Abstract: In this paper, we used the semiconducting and lightfastness properties of synthetic and mineral arsenic sulfide pigments to study their stability by means of electrochemical and microfadometric techniques. A combination of these techniques shows that in the early stage of the degradation process, amorphous arsenic sulfides are more stable than both crystalline forms, while upon longer exposure time, amorphous pigments will fade more than both mineral pigments, making it less suitable. While the stability study was carried out on unbound pigments, the influence of the organic binder on the relative degradation of the arsenic sulfide pigments was investigated through a multi-analytical approach on pigment/binder mock-up paint samples. For this purpose, the formation of arsenic trioxide was assessed by micro Fourier transform infrared (μ-FTIR) spectroscopy while the influence of the binder on the formation of sulfates was studied by means of synchrotron radiation X-ray near edge structure (μ-XANES). Both techniques elucidate a higher stability of all pigments in gum arabic while the use of egg yolk as binder leads to the most degradation, most likely due to its sulfur-rich composition. In the context of the degradation of arsenic sulfide pigments, other binders such as animal glue, egg white or linseed oil show an intermediate impact.

Abstract: Environmental factors, such as light, humidity and temperature are triggering agents for the alteration of organic and/or inorganic constituents of oil paintings. The oxidation of the organic material is favored by increasing of relative humidity and temperature, whereas processes involving changes of the oxidation states of a number of inorganic pigments (e.g., vermilion, cadmium yellows, zinc yellows, chrome yellows) are mainly activated by light-exposure. In view of the optimization of the long-term conservation and restoration strategies of paintings it is of relevant interest to establish the consequences of thermal parameters (temperature and relative humidity) on the chemical/photochemical-reactivity and the nature of the alteration products of light sensitive-pigments in oil medium. To this aim here we propose a multi-method analytical approach based on the combination of diffuse reflectance UV-Vis, FTIR, synchrotron radiation (SR)-based micro X-ray fluorescence (mu-XRF)/micro-X-ray absorption neat edge structure ()CANES) and electron paramagnetic resonance (EPR) spectroscopies for studying the effects of different relative humidity conditions before and after light exposure on the reactivity of a series of lead chromate-based pigments [such as PbCrO4 center dot PbO (monoclinic), PbCrO4 (monoclinic) and PbCr0.2S0.8O4 (orthorhombic)] in an oil medium. The investigation of paint models was also compared to that of a late 19th century historical orthorhombic PbCr0.4S0.6O4 oil paint. Diffuse reflectance UV-Vis and FTIR spectroscopies were used to obtain information associated with chromatic changes and the formation of organo-metal degradation products at the paint surface. SR-based Cr K-edge mu-XANES/mu-XRF mapping analysis and EPR spectroscopy were employed in a complementary fashion to determine the amount, nature and distribution of Cr(III) and Cr(V)-based alteration compounds within the paints with micrometric spatial resolution. Under the employed thermal aging conditions, lead(II)-carboxylates and reduced Cr-compounds (in abundance of up to about 35% at the surface) have been identified in the lead chromate-based paints. The tendency of chromates to become reduced increased with increasing moisture levels and was favored for the orthorhombic PbCr0.2S0.8O4 compounds. The redox process gave rise to the formation of Cr(V)-species in relative amount much higher than that was formed in the equivalent paint which was exposed only to light. After light-exposure of the thermally aged paints, compounds ascribable to the oxidation of the organic binder were detected for all the types of pigments. Nevertheless, the previous thermal treatment increased the tendency toward photo-reduction of only the PbCr0.2S0.8O4 pigment. For this light-sensitive compound, the thickness variation of the reduced Cr-rich (ca. 70%) photo-alteration layer with moisture levels could be ascribed to a surface passivation phenomenon that had already occurred before photochemical aging. (C) 2015 Elsevier B.V. All rights reserved.

Abstract: Within the last decade, the established synchrotron- and laboratory-based micro-XRF scanning technology inspired the development of mobile instruments that allow performing in situ experiments on paintings on a macro scale. Since the development of the first mobile scanner at the start of this decade, this chemical imaging technique has brought new insights with respect to several iconic paintings, especially in cases when standard imaging techniques such as X-Ray Radiography (XRR) or Infrared Refiectography (IRR) yielded ambiguous results. The ability of scanning MA-XRF to visualise the distribution of elements detected at and below the paint surface renders this spectrometric method particularly helpful for studying painting techniques and revealing materials that remain hidden below the paint surface. The latter aspect is especially relevant for the technical study of works by Pieter Paul Rubens (1577-1640) as this highly productive seventeenth century master is particularly renowned for the continuous application of modifications during (and even after) the entire course of the creative process. In this work, the added value of MA-XRF scanning experiments for visualising these subsurface features is exemplified by interpreting the chemical images obtained on three of Rubens' key works. Special attention is given to three types of adjustments that are particularly relevant for the technical study of Rubens' oeuvre: (1) compositional changes ('pentimenti'), exemplified by results obtained on The Portrait of Helene Fourment (ca. 1638), (2) extensions to the support ('Anstlickungen.), illustrated by imaging experiments performed on the Venus Frigida (1614) and (3) Rubens' intriguing halos around flesh tones, as found amongst others in The Incredulity of Saint Thomas (1613). The ensuing insights in the paint stratigraphy and the underlying supporting structure illustrate the potential of MA-XRF scanning for the non-invasive, comparative study of Rubens' oeuvre. The results do not only augment the understanding of the complex genesis of Rubens' works of art and his efficient painting technique, but prove valuable during conservation treatments as well, as addressed in this paper. (C) 2018 Elsevier B.V. All rights reserved.

Abstract: Illuminated manuscript fragments are some of the best preserved objects of Western cultural heritage. Therefore, scholars are limited to non-invasive – often point-based – methods, to answer questions on material usage, technique, origin and previous treatments. These powerful methods yield specific information; however, the information is limited to the number of points analyzed. Imaging spectroscopies such as MA-XRF and MA-rFTIR combine specificity with the power of imaging, resulting in distribution images that are interpretable by non-spectroscopists and the public at large. In this paper the possible added value of using imaging spectroscopy is discussed. Do these methods yield the same results as an extensive point-based spectroscopic campaign and can they bring novel information? As a case study, a 15th century illuminated manuscript fragment is employed in order to explore the differences between these approaches and present an inventory of their advantages and limitations. (C) 2018 Elsevier B.V. All rights reserved.

Abstract: The painting Saul and David, considered to date from c. 1652 and previously attributed to Rembrandt van Rijn and/or his studio, is a complex work of art that has been recently subjected to intensive investigation and conservation treatment. The goal of the research was to give insight into the painting's physical construction and condition in preparation for conservation treatment. It was also anticipated that analysis would shed light on authenticity questions and Rembrandt's role in the creation of the painting. The painting depicts the Old Testament figures of King Saul and David. At left is Saul, seated, holding a spear and wiping a tear from his eye with a curtain. David kneels before him at the right playing his harp. In the past, the large sections with the life-size figures were cut apart and later reassembled. A third piece of canvas was added to replace a missing piece of canvas above the head of David. As part of the investigation into the authenticity of the curtain area, a number of paint micro samples were examined with LM and SEM-EDX. Given that the earth, smalt and lake pigments used in the painting could not be imaged with traditional imaging techniques, the entire painting was also examined with state of the art non-destructive imaging techniques. Special attention was devoted to the presence of cobalt-containing materials, specifically the blue glass pigment smalt considered characteristic for the late Rembrandt. A combination of quantitative electron microprobe analysis and macroscopic X-ray fluorescence scanning revealed that three types of cobalt-containing materials are present in the painting. The first type is a cobalt drier that was found in the overpaint used to cover up the canvas inset and the joins that were added in the 19th century. The other two Co-containing materials are part of the original paint used by Rembrandt and comprise two varieties of smalt, a K-rich glass pigment that derives its gray-blue color by doping with Co-ions. Smalt paint with a higher Ni content (NiO:CoO ratio of around 1:4) was used to depict the blue stripes in Saul's colorful turban, while smalt with a lower Ni content was employed (NiO:CoO ratio of around 1:5) for the broad expanses of Saul's garments. The presence of two types of smalt not only supports the recent re-attribution of the painting to Rembrandt, but also that the picture was painted in two phases. Saul's dark red garment is painted in a rough, “loose” manner and the now discolored smalt-rich layer was found to have been partially removed during a past restoration treatment/s. In contrast, the blue-green smalt in the turban is much better preserved and provides a colorful accent. While the use of different types of smalt in a Rembrandt painting has been previously identified using quantitative EDX analysis of paint cross-sections, to the best of our knowledge this is the first time such a distinction has been observed in a 17th-century painting using non-destructive imaging techniques. In addition to the XRF-based non-invasive elemental mapping, hyperspectral imaging in the visual to near-infrared (VNIR) region was also carried out. (C) 2016 Elsevier B.V. All rights reserved.

Abstract: In this article, results using confocal µ-Raman to analyse the cross-section of paint samples are presented. Results obtained with light microscopy, scanning electron microscopy (SEM) combined with an energy dispersive X-ray analysis (EDX) and micro-X-ray fluorescence (µ-XRF) are mentioned and compared to the ones obtained with confocal (MRS). In some cases, pigment identification was possible only by combining analytical results from different techniques. The samples were drawn from five paintings belonging to the Academy of Fine Arts of Antwerp, which are part of a collection of 34 paintings made by students from the Academy between 1819 and 1920. Since, on the one hand, the painting techniques and materials, especially pigments, used in this period are still not completely known, and on the other hand, this collection constitutes a very important and reliable resource of information, these paintings were chosen for a systematic investigation. They represent the evolution of painting in Belgium over approximately a century.

Abstract: Chrome yellows, a class of pigments frequently used by painters of the Impressionism and Post-impressionism period, are known for their different chemical stability; the latter depends on the chemical composition (PbCrO4, PbCr1-xSxO4) and crystalline structure (monoclinic or orthorhombic) of the material. The possibility to distinguish among different forms of this pigment is therefore relevant in order to extend knowledge on the corresponding degradation process that is observed on several original paintings. For this purpose, three paintings conserved at the Van Gogh Museum (Amsterdam) were analyzed using noninvasive Raman spectroscopy, while equivalent investigations employing bench-top instrumentation were performed to obtain information from micro-samples originating from these works of art. In each painting, the chrome yellow was identified either as monoclinic PbCrO4 or in the form of monoclinic PbCr1-xSxO4 (x<0.25) or S-rich orthorhombic PbCr1-xSxO4 (x similar to 0.5). Our ability to make this fairly subtle distinction is based on a Raman study of several oil paint model samples made up of monoclinic and/or orthorhombic crystalline forms of PbCrO4 and PbCr1-xSxO4 (0.1x0.8). These paints were studied using several excitation wavelengths (namely 785.0, 532.0, 514.5, and 488nm). Because of the absence of the resonance Raman effect, which strongly enhances the chromate symmetric stretching band, and the absence of any laser-induced photodecomposition, it is advantageous to acquire data at 785.0nm. The band-shape and the position of the chromate bending modes proved to be more sensitive to the solid solution composition and crystalline structure than the stretching modes and can be used as distinctive spectral markers to discriminate among the different chrome yellow forms that are present. Copyright (c) 2014 John Wiley & Sons, Ltd.

Abstract: Infrared thermography is a fast, non-destructive and contactless testing technique which is increasingly used in heritage science. The aim of this study was to assess the ability of infrared thermography, in combination with a data clustering approach, to differentiate between the different types of historical glass that were included in a colorless leaded-glass windows during previous restoration interventions. Inspection of the thermograms and the application of two data mining techniques on the thermal data, i.e., k-means clustering and hierarchical clustering, allowed identifying different groups of window panes that show a different thermal behavior. Both clustering approaches arrive at similar groupings of the glass with a clear separation of three types. However, the lead cames that hold the glass panes appear to have a substantial impact on the thermal behavior of the surrounding glass, thus preventing classification of the smallest glass panes. For the larger panes, this was not a critical issue as the center of the glass remained unaffected. Subtle visual color differences between panes, implying a variation in coloring metal ions, was not always distinguished by IRT. Nevertheless, data clustering assisted infrared thermography shows potential as an efficient and swift method for documenting the material intervention history of leaded-glass windows during or in preparation of conservation treatments.

Abstract: A hundred 18th-century glass fragments were recovered at the Clairefontaine monastery in the Belgian province of Luxembourg. They were analysed by a combination of SEM-EDX and LA-ICP-MS in order to determine their major composition as well as their trace element signature. Multivariate statistical methods such as hierarchical clustering and principal component analysis were used to divide the glass fragments into four main groups: potassium-rich glass, sodium-rich glass, potassium/lime-rich glass and high-lime-low-alkali glass. Within every group, not only a similarity in composition is observed, but also in colour, morphology and deterioration patterns. Potash glass fragments are the most abundant and show extensive deterioration; two classes of potash glass were identified: one similar to certain Central European glass compositions, while the other one, characterised by large variations in potash: lime ratio, may be attributed to local (regional) glass production. (C) 2014 Elsevier Ltd. All rights reserved.

Abstract: The early medieval period marks an important turning point in the history of glassmaking, since it comprises the transition period between the mineral-based silica-soda-lime glass of the Roman tradition and the plant ash-based glass. With the aim of expanding the knowledge on the glass recipes and technologies of this period, 37 glass samples were analyzed, originating from the archaeological excavations of San Genesio (Tuscany) and dated from the fourth to the eleventh century. The major and minor element concentrations were measured with SEM-EDX, while the trace elements were quantified with LA-ICP-MS. The results were compared with published compositions of glass samples of similar age in order to highlight differences and similarities. The results offer a very interesting view on the glass circulation in the religious/residential/manufacturing center of San Genesio in the early medieval period. Most of the glass has a typical late-Roman composition, but some glass fragments are identified as soda ash glass. These are among the earliest medieval ash-fluxed glasses ever found in the Italian peninsula. (C) 2011 Elsevier Ltd. All rights reserved.

Abstract: LA-ICP-MS analyses were performed on a set of Tuscan (post) medieval archaeological glass finds dated to the 1316th century in order to quantitatively determine the trace element contents. The results are used for defining and distinguishing several compositional groups. The trace element data are consistent with the distinctions obtained by considering the major element data determined via quantitative SEM-EDX, but allow to obtain new insights into the nature and quality of the silica sources employed and the presumed method of ash purification.

Abstract: The chemical composition, as determined by electron probe X-ray microanalysis of a series of ca. 100 archaeological glass fragments, excavated at the Raversijde site (Belgium) is discussed. In the 15th-16th century, Raversijde was a flourishing fishermen town located on the shore of the North Sea, close to the city of Ostend. As a consequence of several battles that were fought in its vicinity, the site was abandoned in the 16th century and was not occupied since then. It is one of the rare archaeological sites in Europe that contains a significant amount of information on the daily life inside a small but affluent medieval community. A comparison of the chemical composition of fragments of vessels and window glass encountered in Raversijde to those found in urban centres in Belgium and to literature date on German and French archaeological finds shows that glass made with wood ash dominates. Usually, it concerns artifacts with a predominantly utilitarian use. A few objects made with sodic (i.e., Na-rich) glass were also encountered, likely to have been imported from Venice during the 15th century or in later periods from an urban centre such as Antwerp, where Facon-de-Venice glass manufacturing activities were established near the start of the 16th century. (C) 2004 Elsevier B.V. All rights reserved.