“Atomistic structure of Cu-containing \beta", precipitates in an Al-Mg-Si-Cu alloy”. Li K, Béché, A, Song M, Sha G, Lu X, Zhang K, Du Y, Ringer SP, Schryvers D, Scripta materialia 75, 86 (2014). http://doi.org/10.1016/j.scriptamat.2013.11.030
Abstract: The beta '' precipitates in a peak-aged Al-Mg-Si-Cu alloy were measured with an average composition of 28.6Al-38.7Mg-26.5Si-5.17Cu (at.%) using atom probe tomography. High-angle annular dark-field observations revealed that Cu incompletely substitutes for the Mg-1 and Si-3 columns, preferentially for one column in each pair of Si-3. Cu-free Si columns form a parallelogram-shaped network that constitutes the basis of subsequent precipitates in the system, with a = 0.37 nm, b = 0.38 nm, gamma = 113 degrees and c = 0.405 nm. (C) 2013 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.747
Times cited: 22
DOI: 10.1016/j.scriptamat.2013.11.030
|
|
|
“Decomposition of a metastable bcc phase in rapidly solidified Ni-9 at.% Zr and Ni-8 at.%X alloys”. Chandrasekaran M, Ghosh G, Schryvers D, de Graef M, Delaey L, Van Tendeloo G, Philosophical magazine: A: physics of condensed matter: defects and mechanical properties 75, 677 (1997)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 5
|
|
|
“Hepatocellular transport and gastrointestinal absorption of lanthanum in chronic renal failure”. Bervoets ARJ, Behets GJ, Schryvers D, Roels F, Yang Z, Verberckmoes SC, Damment SJP, Dauwe S, Mubiana VK, Blust R, de Broe ME, d' Haese PC, Kidney international 75, 389 (2009). http://doi.org/10.1038/ki.2008.571
Abstract: Lanthanum carbonate is a new phosphate binder that is poorly absorbed from the gastrointestinal tract and eliminated largely by the liver. After oral treatment, we and others had noticed 23 fold higher lanthanum levels in the livers of rats with chronic renal failure compared to rats with normal renal function. Here we studied the kinetics and tissue distribution, absorption, and subcellular localization of lanthanum in the liver using transmission electron microscopy, electron energy loss spectrometry, and X-ray fluoresence. We found that in the liver lanthanum was located in lysosomes and in the biliary canal but not in any other cellular organelles. This suggests that lanthanum is transported and eliminated by the liver via a transcellular, endosomal-lysosomal-biliary canicular transport route. Feeding rats with chronic renal failure orally with lanthanum resulted in a doubling of the liver levels compared to rats with normal renal function, but the serum levels were similar in both animal groups. These levels plateaued after 6 weeks at a concentration below 3 g/g in both groups. When lanthanum was administered intravenously, thereby bypassing the gastrointestinal tract-portal vein pathway, no difference in liver levels was found between rats with and without renal failure. This suggests that there is an increased gastrointestinal permeability or absorption of oral lanthanum in uremia. Lanthanum levels in the brain and heart fluctuated near its detection limit with long-term treatment (20 weeks) having no effect on organ weight, liver enzyme activities, or liver histology. We suggest that the kinetics of lanthanum in the liver are consistent with a transcellular transport pathway, with higher levels in the liver of uremic rats due to higher intestinal absorption.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Pathophysiology
Impact Factor: 8.395
Times cited: 29
DOI: 10.1038/ki.2008.571
|
|
|
“Holotomography: quantitative phase tomography with micrometer resolution using hard synchrotron radiation X-rays”. Cloetens P, Ludwig W, Baruchel J, van Dyck D, van Landuyt J, Guigay JP, Schlenker M, Applied physics letters 75, 2912 (1999). http://doi.org/10.1063/1.125225
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 3.411
Times cited: 481
DOI: 10.1063/1.125225
|
|
|
“Microstructure of adiabatic shear bands in Ti6Al4V”. Peirs J, Tirry W, Amin-Ahmadi B, Coghe F, Verleysen P, Rabet L, Schryvers D, Degrieck J, Materials characterization 75, 79 (2013). http://doi.org/10.1016/j.matchar.2012.10.009
Abstract: Microstructural deformation mechanisms in adiabatic shear bands in Ti6Al4V are studied using traditional TEM and selected area diffraction, and more advanced microstructural characterisation techniques such as energy dispersive X-ray spectroscopy, high angle annular dark field STEM and conical dark field TEM. The shear bands under investigation are induced in Ti6Al4V samples by high strain rate compression of cylindrical and hat-shaped specimens in a split Hopkinson pressure bar setup. Samples from experiments interrupted at different levels of deformation are used to study the evolution of the microstructure in and nearby the shear bands. From the early stages of adiabatic shear band formation, TEM revealed strongly elongated equiaxed grains in the shear band. These band-like grains become narrower towards the centre of the band and start to fraction even further along their elongated direction to finally result in a nano-crystalline region in the core. In fully developed shear bands, twins and a needle-like martensite morphology are observed near the shear band.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.714
Times cited: 56
DOI: 10.1016/j.matchar.2012.10.009
|
|
|
“Oscillations of the superconducting temperature induced by quantum well states in thin metallic films: numerical solution of the Bogoliubov-de Gennes equations”. Shanenko AA, Croitoru MD, Peeters FM, Physical review : B : condensed matter and materials physics 75, 014519 (2007). http://doi.org/10.1103/PhysRevB.75.014519
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Condensed Matter Theory (CMT)
Impact Factor: 3.836
Times cited: 85
DOI: 10.1103/PhysRevB.75.014519
|
|
|
“Synthesis and structural characterization of a novel Sillén &ndash, Aurivillius bismuth oxyhalide, PbBi3VO7.5Cl, and its derivatives”. Charkin DO, Plokhikh IV, Kazakov SM, Kalmykov SN, Akinfiev VS, Gorbachev AV, Batuk M, Abakumov AM, Teterin YA, Maslakov KI, Teterin AY, Ivanov KE, Solid state sciences 75, 27 (2018). http://doi.org/10.1016/j.solidstatesciences.2017.11.006
Abstract: A new Sillen – Aurivillius family of layered bismuth oxyhalides has been designed and successfully constructed on the basis of PbBiO2X(X = halogen) synthetic perites and g-form of Bi2VO5.5 solid elec- trolyte. This demonstrates, for the first time, the ability of the latter to serve as a building block in construction of mixed-layer structures. The parent compound PbBi3VO7.5-dCl (d = 0.05) has been investigated by powder XRD, TEM, XPS methods and magnetic susceptibility measurements. An unexpected but important condition for the formation of the mixed-layer structure is partial (ca. 5%) reduction of VV into VIV which probably suppresses competitive formation of apatite-like Pb – Bi vanadates. This reduction also stabilizes the g polymorphic form of Bi2VO5.5 not only in the intergrowth structure, but in Bi2V1-xMxO5.5-y (M – Nb, Sb) solid solutions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.811
Times cited: 1
DOI: 10.1016/j.solidstatesciences.2017.11.006
|
|
|
“Interstitial defects in the van der Waals gap of Bi2Se3”. Callaert C, Bercx M, Lamoen D, Hadermann J, Acta Crystallographica. Section B: Structural Science, Crystal Engineering and Materials (Online) 75, 717 (2019). http://doi.org/10.1107/S2052520619008357
Abstract: Bi<sub>2</sub>Se<sub>3</sub>is a thermoelectric material and a topological insulator. It is slightly conducting in its bulk due to the presence of defects and by controlling the defects different physical properties can be fine tuned. However, studies of the defects in this material are often contradicting or inconclusive. Here, the defect structure of Bi<sub>2</sub>Se<sub>3</sub>is studied with a combination of techniques: high-resolution scanning transmission electron microscopy (HR-STEM), high-resolution energy-dispersive X-ray (HR-EDX) spectroscopy, precession electron diffraction tomography (PEDT), X-ray diffraction (XRD) and first-principles calculations using density functional theory (DFT). Based on these results, not only the observed defects are discussed, but also the discrepancies in results or possibilities across the techniques. STEM and EDX revealed interstitial defects with mainly Bi character in an octahedral coordination in the van der Waals gap, independent of the applied sample preparation method (focused ion beam milling or cryo-crushing). The inherent character of these defects is supported by their observation in the structure refinement of the EDT data. Moreover, the occupancy probability of the defects determined by EDT is inversely proportional to their corresponding DFT calculated formation energies. STEM also showed the migration of some atoms across and along the van der Waals gap. The kinetic barriers calculated using DFT suggest that some paths are possible at room temperature, while others are most probably beam induced.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.032
DOI: 10.1107/S2052520619008357
|
|
|
“Introducton to the special issue on electron crystallography”. Hadermann J, Palatinus L, And Materials 75, 462 (2019). http://doi.org/10.1107/S2052520619010783
Keywords: Editorial; Electron microscopy for materials research (EMAT)
Times cited: 2
DOI: 10.1107/S2052520619010783
|
|
|
“Structure solution and refinement of metal-ion battery cathode materials using electron diffraction tomography”. Hadermann J, Abakumov AM, And Materials 75, 485 (2019). http://doi.org/10.1107/S2052520619008291
Abstract: The applicability of electron diffraction tomography to the structure solution and refinement of charged, discharged or cycled metal-ion battery positive electrode (cathode) materials is discussed in detail. As these materials are often only available in very small amounts as powders, the possibility of obtaining single-crystal data using electron diffraction tomography (EDT) provides unique access to crucial information complementary to X-ray diffraction, neutron diffraction and high-resolution transmission electron microscopy techniques. Using several examples, the ability of EDT to be used to detect lithium and refine its atomic position and occupancy, to solve the structure of materials ex situ at different states of charge and to obtain in situ data on structural changes occurring upon electrochemical cycling in liquid electrolyte is discussed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 2
DOI: 10.1107/S2052520619008291
|
|
|
“Microwave plasma-based dry reforming of methane: Reaction performance and carbon formation”. Kelly S, Mercer E, De Meyer R, Ciocarlan R-G, Bals S, Bogaerts A, Journal of CO2 utilization 75, 102564 (2023). http://doi.org/10.1016/j.jcou.2023.102564
Abstract: e investigate atmospheric pressure microwave (MW) plasma (2.45 GHz) conversion in CO2 and CH4 mixtures (i.e., dry reforming of methane, DRM) focusing on reaction performance and carbon formation. Promising energy costs of ~2.8–3.0 eV/molecule or ~11.1–11.9 kJ/L are amongst the best performance to date considering the current state-of-the-art for plasma-based DRM for all types of plasma. The conversion is in the range of ~46–49% and ~55–67% for CO2 and CH4, respectively, producing primarily syngas (i.e., H2 and CO) with H2/CO ratios of ~0.6–1 at CH4 fractions ranging from 30% to 45%. Water is the largest byproduct with levels ranging ~7–14% in the exhaust. Carbon particles visibly impact the plasma at higher CH4 fractions (> 30%), where they become heated and incandescent. Particle luminosity increases with increasing CH4 fractions, with the plasma becoming unstable near a 1:1 mixture (i.e., > 45% CH4). Electron microscopy of the carbon material reveals an agglomerated morphology of pure carbon nanoparticles. The mean particle size is determined as ~20 nm, free of any metal contamination, consistent with the electrode-less MW design.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA); Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 7.7
Times cited: 6
DOI: 10.1016/j.jcou.2023.102564
|
|
|
“0 and &pi, phase Josephson coupling through an insulating barrier with magnetic impurities”. Vávra O, Gaži S, Golubović, DS, Vávra I, Dérer J, Verbeeck J, Van Tendeloo G, Moshchalkov VV, Physical review : B : condensed matter and materials physics 74, 020502 (2006). http://doi.org/10.1103/PhysRevB.74.020502
Abstract: We have studied the temperature and field dependencies of the critical current I(C) in the Nb-Fe(0.1)Si(0.9)-Nb Josephson junction with a tunneling barrier formed by a paramagnetic insulator. We demonstrate that in these junctions coexistence of both the 0 and the pi states within one tunnel junction occurs, and leads to the appearance of a sharp cusp in the temperature dependence I(C)(T), similar to the I(C)(T) cusp found for the 0-pi transition in metallic pi junctions. This cusp is not related to the 0-pi temperature-induced transition itself, but is caused by the different temperature dependencies of the opposing 0 and pi supercurrents through the barrier.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 27
DOI: 10.1103/PhysRevB.74.020502
|
|
|
“The chirality of carbon nanotubules determined by dark-field electron microscopy”. Bernaerts D, op de Beeck M, Amelinckx S, van Landuyt J, Van Tendeloo G, Philosophical magazine: A: physics of condensed matter: defects and mechanical properties 74, 723 (1996). http://doi.org/10.1080/01418619608243538
Abstract: Multishell carbon nanotubules are studied by means of diffraction contrast dark field images. This results in an electron microscopy method for the determination of the sign of the chiral angles in carbon nanotubes. The method is justified by a reasoning either in direct space or in diffraction space. We also investigate a carbon nanotubule exhibiting a bend and we confront the observations with the heptagon-pentagon pair model.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 20
DOI: 10.1080/01418619608243538
|
|
|
“Fitting the momentum dependent loss function in EELS”. Bertoni G, Verbeeck J, Brosens F, Microscopy research and technique 74, 212 (2011). http://doi.org/10.1002/jemt.20894
Abstract: Momentum dependent inelastic plasmon scattering can be measured by electron energy loss in a transmission electron microscope. From energy filtered diffraction, the characteristic angle of scattering and the cutoff angle are measured, using a thin film of aluminum as a model test. Rather than deconvolving the data (as done in previous works), a fitting technique is used to extract the loss function from angular resolved spectra, starting from a simple model simulation.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Theory of quantum systems and complex systems
Impact Factor: 1.147
Times cited: 6
DOI: 10.1002/jemt.20894
|
|
|
“A potential method to correlate electrical properties and microstructure of a unique high-Tc superconducting Josephson junction”. Verbist K, Lebedev OI, Van Tendeloo G, Tafuri F, Granozio FM, Di Chiara A, Bender H, Applied physics letters 74, 1024 (1999). http://doi.org/10.1063/1.123443
Abstract: A method to correlate microstructure from cross-section transmission electron microscopy (TEM) investigations and transport properties of a single well characterized high-T-c artificial grain boundary junction is reported. A YBa2Cu3O7-delta 45 degrees twist junction exhibiting the typical phenomenology of high T-c Josephson weak links was employed. The TEM sample preparation is based on focused ion beam etching and allows to easily localize the electron transparent area on a microbridge. The reported technique opens clear perspectives in the determination of the microstructural origin of variations in Josephson junction properties, such as the spread in I-c and IcRN values and the presence of different transport regimes in nominally identical junctions. (C) 1999 American Institute of Physics. [S0003-6951(99)03404-X].
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 5
DOI: 10.1063/1.123443
|
|
|
“Reducing the formation of FIB-induced FCC layers on Cu-Zn-Al austenite”. Zelaya E, Schryvers D, Microscopy research and technique 74, 84 (2011). http://doi.org/10.1002/jemt.20877
Abstract: The irradiation effects of thinning a sample of a Cu-Zn-Al shape memory alloy to electron transparency by a Ga+ focused ion beam were investigated. This thinning method was compared with conventional electropolishing and Ar+ ion milling. No implanted Ga was detected but surface FCC precipitation was found as a result of the focused ion beam sample preparation. Decreasing the irradiation dose by lowering the energy and current of the Ga+ ions did not lead to a complete disappearance of the FCC structure. The latter could only be removed after gentle Ar+ ion milling of the sample. It was further concluded that the precipitation of the FCC is independent of the crystallographic orientation of the surface.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.147
Times cited: 2
DOI: 10.1002/jemt.20877
|
|
|
“A simplified approach to the band gap correction of defect formation energies : Al, Ga, and In-doped ZnO”. Saniz R, Xu Y, Matsubara M, Amini MN, Dixit H, Lamoen D, Partoens B, The journal of physics and chemistry of solids 74, 45 (2013). http://doi.org/10.1016/j.jpcs.2012.07.017
Abstract: The calculation of defect levels in semiconductors within a density functional theory approach suffers greatly from the band gap problem. We propose a band gap correction scheme that is based on the separation of energy differences in electron addition and relaxation energies. We show that it can predict defect levels with a reasonable accuracy, particularly in the case of defects with conduction band character, and yet is simple and computationally economical. We apply this method to ZnO doped with group III elements (Al, Ga, In). As expected from experiment, the results indicate that Zn substitutional doping is preferred over interstitial doping in Al, Ga, and In-doped ZnO, under both zinc-rich and oxygen-rich conditions. Further, all three dopants act as shallow donors, with the +1 charge state having the most advantageous formation energy. Also, doping effects on the electronic structure of ZnO are sufficiently mild so as to affect little the fundamental band gap and lowest conduction bands dispersion, which secures their n-type transparent conducting behavior. A comparison with the extrapolation method based on LDA+U calculations and with the HeydScuseriaErnzerhof hybrid functional (HSE) shows the reliability of the proposed scheme in predicting the thermodynamic transition levels in shallow donor systems.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Condensed Matter Theory (CMT)
Impact Factor: 2.059
Times cited: 36
DOI: 10.1016/j.jpcs.2012.07.017
|
|
|
“Site occupation of Nb atoms in ternary Ni-Ti-Nb shape memory alloys”. Shi H, Frenzel J, Martinez GT, Van Rompaey S, Bakulin A, Kulkova A, Van Aert S, Schryvers D, Acta materialia 74, 85 (2014). http://doi.org/10.1016/j.actamat.2014.03.062
Abstract: Nb occupancy in the austenite B2-NiTi matrix and Ti2Ni phase in NiTiNb shape memory alloys was investigated by aberration-corrected scanning transmission electron microscopy and precession electron diffraction. In both cases, Nb atoms were found to prefer to occupy the Ti rather than Ni sites. A projector augmented wave method within density functional theory was used to calculate the atomic and electronic structures of the austenitic B2-NiTi matrix phase and the Ti2Ni precipitates both with and without addition of Nb. The obtained formation energies and analysis of structural and electronic characteristics explain the preference for Ti sites for Nb over Ni sites.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 5.301
Times cited: 21
DOI: 10.1016/j.actamat.2014.03.062
|
|
|
“Size-dependent enhancement of superconductivity in Al and Sn nanowires: shape-resonance effect”. Shanenko AA, Croitoru MD, Zgirski M, Peeters FM, Arutyunov K, Physical review : B : condensed matter and materials physics 74, 052502 (2006). http://doi.org/10.1103/PhysRevB.74.052502
Keywords: A1 Journal article; Condensed Matter Theory (CMT); Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 95
DOI: 10.1103/PhysRevB.74.052502
|
|
|
“Adsorption of sulfur onto a surface of silver nanoparticles stabilized with sago starch biopolymer”. Djoković, V, Krsmanović, R, Božanić, DK, McPherson M, Van Tendeloo G, Nair PS, Georges MK, Radhakrishnan T, Colloids and surfaces: B : biointerfaces 73, 30 (2009). http://doi.org/10.1016/j.colsurfb.2009.04.022
Abstract: Adsorption of sulfide ions onto a surface of starch capped silver nanoparticles upon addition of thioacetamide was investigated. UVvis absorption spectroscopy revealed that the adsorption of the sulfide ion on the surface of the silver nanoparticles induced damping as well as blue shift of the silver surface plasmon resonance band. Further increase in thioacetamide concentration led to shift of the resonance band toward higher wavelengths indicating the formation of the continuous Ag2S layer on the silver surface. Thus fabricated nanoparticles were investigated using electron microscopy techniques (TEM, HRTEM, and HAADF-STEM) and X-ray photoelectron spectroscopy (XPS), which confirmed their coreshell structure.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.887
Times cited: 41
DOI: 10.1016/j.colsurfb.2009.04.022
|
|
|
“Atomic-scale modification of hybrid FePt cluster-assembled films”. Dobrynin AN, Ievlev DN, Verschoren G, Swerts J, van Bael MJ, Temst K, Lievens P, Piscopiello E, Van Tendeloo G, Zhou SQ, Vantomme A, Physical review : B : condensed matter and materials physics 73, 104421 (2006). http://doi.org/10.1103/PhysRevB.73.104421
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 13
DOI: 10.1103/PhysRevB.73.104421
|
|
|
“Defect structure of ferromagnetic superconducting RuSr2GdCu2O8”. Lebedev OI, Van Tendeloo G, Attfield JP, McLaughlin AC, Physical review : B : condensed matter and materials physics 73 (2006). http://doi.org/10.1103/PhysRevB.73.224524
Abstract: The structure and defect structure of superconducting ferromagnetic bulk RuSr2GdCu2O8 has been investigated using high-resolution transmission electron microscopy and high-resolution scanning transmission microscopy. Two distinct, but closely related structures, due to ordering of rotated RuO6 octahedra and due to Cu substitution in the Ru-O layer, have been revealed. The structure of Ru1-xSr2GdCu2+xO8-delta can be described as a periodic alteration along the c axis of CuO4 planes and RuO6 octahedra. The unit-cell parameters of this phase are root 2a(p) x root 2a(p) x 2c. The possible influence of this phase and defect structure on the sensitivity of the superconductivity and magnetic properties is discussed. Local defects such as 90 S domain boundaries, (130) antiphase boundaries, and the associated dislocations are analyzed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 11
DOI: 10.1103/PhysRevB.73.224524
|
|
|
“Influence of finite size effects on exchange anisotropy in oxidized Co nanocluster assembled films”. Dobrynin AN, Ievlev DN, Hendrich C, Temst K, Lievens P, Hörmann U, Verbeeck J, Van Tendeloo G, Vantomme A, Physical review : B : condensed matter and materials physics 73, 245416 (2006). http://doi.org/10.1103/PhysRevB.73.245416
Abstract: We compare the magnetic properties of Co cluster assembled films with different degrees of oxidation. Clusters with grain size (2.3 +/- 0.7) nm are produced in a laser vaporization cluster source and soft-landed in ultrahigh vacuum conditions, forming highly porous nanogranular films. After exposure to air for different periods of time, the Co clusters oxidize and the sample may be considered as a thin antiferromagnetic Co oxide matrix containing ferromagnetic Co clusters. Magnetization measurements were performed in a temperature range from 300 down to 5 K, at applied magnetic fields up to 30 kOe. The exchange bias value at 5 K for the strongly oxidized sample is 4.8 kOe against the value of 0.75 kOe for the less oxidized sample. The mean values of the thicknesses of the Co oxide layers are estimated to be 0.6 and 0.3 nm for the more and less oxidized sample, respectively. We propose a method of measuring the exchange bias inducing temperature, i.e., the temperature at which exchange anisotropy is established. We determined the mean inducing temperatures for both samples, which are 55 and 25 K, respectively, for the more and less oxidized samples. Both temperatures are well below the bulk CoO Neel temperature of 292 K. A low value of the inducing temperature of the Co oxide layer is a consequence of its subnanometer thickness, while a large exchange bias value is a consequence of different dimensionality of Co clusters and Co oxide matrix.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 17
DOI: 10.1103/PhysRevB.73.245416
|
|
|
“Shape resonances in the superconducting order parameter of ultrathin nanowires”. Shanenko AA, Croitoru MD, Physical review : B : condensed matter and materials physics 73, 012510 (2006). http://doi.org/10.1103/PhysRevB.73.012510
Keywords: A1 Journal article; Condensed Matter Theory (CMT); Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 41
DOI: 10.1103/PhysRevB.73.012510
|
|
|
“Energy-loss near-edge structure changes with bond length in carbon systems”. Titantah JT, Lamoen D, Physical review : B : condensed matter and materials physics 72, 193104 (2005). http://doi.org/10.1103/PhysRevB.72.193104
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 24
DOI: 10.1103/PhysRevB.72.193104
|
|
|
“First-principles calculations of 002 structure factors for electron scattering in strained InxGa1-xAs”. Rosenauer A, Schowalter M, Glas F, Lamoen D, Physical Review B 72, 1 (2005). http://doi.org/10.1103/PhysRevB.72.085326
Abstract: This work provides values of electron scattering 002 structure factors for InxGa1-xAs as a function of the In concentration x=0 to 1. These results allow accurate compositional analysis of pseudomorphically grown InxGa1-xAs/GaAs layers by transmission electron microscopy methods relying on the chemical sensitivity of the (002) beam. The calculations go beyond the limits of the isolated atom approximation, because they take into account charge redistribution effects between atomic sites in the crystal, strain, and static atomic displacements. The computations were performed by the full potential linearized augmented plane-wave method using a generalized gradient approximation for the exchange and correlation part of the potential. The calculations of strained InxGa1-xAs correspond to the strain state in specimens with large, small, and intermediate thickness in the electron beam direction. Additionally, the effect of static atomic displacements is taken into account. All results are listed in a parameterized form. The calculated 002 structure factor vanishes at an In concentration of 16.4%. This value is in a good agreement with previously reported experimental measurements. Hence, our results are a significant improvement with respect to the isolated atom approximation which is conventionally applied in transmission electron microscopy simulations, and which predicts a value of 22.5%.
Keywords: A1 Journal article; Electron Microscopy for Materials Science (EMAT);
Impact Factor: 3.836
Times cited: 42
DOI: 10.1103/PhysRevB.72.085326
|
|
|
“High resolution electron microscopy and X-ray photoelectron spectroscopy studies of heteroepitaxial SixGe1-x alloys produced through laser induced processing”. Frangis N, van Landuyt J, Lartiprete R, Martelli S, Borsella E, Chiussi S, Castro J, Leon B, Applied physics letters 72, 2877 (1998). http://doi.org/10.1063/1.121487
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 16
DOI: 10.1063/1.121487
|
|
|
“R-phase transition and related mechanical properties controlled by low-temperature aging treatment in a Ti50.8 at.% Ni thin wire”. Wang X, Li K, Schryvers D, Verlinden B, Van Humbeeck J, Scripta materialia 72-73, 21 (2014). http://doi.org/10.1016/j.scriptamat.2013.10.006
Abstract: A cold-drawn Ti50.8 at.% Ni wire was annealed at 600 °C for 30 min, followed by aging at 250 °C for different times. A microstructure with small grains and nanoscaled precipitates was obtained. The thermally induced martensite transformation is suppressed in the samples aged for 4 h or longer, leaving a one-stage R-phase transition between −150 and +150 °C. The transformation behavior, work output and recovery stress associated with the R-phase transition are presented.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.747
Times cited: 27
DOI: 10.1016/j.scriptamat.2013.10.006
|
|
|
“Twinning in pure Ti subjected to monotonic simple shear deformation”. Tirry W, Bouvier S, Benmhenni N, Hammami W, Habraken AM, Coghe F, Schryvers D, Rabet L, Materials characterization 72, 24 (2012). http://doi.org/10.1016/j.matchar.2012.07.001
Abstract: The aim of this paper is to provide a thorough study on the occurrence and importance of deformation twinning in simple shear deformed pure α-Ti. A statistically relevant inspection of the morphology of the deformation twins in relation to the applied strain/deformation is performed. The investigated microstructural aspects are the twin volume fraction, the twin thickness distribution and the resolved shear stress distribution on the twin plane. All these aspects are examined as a function of the twin types and two initial textures. Monotonic simple shear experiments are carried out for three different loading directions with respect to a direction linked to the initial crystallographic texture. EBSD and TEM observations reveal the presence of View the MathML source and View the MathML source twins. The statistical analysis reveals that View the MathML source and View the MathML source twins have a similar average thickness around 1.9 nm, but the View the MathML source twins show a far larger spread on their thickness and can grow to almost the size of the original parent grain. Correlation of the twin fractions with the RSS analysis shows that RSS is an acceptable method explaining the difference in twin fractions for different textures and orientations. A detailed analysis shows that View the MathML source twins occur in average with a smaller volume fraction but with a higher RSS, indicating they are more difficult to nucleate or grow compared to View the MathML source twinning. In general a higher RSS value on the twin plane is not connected to a higher twin thickness; only in the case of View the MathML source twins the highest RSS values show clearly thicker twins.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.714
Times cited: 25
DOI: 10.1016/j.matchar.2012.07.001
|
|
|
“Electron microscopy study of coiled carbon tubules”. Bernaerts D, Zhang XB, Zhang XF, Amelinckx S, Van Tendeloo G, van Landuyt J, Ivanov V, Nagy JB, Philosophical magazine: A: physics of condensed matter: defects and mechanical properties 71, 605 (1995). http://doi.org/10.1080/01418619508244470
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 72
DOI: 10.1080/01418619508244470
|
|