Abstract: This work reports the first systematic chemical characterization of Portuguese 18th century glassware. 28 selected glass fragments, recovered from an archaeological excavation carried out in the site where King D. João V of Portugal established an important glass manufacture, Real Fábrica de Vidros de Coina (Coina Royal Glass Factory), were studied. This factory operated from 1719 until 1747, the year in which the factory was transferred to Marinha Grande. The fragments were analysed by micro-energy dispersive X-ray fluorescence (micro-EDXRF), using a portable spectrometer ArtTAX, and scanning electron microscopy (SEM-EDX). The analytical data showed that a large variety of glass types was manufactured in that factory, namely soda-lime glass, mixed-alkali glass, high lime-low alkali glass, potash glass and lead glass. In general, the composition of the glass varies according to the function of the objects. It was demonstrated that micro-EDXRF can be an important tool to characterize museum glass objects when only in situ non-invasive analytical methods are allowed.

Abstract: The spontaneous chemical alteration of artists' pigment materials may be caused by several degradation processes. Some of these are well known while others are still in need of more detailed investigation and documentation. These changes often become apparent as color modifications, either caused by a change in the oxidation state in the original material or the formation of degradation products or salts, via simple or more complex, multistep reactions. Arsenic-based pigments such as orpiment (As2S3) or realgar (alpha-As4S4) are prone to such alterations and are often described as easily oxidizing upon exposure to light. Macroscopic X-ray powder diffraction (MA-XRPD) imaging on a sub area of a still life painting by the 17th century Dutch painter Martinus Nellius was employed in combination with microscopic (mu-) XRPD imaging of a paint cross section taken in the area imaged by MA-XRPD. In this way, the in situ formation of secondary metal arsenate and sulfate species and their migration through the paint layer stack they originate from could be visualized. In the areas originally painted with orpiment, it could be shown that several secondary minerals such as schultenite (PbHAsO4), mimetite (Pb-5(AsO4)(3)Cl), palmierite (K2Pb(SO4)(2)) and syngenite (K2Ca(SO4)(2)center dot H2O) have formed. Closer inspection of the cross-sectioned paint layer stack with mu-XRPD illustrates that the arsenate minerals schultenite and mimetite have precipitated at the interface between the orpiment layer and the layer below that is rich in lead white, i.e. close to the depth of formation of the arsenate ions. The sulfate palmierite has mostly precipitated at the surface and upper layers of the painting.

Abstract: An extended set of 18th century glass vessels was analyzed by means of SEM-EDX (major and minor element composition) The fragmented archaeological objects were recovered from a latrine belonging to the early 18th century building phase of the nunnery of Clairefontaine, near Arlon (B). On the basis of typology and decoration, the major part of the vessels could be dated around the middle of the 18th century. Variety in color and weathering of the glass suggest differences in glassmaking recipes and in the composition and origin of raw materials. The results of the analysis show how two main compositional groups constitute about 90% of the analyzed glass set, and these are constituted by potash glass (transparent beakers) and high lime low alkali glass (green bottles). Next to these, a few potash-lime and soda glasses are also found. The type of alteration has also a clear relation with the original glass composition.