“Surface modification of mesostructured cellular foam to enhance hydrogen storage in binary THF/H₂, clathrate hydrate”. Kummamuru NB, Ciocarlan R-G, Houlleberghs M, Martens J, Breynaert E, Verbruggen SW, Cool P, Perreault P, Sustainable energy &, fuels , 1 (2024). http://doi.org/10.1039/D4SE00114A
Abstract: This study introduces solid-state tuning of a mesostructured cellular foam (MCF) to enhance hydrogen (H-2) storage in clathrate hydrates. Grafting of promoter-like molecules (e.g., tetrahydrofuran) at the internal surface of the MCF resulted in a substantial improvement in the kinetics of formation of binary H-2-THF clathrate hydrate. Identification of the confined hydrate as sII clathrate hydrate and enclathration of H-2 in its small cages was performed using XRD and high-pressure H-1 NMR spectroscopy respectively. Experimental findings show that modified MCF materials exhibit a similar to 1.3 times higher H-2 storage capacity as compared to non-modified MCF under the same conditions (7 MPa, 265 K, 100% pore volume saturation with a 5.56 mol% THF solution). The enhancement in H-2 storage is attributed to the hydrophobicity originating from grafting organic molecules onto pristine MCF, thereby influencing water interactions and fostering an environment conducive to H-2 enclathration. Gas uptake curves indicate an optimal tuning point for higher H-2 storage, favoring a lower density of carbon per nm(2). Furthermore, a direct correlation emerges between higher driving forces and increased H-2 storage capacity, culminating at 0.52 wt% (46.77 mmoles of H-2 per mole of H2O and 39.78% water-to-hydrate conversions) at 262 K for the modified MCF material with fewer carbons per nm(2). Notably, the substantial H-2 storage capacity achieved without energy-intensive processes underscores solid-state tuning's potential for H-2 storage in the synthesized hydrates. This study evaluated two distinct kinetic models to describe hydrate growth in MCF. The multistage kinetic model showed better predictive capabilities for experimental data and maintained a low average absolute deviation. This research provides valuable insights into augmenting H-2 storage capabilities and holds promising implications for future advancements.
Keywords: A1 Journal article; Engineering sciences. Technology; Laboratory of adsorption and catalysis (LADCA)
DOI: 10.1039/D4SE00114A
|
|
|
“Aluminum incorporation into MCM-48 toward the creation of Brønsted acidity”. Collart O, Cool P, van der Voort P, Meynen V, Vansant EF, Houthoofd KJ, Grobet PJ, Lebedev OI, Van Tendeloo G, The journal of physical chemistry : B : condensed matter, materials, surfaces, interfaces and biophysical 108, 13905 (2004). http://doi.org/10.1021/jp049837x
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 3.177
Times cited: 13
DOI: 10.1021/jp049837x
|
|
|
“The influence of the alcohol concentration on the structural ordering of mesoporous silica: cosurfactant versus cosolvent”. Liu S, Cool P, Collart O, van der Voort P, Vansant EF, Lebedev OI, Van Tendeloo G, Jiang M, The journal of physical chemistry : B : condensed matter, materials, surfaces, interfaces and biophysical 107, 10405 (2003). http://doi.org/10.1021/jp034410w
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 3.177
Times cited: 134
DOI: 10.1021/jp034410w
|
|
|
“Investigation of the morphology of the mesoporous SBA-16 and SBA-15 materials”. Stevens WJJ, Lebeau K, Mertens M, Van Tendeloo G, Cool P, Vansant EF, The journal of physical chemistry : B : condensed matter, materials, surfaces, interfaces and biophysical 110, 9183 (2006). http://doi.org/10.1021/jp0548725
Keywords: A1 Journal article; Laboratory of adsorption and catalysis (LADCA); Electron microscopy for materials research (EMAT)
Impact Factor: 3.177
Times cited: 109
DOI: 10.1021/jp0548725
|
|
|
“Leached natural saponite as the silicate source in the synthesis of aluminosilicate hexagonal mesoporous materials”. Linssen T, Cool P, Baroudi M, Cassiers K, Vansant EF, Lebedev O, van Landuyt J, The journal of physical chemistry : B : condensed matter, materials, surfaces, interfaces and biophysical 106, 4470 (2002). http://doi.org/10.1021/jp015578p
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 3.177
Times cited: 23
DOI: 10.1021/jp015578p
|
|
|
“Mechanistic Insight into the Photocatalytic Working of Fluorinated Anatase {001} Nanosheets”. Kus M, Altantzis T, Vercauteren S, Caretti I, Leenaerts O, Batenburg KJ, Mertens M, Meynen V, Partoens B, Van Doorslaer S, Bals S, Cool P, The journal of physical chemistry: C : nanomaterials and interfaces 121, 26275 (2017). http://doi.org/10.1021/acs.jpcc.7b05586
Abstract: Anatase nanosheets with exposed {001} facets
have gained increasing interest for photocatalytic applications. To
fully understand the structure-to-activity relation, combined
experimental and computational methods have been exploited.
Anatase nanosheets were prepared under hydrothermal conditions
in the presence of fluorine ions. High resolution scanning
transmission electron microscopy was used to fully characterize
the synthesized material, confirming the TiO2 nanosheet
morphology. Moreover, the surface structure and composition
of a single nanosheet could be determined by annular bright-field
scanning transmission electron microscopy (ABF-STEM) and
STEM electron energy loss spectroscopy (STEM-EELS). The photocatalytic activity was tested for the decomposition of organic
dyes rhodamine 6G and methyl orange and compared to a reference TiO2 anatase sample. The anatase nanosheets with exposed
{001} facets revealed a significantly lower photocatalytic activity compared to the reference. In order to understand the
mechanism for the catalytic performance, and to investigate the role of the presence of F−, light-induced electron paramagnetic
resonance (EPR) experiments were performed. The EPR results are in agreement with TEM, proving the presence of Ti3+
species close to the surface of the sample and allowing the analysis of the photoinduced formation of paramagnetic species.
Further, ab initio calculations of the anisotropic effective mass of electrons and electron holes in anatase show a very high effective
mass of electrons in the [001] direction, having a negative impact on the mobility of electrons toward the {001} surface and thus
the photocatalysis. Finally, motivated by the experimental results that indicate the presence of fluorine atoms at the surface, we
performed ab initio calculations to determine the position of the band edges in anatase slabs with different terminations of the
{001} surface. The presence of fluorine atoms near the surface is shown to strongly shift down the band edges, which indicates
another reason why it can be expected that the prepared samples with a large amount of {001} surface, but with fluorine atoms
near the surface, show only a low photocatalytic activity.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Condensed Matter Theory (CMT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 4.536
Times cited: 20
DOI: 10.1021/acs.jpcc.7b05586
|
|
|
“Pore REconstruction and Segmentation (PORES) method for improved porosity quantification of nanoporous materials”. Van Eyndhoven G, Kurttepeli M, van Oers CJ, Cool P, Bals S, Batenburg KJ, Sijbers J, Ultramicroscopy 148, 10 (2015). http://doi.org/10.1016/j.ultramic.2014.08.008
Abstract: Electron tomography is currently a versatile tool to investigate the connection between the structure and properties of nanomaterials. However, a quantitative interpretation of electron tomography results is still far from straightforward. Especially accurate quantification of pore-space is hampered by artifacts introduced in all steps of the processing chain, i.e., acquisition, reconstruction, segmentation and quantification. Furthermore, most common approaches require subjective manual user input. In this paper, the PORES algorithm POre REconstruction and Segmentation is introduced; it is a tailor-made, integral approach, for the reconstruction, segmentation, and quantification of porous nanomaterials. The PORES processing chain starts by calculating a reconstruction with a nanoporous-specific reconstruction algorithm: the Simultaneous Update of Pore Pixels by iterative REconstruction and Simple Segmentation algorithm (SUPPRESS). It classifies the interior region to the pores during reconstruction, while reconstructing the remaining region by reducing the error with respect to the acquired electron microscopy data. The SUPPRESS reconstruction can be directly plugged into the remaining processing chain of the PORES algorithm, resulting in accurate individual pore quantification and full sample pore statistics. The proposed approach was extensively validated on both simulated and experimental data, indicating its ability to generate accurate statistics of nanoporous materials.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab; Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 2.843
Times cited: 7
DOI: 10.1016/j.ultramic.2014.08.008
|
|
|
“Quantification of crystalline and amorphous content in porous TiO2 samples from electron energy loss spectroscopy”. Bertoni G, Beyers E, Verbeeck J, Mertens M, Cool P, Vansant EF, Van Tendeloo G, Ultramicroscopy 106, 630 (2006). http://doi.org/10.1016/j.ultramic.2006.03.006
Abstract: We present an efficient method for the quantification of crystalline versus amorphous phase content in mesoporous materials, making use of electron energy loss spectroscopy. The method is based on fitting a superposition of core-loss edges using the maximum likelihood method with measured reference spectra. We apply the method to mesoporous TiO2 samples. We show that the absolute amount of the crystalline phase can be determined with an accuracy below 5%. This method takes also the amorphous phase into account, where standard X-ray diffraction is only quantitative for crystalline phases and not for amorphous phase. (c) 2006 Elsevier B.V.. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 2.843
Times cited: 83
DOI: 10.1016/j.ultramic.2006.03.006
|
|
|
“Automated discrete electron tomography &ndash, Towards routine high-fidelity reconstruction of nanomaterials”. Zhuge X, Jinnai H, Dunin-Borkowski RE, Migunov V, Bals S, Cool P, Bons A-J, Batenburg KJ, Ultramicroscopy 175, 87 (2017). http://doi.org/10.1016/j.ultramic.2017.01.009
Abstract: Electron tomography is an essential imaging technique for the investigation of morphology and 3D structure of nanomaterials. This method, however, suffers from well-known missing wedge artifacts due to a restricted tilt range, which limits the objectiveness, repeatability and efficiency of quantitative structural analysis. Discrete tomography represents one of the promising reconstruction techniques for materials science, potentially capable of delivering higher fidelity reconstructions by exploiting the prior knowledge of the limited number of material compositions in a specimen. However, the application of discrete tomography to practical datasets remains a difficult task due to the underlying challenging mathematical problem. In practice, it is often hard to obtain consistent reconstructions from experimental datasets. In addition, numerous parameters need to be tuned manually, which can lead to bias and non-repeatability. In this paper, we present the application of a new
iterative reconstruction technique, named TVR-DART, for discrete electron tomography. The technique is capable of consistently delivering reconstructions with significantly reduced missing wedge artifacts for a variety of challenging data and imaging conditions, and can automatically estimate its key parameters. We describe the principles of the technique and apply it to datasets from three different types of samples acquired under diverse imaging modes. By further reducing the available tilt range and number of projections, we show that the
proposed technique can still produce consistent reconstructions with minimized missing wedge artifacts. This new development promises to provide the electron microscopy community with an easy-to-use and robust tool for high-fidelity 3D characterization of nanomaterials.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 2.843
Times cited: 22
DOI: 10.1016/j.ultramic.2017.01.009
|
|