Sieger, M.; Pahlke, P.; Ottolinger, R.; Stafford, B.H.; Lao, M.; Meledin, A.; Bauer, M.; Eisterer, M.; Van Tendeloo, G.; Schultz, L.; Nielsch, K.; Hühne, R. |
![goto web page (via DOI) doi](http://nano.uantwerpen.be/nanorefs/img/doi.gif)
|
|
Title |
Influence of substrate tilt angle on the incorporation of BaHfO3 in thick YBa2Cu3O7-δ films |
Type |
A1 Journal article |
|
Year |
2016 |
Publication |
IEEE transactions on applied superconductivity |
Abbreviated Journal |
|
|
|
Volume |
27 |
Issue |
27 |
Pages |
1-4 |
|
|
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
|
|
Abstract |
High critical current densities can be realized in high-temperature superconductors such as YBa2Cu3O7-δ (YBCO) by controlling density, shape, size and direction of a secondary phase. Whereas the dependence on the growth rate and deposition temperature has been widely studied as key parameters for nano-engineering the pinning landscape, the vicinal tilt of the substrate surface might have an additional influence. Therefore, we deposited 6 mol% BaHfO3 (BHO) doped YBCO on SrTiO3 (STO) substrates with vicinal angles α between 0° and 40° to identify the influence of the tilt on the growth mode of BHO. An undisturbed epitaxial growth of the superconductor as well as an epitaxial integration of the BHO phase in the YBCO matrix is observed for all vicinal angles investigated. The critical temperature is constant up to α = 20°, whereas the self-field critical current density at 77 K starts to decrease above 10°. A detailed structural analysis of the film cross sections showed that the growth mode of BHO changes already for a vicinal tilt of 2° from a pure c-axis oriented growth to a layered structure with BHO aligned parallel to the YBCO ab-plane. We identified a strong influence of such a microstructure on the current flow in BHO doped YBCO films on STO substrates as well as on MgO based coated conductors prepared by inclined substrate deposition |
|
|
Address |
|
|
|
Corporate Author |
|
Thesis ![sorted by Thesis field, descending order (down)](img/sort_desc.gif) |
|
|
|
Publisher |
Institute of Electrical and Electronics Engineers (IEEE) |
Place of Publication |
|
Editor |
|
|
|
Language |
|
Wos |
000418469400001 |
Publication Date |
2016-11-22 |
|
|
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
|
|
Series Volume |
|
Series Issue |
|
Edition |
|
|
|
ISSN |
1051-8223 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
|
|
Impact Factor |
|
Times cited |
3 |
Open Access |
|
|
|
Notes |
This work was supported by EUROTAPES, a collaborative project funded by the European Commission’s Seventh Framework Program (FP7 / 2007 – 2013) under Grant Agreement n.280432.The authors would like to thank R. Nast, M. Reitner, M. Kühnel, U. Fiedler and J. Scheiter for technical assistance. |
Approved |
Most recent IF: NA |
|
|
Call Number |
EMAT @ emat @ Sieger_2016a c:irua:138603 |
Serial |
4317 |
|
Permanent link to this record |
|
|
|
|
Author |
Sieger, M.; Pahlke, P.; Lao, M.; Eisterer, M.; Meledin, A.; Van Tendeloo, G.; Ottolinger, R.; Haenisch, J.; Holzapfel, B.; Usoskin, A.; Kursumovic, A.; MacManus-Driscoll, J.L.; Stafford, B.H.; Bauer, M.; Nielsch, K.; Schultz, L.; Huehne, R. |
![goto web page (via DOI) doi](http://nano.uantwerpen.be/nanorefs/img/doi.gif)
|
|
Title |
Tailoring microstructure and superconducting properties in thick BaHfO3 and Ba2YNb/Ta)O-6 doped YBCO films on technical templates |
Type |
A1 Journal article |
|
Year |
2017 |
Publication |
IEEE transactions on applied superconductivity |
Abbreviated Journal |
|
|
|
Volume |
27 |
Issue |
4 |
Pages |
6601407 |
|
|
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
|
|
Abstract |
The current transport capability of YBa2Cu3O7-x(YBCO) based coated conductors (CCs) is mainly limited by two features: the grain boundaries of the used textured template, which are transferred into the superconducting film through the buffer layers, and the ability to pin magnetic flux lines by incorporation of defined defects in the crystal lattice. By adjusting the deposition conditions, it is possible to tailor the pinning landscape in doped YBCO in order to meet specific working conditions (T, B) for CC applications. To study these effects, we deposited YBCO layers with a thickness of about 1-2 mu m using pulsed laser deposition on buffered rolling-assisted biaxially textured Ni-W substrates as well as on metal tapes having either an ion-beam-texturedYSZbuffer or an MgO layer textured by inclined substrate deposition. BaHfO3 and the mixed double-perovskite Ba2Y(Nb/Ta)O-6 were incorporated as artificial pinning centers in these YBCO layers. X-ray diffraction confirmed the epitaxial growth of the superconductor on these templates as well as the biaxially oriented incorporation of the secondary phase additions in the YBCO matrix. A critical current density J(c) of more than 2 MA/cm(2) was achieved at 77 K in self-field for 1-2 mu m thick films. Detailed TEM (transmission electron microscopy) studies revealed that the structure of the secondary phase can be tuned, forming c-axis aligned nanocolumns, ab-oriented platelets, or a combination of both. Transport measurements show that the J(c) anisotropy in magnetic fields is reduced by doping and the peak in the J(c) (theta) curves can be correlated to the microstructural features. |
|
|
Address |
|
|
|
Corporate Author |
|
Thesis ![sorted by Thesis field, descending order (down)](img/sort_desc.gif) |
|
|
|
Publisher |
|
Place of Publication |
New York, N.Y. |
Editor |
|
|
|
Language |
|
Wos |
000394588100001 |
Publication Date |
2016-12-24 |
|
|
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
|
|
Series Volume |
|
Series Issue |
|
Edition |
|
|
|
ISSN |
1051-8223 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
|
|
Impact Factor |
|
Times cited |
12 |
Open Access |
OpenAccess |
|
|
Notes |
; This work was supported by EUROTAPES, a collaborative project funded by the European Commission's Seventh Framework Program (FP7/2007-2013) under Grant Agreement no. 280432. ; |
Approved |
Most recent IF: NA |
|
|
Call Number |
UA @ lucian @ c:irua:141961 |
Serial |
4693 |
|
Permanent link to this record |
|
|
|
|
Author |
Stafford, B.H.; Sieger, M.; Ottolinger, R.; Meledin, A.; Strickland, N.M.; Wimbush, S.C.; Van Tendeloo, G.; Huehne, R.; Schultz, L. |
![goto web page (via DOI) doi](http://nano.uantwerpen.be/nanorefs/img/doi.gif)
|
|
Title |
Tilted BaHfO3 nanorod artificial pinning centres in REBCO films on inclined substrate deposited-MgO coated conductor templates |
Type |
A1 Journal article |
|
Year |
2017 |
Publication |
Superconductor science and technology |
Abbreviated Journal |
Supercond Sci Tech |
|
|
Volume |
30 |
Issue |
5 |
Pages |
055002 |
|
|
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
|
|
Abstract |
We grow BaHfO3 (BHO) nanorods in REBa2Cu3O7-x (REBCO, RE: Gd or Y) thin films on metal tapes coated with the inclined substrate deposited (ISD)-MgO template by both electron beam physical vapour deposition and pulsed laser deposition. In both cases the nanorods are inclined by an angle of 21 degrees-29 degrees with respect to the sample surface normal as a consequence of the tilted growth of the REBCO film resulting from the ISD-MgO layer. We present angular critical current density (J(c)) anisotropy as well as field- and temperature-dependant J(c) data of the BHO nanorod-containing GdBCO films demonstrating an increase in J(c) over a wide range of temperatures between 30 and 77 K and magnetic fields up to 8 T. In addition, we show that the angle of the peak in the J(c) anisotropy curve resulting from the nanorods is dependent both on temperature and magnetic field. The largest J(c) enhancement from the addition of the nanorods was found to occur at 30 K, 3 T, resulting in a J(c) of 3.0 MA cm(-2). |
|
|
Address |
|
|
|
Corporate Author |
|
Thesis ![sorted by Thesis field, descending order (down)](img/sort_desc.gif) |
|
|
|
Publisher |
|
Place of Publication |
Bristol |
Editor |
|
|
|
Language |
|
Wos |
000398860300001 |
Publication Date |
2017-02-22 |
|
|
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
|
|
Series Volume |
|
Series Issue |
|
Edition |
|
|
|
ISSN |
0953-2048 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
|
|
Impact Factor |
2.878 |
Times cited |
6 |
Open Access |
Not_Open_Access |
|
|
Notes |
; The authors would like to thank Anh Tu Bohn and other colleagues at THEVA Dunnschichtechnik GmbH for technical assistance and helpful discussion and R Nast for assistance with sample patterning. We also acknowledge partial support from EUROTAPES, a collaborative project funded by the European Commission's Seventh Framework Program (FP7/2007-2013) under Grant Agreement n. 280432. ; |
Approved |
Most recent IF: 2.878 |
|
|
Call Number |
UA @ lucian @ c:irua:143641 |
Serial |
4694 |
|
Permanent link to this record |