“Synthesis and characterisation of lanthanide-based dioxide”. Esquivel MR, Zelaya E, Advances in applied ceramics 110, 219 (2011). http://doi.org/10.1179/1743676110Y.0000000021
Abstract: In the present work, the microstructure and structure of La(0.25)Ce(0.52)Nd(0.17)Pr(0.06)(OH)(3) and La(0.25)Ce(0.52)Nd(0.17)Pr(0.06)O(2) is obtained from transmission electron microscopy and X-ray diffraction measurements. Space group P6(3)/m is assigned to the structure of La(0.25)Ce(0.52)Nd(0.17)Pr(0.06)(OH)(3). Lanthanides are assigned to Wyckoff positions 2c. Cell parameters are a=6.375(5) angstrom and c=3.753(5) angstrom. The thermal decomposition of this compound was studied by differential scanning calorimetry. The process is exothermal with an enthalpy change Delta H degrees value of -254 +/- 10 kJ mol(-1). The decomposition kinetics is complex and two global processes with E(a) values of 98 +/- 4 and 61 +/- 2 kJ mol 21 were observed. The product is a lanthanide dioxide. Space group Fm3m is assigned to the La(0.25)Ce(0.52)Nd(0.17)Pr(0.06)O(2). Lanthanides are distributed in Wyckoff positions 4a. The cell parameter is a=5.479(5) angstrom. Nanopores in the oxide surface are obtained using this method and characterised by STEM measurements.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.325
Times cited: 3
DOI: 10.1179/1743676110Y.0000000021
|
|
|
“Synthesis and crystal structure of the new complex oxide Ca7Mn2.14Ga5.86O17.93”. Kalyuzhnaya AS, Abakumov AM, Rozova MG, d' Hondt H, Hadermann J, Antipov EV, Russian chemical bulletin 59, 706 (2010). http://doi.org/10.1007/s11172-010-0150-z
Abstract: The complex oxide Ca7Mn2.14Ga5.86O17.93 was synthesized by the solid-state reaction in a sealed evacuated quartz tube at 1000 °C. Its crystal structure was determined by electron diffraction and X-ray powder diffraction. The structure can be represented as a tetrahedral framework, viz., the polyanion [(Mn0.285Ga0.715)15O29.86]19- stabilized by the incorporated cation [Ca14GaO6]19+. The polycation consists of the GaO6 octahedra surrounded by the Ca atoms, which are arranged to form a cube capped at all places. The tetrahedral framework is partially disordered due to the presence of tetrahedra with two possible orientations in the positions (0, 0, 0) and (x, x, x) with x ≈ 0.15 and 0.17. The relationship between the Ca7Mn2.14Ga5.86O17.93 structures and related ordered phases with the symmetry F23, as well as the influence of the oxygen content on the ordering in the tetrahedral framework, are discussed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.529
Times cited: 1
DOI: 10.1007/s11172-010-0150-z
|
|
|
“Ag1/8Pr5/8MoO4: an incommensurately modulated scheelite-type structure”. Morozov VA, Mironov AV, Lazoryak BI, Khaikina EG, Basovich OM, Rossell MD, Van Tendeloo G, Journal of solid state chemistry 179, 1183 (2006). http://doi.org/10.1016/j.jssc.2005.12.041
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 35
DOI: 10.1016/j.jssc.2005.12.041
|
|
|
“The domain configuration of the Au11In3 phase”. Kifune K, Yamamoto K, Maruyama S, Van Tendeloo G, Philosophical magazine letters 69, 211 (1994). http://doi.org/10.1080/09500839408241594
Abstract: The crystal structure of Au11In3 thin film alloys have been analysed by means of electron diffraction and high-resolution electron microscopy. The electron diffraction pattern and the high-resolution electron microscopy revealed that this structure was incommensurate and had a domain structure consisting of three kinds of structural unit. The approximant structural model, which is based on a h.c.p. stacking of the layers, is hexagonal with lattice parameters a = 7.612 nm and c = 0-478 nm.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.087
Times cited: 2
DOI: 10.1080/09500839408241594
|
|
|
“The study of carbon nanotubules produced by catalytic method”. Ivanov V, Nagy JB, Lambin P, Lucas A, Zhang XB, Zhang XF, Bernaerts D, Van Tendeloo G, Amelinckx S, van Landuyt J, Chemical physics letters 223, 329 (1994). http://doi.org/10.1016/0009-2614(94)00467-6
Abstract: Catalytic methods for the production of carbon nanotubules have been developed based on the decomposition of acetylene on well-dispersed metal particles strongly adsorbed on a support. Cobalt on silica was found to be the best catalyst-support combination for the production of graphitic tubules. The method for the catalyst preparation and the reaction conditions were optimized. Straight and coiled carbon tubules were obtained with inner and outer diameter of 3-7 and 15-20 nm, respectively, and up to 30 mum in length. These nanotubules were not coated by amorphous carbon. Traces of amorphous carbon could be removed by hydrogen. High resolution electron microscopy images and electron diffraction patterns of the straight nanotubules were similar to those obtained by the arc-discharge method. Coiled nanotubules were revealed by TEM to be regular polygonized helices where the bends are caused by pairs of pentagon-heptagon carbon rings among the hexagonal network.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.897
Times cited: 405
DOI: 10.1016/0009-2614(94)00467-6
|
|
|
“Tomographic spectroscopic imaging, an experimental proof of concept”. van den Broek W, Verbeeck J, Schryvers D, de Backer S, Scheunders P, Ultramicroscopy 109, 296 (2009). http://doi.org/10.1016/j.ultramic.2008.11.022
Abstract: Recording the electron energy loss spectroscopy data cube with a series of energy filtered images is a dose inefficient process because the energy slit blocks most of the electrons. When recording the data cube by scanning an electron probe over the sample, perfect dose efficiency is attained; but due to the low current in nanoprobes, this often is slower, with a smaller field of view. In W. Van den Broek et al. [Ultramicroscopy, 106 (2006) 269], we proposed a new method to record the data cube, which is more dose efficient than an energy filtered series. It produces a set of projections of the data cube and then tomographically reconstructs it. In this article, we demonstrate these projections in practice, we present a simple geometrical model that allows for quantification of the projection angles and we present the first successful experimental reconstruction, all on a standard post-column instrument.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 2.843
Times cited: 1
DOI: 10.1016/j.ultramic.2008.11.022
|
|
|
“A vacancy-disordered, oxygen-deficient perovskite with long-range magnetic ordering : local and average structures and magnetic properties of Sr2Fe1.5Cr0.5O5”. Ramezanipour F, Greedan JE, Siewenie J, Donaberger RL, Turner S, Botton GA, Inorganic chemistry 51, 2638 (2012). http://doi.org/10.1021/ic202590r
Abstract: The local and average crystal structures and magnetic properties of the oxygen-deficient perovskite Sr2Fe1.5Cr0.5O5+y were studied using powder X-ray and neutron diffraction, neutron-pair distribution function analysis, and electron energy-loss spectroscopy. This material crystallizes in the cubic Pm3̅m space group, with a = 3.94491(14) Å. The oxygen vacancies are distributed randomly throughout the perovskite-type structure, and the average coordination number of the Fe(Cr) sites is 5. Refinement of the neutron diffraction data indicates y 0.05. This is in discordance with an earlier report on a material with the same nominal composition and cell constant. Electron energy-loss Cr L2,3-edge spectroscopy shows that Cr3+ is present, which is also contrary to previous speculation. Neutron-pair distribution function studies show that a brownmillerite-like model involving ordered vacancies and alternating octahedral and tetrahedral coordination at the metal sites, gives a better description of the local structure out to 5 Å. A remarkable phenomenon determined by neutron diffraction in Sr2Fe1.5Cr0.5O5 is the occurrence of a long-range G-type antiferromagnetic ordering with Tc ≈ 565 K because cubic oxygen-deficient perovskites with B-site disorder usually do not undergo transitions to magnetically ordered states. The observation of long-range antiferromagnetic order and the Tc value are in accordance with previous Mössbauer spectroscopic studies.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 12
DOI: 10.1021/ic202590r
|
|
|
“Well shaped Mn3O4 nano-octahedra with anomalous magnetic behavior and enhanced photodecomposition properties”. Li Y, Tan H, Yang X-Y, Goris B, Verbeeck J, Bals S, Colson P, Cloots R, Van Tendeloo G, Su B-L, Small 7, 475 (2011). http://doi.org/10.1002/smll.201001403
Abstract: Very uniform and well shaped Mn3O4 nano-octahedra are synthesized using a simple hydrothermal method under the help of polyethylene glycol (PEG200) as a reductant and shape-directing agent. The nano-octahedra formation mechanism is monitored. The shape and crystal orientation of the nanoparticles is reconstructed by scanning electron microscopy and electron tomography, which reveals that the nano-octahedra only selectively expose {101} facets at the external surfaces. The magnetic testing demonstrates that the Mn3O4 nano-octahedra exhibit anomalous magnetic properties: the Mn3O4 nano-octahedra around 150 nm show a similar Curie temperature and blocking temperature to Mn3O4 nanoparticles with 10 nm size because of the vertical axis of [001] plane and the exposed {101} facets. With these Mn3O4 nano-octahedra as a catalyst, the photodecomposition of rhodamine B is evaluated and it is found that the photodecomposition activity of Mn3O4 nano-octahedra is much superior to that of commercial Mn3O4 powders. The anomalous magnetic properties and high superior photodecomposition activity of well shaped Mn3O4 nano-octahedra should be related to the special shape of the nanoparticles and the abundantly exposed {101} facets at the external surfaces. Therefore, the shape preference can largely broaden the application of the Mn3O4 nano-octahedra.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 8.643
Times cited: 131
DOI: 10.1002/smll.201001403
|
|
|
“Enhanced 77K vortex-pinning in YBa2Cu3O7−x films with Ba2YTaO6 and mixed Ba2YTaO6 + Ba2YNbO6 nano-columnar inclusions with irreversibility field to 11T”. Rizzo F, Augieri A, Angrisani Armenio A, Galluzzi V, Mancini A, Pinto V, Rufoloni A, Vannozzi A, Bianchetti M, Kursumovic A, MacManus-Driscoll JL, Meledin A, Van Tendeloo G, Celentano G, APL materials 4, 061101 (2016). http://doi.org/10.1063/1.4953436
Abstract: Pulsed laser deposited thin YBa2Cu3O7−x (YBCO) films with pinning additions of 5at.% Ba2YTaO6 (BYTO) were compared to films with 2.5at.% Ba2YTaO6 + 2.5at.% Ba2YNbO6 (BYNTO) additions. Excellent magnetic flux-pinning at 77 K was obtained with remarkably high irreversibility fields greater than 10T (YBCO-BYTO) and 11T (YBCO-BYNTO), representing the highest ever achieved values in YBCO films.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.335
Times cited: 19
DOI: 10.1063/1.4953436
|
|
|
“Highly efficient rutile TiO2 photocatalysts with single Cu(II) and Fe(III) surface catalytic sites”. Neubert S, Mitoraj D, Shevlin SA, Pulisova P, Heimann M, Du Y, Goh GKL, Pacia M, Kruczała K, Turner S, Macyk W, Guo ZX, Hocking RK, Beranek R;, Journal of materials chemistry A : materials for energy and sustainability 4, 3127 (2016). http://doi.org/10.1039/c5ta07036h
Abstract: Highly active photocatalysts were obtained by impregnation of nanocrystalline rutile TiO2 powders with small amounts of Cu(II) and Fe(III) ions, resulting in the enhancement of initial rates of photocatalytic degradation of 4-chlorophenol in water by factors of 7 and 4, compared to pristine rutile, respectively. Detailed structural analysis by EPR and X-ray absorption spectroscopy (EXAFS) revealed that Cu(II) and Fe(III) are present as single species on the rutile surface. The mechanism of the photoactivity enhancement was elucidated by a combination of DFT calculations and detailed experimental mechanistic studies including photoluminescence measurements, photocatalytic experiments using scavengers, OH radical detection, and photopotential transient measurements. The results demonstrate that the single Cu(II) and Fe(III) ions act as effective cocatalytic sites, enhancing the charge separation, catalyzing “dark” redox reactions at the interface, thus improving the normally very low quantum yields of UV light-activated TiO2 photocatalysts. The exact mechanism of the photoactivity enhancement differs depending on the nature of the cocatalyst. Cu(II)-decorated samples exhibit fast transfer of photogenerated electrons to Cu(II/I) sites, followed by enhanced catalysis of dioxygen reduction, resulting in improved charge separation and higher photocatalytic degradation rates. At Fe(III)-modified rutile the rate of dioxygen reduction is not improved and the photocatalytic enhancement is attributed to higher production of highly oxidizing hydroxyl radicals produced by alternative oxygen reduction pathways opened by the presence of catalytic Fe(III/II) sites. Importantly, it was demonstrated that excessive heat treatment (at 450 degrees C) of photocatalysts leads to loss of activity due to migration of Cu(II) and Fe(III) ions from TiO2 surface to the bulk, accompanied by formation of oxygen vacancies. The demonstrated variety of mechanisms of photoactivity enhancement at single site catalyst-modified photocatalysts holds promise for developing further tailored photocatalysts for various applications.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 8.867
Times cited: 44
DOI: 10.1039/c5ta07036h
|
|
|
“PDMS membranes containing ZIF-coated mesoporous silica spheres for efficient ethanol recovery via pervaporation”. Naik PV, Wee LH, Meledina M, Turner S, Li Y, Van Tendeloo G, Martens JA, Vankelecom IFJ, Journal of materials chemistry A : materials for energy and sustainability 4, 12790 (2016). http://doi.org/10.1039/C6TA04700A
Abstract: The design of functional micro- and mesostructured composite materials is significantly important for separation processes. Mesoporous silica is an attractive material for fast diffusion, while microporous zeolitic imidazolate frameworks (ZIFs) are beneficial for selective adsorption and diffusion. In this work, ZIF-71 and ZIF-8 nanocrystals were grown on the surface of mesoporous silica spheres (MSS) via the seeding and regrowth approach in order to obtain monodispersed MSS-ZIF-71 and MSS-ZIF-8 spheres with a particle size of 2-3 mm. These MSS-ZIF spheres were uniformly dispersed into a polydimethylsiloxane (PDMS) matrix to prepare mixed matrix membranes (MMMs). These MMMs were evaluated for the separation of ethanol from water via pervaporation. The pervaporation results reveal that the MSS-ZIF filled MMMs substantially improve the ethanol recovery in both aspects viz. flux and separation factor. These MMMs outperforms the unfilled PDMS membranes and the conventional carbon and zeolite filled MMMs. As expected, the mesoporous silica core allows very fast flow of the permeating compound, while the hydrophobic ZIF coating enhances the ethanol selectivity through its specific pore structure, hydrophobicity and surface chemistry. It can be seen that ZIF-8 mainly has a positive impact on the selectivity, while ZIF-71 enhances fluxes more significantly.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 8.867
Times cited: 26
DOI: 10.1039/C6TA04700A
|
|
|
“The mechanical behavior during (de)lithiation of coated silicon nanoparticles as anode material for lithium-ion batteries studied by InSitu transmission electron microscopy”. Van Havenbergh K, Turner S, Marx N, Van Tendeloo G, Energy technology 4, 1005 (2016). http://doi.org/10.1002/ENTE.201600057
Abstract: One approach to cope with the continuous irreversible capacity loss in Si-based electrodes, attributed to lithiation-induced volume changes and the formation of a solid-electrolyte interface (SEI), is by coating silicon nanoparticles. A coating can improve the conductivity of the electrode, form a chemical shield against the electrolyte, or provide mechanical confinement to reduce the volume increase. The influence of such a coating on the mechanical behavior of silicon nanoparticles during Li insertion and Li extraction was investigated by insitu transmission electron microscopy. The type of coating was shown to influence the size of the unreacted core that remains after reaction of silicon with lithium. Furthermore, two mechanisms to relieve the stress generated during volume expansion are reported: the initiation of cracks and the formation of nanovoids. Both result in a full reaction of the silicon nanoparticles, whereas with the formation of cracks, additional surface area is created, on which an SEI can be formed.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 2.789
Times cited: 6
DOI: 10.1002/ENTE.201600057
|
|
|
“Energy Level Alignment and Cation Charge States at the LaFeO3/LaMnO3(001) Heterointerface”. Smolin SY, Choquette AK, Wilks RG, Gauquelin N, Félix R, Gerlach D, Ueda S, Krick AL, Verbeeck J, Bär M, Baxter JB, May SJ, Advanced Materials Interfaces 4, 1700183 (2017). http://doi.org/10.1002/admi.201700183
Abstract: The electronic properties of LaFeO 3 /LaMnO 3 epitaxial heterojunctions are investigated to determine the valence and conduction band offsets and the nominal Mn and Fe valence states at the interface. Studying a systematic series of (LaFeO 3 ) n /(LaMnO 3 ) m bilayers (m ≈ 50) epitaxially grown in the (001) orientation using molecular beam epitaxy, layer-resolved electron energy loss spectroscopy reveals a lack of significant interfacial charge transfer, with a nominal 3+ valence state observed for both Mn and Fe across the interface. Through a combination of variable angle spectroscopic ellipsometry and hard X-ray photoelectron spectroscopy, type I energy level alignments are obtained at the LaFeO 3 /LaMnO 3 interface with positive valence and conduction band offsets of (1.20 ± 0.07) eV and (0.5–0.7 ± 0.3) eV, respectively, with minimal band bending. Variable temperature resistivity measurements reveal that the bilayers remain insulating and that the presence of the heterojunction does not result in a conducting interface.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.279
Times cited: 14
DOI: 10.1002/admi.201700183
|
|
|
“Synthesis, structure, and electrochemical properties of k-based sulfates K2M2(SO4)3) with M = Fe and Cu”. Lander L, Rousse G, Batuk D, Colin CV, Dalla Corte DA, Tarascon J-M, Inorganic chemistry 56, 2013 (2017). http://doi.org/10.1021/ACS.INORGCHEM.6B02526
Abstract: Stabilizing new host structures through potassium extraction from K-based polyanionic materials has been proven to be an interesting approach to develop new Li+/Na+ insertion materials. Pursuing the same trend, we here report the feasibility of preparing langbeinite “Fe-2(SO4)(3)” via electrochemical and chemical oxidation of K2Fe2(SO4)(3). Additionally, we succeeded in stabilizing a new K2Cu2(SO4)(3) phase via a solid-state synthesis approach. This novel compound crystallizes in a complex orthorhombic structure that differs from that of langbeinite as deduced from synchrotron X-ray and neutron powder diffraction. Electrochemically, the performance of this new phase is limited, which we explain in terms of sluggish diffusion kinetics. We further show that K2Cu2(SO4)(3) decomposes into K2Cu3O(SO4)(3) on heating, and we report for the first time the synthesis of fedotovite K2Cu3O(SO4)(3). Finally, the fundamental attractiveness of these S = 1/2 systems for physicists is examined by neutron magnetic diffraction, which reveals the absence of a long-range ordering of Cu2+ magnetic moments down to 1.5 K.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 13
DOI: 10.1021/ACS.INORGCHEM.6B02526
|
|
|
“Tailoring microstructure and superconducting properties in thick BaHfO3 and Ba2YNb/Ta)O-6 doped YBCO films on technical templates”. Sieger M, Pahlke P, Lao M, Eisterer M, Meledin A, Van Tendeloo G, Ottolinger R, Haenisch J, Holzapfel B, Usoskin A, Kursumovic A, MacManus-Driscoll JL, Stafford BH, Bauer M, Nielsch K, Schultz L, Huehne R, IEEE transactions on applied superconductivity 27, 6601407 (2017). http://doi.org/10.1109/TASC.2016.2644858
Abstract: The current transport capability of YBa2Cu3O7-x(YBCO) based coated conductors (CCs) is mainly limited by two features: the grain boundaries of the used textured template, which are transferred into the superconducting film through the buffer layers, and the ability to pin magnetic flux lines by incorporation of defined defects in the crystal lattice. By adjusting the deposition conditions, it is possible to tailor the pinning landscape in doped YBCO in order to meet specific working conditions (T, B) for CC applications. To study these effects, we deposited YBCO layers with a thickness of about 1-2 mu m using pulsed laser deposition on buffered rolling-assisted biaxially textured Ni-W substrates as well as on metal tapes having either an ion-beam-texturedYSZbuffer or an MgO layer textured by inclined substrate deposition. BaHfO3 and the mixed double-perovskite Ba2Y(Nb/Ta)O-6 were incorporated as artificial pinning centers in these YBCO layers. X-ray diffraction confirmed the epitaxial growth of the superconductor on these templates as well as the biaxially oriented incorporation of the secondary phase additions in the YBCO matrix. A critical current density J(c) of more than 2 MA/cm(2) was achieved at 77 K in self-field for 1-2 mu m thick films. Detailed TEM (transmission electron microscopy) studies revealed that the structure of the secondary phase can be tuned, forming c-axis aligned nanocolumns, ab-oriented platelets, or a combination of both. Transport measurements show that the J(c) anisotropy in magnetic fields is reduced by doping and the peak in the J(c) (theta) curves can be correlated to the microstructural features.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 12
DOI: 10.1109/TASC.2016.2644858
|
|
|
“The influence of branched alkyl side chains in A-D-A oligothiophenes on the photovoltaic performance and morphology of solution-processed bulk-heterojunction solar cells”. Ata I, Ben Dkhil S, Pfannmoeller M, Bals S, Duche D, Simon J-J, Koganezawa T, Yoshimoto N, Videlot-Ackermann C, Margeat O, Ackermann J, Baeuerle P, Organic chemistry frontiers : an international journal of organic chemistry 4, 1561 (2017). http://doi.org/10.1039/C7QO00222J
Abstract: Besides providing sufficient solubility, branched alkyl chains also affect the film-forming and packing properties of organic semiconductors. In order to avoid steric hindrance as it is present in wide-spread alkyl chains comprising a branching point position at the C2-position, i.e., 2-ethylhexyl, the branching point can be moved away from the pi-conjugated backbone. In this report, we study the influence of the modification of the branching point position from the C2-position in 2-hexyldecylamine (1) to the C4-position in 4-hexyldecylamine (2) connected to the central dithieno[3,2-b: 2', 3'-d] pyrrole (DTP) moiety in a well-studied A-D-A oligothiophene on the optoelectronic properties and photovoltaic performance in solution- processed bulk heterojunction solar cells (BHJSCs) with [6,6]-phenyl-C71-butyric acid methyl ester (PC71BM) as the acceptor material. Post-treatment of the photoactive layers is performed via solvent vapor annealing (SVA) in order to improve the film microstructure of the bulk heterojunction. The time evolution of nanoscale morphological changes is followed by combining scanning transmission electron microscopy with low-energy-loss spectroscopic imaging (STEM-SI), solid-state absorption spectroscopy, and two-dimensional grazing incidence X-ray diffraction (2D-GIXRD). Our results show an improvement of the photovoltaic performance that is dependent on the branching point position in the donor oligomer. Optical spacers are utilized to increase light absorption inside the co-oligomer 2-based BHJSCs leading to increased power conversion efficiencies (PCEs) of 8.2% when compared to the corresponding co-oligomer 1-based devices. A STEM-SI analysis of the respective device cross-sections of active layers containing 1 and 2 as donor materials indeed reveals significant differences in their respective active layer morphologies.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.955
Times cited: 24
DOI: 10.1039/C7QO00222J
|
|
|
“Thermal characterization of polycrystalline diamond thin film heat spreaders grown on GaN HEMTs”. Zhou Y, Ramaneti R, Anaya J, Korneychuk S, Derluyn J, Sun H, Pomeroy J, Verbeeck J, Haenen K, Kuball M, Applied physics letters 111, 041901 (2017). http://doi.org/10.1063/1.4995407
Abstract: Polycrystalline diamond (PCD) was grown onto high-k dielectric passivated AlGaN/GaN-on-Si high electron mobility transistor (HEMT) structures, with film thicknesses ranging from 155 to 1000 nm. Transient thermoreflectance results were combined with device thermal simulations to investigate the heat spreading benefit of the diamond layer. The observed thermal conductivity (k(Dia)) of PCD films is one-to-two orders of magnitude lower than that of bulk PCD and exhibits a strong layer thickness dependence, which is attributed to the grain size evolution. The films exhibit a weak temperature dependence of k(Dia) in the measured 25-225 degrees C range. Device simulation using the experimental jDia and thermal boundary resistance values predicts at best a 15% reduction in peak temperature when the source-drain opening of a passivated AlGaN/GaN-on-Si HEMT is overgrown with PCD. Published by AIP Publishing.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 78
DOI: 10.1063/1.4995407
|
|
|
“Vapor Phase Fabrication of Nanoheterostructures Based on ZnO for Photoelectrochemical Water Splitting”. Barreca D, Carraro G, Gasparotto A, Maccato C, Altantzis T, Sada C, Kaunisto K, Ruoko T-P, Bals S, Advanced Materials Interfaces 4, 1700161 (2017). http://doi.org/10.1002/admi.201700161
Abstract: Nanoheterostructures based on metal oxide semiconductors have emerged
as promising materials for the conversion of sunlight into chemical energy.
In the present study, ZnO-based nanocomposites have been developed by
a hybrid vapor phase route, consisting in the chemical vapor deposition
of ZnO systems on fluorine-doped tin oxide substrates, followed by the
functionalization with Fe2O3 or WO3 via radio frequency-sputtering. The
target systems are subjected to thermal treatment in air both prior and after
sputtering, and their properties, including structure, chemical composition,
morphology, and optical absorption, are investigated by a variety of characterization
methods. The obtained results evidence the formation of highly
porous ZnO nanocrystal arrays, conformally covered by an ultrathin Fe2O3
or WO3 overlayer. Photocurrent density measurements for solar-triggered
water splitting reveal in both cases a performance improvement with respect
to bare zinc oxide, that is mainly traced back to an enhanced separation of
photogenerated charge carriers thanks to the intimate contact between the
two oxides. This achievement can be regarded as a valuable result in view of
future optimization of similar nanoheterostructured photoanodes.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.279
Times cited: 30
DOI: 10.1002/admi.201700161
|
|
|
“Room Temperature Magnetically Ordered Polar Corundum GaFeO3 Displaying Magnetoelectric Coupling”. Niu H, Pitcher MJ, Corkett AJ, Ling S, Mandal P, Zanella M, Dawson K, Stamenov P, Batuk D, Abakumov AM, Bull CL, Smith RI, Murray CA, Day SJ, Slater B, Cora F, Claridge JB, Rosseinsky MJ, Journal of the American Chemical Society 139, 1520 (2017). http://doi.org/10.1021/jacs.6b11128
Abstract: The polar corundum structure type offers a route to new room temperature multiferroic materials, as the partial LiNbO3-type cation ordering that breaks inversion symmetry may be combined with long-range magnetic ordering of high spin d(5) cations above room temperature in the AFeO(3) system. We report the synthesis of a polar corundum GaFeO3 by a high-pressure, high-temperature route and demonstrate that its polarity arises from partial LiNbO3 -type cation ordering by complementary use of neutron, X-ray, and electron diffraction methods. In situ neutron diffraction shows that the polar corundum forms directly from AlFeO3-type GaFeO3 under the synthesis conditions. The A(3+)/Fe3+ cations are shown to be more ordered in polar corundum GaFeO3 than in isostructural ScFeO3. This is explained by DFT calculations which indicate that the extent of ordering is dependent on the configurational entropy available to each system at the very different synthesis temperatures required to form their corundum structures. Polar corundum GaFeO3 exhibits weak ferromagnetism at room temperature that arises from its Fe2O3-like magnetic ordering, which persists to a temperature of 408 K. We demonstrate that the polarity and magnetization are coupled in this system with a measured linear magnetoelectric coupling coefficient of 0.057 ps/m. Such coupling is a prerequisite for potential applications of polar corundum materials in multiferroic/magnetoelectric devices.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 13.858
Times cited: 12
DOI: 10.1021/jacs.6b11128
|
|
|
“Asymmetric Modulation on Exchange Field in a Graphene/BiFeO3Heterostructure by External Magnetic Field”. Song H-D, Wu Y-F, Yang X, Ren Z, Ke X, Kurttepeli M, Tendeloo GV, Liu D, Wu H-C, Yan B, Wu X, Duan C-G, Han G, Liao Z-M, Yu D, Nano letters 18, 2435 (2018). http://doi.org/10.1021/acs.nanolett.7b05480
Abstract: Graphene, having all atoms on its surface, is favorable to extend the functions by introducing the spin–orbit coupling and magnetism through proximity effect. Here, we report the tunable interfacial exchange field produced by proximity coupling in graphene/BiFeO3 heterostructures. The exchange field has a notable dependence with external magnetic field, and it is much larger under negative magnetic field than that under positive magnetic field. For negative external magnetic field, interfacial exchange coupling gives rise to evident spin splitting for N ≠ 0 Landau levels and a quantum Hall metal state for N = 0 Landau level. Our findings suggest graphene/BiFeO3 heterostructures are promising for spintronics.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.712
Times cited: 9
DOI: 10.1021/acs.nanolett.7b05480
|
|
|
“The role of the electrode surface in Na-Air batteries : insights in electrochemical product formation and chemical growth of NaO2”. Lutz L, Corte DAD, Chen Y, Batuk D, Johnson LR, Abakumov A, Yate L, Azaceta E, Bruce PG, Tarascon J-M, Grimaud A, Advanced energy materials 8, 1701581 (2018). http://doi.org/10.1002/AENM.201701581
Abstract: The Na-air battery, because of its high energy density and low charging overpotential, is a promising candidate for low-cost energy storage, hence leading to intensive research. However, to achieve such a battery, the role of the positive electrode material in the discharge process must be understood. This issue is herein addressed by exploring the electrochemical reduction of oxygen, as well as the chemical formation and precipitation of NaO2 using different electrodes. Whereas a minor influence of the electrode surface is demonstrated on the electrochemical formation of NaO2, a strong dependence of the subsequent chemical precipitation of NaO2 is identified. In the origin, this effect stems from the surface energy and O-2/O-2(-) affinity of the electrode. The strong interaction of Au with O-2/O-2(-) increases the nucleation rate and leads to an altered growth process when compared to C surfaces. Consequently, thin (3 mu m) flakes of NaO2 are found on Au, whereas on C large cubes (10 mu m) of NaO2 are formed. This has significant impact on the cell performance and leads to four times higher capacity when C electrodes with low surface energy and O-2/O-2(-) affinity are used. It is hoped that these findings will enable the design of new positive electrode materials with optimized surfaces.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 16.721
Times cited: 13
DOI: 10.1002/AENM.201701581
|
|
|
“Inkjet printing multideposited YBCO on CGO/LMO/MgO/Y2O3/Al2O3/Hastelloy tape for 2G-coated conductors”. Roxana Vlad V, Bartolome E, Vilardell M, Calleja A, Meledin A, Obradors X, Puig T, Ricart S, Van Tendeloo G, Usoskin A, Lee S, Petrykin V, Molodyk A, IEEE transactions on applied superconductivity 28, 6601805 (2018). http://doi.org/10.1109/TASC.2018.2808403
Abstract: We present the preparation of a new architecture of coated conductor by Inkjet printing of low fluorine YBa2Cu3O7-x (YBCO) on top of SuperOx tape: CGO/LMO/IBAD-MgO/Y2O3/Al-2 O-3/Hastelloy. A five-layered multideposited, 475-nm-thick YBCO film was structurally and magnetically characterized. A good texture was achieved using this combination of buffer layers, requiring only a 30-nm-thin ion-beam-assisted deposition (IBAD)-MgO layer. The LF-YBCO CC reaches self-field critical current density values of J(c)(GB) similar to NJ 15.9 MA/cm(2) (5 K), similar to 1.23 MA/cm(2) (77 K) corresponding to an I-c (77 K) = 58.4 A/cm-width. Inkjet printing offers a flexible and cost effective method for YBCO deposition, allowing patterning of structures.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.288
Times cited: 2
DOI: 10.1109/TASC.2018.2808403
|
|
|
“Thick secondary phase pinning-enhanced YBCO films on technical templates”. Sieger M, Pahlke P, Lao M, Meledin A, Eisterer M, Van Tendeloo G, Schultz L, Nielsch K, Huehne R, IEEE transactions on applied superconductivity 28, 8000505 (2018). http://doi.org/10.1109/TASC.2018.2799419
Abstract: The critical current I-c(B) of YBa2Cu3O7-delta (YBCO) coated conductors can be increased by growing thicker superconductor layers as well as improving the critical current density J(c)(B) by the incorporation of artificial pinning centers. We studied the properties of pulsed laser deposited BaHfO3 (BHO)-doped YBCO films with thicknesses of up to 5 mu m on buffered rolling-assisted biaxially textured Ni-5 at % W tape and alternating beam assisted deposition textured Yttrium-stabilized ZrO2 layers on stainless steel. X-Ray diffraction confirms the epitaxial growth of the superconductor on the buffered metallic template. BHO additions reduce the film porosity and lower the probability to grow misoriented grains, hence preventing the J(c) decrease observed in undoped YBCO films with thicknesses > 2 mu m. Thereby, a continuous increase in I-c at 77 K is achieved. A mixed structure of secondary phase nanorods and platelets with different orientations increases J(c)(B) in the full angular range and simultaneously lowers the J(c) anisotropy compared to pristine YBCO.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.288
Times cited: 1
DOI: 10.1109/TASC.2018.2799419
|
|
|
“Influence of artificial pinning centers on structural and superconducting properties of thick YBCO films on ABAD-YSZ templates”. Pahlke P, Sieger M, Ottolinger R, Lao M, Eisterer M, Meledin A, Van Tendeloo G, Haenisch J, Holzapfel B, Schultz L, Nielsch K, Huehne R, Superconductor science and technology 31, 044007 (2018). http://doi.org/10.1088/1361-6668/AAAFBE
Abstract: Recent efforts in the development of YBa2Cu3O7-x (YBCO) coated conductors are devoted to the increase of the critical current I-c in magnetic fields. This is typically realized by growing thicker YBCO layers as well as by the incorporation of artificial pinning centers. We studied the growth of doped YBCO layers with a thickness of up to 7 mu m using pulsed laser deposition with a growth rate of about 1.2 nm s(-1). Industrially fabricated ion-beam textured YSZ templates based on metal tapes were used as substrates for this study. The incorporation of BaHfO3 (BHO) or Ba2Y(Nb0.5Ta0.5)O-6 (BYNTO) secondary phase additions leads to a denser microstructure compared to undoped films. A purely c-axis-oriented YBCO growth is preserved up to a thickness of about 4 mu m, whereas misoriented texture components were observed in thicker films. The critical temperature is slightly reduced compared to undoped films and independent of film thickness. The critical current density J(c) of the BHO- and BYNTO-doped YBCO layers is lower at 77 K and self-field compared to pure YBCO layers; however, I-c increases up to a thickness of 5 mu m. A comparison between films with a thickness of 1.3 mu m revealed that the anisotropy of the critical current density J(c)(theta) strongly depends on the incorporated pinning centers. Whereas BHO nanorods lead to a strong B vertical bar vertical bar c-axis peak, the overall anisotropy is significantly reduced by the incorporation of BYNTO forming a mixture of short c-axis-oriented nanorods and small (a-b)-oriented platelets. As a result, the J(c) values of the doped films outperform the undoped samples at higher fields and lower temperatures for most magnetic field directions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.878
Times cited: 9
DOI: 10.1088/1361-6668/AAAFBE
|
|
|
“Interstitial defects in the van der Waals gap of Bi2Se3”. Callaert C, Bercx M, Lamoen D, Hadermann J, Acta Crystallographica. Section B: Structural Science, Crystal Engineering and Materials (Online) 75, 717 (2019). http://doi.org/10.1107/S2052520619008357
Abstract: Bi<sub>2</sub>Se<sub>3</sub>is a thermoelectric material and a topological insulator. It is slightly conducting in its bulk due to the presence of defects and by controlling the defects different physical properties can be fine tuned. However, studies of the defects in this material are often contradicting or inconclusive. Here, the defect structure of Bi<sub>2</sub>Se<sub>3</sub>is studied with a combination of techniques: high-resolution scanning transmission electron microscopy (HR-STEM), high-resolution energy-dispersive X-ray (HR-EDX) spectroscopy, precession electron diffraction tomography (PEDT), X-ray diffraction (XRD) and first-principles calculations using density functional theory (DFT). Based on these results, not only the observed defects are discussed, but also the discrepancies in results or possibilities across the techniques. STEM and EDX revealed interstitial defects with mainly Bi character in an octahedral coordination in the van der Waals gap, independent of the applied sample preparation method (focused ion beam milling or cryo-crushing). The inherent character of these defects is supported by their observation in the structure refinement of the EDT data. Moreover, the occupancy probability of the defects determined by EDT is inversely proportional to their corresponding DFT calculated formation energies. STEM also showed the migration of some atoms across and along the van der Waals gap. The kinetic barriers calculated using DFT suggest that some paths are possible at room temperature, while others are most probably beam induced.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.032
DOI: 10.1107/S2052520619008357
|
|
|
“Introducton to the special issue on electron crystallography”. Hadermann J, Palatinus L, And Materials 75, 462 (2019). http://doi.org/10.1107/S2052520619010783
Keywords: Editorial; Electron microscopy for materials research (EMAT)
Times cited: 2
DOI: 10.1107/S2052520619010783
|
|
|
“Structure solution and refinement of metal-ion battery cathode materials using electron diffraction tomography”. Hadermann J, Abakumov AM, And Materials 75, 485 (2019). http://doi.org/10.1107/S2052520619008291
Abstract: The applicability of electron diffraction tomography to the structure solution and refinement of charged, discharged or cycled metal-ion battery positive electrode (cathode) materials is discussed in detail. As these materials are often only available in very small amounts as powders, the possibility of obtaining single-crystal data using electron diffraction tomography (EDT) provides unique access to crucial information complementary to X-ray diffraction, neutron diffraction and high-resolution transmission electron microscopy techniques. Using several examples, the ability of EDT to be used to detect lithium and refine its atomic position and occupancy, to solve the structure of materials ex situ at different states of charge and to obtain in situ data on structural changes occurring upon electrochemical cycling in liquid electrolyte is discussed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 2
DOI: 10.1107/S2052520619008291
|
|
|
“Nickel-containing N-doped carbon as effective electrocatalysts for the reduction of CO2 to CO in a continuous-flow electrolyzer”. Daems N, De Mot B, Choukroun D, Van Daele K, Li C, Hubin A, Bals S, Hereijgers J, Breugelmans T, Sustainable energy &, fuels 4, 1296 (2019). http://doi.org/10.1039/C9SE00814D
Abstract: Nickel-containing N-doped carbons were synthesized for the electrochemical reduction of CO2 to CO, which is a promising approach to reduce the atmospheric CO2 levels and its negative impact on the environment. Unfortunately, poor performance (activity, selectivity and/or stability) is still a major hurdle for the economical implementation of this type of materials. The electrocatalysts were prepared through an easily up-scalable and easily tunable method based on the pyrolysis of Ni-containing N-doped carbons. Ni–N–AC–B1 synthesized with a high relative amount of nitrogen and nickel with respect to carbon, was identified as the most promising candidate for this reaction based on its partial CO current density (4.2 mA cm−2), its overpotential (0.57 V) and its faradaic efficiency to CO (>99%). This results in unprecedented values for the current density per g active sites (690 A g−1 active sites). Combined with its decent stability and its high performance in an actual electrolyzer setup, this makes it a promising candidate for the electrochemical reduction of CO2 to CO on a larger scale. Finally, the evaluation of this kind of material in a flow-cell setup has been limited and to the best of our knowledge never included an evaluation of several crucial parameters (e.g. electrolyte type, anode composition and membrane type) and is an essential investigation in the move towards up-scaling and ultimately industrial application of this technique. This study resulted in an optimal cell configuration, consisting of Pt as an anode, Fumatech® as the membrane and 1 M KHCO3 and 2 M KOH as catholyte and anolyte, respectively. In conclusion, this research offers a unique combination of electrocatalyst development and reactor optimization.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Applied Electrochemistry & Catalysis (ELCAT)
Times cited: 14
DOI: 10.1039/C9SE00814D
|
|
|
“Insight into the Mechanisms of High Activity and Stability of Iridium Supported on Antimony-Doped Tin Oxide Aerogel for Anodes of Proton Exchange Membrane Water Electrolyzers”. Saveleva VA, Wang L, Kasian O, Batuk M, Hadermann J, Gallet J-j, Bournel F, Alonso-Vante N, Ozouf G, Beauger C, Mayrhofer KJJ, Cherevko S, Gago AS, Friedrich KA, Zafeiratos S, Savinova ER, Acs Catalysis 10, 2508 (2020). http://doi.org/10.1021/acscatal.9b04449
Abstract: The use of high amounts of iridium in industrial proton exchange membrane water electrolysers (PEMWE) could hinder their widespread use for the decarbonisation of society with hydrogen. Non-thermally oxidised Ir nanoparticles supported on antimony-doped tin oxide (SnO2:Sb, ATO) aerogel allow decreasing the use of the precious metal by more than 70 %, while enhancing the electro-catalytic activity and stability. To date the origin of these benefits remains unknown. Here we present clear evidence on the mechanisms that lead to the enhancement of the electrochemical properties of the catalyst. Operando near ambient pressure X-ray photoelectron spectroscopy on membrane electrode assemblies reveals a low degree of Ir oxidation, attributed to the oxygen spill-over from Ir to SnO2:Sb. Furthermore, the formation of highly unstable Ir(III) species is mitigated, while the decrease of Ir dissolution in Ir/SnO2:Sb is confirmed by inductively coupled plasma mass spectrometry (ICP-MS). The mechanisms that lead to the high activity and stability of Ir catalyst supported on SnO2:Sb aerogel for PEMWE are thus unveiled.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 12.9
DOI: 10.1021/acscatal.9b04449
|
|
|
“YBa2Cu3O7−xfilms with Ba2Y(Nb,Ta)O6nanoinclusions for high-field applications”. Celentano G, Rizzo F, Augieri A, Mancini A, Pinto V, Rufoloni A, Vannozzi A, MacManus-Driscoll JL, Feighan J, Kursumovic A, Meledin A, Mayer J, Van Tendeloo G, Superconductor Science &, Technology 33, 044010 (2020). http://doi.org/10.1088/1361-6668/ab6ee5
Abstract: The structural and transport properties of YBa2Cu3O7−x films grown by pulsed laser deposition with mixed 2.5 mol% Ba2YTaO6 (BYTO) and 2.5 mol% Ba2YNbO6 (BYNO) double-perovskite secondary phases are investigated in an extended film growth rate, R = 0.02–1.8 nm s−1. The effect of R on the film microstructure analyzed by TEM techniques shows an evolution from sparse and straight to denser, thinner and splayed continuous columns, with mixed BYNO + BYTO (BYNTO) composition, as R increases from 0.02 nm s−1 to 1.2 nm s−1. This microstructure results in very efficient flux pinning at 77 K, leading to a remarkable improvement in the critical current density (J c) behaviour, with the maximum pinning force density F p(Max) = 13.5 GN m−3 and the irreversibility field in excess of 11 T. In this range, the magnetic field values at which the F p is maximized varies from 1 T to 5 T, being related to the BYNTO columnar density. The film deposited when R = 0.3 nm s−1 exhibits the best performances over the whole temperature and magnetic field ranges, achieving F p(Max) = 900 GN m−3 at 10 K and 12 T. At higher rates, R > 1.2 nm s−1, BYNTO columns show a meandering nature and are prone to form short nanorods. In addition, in the YBCO film matrix a more disordered structure with a high density of short stacking faults is observed. From the analysis of the F p(H, T) curves it emerges that in films deposited at the high R limit, the vortex pinning is no longer dominated by BYNTO columnar defects, but by a new mechanism showing the typical temperature scaling law. Even though this microstructure produces a limited improvement at 77 K, it exhibits a strong J c improvement at lower temperature with F p = 700 GN m−3 at 10 K, 12 T and 900 GN m−3 at 4.2 K, 18 T.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.6
DOI: 10.1088/1361-6668/ab6ee5
|
|