Abstract: ITEM specimens of a LaAlO3/SrTiO3 multilayer are prepared by FIB with internal lift out. Using a Ga+1 beam of 5 kV, a final cleaning step yielding top, top-angle, side, and bottom-angle cleaning is performed. Different cleaning procedures, which can be easily implemented in a dual beam FIB system, are described and compared; all cleaning types produce thin lamellae, useful for HRTEM and HAADF-STEM work up to atomic resolution. However, the top cleaned lamellae are strongly affected by the curtain effect. Top-angle cleaned specimens show an amorphous layer of around 5 nm at the specimen surfaces, due to damage and redeposition. Furthermore, it is observed that the LaAlO3 layers are preferentially destroyed and transformed into amorphous material, during the thinning process.

Abstract: The properties of the shape memory behaviour of Ni-rich binary NiTi are strongly dependant on the thermal history of the material. In this respect the changing of transformation temperatures of the underlying martensitic transformation and the occurrence of multiple step transformations are the most important phenomena. Part of the explanation is found in the presence of Ni4Ti3 precipitates in the B2 matrix after particular heat treatments. The formation of these precipitates changes the Ni concentration of the matrix and induces a strain field, with both of these aspects expected to be of importance. In this work atomic resolution and analytical TEM (transmission electron microscopy) techniques are used to obtain quantitative information concerning these two main features. Furthermore, the known structure of Ni4Ti3 is refined by a least squares optimization of quantitative electron diffraction data. The high-resolution TEM results show that there are strains up to 2% in the matrix surrounding the precipitates and they gradually increase until a maximum is reached when moving away from the interface. Analytical results reveal a global decrease of Ni content in the matrix when sufficient precipitates are present and a gradient in their close vicinity. The refinement of the structure shows atomic displacements, thereby increasing our understanding of the shrinking of the precipitate lattice with respect to the matrix.

Abstract: Lattice deformations and concentration gradients surrounding Ni4Ti3 precipitates grown by appropriate annealing in a Ni51Ti49 B2 austenite matrix are determined by a combination of TEM techniques. Quantitative Fourier analysis of HRTEM images reveals a deformed nanoscale region with lattice deformations up to 2% while EELS and EDX indicate a Ni depleted zone up to 150 nm away from the matrix-precipitate interface.

Abstract: Electron energy loss spectroscopy was used to investigate the bonding of plasma deposited carbon films. The experimental conditions include the use of a specific collection angle for which the shape of the spectra is free of the orientation dependency usually encountered in graphite due to its anisotropic structure. The first quantification process of the energy loss near-edge structure was performed by a standard fit of the collected spectrum, corrected for background and multiple scattering, with three Gaussian functions followed by a comparison with the graphite spectrum obtained under equivalent experimental conditions. In a second approach a fitting model directly incorporating the background subtraction and multiple scattering removal was applied. The final numerical results are interpreted in view of the deposition conditions of the films and the actual fitting procedure with the related choice of parameters.