“Positive graphene by chemical design : tuning supramolecular strategies for functional surfaces”. Hadad C, Ke X, Carraro M, Sartorel A, Bittencourt C, Van Tendeloo G, Bonchio M, Quintana M, Prato M, Chemical communications 50, 885 (2014). http://doi.org/10.1039/c3cc47056c
Abstract: A diazonium based-arylation reaction was efficiently used for the covalent addition of 4-amino-N,N,N-trimethylbenzene ammonium to stable dispersions of few layer graphene (FLG) yielding an innovative FLG platform with positive charges to immobilize inorganic polyanions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.319
Times cited: 19
DOI: 10.1039/c3cc47056c
|
|
|
“Post-synthesis deposition of V-Zeolitic nanoparticles in SBA-15”. Meynen V, Beyers E, Cool P, Vansant EF, Mertens M, Weyten H, Lebedev OI, Van Tendeloo G, Chemical communications , 898 (2004). http://doi.org/10.1039/b400636d
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 6.319
Times cited: 22
DOI: 10.1039/b400636d
|
|
|
“Production of large graphene sheets by exfoliation of graphite under high power ultrasound in the presence of tiopronin”. Quintana M, Grzelczak M, Spyrou K, Kooi B, Bals S, Van Tendeloo G, Rudolf P, Prato M, Chemical communications 48, 12159 (2012). http://doi.org/10.1039/c2cc35298b
Abstract: Under ultrasonication, the production of high quality graphene layers by exfoliation of graphite was achieved via addition of tiopronin as an antioxidant.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.319
Times cited: 39
DOI: 10.1039/c2cc35298b
|
|
|
“A protecting group approach toward synthesis of Au-silica Janus nanostars”. Rodríguez-Fernández D, Altantzis T, Heidari H, Bals S, Liz-Marzan LM, Chemical communications 50, 79 (2014). http://doi.org/10.1039/c3cc47531j
Abstract: The concept of protecting groups, widely used in organic chemistry, has been applied for the synthesis of Au-silica Janus stars, in which gold branches protrude from one half of Au-silica Janus spheres. This configuration opens up new possibilities to apply the plasmonic properties of gold nanostars, as well as a variety of chemical functionalizations on the silica component.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.319
Times cited: 26
DOI: 10.1039/c3cc47531j
|
|
|
“Selective organic functionalization of graphene bulk or graphene edges”. Quintana M, Montellano A, Esau del Rio Castillo A, Van Tendeloo G, Bittencourt C, Prato M, Chemical communications 47, 9330 (2011). http://doi.org/10.1039/c1cc13254g
Abstract: Graphene sheets have been functionalized with a PAMAM dendron, finding that graphene can be efficiently functionalized all over the surface, or only at the edges, depending on the reactions used in the functionalization process.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.319
Times cited: 84
DOI: 10.1039/c1cc13254g
|
|
|
“Synthesis of highly stable pure-silica thin-walled hexagonally ordered mesoporous material”. Verlooy P, Aerts A, Lebedev OI, Van Tendeloo G, Kirschhock C, Martens JA, Chemical communications , 4287 (2009). http://doi.org/10.1039/b901796h
Abstract: Hexagonally ordered mesoporous silica with a very narrow mesopore size distribution and exceptionally high stability paired with unusually thin pore walls was prepared using piperidine and cetyltrimethylammonium bromide.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.319
Times cited: 17
DOI: 10.1039/b901796h
|
|
|
“Synthesis of single wall carbon nanotubes by catalytic decomposition of hydrocarbons”. Colomer J-F, Bister G, Willems I, Konya Z, Fonseca A, Van Tendeloo G, Nagy JB, Chemical communications , 1343 (1999). http://doi.org/10.1039/a903142a
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.319
Times cited: 110
DOI: 10.1039/a903142a
|
|
|
“Janus Gold Nanoparticles Obtained via Spontaneous Binary Polymer Shell Segregation”. Percebom AMM, Giner-casares JJ, Claes N, Bals S, Loh W, Liz-Marzan LM, Chemical communications 52, 4278 (2016). http://doi.org/10.1039/C5CC10454H
Abstract: Janus gold nanoparticles are of high interest because they allow directed self-assembly and display plasmonic properties. We succeeded in coating gold nanoparticles with two different polymers that form a Janus shell. The spontaneous segregation of two immiscible polymers at the surface of the nanoparticles was verified by NOESY NMR and most importantly by electron microscopy analysis in two and three dimensions. The Janus structure is additionally shown to affect the aggregation behavior of the nanoparticles.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.319
Times cited: 44
DOI: 10.1039/C5CC10454H
|
|
|
“High viscosity to highly dispersed PtPd bimetallic nanocrystals for enhanced catalytic activity and stability”. Ying J, Hu Z-Y, Yang X-Y, Wei H, Xiao Y-X, Janiak C, Mu S-C, Tian G, Pan M, Van Tendeloo G, Su B-L, Chemical communications 52, 8219 (2016). http://doi.org/10.1039/c6cc00912c
Abstract: A facile high-viscosity-solvent method is presented to synthesize PtPd bimetallic nanocrystals highly dispersed in different mesostructures (2D and 3D structures), porosities (large and small pore sizes), and compositions (silica and carbon). Further, highly catalytic activity, stability and durability of the nanometals have been proven in different catalytic reactions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.319
Times cited: 19
DOI: 10.1039/c6cc00912c
|
|
|
“Polydopamine nanocoated whole-cell asymmetric biocatalysts”. Wang L, Hu Z-Y, Yang X-Y, Zhang B-B, Geng W, Van Tendeloo G, Su B-L, Chemical communications 53, 6617 (2017). http://doi.org/10.1039/C7CC01283G
Abstract: Our whole-cell biocatalyst with a polydopamine nanocoating shows high catalytic activity (5 times better productivity than the native cell) and reusability (84% of the initial yield after 5 batches, 8 times higher than the native cell) in asymmetric reduction. It also integrates with titania, silica, and magnetic nanoparticles for multi-functionalization.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.319
Times cited: 15
DOI: 10.1039/C7CC01283G
|
|
|
“Disentangling the effect of seed size and crystal habit on gold nanoparticle seeded growth”. González-Rubio G, de Oliveira TM, Altantzis T, La Porta A, Guerrero-Martínez A, Bals S, Scarabelli L, Liz-Marzán LM, Chemical communications 53, 11360 (2017). http://doi.org/10.1039/C7CC06854A
Abstract: Oxidative etching was used to produce gold seeds of different sizes and crystal habits. Following detailed characterization, the seeds were grown under different conditions. Our results bring new insights toward understanding the effect of size and crystallinity on the growth of anisotropic particles, whilst identifying guidelines for the optimisation of new synthetic protocols of predesigned seeds.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.319
Times cited: 29
DOI: 10.1039/C7CC06854A
|
|
|
“The design of magneto-plasmonic nanostructures formed by magnetic Prussian Blue-type nanocrystals decorated with Au nanoparticles”. Sanchis-Gual R, Susic I, Torres-Cavanillas R, Arenas-Esteban D, Bals S, Mallah T, Coronado-Puchau M, Coronado E, Chemical Communications 57, 1903 (2021). http://doi.org/10.1039/D0CC08034A
Abstract: We have developed a general protocol for the preparation of hybrid nanostructures formed by nanoparticles (NPs) of molecule-based magnets based on Prussian Blue Analogues (PBAs) decorated with plasmonic Au NPs of different shapes. By adjusting the pH, Au NPs can be attached preferentially along the edges of the PBA or randomly on the surface. The protocol allows tuning the plasmonic properties of the hybrids in the whole visible spectrum.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.319
Times cited: 5
DOI: 10.1039/D0CC08034A
|
|
|
“Optical encoding of luminescent carbon nanodots in confined spaces”. Bartholomeeusen E, De Cremer G, Kennes K, Hammond C, Hermans I, Lu J-B, Schryvers D, Jacobs PA, Roeffaers MBJ, Hofkens J, Sels BF, Coutino-Gonzalez E, Chemical Communications 57, 11952 (2021). http://doi.org/10.1039/D1CC04777A
Abstract: Stable emissive carbon nanodots were generated in zeolite crystals using near infrared photon irradiation gradually converting the occluded organic template, originally used to synthesize the zeolite crystals, into discrete luminescent species consisting of nano-sized carbogenic fluorophores, as ascertained using Raman microscopy, and steady-state and time-resolved spectroscopic techniques. Photoactivation in a confocal laser fluorescence microscope allows 3D resolved writing of luminescent carbon nanodot patterns inside zeolites providing a cost-effective and non-toxic alternative to previously reported metal-based nanoclusters confined in zeolites, and opens up opportunities in bio-labelling and sensing applications.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.319
DOI: 10.1039/D1CC04777A
|
|
|
“Hierarchical zeolites containing embedded Cd0.2Zn0.8S as a photocatalyst for hydrogen production from seawater”. Yuan Y, Wu F-J, Xiao S-T, Wang Y-T, Yin Z-W, Van Tendeloo G, Chang G-G, Tian G, Hu Z-Y, Wu S-M, Yang X-Y, Chemical communications 59, 7275 (2023). http://doi.org/10.1039/D3CC01409F
Abstract: Uncovering an efficient and stable photocatalytic system for seawater splitting is a highly desirable but challenging goal. Herein, Cd0.2Zn0.8S@Silicalite-1 (CZS@S-1) composites, in which CZS is embedded in the hierarchical zeolite S-1, were prepared and show remarkably high activity, stability and salt resistance in seawater.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.9
DOI: 10.1039/D3CC01409F
|
|
|
“Photocatalytic process optimisation for ethylene oxidation”. Tytgat T, Hauchecorne B, Abakumov AM, Smits M, Verbruggen SW, Lenaerts S, Chemical engineering journal 209, 494 (2012). http://doi.org/10.1016/j.cej.2012.08.032
Abstract: When studying photocatalysis it is important to consider, beside the chemical approach, the engineering part related to process optimisation. To achieve this a fixed bed photocatalytic set-up consisting of different catalyst placings, in order to vary catalyst distribution, is studied. The use of a fixed quantity of catalyst placed packed or randomly distributed in the reactor, results in an almost double degradation for the distributed catalyst. Applying this knowledge leads to an improved performance with limited use of catalyst. A reactor only half filled with catalyst leads to higher degradation performance compared to a completely filled reactor. Taking into account this simple process optimisation by better distributing the catalyst a more sustainable photocatalytic air purification process is achieved. (C) 2012 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Sustainable Energy, Air and Water Technology (DuEL)
Impact Factor: 6.216
Times cited: 12
DOI: 10.1016/j.cej.2012.08.032
|
|
|
“Smart heating profiles for the synthesis of benzene bridged periodic mesoporous organosilicas”. Smeulders G, van Oers C, Van Havenbergh K, Houthoofd K, Mertens M, Martens JA, Bals S, Maes BUW, Meynen V, Cool P, Chemical engineering journal 175, 585 (2011). http://doi.org/10.1016/j.cej.2011.09.116
Abstract: In this study the effects of the heating rate and heating time on the formation of crystal-like benzene bridged periodic mesoporous organosilicas (PMOs) are investigated. The time needed to heat up an autoclave during the hydrothermal treatment has shown to be crucial in the synthesis of PMOs, while the total duration of heating gave rise to only minor differences. By choosing a smart heating profile, superior PMO materials can be obtained in a short time. Different heating profiles in a range from one minute to one hour are adopted by microwave equipment and compared with conventional heating methods. The heating rate has a large influence on the porosity characteristics and the uniformity of the obtained particles. Moreover, two new alternative synthetic strategies to adopt the smart heating profile are presented, in order to give some possible solutions for the expensive microwave equipment.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA); Organic synthesis (ORSY)
Impact Factor: 6.216
Times cited: 7
DOI: 10.1016/j.cej.2011.09.116
|
|
|
“Gas phase photocatalytic spiral reactor for fast and efficient pollutant degradation”. Blommaerts N, Asapu R, Claes N, Bals S, Lenaerts S, Verbruggen SW, Chemical engineering journal 316, 850 (2017). http://doi.org/10.1016/j.cej.2017.02.038
Abstract: Photocatalytic reactors for the degradation of gaseous organic pollutants often suffer from major limitations such as small reaction area, sub-optimal irradiation conditions and thus limited reaction rate. In this work, an alternative solution is presented that involves a glass tube coated on the inside with (silvermodified) TiO2 and spiraled around a UVA lamp. First, the spiral reactor is coated from the inside with TiO2 using an experimentally verified procedure that is optimized toward UV light transmission. This procedure is kept as simple as possible and involves a single casting step of a 1 wt% suspension of TiO2 in ethanol through the spiral. This results in a coated tube that absorbs nearly all incident UV light under the experimental conditions used. The optimized coated spiral reactor is then benchmarked to a conventional annular photoreactor of the same outer dimensions and total catalyst loading over a broad range of experimental conditions. Although residence time distribution experiments indicate slightly longer dwelling of molecules in the spiral reactor, no significant difference in by-passing of gas between the spiral reactor and the annular reactor can be claimed. Acetaldehyde degradation efficiency of 100% is obtained with the spiral reactor for a residence time as low as 60 s, whereas the annular reactor could not achieve full degradation even at 1000 s residence time. In a final case study, addition of long-term stable silver nanoparticles, protected by an ultra-thin polymer shell applied via the layer-by-layer (LbL) method, to the spiral reactor coating is shown to double the degradation efficiency and provides an interesting strategy to cope with higher pollutant concentrations without changing the overall dimensions.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Sustainable Energy, Air and Water Technology (DuEL)
Impact Factor: 6.216
Times cited: 30
DOI: 10.1016/j.cej.2017.02.038
|
|
|
“Simultaneous creation of metal nanoparticles in metal organic frameworks via spray drying technique”. Gholampour N, Chaemchuen S, Hu Z-Y, Mousavi B, Van Tendeloo G, Verpoort F, Chemical engineering journal 322, 702 (2017). http://doi.org/10.1016/J.CEJ.2017.04.085
Abstract: In-situ fabrication of palladium(0) nanoparticles inside zeolitic imidazolate frameworks (ZIF-8) has been established via one-step facile spray-dry technique. Crystal structures and morphologies of the Pd@ZIF-8 samples are investigated by powder XRD, TEM, SAED, STEM, and EDX techniques. High angle annular dark field scanning transmission electron microscopy (HAAD-STEM) and 3D tomographic analysis confirm the presence of palladium nanoparticles inside the ZIF-8 structure. The porosity, surface area and N-2 physisorption properties are evaluated for Pd@ZIF-8 with various palladium contents. Furthermore, Pd@ZIF-8 samples are effectively applied as heterogeneous catalysts in alkenes hydrogenation. This straightforward method is able to speed up the synthesis of encapsulation of metal nanoparticles in metal organic frameworks. (C) 2017 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.216
Times cited: 14
DOI: 10.1016/J.CEJ.2017.04.085
|
|
|
“Tuning the turnover frequency and selectivity of photocatalytic CO2 reduction to CO and methane using platinum and palladium nanoparticles on Ti-Beta zeolites”. Blommaerts N, Hoeven N, Arenas Esteban D, Campos R, Mertens M, Borah R, Glisenti A, De Wael K, Bals S, Lenaerts S, Verbruggen SW, Cool P, Chemical Engineering Journal 410, 128234 (2021). http://doi.org/10.1016/j.cej.2020.128234
Abstract: A Ti-Beta zeolite was used in gas phase photocatalytic CO2 reduction to reduce the charge recombination rate and increase the surface area compared to P25 as commercial benchmark, reaching 607 m2 g-1. By adding Pt nanoparticles, the selectivity can be tuned toward CO, reaching a value of 92% and a turnover frequency (TOF) of 96 µmol.gcat-1.h-1, nearly an order of magnitude higher in comparison with P25. By adding Pd nanoparticles the selectivity can be shifted from CO (70% for a bare Ti-Beta zeolite), toward CH4 as the prevalent species (60%). In this way, the selectivity toward CO or CH4 can be tuned by either using Pt or Pd. The TOF values obtained in this work outperform reported state-of-the-art values in similar research. The improved activity by adding the nanoparticles was attributed to an improved charge separation efficiency, together with a plasmonic contribution of the metal nanoparticles under the applied experimental conditions.
Keywords: A1 Journal article; Engineering sciences. Technology; Sustainable Energy, Air and Water Technology (DuEL); Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA); AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 6.216
Times cited: 15
DOI: 10.1016/j.cej.2020.128234
|
|
|
“The structure of different phases of pure C70 crystals”. Verheijen MA, Meekes H, Meijer G, Bennema P, de Boer JL, van Smaalen S, Van Tendeloo G, Amelinckx S, Muto S, van Landuyt J, Chemical physics 166, 287 (1992). http://doi.org/10.1016/0301-0104(92)87026-6
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.652
Times cited: 168
DOI: 10.1016/0301-0104(92)87026-6
|
|
|
“Bulk production of multi-wall carbon nanotube bundles on sol-gel prepared catalyst”. Ning Y, Zhang X, Wang Y, Sun Y, Shen L, Yang X, Van Tendeloo G, Chemical physics letters 366, 555 (2002). http://doi.org/10.1016/S0009-2614(02)01647-0
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.815
Times cited: 41
DOI: 10.1016/S0009-2614(02)01647-0
|
|
|
“Characterization of single-wall carbon nanotubes produced by CCVD method”. Colomer J-F, Benoit J-M, Stephan C, Lefrant S, Van Tendeloo G, Nagy JB, Chemical physics letters 345, 11 (2001). http://doi.org/10.1016/S0009-2614(01)00841-7
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.815
Times cited: 45
DOI: 10.1016/S0009-2614(01)00841-7
|
|
|
“Control of the outer diameter of thin carbon nanotubes synthesized by catalytic decomposition of hydrocarbons”. Willems I, Konya Z, Colomer JF, Van Tendeloo G, Nagaraju N, Fonseca A, Nagy JB, Chemical physics letters 317, 71 (2000). http://doi.org/10.1016/S0009-2614(99)01300-7
Abstract: Multi-wall carbon nanotubes have been produced by the catalytic decomposition of acetylene. Go-Mo, Co-V and Co-Fe mixtures supported either on zeolite or corundum alumina were used as catalysts. When Fe or V is added to Co, the carbon deposit increases. The nanotubes were characterized by both low and high resolution TEM. From histograms representing the outer diameter distributions, it is clear that the outer diameter of the nanotubes can be controlled by choosing the appropriate catalyst. (C) 2000 Elsevier Science B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.815
Times cited: 130
DOI: 10.1016/S0009-2614(99)01300-7
|
|
|
“Controlling the diameters in large-scale synthesis of single-walled carbon nanotubes by catalytic decomposition of CH4”. Li Y, Zhang X, Shen L, Luo J, Tao X, Liu F, Xu G, Wang Y, Geise HJ, Van Tendeloo G, Chemical physics letters 398, 276 (2004). http://doi.org/10.1016/j.cplett.2004.09.068
Abstract: High-quality single-walled carbon nanotubes (SWNTs) are synthesized in gram amount on Fe-Mo/MgO catalysts by catalytic decomposition of CH4 in H-2 or N-2. Raman data reveal that the as-prepared SATNTs have a diameter of about 0.74-1.29 nm. It is found that the diameter of the as-prepared SWNTs can be controlled mainly by adjusting the molar ratio of Fe-Mo versus the MgO support. Several other factors that potentially influence the growth of SWNTs have been studied in detail. The experimental results show that the nature of the catalyst determines the diameter of the as-prepared SWNTs. (C) 2004 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.815
Times cited: 45
DOI: 10.1016/j.cplett.2004.09.068
|
|
|
“Decorating carbon nanotubes with nickel nanoparticles”. Bittencourt C, Felten A, Ghijsen J, Pireaux J-J, Drube W, Erni R, Van Tendeloo G, Chemical physics letters 436, 368 (2007). http://doi.org/10.1016/j.cplett.2007.01.065
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.815
Times cited: 78
DOI: 10.1016/j.cplett.2007.01.065
|
|
|
“Geometry and electronic structure of porphyrines and porphyrazines”. Lamoen D, Parrinello M, Chemical Physics Letters 248, 309 (1996)
Keywords: A1 Journal article; Electron Microscopy for Materials Science (EMAT);
Impact Factor: 1.897
Times cited: 46
|
|
|
“Large-scale synthesis of single-wall carbon nanotubes by catalytic chemical vapor deposition (CCVD) method”. Colomer JF, Stephan C, Lefrant S, Van Tendeloo G, Willems I, Konya Z, Fonseca A, Laurent C, Nagy JB, Chemical physics letters 317, 83 (2000). http://doi.org/10.1016/S0009-2614(99)01338-X
Abstract: The large-scale production of single-wall carbon nanotubes (SWNTs) is reported. Large quantities of SWNTs can be synthesised by catalytic decomposition of methane over well-dispersed metal particles supported on MgO at 1000 degrees C. The thus produced SWNTs can be separated easily from the support by a simple acidic treatment to obtain a product with high yields (70-80%) of SWNTs. Because the typical synthesis time is 10 min, 1 g of SWNTs can be synthesised per day by this method. The SWNTs are characterized by high-resolution transmission electron microscopy and by Raman spectroscopy, showing the quality and the quantity of products. (C) 2000 Elsevier Science B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.815
Times cited: 344
DOI: 10.1016/S0009-2614(99)01338-X
|
|
|
“NEXAFS spectromicroscopy of suspended carbon nanohorns”. Bittencourt C, Ke X, Van Tendeloo G, Tagmatarchis N, Guttmann P, Chemical physics letters 587, 85 (2013). http://doi.org/10.1016/j.cplett.2013.09.034
Abstract: We demonstrate that near-edge X-ray-absorption fine-structure spectroscopy combined with full-field transmission X-ray microscopy can be used to study the electronic structure of suspended carbon nanohorns. Based on reports of electronic structure calculations additional spectral features observed in the π region of the NEXAFS spectrum recorded on the carbon nanohorns were associated to the presence of the pentagonal rings and the folding of the graphene sheet.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.815
Times cited: 4
DOI: 10.1016/j.cplett.2013.09.034
|
|
|
“Platinum and palladium on carbon nanotubes : experimental and theoretical studies”. Adjizian JJ, De Marco P, Suarez-Martinez I, El Mel AA, Snyders R, Gengler RYN, Rudolf P, Ke X, Van Tendeloo G, Bittencourt C, Ewels CP;, Chemical physics letters 571, 44 (2013). http://doi.org/10.1016/j.cplett.2013.03.079
Abstract: Pristine and oxygen plasma functionalised carbon nanotubes (CNTs) were studied after the evaporation of Pt and Pd atoms. High resolution transmission electron microscopy shows the formation of metal nanoparticles at the CNT surface. Oxygen functional groups grafted by the plasma functionalization act as nucleation sites for metal nanoparticles. Analysis of the C1s core level spectra reveals that there is no covalent bonding between the Pt or Pd atoms and the CNT surface. Unlike other transition metals such as titanium and copper, neither Pd nor Pt show strong oxygen interaction or surface oxygen scavenging behaviour.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.815
Times cited: 23
DOI: 10.1016/j.cplett.2013.03.079
|
|
|
“Platinumcarbon nanotube interaction”. Bittencourt C, Hecq M, Felten A, Pireaux JJ, Ghijsen J, Felicissimo MP, Rudolf P, Drube W, Ke X, Van Tendeloo G, Chemical physics letters 462, 260 (2008). http://doi.org/10.1016/j.cplett.2008.07.082
Abstract: The interaction between evaporated Pt and pristine or oxygen-plasma-treated multiwall carbon nanotubes (CNTs) is investigated. Pt is found to nucleate at defect sites, whether initially present or introduced by oxygen plasma treatment. The plasma treatment induces a uniform dispersion of Pt nanoparticles at the CNT surface. The absence of additional features in the C 1s core level spectrum indicates that no mixed PtC phase is formed. The formation of COPt bonds at the cluster-CNT interface is suggested to reduce the electronic interaction between Pt nanoparticles and the CNT surface.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.815
Times cited: 62
DOI: 10.1016/j.cplett.2008.07.082
|
|