“Towards biolubricant compatible vegetable oils by pore mouth hydrogenation with shape-selective Pt/ZSM-5 catalysts”. Van Aelst J, Philippaerts A, Bartholomeeusen E, Fayad E, Thibault-Starzyk F, Lu J, Schryvers D, Ooms R, Verboekend D, Jacobs P, Sels B, Catalysis science &, technology 6, 2820 (2016). http://doi.org/10.1039/C6CY00498A
Abstract: Pt/ZSM-5 catalysts with various crystal sizes were prepared via competitive ion-exchange, followed by a slow activation procedure. Even when using very large ZSM-5 crystals, highly dispersed Pt nano-clusters were contained within the zeolite crystal's voids, as ascertained by 2D pressure-jump IR spectroscopy of adsorbed CO and focussed ion-beam transmission electron microscopy. The shape-selective properties of the Pt/ZSM-5 catalysts were evaluated in the partial hydrogenation of soybean oil. Unique hydrogenation selectivities were observed, as the fatty acids located at the central position of the triacylglycerol (TAG) molecules were preferentially hydrogenated. The resulting oil has therefore high levels of intermediately melting TAGs, which are compatible with biolubricants due to their improved oxidative stability and still appropriate low-temperature fluidity. The TAG distribution in the partially hydrogenated soybean oil samples was independent from the zeolite crystal size, while the hydrogenation activity linearly increases with the crystal's external surface area. This trend was confirmed with a Pt loaded mesoporous ZSM-5 zeolite, obtained via a mild alkaline treatment. These observations imply and confirm a genuine pore mouth catalysis mechanism, in which only one fatty acid chain of the TAG is able to enter the micropores of ZSM-5, where the double bonds are hydrogenated by the crystal encapsulated Pt-clusters.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.773
Times cited: 5
DOI: 10.1039/C6CY00498A
|
|
|
“A Universal Deposition Protocol for Planar Heterojunction Solar Cells with High Efficiency Based on Hybrid Lead Halide Perovskite Families”. Conings B, Babayigit A, Klug M T, Bai S, Gauquelin N, Sakai N, Wang J T-W, Verbeeck J, Boyen H-G, Advanced materials 28, 10701 (2016). http://doi.org/10.1002/adma.201603747
Abstract: A robust and expedient gas quenching method is developed for the solution deposition of hybrid perovskite thin films. The method offers a reliable standard practice for the fabrication of a non-exhaustive variety of perovskites exhibiting excellent film morphology and commensurate high performance in both regular and inverted structured solar cell architectures.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 19.791
Times cited: 95
DOI: 10.1002/adma.201603747
|
|
|
“Quantitative measurement for the microstructural parameters of nano-precipitates in Al-Mg-Si-Cu alloys”. Li K, Idrissi H, Sha G, Song M, Lu J, Shi H, Wang W, Ringer SP, Du Y, Schryvers D, Materials characterization 118, 352 (2016). http://doi.org/10.1016/j.matchar.2016.06.007
Abstract: Size, number density and volume fraction of nano-precipitates are important microstructural parameters controlling the strengthening of materials. In this work a widely accessible, convenient, moderately time efficient method with acceptable accuracy and precision has been provided for measurement of volume fraction of nano-precipitates in crystalline materials. The method is based on the traditional but highly accurate technique of measuring foil thickness via convergent beam electron diffraction. A new equation is proposed and verified with the aid of 3-dimensional atom probe (3DAP) analysis, to compensate for the additional error resulted from the hardly distinguishable contrast of too short incomplete precipitates cut by the foil surface. The method can be performed on a regular foil specimen with a modem LaB6 or field-emission-gun transmission electron microscope. Precisions around +/- 16% have been obtained for precipitate volume fractions of needle-like beta ''/C and Q precipitates in an aged Al-Mg-Si-Cu alloy. The measured number density is dose to that directly obtained using 3DAP analysis by a misfit of 45%, and the estimated precision for number density measurement is about +/- 11%. The limitations of the method are also discussed.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 2.714
Times cited: 9
DOI: 10.1016/j.matchar.2016.06.007
|
|
|
“Influence of defect distribution on the reducibility of CeO2-x nanoparticles”. Spadaro MC, Luches P, Bertoni G, Grillo V, Turner S, Van Tendeloo G, Valeri S, D'Addato S, Nanotechnology 27, 425705 (2016). http://doi.org/10.1088/0957-4484/27/42/425705
Abstract: Ceria nanoparticles (NPs) are fundamental in heterogeneous catalysis because of their ability to store or release oxygen depending on the ambient conditions. Their oxygen storage capacity is strictly related to the exposed planes, crystallinity, density and distribution of defects. In this work a study of ceria NPs produced with a ligand-free, physical synthesis method is presented. The NP films were grown by a magnetron sputtering based gas aggregation source and studied by high resolution- and scanning-transmission electron microscopy and x-ray photoelectron spectroscopy. In particular, the influence of the oxidation procedure on the NP reducibility has been investigated. The different reducibility has been correlated to the exposed planes, crystallinity and density and distribution of structural defects. The results obtained in this work represent a basis to obtain cerium oxide NP with desired oxygen transport properties.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.44
Times cited: 11
DOI: 10.1088/0957-4484/27/42/425705
|
|
|
“Intergranular fracture in irradiated Inconel X-750 containing very high concentrations of helium and hydrogen”. Colin D Judge Nicolas Gauquelin Lori Walters Mike Wright James I Cole James Madden Gianluigi A Botton Malcolm Griffiths, Journal of Nuclear Materials 457, 165 (2015). http://doi.org/10.1016/j.jnucmat.2014.10.008
Abstract: In recent years, it has been observed that Inconel X-750 spacers in CANDU reactors exhibits lower ductility with reduced load carrying capacity following irradiation in a reactor environment. The fracture behaviour of ex-service material was also found to be entirely intergranular at high doses. The thermalized flux spectrum in a CANDU reactor leads to transmutation of 58Ni to 59Ni. The 59Ni itself has unusually high thermal neutron reaction cross-sections of the type: (n, γ), (n, p), and (n, α). The latter two reactions, in particular, contribute to a significant enhancement of the atomic displacements in addition to creating high concentrations of hydrogen and helium within the material. Microstructural examinations by transmission electron microscopy (TEM) have confirmed the presence of helium bubbles in the matrix and aligned along grain boundaries and matrix–precipitate interfaces. Helium bubble size and density are found to be highly dependent on the irradiation temperature and material microstructure; the bubbles are larger within grain boundary precipitates. TEM specimens extracted from fracture surfaces and crack tips provide information that is consistent with crack propagation along grain boundaries due to the presence of He bubbles.
Keywords: A1 Journal Article; Electron Microscopy for Materials Science (EMAT) ;
Times cited: 29
DOI: 10.1016/j.jnucmat.2014.10.008
|
|
|
“Element Specific Monolayer Depth Profiling”. Macke S, Radi A, Hamann-Borrero JE, Verna A, Bluschke M, Brück S, Goering E, Sutarto R, He F, Cristiani G, Wu M, Benckiser E, Habermeier H-U, Logvenov G, Gauquelin N, Botton GA, Kajdos AP, Stemmer S, Sawatzky GA, Haverkort MW, Keimer B, Hinkov V, Advanced Materials 26, 6554 (2014). http://doi.org/10.1002/adma.201402028
Abstract: The electronic phase behavior and functionality of interfaces and surfaces in complex materials are strongly correlated to chemical composition profiles, stoichiometry and intermixing. Here a novel analysis scheme for resonant X-ray reflectivity maps is introduced to determine such profiles, which is element specific and non-destructive, and which exhibits atomic-layer resolution and a probing depth of hundreds of nanometers.
Keywords: A1 Journal Article; Electron Microscopy for Materials Science (EMAT)
Impact Factor: 19.791
Times cited: 34
DOI: 10.1002/adma.201402028
|
|
|
“Single-atom Catalysis Using Pt/Graphene Achieved through Atomic Layer Deposition”. Shuhui Sun Gaixia Zhang Nicolas Gauquelin Ning Chen Jigang Zhou Songlan Yang Weifeng Chen Xiangbo Meng Dongsheng Geng Mohammad N Banis Ruying Li Siyu Ye Shanna Knights Gianluigi A Botton Tsun-Kong Sham &, Xueliang Sun, Scientific Reports 3, 1775 (2013). http://doi.org/10.1038/srep01775
Abstract: Platinum-nanoparticle-based catalysts are widely used in many important chemical processes and
automobile industries. Downsizing catalyst nanoparticles to single atoms is highly desirable to maximize
their use efficiency, however, very challenging. Here we report a practical synthesis for isolated single Pt
atoms anchored to graphene nanosheet using the atomic layer deposition (ALD) technique. ALD offers the
capability of precise control of catalyst size span from single atom, subnanometer cluster to nanoparticle.
The single-atom catalysts exhibit significantly improved catalytic activity (up to 10 times) over that of the
state-of-the-art commercial Pt/C catalyst. X-ray absorption fine structure (XAFS) analyses reveal that the
low-coordination and partially unoccupied densities of states of 5d orbital of Pt atoms are responsible for the
excellent performance. This work is anticipated to form the basis for the exploration of a next generation of
highly efficient single-atom catalysts for various applications.
Keywords: A1 Journal Article; Electron Microscopy for Materials Science (EMAT) ;
Times cited: 345
DOI: 10.1038/srep01775
|
|
|
“Atomically resolved EELS mapping of the interfacial structure of epitaxially strained LaNiO3/LaAlO3 superlattices”. N Gauquelin E Benckiser M K Kinyanjui M Wu Y Lu G Christiani G Logvenov H-U Habermeier U Kaiser B Keimer and G A Botton, Physical Review B 90, 195140 (2014). http://doi.org/10.1103/PhysRevB.90.195140
Abstract: The interfacial atomic structure of a metallic LaNiO3/LaAlO3 superlattice grown on a LaSrAlO4 substrate was
investigated using a combination of atomically resolved electron energy loss spectroscopy (EELS) at the Al K,
Al L2,3, Sr L2,3, Ni L2,3, La M4,5, and O K edges as well as hybridization mapping of selected features of the O
K-edge fine structure.We observe an additional La1−xSrxAl1−yNiyO3 layer at the substrate-superlattice interface,
possibly linked to diffusion of Al and Sr into the growing film or a surface reconstruction due to Sr segregation.
The roughness of the LaNiO3/LaAlO3 interfaces is found to be on average around one pseudocubic unit cell. The
O K-edge EELS spectra revealed reduced spectral weight of the prepeak derived from Ni-O hybridized states in
the LaNiO3 layers. We rule out oxygen nonstoichiometry of the LaNiO3 layers and discuss changes in the Ni-O
hybridization due to heterostructuring as possible origin.
Keywords: A1 Journal Article; Electron Microscopy for Materials Science (EMAT) ;
Times cited: 17
DOI: 10.1103/PhysRevB.90.195140
|
|
|
“Paths to collapse for isolated skyrmions in few-monolayer ferromagnetic films”. Stosic D, Mulkers J, Van Waeyenberge B, Ludermir TB, Milošević, MV, Physical review B 95, 214418 (2017). http://doi.org/10.1103/PhysRevB.95.214418
Abstract: Magnetic skyrmions are topological spin configurations in materials with chiral Dzyaloshinskii-Moriya interaction (DMI), that are potentially useful for storing or processing information. To date, DMI has been found in few bulk materials, but can also be induced in atomically thin magnetic films in contact with surfaces with large spin-orbit interactions. Recent experiments have reported that isolated magnetic skyrmions can be stabilized even near room temperature in few-atom-thick magnetic layers sandwiched between materials that provide asymmetric spin-orbit coupling. Here we present the minimum-energy path analysis of three distinct mechanisms for the skyrmion collapse, based on ab initio input and the performed atomic-spin simulations. We focus on the stability of a skyrmion in three atomic layers of Co, either epitaxial on the Pt(111) surface or within a hybrid multilayer where DMI nontrivially varies per monolayer due to competition between different symmetry breaking from two sides of the Co film. In laterally finite systems, their constrained geometry causes poor thermal stability of the skyrmion toward collapse at the boundary, which we show to be resolved by designing the high-DMI structure within an extended film with lower or no DMI.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 3.836
Times cited: 48
DOI: 10.1103/PhysRevB.95.214418
|
|
|
“Symmetry-constrained electron vortex propagation”. Clark L, Guzzinati G, Béché, A, Lubk A, Verbeeck J, Physical review A 93, 063840 (2016). http://doi.org/10.1103/PhysRevA.93.063840
Abstract: Electron vortex beams hold great promise for development in transmission electron microscopy but have yet to be widely adopted. This is partly due to the complex set of interactions that occur between a beam carrying orbital angular momentum (OAM) and a sample. Herein, the system is simplified to focus on the interaction between geometrical symmetries, OAM, and topology. We present multiple simulations alongside experimental data to study the behavior of a variety of electron vortex beams after interacting with apertures of different symmetries and investigate the effect on their OAM and vortex structure, both in the far field and under free-space propagation.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.925
Times cited: 7
DOI: 10.1103/PhysRevA.93.063840
|
|
|
“Atomic and electronic structures of BaHfO3-doped TFA-MOD-derived YBa2Cu3O7−δthin films”. Molina-Luna L, Duerrschnabel M, Turner S, Erbe M, Martinez GT, Van Aert S, Holzapfel B, Van Tendeloo G, Superconductor science and technology 28, 115009 (2015). http://doi.org/10.1088/0953-2048/28/11/115009
Abstract: Tailoring the properties of oxide-based nanocomposites is of great importance for a wide range of materials relevant for energy technology. YBa2Cu3O7−δ (YBCO) superconducting thin films containing nanosized BaHfO3 (BHO) particles yield a significant improvement of the magnetic flux pinning properties and a reduced anisotropy of the critical current density. These films were prepared by chemical solution deposition (CSD) on (100) SrTiO3 (STO) substrates yielding critical current densities up to 3.6 MA cm−2 at 77 K and self-field. Transport in-field J c measurements demonstrated a high pinning force maximum of around 6 GN/m3 for a sample annealed at T = 760 °C that has a doping of 12 mol% of BHO. This sample was investigated by scanning transmission electron microscopy (STEM) in combination with electron energy-loss spectroscopy (EELS) yielding strain and spectral maps. Spherical BHO nanoparticles of 15 nm in size were found in the matrix, whereas the particles at the interface were flat. A 2 nm diffusion layer containing Ti was found at the YBCO (BHO)/STO interface. Local lattice deformation mapping at the atomic scale revealed crystal defects induced by the presence of both sorts of BHO nanoparticles, which can act as pinning centers for magnetic flux lines. Two types of local lattice defects were identified and imaged: (i) misfit edge dislocations and (ii) Ba-Cu-Cu-Ba stacking faults (Y-248 intergrowths). The local electronic structure and charge transfer were probed by high energy resolution monochromated electron energy-loss spectroscopy. This technique made it possible to distinguish superconducting from non-superconducting areas in nanocomposite samples with atomic resolution in real space, allowing the identification of local pinning sites on the order of the coherence length of YBCO (~1.5 nm) and the determination of 0.25 nm dislocation cores.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.878
Times cited: 4
DOI: 10.1088/0953-2048/28/11/115009
|
|
|
“Electron Microscopy of Probability Currents at Atomic Resolution”. Lubk A, Béché, A, Verbeeck J, Physical review letters 115, 176101 (2015). http://doi.org/10.1103/PhysRevLett.115.176101
Abstract: Atomic resolution transmission electron microscopy records the spatially resolved scattered electron density to infer positions, density, and species of atoms. These data are indispensable for studying the relation between structure and properties in solids. Here, we show how this signal can be augmented by the lateral probability current of the scattered electrons in the object plane at similar resolutions and fields of view. The currents are reconstructed from a series of three atomic resolution TEM images recorded under a slight difference of perpendicular line foci. The technique does not rely on the coherence of the electron beam and can be used to reveal electric, magnetic, and strain fields with incoherent electron beams as well as correlations in inelastic transitions, such as electron magnetic chiral dichroism.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 8.462
Times cited: 12
DOI: 10.1103/PhysRevLett.115.176101
|
|
|
“3D Magnetic Induction Maps of Nanoscale Materials Revealed by Electron Holographic Tomography”. Wolf D, Rodriguez LA, Béché, A, Javon E, Serrano L, Magen C, Gatel C, Lubk A, Lichte H, Bals S, Van Tendeloo G, Fernández-Pacheco A, De Teresa JM, Snoeck E, Chemistry of materials 27, 6771 (2015). http://doi.org/10.1021/acs.chemmater.5b02723
Abstract: The investigation of three-dimensional (3D) ferromagnetic nanoscale materials constitutes one of the key research areas of the current magnetism roadmap, and carries great potential to impact areas such as data storage, sensing and biomagnetism. The properties of such nanostructures are closely connected with their 3D magnetic nanostructure, making their determination highly valuable. Up to now, quantitative 3D maps providing both the internal magnetic and electric configuration of the same specimen with high spatial resolution are missing. Here, we demonstrate the quantitative 3D reconstruction of the dominant axial component of the magnetic induction and electrostatic potential within a cobalt nanowire (NW) of 100 nm in diameter with spatial resolution below 10 nanometers by applying electron holographic tomography. The tomogram was obtained using a dedicated TEM sample holder for acquisition, in combination with advanced alignment and tomographic reconstruction routines. The powerful approach presented here is widely applicable to a broad range of 3D magnetic nanostructures and may trigger the progress of novel spintronic non-planar nanodevices.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 50
DOI: 10.1021/acs.chemmater.5b02723
|
|
|
“Rayleigh instability of confined vortex droplets in critical superconductors”. Lukyanchuk I, Vinokur VM, Rydh A, Xie R, Milošević, MV, Welp U, Zach M, Xiao ZL, Crabtree GW, Bending SJ, Peeters FM, Kwok WK, Nature physics 11, 21 (2015). http://doi.org/10.1038/NPHYS3146
Abstract: Depending on the Ginzburg-Landau parameter kappa, superconductors can either be fully diamagnetic if kappa < 1/root 2 (type I superconductors) or allow magnetic flux to penetrate through Abrikosov vortices if kappa > 1/root 2 (type II superconductors; refs 1,2). At the Bogomolny critical point, kappa = kappa(c) = 1/root 2, a state that is infinitely degenerate with respect to vortex spatial configurations arises(3,4). Despite in-depth investigations of conventional type I and type II superconductors, a thorough understanding of the magnetic behaviour in the near-Bogomolny critical regime at kappa similar to kappa(c) remains lacking. Here we report that in confined systems the critical regime expands over a finite interval of kappa forming a critical superconducting state. We show that in this state, in a sample with dimensions comparable to the vortex core size, vortices merge into a multi-quanta droplet, which undergoes Rayleigh instability(5) on increasing kappa and decays by emitting single vortices. Superconducting vortices realize Nielsen-Olesen singular solutions of the Abelian Higgs model, which is pervasive in phenomena ranging from quantum electrodynamics to cosmology(6-9). Our study of the transient dynamics of Abrikosov-Nielsen-Olesen vortices in systems with boundaries promises access to non-trivial effects in quantum field theory by means of bench-top laboratory experiments.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 22.806
Times cited: 20
DOI: 10.1038/NPHYS3146
|
|
|
“Prospects for versatile phase manipulation in the TEM : beyond aberration correction”. Guzzinati G, Clark L, Béché, A, Juchtmans R, Van Boxem R, Mazilu M, Verbeeck J, Ultramicroscopy 151, 85 (2015). http://doi.org/10.1016/j.ultramic.2014.10.007
Abstract: In this paper we explore the desirability of a transmission electron microscope in which the phase of the electron wave can be freely controlled. We discuss different existing methods to manipulate the phase of the electron wave and their limitations. We show how with the help of current techniques the electron wave can already be crafted into specific classes of waves each having their own peculiar properties. Assuming a versatile phase modulation device is feasible, we explore possible benefits and methods that could come into existence borrowing from light optics where the so-called spatial light modulators provide programmable phase plates for quite some time now. We demonstrate that a fully controllable phase plate building on Harald Rose׳s legacy in aberration correction and electron optics in general would open an exciting field of research and applications.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.843
Times cited: 19
DOI: 10.1016/j.ultramic.2014.10.007
|
|
|
“The uptake and elimination of ZnO and CuO nanoparticles in Daphnia magna under chronic exposure scenarios”. Adam N, Leroux F, Knapen D, Bals S, Blust R, Water research 68, 249 (2015). http://doi.org/10.1016/j.watres.2014.10.001
Abstract: In this study, the uptake and elimination of ZnO and CuO nanoparticles in Daphnia magna was tested. Daphnids were exposed during 10 days to sublethal concentrations of ZnO and CuO nanoparticles and corresponding metal salts (ZnCl2 and CuCl2.2H2O), after which they were transferred to unexposed medium for another 10 days. At different times during the exposure and none-exposure, the total and internal zinc or copper concentration of the daphnids was determined and the nanoparticles were localized in the organism using electron microscopy. The exposure concentrations were characterized by measuring the dissolved, nanoparticle and aggregated fraction in the medium. The results showed that the ZnO nanoparticles quickly dissolved after addition to the medium. Contrarily, only a small fraction (corresponding to the dissolved metal salt) of the CuO nanoparticles dissolved, while most of these nanoparticles formed large aggregates. Despite an initial increase in zinc and copper concentration during the first 48 hour to 5 day exposure, the body concentration reached a plateau level that was comparable for the ZnO nanoparticles and ZnCl2, but much higher for the CuO nanoparticles (with visible aggregates accumulating in the gut) than CuCl2.2H2O. During the remaining exposure and subsequent none-exposure phase, the zinc and copper concentration decreased fast to concentrations comparable with the unexposed daphnids. The results indicate that D. magna can regulate its internal zinc and copper concentration after exposure to ZnO and CuO nanoparticles, similar as after exposure to metal salts. The combined dissolution, accumulation and toxicity results confirm that the toxicity of ZnO and CuO nanoparticles is caused by the dissolved fraction. Keywords nano; zinc; copper; dissolution; aggregation; electron microscopy
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Veterinary physiology and biochemistry
Impact Factor: 6.942
Times cited: 51
DOI: 10.1016/j.watres.2014.10.001
|
|
|
“Enhanced 77K vortex-pinning in YBa2Cu3O7−x films with Ba2YTaO6 and mixed Ba2YTaO6 + Ba2YNbO6 nano-columnar inclusions with irreversibility field to 11T”. Rizzo F, Augieri A, Angrisani Armenio A, Galluzzi V, Mancini A, Pinto V, Rufoloni A, Vannozzi A, Bianchetti M, Kursumovic A, MacManus-Driscoll JL, Meledin A, Van Tendeloo G, Celentano G, APL materials 4, 061101 (2016). http://doi.org/10.1063/1.4953436
Abstract: Pulsed laser deposited thin YBa2Cu3O7−x (YBCO) films with pinning additions of 5at.% Ba2YTaO6 (BYTO) were compared to films with 2.5at.% Ba2YTaO6 + 2.5at.% Ba2YNbO6 (BYNTO) additions. Excellent magnetic flux-pinning at 77 K was obtained with remarkably high irreversibility fields greater than 10T (YBCO-BYTO) and 11T (YBCO-BYNTO), representing the highest ever achieved values in YBCO films.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.335
Times cited: 19
DOI: 10.1063/1.4953436
|
|
|
“CVD diamond growth from nanodiamond seeds buried under a thin chromium layer”. Degutis G, Pobedinskas P, Turner S, Lu Y-G, Al Riyami S, Ruttens B, Yoshitake T, D'Haen J, Haenen K, Verbeeck J, Hardy A, Van Bael MK, Diamond and related materials 64, 163 (2016). http://doi.org/10.1016/j.diamond.2016.02.013
Abstract: This work presents a morphological and structural analysis of CVD diamond growth on silicon from nanodiamond seeds covered by a 50 nm thick chromium layer. The role of carbon diffusion as well as chromium and carbon silicide formation is analyzed. The local diamond environment is investigated by scanning transmission electron microscopy in combination with electron energy-loss spectroscopy. The evolution of the diamond phase composition (sp3/sp2) is evaluated by micro-Raman spectroscopy. Raman and X-ray diffraction analysis are used to identify the interfacial phases formed during CVD growth. Based upon the observed morphological and structural evolution, a diamond growth model from nanodiamond seeds buried beneath a thin Cr layer is proposed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.561
Times cited: 11
DOI: 10.1016/j.diamond.2016.02.013
|
|
|
“Microstructure and phase composition characterization in a Co38Ni33Al29 ferromagnetic shape memory alloy”. Lu JB, Schryvers D, Materials characterization 118, 9 (2016). http://doi.org/10.1016/j.matchar.2016.04.028
Abstract: Transmission electron microscopy was performed to investigate the microstructures of a secondary phase and its surrounding matrix in a Co38Ni33Al29 ferromagnetic shape memory alloy. The secondary phase shows a γ′ L12 structure exhibiting a dendritic morphology with enclosed B2 austenite regions while the matrix shows the L10 martensitic structure. A secondary phase-austenite-martensite sandwich structure with residual austenite ranging from several hundred nanometers to several micrometers wide is observed at the secondary phase-martensite interface due to the depletion of Co and enrichment of Al in the chemical gradient zone and the effect of the strong martensitic start temperature dependency of the element concentrations. The crystallographic orientation relationship of the secondary phase and the B2 austenite fits the Kurdjumov-Sachs relationship.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 2.714
Times cited: 3
DOI: 10.1016/j.matchar.2016.04.028
|
|
|
“Homogeneous Protein Analysis by Magnetic Core-Shell Nanorod Probes”. Schrittwieser S, Pelaz B, Parak WJ, Lentijo-Mozo S, Soulantica K, Dieckhoff J, Ludwig F, Altantzis T, Bals S, Schotter J, ACS applied materials and interfaces 8, 8893 (2016). http://doi.org/10.1021/acsami.5b11925
Abstract: Studying protein interactions is of vital importance both to fundamental biology research and to medical applications. Here, we report on the experimental proof of a universally applicable label-free homogeneous platform for rapid protein analysis. It is based on optically detecting changes in the rotational dynamics of magnetically agitated core-shell nanorods upon their specific interaction with proteins. By adjusting the excitation frequency, we are able to optimize the measurement signal for each analyte protein size. In addition, due to the locking of the optical signal to the magnetic excitation frequency, background signals are suppressed, thus allowing exclusive studies of processes at the nanoprobe surface only. We study target proteins (soluble domain of the human epidermal growth factor receptor 2 – sHER2) specifically binding to antibodies (trastuzumab) immobilized on the surface of our nanoprobes and demonstrate direct deduction of their respective sizes. Additionally, we examine the dependence of our measurement signal on the concentration of the analyte protein, and deduce a minimally detectable sHER2 concentration of 440 pM. For our homogeneous measurement platform, good dispersion stability of the applied nanoprobes under physiological conditions is of vital importance. To that end, we support our measurement data by theoretical modeling of the total particle-particle interaction energies. The successful implementation of our platform offers scope for applications in biomarker-based diagnostics as well as for answering basic biology questions.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 7.504
Times cited: 16
DOI: 10.1021/acsami.5b11925
|
|
|
“Heat-induced transformation of CdSe-CdS-ZnS coremultishell quantum dots by Zn diffusion into inner layers”. Yalcin AO, Goris B, van Dijk-Moes RJA, Fan Z, Erdamar AK, Tichelaar FD, Vlugt TJH, Van Tendeloo G, Bals S, Vanmaekelbergh D, Zandbergen HW, van Huis MA;, Chemical communications 51, 3320 (2015). http://doi.org/10.1039/C4CC08647C
Abstract: In this work, we investigate the thermal evolution of CdSeCdSZnS coremultishell quantum dots (QDs) in situ using transmission electron microscopy (TEM). Starting at a temperature of approximately 250 °C, Zn diffusion into inner layers takes place together with simultaneous evaporation of particularly Cd and S. As a result of this transformation, CdxZn1−xSeCdyZn1−yS coreshell QDs are obtained.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.319
Times cited: 21
DOI: 10.1039/C4CC08647C
|
|
|
“Direct imaging of boron segregation at dislocations in B:diamond heteroepitaxial films”. Turner S, Idrissi H, Sartori AF, Korneychuck S, Lu Y-G, Verbeeck J, Schreck M, Van Tendeloo G, Nanoscale 8, 2212 (2016). http://doi.org/10.1039/c5nr07535a
Abstract: A thin film of heavily B-doped diamond has been grown epitaxially by microwave plasma chemical vapor deposition on an undoped diamond layer, on top of a Ir/YSZ/Si(001) substrate stack, to study the boron segregation and boron environment at the dislocations present in the film. The density and nature of the dislocations were investigated by conventional and weak-beam dark-field transmission electron microscopy techniques, revealing the presence of two types of dislocations: edge and mixed-type 45 degrees dislocations. The presence and distribution of B in the sample was studied using annular dark-field scanning transmission electron microscopy and spatially resolved electron energy-loss spectroscopy. Using these techniques, a segregation of B at the dislocations in the film is evidenced, which is shown to be intermittent along the dislocation. A single edge-type dislocation was selected to study the distribution of the boron surrounding the dislocation core. By imaging this defect at atomic resolution, the boron is revealed to segregate towards the tensile strain field surrounding the edge-type dislocations. An investigation of the fine structure of the B-K edge at the dislocation core shows that the boron is partially substitutionally incorporated into the diamond lattice and partially present in a lower coordination (sp(2)-like hybridization).
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 7.367
Times cited: 15
DOI: 10.1039/c5nr07535a
|
|
|
“Ferroelastic switching in a layered-perovskite thin film”. Wang C, Ke X, Wang J, Liang R, Luo Z, Tian Y, Yi D, Zhang Q, Wang J, Han X-F, Van Tendeloo G, Chen L-Q, Nan C-W, Ramesh R, Zhang J, Nature communications 7, 10636 (2016). http://doi.org/10.1038/ncomms10636
Abstract: A controllable ferroelastic switching in ferroelectric/multiferroic oxides is highly desirable due to the non-volatile strain and possible coupling between lattice and other order parameter in heterostructures. However, a substrate clamping usually inhibits their elastic deformation in thin films without micro/nano-patterned structure so that the integration of the non-volatile strain with thin film devices is challenging. Here, we report that reversible in-plane elastic switching with a non-volatile strain of approximately 0.4% can be achieved in layered-perovskite Bi2WO6 thin films, where the ferroelectric polarization rotates by 90 degrees within four in-plane preferred orientations. Phase-field simulation indicates that the energy barrier of ferroelastic switching in orthorhombic Bi2WO6 film is ten times lower than the one in PbTiO3 films, revealing the origin of the switching with negligible substrate constraint. The reversible control of the in-plane strain in this layered-perovskite thin film demonstrates a new pathway to integrate mechanical deformation with nanoscale electronic and/or magnetoelectronic applications.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.124
Times cited: 40
DOI: 10.1038/ncomms10636
|
|
|
“Appearance of a conductive carbonaceous coating in a CO2dielectric barrier discharge and its influence on the electrical properties and the conversion efficiency”. Belov I, Paulussen S, Bogaerts A, Plasma sources science and technology 25, 015023 (2016). http://doi.org/10.1088/0963-0252/25/1/015023
Abstract: This work examines the properties of a dielectric barrier discharge (DBD) reactor, built for CO2 decomposition, by means of electrical characterization, optical emission spectroscopy and gas chromatography. The discharge, formed in an electronegative gas (such as CO2, but also O2), exhibits clearly different electrical characteristics, depending on the surface conductivity of the reactor walls. An asymmetric current waveform is observed in the metaldielectric (MD) configuration, with sparse high-current pulses in the positive half-cycle (HC) and a more uniform regime in the negative HC. This indicates that the discharge is operating in two alternating regimes with rather different properties. At high CO2 conversion regimes, a conductive coating is deposited on the dielectric. This so-called coated MD configuration yields a symmetric current waveform, with current peaks in both the positive and negative HCs. In a double-dielectric (DD) configuration, the current waveform is also symmetric, but without current peaks in both the positive and negative HC. Finally, the DD configuration with conductive coating on the inner surface of the outer dielectric, i.e. so-called coated DD, yields again an asymmetric current waveform, with current peaks in the negative HC. These different electrical characteristics are related to the presence of the conductive coating on the dielectric wall of the reactor and can be explained by an increase of the local barrier capacitance available for charge transfer. The different discharge regimes affect the CO2 conversion, more specifically, the CO2 conversion is lowest in the clean DD configuration. It is somewhat higher in the coated DD configuration, and still higher in the MD configuration. The clean and coated MD configuration, however, gave similar CO2 conversion. These results indicate that the conductivity of the dielectric reactor walls can highly promote the development of the high-amplitude discharge current pulses and subsequently the CO2 conversion.
Keywords: A1 Journal article; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 3.302
Times cited: 25
DOI: 10.1088/0963-0252/25/1/015023
|
|
|
“Heterogeneous interfacial chemical nature and bonds in a W-coated diamond/Al composite”. Ji G, Tan Z, Lu Y, Schryvers D, Li Z, Zhang D, Materials characterization 112, 129 (2016). http://doi.org/10.1016/j.matchar.2015.12.013
Abstract: Heterogeneous Al/Al4C3/Al2O3/diamond{111}, Al/nanolayered Al4C3/diamond{111} and Al12W particle/Al4C3/Al2O3/diamond{111} multi-interfaces have been developed at the nanoscale in a W-coated diamond/Al composite produced by vacuum hot pressing. The formation of nanoscale Al4C3 crystals is strongly associated with local O enrichment and can be further promoted by Al12W interfacial particles. The latter effectively contributes to enhance interfacial chemical bonding reducing interfacial thermal resistance and, in turn, enhancing thermal conductivity.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 2.714
Times cited: 7
DOI: 10.1016/j.matchar.2015.12.013
|
|
|
“BaHfO3artificial pinning centres in TFA-MOD-derived YBCO and GdBCO thin films”. Erbe M, Hänisch J, Hühne R, Freudenberg T, Kirchner A, Molina-Luna L, Damm C, Van Tendeloo G, Kaskel S, Schultz L, Holzapfel B, Superconductor science and technology 28, 114002 (2015). http://doi.org/10.1088/0953-2048/28/11/114002
Abstract: Chemical solution deposition (CSD) is a promising way to realize REBa2Cu3O7−x (REBCO;RE = rare earth (here Y, Gd))-coated conductors with high performance in applied magnetic fields. However, the preparation process contains numerous parameters which need to be tuned to achieve high-quality films. Therefore, we investigated the growth of REBCO thin films containing nanometre-scale BaHfO3 (BHO) particles as pinning centres for magnetic flux lines, with emphasis on the influence of crystallization temperature and substrate on the microstructure and superconductivity. Conductivity, microscopy and x-ray investigations show an enhanced performance of BHO nano-composites in comparison to pristine REBCO. Further, those measurements reveal the superiority of GdBCO to YBCO—e.g. by inductive critical current densities, Jc, at self-field and 77 K. YBCO is outperformed by more than 1 MA cm−2 with Jc values of up to 5.0 MA cm−2 for 265 nm thick layers of GdBCO(BHO) on lanthanum aluminate. Transport in-field Jc measurements demonstrate high pinning force maxima of around 4 GN m−3 for YBCO(BHO) and GdBCO(BHO). However, the irreversibility fields are appreciably higher for GdBCO. The critical temperature was not significantly reduced upon BHO addition to both YBCO and GdBCO, indicating a low tendency for Hf diffusion into the REBCO matrix. Angular-dependent Jc measurements show a reduction of the anisotropy in the same order of magnitude for both REBCO compounds. Theoretical models suggest that more than one sort of pinning centre is active in all CSD films.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.878
Times cited: 36
DOI: 10.1088/0953-2048/28/11/114002
|
|
|
“Portlandite crystal : bulk, bilayer, and monolayer structures”. Aierken Y, Sahin H, Iyikanat F, Horzum S, Suslu A, Chen B, Senger RT, Tongay S, Peeters FM, Physical review : B : condensed matter and materials physics 91, 245413 (2015). http://doi.org/10.1103/PhysRevB.91.245413
Abstract: Ca(OH)(2) crystals, well known as portlandite, are grown in layered form, and we found that they can be exfoliated on different substrates. We performed first principles calculations to investigate the structural, electronic, vibrational, and mechanical properties of bulk, bilayer, and monolayer structures of this material. Different from other lamellar structures such as graphite and transition-metal dichalcogenides, intralayer bonding in Ca(OH)(2) is mainly ionic, while the interlayer interaction remains a weak dispersion-type force. Unlike well-known transition-metal dichalcogenides that exhibit an indirect-to-direct band gap crossover when going from bulk to a single layer, Ca(OH)(2) is a direct band gap semiconductor independent of the number layers. The in-plane Young's modulus and the in-plane shear modulus of monolayer Ca(OH)(2) are predicted to be quite low while the in-plane Poisson ratio is larger in comparison to those in the monolayer of ionic crystal BN. We measured the Raman spectrum of bulk Ca(OH)(2) and identified the high-frequency OH stretching mode A(1g) at 3620 cm(-1). In this study, bilayer and monolayer portlandite [Ca(OH)(2)] are predicted to be stable and their characteristics are analyzed in detail. Our results can guide further research on ultrathin hydroxites.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 3.836
Times cited: 29
DOI: 10.1103/PhysRevB.91.245413
|
|
|
“Identification of the biologically active liquid chemistry induced by a nonthermal atmospheric pressure plasma jet”. Wende K, Williams P, Dalluge J, Van Gaens W, Aboubakr H, Bischof J, von Woedtke T, Goyal SM, Weltmann KD, Bogaerts A, Masur K, Bruggeman PJ;, Biointerphases 10, 029518 (2015). http://doi.org/10.1116/1.4919710
Abstract: The mechanism of interaction of cold nonequilibrium plasma jets with mammalian cells in physiologic liquid is reported. The major biological active species produced by an argon RF plasma jet responsible for cell viability reduction are analyzed by experimental results obtained through physical, biological, and chemical diagnostics. This is complemented with chemical kinetics modeling of the plasma source to assess the dominant reactive gas phase species. Different plasma chemistries are obtained by changing the feed gas composition of the cold argon based RF plasma jet from argon, humidified argon (0.27%), to argon/oxygen (1%) and argon/air (1%) at constant power. A minimal consensus physiologic liquid was used, providing isotonic and isohydric conditions and nutrients but is devoid of scavengers or serum constituents. While argon and humidified argon plasma led to the creation of hydrogen peroxide dominated action on the mammalian cells, argonoxygen and argonair plasma created a very different biological action and was characterized by trace amounts of hydrogen peroxide only. In particular, for the argonoxygen (1%), the authors observed a strong negative effect on mammalian cell proliferation and metabolism. This effect was distance dependent and showed a half life time of 30 min in a scavenger free physiologic buffer. Neither catalase and mannitol nor superoxide dismutase could rescue the cell proliferation rate. The strong distance dependency of the effect as well as the low water solubility rules out a major role for ozone and singlet oxygen but suggests a dominant role of atomic oxygen. Experimental results suggest that O reacts with chloride, yielding Cl2 − or ClO−. These chlorine species have a limited lifetime under physiologic conditions and therefore show a strong time dependent biological activity. The outcomes are compared with an argon MHz plasma jet (kinpen) to assess the differences between these (at least seemingly) similar plasma sources.
Keywords: A1 Journal article; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 2.603
Times cited: 137
DOI: 10.1116/1.4919710
|
|
|
“Environmental changes in MoTe2 excitonic dynamics by defects-activated molecular interaction”. Chen B, Sahin H, Suslu A, Ding L, Bertoni MI, Peeters FM, Tongay S, ACS nano 9, 5326 (2015). http://doi.org/10.1021/acsnano.5b00985
Abstract: Monolayers of group VI transition metal dichalcogenides possess direct gaps in the visible spectrum with the exception of MoTe2, where its gap is suitably located in the infrared region but its stability is of particular interest, as tellurium compounds are acutely sensitive to oxygen exposure. Here, our environmental (time-dependent) measurements reveal two distinct effects on MoTe2 monolayers: For weakly luminescent monolayers, photoluminescence signal and optical contrast disappear, as if they are decomposed, but yet remain intact as evidenced by AFM and Raman measurements. In contrast, strongly luminescent monolayers retain their optical contrast for a prolonged amount of time, while their PL peak blue-shifts and PL intensity saturates to slightly lower values. Our X-ray photoelectron spectroscopy measurements and DFT calculations suggest that the presence of defects and functionalization of these defect sites with O-2 molecules strongly dictate their material properties and aging response by changing the excitonic dynamics due to deep or shallow states that are created within the optical band gap. Presented results not only shed light on environmental effects on fundamental material properties and excitonic dynamics of MoTe2 monolayers but also highlight striking material transformation for metastable 20 systems such as WTe2, silicone, and phosphorene.
Keywords: A1 Journal article; Engineering sciences. Technology; Condensed Matter Theory (CMT)
Impact Factor: 13.942
Times cited: 150
DOI: 10.1021/acsnano.5b00985
|
|
|
“Electronic band structures and native point defects of ultrafine ZnO nanocrystals”. Zeng Y-J, Schouteden K, Amini MN, Ruan S-C, Lu Y-F, Ye Z-Z, Partoens B, Lamoen D, Van Haesendonck C, ACS applied materials and interfaces 7, 10617 (2015). http://doi.org/10.1021/acsami.5b02545
Abstract: Ultrafine ZnO nanocrystals with a thickness down to 0.25 nm are grown by a metalorganic chemical vapor deposition method. Electronic band structures and native point defects of ZnO nanocrystals are studied by a combination of scanning tunneling microscopy/spectroscopy and first-principles density functional theory calculations. Below a critical thickness of nm ZnO adopts a graphitic-like structure and exhibits a wide band gap similar to its wurtzite counterpart. The hexagonal wurtzite structure, with a well-developed band gap evident from scanning tunneling spectroscopy, is established for a thickness starting from similar to 1.4 nm. With further increase of the thickness to 2 nm, V-O-V-Zn defect pairs are easily produced in ZnO nanocrystals due to the self-compensation effect in highly doped semiconductors.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Condensed Matter Theory (CMT)
Impact Factor: 7.504
Times cited: 15
DOI: 10.1021/acsami.5b02545
|
|