“Au@ZIFs: stabilization and encapsulation of cavity-size matching gold clusters inside functionalized Zeolite Imidazolate Frameworks, ZIFs”. Esken D, Turner S, Lebedev OI, Van Tendeloo G, Fischer RA, Chemistry of materials 22, 6393 (2010). http://doi.org/10.1021/cm102529c
Abstract: The selective formation and stabilization of very small, naked metal particles inside the cavities of metal organic frameworks (MOFs) and the simultaneous realization of an even distribution of the particles throughout the crystalline MOF host matrix over a wide range of metal loading are challenging goals. MOFs reveal high specific surface areas, tunable pore sizes, and organic linkers, which are able to interact with guests. The chemically very robust zeolite imidazolate frameworks (ZIFs) are a subclass of MOFs. We chose the microporous sodalite-like ZIF-8 (Zn(MelM)(2); IM = imidazolate) and ZIF-90 (Zn(ICA)(2); ICA = imidazolate-2-carboxyaldehyde) as host matrices to influence the dispersion of imbedded gold nanoparticles (Au NPs). The metal loading was achieved via gas phase infiltration of [Au(CO)Cl] followed by a thermal hydrogenation step to form the Au NPs. Low-dose high-resolution transmission electron microscopy ((HR)TEM) and electron tomography reveal a homogeneous distribution of Au NPs throughout the ZIF matrix. The functional groups of ZIF-90 direct the anchoring of intermediate Au species and stabilize drastically smaller and quite monodisperse Au NPs in contrast to the parent not functionalized ZIF-8. The particles can be very small, match the cavity size and approach defined molecular clusters of magic numbers, i.e., Au(55), independently from the level of loading. Post-synthetic oxidation of the aldehyde groups to yield alkyl esters by the adjacent, catalytically active metal NPs is presented as a new concept of encapsulating nanoparticles inside MOFs and allows multiple steps of metal loadings without decomposition of the MOF.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 194
DOI: 10.1021/cm102529c
|
|
|
“Austenite and martensite microstructures in splat-cooled Ni-Al”. Schryvers D, Holland-Moritz D, Intermetallics 6, 427 (1998). http://doi.org/10.1016/S0966-9795(97)00091-5
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.14
Times cited: 13
DOI: 10.1016/S0966-9795(97)00091-5
|
|
|
“Automated discrete electron tomography &ndash, Towards routine high-fidelity reconstruction of nanomaterials”. Zhuge X, Jinnai H, Dunin-Borkowski RE, Migunov V, Bals S, Cool P, Bons A-J, Batenburg KJ, Ultramicroscopy 175, 87 (2017). http://doi.org/10.1016/j.ultramic.2017.01.009
Abstract: Electron tomography is an essential imaging technique for the investigation of morphology and 3D structure of nanomaterials. This method, however, suffers from well-known missing wedge artifacts due to a restricted tilt range, which limits the objectiveness, repeatability and efficiency of quantitative structural analysis. Discrete tomography represents one of the promising reconstruction techniques for materials science, potentially capable of delivering higher fidelity reconstructions by exploiting the prior knowledge of the limited number of material compositions in a specimen. However, the application of discrete tomography to practical datasets remains a difficult task due to the underlying challenging mathematical problem. In practice, it is often hard to obtain consistent reconstructions from experimental datasets. In addition, numerous parameters need to be tuned manually, which can lead to bias and non-repeatability. In this paper, we present the application of a new
iterative reconstruction technique, named TVR-DART, for discrete electron tomography. The technique is capable of consistently delivering reconstructions with significantly reduced missing wedge artifacts for a variety of challenging data and imaging conditions, and can automatically estimate its key parameters. We describe the principles of the technique and apply it to datasets from three different types of samples acquired under diverse imaging modes. By further reducing the available tilt range and number of projections, we show that the
proposed technique can still produce consistent reconstructions with minimized missing wedge artifacts. This new development promises to provide the electron microscopy community with an easy-to-use and robust tool for high-fidelity 3D characterization of nanomaterials.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 2.843
Times cited: 22
DOI: 10.1016/j.ultramic.2017.01.009
|
|
|
“Automatic correction of nonlinear damping effects in HAADF-STEM tomography for nanomaterials of discrete compositions”. Zhong Z, Aveyard R, Rieger B, Bals S, Palenstijn WJ, Batenburg KJ, Ultramicroscopy 184, 57 (2018). http://doi.org/10.1016/J.ULTRAMIC.2017.10.013
Abstract: <script type='text/javascript'>document.write(unpmarked('HAADF-STEM tomography is a common technique for characterizing the three-dimensional morphology of nanomaterials. In conventional tomographic reconstruction algorithms, the image intensity is assumed to be a linear projection of a physical property of the specimen. However, this assumption of linearity is not completely valid due to the nonlinear damping of signal intensities. The nonlinear damping effects increase w.r.t the specimen thickness and lead to so-called \u0022cupping artifacts\u0022, due to a mismatch with the linear model used in the reconstruction algorithm. Moreover, nonlinear damping effects can strongly limit the applicability of advanced reconstruction approaches such as Total Variation Minimization and discrete tomography. In this paper, we propose an algorithm for automatically correcting the nonlinear effects and the subsequent cupping artifacts. It is applicable to samples in which chemical compositions can be segmented based on image gray levels. The correction is realized by iteratively estimating the nonlinear relationship between projection intensity and sample thickness, based on which the projections are linearized. The correction and reconstruction algorithms are tested on simulated and experimental data. (C) 2017 Elsevier B.V. All rights reserved.'));
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.843
Times cited: 8
DOI: 10.1016/J.ULTRAMIC.2017.10.013
|
|
|
“Au2Sx/CdS nanorods by cation exchange : mechanistic insights into the competition between cation-exchange and metal ion reduction”. Kundu S, Kundu P, Van Tendeloo G, Ravishankar N, Small 10, 3895 (2014). http://doi.org/10.1002/smll.201400524
Abstract: Thumbnail image of graphical abstract It is well known that metals with higher electron affinity like Au tend to undergo reduction rather than cation-exchange. It is experimentally shown that under certain conditions cation-exchange is dominant over reduction. Thermodynamic calculation further consolidates the understanding and paves the way for better predictability of cation-exchange/reduction reactions for other systems.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 8.643
Times cited: 8
DOI: 10.1002/smll.201400524
|
|
|
“AVPO4F (A = Li, K): A 4 V Cathode Material for High-Power Rechargeable Batteries”. Fedotov SS, Khasanova NR, Samarin AS, Drozhzhin OA, Batuk D, Karakulina OM, Hadermann J, Abakumov AM, Antipov EV, Chemistry of materials 28, 411 (2016). http://doi.org/10.1021/acs.chemmater.5b04065
Abstract: A novel potassium-based fluoride-phosphate, KVPO4F, with a KTiOPO4 (KTP) type structure is synthesized and characterized. About 85% of potassium has been electrochemically extracted on oxidation producing a cathode material with attractive performance for Li-ion batteries. The material operates at the electrode potential near 4V vs Li/Li+ exhibiting a sloping voltage profile, extremely low polarization, small volume change of about 2% and excellent rate capability, maintaining more than 75% of the initial capacity at 40C discharge rate without significant fading.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 46
DOI: 10.1021/acs.chemmater.5b04065
|
|
|
“B-site ordered perovskite LaSrMnNbO6 : synthesis, structure and antiferromagnetism”. Yang T, Perkisas T, Hadermann J, Croft M, Ignatov A, Greenblatt M, Journal of solid state chemistry 183, 2689 (2010). http://doi.org/10.1016/j.jssc.2010.08.041
Abstract: LaSrMnNbO6 has been synthesized by high temperature solid state reaction under 1% H2/Ar dynamic flow. The structure is determined by Rietveld refinement of the powder X-ray diffraction data. It crystallizes in the monoclinic space group P21/n with the unit cell parameters: a=5.69187(12), b=5.74732(10), c=8.07018(15) Å and β=90.0504(29)°, which were also confirmed by electron diffraction. The Mn2+ and Nb5+ ions, whose valence states are confirmed by X-ray absorption near-edge spectroscopy, are almost completely ordered over the B-site (<1% inversion) of the perovskite structure due to the large differences of both cationic size (0.19 Å) and charge. The octahedral framework displays significant tilting distortion according to Glazers tilt system a−b−c+. Upon heating, LaSrMnNbO6 decomposes at 690 °C under O2 flow or at 775 °C in air. The magnetic susceptibility data indicate the presence of long-range antiferromagnetic ordering at TN=8 K; the experimentally observed effective paramagnetic moment, μeff=5.76 μB for high spin Mn2+ (3d5, S=5/2) is in good agreement with the calculated value (μcalcd=5.92 μB).
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 13
DOI: 10.1016/j.jssc.2010.08.041
|
|
|
“Ba-3(Cr0.97(1)Te0.03(1))(2)TeO9: in Search of Jahn-Teller Distorted Cr(II) Oxide”. Li M-R, Deng Z, Lapidus SH, Stephens PW, Segre CU, Croft M, Sena RP, Hadermann J, Walker D, Greenblatt M, Inorganic chemistry 55, 10135 (2016). http://doi.org/10.1021/ACS.INORGCHEM.6B01047
Abstract: A novel 6H-type hexagonal perovskite Ba-3(Cr0.97(1)Te0.03(1))(2)TeO9 was prepared at high pressure (6 GPa) and temperature (1773 K). Both transmission electron microscopy and synchrotron powder X-ray diffraction data demonstrate that Ba-3(Cr0.97(1)Te0.03(1))(2)TeO9 crystallizes in P6(3)/mmc with face-shared (Cr0.97(1)Te0.03(1))O-6 octahedral pairs interconnected with TeO6 octahedra via corner-sharing. Structure analysis shows a mixed Cr2+/Cr3+ valence state with similar to 10% Cr2+. The existence of Cr2+ in Ba-3(Cr0.10(1)2+Cr0.87(1)3+Te0.036+)(2)TeO9 is further evidenced by X-ray absorption near-edge spectroscopy. Magnetic properties measurements show a paramagnetic response down to 4 K and a small glassy-state curvature at low temperature. In this work, the octahedral Cr2+O6 component is stabilized in an oxide material for the first time; the expected Jahn-Teller distortion of high-spin (d(4)) Cr2+ is not found, which is attributed to the small proportion of Cr2+ (similar to 10%) and the face-sharing arrangement of CrO6 octahedral pairs, which structurally disfavor axial distortion.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 2
DOI: 10.1021/ACS.INORGCHEM.6B01047
|
|
|
“BaHfO3artificial pinning centres in TFA-MOD-derived YBCO and GdBCO thin films”. Erbe M, Hänisch J, Hühne R, Freudenberg T, Kirchner A, Molina-Luna L, Damm C, Van Tendeloo G, Kaskel S, Schultz L, Holzapfel B, Superconductor science and technology 28, 114002 (2015). http://doi.org/10.1088/0953-2048/28/11/114002
Abstract: Chemical solution deposition (CSD) is a promising way to realize REBa2Cu3O7−x (REBCO;RE = rare earth (here Y, Gd))-coated conductors with high performance in applied magnetic fields. However, the preparation process contains numerous parameters which need to be tuned to achieve high-quality films. Therefore, we investigated the growth of REBCO thin films containing nanometre-scale BaHfO3 (BHO) particles as pinning centres for magnetic flux lines, with emphasis on the influence of crystallization temperature and substrate on the microstructure and superconductivity. Conductivity, microscopy and x-ray investigations show an enhanced performance of BHO nano-composites in comparison to pristine REBCO. Further, those measurements reveal the superiority of GdBCO to YBCO—e.g. by inductive critical current densities, Jc, at self-field and 77 K. YBCO is outperformed by more than 1 MA cm−2 with Jc values of up to 5.0 MA cm−2 for 265 nm thick layers of GdBCO(BHO) on lanthanum aluminate. Transport in-field Jc measurements demonstrate high pinning force maxima of around 4 GN m−3 for YBCO(BHO) and GdBCO(BHO). However, the irreversibility fields are appreciably higher for GdBCO. The critical temperature was not significantly reduced upon BHO addition to both YBCO and GdBCO, indicating a low tendency for Hf diffusion into the REBCO matrix. Angular-dependent Jc measurements show a reduction of the anisotropy in the same order of magnitude for both REBCO compounds. Theoretical models suggest that more than one sort of pinning centre is active in all CSD films.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.878
Times cited: 36
DOI: 10.1088/0953-2048/28/11/114002
|
|
|
“Ball milling effect on the structure of single-wall carbon nanotubes”. Pierard N, Fonseca A, Colomer J-F, Bossuot C, Benoit J-M, Van Tendeloo G, Pirard J-P, Nagy JB, Carbon 42, 1691 (2004). http://doi.org/10.1016/j.carbon.2004.02.031
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.337
Times cited: 133
DOI: 10.1016/j.carbon.2004.02.031
|
|
|
“Band flattening in buckled monolayer graphene”. Milovanović, SP, Andelkovic M, Covaci L, Peeters FM, Physical Review B 102, 245427 (2020). http://doi.org/10.1103/PHYSREVB.102.245427
Abstract: The strain fields of periodically buckled graphene induce a periodic pseudomagnetic field (PMF) that modifies the electronic band structure. From the geometry, amplitude, and period of the periodic pseudomagnetic field, we determine the necessary conditions to access the regime of correlated phases by examining the band flattening. As compared to twisted bilayer graphene the proposed system has the advantages that (1) only a single layer of graphene is needed, (2) one is not limited to hexagonal superlattices, and (3) narrower flat bandwidth and larger separation between flat bands can be induced. We, therefore, propose that periodically strained graphene single layers can become a platform for the exploration of exotic many-body phases.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Condensed Matter Theory (CMT)
Impact Factor: 3.7
Times cited: 11
DOI: 10.1103/PHYSREVB.102.245427
|
|
|
“Band structure quantization in nanometer sized ZnO clusters”. Schouteden K, Zeng Y-J, Lauwaet K, Romero CP, Goris B, Bals S, Van Tendeloo G, Lievens P, Van Haesendonck C, Nanoscale 5, 3757 (2013). http://doi.org/10.1039/c3nr33989k
Abstract: Nanometer sized ZnO clusters are produced in the gas phase and subsequently deposited on clean Au(111) surfaces under ultra-high vacuum conditions. The zinc blende atomic structure of the approximately spherical ZnO clusters is resolved by high resolution scanning transmission electron microscopy. The large band gap and weak n-type conductivity of individual clusters are determined by scanning tunnelling microscopy and spectroscopy at cryogenic temperatures. The conduction band is found to exhibit clear quantization into discrete energy levels, which can be related to finite-size effects reflecting the zero-dimensional confinement. Our findings illustrate that gas phase cluster production may provide unique possibilities for the controlled fabrication of high purity quantum dots and heterostructures that can be size selected prior to deposition on the desired substrate under controlled ultra-high vacuum conditions.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 7.367
Times cited: 13
DOI: 10.1039/c3nr33989k
|
|
|
“Bandgap measurement of high refractive index materials by off-axis EELS”. Vatanparast M, Egoavil R, Reenaas TW, Verbeeck J, Holmestad R, Vullum PE, Ultramicroscopy 182, 92 (2017). http://doi.org/10.1016/J.ULTRAMIC.2017.06.019
Abstract: In the present work Cs aberration corrected and monochromated scanning transmission electron microscopy electron energy loss spectroscopy (STEM-EELS) has been used to explore experimental setups that allow bandgaps of high refractive index materials to be determined. Semi-convergence and collection angles in the mu rad range were combined with off-axis or dark field EELS to avoid relativistic losses and guided light modes in the low loss range to contribute to the acquired EEL spectra. Off-axis EELS further supressed the zero loss peak and the tail of the zero loss peak. The bandgap of several GaAs-based materials were successfully determined by simple regression analyses of the background subtracted EEL spectra. The presented set-up does not require that the acceleration voltage is set to below the. Cerenkov limit and can be applied over the entire acceleration voltage range of modern TEMs and for a wide range of specimen thicknesses. (C) 2017 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.843
Times cited: 3
DOI: 10.1016/J.ULTRAMIC.2017.06.019
|
|
|
“Barium-based manganites Ln1-xBaxMnO3 with Ln = {Pr, La}: phase transitions and magnetoresistance properties”. Barnabé, A, Millange F, Maignan A, Hervieu M, Raveau B, Van Tendeloo G, Laffez P, Chem. mater. 10, 252 (1998). http://doi.org/10.1021/cm9704084
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 48
DOI: 10.1021/cm9704084
|
|
|
“Barrier efficiency of sponge-like La2Zr2O7 buffer layers for YBCO-coated conductors”. Molina L, Tan H, Biermans E, Batenburg KJ, Verbeeck J, Bals S, Van Tendeloo G, Superconductor science and technology 24, 065019 (2011). http://doi.org/10.1088/0953-2048/24/6/065019
Abstract: Solution derived La2Zr2O7 films have drawn much attention for potential applications as thermal barriers or low-cost buffer layers for coated conductor technology. Annealing and coating parameters strongly affect the microstructure of La2Zr2O7, but different film processing methods can yield similar microstructural features such as nanovoids and nanometer-sized La2Zr2O7 grains. Nanoporosity is a typical feature found in such films and the implications for the functionality of the films are investigated by a combination of scanning transmission electron microscopy (STEM), electron energy-loss spectroscopy (EELS) and quantitative electron tomography. Chemical solution based La2Zr2O7 films deposited on flexible Ni5 at.%W substrates with a {100}lang001rang biaxial texture were prepared for an in-depth characterization. A sponge-like structure composed of nanometer-sized voids is revealed by high-angle annular dark-field scanning transmission electron microscopy in combination with electron tomography. A three-dimensional quantification of nanovoids in the La2Zr2O7 film is obtained on a local scale. Mostly non-interconnected highly faceted nanovoids compromise more than one-fifth of the investigated sample volume. The diffusion barrier efficiency of a 170 nm thick La2Zr2O7 film is investigated by STEM-EELS, yielding a 1.8 ± 0.2 nm oxide layer beyond which no significant nickel diffusion can be detected and intermixing is observed. This is of particular significance for the functionality of YBa2Cu3O7 − δ coated conductor architectures based on solution derived La2Zr2O7 films as diffusion barriers.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 2.878
Times cited: 31
DOI: 10.1088/0953-2048/24/6/065019
|
|
|
“Ba2Y(Nb/Ta)O6–Doped YBCO Films on Biaxially Textured Ni–5at.% W Substrates”. Sieger M, Pahlke P, Hanisch J, Sparing M, Bianchetti M, MacManus-Driscoll J, Lao M, Eisterer M, Meledin A, Van Tendeloo G, Nast R, Schultz L, Holzapfel B, Huhne R, IEEE transactions on applied superconductivity 26, 1 (2016). http://doi.org/10.1109/TASC.2016.2539254
Abstract: The incorporation of nanoscaled pinning centers in superconducting YBa2Cu3O7-d (YBCO) films is one of the core topics to enhance the critical current density Jc(B, Q) of coated conductors. The mixed double-perovskite Ba2Y(Nb/Ta)O6 (BYNTO) can be grown in nanosized columns parallel the YBCO c-axis and in step-like patterns, making it customizable to meet specific working conditions (T, B, Q). We compare a 1.6 μm thick film of pure YBCO and a similar film with additional 5 mol% of BYNTO, grown by pulsed laser deposition with a growth rate of 1.6 nm/s on buffered biaxially textured Ni-5at.% W tape. Our doped sample shows nanosized BYNTO columns parallel cYBCO and plates in the ab-plane containing Y, Nb and Ta. An improved homogeneity of the critical current density Jc over the sample was evaluated from trapped field profiles measured with a scanning Hall probe microscope. The mean Jc in rolling direction of the tape is 1.8 MA/cm² (77 K, self-field) and doubles the value of the undoped sample. Angular dependent measurements of the critical current density, Jc(Q), show a decreased anisotropy of the doped film for various magnetic fields at 77 K as well as 64 K.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 6
DOI: 10.1109/TASC.2016.2539254
|
|
|
“Behavior of Ni-doped MgMoO4 single-phase catalysts for synthesis of multiwalled carbon nanotube bundles”. Li Y, Zhang X, Geise HJ, Van Tendeloo G, Chemical vapor deposition 13, 30 (2007). http://doi.org/10.1002/cvde.200606531
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.333
Times cited: 4
DOI: 10.1002/cvde.200606531
|
|
|
“Bending Gold Nanorods with Light”. Babynina A, Fedoruk M, Kuhler P, Meledin A, Doblinger M, Lohmueller T, Nano letters 16, 6485 (2016). http://doi.org/10.1021/acs.nanolett.6b03029
Abstract: V-shaped gold nanoantennas are the functional components of plasmonic metasurfaces, which are capable of manipulating light in unprecedented ways. Designing a metasurface requires the custom arrangement of individual antennas with controlled shape and orientation. Here, we show how highly crystalline gold nanorods in solution can be bend, one-by one, into a V-shaped geometry and printed to the surface of a solid support through a combination of plasmonic heating and optical force. Significantly, we demonstrate that both the bending angle and the orientation of each rod-antenna can be adjusted independent from each other by tuning the laser intensity and polarization. This approach is applicable for the patterning of V-shaped plasmonic antennas on almost any substrate, which holds great potential for the fabrication of ultrathin optical components and devices.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 12.712
Times cited: 24
DOI: 10.1021/acs.nanolett.6b03029
|
|
|
“Bending martensite needles in Ni65Al35 investigated by two-dimensional elasticity and high-resolution transmission electron microscopy”. Boullay P, Schryvers D, Kohn RV, Physical review : B : condensed matter and materials physics 64, 144105 (2001). http://doi.org/10.1103/PhysRevB.64.144105
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 18
DOI: 10.1103/PhysRevB.64.144105
|
|
|
“Berry phase engineering at oxide interfaces”. Groenendijk DJ, Autieri C, van Thiel TC, Brzezicki W, Hortensius JR, Afanasiev D, Gauquelin N, Barone P, van den Bos KHW, van Aert S, Verbeeck J, Filippetti A, Picozzi S, Cuoco M, Caviglia AD, 2, 023404 (2020). http://doi.org/10.1103/PhysRevResearch.2.023404
Abstract: Three-dimensional strontium ruthenate (SrRuO3) is an itinerant ferromagnet that features Weyl points acting as sources of emergent magnetic fields, anomalous Hall conductivity, and unconventional spin dynamics. Integrating SrRuO3 in oxide heterostructures is potentially a novel route to engineer emergent electrodynamics, but its electronic band topology in the two-dimensional limit remains unknown. Here we show that ultrathin SrRuO3 exhibits spin-polarized topologically nontrivial bands at the Fermi energy. Their band anticrossings show an enhanced Berry curvature and act as competing sources of emergent magnetic fields. We control their balance by designing heterostructures with symmetric (SrTiO3/SrRuO3/SrTiO3 and SrIrO3/SrRuO3/SrIrO3) and asymmetric interfaces (SrTiO3/SrRuO3/SrIrO3). Symmetric structures exhibit an interface-tunable single-channel anomalous Hall effect, while ultrathin SrRuO3 embedded in asymmetric structures shows humplike features consistent with multiple Hall contributions. The band topology of two-dimensional SrRuO3 proposed here naturally accounts for these observations and harmonizes a large body of experimental results.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 58
DOI: 10.1103/PhysRevResearch.2.023404
|
|
|
“Beyond surface redox and oxygen mobility at pd-polar ceria (100) interface : underlying principle for strong metal-support interactions in green catalysis”. Mahadi AH, Ye L, Fairclough SM, Qu J, Wu S, Chen W, Papaioannou E, Ray B, Pennycook TJ, Haigh SJ, Young NP, Tedsree K, Metcalfe IS, Tsang SCE, Applied Catalysis B-Environmental 270, 118843 (2020). http://doi.org/10.1016/J.APCATB.2020.118843
Abstract: When ceria is used as a support for many redox catalysis involved in green catalysis, it is well-known that the overlying noble metal can gain access to a significant quantity of oxygen atoms with high mobility and fast reduction and oxidation properties under mild conditions. However, it is as yet unclear what the underlying principle and the nature of the ceria surface involved are. By using two tailored morphologies of ceria nanocrystals, namely cubes and rods, it is demonstrated from Scanning Transmission Electron Microscopy with Electron Energy Loss Spectroscopy (STEM-EELS) mapping and Pulse Isotopic Exchange (PIE) that ceria nano-cubes terminated with a polar surface (100) can give access to more than the top most layer of surface oxygen atoms. Also, they give higher oxygen mobility than ceria nanorods with a non-polar facet of (110). A new insight for the possible additional role of polar ceria surface plays in the oxygen mobility is obtained from Density Functional Theory (DFT) calculations which suggest that the (100) surface sites that has more than half-filled O on same plane can drive oxygen atoms to oxidise adsorbate(s) on Pd due to the strong electrostatic repulsion.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 22.1
DOI: 10.1016/J.APCATB.2020.118843
|
|
|
“Bi(3n+1)Ti7Fe(3n-3)O(9n+11) Homologous Series: Slicing Perovskite Structure with Planar Interfaces Containing Anatase-like Chains”. Batuk D, Tsirlin AA, Filimonov DS, Zakharov KV, Volkova OS, Vasiliev A, Hadermann J, Abakumov AM, Inorganic chemistry 55, 1245 (2016). http://doi.org/10.1021/acs.inorgchem.5b02465
Abstract: The n = 3-6 members of a new perovskite-based homologous series Bi(3n+1)Ti7Fe(3n-3)O(9n+11) are reported. The crystal structure of the n = 3 Bi10Ti7Fe6O38 member is refined using a combination of X-ray and neutron powder diffraction data (a = 11.8511(2) A, b = 3.85076(4) A, c = 33.0722(6) A, S.G. Immm), unveiling the partially ordered distribution of Ti(4+) and Fe(3+) cations and indicating the presence of static random displacements of the Bi and O atoms. All Bi(3n+1)Ti7Fe(3n-3)O(9n+11) structures are composed of perovskite blocks separated by translational interfaces parallel to the (001)p perovskite planes. The thickness of the perovskite blocks increases with n, while the atomic arrangement at the interfaces remains the same. The interfaces comprise chains of double edge-sharing (Fe,Ti)O6 octahedra connected to the octahedra of the perovskite blocks by sharing edges and corners. This configuration shifts the adjacent perovskite blocks relative to each other over a vector (1/2)[110]p and creates S-shaped tunnels along the [010] direction. The tunnels accommodate double columns of the Bi(3+) cations, which stabilize the interfaces owing to the stereochemical activity of their lone electron pairs. The Bi(3n+1)Ti7Fe(3n-3)O(9n+11) structures can be formally considered either as intergrowths of perovskite modules and polysynthetically twinned modules of the Bi2Ti4O11 structure or as intergrowths of the 2D perovskite and 1D anatase fragments. Transmission electron microscopy (TEM) on Bi10Ti7Fe6O38 reveals that static atomic displacements of Bi and O inside the perovskite blocks are not completely random; they are cooperative, yet only short-range ordered. According to TEM, the interfaces can be laterally shifted with respect to each other over +/-1/3a, introducing an additional degree of disorder. Bi10Ti7Fe6O38 is paramagnetic in the 1.5-1000 K temperature range due to dilution of the magnetic Fe(3+) cations with nonmagnetic Ti(4+). The n = 3, 4 compounds demonstrate a high dielectric constant of 70-165 at room temperature.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 3
DOI: 10.1021/acs.inorgchem.5b02465
|
|
|
“Biaxially aligned titanium nitride thin films deposited by reactive unbalanced magnetron sputtering”. Mahieu S, Ghekiere P, de Winter G, de Gryse R, Depla D, Van Tendeloo G, Lebedev OI, Surface and coatings technology 200, 2764 (2006). http://doi.org/10.1016/j.surfcoat.2004.09.012
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.589
Times cited: 36
DOI: 10.1016/j.surfcoat.2004.09.012
|
|
|
“Biaxially aligned yttria stabilized zirconia and titanium nitride layers deposited by unbalanced magnetron sputtering”. Mahieu S, Ghekiere P, de Winter G, de Gryse R, Depla D, Lebedev OI, Diffusion and defect data : solid state data : part B : solid state phenomena
T2 –, 2nd International Conference on Texture and Anisotropy of Polycrystals, JUL 07-09, 2004, Metz, FRANCE 105, 447 (2005)
Abstract: Control of the texture and the biaxial alignment of sputter deposited films has provoked a great deal of interest due to its technological importance. indeed, many physical properties of thin films are influenced by the biaxial alignment. In this context, extensive research has been established to understand the growth mechanism of biaxially aligned Yttria Stabilized Zirconia (YSZ) as a buffer layer for high temperature superconducting copper oxides. In this work, the growth mechanism in general and the mechanism responsible of the biaxial alignment in detail were investigated for thin films of YSZ and TiN deposited by unbalanced magnetron sputtering using non-aligned polycrystalline stainless steel substrates. The mechanism responsible for the preferential out-of-plane alignment has been investigated by performing depositions on a non-tilted substrate. However, to study the in-plane alignment a tilted substrate was used. The microstructure of the deposited layers was characterised by Scanning Electron Microscopy (SEM) and Transmission Electron Microscopy (TEM). The crystallographic alignment has been investigated by X-ray diffraction (XRD) (angular scans and pole figures) and by Selective Area Diffraction (SAD). It was observed that the deposited layers show a zone T or zone II structure and the layers with a zone T structure consist of faceted grains. There seems to be a correlation between the crystal habit of these faceted grains and the measured biaxial alignment. A model for the preferential out-of-plane orientation, the in-plane alignment and the correlation between the microstructure and the biaxial alignment is proposed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
|
|
|
“Bifunctional nickel-nitrogen-doped-carbon-supported copper electrocatalyst for CO2 reduction”. Choukroun D, Daems N, Kenis T, Van Everbroeck T, Hereijgers J, Altantzis T, Bals S, Cool P, Breugelmans T, Journal Of Physical Chemistry C 124, 1369 (2020). http://doi.org/10.1021/ACS.JPCC.9B08931
Abstract: Bifunctionality is a key feature of many industrial catalysts, supported metal clusters and particles in particular, and the development of such catalysts for the CO2 reduction reaction (CO2RR) to hydrocarbons and alcohols is gaining traction in light of recent advancements in the field. Carbon-supported Cu nanoparticles are suitable candidates for integration in the state-of-the-art reaction interfaces, and here, we propose, synthesize, and evaluate a bifunctional Ni–N-doped-C-supported Cu electrocatalyst, in which the support possesses active sites for selective CO2 conversion to CO and Cu nanoparticles catalyze either the direct CO2 or CO reduction to hydrocarbons. In this work, we introduce the scientific rationale behind the concept, its applicability, and the challenges with regard to the catalyst. From the practical aspect, the deposition of Cu nanoparticles onto carbon black and Ni–N–C supports via an ammonia-driven deposition precipitation method is reported and explored in more detail using X-ray diffraction, thermogravimetric analysis, and hydrogen temperature-programmed reduction. High-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM) and energy-dispersive X-ray spectroscopy (EDXS) give further evidence of the presence of Cu-containing nanoparticles on the Ni–N–C supports while revealing an additional relationship between the nanoparticle’s composition and the electrode’s electrocatalytic performance. Compared to the benchmark carbon black-supported Cu catalysts, Ni–N–C-supported Cu delivers up to a 2-fold increase in the partial C2H4 current density at −1.05 VRHE (C1/C2 = 0.67) and a concomitant 10-fold increase of the CO partial current density. The enhanced ethylene production metrics, obtained by virtue of the higher intrinsic activity of the Ni–N–C support, point out toward a synergistic action between the two catalytic functionalities.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA); Applied Electrochemistry & Catalysis (ELCAT)
Impact Factor: 3.7
Times cited: 24
DOI: 10.1021/ACS.JPCC.9B08931
|
|
|
“Binary icosahedral clusters of hard spheres in spherical confinement”. Wang D, Dasgupta T, van der Wee EB, Zanaga D, Altantzis T, Wu Y, Coli GM, Murray CB, Bals S, Dijkstra M, van Blaaderen A, Nature Physics , 1 (2020). http://doi.org/10.1038/S41567-020-1003-9
Abstract: The influence of geometry on the local and global packing of particles is important to many fundamental and applied research themes, such as the structure and stability of liquids, crystals and glasses. Here we show by experiments and simulations that a binary mixture of hard-sphere-like nanoparticles crystallizing into a MgZn(2)Laves phase in bulk spontaneously forms icosahedral clusters in slowly drying droplets. Using advanced electron tomography, we are able to obtain the real-space coordinates of all the spheres in the icosahedral clusters of up to about 10,000 particles. The local structure of 70-80% of the particles became similar to that of the MgCu(2)Laves phase. These observations are important for photonic applications. In addition, we observed in simulations that the icosahedral clusters nucleated away from the spherical boundary, which is distinctly different from that of the single species clusters. Our findings open the way for particle-level studies of nucleation and growth of icosahedral clusters, and of binary crystallization. The authors investigate out-of-equilibrium crystallization of a binary mixture of sphere-like nanoparticles in small droplets. They observe the spontaneous formation of an icosahedral structure with stable MgCu(2)phases, which are promising for photonic applications.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Applied Electrochemistry & Catalysis (ELCAT)
Impact Factor: 19.6
Times cited: 38
DOI: 10.1038/S41567-020-1003-9
|
|
|
“Biocompatibility and corrosion behavior of the shape memory NiTi alloy in the physiological environments simulated with body fluids for medical applications”. Khalil-Allafi J, Amin-Ahmadi B, Zare M, Materials science and engineering: part C: biomimetic materials 30, 1112 (2010). http://doi.org/10.1016/j.msec.2010.06.007
Abstract: Due to unique properties of NiTi shape memory alloys such as high corrosion resistance, biocompatibility, super elasticity and shape memory behavior, NiTi shape memory alloys are suitable materials for medical applications. Although TiO2 passive layer in these alloys can prevent releasing of nickel to the environment, high nickel content and stability of passive layer in these alloys are very debatable subjects. In this study a NiTi shape memory alloy with nominal composition of 50.7 atom% Ni was investigated by corrosion tests. Electrochemical tests were performed in two physiological environments of Ringer solution and NaCl 0.9% solution. Results indicate that the breakdown potential of the NiTi alloy in NaCl 0.9% solution is higher than that in Ringer solution. The results of Scanning Electron Microscope (SEM) reveal that low pitting corrosion occurred in Ringer solution compared with NaCl solution at potentiostatic tests. The pH value of the solutions increases after the electrochemical tests. The existence of hydride products in the X-ray diffraction analysis confirms the decrease of the concentration of hydrogen ion in solutions. Topographical evaluations show that corrosion products are nearly same in all samples. The biocompatibility tests were performed by reaction of mouse fibroblast cells (L929). The growth and development of cells for different times were measured by numbering the cells or statistics investigations. The figures of cells for different times showed natural growth of cells. The different of the cell numbers between the test specimen and control specimen was negligible; therefore it may be concluded that the NiTi shape memory alloy is not toxic in the physiological environments simulated with body fluids.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.164
Times cited: 34
DOI: 10.1016/j.msec.2010.06.007
|
|
|
“Biocompatible Zr-based nanoscale MOFs coated with modified poly(epsilon-caprolactone) as anticancer drug carriers”. Filippousi M, Turner S, Leus K, Siafaka PI, Tseligka ED, Vandichel M, Nanaki SG, Vizirianakis IS, Bikiaris DN, Van Der Voort P, Van Tendeloo G, International journal of pharmaceutics 509, 208 (2016). http://doi.org/10.1016/j.ijpharm.2016.05.048
Abstract: Nanoscale Zr-based metal organic frameworks (MOFs) UiO-66 and UiO-67 were studied as potential anticancer drug delivery vehicles. Two model drugs were used, hydrophobic paclitaxel and hydrophilic cisplatin, and were adsorbed onto/into the nano MOFs (NMOFs). The drug loaded MOFs were further encapsulated inside a modified poly(epsilon-caprolactone) with d-alpha-tocopheryl polyethylene glycol succinate polymeric matrix, in the form of microparticles, in order to prepare sustained release formulations and to reduce the drug toxicity. The drugs physical state and release rate was studied at 37 degrees C using Simulated Body Fluid. It was found that the drug release depends on the interaction between the MOFs and the drugs while the controlled release rates can be attributed to the microencapsulated formulations. The in vitro antitumor activity was assessed using HSC-3 (human oral squamous carcinoma; head and neck) and U-87 MG (human glioblastoma grade IV; astrocytoma) cancer cells. Cytotoxicity studies for both cell lines showed that the polymer coated, drug loaded MOFs exhibited better anticancer activity compared to free paclitaxel and cisplatin solutions at different concentrations.
Keywords: A1 Journal article; Pharmacology. Therapy; Electron microscopy for materials research (EMAT)
Impact Factor: 3.649
Times cited: 37
DOI: 10.1016/j.ijpharm.2016.05.048
|
|
|
“Bioinspired noncyclic transfer pathway electron donors for unprecedented hydrogen production”. Liu J, Wang C, Yu W, Zhao H, Hu Z-Y, Liu F, Hasan T, Li Y, Van Tendeloo G, Li C, Su B-L, CCS chemistry 5, 1470 (2023). http://doi.org/10.31635/CCSCHEM.022.202202071
Abstract: Electron donors are widely exploited in visible-light photocatalytic hydrogen production. As a typical electron donor pair and often the first choice for hydrogen production, the sodium sulfide-sodium sulfite pair has been extensively used. However, the resultant thiosulfate ions consume the photogenerated electrons to form an undesirable pseudocyclic electron transfer pathway during the photocatalytic process, strongly limiting the solar energy conversion efficiency. Here, we report novel and bioinspired electron donor pairs offering a noncyclic electron transfer pathway that provides more electrons without the consumption of the photogenerated electrons. Compared to the state-of-the-art electron donor pair Na2S-Na2SO3, these novel Na2S-NaH2PO2 and Na2S-NaNO2 electron donor pairs enable an unprecedented enhancement of up to 370% and 140% for average photocatalytic H-2 production over commercial CdS nanoparticles, and they are versatile for a large series of photocatalysts for visible-light water splitting. The discovery of these novel electron donor pairs can lead to a revolution in photocatalysis and is of great significance for industrial visible-light-driven H-2 production. [GRAPHICS] .
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
DOI: 10.31635/CCSCHEM.022.202202071
|
|
|
“Bipolaron stability in an ellipsoidal potential well”. Pokatilov EP, Croitoru MD, Fomin VM, Devreese JT, Physica status solidi: B: basic research 237, 244 (2003). http://doi.org/10.1002/pssb.200301785
Keywords: A1 Journal article; Theory of quantum systems and complex systems; Condensed Matter Theory (CMT); Electron microscopy for materials research (EMAT)
Impact Factor: 1.674
Times cited: 7
DOI: 10.1002/pssb.200301785
|
|