Records |
Author |
Egoavil, R.; Gauquelin, N.; Martinez, G.T.; Van Aert, S.; Van Tendeloo, G.; Verbeeck, J. |
Title |
Atomic resolution mapping of phonon excitations in STEM-EELS experiments |
Type |
A1 Journal article |
Year |
2014 |
Publication |
Ultramicroscopy |
Abbreviated Journal |
Ultramicroscopy |
Volume |
147 |
Issue |
|
Pages |
1-7 |
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
Abstract |
Atomically resolved electron energy-loss spectroscopy experiments are commonplace in modern aberration-corrected transmission electron microscopes. Energy resolution has also been increasing steadily with the continuous improvement of electron monochromators. Electronic excitations however are known to be delocalized due to the long range interaction of the charged accelerated electrons with the electrons in a sample. This has made several scientists question the value of combined high spatial and energy resolution for mapping interband transitions and possibly phonon excitation in crystals. In this paper we demonstrate experimentally that atomic resolution information is indeed available at very low energy losses around 100 meV expressed as a modulation of the broadening of the zero loss peak. Careful data analysis allows us to get a glimpse of what are likely phonon excitations with both an energy loss and gain part. These experiments confirm recent theoretical predictions on the strong localization of phonon excitations as opposed to electronic excitations and show that a combination of atomic resolution and recent developments in increased energy resolution will offer great benefit for mapping phonon modes in real space. |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
Amsterdam |
Editor |
|
Language |
|
Wos |
000343157400001 |
Publication Date |
2014-05-29 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
0304-3991; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
2.843 |
Times cited |
22 |
Open Access |
|
Notes |
246102 IFOX; 278510 VORTEX; 246791 COUNTATOMS; Hercules; 312483 ESTEEM2; esteem2jra3 ECASJO; |
Approved |
Most recent IF: 2.843; 2014 IF: 2.436 |
Call Number |
UA @ lucian @ c:irua:118332UA @ admin @ c:irua:118332 |
Serial |
177 |
Permanent link to this record |
|
|
|
Author |
Cabana, L.; Gonzalez-Campo, A.; Ke, X.; Van Tendeloo, G.; Nunez, R.; Tobias, G. |
Title |
Efficient Chemical Modification of Carbon Nanotubes with Metallacarboranes |
Type |
A1 Journal article |
Year |
2015 |
Publication |
Chemistry: a European journal |
Abbreviated Journal |
Chem-Eur J |
Volume |
21 |
Issue |
21 |
Pages |
16792-16795 |
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
Abstract |
As-produced single-walled carbon nanotubes (SWCNTs) tend to aggregate in bundles due to pi-pi interactions. Several approaches are nowadays available to debundle, at least partially, the nanotubes through surface modification by both covalent and noncovalent approaches. Herein, we explore different strategies to afford an efficient covalent functionalization of SWCNTs with cobaltabisdicarbollide anions. Aberration-corrected HRTEM analysis reveals the presence of metallacarboranes along the walls of the SWCNTs. This new family of materials presents an outstanding water dispersibility that facilitates its processability for potential applications. |
Address |
Institut de Ciencia de Materials de Barcelona (ICMAB-CSIC), Campus Universitari de la UAB. 08193, Bellaterra (Spain). gerard.tobias@icmab.es |
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
|
Editor |
|
Language |
|
Wos |
000366501600011 |
Publication Date |
2015-10-06 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
0947-6539; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
5.317 |
Times cited |
5 |
Open Access |
|
Notes |
The research leading to these results received financial support from MINECO (MAT2014-53500-R; CTQ2013-44670-R), Generalitat de Catalunya (2014/SGR/149), and from the European Commission under the FP7 ITN Marie-Curie Network programme RADDEL (grant agreement 290023), the Integrated Infrastructure Initiative No. 262348 European Soft Matter Infrastructure (ESMI) and the European Research Council, ERC Grant No 246791-COUNTATOMS. A.G.C. thanks the CSIC for the JAE-DOC grant. |
Approved |
Most recent IF: 5.317; 2015 IF: 5.731 |
Call Number |
c:irua:129215 |
Serial |
3964 |
Permanent link to this record |
|
|
|
Author |
Shestakov, M.V.; Meledina, M.; Turner, S.; Tikhomirov, V.K.; Verellen, N.; Rodríguez, V.D.; Velázquez, J.J.; Van Tendeloo, G.; Moshchalkov, V.V. |
Title |
The size and structure of Ag particles responsible for surface plasmon effects and luminescence in Ag homogeneously doped bulk glass |
Type |
A1 Journal article |
Year |
2013 |
Publication |
Journal of applied physics |
Abbreviated Journal |
J Appl Phys |
Volume |
114 |
Issue |
7 |
Pages |
073102-73105 |
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
Abstract |
As-prepared and heat-treated oxyfluoride glasses, co-doped with Ag nanoclusters/nanoparticles, are prepared at 0.15 at. % Ag concentration. The as-prepared glass shows an absorption band in the UV/violet attributed to the presence of amorphous Ag nanoclusters with an average size of 1.1 nm. The luminescence spectra of the untreated glass can also be ascribed to these Ag nanoclusters. Upon heat-treatment, the clusters coalesce into Ag nanoparticles with an average size of 2.3 nm, and the glasses show an extra surface plasmon absorption band in the visible. These particles, however, cease to emit due to ascribing plasmonic properties of bulk silver. |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
American Institute of Physics |
Place of Publication |
New York, N.Y. |
Editor |
|
Language |
|
Wos |
000323510900003 |
Publication Date |
2013-08-16 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
0021-8979; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
2.068 |
Times cited |
19 |
Open Access |
|
Notes |
Fwo |
Approved |
Most recent IF: 2.068; 2013 IF: 2.185 |
Call Number |
UA @ lucian @ c:irua:109455 |
Serial |
3031 |
Permanent link to this record |
|
|
|
Author |
McCalla, E.; Abakumov, A.; Rousse, G.; Reynaud, M.; Sougrati, M.T.; Budic, B.; Mahmoud, A.; Dominko, R.; Van Tendeloo, G.; Hermann, R.P.; Tarascon, J.M.; |
Title |
Novel complex stacking of fully-ordered transition metal layers in Li4FeSbO6 materials |
Type |
A1 Journal article |
Year |
2015 |
Publication |
Chemistry of materials |
Abbreviated Journal |
Chem Mater |
Volume |
27 |
Issue |
27 |
Pages |
1699-1708 |
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
Abstract |
As part of a broad project to explore Li4MM'O-6 materials (with M and M' being selected from a wide variety of metals) as positive electrode materials for Li-ion batteries, the structures of Li4FeSbO6 materials with both stoichiometric and slightly deficient lithium contents are studied here. For lithium content varying from 3.8 to 4.0, the color changes from yellow to black and extra superstructure peaks are seen in the XRD patterns. These extra peaks appear as satellites around the four superstructure peaks affected by the stacking of the transition metal atoms. Refinements of both XRD and neutron scattering patterns show a nearly perfect ordering of Li, Fe, and Sb in the transition metal layers of all samples, although these refinements must take the stacking faults into account in order to extract information about the structure of the TM layers. The structure of the most lithium rich sample, where the satellite superstructure peaks are seen, was determined with the help of HRTEM, XRD, and neutron scattering. The satellites arise due to a new stacking sequence where not all transition metal layers are identical but instead two slightly different compositions stack in an AABB sequence giving a unit cell that is four times larger than normal for such monoclinic layered materials. The more lithium deficient samples are found to contain metal site vacancies based on elemental analysis and Mossbauer spectroscopy results. The significant changes in physical properties are attributed to the presence of these vacancies. This study illustrates the great importance of carefully determining the final compositions in these materials, as very small differences in compositions may have large impacts on structures and properties. |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
|
Editor |
|
Language |
|
Wos |
000350919000032 |
Publication Date |
2015-02-12 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
0897-4756;1520-5002; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
9.466 |
Times cited |
22 |
Open Access |
|
Notes |
|
Approved |
Most recent IF: 9.466; 2015 IF: 8.354 |
Call Number |
c:irua:125469 |
Serial |
2373 |
Permanent link to this record |
|
|
|
Author |
Sun, M.-H.; Zhou, J.; Hu, Z.-Y.; Chen, L.-H.; Li, L.-Y.; Wang, Y.-D.; Xie, Z.-K.; Turner, S.; Van Tendeloo, G.; Hasan, T.; Su, B.-L. |
Title |
Hierarchical zeolite single-crystal reactor for excellent catalytic efficiency |
Type |
A1 Journal article |
Year |
2020 |
Publication |
Matter |
Abbreviated Journal |
|
Volume |
3 |
Issue |
4 |
Pages |
1226-1245 |
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
Abstract |
As a size- and shape-selective catalyst, zeolites are widely used in petroleum and fine-chemicals processing. However, their small micropores severely hinder molecular diffusion and are sensitive to coke formation. Hierarchically porous zeolite single crystals with fully interconnected, ordered, and tunable multimodal porosity at macro-, meso-, and microlength scale, like in leaves, offer the ideal solution. However, their synthesis remains highly challenging. Here, we report a versatile confined zeolite crystallization process to achieve these superior properties. Such zeolite single crystals lead to significantly improved mass transport properties by shortening the diffusion length while maintaining shape-selective properties, endowing them with a high efficiency of zeolite crystals, enhanced catalytic activities and lifetime, highly reduced coke formation, and reduced deactivation rate in bulky-molecule reactions and methanol-to-olefins process. Their industrial utilization can lead to the design of innovative and intensified reactors and processes with highly enhanced efficiency and minimum energy consumption. |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
|
Editor |
|
Language |
|
Wos |
000581132600021 |
Publication Date |
2020-08-12 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
|
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
|
Times cited |
|
Open Access |
OpenAccess |
Notes |
|
Approved |
Most recent IF: NA |
Call Number |
UA @ admin @ c:irua:174329 |
Serial |
6727 |
Permanent link to this record |
|
|
|
Author |
Ding, Y.; Maitra, S.; Arenas Esteban, D.; Bals, S.; Vrielinck, H.; Barakat, T.; Roy, S.; Van Tendeloo, G.; Liu, J.; Li, Y.; Vlad, A.; Su, B.-L. |
Title |
Photochemical production of hydrogen peroxide by digging pro-superoxide radical carbon vacancies in carbon nitride |
Type |
A1 Journal article |
Year |
2022 |
Publication |
Cell reports physical science |
Abbreviated Journal |
|
Volume |
3 |
Issue |
5 |
Pages |
100874-17 |
Keywords |
A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT) |
Abstract |
Artificial photosynthesis of H2O2, an environmentally friendly oxidant and a clean fuel, holds great promise. However, improving its efficiency and stability for industrial implementation remains highly challenging. Here, we report the visible-light H2O2 artificial photosynthesis by digging pro-superoxide radical carbon vacancies in three-dimensional hierarchical porous g-C3N4 through a simple hydrolysis-freeze-drying-thermal treatment. A significant electronic structure change is revealed upon the implantation of carbon vacancies, broadening visible-light absorption and facilitating the photogenerated charge separation. The strong electron affinity of the carbon vacancies promotes superoxide radical (O-center dot(2)-) formation, significantly boosting the H2O2 photocatalytic production. The developed photocatalyst shows an H2O2 evolution rate of 6287.5 mM g(-1) h(-1) under visible-light irradiation with a long cycling stability being the best-performing photocatalyst among all reported g-C3N4-based systems. Our work provides fundamental insight into highly active and stable photocatalysts with great potential for safe industrial H2O2 production. |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
|
Editor |
|
Language |
|
Wos |
000805830100006 |
Publication Date |
2022-04-28 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
|
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
|
Times cited |
12 |
Open Access |
OpenAccess |
Notes |
Y.D. thanks the China Scholarship Council (201808310127) for financial support. This work is financially supported by the National Natural Science Foundation of China (U1663225) , Program for Changjiang Scholars and Innovative Research Team in University (IRT_15R52) of the Chinese Ministry of Education, Program of Introducing Talents of Discipline to Universities-Plan 111 (grant no. B20002) from the Ministry of Science and Technology and the Ministry of Education of China, and the National Key R&D Program of China (2016YFA0202602) . This research was also supported by the European Commission Interreg V France-Wallonie-Vlaanderen project “DepollutAir”. |
Approved |
Most recent IF: NA |
Call Number |
UA @ admin @ c:irua:189706 |
Serial |
7090 |
Permanent link to this record |
|
|
|
Author |
Lottini, E.; López-Ortega, A.; Bertoni, G.; Turner, S.; Meledina, M.; Van Tendeloo, G.; de Julián Fernández, C.; Sangregorio, C. |
Title |
Strongly Exchange Coupled Core|Shell Nanoparticles with High Magnetic Anisotropy: A Strategy toward Rare-Earth-Free Permanent Magnets |
Type |
A1 Journal article |
Year |
2016 |
Publication |
Chemistry of materials |
Abbreviated Journal |
Chem Mater |
Volume |
28 |
Issue |
28 |
Pages |
4214-4222 |
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
Abstract |
Antiferromagnetic(AFM)|ferrimagnetic(FiM) core|shell (CS) nanoparticles (NPs) of formula Co0.3Fe0.7O|Co0.6Fe2.4O4 with mean diameter from 6 to 18 nm have been synthesized through a one-pot thermal decomposition process. The CS structure has been generated by topotaxial oxidation of the core region, leading to the formation of a highly monodisperse single inverted AFM|FiM CS system with variable AFM-core diameter and constant FiM-shell thickness (~2 nm). The sharp interface, the high structural matching between both phases and the good crystallinity of the AFM material have been structurally demonstrated and are corroborated by the robust exchange-coupling between AFM and FiM phases, which gives rise to one among the largest exchange bias (HE) values ever reported for CS NPs (8.6 kOe) and to a strongly enhanced coercive field (HC). In addition, the investigation of the magnetic properties as a function of the AFM-core size (dAFM), revealed a non-monotonous trend of both HC and HE, which display a maximum value for dAFM = 5 nm (19.3 and 8.6 kOe, respectively). These properties induce a huge improvement of the capability of storing energy of the material, a result which suggests that the combination of highly anisotropic AFM|FiM materials can be an efficient strategy towards the realization of novel Rare Earth-free permanent magnets. |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
|
Editor |
|
Language |
|
Wos |
000378973100013 |
Publication Date |
2016-05-20 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
0897-4756 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
9.466 |
Times cited |
48 |
Open Access |
|
Notes |
This work was supported by the EU-FP7 through NANOPYME Project (No. 310516) and Integrated Infrastructure Initiative ESTEEM2 (No. 312483). S.T. gratefully acknowledges the FWO Flanders for a post-doctoral scholarship.; esteem2_ta |
Approved |
Most recent IF: 9.466 |
Call Number |
c:irua:134084 c:irua:134084 |
Serial |
4092 |
Permanent link to this record |
|
|
|
Author |
Bals, S.; Van Tendeloo, G.; Kisielowski, C. |
Title |
A new approach for electron tomography: annular dark-field transmission electron microscopy |
Type |
A1 Journal article |
Year |
2006 |
Publication |
Advanced materials |
Abbreviated Journal |
Adv Mater |
Volume |
18 |
Issue |
7 |
Pages |
892-895 |
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
Abstract |
Annular dark-field transmission electron microscopy uses an annular objective aperture that blocks the central beam and all electrons scattered up to a certain serniangle. A contrast suitable for electron tomography is generated and 3D reconstructions of CdTe tetrapods and C nanotubes (see figure) are successfully obtained. With short exposure times and high contrast, the technique could be useful not only for materials science, but also for biological applications. |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
Weinheim |
Editor |
|
Language |
|
Wos |
000236950500013 |
Publication Date |
2006-03-24 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
0935-9648;1521-4095; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
19.791 |
Times cited |
53 |
Open Access |
|
Notes |
Fwo |
Approved |
Most recent IF: 19.791; 2006 IF: NA |
Call Number |
UA @ lucian @ c:irua:58258 |
Serial |
2306 |
Permanent link to this record |
|
|
|
Author |
Verbist, K.; Van Tendeloo, G.; Ye, M.; Mehbod, M.; Deltour, R. |
Title |
TEM study of YBa2Cu3O7-x thin films with Zn and Fe |
Type |
A1 Journal article |
Year |
1994 |
Publication |
Physica: C : superconductivity |
Abbreviated Journal |
Physica C |
Volume |
235 |
Issue |
1 |
Pages |
663-664 |
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
Abstract |
Analytical and high resolution electron microscopy have been used to study the effect of Zn- and Fe-doping on the micro structure of [001] YBa2Cu3O7-x thin films on [001] MgO substrates grown by magnetron sputtering. Special attention was paid to the presence of second phase inclusions and surface outgrowths such as CuO, Y2Ba1Cu1O5-x, Y2O3 in order to establish a relationship with the critical current density. |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
Amsterdam |
Editor |
|
Language |
|
Wos |
A1994QA39000261 |
Publication Date |
2002-10-17 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
0921-4534; |
ISBN |
|
Additional Links |
UA library record; WoS full record |
Impact Factor |
0.942 |
Times cited |
|
Open Access |
|
Notes |
|
Approved |
no |
Call Number |
UA @ lucian @ c:irua:10047 |
Serial |
3492 |
Permanent link to this record |
|
|
|
Author |
Rizzo, F.; Augieri, A.; Kursumovic, A.; Bianchetti, M.; Opherden, L.; Sieger, M.; Huehne, R.; Haenisch, J.; Meledin, A.; Van Tendeloo, G.; MacManus-Driscoll, J.L.; Celentano, G. |
Title |
Pushing the limits of applicability of REBCO coated conductor films through fine chemical tuning and nanoengineering of inclusions |
Type |
A1 Journal article |
Year |
2018 |
Publication |
Nanoscale |
Abbreviated Journal |
Nanoscale |
Volume |
10 |
Issue |
17 |
Pages |
8187-8195 |
Keywords |
A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT) |
Abstract |
An outstanding current carrying performance (namely critical current density, J(c)) over a broad temperature range of 10-77 K for magnetic fields up to 12 T is reported for films of YBa2Cu3O7-x with Ba2Y(Nb,Ta)O-6 inclusion pinning centres (YBCO-BYNTO) and thicknesses in the range of 220-500 nm. J(c) values of 10 MA cm(-2) were measured at 30 K – 5 T and 10 K – 9 T with a corresponding maximum of the pinning force density at 10 K close to 1 TN m(-3). The system is very flexible regarding properties and microstructure tuning, and the growth window for achieving a particular microstructure is wide, which is very important for industrial processing. Hence, the dependence of J(c) on the magnetic field angle was readily controlled by fine tuning the pinning microstructure. Transmission electron microscopy (TEM) analysis highlighted that higher growth rates induce more splayed and denser BYNTO nanocolumns with a matching field as high as 5.2 T. Correspondingly, a strong peak at the B||c-axis is noticed when the density of vortices is lower than the nanocolumn density. YBCO-BYNTO is a very robust and reproducible composite system for high-current coated conductors over an extended range of magnetic fields and temperatures. |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
Cambridge |
Editor |
|
Language |
|
Wos |
000432261400037 |
Publication Date |
2018-03-26 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
2040-3364 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
7.367 |
Times cited |
9 |
Open Access |
OpenAccess |
Notes |
; This work was partially financially supported by EUROTAPES, a collaborative project funded by the European Commission's Seventh Framework Program (FP7/ 2007-2013) under Grant Agreement No. 280432. This work has been partially carried out within the framework of the EUROfusion Consortium and has received funding from the Euratom research and training programme 2014-2018 under grant agreement no. 633053. The views and opinions expressed herein do not necessarily reflect those of the European Commission. ; |
Approved |
Most recent IF: 7.367 |
Call Number |
UA @ lucian @ c:irua:151520 |
Serial |
5038 |
Permanent link to this record |
|
|
|
Author |
Dominiczak, M.; Ruyter, A.; Limelette, P.; Monot-Laffez, I.; Giovannelli, F.; Rossell, M.D.; Van Tendeloo, G. |
Title |
Effects of nanocracks on the magnetic and electrical properties of La0.8Sr0.2MnO3 single crystals |
Type |
A1 Journal article |
Year |
2009 |
Publication |
Solid state communications |
Abbreviated Journal |
Solid State Commun |
Volume |
149 |
Issue |
37/38 |
Pages |
1543-1548 |
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
Abstract |
An investigation of the physical properties of La0.8Sr0.2MnO3 single crystals grown by the molten zone technique is realized close to the metal-to-insulator transition temperature (TMI). In this paper, we review the effect of the structural defects through magnetotransport and local magnetic microstructures. From electron microscopy observations, some nanocrack defects (i.e. defects at a nanometer scale) were found, essentially in the center part of the single crystals. At room temperature, magnetic force microscopy measurements have shown that the absence of defects allowed a magnetic ordering of the domains at the crystal edge, which is the best-crystallized region. In addition, the magnetization loops have permitted us to verify that the crystal was ferromagnetically weaker in the center. On analyzing the electrical resistivity data, we observed in the linear current regime a sensitive variation of the resistivity due to defects, by comparing the center and the edge of the material at TMI. Additionally, at strong current, non-linearity phenomena have been supposed to be related to local heating. Finally, we discuss the structural disorder effect on the relaxation of the ferromagnetic domains. |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
New York, N.Y. |
Editor |
|
Language |
|
Wos |
000269679500012 |
Publication Date |
2009-06-09 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
0038-1098; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
1.554 |
Times cited |
3 |
Open Access |
|
Notes |
|
Approved |
Most recent IF: 1.554; 2009 IF: 1.837 |
Call Number |
UA @ lucian @ c:irua:78289 |
Serial |
868 |
Permanent link to this record |
|
|
|
Author |
Gehrke, K.; Moshnyaga, V.; Samwer, K.; Lebedev, O.I.; Verbeeck, J.; Kirilenko, D.; Van Tendeloo, G. |
Title |
Interface controlled electronic variations in correlated heterostructures |
Type |
A1 Journal article |
Year |
2010 |
Publication |
Physical review : B : condensed matter and materials physics |
Abbreviated Journal |
Phys Rev B |
Volume |
82 |
Issue |
11 |
Pages |
113101,1-113101,4 |
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
Abstract |
An interface modification of (LaCa)MnO3-BaTiO3 superlattices was found to massively influence magnetic and magnetotransport properties. Moreover it determines the crystal structure of the manganite layers, changing it from orthorhombic (Pnma) for the conventional superlattice (cSL), to rhombohedral (R3̅ c) for the modified one (mSL). While the cSL shows extremely nonlinear ac transport, the mSL is an electrically homogeneous material. The observations go beyond an oversimplified picture of dead interface layers and evidence the importance of electronic correlations at perovskite interfaces. |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
|
Editor |
|
Language |
|
Wos |
000281643200001 |
Publication Date |
2010-09-07 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
1098-0121;1550-235X; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
3.836 |
Times cited |
9 |
Open Access |
|
Notes |
This work was supported by DFG via SFB 602, TPA2. |
Approved |
Most recent IF: 3.836; 2010 IF: 3.774 |
Call Number |
UA @ lucian @ c:irua:84249UA @ admin @ c:irua:84249 |
Serial |
1691 |
Permanent link to this record |
|
|
|
Author |
Maignan, A.; Singh, K.; Simon, C.; Lebedev, O.I.; Martin, C.; Tan, H.; Verbeeck, J.; Van Tendeloo, G. |
Title |
Magnetic and magnetodielectric properties of erbium iron garnet ceramic |
Type |
A1 Journal article |
Year |
2013 |
Publication |
Journal of applied physics |
Abbreviated Journal |
J Appl Phys |
Volume |
113 |
Issue |
3 |
Pages |
033905-5 |
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
Abstract |
An Er3Fe5O12 ceramic has been sintered in oxygen atmosphere at 1400 °C for dielectric measurements. Its structural quality at room temperature has been checked by combining transmission electron microscopy and X-ray diffraction. It crystallizes in the cubic space group Ia3d with a = 12.3488(1). The dielectric permittivity ([variantgreekepsilon]′) and losses (tan δ) measurements as a function of temperature reveal the existence of two anomalies, a broad one between 110 K and 80 K, attributed to the Er3+ spin reorientation, and a second sharper feature at about 45 K associated to the appearance of irreversibility on the magnetic susceptibility curves. In contrast to the lack of magnetic field impact on [variantgreekepsilon]′ for the former anomaly, a complex magnetic field effect has been evidenced below 45 K. The isothermal [variantgreekepsilon]′(H) curves show the existence of positive magnetodielectric effect, reaching a maximum of 0.14% at 3 T and 10 K. Its magnitude decreases as H is further increased. Interestingly, for the lowest H values, a linear regime in the [variantgreekepsilon]′(H) curve is observed. From this experimental study, it is concluded that the [variantgreekepsilon]′ anomaly, starting above the compensation temperature Tc (75 K) and driven by the internal magnetic field, is not sensitive to an applied external magnetic field. Thus, below 45 K, it is the magnetic structure which is responsible for the coupling between spin and charge in this iron garnet. |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
American Institute of Physics |
Place of Publication |
New York, N.Y. |
Editor |
|
Language |
|
Wos |
000313670600042 |
Publication Date |
2013-01-16 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
0021-8979; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
2.068 |
Times cited |
15 |
Open Access |
|
Notes |
Vortex; Countatoms ECASJO_; |
Approved |
Most recent IF: 2.068; 2013 IF: 2.185 |
Call Number |
UA @ lucian @ c:irua:106182UA @ admin @ c:irua:106182 |
Serial |
1861 |
Permanent link to this record |
|
|
|
Author |
Verbeeck, J.; Lebedev, O.I.; Van Tendeloo, G.; Silcox, J.; Mercey, B.; Hervieu, M.; Haghiri-Gosnet, A.M. |
Title |
Electron energy-loss spectroscopy study of a (LaMnO3)8(SrMnO3)4 heterostructure |
Type |
A1 Journal article |
Year |
2001 |
Publication |
Applied physics letters |
Abbreviated Journal |
Appl Phys Lett |
Volume |
79 |
Issue |
13 |
Pages |
2037-2039 |
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
Abstract |
An epitaxially grown heterostructure consisting of alternating layers of LaMnO3 (8 unit cells) and SrMnO3 (4 unit cells) on a SrTiO3 substrate has been studied by a combination of electron energy-loss spectroscopy (EELS) and high-resolution transmission electron microscopy (HRTEM) on an atomic scale. Excitation edges of all elements are captured with subnanometer spatial accuracy, and parametrized to obtain chemical profiles. The fine-edge structure of O K and Mn L-2,L-3 edges are interpreted as signatures of the local electronic structure and show a spatial modulation of the concentration of holes with O 2p character. The chemical concentration is found to be different for the bottom and top interface of a SrMnO3 layer. HRTEM complements the EELS results and confirms the asymmetry of the interfaces. (C) 2001 American Institute of Physics. |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
American Institute of Physics |
Place of Publication |
New York, N.Y. |
Editor |
|
Language |
|
Wos |
000171015200036 |
Publication Date |
2002-07-26 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
0003-6951; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
3.411 |
Times cited |
19 |
Open Access |
|
Notes |
|
Approved |
Most recent IF: 3.411; 2001 IF: 3.849 |
Call Number |
UA @ lucian @ c:irua:54799UA @ admin @ c:irua:54799 |
Serial |
933 |
Permanent link to this record |
|
|
|
Author |
Egoavil, R.; Tan, H.; Verbeeck, J.; Bals, S.; Smith, B.; Kuiper, B.; Rijnders, G.; Koster, G.; Van Tendeloo, G. |
Title |
Atomic scale investigation of a PbTiO3/SrRuO3/DyScO3 heterostructure |
Type |
A1 Journal article |
Year |
2013 |
Publication |
Applied physics letters |
Abbreviated Journal |
Appl Phys Lett |
Volume |
102 |
Issue |
22 |
Pages |
223106-5 |
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
Abstract |
An epitaxial PbTiO3 thin film grown on self-organized crystalline SrRuO3 nanowires deposited on a DyScO3 substrate with ordered DyO and ScO2 chemical terminations is investigated by transmission electron microscopy. In this PbTiO3/SrRuO3/DyScO3 heterostructure, the SrRuO3 nanowires are assumed to grow on only one type of substrate termination. Here, we report on the structure, morphology, and chemical composition analysis of this heterostructure. Electron energy loss spectroscopy reveals the exact termination sequence in this complex structure. The energy loss near-edge structure of the Ti-L-2,L-3, Sc-L-2,L-3, and O K edges shows intrinsic interfacial electronic reconstruction. Furthermore, PbTiO3 domain walls are observed to start at the end of the nanowires resulting in atomic steps on the film surface. (C) 2013 AIP Publishing LLC. |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
American Institute of Physics |
Place of Publication |
New York, N.Y. |
Editor |
|
Language |
|
Wos |
000320621600070 |
Publication Date |
2013-06-05 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
0003-6951; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
3.411 |
Times cited |
12 |
Open Access |
|
Notes |
Ifox; Esteem2; Countatoms; Vortex; esteem2jra3 ECASJO; |
Approved |
Most recent IF: 3.411; 2013 IF: 3.515 |
Call Number |
UA @ lucian @ c:irua:109606UA @ admin @ c:irua:109606 |
Serial |
185 |
Permanent link to this record |
|
|
|
Author |
Vlasov, I.I.; Shenderova, O.; Turner, S.; Lebedev, O.I.; Basov, A.A.; Sildos, I.; Rähn, M.; Shiryaev, A.A.; Van Tendeloo, G. |
Title |
Nitrogen and luminescent nitrogen-vacancy defects in detonation nanodiamond |
Type |
A1 Journal article |
Year |
2010 |
Publication |
Small |
Abbreviated Journal |
Small |
Volume |
6 |
Issue |
5 |
Pages |
687-694 |
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
Abstract |
An efficient method to investigate the microstructure and spatial distribution of nitrogen and nitrogen-vacancy (N-V) defects in detonation nanodiamond (DND) with primary particle sizes ranging from approximately 3 to 50 nm is presented. Detailed analysis reveals atomic nitrogen concentrations as high as 3 at% in 50% of diamond primary particles with sizes smaller than 6 nm. A non-uniform distribution of nitrogen within larger primary DND particles is also presented, indicating a preference for location within the defective central part or at twin boundaries. A photoluminescence (PL) spectrum with well-pronounced zero-phonon lines related to the N-V centers is demonstrated for the first time for electron-irradiated and annealed DND particles at continuous laser excitation. Combined Raman and PL analysis of DND crystallites dispersed on a Si substrate leads to the conclusion that the observed N-V luminescence originates from primary particles with sizes exceeding 30 nm. These findings demonstrate that by manipulation of the size/nitrogen content in DND there are prospects for mass production of nanodiamond photoemitters based on bright and stable luminescence from nitrogen-related defects. |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
Weinheim |
Editor |
|
Language |
|
Wos |
000275972400013 |
Publication Date |
2010-01-27 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
1613-6810;1613-6829; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
8.643 |
Times cited |
84 |
Open Access |
|
Notes |
Esteem 026019 |
Approved |
Most recent IF: 8.643; 2010 IF: 7.336 |
Call Number |
UA @ lucian @ c:irua:82364 |
Serial |
2341 |
Permanent link to this record |
|
|
|
Author |
Meledin, A.; Turner, S.; Cayado, P.; Mundet, B.; Solano, E.; Ricart, S.; Ros, J.; Puig, T.; Obradors, X.; Van Tendeloo, G. |
Title |
Unique nanostructural features in Fe, Mn-doped YBCO thin films |
Type |
A1 Journal article |
Year |
2016 |
Publication |
Superconductor science and technology |
Abbreviated Journal |
Supercond Sci Tech |
Volume |
29 |
Issue |
29 |
Pages |
125009 |
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
Abstract |
An attempt to grow a thin epitaxial composite film of YBa2Cu3O7−δ (YBCO) with spinel MnFe2O4 (MFO) nanoparticles on a LAO substrate using the CSD approach resulted in a decomposition of the spinel and various doping modes of YBCO with the Fe and Mn cations. These nanostructural effects lead to a lowering of T c and a slight J c increase in field. Using a combination of advanced transmission electron microscopy (TEM) techniques such as atomic resolution high-angle annular dark field scanning TEM, energy dispersive x-ray spectroscopy and electron energy-loss spectroscopy we have been able to decipher and characterize the effects of the Fe and Mn doping on the film architecture. The YBaCuFeO5 anion-deficient double perovskite phase was detected in the form of 3D inclusions as well as epitaxially grown lamellas within the YBCO matrix. These nano-inclusions play a positive role as pinning centers responsible for the J c/J sf (H) dependency smoothening at high magnetic fields in the YBCO-MFO films with respect to the pristine YBCO films. |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
|
Editor |
|
Language |
|
Wos |
000387680100001 |
Publication Date |
2016-10-31 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
0953-2048 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
2.878 |
Times cited |
6 |
Open Access |
|
Notes |
The authors gratefully acknowledge Prof. Dr. A. Abakumov and Dr. J. Gazquez for discussions and corrections. Part of this work was performed within the framework of the EUROTAPES project (FP7-NMP.2011.2.2-1 Grant no. 280432), funded by the European Union. ICMAB research was financed by the Ministry of Economy and Competitiveness, and FEDER funds under the projects MAT2011-28874-C02-01, MAT2014-51778-C2-1-R, ENE2014-56109-C3-3-R and Consolider Nanoselect CSD2007-00041, and by Generalitat de Catalunya (2009 SGR 770, 2015 SGR 753 and Xarmae). ICMAB acknowledges support from Severo Ochoa Program (MINECO, Grant SEV-2015-0496). |
Approved |
Most recent IF: 2.878 |
Call Number |
EMAT @ emat @ c:irua:136444 |
Serial |
4295 |
Permanent link to this record |
|
|
|
Author |
Meng, X.; Chen, S.; Peng, H.; Bai, H.; Zhang, S.; Su, X.; Tan, G.; Van Tendeloo, G.; Sun, Z.; Zhang, Q.; Tang, X.; Wu, J. |
Title |
Ferroelectric engineering : enhanced thermoelectric performance by local structural heterogeneity |
Type |
A1 Journal article |
Year |
2022 |
Publication |
Science China : materials |
Abbreviated Journal |
Sci China Mater |
Volume |
|
Issue |
|
Pages |
|
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
Abstract |
Although traditional ferroelectric materials are usually dielectric and nonconductive, GeTe is a typical ferroelectric semiconductor, possessing both ferroelectric and semiconducting properties. GeTe is also a widely studied thermoelectric material, whose performance has been optimized by doping with various elements. However, the impact of the ferroelectric domains on the thermoelectric properties remains unclear due to the difficulty to directly observe the ferroelectric domains and their evolutions under actual working conditions where the material is exposed to high temperatures and electric currents. Herein, based on in-situ investigations of the ferroelectric domains and domain walls in both pure and Sb-doped GeTe crystals, we have been able to analyze the dynamic evolution of the ferroelectric domains and domain walls, exposed to an electric field and temperature. Local structural heterogeneities and nano-sized ferroelectric domains are generated due to the interplay of the Sb3+ dopant and the Ge-vacancies, leading to the increased number of charged domain walls and a much improved thermoelectric performance. This work reveals the fundamental mechanism of ferroelectric thermoelectrics and provides insights into the decoupling of previously interdependent properties such as thermo-power and electrical conductivity. |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
|
Editor |
|
Language |
|
Wos |
000749973500001 |
Publication Date |
2022-02-02 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
2095-8226; 2199-4501 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
8.1 |
Times cited |
|
Open Access |
Not_Open_Access |
Notes |
|
Approved |
Most recent IF: 8.1 |
Call Number |
UA @ admin @ c:irua:186429 |
Serial |
6959 |
Permanent link to this record |
|
|
|
Author |
Verheyen, E.; Joos, L.; Van Havenbergh, K.; Breynaert, E.; Kasian, N.; Gobechiya, E.; Houthoofd, K.; Martineau, C.; Hinterstein, M.; Taulelle, F.; Van Speybroeck, V.; Waroquier, M.; Bals, S.; Van Tendeloo, G.; Kirschhock, C.E.A.; Martens, J.A.; |
Title |
Design of zeolite by inverse sigma transformation |
Type |
A1 Journal article |
Year |
2012 |
Publication |
Nature materials |
Abbreviated Journal |
Nat Mater |
Volume |
11 |
Issue |
12 |
Pages |
1059-1064 |
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
Abstract |
Although the search for new zeolites has traditionally been based on trial and error, more rational methods are now available. The theoretical concept of inverse transformation of a zeolite framework to generate a new structure by removal of a layer of framework atoms and contraction has for the first time been achieved experimentally. The reactivity of framework germanium atoms in strong mineral acid was exploited to selectively remove germanium-containing four-ring units from an UTL type germanosilicate zeolite. Annealing of the leached framework through calcination led to the new all-silica COK-14 zeolite with intersecting 12- and 10-membered ring channel systems. An intermediate stage of this inverse transformation with dislodged germanate four-rings still residing in the pores could be demonstrated. Inverse transformation involving elimination of germanium-containing structural units opens perspectives for the synthesis of many more zeolites. |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
London |
Editor |
|
Language |
|
Wos |
000311432600025 |
Publication Date |
2012-10-19 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
1476-1122;1476-4660; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
39.737 |
Times cited |
140 |
Open Access |
|
Notes |
Fwo |
Approved |
Most recent IF: 39.737; 2012 IF: 35.749 |
Call Number |
UA @ lucian @ c:irua:101783 |
Serial |
661 |
Permanent link to this record |
|
|
|
Author |
Sathiya, M.; Abakumov, A.M.; Foix, D.; Rousse, G.; Ramesha, K.; Saubanère, M.; Doublet, M. .; Vezin, H.; Laisa, C.P.; Prakash, A.S.; Gonbeau, D.; Van Tendeloo, G.; Tarascon, J.M. |
Title |
Origin of voltage decay in high-capacity layered oxide electrodes |
Type |
A1 Journal article |
Year |
2015 |
Publication |
Nature materials |
Abbreviated Journal |
Nat Mater |
Volume |
14 |
Issue |
14 |
Pages |
230-238 |
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
Abstract |
Although Li-rich layered oxides (Li1+xNiyCozMn1−x−y−zO2 > 250 mAh g−1) are attractive electrode materials providing energy densities more than 15% higher than todays commercial Li-ion cells, they suffer from voltage decay on cycling. To elucidate the origin of this phenomenon, we employ chemical substitution in structurally related Li2RuO3 compounds. Li-rich layered Li2Ru1−yTiyO3 phases with capacities of ~240 mAh g−1 exhibit the characteristic voltage decay on cycling. A combination of transmission electron microscopy and X-ray photoelectron spectroscopy studies reveals that the migration of cations between metal layers and Li layers is an intrinsic feature of the chargedischarge process that increases the trapping of metal ions in interstitial tetrahedral sites. A correlation between these trapped ions and the voltage decay is established by expanding the study to both Li2Ru1−ySnyO3 and Li2RuO3; the slowest decay occurs for the cations with the largest ionic radii. This effect is robust, and the finding provides insights into new chemistry to be explored for developing high-capacity layered electrodes that evade voltage decay. |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
London |
Editor |
|
Language |
|
Wos |
000348600200024 |
Publication Date |
2014-12-01 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
1476-1122;1476-4660; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
39.737 |
Times cited |
395 |
Open Access |
|
Notes |
246791 Countatoms; 312483 Esteem2; esteem2_ta |
Approved |
Most recent IF: 39.737; 2015 IF: 36.503 |
Call Number |
c:irua:132555 c:irua:132555 |
Serial |
2528 |
Permanent link to this record |
|
|
|
Author |
De Keukeleere, K.; Cayado, P.; Meledin, A.; Vallès, F.; De Roo, J.; Rijckaert, H.; Pollefeyt, G.; Bruneel, E.; Palau, A.; Coll, M.; Ricart, S.; Van Tendeloo, G.; Puig, T.; Obradors, X.; Van Driessche, I. |
Title |
Superconducting YBa2Cu3O7-δNanocomposites Using Preformed ZrO2Nanocrystals: Growth Mechanisms and Vortex Pinning Properties |
Type |
A1 Journal article |
Year |
2016 |
Publication |
Advanced Electronic Materials |
Abbreviated Journal |
|
Volume |
2 |
Issue |
2 |
Pages |
1600161 |
Keywords |
A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT) |
Abstract |
Although high temperature superconductors are promising for power applications, the production of low-cost coated conductors with high current densities—at high magnetic fields—remains challenging. A superior superconducting YBa2Cu3O7–δ nanocomposite is fabricated via chemical solution deposition (CSD) using preformed nanocrystals (NCs). Preformed, colloidally stable ZrO2 NCs are added to the trifluoroacetic acid based precursor solution and the NCs' stability is confirmed up to 50 mol% for at least 2.5 months. These NCs tend to disrupt the epitaxial growth of YBa2Cu3O7–δ, unless a thin seed layer is applied. A 10 mol% ZrO2 NC addition proved to be optimal, yielding a critical current density JC of 5 MA cm−2 at 77 K in self-field. Importantly, this new approach results in a smaller magnetic field decay of JC(H//c) for the nanocomposite compared to a pristine film. Furthermore, microstructural analysis of the YBa2Cu3O7–δ nanocomposite films reveals that different strain generation mechanisms may occur compared to the spontaneous segregation approach. Yet, the generated nanostrain in the YBa2Cu3O7–δ nanocomposite results in an improvement of the superconducting properties similar to the spontaneous segregation approach. This new approach, using preformed NCs in CSD coatings, can be of great potential for high magnetic field applications. |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
|
Editor |
|
Language |
|
Wos |
000386624100003 |
Publication Date |
2016-09-05 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
2199160X |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
|
Times cited |
26 |
Open Access |
|
Notes |
This work was financially supported by a BOF research fund of Ghent University (BOF11/DOC/286), FWO Flanders (F08512), and Eurotapes, a collaborative project funded by the European Community’s Seven Framework Program (EU-FP7 NMP-LA-2012-280432). We also acknowledge MINECO and FEDER funds for MAT2014-51778-C2-1-R and the Center of Excellence award Severo Ochoa SEV-2015-0496, and SGR753 from the Generalitat of Catalunya. MC acknowledges RyC contract 2013-12448 |
Approved |
Most recent IF: NA |
Call Number |
EMAT @ emat @ c:irua:135171 |
Serial |
4118 |
Permanent link to this record |
|
|
|
Author |
Filez, M.; Poelman, H.; Redekop, E.A.; Galvita, V.V.; Alexopoulos, K.; Meledina, M.; Ramachandran, R.K.; Dendooven, J.; Detavernier, C.; Van Tendeloo, G.; Safonova, O.V.; Nachtegaal, M.; Weckhuysen, B.M.; Marin, G.B. |
Title |
Kinetics of lifetime changes in bimetallic nanocatalysts revealed by quick X-ray absorption spectroscopy |
Type |
A1 Journal article |
Year |
2018 |
Publication |
Angewandte Chemie: international edition in English |
Abbreviated Journal |
Angew Chem Int Edit |
Volume |
57 |
Issue |
38 |
Pages |
12430-12434 |
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
Abstract |
Alloyed metal nanocatalysts are of environmental and economic importance in a plethora of chemical technologies. During the catalyst lifetime, supported alloy nanoparticles undergo dynamic changes which are well-recognized but still poorly understood. High-temperature O-2-H-2 redox cycling was applied to mimic the lifetime changes in model Pt13In9 nanocatalysts, while monitoring the induced changes by insitu quick X-ray absorption spectroscopy with one-second resolution. The different reaction steps involved in repeated Pt13In9 segregation-alloying are identified and kinetically characterized at the single-cycle level. Over longer time scales, sintering phenomena are substantiated and the intraparticle structure is revealed throughout the catalyst lifetime. The insitu time-resolved observation of the dynamic habits of alloyed nanoparticles and their kinetic description can impact catalysis and other fields involving (bi)metallic nanoalloys. |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
Weinheim |
Editor |
|
Language |
|
Wos |
000444225100038 |
Publication Date |
2018-08-03 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
1433-7851; 0570-0833 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
11.994 |
Times cited |
4 |
Open Access |
OpenAccess |
Notes |
; M.F. acknowledges a European Union's Horizon 2020 research and innovation program under the Marie Sklodowska-Curie grant agreement (No. 748563). E.A.R acknowledges the Marie Curie International Incoming Fellowship granted by the European Commission (No. 301703). This work was supported by the Fund for Scientific Research Flanders (G.0209.11), the “Long Term Structural Methusalem Funding by the Flemish Government”. The research leading to these results has received funding from the European Community's Seventh Framework Programme (FP7 /2007-2013) under grant agreement No. 312284 (CALIPSO). We thanks the Swiss Light Source for providing beamtime at the SuperXAS beamline. ; |
Approved |
Most recent IF: 11.994 |
Call Number |
UA @ lucian @ c:irua:153633 |
Serial |
5111 |
Permanent link to this record |
|
|
|
Author |
Gkanatsiou, A.; Lioutas, C.B.; Frangis, N.; Polychroniadis, E.K.; Prystawko, P.; Leszczynski, M.; Altantzis, T.; Van Tendeloo, G. |
Title |
Influence of 4H-SiC substrate miscut on the epitaxy and microstructure of AlGaN/GaN heterostructures |
Type |
A1 Journal article |
Year |
2019 |
Publication |
Materials science in semiconductor processing |
Abbreviated Journal |
Mat Sci Semicon Proc |
Volume |
91 |
Issue |
|
Pages |
159-166 |
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
Abstract |
AlGaN/GaN heterostructures were grown on “on-axis” and 2° off (0001) 4H-SiC substrates by metalorganic vapor phase epitaxy (MOVPE). Structural characterization was performed by transmission electron microscopy. The dislocation density, being greater in the on-axis case, is gradually reduced in the GaN layer and is forming
dislocation loops in the lower region. Steps aligned along [11̅00] in the off-axis case give rise to simultaneous defect formation. In the on-axis case, an almost zero density of steps is observed, with the main origin of defects probably being the orientation mismatch at the grain boundaries between the small not fully coalesced AlN grains. V-shaped formations are observed in the AlN nucleation layer, but are more frequent in the off-axis case, probably enhanced by the presence of steps. These V-shaped formations are completely overgrown by the GaN layer, during the subsequent deposition, presenting AlGaN areas in the walls of the defect, indicating an interdiffusion between the layers. Finally, at the AlGaN/GaN heterostructure surface in the on-axis case, V-shapes are observed, with the AlN spacer and AlGaN (21% Al) thickness on relaxed GaN exceeding the critical thickness for relaxation. On the other hand, no relaxation in the form of V-shape creation is observed in the off-axis case, probably due to the smaller AlGaN thickness (less than 21% Al). The AlN spacer layer, grown in between the heterostructure, presents a uniform thickness and clear interfaces. |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
|
Editor |
|
Language |
|
Wos |
000454537700022 |
Publication Date |
2018-11-26 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
1369-8001 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
2.359 |
Times cited |
1 |
Open Access |
Not_Open_Access |
Notes |
Funding: This work was supported by the IKY Fellowships of Excellence for Postgraduate Studies in Greece-SIEMENS Program; the Greek General Secretariat for Research and Technology, contract SAE 013/8–2009SE 01380012; and the JU ENIAC Project LAST POWER Large Area silicon carbide Substrates and heteroepitaxial GaN for POWER device applications [grant number 120218]. Also part of the research leading to these results has received funding from the European Union Seventh Framework Program under Grant Agreement 312483 – ESTEEM2 (Integrated Infrastructure Initiative–I3). T.A. acknowledges financial support from the Research Foundation Flanders (FWO, Belgium) through a post-doctoral grant. |
Approved |
Most recent IF: 2.359 |
Call Number |
EMAT @ emat @UA @ admin @ c:irua:156200 |
Serial |
5149 |
Permanent link to this record |
|
|
|
Author |
Simon, Q.; Barreca, D.; Bekermann, D.; Gasparotto, A.; Maccato, C.; Comini, E.; Gombac, V.; Fornasiero, P.; Lebedev, O.I.; Turner, S.; Devi, A.; Fischer, R.A.; Van Tendeloo, G. |
Title |
Plasma-assisted synthesis of Ag/ZnO nanocomposites : first example of photo-induced H2 production and sensing |
Type |
A1 Journal article |
Year |
2011 |
Publication |
International journal of hydrogen energy |
Abbreviated Journal |
Int J Hydrogen Energ |
Volume |
36 |
Issue |
24 |
Pages |
15527-15537 |
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
Abstract |
Ag/ZnO nanocomposites were developed by a plasma-assisted approach. The adopted strategy exploits the advantages of Plasma Enhanced-Chemical Vapor Deposition (PE-CVD) for the growth of columnar ZnO arrays on Si(100) and Al2O3 substrates, in synergy with the infiltration power of the Radio Frequency (RF)-sputtering technique for the subsequent dispersion of different amounts of Ag nanoparticles (NPs). The resulting composites, both as-prepared and after annealing in air, were thoroughly characterized with particular attention on their morphological organization, structure and composition. For the first time, the above systems have been used as catalysts in the production of hydrogen by photo-reforming of alcoholic solutions, yielding a stable H2 evolution even by the sole use of simulated solar radiation. In addition, Ag/ZnO nanocomposites presented an excellent response in the gas-phase detection of H2, opening attractive perspectives for advanced technological applications. |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
Oxford |
Editor |
|
Language |
|
Wos |
000297089700006 |
Publication Date |
2011-10-14 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
0360-3199; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
3.582 |
Times cited |
62 |
Open Access |
|
Notes |
Esteem 026019; Fwo |
Approved |
Most recent IF: 3.582; 2011 IF: 4.054 |
Call Number |
UA @ lucian @ c:irua:91901 |
Serial |
2627 |
Permanent link to this record |
|
|
|
Author |
Maccato, C.; Simon, Q.; Carraro, G.; Barreca, D.; Gasparotto, A.; Lebedev, O.I.; Turner, S.; Van Tendeloo, G. |
Title |
Zinc and copper oxides functionalized with metal nanoparticles : an insight into their nano-organization |
Type |
A1 Journal article |
Year |
2012 |
Publication |
Journal of advanced microscopy research |
Abbreviated Journal |
|
Volume |
7 |
Issue |
2 |
Pages |
84-90 |
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
Abstract |
Ag/ZnO and Au/CuxO (x = 1, 2) nanocomposites supported on Si(100) and polycrystalline Al2O3 were synthesised by hybrid approaches, combining chemical vapor deposition (either thermal or plasma-assisted) of host oxide matrices and subsequent radio frequency-sputtering of guest metal particles. The influence of the adopted synthetic parameters on the nanocomposite morphological and compositional features was investigated by field emission-scanning electron microscopy, transmission electron microscopy, energy dispersive X-ray spectroscopy and X-ray photoelectron spectroscopy. Results confirm the synthesis of ZnO and CuxO nanoarchitectures, characterized by a tailored morphology and an intimate metal/oxide contact. A careful control of the processing conditions enabled a fine tuning of the mutual constituent distribution, opening thus attractive perspectives for the engineering of advanced nanomaterials. |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
|
Editor |
|
Language |
|
Wos |
|
Publication Date |
2012-12-04 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
2156-7573;2156-7581; |
ISBN |
|
Additional Links |
UA library record |
Impact Factor |
|
Times cited |
|
Open Access |
|
Notes |
Esteem |
Approved |
Most recent IF: NA |
Call Number |
UA @ lucian @ c:irua:105298 |
Serial |
3932 |
Permanent link to this record |
|
|
|
Author |
Shestakov, M.V.; Meledina, M.; Turner, S.; Baekelant, W.; Verellen, N.; Chen, X.; Hofkens, J.; Van Tendeloo, G.; Moshchalkov, V.V. |
Title |
Luminescence of fixed site Ag nanoclusters in a simple oxyfluoride glass host and plasmon absorption of amorphous Ag nanoparticles in a complex oxyfluoride glass host |
Type |
P1 Proceeding |
Year |
2015 |
Publication |
Proceedings of the Society of Photo-optical Instrumentation Engineers
T2 – 8th International Conference on Photonics, Devices, and System VI, AUG 27-29, 2014, Prague, CZECH REPUBLIC |
Abbreviated Journal |
|
Volume |
|
Issue |
|
Pages |
Unsp 94501n |
Keywords |
P1 Proceeding; Electron microscopy for materials research (EMAT) |
Abstract |
Ag nanocluster-doped glasses have been prepared by a conventional melt-quenching method. The effect of melt temperature and dwell time on the formation of Ag nanoclusters and Ag nanoparticles in simple host oxyfluoride glasses has been studied. The increase of melt temperature and dwell time results in the dissolution of Ag nanoparticles and substantial red-shift of absorption and photoluminescence spectra of the prepared glasses. The quantum yield of the glasses is similar to 5% and does not depend on melt temperature and dwell time. The prepared glasses may be used as red phosphors or down-conversion layers for solar-cells. |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
Spie-int soc optical engineering |
Place of Publication |
Bellingham |
Editor |
|
Language |
|
Wos |
000349404500057 |
Publication Date |
2015-01-06 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
9450 |
Series Issue |
|
Edition |
|
ISSN |
978-1-62841-566-7 |
ISBN |
|
Additional Links |
UA library record; WoS full record |
Impact Factor |
|
Times cited |
|
Open Access |
|
Notes |
|
Approved |
Most recent IF: NA |
Call Number |
UA @ lucian @ c:irua:144783 |
Serial |
4668 |
Permanent link to this record |
|
|
|
Author |
Djoković, V.; Krsmanović, R.; Božanić, D.K.; McPherson, M.; Van Tendeloo, G.; Nair, P.S.; Georges, M.K.; Radhakrishnan, T. |
Title |
Adsorption of sulfur onto a surface of silver nanoparticles stabilized with sago starch biopolymer |
Type |
A1 Journal article |
Year |
2009 |
Publication |
Colloids and surfaces: B : biointerfaces |
Abbreviated Journal |
Colloid Surface B |
Volume |
73 |
Issue |
1 |
Pages |
30-35 |
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
Abstract |
Adsorption of sulfide ions onto a surface of starch capped silver nanoparticles upon addition of thioacetamide was investigated. UVvis absorption spectroscopy revealed that the adsorption of the sulfide ion on the surface of the silver nanoparticles induced damping as well as blue shift of the silver surface plasmon resonance band. Further increase in thioacetamide concentration led to shift of the resonance band toward higher wavelengths indicating the formation of the continuous Ag2S layer on the silver surface. Thus fabricated nanoparticles were investigated using electron microscopy techniques (TEM, HRTEM, and HAADF-STEM) and X-ray photoelectron spectroscopy (XPS), which confirmed their coreshell structure. |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
Amsterdam |
Editor |
|
Language |
|
Wos |
000268657500005 |
Publication Date |
2009-05-05 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
0927-7765; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
3.887 |
Times cited |
41 |
Open Access |
|
Notes |
Esteem 026019 |
Approved |
Most recent IF: 3.887; 2009 IF: 2.600 |
Call Number |
UA @ lucian @ c:irua:77972 |
Serial |
66 |
Permanent link to this record |
|
|
|
Author |
Rauwel, E.; Dubourdieu, C.; Holländer, B.; Rochat, N.; Ducroquet, F.; Rossell, M.D.; Van Tendeloo, G.; Pelissier, B. |
Title |
Stabilization of the cubic phase of HfO2 by Y addition in films grown by metal organic chemical vapor deposition |
Type |
A1 Journal article |
Year |
2006 |
Publication |
Applied physics letters |
Abbreviated Journal |
Appl Phys Lett |
Volume |
89 |
Issue |
1 |
Pages |
012902,1-012902,3 |
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
Abstract |
Addition of yttrium in HfO(2) thin films prepared on silicon by metal organic chemical vapor deposition is investigated in a wide compositional range (2.0-99.5 at. %). The cubic structure of HfO(2) is stabilized for 6.5 at. %. The permittivity is maximum for yttrium content of 6.5-10 at. %; in this range, the effective permittivity, which results from the contribution of both the cubic phase and silicate phase, is of 22. These films exhibit low leakage current density (5x10(-7) A/cm(2) at -1 V for a 6.4 nm film). The cubic phase is stable upon postdeposition high temperature annealing at 900 degrees C under NH(3). (c) 2006 American Institute of Physics. |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
American Institute of Physics |
Place of Publication |
New York, N.Y. |
Editor |
|
Language |
|
Wos |
000238849200046 |
Publication Date |
2006-07-06 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
0003-6951; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
3.411 |
Times cited |
78 |
Open Access |
|
Notes |
Medea T207 |
Approved |
Most recent IF: 3.411; 2006 IF: 3.977 |
Call Number |
UA @ lucian @ c:irua:59632 |
Serial |
3138 |
Permanent link to this record |
|
|
|
Author |
Verbruggen, S.W.; Keulemans, M.; Filippousi, M.; Flahaut, D.; Van Tendeloo, G.; Lacombe, S.; Martens, J.A.; Lenaerts, S. |
Title |
Plasmonic goldsilver alloy on TiO2 photocatalysts with tunable visible light activity |
Type |
A1 Journal article |
Year |
2014 |
Publication |
Applied catalysis : B : environmental |
Abbreviated Journal |
Appl Catal B-Environ |
Volume |
156 |
Issue |
|
Pages |
116-121 |
Keywords |
A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Sustainable Energy, Air and Water Technology (DuEL) |
Abstract |
Adaptation of the photoresponse of anatase TiO2 to match the solar spectrum is an important scientific challenge. Modification of TiO2 with noble metal nanoparticles displaying surface plasmon resonance effects is one of the promising approaches. Surface plasmon resonance typically depends on chemical composition, size, shape and spatial organization of the metal nanoparticles in contact with TiO2. AuxAg(1 − x) alloy nanoparticles display strong composition-dependent surface plasmon resonance in the visible light region of the spectrum. In this work, a general strategy is presented to prepare plasmonic TiO2-based photocatalysts with a visible light response that can be accurately tuned over a broad range of the spectrum. The application as self-cleaning material toward the degradation of stearic acid is demonstrated for a plasmonic TiO2 photocatalyst displaying visible light photoactivity at the intensity maximum of solar light around 490 nm. |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
Amsterdam |
Editor |
|
Language |
|
Wos |
000336013200014 |
Publication Date |
2014-03-22 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
0926-3373; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
9.446 |
Times cited |
84 |
Open Access |
|
Notes |
Flanders(FWO); Methusalem |
Approved |
Most recent IF: 9.446; 2014 IF: 7.435 |
Call Number |
UA @ lucian @ c:irua:115552 |
Serial |
2646 |
Permanent link to this record |
|
|
|
Author |
Yu, W.-B.; Hu, Z.-Y.; Jin, J.; Yi, M.; Yan, M.; Li, Y.; Wang, H.-E.; Gao, H.-X.; Mai, L.-Q.; Hasan, T.; Xu, B.-X.; Peng, D.-L.; Van Tendeloo, G.; Su, B.-L. |
Title |
Unprecedented and highly stable lithium storage capacity of (001) faceted nanosheet-constructed hierarchically porous TiO₂/rGO hybrid architecture for high-performance Li-ion batteries |
Type |
A1 Journal article |
Year |
2020 |
Publication |
National Science Review |
Abbreviated Journal |
Natl Sci Rev |
Volume |
7 |
Issue |
6 |
Pages |
1046-1058 |
Keywords |
A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT) |
Abstract |
Active crystal facets can generate special properties for various applications. Herein, we report a (001) faceted nanosheet-constructed hierarchically porous TiO2/rGO hybrid architecture with unprecedented and highly stable lithium storage performance. Density functional theory calculations show that the (001) faceted TiO2 nanosheets enable enhanced reaction kinetics by reinforcing their contact with the electrolyte and shortening the path length of Li+ diffusion and insertion-extraction. The reduced graphene oxide (rGO) nanosheets in this TiO2/rGO hybrid largely improve charge transport, while the porous hierarchy at different length scales favors continuous electrolyte permeation and accommodates volume change. This hierarchically porous TiO2/rGO hybrid anode material demonstrates an excellent reversible capacity of 250 mAh g(-1) at 1 C (1 C = 335 mA g(-1)) at a voltage window of 1.0-3.0 V. Even after 1000 cycles at 5 C and 500 cycles at 10 C, the anode retains exceptional and stable capacities of 176 and 160 mAh g(-1), respectively. Moreover, the formed Li2Ti2O4 nanodots facilitate reversed Li+ insertion-extraction during the cycling process. The above results indicate the best performance of TiO2-based materials as anodes for lithium-ion batteries reported in the literature. |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
|
Editor |
|
Language |
|
Wos |
000544175300013 |
Publication Date |
2020-02-16 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
2095-5138 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
20.6 |
Times cited |
3 |
Open Access |
OpenAccess |
Notes |
; This work was supported by the National Key R&D Program of China (2016YFA0202602 and 2016YFA0202603), the National Natural Science Foundation of China (U1663225) and Program for Changjiang Scholars and Innovative Research Team in University (IRT_15R52). ; |
Approved |
Most recent IF: 20.6; 2020 IF: 8.843 |
Call Number |
UA @ admin @ c:irua:170776 |
Serial |
6648 |
Permanent link to this record |