Abstract: An extended set of 18th century glass vessels was analyzed by means of SEM-EDX (major and minor element composition) The fragmented archaeological objects were recovered from a latrine belonging to the early 18th century building phase of the nunnery of Clairefontaine, near Arlon (B). On the basis of typology and decoration, the major part of the vessels could be dated around the middle of the 18th century. Variety in color and weathering of the glass suggest differences in glassmaking recipes and in the composition and origin of raw materials. The results of the analysis show how two main compositional groups constitute about 90% of the analyzed glass set, and these are constituted by potash glass (transparent beakers) and high lime low alkali glass (green bottles). Next to these, a few potash-lime and soda glasses are also found. The type of alteration has also a clear relation with the original glass composition.

Abstract: The intensity distributions of the coherent and partially coherent x-rays passed through a poly-capillary lens have been computed at the focal plane. The computations showed that at the appropriate experimental conditions the interference phenomenon does affect the intensity distribution. In the case of the coherent input radiation with the photon energy of 0.1 keV, the interference fringes were observed, while the non-coherent x-ray radiation produced no interference-like intensity distributions.

Abstract: Historical glass, especially medieval glass, can undergo weathering under the influence of time and environmental conditions. The aim of this investigation was to better understand the processes involved in this natural degradation process by studying artificially altered glass samples prepared for the use of evaluation of conservation methods. Non-durable glass sensors produced by the Fraunhofer Institute (type M1.0) were used as a starting material for artificial alteration. These were immersed in acidic (pH = 0, 2, 4) and neutral solutions (1 h – 8 h). In a second stage the glass samples were immersed in a 0.5 M MnCl2 solution (24 h, 48 h and 72 h), allowing intrusion of Mn from the solution into the gel layer. The samples were characterized at different stages with reflectance FTIR spectroscopy, mu XRF mapping and mu XANES. All measurements were carried out at ESRF, beamline ID21. Reflectance FTIR spectroscopy measurements were performed in the 800 4000 cm(-1) range. Cluster analysis of the resulting maps evidenced the rapid growth of the gel layer in strong acidic conditions. The average spectra for each cluster feature show for the original glass a strong Si-O- stretching band between 900 and 1000 cm(-1), whereas the gel layer could be identified by the increasing Si-O-Si bands around 1100 and 1250 cm(-1). mu XRF maps were recorded at different stages of the experiment at energies around the Mn-K edge (6.539 keV) and with a step size of 2 by 2 m. These confirm the leaching of K+ and Ca+2 from the glass and the intrusion of Mn from the solution. Mn was found throughout the entire gel layer, but with a concentration gradient peaking at the surface. XANES point measurements were recorded at various points where Mn was present. No spatial variation was found, but linear combination fitting of the spectra with various Mn reference compounds indicated that Mn2+Mn23+O4 is the main Mn compound in the gel layer, as was hypothesised by Watkinson et al. The standard corroded glass samples studied here can be used for the evaluation of conservation treatments in follow-up experiments. (C) 2013 The Authors. Published by Elsevier B.V. Selection and peer-review under responsibility of the IA-CS (Italian Association of Conservation Scientists) and University of Antwerp

Abstract: The degradation of colors in historical paintings affects our cultural heritage in both museums and archeological sites. Despite intensive experimental studies, the origin of darkening of one of the most ancient pigments known to humankind, vermilion (α-HgS), remains unexplained. Here, by combining many-body theoretical spectroscopy and high-resolution microscopic x-ray diffraction, we clarify the composition of the damaged paint work and demonstrate possible physicochemical processes, induced by illumination and exposure to humidity and air, that cause photoactivation of the original pigment and the degradation of the secondary minerals. The results suggest a new path for the darkening process which was never considered by previous studies and prompt a critical examination of their findings.

Abstract: The painter, Vincent van Gogh, and some of his contemporaries frequently made use of the pigment chrome yellow that is known to show a tendency toward darkening. This pigment may correspond to various chemical compounds such as PbCrO4 and PbCr1-xSxO4, that may each be present in various crystallographic forms with different tendencies toward degradation. Investigations by X-ray diffraction (XRD), mid-Fourier Transform infrared (FTIR), and Raman instruments (benchtop and portable) and synchrotron radiation-based micro-XRD and X-ray absorption near edge structure spectroscopy performed on oil-paint models, prepared with in-house synthesized PbCrO4 and PbCr1-xSxO4, permitted us to characterize the spectroscopic features of the various forms. On the basis of these results, an extended study has been carried out on historic paint tubes and on embedded paint microsamples taken from yellow-orange/pale yellow areas of 12 Van Gogh paintings, demonstrating that Van Gogh effectively made use of different chrome yellow types. This conclusion was also confirmed by in situ mid-FTIR investigations on Van Goghs Portrait of Gauguin (Van Gogh Museum, Amsterdam).

Abstract: Stained glass windows incorporating dark blue and purple enamel paint layers are in some cases subject to severe degradation while others from the same period survived the ravages of time. A series of dark blue, greenblue and purple enamel glass paints from the same region (Northwestern Europe) and from the same period (16early 20th centuries) has been studied by means of a combination of microscopic X-ray fluorescence analysis, electron probe micro analysis and transmission electron microscopy with the aim of better understanding the causes of the degradation. The chemical composition of the enamels diverges from the average chemical composition of window glass. Some of the compositions appear to be unstable, for example those with a high concentration of K2O and a low content of CaO and PbO. In other cases, the deterioration of the paint layers was caused by the less than optimal vitrification of the enamel during the firing process. Recipes and chemical compositions indicate that glassmakers of the 1617th century had full control over the color of the enamel glass paints they made. They mainly used three types of coloring agents, based on Co (dark blue), Mn (purple) and Cu (light-blue or greenblue) as coloring elements. Bluepurple enamel paints were obtained by mixing two different coloring agents. The coloring agent for redpurple enamel, introduced during the 19th century, was colloidal gold embedded in grains of lead glass.

Abstract: We study an exciton in a type-II quantum dot, where the electron is confined in the dot, but the hole is located in the barrier material. The exciton properties are studied as a function of a perpendicular magnetic field using a Hartree-Fock mesh calculation. Our model system consists of a planar quantum disk. Angular momentum (l) transitions are predicted with increasing magnetic field. We, also study the transition from a type-I to a type-H quantum dot which is induced by changing the confinement potential of the hole. For sufficiently large magnetic fields a reentrant behavior is found from l(h) = 0 to l(h) not equal 0 and back to l(h) = 0, which results in a transition from type II to type I.