Abstract |
ITEM specimens of a LaAlO3/SrTiO3 multilayer are prepared by FIB with internal lift out. Using a Ga+1 beam of 5 kV, a final cleaning step yielding top, top-angle, side, and bottom-angle cleaning is performed. Different cleaning procedures, which can be easily implemented in a dual beam FIB system, are described and compared; all cleaning types produce thin lamellae, useful for HRTEM and HAADF-STEM work up to atomic resolution. However, the top cleaned lamellae are strongly affected by the curtain effect. Top-angle cleaned specimens show an amorphous layer of around 5 nm at the specimen surfaces, due to damage and redeposition. Furthermore, it is observed that the LaAlO3 layers are preferentially destroyed and transformed into amorphous material, during the thinning process. |
|