Abstract: We report a new mode of precipitation in a B19 martensitic Ti50Ni30Pd20 shape memory alloy consisting of a central Ti2Ni(Pd) precipitate surrounded by an austenite area containing Ti2Pd(Ni) precipitates. The morphology and crystallography of the precipitation area is investigated using conventional and high resolution electron microscopy. In particular, the orientation relationship and the coherency strain between the Ti2Pd(Ni) precipitate and the surrounding retained B2 matrix are discussed. A study of local composition in relation with a ternary phase diagram using X-ray energy dispersive spectroscopy with a nanoprobe gives evidences of the formation mechanism.

Abstract: Electron spin resonance and electronic spectroscopy techniques were used to study the symmetry and electronic structure of Mn2+ dopants in solvothermally synthesized ZnS nanowires. The average diameter of ∼ 5 nm leads to the observable quantum confinement effects in the photoluminescence excitation spectra. The results clearly demonstrate the three symmetry locations of Mn2+ incorporation. Together with the inferred Mn2+ center densities, these data indicate a much higher efficiency of Mn2+ substitution in the nanowire sample with about two times larger diameter.

Abstract: The transport and magnetic measurements of polycrystalline Pb1.6V8O16 hollandite reveal a concomitant metal to insulator and antiferromagnetic transition at TMI≈140 K. A clear localization is found below TMI, evidenced by a rapid increase in the absolute value of the negative Seebeck coefficient. The structural study by x-ray and transmission electron microscopy confirms the hollandite structure and shows that no structural transition occurs at TMI, ruling out a possible charge orbital ordering. The negative Seebeck coefficient observed from 50 K up to 900 K, with values reaching S=−38 μV K−1 at 900 K, is explained by the electron doping of ∼1.4e− in the V empty t2g orbitals responsible for the bad metal resistivity (ρ900 K∼2 mΩ cm). As this S value is close to that obtained by considering only the spin and orbital degeneracies, it is expected that |S| for such vanadates will not be sensitive at high temperature to the t2g band filling

Abstract: FeMnC and FeMnSiAl TWIP steels deformed under the same conditions exhibit different work-hardening rates. The present study investigates the microstructure of plastically deformed FeMnC and FeMnSiAl samples, particularly the internal structure of the mechanically generated twins and their topology at the grain scale. Twins in the FeMnC steel are finer and full of sessile dislocations, rendering this material distinctly stronger with an improved work-hardening rate.

Abstract: A widely used performance criterion in high-resolution transmission electron microscopy (HRTEM) is the information limit. It corresponds to the inverse of the maximum spatial object frequency that is linearly transmitted with sufficient intensity from the exit plane of the object to the image plane and is limited due to partial temporal coherence. In practice, the information limit is often measured from a diffractogram or from Young's fringes assuming a weak phase object scattering beyond the inverse of the information limit. However, for an aberration corrected electron microscope, with an information limit in the sub-angstrom range, weak phase objects are no longer applicable since they do not scatter sufficiently in this range. Therefore, one relies on more strongly scattering objects such as crystals of heavy atoms observed along a low index zone axis. In that case, dynamical scattering becomes important such that the non-linear and linear interaction may be equally important. The non-linear interaction may then set the experimental cut-off frequency observed in a diffractogram. The goal of this paper is to quantify both the linear and the non-linear information transfer in terms of closed form analytical expressions. Whereas the cut-off frequency set by the linear transfer can be directly related with the attainable resolution, information from the non-linear transfer can only be extracted using quantitative, model-based methods. In contrast to the historic definition of the information limit depending on microscope parameters only, the expressions derived in this paper explicitly incorporate their dependence on the structure parameters as well. In order to emphasize this dependence and to distinguish from the usual information limit, the expressions derived for the inverse cut-off frequencies will be referred to as the linear and non-linear structural information limit. The present findings confirm the well-known result that partial temporal coherence has different effects on the transfer of the linear and non-linear terms, such that the non-linear imaging contributions are damped less than the linear imaging contributions at high spatial frequencies. This will be important when coherent aberrations such as spherical aberration and defocus are reduced.

Abstract: The presence of defects in carbon nanotubes strongly modifies their electrical, mechanical, and chemical properties. It was long thought undesirable, but recent experiments have shown that introduction of structural defects using ion or electron irradiation can lead to novel nanodevices. We demonstrate a method for detecting and quantifying point defect density in individual carbon nanotubes (CNTs) based on measuring the polarization dependence (linear dichroism) of the C 1s → π* transition at specific locations along individual CNTs with a scanning transmission X-ray microscope (STXM). We show that STXM can be used to probe defect density in individual CNTs with high spatial resolution. The quantitative relationship between ion dose, nanotube diameter, and defect density was explored by purposely irradiating selected sections of nanotubes with kiloelectronvolt (keV) Ga+ ions. Our results establish polarization-dependent X-ray microscopy as a new and very powerful characterization technique for carbon nanotubes and other anisotropic nanostructures.

Abstract: Multiple-step martensitic transformations of an aged Ni51Ti49 single crystal using calorimetric method were investigated. Results show that for short aging times (1045 min) multiple-step martensitic transformations on cooling occur in two steps. Applying intermediate aging times (1.254 h) results in three steps and long aging times (more than 8 h) lead to two-step martensitic transformations again. This behavior has not been recognized in NiTi single crystals in literatures. It can be related to the heterogeneity of composition and stress fields around Ni4Ti3 precipitates.

Abstract: Due to unique properties of NiTi shape memory alloys such as high corrosion resistance, biocompatibility, super elasticity and shape memory behavior, NiTi shape memory alloys are suitable materials for medical applications. Although TiO2 passive layer in these alloys can prevent releasing of nickel to the environment, high nickel content and stability of passive layer in these alloys are very debatable subjects. In this study a NiTi shape memory alloy with nominal composition of 50.7 atom% Ni was investigated by corrosion tests. Electrochemical tests were performed in two physiological environments of Ringer solution and NaCl 0.9% solution. Results indicate that the breakdown potential of the NiTi alloy in NaCl 0.9% solution is higher than that in Ringer solution. The results of Scanning Electron Microscope (SEM) reveal that low pitting corrosion occurred in Ringer solution compared with NaCl solution at potentiostatic tests. The pH value of the solutions increases after the electrochemical tests. The existence of hydride products in the X-ray diffraction analysis confirms the decrease of the concentration of hydrogen ion in solutions. Topographical evaluations show that corrosion products are nearly same in all samples. The biocompatibility tests were performed by reaction of mouse fibroblast cells (L929). The growth and development of cells for different times were measured by numbering the cells or statistics investigations. The figures of cells for different times showed natural growth of cells. The different of the cell numbers between the test specimen and control specimen was negligible; therefore it may be concluded that the NiTi shape memory alloy is not toxic in the physiological environments simulated with body fluids.

Abstract: X-ray powder-diffraction(XRD),high-resolutiontransmissionelectronmicroscopy(HRTEM),electron diffraction(ED),infraredspectroscopy(IR),thermogravimetry(TG)andmassspectroscopy(MS)were performedtoinvestigatethecompositionandthecrystalstructureoftetra-bariumdi-niobate(V) Ba4Nb2O9. TheTG,MSandIRstudiesrevealedthatthecompoundisahydratedoxycarbonate.Assuming that thecarbonatestoichiometricallyreplacesoxygen,thecompositionofthelow-temperature a-modification,obtainedbyslowcoolingfrom1100 1C, correspondstoBa4Nb2O8.8(CO3)0.2 0.1H2O, while thequenchedhigh-temperature g-modificationhastheBa4Nb2O8.42(CO3)0.58 0.38H2O composi- tion. The a-phase hasacompositeincommensuratelymodulatedstructureconsistingoftwomutually interacting[Ba]N and the[(Nb,)O3]N subsystems.Thecompositemodulatedcrystalstructureofthe a-phase canbedescribedwiththelatticeparameters a¼10.2688(1) A˚ , c¼2.82426(8) A˚ , q¼0.66774(2)c* and asuperspacegroup R3m(00g)0s. TheHRTEManalysisdemonstratesthenanoscale twinningofthetrigonaldomainsparalleltothe{100}crystallographicplanes.Thetwinningintroduces a one-dimensionaldisorderintothe[(Nb,)O3]N subsystem,whichresultsinanaverage P62c crystal structureofthe a-phase. Possibleplacesforthecarbonategroupinthestructurearediscussedusinga comparisonwithotherhexagonalperovskite-basedoxycarbonates.

Abstract: The magnetotransport and magnetic properties of the PbV6O11 vanadate, crystallizing in the P63mc space group, reveal the existence of a negative magnetoresistance related to its ferromagnetic state (TC ∼ 90 K). The maximum effect is observed at 20 K reaching −30% in 9 T. The structural study of this ceramic reveals a V/Pb ratio smaller than expected from the formula. This is explained by the presence of numerous stacking faults observed by high resolution transmission electron microscopy. The existence of these planar defects acting as resistive barriers along the c axis could be responsible for tunneling magnetoresistance.

Abstract: Polyester-grafted polyhedral oligomeric silsesquioxane (POSS) nanohybrids selectively produced by ring-opening polymerization of ε-caprolactone and L,L-lactide (A.-L. Goffin, E. Duquesne, S. Moins, M. Alexandre, Ph. Dubois, Eur. Polym. Journal, 2007, 43, 4103) were studied as masterbatches by melt-blending within their corresponding commercial polymeric matrices, i.e., poly(ε-caprolactone) (PCL) and poly(L,L-lactide) (PLA). For the sake of comparison, neat POSS nanoparticles were also dispersed in PCL and PLA. The objective was to prepare aliphatic polyester-based nanocomposites with enhanced crystallization behavior, and therefore, enhanced thermo-mechanical properties. Wide-angle X-ray scattering and transmission electron microscopy attested for the dispersion of individualized POSS nanoparticles in the resulting nanocomposite materials only when the polyester-grafted POSS nanohybrid was used as a masterbatch. The large impact of such finely dispersed (grafted) nanoparticles on the crystallization behavior for the corresponding polyester matrices was noticed, as evidenced by differential scanning calorimetry analysis. Indeed, well-dispersed POSS nanoparticles acted as efficient nucleating sites, significantly increasing the crystallinity degree of both PCL and PLA matrices. As a result, a positive impact on thermo-mechanical properties was highlighted by dynamic mechanical thermal analysis.

Abstract: Effects of cooling slope angle and the temperature of molten metal on the globular structure of M2 high speed steel after holding at the semisolid state have been investigated. The globular structure was achieved by pouring the molten metal at 1595 °C on the ceramic cooling slope with the length of 200 mm and the angle of 25°. The globular structure of M2 high speed steel in the form of rolledannealed and as cast condition after holding at semisolid state has been achieved. The size of globular grains of cooling slope sample was smaller than that of the rolledannealed and as cast samples. Solid particles of rolledannealed sample after holding at semisolid state had better roundness compared with cooling slope sample. Dissolution of carbides in the austenite phase at grain boundaries leads to formation of globular particles in the semisolid state. MC-type and M6C-type eutectic carbides reprecipitate during cooling cycle along grain boundaries.

Abstract: Crystal structure and magnetic properties of the layered vanadium phosphate PbZnVO(PO4)2 are studied using x-ray powder diffraction, magnetization and specific-heat measurements, as well as band-structure calculations. The compound resembles AA′VO(PO4)2 vanadium phosphates and fits to the extended frustrated square-lattice model with the couplings J1, J1′ between nearest neighbors and J2, J2′ between next-nearest neighbors. The temperature dependence of the magnetization yields estimates of averaged nearest-neighbor and next-nearest-neighbor couplings, J̅ 1≃−5.2 K and J̅ 2≃10.0 K, respectively. The effective frustration ratio α=J̅ 2/J̅ 1 amounts to −1.9 and suggests columnar antiferromagnetic ordering in PbZnVO(PO4)2. Specific-heat data support the estimates of J̅ 1 and J̅ 2 and indicate a likely magnetic ordering transition at 3.9 K. However, the averaged couplings underestimate the saturation field, thus pointing to the spatial anisotropy of the nearest-neighbor interactions. Band-structure calculations confirm the identification of ferromagnetic J1, J1′ and antiferromagnetic J2, J2′ in PbZnVO(PO4)2 and yield (J1′−J1)≃1.1 K in excellent agreement with the experimental value of 1.1 K, deduced from the difference between the expected and experimentally measured saturation fields. Based on the comparison of layered vanadium phosphates with different metal cations, we show that a moderate spatial anisotropy of the frustrated square lattice has minor influence on the thermodynamic properties of the model. We discuss relevant geometrical parameters, controlling the exchange interactions in these compounds and propose a strategy for further design of strongly frustrated square-lattice materials.

Abstract: The Ni(1+)/Ni(2+) states of nickelates have the identical (3d(9)/3d(8)) electronic configuration as Cu(2+)/Cu(3+) in the high temperature superconducting cuprates, and are expected to show interesting properties. An intriguing question is whether mimicking the electronic and structural features of cuprates would also result in superconductivity in nickelates. Here we report experimental evidence for a bulklike magnetic transition in La(4)Ni(3)O(8) at 105 K. Density functional theory calculations relate the transition to a spin density wave nesting instability of the Fermi surface.