakumov AM, Hadermann J, Acta crystallographica: section B: structural science 71, 127 (2015). http://doi.org/10.1107/S2052520615005466
Abstract: The crystal structure solution of modulated compounds is often very challenging, even using the well established methodology of single-crystal X-ray crystallography. This task becomes even more difficult for materials that cannot be prepared in a single-crystal form, so that only polycrystalline powders are available. This paper illustrates that the combined application of transmission electron microscopy (TEM) and powder diffraction is a possible solution to the problem. Using examples of anion-deficient perovskites modulated by periodic crystallographic shear planes, it is demonstrated what kind of local structural information can be obtained using various TEM techniques and how this information can be implemented in the crystal structure refinement against the powder diffraction data. The following TEM methods are discussed: electron diffraction (selected area electron diffraction, precession electron diffraction), imaging (conventional high-resolution TEM imaging, high-angle annular dark-field and annular bright-field scanning transmission electron microscopy) and state-of-the-art spectroscopic techniques (atomic resolution mapping using energy-dispersive X-ray analysis and electron energy loss spectroscopy).
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.032
Times cited: 11
DOI: 10.1107/S2052520615005466
|
|
|
“Refining short-range order parameters from the three-dimensional diffuse scattering in single-crystal electron diffraction data”. Poppe R, Roth N, Neder RB, Palatinus L, Iversen BB, Hadermann J, IUCrJ 11, 82 (2024). http://doi.org/10.1107/S2052252523010254
Abstract: Our study compares short-range order parameters refined from the diffuse scattering in single-crystal X-ray and single-crystal electron diffraction data. Nb0.84CoSb was chosen as a reference material. The correlations between neighbouring vacancies and the displacements of Sb and Co atoms were refined from the diffuse scattering using a Monte Carlo refinement in DISCUS. The difference between the Sb and Co displacements refined from the diffuse scattering and the Sb and Co displacements refined from the Bragg reflections in single-crystal X-ray diffraction data is 0.012 (7) angstrom for the refinement on diffuse scattering in single-crystal X-ray diffraction data and 0.03 (2) angstrom for the refinement on the diffuse scattering in single-crystal electron diffraction data. As electron diffraction requires much smaller crystals than X-ray diffraction, this opens up the possibility of refining short-range order parameters in many technologically relevant materials for which no crystals large enough for single-crystal X-ray diffraction are available.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.9
DOI: 10.1107/S2052252523010254
|
|
|
“Quantitative analysis of diffuse electron scattering in the lithium-ion battery cathode material Li1.2Ni0.13Mn0.54Co0.13O2”. Poppe R, Vandemeulebroucke D, Neder RB, Hadermann J, IUCrJ 9, 695 (2022). http://doi.org/10.1107/S2052252522007746
Abstract: In contrast to perfectly periodic crystals, materials with short-range order produce diffraction patterns that contain both Bragg reflections and diffuse scattering. To understand the influence of short-range order on material properties, current research focuses increasingly on the analysis of diffuse scattering. This article verifies the possibility to refine the short-range order parameters in submicrometre-sized crystals from diffuse scattering in single-crystal electron diffraction data. The approach was demonstrated on Li<sub>1.2</sub>Ni<sub>0.13</sub>Mn<sub>0.54</sub>Co<sub>0.13</sub>O<sub>2</sub>, which is a state-of-the-art cathode material for lithium-ion batteries. The intensity distribution of the 1D diffuse scattering in the electron diffraction patterns of Li<sub>1.2</sub>Ni<sub>0.13</sub>Mn<sub>0.54</sub>Co<sub>0.13</sub>O<sub>2</sub>depends on the number of stacking faults and twins in the crystal. A model of the disorder in Li<sub>1.2</sub>Ni<sub>0.13</sub>Mn<sub>0.54</sub>Co<sub>0.13</sub>O<sub>2</sub>was developed and both the stacking fault probability and the percentage of the different twins in the crystal were refined using an evolutionary algorithm in<italic>DISCUS</italic>. The approach was applied on reciprocal space sections reconstructed from 3D electron diffraction data since they exhibit less dynamical effects compared with in-zone electron diffraction patterns. A good agreement was achieved between the calculated and the experimental intensity distribution of the diffuse scattering. The short-range order parameters in submicrometre-sized crystals can thus successfully be refined from the diffuse scattering in single-crystal electron diffraction data using an evolutionary algorithm in<italic>DISCUS</italic>.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.9
DOI: 10.1107/S2052252522007746
|
|
|
“Advanced electron crystallography through model-based imaging”. Van Aert S, De Backer A, Martinez GT, den Dekker AJ, Van Dyck D, Bals S, Van Tendeloo G, IUCrJ 3, 71 (2016). http://doi.org/10.1107/S2052252515019727
Abstract: The increasing need for precise determination of the atomic arrangement of non-periodic structures in materials design and the control of nanostructures explains the growing interest in quantitative transmission electron microscopy. The aim is to extract precise and accurate numbers for unknown structure parameters including atomic positions, chemical concentrations and atomic numbers. For this purpose, statistical parameter estimation theory has been shown to provide reliable results. In this theory, observations are considered purely as data planes, from which structure parameters have to be determined using a parametric model describing the images. As such, the positions of atom columns can be measured with a precision of the order of a few picometres, even though the resolution of the electron microscope is still one or two orders of magnitude larger. Moreover, small differences in average atomic number, which cannot be distinguished visually, can be quantified using high-angle annular dark-field scanning transmission electron microscopy images. In addition, this theory allows one to measure compositional changes at interfaces, to count atoms with single-atom sensitivity, and to reconstruct atomic structures in three dimensions. This feature article brings the reader up to date, summarizing the underlying theory and highlighting some of the recent applications of quantitative model-based transmisson electron microscopy.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab; Engineering Management (ENM)
Impact Factor: 5.793
Times cited: 30
DOI: 10.1107/S2052252515019727
|
|
|
“Superspace crystallography : a key to the chemistry and properties”. Pinheiro CB, Abakumov AM, IUCrJ 2, 137 (2015). http://doi.org/10.1107/S2052252514023550
Abstract: An overview is given of the recent advances in the field of modulated molecular and inorganic crystals with an emphasis on the links between incommensurability, intermolecular and interatomic interactions and, wherever possible, the properties of the materials. The importance of detailed knowledge on the modulated structure for understanding the crystal chemistry and the functional properties of modulated phases is shown using selected examples of incommensurate modulations in organic molecular compounds and inorganic complex oxides.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.793
Times cited: 15
DOI: 10.1107/S2052252514023550
|
|
|
“Refinement of the uranium dispersion corrections from anomalous diffraction”. Leinders G, Grendal OG, Arts I, Bes R, Prozheev I, Orlat S, Fitch A, Kvashnina K, Verwerft M, Journal of Applied Crystallography 57, 284 (2024). http://doi.org/10.1107/S1600576723010889
Abstract: The evolution of the uranium chemical state in uranium compounds, principally in the oxides, is of concern in the context of nuclear fuel degradation under storage and repository conditions, and in accident scenarios. The U–O system shows complicated phase relations between single-valence uranium dioxide (UO<sub>2</sub>) and different mixed-valence compounds (<italic>e.g.</italic>U<sub>4</sub>O<sub>9</sub>, U<sub>3</sub>O<sub>7</sub>and U<sub>3</sub>O<sub>8</sub>). To try resolving the electronic structure associated with unique atomic positions, a combined application of diffraction and spectroscopic techniques, such as diffraction anomalous fine structure (DAFS), can be considered. Reported here is the application of two newly developed routines for assessing a DAFS data set, with the aim of refining the uranium X-ray dispersion corrections. High-resolution anomalous diffraction data were acquired from polycrystalline powder samples of UO<sub>2</sub>(containing tetravalent uranium) and potassium uranate (KUO<sub>3</sub>, containing pentavalent uranium) using synchrotron radiation in the vicinity of the U<italic>L</italic><sub>3</sub>edge (17.17 keV). Both routines are based on an iterative refinement of the dispersion corrections, but they differ in either using the intensity of a selection of reflections or doing a full-pattern (Rietveld method) refinement. The uranium dispersion corrections obtained using either method are in excellent agreement with each other, and they show in great detail the chemical shifts and differences in fine structure expected for tetravalent and pentavalent uranium. This approach may open new possibilities for the assessment of other, more complicated, materials such as mixed-valence compounds. Additionally, the DAFS methodology can offer a significant resource optimization because each data set contains both structural (diffraction) and chemical (spectroscopy) information, which can avoid the requirement to use multiple experimental stations at synchrotron sources.
Keywords: A1 Journal Article; Electron Microscopy for Materials Science (EMAT) ;
Impact Factor: 6.1
DOI: 10.1107/S1600576723010889
|
|
|
“Statics and dynamics of skyrmions interacting with disorder and nanostructures”. Reichhardt C, Reichhardt CJO, Milošević, MV, Reviews of modern physics 94, 035005 (2022). http://doi.org/10.1103/REVMODPHYS.94.035005
Abstract: Magnetic skyrmions are topologically stable nanoscale particlelike objects that were discovered in 2009. Since that time, intense research interest in the field has led to the identification of numerous compounds that support skyrmions over a range of conditions spanning from cryogenic to room temperatures. Skyrmions can be set into motion under various types of driving, and the combination of their size, stability, and dynamics makes them ideal candidates for numerous applications. At the same time, skyrmions represent a new class of system in which the energy scales of the skyrmion-skyrmion interactions, sample disorder, temperature, and drive can compete. A growing body of work indicates that the static and dynamic states of skyrmions can be influenced strongly by pinning or disorder in the sample; thus, an understanding of such effects is essential for the eventual use of skyrmions in applications. The current state of knowledge regarding individual skyrmions and skyrmion assemblies interacting with quenched disorder or pinning is reviewed. The microscopic mechanisms for skyrmion pinning, including the repulsive and attractive interactions that can arise from impurities, grain boundaries, or nanostructures, are outlined. This is followed by descriptions of depinning phenomena, sliding states over disorder, the effect of pinning on the skyrmion Hall angle, the competition between thermal and pinning effects, the control of skyrmion motion using ordered potential landscapes such as one-or two-dimensional periodic asymmetric substrates, the creation of skyrmion diodes, and skyrmion ratchet effects. Highlighted are the distinctions arising from internal modes and the strong gyrotropic or Magnus forces that cause the dynamical states of skyrmions to differ from those of other systems with pinning, such as vortices in type-II superconductors, charge density waves, or colloidal particles. Throughout this review future directions and open questions related to the and in are also discussed.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 44.1
Times cited: 12
DOI: 10.1103/REVMODPHYS.94.035005
|
|
|
“Translation-rotation coupling, phase transitions and elastic phenomena in orientationally disordered crystals”. Lynden-Bell RM, Michel KH, Reviews of modern physics 66, 721 (1994). http://doi.org/10.1103/RevModPhys.66.721
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 29.604
Times cited: 128
DOI: 10.1103/RevModPhys.66.721
|
|
|
“Nonvolatile resistive switching in Pt/LaAlO3/SrTiO3 heterostructures”. Wu S, Luo X, Turner S, Peng H, Lin W, Ding J, David A, Wang B, Van Tendeloo G, Wang J, Wu T;, Physical review X 3, 041027 (2013). http://doi.org/10.1103/PhysRevX.3.041027
Abstract: Resistive switching heterojunctions, which are promising for nonvolatile memory applications, usually share a capacitorlike metal-oxide-metal configuration. Here, we report on the nonvolatile resistive switching in Pt/LaAlO3/SrTiO3 heterostructures, where the conducting layer near the LaAlO3/SrTiO3 interface serves as the unconventional bottom electrode although both oxides are band insulators. Interestingly, the switching between low-resistance and high-resistance states is accompanied by reversible transitions between tunneling and Ohmic characteristics in the current transport perpendicular to the planes of the heterojunctions. We propose that the observed resistive switching is likely caused by the electric-field-induced drift of charged oxygen vacancies across the LaAlO3/SrTiO3 interface and the creation of defect-induced gap states within the ultrathin LaAlO3 layer. These metal-oxide-oxide heterojunctions with atomically smooth interfaces and defect-controlled transport provide a platform for the development of nonvolatile oxide nanoelectronics that integrate logic and memory devices.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 12.789
Times cited: 77
DOI: 10.1103/PhysRevX.3.041027
|
|
|
“Intact dirac cones at broken sublattice symmetry : photoemission study of graphene on Ni and Co”. Varykhalov A, Marchenko D, Sanchez-Barriga J, Scholz MR, Verberck B, Trauzettel B, Wehling TO, Carbone C, Rader O, Physical review X 2, 041017 (2012). http://doi.org/10.1103/PhysRevX.2.041017
Abstract: The appearance of massless Dirac fermions in graphene requires two equivalent carbon sublattices of trigonal shape. While the generation of an effective mass and a band gap at the Dirac point remains an unresolved problem for freestanding extended graphene, it is well established by breaking translational symmetry by confinement and by breaking sublattice symmetry by interaction with a substrate. One of the strongest sublattice-symmetry-breaking interactions with predicted and measured band gaps ranging from 400 meV to more than 3 eV has been attributed to the interfaces of graphene with Ni and Co, which are also promising spin-filter interfaces. Here, we apply angle-resolved photoemission to epitaxial graphene on Ni (111) and Co(0001) to show the presence of intact Dirac cones 2.8 eV below the Fermi level. Our results challenge the common belief that the breaking of sublattice symmetry by a substrate and the opening of the band gap at the Dirac energy are in a straightforward relation. A simple effective model of a biased bilayer structure composed of graphene and a sublattice-symmetry-broken layer, corroborated by density-functional-theory calculations, demonstrates the general validity of our conclusions.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 12.789
Times cited: 86
DOI: 10.1103/PhysRevX.2.041017
|
|
|
“Electron vortex beams in a magnetic field : a new twist on Landau levels and Aharonov-Bohm states”. Bliokh KY, Schattschneider P, Verbeeck J, Nori F, Physical review X 2, 041011 (2012). http://doi.org/10.1103/PhysRevX.2.041011
Abstract: We examine the propagation of the recently discovered electron vortex beams in a longitudinal magnetic field. We consider both the Aharonov-Bohm configuration with a single flux line and the Landau case of a uniform magnetic field. While stationary Aharonov-Bohm modes represent Bessel beams with flux- and vortex-dependent probability distributions, stationary Landau states manifest themselves as nondiffracting Laguerre-Gaussian beams. Furthermore, the Landau-state beams possess field- and vortex-dependent phases: (i) the Zeeman phase from coupling the quantized angular momentum to the magnetic field and (ii) the Gouy phase, known from optical Laguerre-Gaussian beams. Remarkably, together these phases determine the structure of Landau energy levels. This unified Zeeman-Landau-Gouy phase manifests itself in a nontrivial evolution of images formed by various superpositions of modes. We demonstrate that, depending on the chosen superposition, the image can rotate in a magnetic field with either (i) Larmor, (ii) cyclotron (double-Larmor), or (iii) zero frequency. At the same time, its centroid always follows the classical cyclotron trajectory, in agreement with the Ehrenfest theorem. Interestingly, the nonrotating superpositions reproduce stable multivortex configurations that appear in rotating superfluids. Our results open an avenue for the direct electron-microscopy observation of fundamental properties of free quantum-electron states in magnetic fields.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 12.789
Times cited: 130
DOI: 10.1103/PhysRevX.2.041011
|
|
|
“In-gap band in the one-dimensional two-orbital Kanamori-Hubbard model with interorbital Coulomb interaction”. Aucar Boidi N, Fernández García H, Nunez-Fernandez Y, Hallberg K, Physical review research 3, 043213 (2021). http://doi.org/10.1103/PHYSREVRESEARCH.3.043213
Abstract: We study the electronic spectral properties at zero temperature of the one-dimensional (1D) version of the degenerate two-orbital Kanamori-Hubbard model, one of the well-established frameworks to study transition metal compounds, using state-of-the-art numerical techniques based on the density matrix renormalization group. While the system is Mott insulating for the half-filled case, as expected for an interacting 1D system, we find interesting and rich structures in the single-particle density of states (DOS) for the hole-doped system. In particular, we find the existence of in-gap states which are pulled down to lower energies from the upper Hubbard band with increasing the interorbital Coulomb interaction V. We analyze the composition of the DOS by projecting it onto different local excitations, and we observe that for large dopings these in-gap excitations are formed mainly by interorbital holon-doublon (HD) states and their energies follow approximately the HD states in the atomic limit. We observe that the Hund interaction J increases the width of the in-gap band, as expected from the two-particle fluctuations in the Hamiltonian. The observation of a finite density of states within the gap between the Hubbard bands for this extended 1D model indicates that these systems present a rich excitation spectra which could help us understand the microscopic physics behind multiorbital compounds.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation); Antwerp X-ray Imaging and Spectroscopy (AXIS)
DOI: 10.1103/PHYSREVRESEARCH.3.043213
|
|
|
“Computing Curie temperature of two-dimensional ferromagnets in the presence of exchange anisotropy”. Tiwari S, Vanherck J, Van de Put ML, Vandenberghe WG, Sorée B, Physical review research 3, 043024 (2021). http://doi.org/10.1103/PHYSREVRESEARCH.3.043024
Abstract: We compare three first-principles methods of calculating the Curie temperature in two-dimensional (2D) ferromagnetic materials (FM), modeled using the Heisenberg model, and propose a simple formula for estimating the Curie temperature with high accuracy that works for all common 2D lattice types. First, we study the effect of exchange anisotropy on the Curie temperature calculated using the Monte Carlo (MC), the Green's function, and the renormalized spin-wave (RNSW) methods. We find that the Green's function method overestimates the Curie temperature in high-anisotropy regimes compared to the MC method, whereas the RNSW method underestimates the Curie temperature compared to the MC and the Green's function methods. Next, we propose a closed-form formula for calculating the Curie temperature of 2D FMs, which provides an estimate of the Curie temperature that is greatly improved over the mean-field expression for magnetic material screening. We apply the closed-form formula to predict the Curie temperature 2D magnets screened from the C2DB database and discover several high Curie temperature FMs, with Fe2F2 and MoI2 emerging as the most promising 2D ferromagnets. Finally, by comparing to experimental results for CrI3, CrCl3, and CrBr3, we conclude that for small effective anisotropies, the Green's-function-based equations are preferable, while for larger anisotropies, MC-based results are more predictive.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
DOI: 10.1103/PHYSREVRESEARCH.3.043024
|
|
|
“Berry phase engineering at oxide interfaces”. Groenendijk DJ, Autieri C, van Thiel TC, Brzezicki W, Hortensius JR, Afanasiev D, Gauquelin N, Barone P, van den Bos KHW, van Aert S, Verbeeck J, Filippetti A, Picozzi S, Cuoco M, Caviglia AD, 2, 023404 (2020). http://doi.org/10.1103/PhysRevResearch.2.023404
Abstract: Three-dimensional strontium ruthenate (SrRuO3) is an itinerant ferromagnet that features Weyl points acting as sources of emergent magnetic fields, anomalous Hall conductivity, and unconventional spin dynamics. Integrating SrRuO3 in oxide heterostructures is potentially a novel route to engineer emergent electrodynamics, but its electronic band topology in the two-dimensional limit remains unknown. Here we show that ultrathin SrRuO3 exhibits spin-polarized topologically nontrivial bands at the Fermi energy. Their band anticrossings show an enhanced Berry curvature and act as competing sources of emergent magnetic fields. We control their balance by designing heterostructures with symmetric (SrTiO3/SrRuO3/SrTiO3 and SrIrO3/SrRuO3/SrIrO3) and asymmetric interfaces (SrTiO3/SrRuO3/SrIrO3). Symmetric structures exhibit an interface-tunable single-channel anomalous Hall effect, while ultrathin SrRuO3 embedded in asymmetric structures shows humplike features consistent with multiple Hall contributions. The band topology of two-dimensional SrRuO3 proposed here naturally accounts for these observations and harmonizes a large body of experimental results.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 58
DOI: 10.1103/PhysRevResearch.2.023404
|
|
|
“Observation of a gel of quantum vortices in a superconductor at very low magnetic fields”. Benito Llorens J, Embon L, Correa A, Gonzalez JD, Herrera E, Guillamon I, Luccas RF, Azpeitia J, Mompean FJ, Garcia-Hernandez M, Munuera C, Aragon Sanchez J, Fasano Y, Milošević, MV, Suderow H, Anahory Y, Physical review research 2, 013329 (2020). http://doi.org/10.1103/PHYSREVRESEARCH.2.013329
Abstract: A gel consists of a network of particles or molecules formed for example using the sol-gel process, by which a solution transforms into a porous solid. Particles or molecules in a gel are mainly organized on a scaffold that makes up a porous system. Quantized vortices in type-II superconductors mostly form spatially homogeneous ordered or amorphous solids. Here we present high-resolution imaging of the vortex lattice displaying dense vortex clusters separated by sparse or entirely vortex-free regions in beta-Bi2Pd superconductor. We find that the intervortex distance diverges upon decreasing the magnetic field and that vortex lattice images follow a multifractal behavior. These properties, characteristic of gels, establish the presence of a novel vortex distribution, distinctly different from the well-studied disordered and glassy phases observed in high-temperature and conventional superconductors. The observed behavior is caused by a scaffold of one-dimensional structural defects with enhanced stress close to the defects. The vortex gel might often occur in type-II superconductors at low magnetic fields. Such vortex distributions should allow to considerably simplify control over vortex positions and manipulation of quantum vortex states.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Times cited: 14
DOI: 10.1103/PHYSREVRESEARCH.2.013329
|
|
|
“Competition of disorder and electron-phonon coupling in 2H-TaSe2-xSx (0≤x≤2) as evidenced by Raman spectroscopy”. Blagojević, J, Mijin SD, Bekaert J, Opačić, M, Liu Y, Milošević, MV, Petrović, C, Popović, ZV, Lazarević, N, Physical review materials 8, 024004 (2024). http://doi.org/10.1103/PHYSREVMATERIALS.8.024004
Abstract: The vibrational properties of 2H-TaSe<sub>2-x</sub>S<sub>x</sub> (0≤x≤2) single crystals were probed using Raman spectroscopy and density functional theory calculations. The end members revealed two out of four symmetry-predicted Raman active modes, together with the pronounced two-phonon structure, attributable to the enhanced electron-phonon coupling. Additional peaks become observable due to crystallographic disorder for the doped samples. The evolution of the E<sub>2</sub>g<sup>2</sup> mode Fano parameter reveals that the disorder has a weak impact on electron-phonon coupling, which is also supported by the persistence of two-phonon structure in doped samples. As such, this research provides thorough insights into the lattice properties, the effects of crystallographic disorder on Raman spectra, and the interplay of this disorder with the electron-phonon coupling in 2H-TaSe<sub>2-x</sub>S<sub>x</sub> compounds.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 3.4
DOI: 10.1103/PHYSREVMATERIALS.8.024004
|
|
|
“Tunable magnon topology in monolayer CrI₃, under external stimuli”. Soenen M, Milošević, MV, Physical review materials 7, 084402 (2023). http://doi.org/10.1103/PHYSREVMATERIALS.7.084402
Abstract: Two-dimensional (2D) honeycomb ferromagnets, such as monolayer chromium trihalides, are predicted to behave as topological magnon insulators, characterized by an insulating bulk and topologically protected edge states, giving rise to a thermal magnon Hall effect. Here we report the behavior of the topological magnons in monolayer CrI3 under external stimuli, including biaxial and uniaxial strain, electric gating, as well as in-plane and out-of-plane magnetic field, revealing that one can thereby tailor the magnetic states as well as the size and the topology of the magnonic bandgap. These findings broaden the perspective of using 2D magnetic materials to design topological magnonic devices.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 3.4
DOI: 10.1103/PHYSREVMATERIALS.7.084402
|
|
|
“Unusual structural rearrangement and superconductivity in infinite layer cuprate superlattices”. Samal D, Gauquelin N, Takamura Y, Lobato I, Arenholz E, Van Aert S, Huijben M, Zhong Z, Verbeeck J, Van Tendeloo G, Koster G, Physical review materials 7, 054803 (2023). http://doi.org/10.1103/PhysRevMaterials.7.054803
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.4
DOI: 10.1103/PhysRevMaterials.7.054803
|
|
|
“Charge order, frustration relief, and spin-orbit coupling in U3O8”. Saniz R, Baldinozzi G, Arts I, Lamoen D, Leinders G, Verwerft M, Physical review materials 7, 054410 (2023). http://doi.org/10.1103/PhysRevMaterials.7.054410
Abstract: Research efforts on the description of the low-temperature magnetic order and electronic properties of U3O8 have been inconclusive so far. Reinterpreting neutron scattering results, we use group representation theory to show that the ground state presents collinear out-of-plane magnetic moments, with antiferromagnetic coupling both in-layer and between layers. Charge order relieves the initial geometric frustration, generating a slightly distorted honeycomb sublattice with Néel-type order. The precise knowledge of the characteristics of this magnetic ground state is then used to explain the fine features of the band gap. In this system, spin-orbit coupling (SOC) is of critical importance, as it strongly affects the electronic structure, narrowing the gap by ∼38%, compared to calculations neglecting SOC. The predicted electronic structure actually explains the salient features of recent optical absorption measurements, further demonstrating the excellent agreement between the calculated ground state properties and experiment.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.4
DOI: 10.1103/PhysRevMaterials.7.054410
|
|
|
“Stacking-dependent topological magnons in bilayer CrI₃”. Soenen M, Bacaksiz C, Menezes RM, Milošević, MV, Physical review materials 7, 024421 (2023). http://doi.org/10.1103/PHYSREVMATERIALS.7.024421
Abstract: Motivated by the potential of atomically thin magnets towards achieving tunable high-frequency magnonics, we detail the spin-wave dispersion of bilayer CrI3. We demonstrate that the magnonic behavior of the bilayer strongly depends on its stacking configuration and the interlayer magnetic ordering, where a topological band gap opens in the dispersion caused by the Dzyaloshinskii-Moriya and Kitaev interactions, classifying bilayer CrI3 as a topological magnon insulator. We further reveal that both the size and the topology of the band gap in a CrI3 bilayer with an antiferromagnetic interlayer ordering are tunable by an external magnetic field.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 3.4
DOI: 10.1103/PHYSREVMATERIALS.7.024421
|
|
|
“Two-dimensional heterostructures formed by graphenelike ZnO and MgO monolayers for optoelectronic applications”. Seyedmohammadzadeh M, Sevik C, Guelseren O, Physical review materials 6, 104004 (2022). http://doi.org/10.1103/PHYSREVMATERIALS.6.104004
Abstract: Two-dimensional heterostructures are an emerging class of materials for novel applications because of extensive engineering potential by tailoring intriguing properties of different layers as well as the ones arising from their interface. A systematic investigation of mechanical, electronic, and optical properties of possible heterostructures formed by bilayer structures graphenelike ZnO and MgO monolayers is presented. Different functionality of each layer makes these heterostructures very appealing for device applications. ZnO layer is convenient for electron transport in these structures, while MgO layer improves electron collection. At the outset, all of the four possible stacking configurations across the heterostructure are mechanically stable. In addition, stability analysis using phonon dispersion reveals that the AB stacking formed by placing the Mg atom on top of the O atom of the ZnO layer is also dynamically stable at zero temperature. Henceforth, we have investigated the optical properties of these stable heterostructures by applying many-body perturbation theory within the framework of GW approximation and solving the Bethe-Salpeter equation. It is demonstrated that strong excitonic effects reduce the optical band gap to the visible light spectrum range. These results show that this new two-dimensional form of ZnO/MgO heterostructures open an avenue for novel optoelectronic device applications.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 3.4
DOI: 10.1103/PHYSREVMATERIALS.6.104004
|
|
|
“Resistance minimum in LaAlO3/Eu1-xLaxTiO3/SrTiO3 heterostructures”. Lebedev N, Huang Y, Rana A, Jannis D, Gauquelin N, Verbeeck J, Aarts J, Physical review materials 6, 075003 (2022). http://doi.org/10.1103/PHYSREVMATERIALS.6.075003
Abstract: In this paper we study LaAlO3/Eu1-xLaxTiO3/SrTiO3 structures with nominally x = 0, 0.1 and different thicknesses of the Eu1-xLaxTiO3 layer. We observe that both systems have many properties similar to previously studied LaAlO3/EuTiO3/SrTiO3 and other oxide interfaces, such as the formation of a two-dimensional electron liquid for two unit cells of Eu1-xLaxTiO3; a metal-insulator transition driven by the increase in thickness of the Eu1-xLaxTiO3 layer; the presence of an anomalous Hall effect when driving the systems above the Lifshitz point with a back-gate voltage; and a minimum in the temperature dependence of the sheet resistance below the Lifshitz point in the one-band regime, which becomes more pronounced with increasing negative gate voltage. However, and notwithstanding the likely presence of magnetism in the system, we do not attribute that minimum to the Kondo effect, but rather to the properties of the SrTiO3 crystal and the inevitable effects of charge trapping when using back gates.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.4
DOI: 10.1103/PHYSREVMATERIALS.6.075003
|
|
|
“Axion insulator states in a topological insulator proximitized to magnetic insulators : a tight-binding characterization”. Shafiei M, Fazileh F, Peeters FM, Milošević, MV, Physical review materials 6, 074205 (2022). http://doi.org/10.1103/PHYSREVMATERIALS.6.074205
Abstract: The recent discovery of axion states in materials such as antiferromagnetic topological insulators has boosted investigations of the magnetoelectric response in topological insulators and their promise towards realizing dissipationless topological electronics. In this paper, we develop a tight-binding methodology to explore the emergence of axion states in Bi2Se3 in proximity to magnetic insulators on the top and bottom surfaces. The topological protection of the surface states is lifted by a time-reversal-breaking perturbation due to the proximity of a magnetic insulator, and a gap is opened on the surfaces, giving rise to half-quantized Hall conductance and a zero Hall plateau-evidencing an axion insulator state. We developed a real-space tight-binding Hamiltonian for Bi2Se3 using first-principles data. Transport properties of the system were obtained within the Landauer-Buttiker formalism, and we discuss the creation of axion states through Hall conductance and a zero Hall plateau at the surfaces, as a function of proximitized magnetization and corresponding potentials at the surfaces, as well as the thickness of the topological insulator.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 3.4
Times cited: 4
DOI: 10.1103/PHYSREVMATERIALS.6.074205
|
|
|
“Two-dimensional electron systems in perovskite oxide heterostructures : role of the polarity-induced substitutional defects”. Lin S-C, Kuo C-T, Shao Y-C, Chuang Y-D, Geessinck J, Huijben M, Rueff J-P, Graff IL, Conti G, Peng Y, Bostwick A, Gullikson E, Nemsak S, Vailionis A, Gauquelin N, Verbeeck J, Ghiringhelli G, Schneider CM, Fadley CS, Physical review materials 4, 115002 (2020). http://doi.org/10.1103/PHYSREVMATERIALS.4.115002
Abstract: The discovery of a two-dimensional electron system (2DES) at the interfaces of perovskite oxides such as LaAlO3 and SrTiO3 has motivated enormous efforts in engineering interfacial functionalities with this type of oxide heterostructures. However, the fundamental origins of the 2DES are still not understood, e.g., the microscopic mechanisms of coexisting interface conductivity and magnetism. Here we report a comprehensive spectroscopic investigation on the depth profile of 2DES-relevant Ti 3d interface carriers using depthand element-specific techniques like standing-wave excited photoemission and resonant inelastic scattering. We found that one type of Ti 3d interface carriers, which give rise to the 2DES are located within three unit cells from the n-type interface in the SrTiO3 layer. Unexpectedly, another type of interface carriers, which are polarity-induced Ti-on-Al antisite defects, reside in the first three unit cells of the opposing LaAlO3 layer (similar to 10 angstrom). Our findings provide a microscopic picture of how the localized and mobile Ti 3d interface carriers distribute across the interface and suggest that the 2DES and 2D magnetism at the LaAlO3/SrTiO3 interface have disparate explanations as originating from different types of interface carriers.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.4
Times cited: 7
DOI: 10.1103/PHYSREVMATERIALS.4.115002
|
|