“Influence of defect distribution on the reducibility of CeO2-x nanoparticles”. Spadaro MC, Luches P, Bertoni G, Grillo V, Turner S, Van Tendeloo G, Valeri S, D'Addato S, Nanotechnology 27, 425705 (2016). http://doi.org/10.1088/0957-4484/27/42/425705
Abstract: Ceria nanoparticles (NPs) are fundamental in heterogeneous catalysis because of their ability to store or release oxygen depending on the ambient conditions. Their oxygen storage capacity is strictly related to the exposed planes, crystallinity, density and distribution of defects. In this work a study of ceria NPs produced with a ligand-free, physical synthesis method is presented. The NP films were grown by a magnetron sputtering based gas aggregation source and studied by high resolution- and scanning-transmission electron microscopy and x-ray photoelectron spectroscopy. In particular, the influence of the oxidation procedure on the NP reducibility has been investigated. The different reducibility has been correlated to the exposed planes, crystallinity and density and distribution of structural defects. The results obtained in this work represent a basis to obtain cerium oxide NP with desired oxygen transport properties.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.44
Times cited: 11
DOI: 10.1088/0957-4484/27/42/425705
|
|
|
“Combined macroscopic, nanoscopic, and atomic-scale characterization of gold-ruthenium bimetallic catalysts for octanol oxidation”. Chinchilla LE, Olmos C, Kurttepeli M, Bals S, Van Tendeloo G, Villa A, Prati L, Blanco G, Calvino JJ, Chen X, Hungría AB, Particle and particle systems characterization 33, 419 (2016). http://doi.org/10.1002/ppsc.201600057
Abstract: A series of gold-ruthenium bimetallic catalysts of increasing Au:Ru molar ratios supported on a Ce0.62Zr0.38O2 mixed oxide are prepared and their structural and chemical features characterized by a combination of macroscopic and atomic-scale techniques based on scanning transmission electron microscopy. The influence of the temperature of the final reduction treatment used as activation step (350-700 degrees C range) is also investigated. The preparation method used allows catalysts to be successfully prepared where a major fraction of the metal nanoparticles is in the size range below 5 nm. The structural complexities characteristic of this type of catalysts are evidenced, as well as the capabilities and limitations of both the macroscopic and microscopic techniques in the characterization of the system of metal nanoparticles. A positive influence of the addition of Ru on both the resistance against sintering and the catalytic performance of the starting supported Au catalyst is evidenced.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.474
Times cited: 7
DOI: 10.1002/ppsc.201600057
|
|
|
“Deactivation study of Fe2O3-CeO2 during redox cycles for CO production from CO2”. Dharanipragada NVRA, Meledina M, Galvita VV, Poelman H, Turner S, Van Tendeloo G, Detavernier C, Marin GB, Industrial and engineering chemistry research 55, 5911 (2016). http://doi.org/10.1021/acs.iecr.6b00963
Abstract: Deactivation was investigated in Fe2O3-CeO2 oxygen storage materials during repeated H-2-reduction and CO2-reoxidation. In situ XRD, XAS, and TEM were used to identify phases, crystallite sizes, and morphological changes upon cycling operation. The effect of redox cycling was investigated both in Fe-rich (80 wt % Fe2O3-CeO2) and Ce-rich (10 wt %Fe2O3-CeO2) materials. The former consisted of 100 nm Fe2O3 particles decorated with 5-10 nm Ce1-xFexO2-x. The latter presented CeO2 with incorporated Fe, i.e. a solid solution of Ce1-xFexO2-x, as the main oxygen carrier. By modeling the EXAFS Ce-K signal for as-prepared 10 wt %Fe2O3-CeO2, the amount of Fe in CeO2 was determined as 21 mol %, corresponding to 86% of the total iron content. Sintering and solid solid transformations, the latter including both new phase formation and element segregation, were identified as deactivation pathways upon redox cycling. In Ce-rich material, perovskite (CeFeO3) was identified by XRD. This phase remained inert during reduction and reoxidation, resulting in an overall lower oxygen storage capacity. Further, Fe segregated from the solid solution, thereby decreasing its reducibility. In addition, an increase in crystallite size occurred for all phases. In Fe-rich material, sintering is the main deactivation pathway, although Fe segregation from the solid solution and perovskite formation cannot be excluded.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.843
Times cited: 26
DOI: 10.1021/acs.iecr.6b00963
|
|
|
“Hollow Zn/Co Zeolitic Imidazolate Framework (ZIF) and Yolk-Shell Metal@Zn/Co ZIF nanostructures”. Roesler C, Aijaz A, Turner S, Filippousi M, Shahabi A, Xia W, Van Tendeloo G, Muhler M, Fischer RA, Chemistry: a European journal 22, 3304 (2016). http://doi.org/10.1002/chem.201503619
Abstract: Metal-organic frameworks (MOFs) feature a great possibility for a broad spectrum of applications. Hollow MOF structures with tunable porosity and multifunctionality at the nanoscale with beneficial properties are desired as hosts for catalytically active species. Herein, we demonstrate the formation of well-defined hollow Zn/Co-based zeolitic imidazolate frameworks (ZIFs) by use of epitaxial growth of Zn-MOF (ZIF-8) on preformed Co-MOF (ZIF-67) nanocrystals that involve in situ self-sacrifice/excavation of the Co-MOF. Moreover, any type of metal nanoparticles can be accommodated in Zn/Co-ZIF shells to generate yolk-shell metal@ZIF structures. Transmission electron microscopy and tomography studies revealed the inclusion of these nanoparticles within hollow Zn/Co-ZIF with dominance of the Zn-MOF as shell. Our findings lead to a generalization of such hollow systems that are working effectively to other types of ZIFs.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.317
Times cited: 43
DOI: 10.1002/chem.201503619
|
|
|
“Texturing of hydrothermally synthesized BaTiO3 in a strong magnetic field by slip casting”. Özen M, Mertens M, Snijkers F, Van Tendeloo G, Cool P, Ceramics international 42, 5382 (2016). http://doi.org/10.1016/j.ceramint.2015.12.073
Abstract: Barium titanate powder was processed by slip casting in a rotating strong magnetic field of 9.4 T. The orientation factor of the sintered compact was analyzed by the X-ray diffraction technique and the microstructure (grain-size) was analyzed by scanning electron microscope. The hydrothermally prepared barium titanate was used as matrix material and the molten-salt synthesized barium titanate, with a larger particle-size, was used as template for the templated grain-growth process. Addition of large template particles was observed to increase the orientation factor of the sintered cast (5 vol% loading). Template particles acted as starting grains for the abnormal grain-growth process and the average grain-size was increased after sintering. Increasing the solid loading (15 vol%) resulted in a similar orientation factor with a decrease of the average grain size by more than half. However, addition of templates to the 15 vol% cast had a negative effect on the orientation factor. The impingement of growing particles was stated as the primary cause of particle misorientation resulting in a low orientation factor after sintering. Different heating conditions were tested and it was determined that a slow heating rate gave the highest orientation factor, the smallest average grain-size and the highest relative density. (C) 2015 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 2.986
Times cited: 11
DOI: 10.1016/j.ceramint.2015.12.073
|
|
|
“Strong oxygen participation in the redox governing the structural and electrochemical properties of Na-rich layered oxide Na2IrO3”. Perez AJ, Batuk D, Saubanère M, Rousse G, Foix D, Mc Calla E, J Berg E, Dugas R, van den Bos K H W, Doublet M-L, Gonbeau D, Abakumov AM, Van Tendeloo G, Tarascon J-M, Chemistry of materials 28, 8278 (2016). http://doi.org/10.1021/acs.chemmater.6b03338
Abstract: The recent revival of the Na-ion battery concept has prompted intense activities in the search for new Na-based layered oxide positive electrodes. The largest capacity to date was obtained for a Na-deficient layered oxide that relies on cationic redox processes only. To go beyond this limit, we decided to chemically manipulate these Na-based layered compounds in a way to trigger the participation of the anionic network. We herein report the electrochemical properties of a Na-rich phase Na2IrO3, which can reversibly cycle 1.5 Na+ per formula unit while not suffering from oxygen release nor cationic migrations. Such large capacities, as deduced by complementary XPS, X-ray/neutron diffraction and transmission electron microscopy measurements, arise from cumulative cationic and anionic redox processes occurring simultaneously at potentials as low as 3.0 V. The inability to remove more than 1.5 Na+ is rooted in the formation of an O1-type phase having highly stabilized Na sites as confirmed by DFT calculations, which could rationalize as well the competing metal/oxygen redox processes in Na2IrO3. This work will help to define the most fertile directions in the search for novel high energy Na-rich materials based on more sustainable elements than Ir.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 45
DOI: 10.1021/acs.chemmater.6b03338
|
|
|
“Unique nanostructural features in Fe, Mn-doped YBCO thin films”. Meledin A, Turner S, Cayado P, Mundet B, Solano E, Ricart S, Ros J, Puig T, Obradors X, Van Tendeloo G, Superconductor science and technology 29, 125009 (2016). http://doi.org/10.1088/0953-2048/29/12/125009
Abstract: An attempt to grow a thin epitaxial composite film of YBa2Cu3O7−δ (YBCO) with spinel MnFe2O4 (MFO) nanoparticles on a LAO substrate using the CSD approach resulted in a decomposition of the spinel and various doping modes of YBCO with the Fe and Mn cations. These nanostructural effects lead to a lowering of T c and a slight J c increase in field. Using a combination of advanced transmission electron microscopy (TEM) techniques such as atomic resolution high-angle annular dark field scanning TEM, energy dispersive x-ray spectroscopy and electron energy-loss spectroscopy we have been able to decipher and characterize the effects of the Fe and Mn doping on the film architecture. The YBaCuFeO5 anion-deficient double perovskite phase was detected in the form of 3D inclusions as well as epitaxially grown lamellas within the YBCO matrix. These nano-inclusions play a positive role as pinning centers responsible for the J c/J sf (H) dependency smoothening at high magnetic fields in the YBCO-MFO films with respect to the pristine YBCO films.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.878
Times cited: 6
DOI: 10.1088/0953-2048/29/12/125009
|
|
|
“Atomic resolution electron tomography”. Bals S, Goris B, de Backer A, Van Aert S, Van Tendeloo G, MRS bulletin 41, 525 (2016). http://doi.org/10.1557/mrs.2016.138
Abstract: Over the last two decades, three-dimensional (3D) imaging by transmission electron microscopy or “electron tomography” has evolved into a powerful tool to investigate a variety of nanomaterials in different fields, such as life sciences, chemistry, solid-state physics, and materials science. Most of these results were obtained with nanometer-scale resolution, but different approaches have recently pushed the resolution to the atomic level. Such information is a prerequisite to understand the specific relationship between the atomic structure and the physicochemical properties of (nano) materials. We provide an overview of the latest progress in the field of atomic-resolution electron tomography. Different imaging and reconstruction approaches are presented, and state-of-the-art results are discussed. This article demonstrates the power and importance of electron tomography with atomic-scale resolution.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.199
Times cited: 19
DOI: 10.1557/mrs.2016.138
|
|
|
“Influence of substrate tilt angle on the incorporation of BaHfO3 in thick YBa2Cu3O7-&delta, films”. Sieger M, Pahlke P, Ottolinger R, Stafford BH, Lao M, Meledin A, Bauer M, Eisterer M, Van Tendeloo G, Schultz L, Nielsch K, Hühne R, IEEE transactions on applied superconductivity 27, 1 (2016). http://doi.org/10.1109/Tasc.2016.2631587
Abstract: High critical current densities can be realized in high-temperature superconductors such as YBa2Cu3O7-δ (YBCO) by controlling density, shape, size and direction of a secondary phase. Whereas the dependence on the growth rate and deposition temperature has been widely studied as key parameters for nano-engineering the pinning landscape, the vicinal tilt of the substrate surface might have an additional influence. Therefore, we deposited 6 mol% BaHfO3 (BHO) doped YBCO on SrTiO3 (STO) substrates with vicinal angles α between 0° and 40° to identify the influence of the tilt on the growth mode of BHO. An undisturbed epitaxial growth of the superconductor as well as an epitaxial integration of the BHO phase in the YBCO matrix is observed for all vicinal angles investigated. The critical temperature is constant up to α = 20°, whereas the self-field critical current density at 77 K starts to decrease above 10°. A detailed structural analysis of the film cross sections showed that the growth mode of BHO changes already for a vicinal tilt of 2° from a pure c-axis oriented growth to a layered structure with BHO aligned parallel to the YBCO ab-plane. We identified a strong influence of such a microstructure on the current flow in BHO doped YBCO films on STO substrates as well as on MgO based coated conductors prepared by inclined substrate deposition
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 3
DOI: 10.1109/Tasc.2016.2631587
|
|
|
“Probing the electrochemical behavior of {111} and {110} faceted hollow Cu2O microspheres for lithium storage”. Yu W-B, Hu Z-Y, Yi M, Huang S-Z, Chen D-S, Jin J, Li Y, Van Tendeloo G, Su B-L, RSC advances 6, 97129 (2016). http://doi.org/10.1039/C6RA21026K
Abstract: Transition metal oxides with exposed highly active facets have become of increasing interest as anode materials for lithium ion batteries, because more dangling atoms exposed at the active surface facilitate the reaction between the transition metal oxides and lithium. In this work, we probed the electrochemical behavior of hollow Cu2O microspheres with {111} and {110} active facets on the polyhedron surface as anodes for lithium storage. Compared to commercial Cu2O nanoparticles, hollow Cu2O microspheres with {111} and {110} active facets show a rising specific capacity at 30 cycles which then decreases after 110 cycles during the cycling process. Via advanced electron microscopy characterization, we reveal that this phenomenon can be attributed to the highly active {111} and {110} facets with dangling “Cu” atoms facilitating the conversion reaction of Cu2O and Li, where part of the Cu2O is oxidized to CuO during the charging process. However, as the reaction proceeds, more and more formed Cu nanoparticles cannot be converted to Cu2O or CuO. This leads to a decrease of the specific capacity. We believe that our study here sheds some light on the progress of the electrochemical behavior of transition metal oxides with respect to their increased specific capacity and the subsequent decrease via a conversion reaction mechanism. These results will be helpful to optimize the design of transition metal oxide micro/nanostructures for high performance lithium storage.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.108
Times cited: 5
DOI: 10.1039/C6RA21026K
|
|
|
“BiVO4/3DOM TiO2 nanocomposites: Effect of BiVO4 as highly efficient visible light sensitizer for highly improved visible light photocatalytic activity in the degradation of dye pollutants”. Zalfani M, Hu Z-Y, Yu W-B, Mahdouani M, Bourguig R, Wu M, Li Y, Van Tendeloo G, Djoued Y, Su B-L, Applied Catalysis B-Environmental 205, 121 (2016). http://doi.org/10.1016/j.apcatb.2016.12.019
Abstract: A series of BiVO4/3DOM TiO2 nanocomposites have been synthesized and their photocatalytic activity was investigated under visible light irradiation using the RhB dye as model pollutant molecule in an aqueous solution. The effect of the amount of BiVO4 as visible light sensitizer on the photocatalytic activity of BiVO4/3DOM TiO2 nanocomposites was highlighted. The heterostructured composite system leads to much higher photocatalytic efficiencies than bare 3DOM TiO2 and BiVO4 nanoparticles. As the proportion of BiVO4 in BiVO4/3DOM TiO2 nanocomposites increases from 0.04 to 0.6, the photocatalytic performance of the BiVO4/3DOM TiO2 nanocomposites increases and then decreases after reaching a maximum at 0.2. This improvement in photocatalytic perfomance is related to 1) the interfacial electron transfer efficiency between the coupled materials, 2) the 3DOM TiO2 inverse opal structure with interconnected pores providing an easy mass transfer of the reactant molecules and high accessibility to the active sites and large surface area and 3) the effect of light sensitizer of BiVO4. Intensive studies on structural, textural, optical and surface properties reveal that the electronic interactions between BiVO4 and TiO2 lead to an improved charge separation of the coupled BiVO4/TiO2 system. The photogenerated charge carrier densities increase with increasing the BiVO4 content, which acts as visible light sensitizer to the TiO2 and is responsible for the enhancement in the rate of photocatalytic degradation. However, the photocatalytic activity is reduced when the BiVO4 amount is much higher than that of 3DOM TiO2. Two reasons could account for this behavior. First, with increasing BiVO4 content, the photogenerated electron/hole pairs are accumulated at the surface of the BiVO4 nanoparticles and the recombination rate increases as shown by the PL results. Second, decreasing the amount of 3DOM TiO2 in the nanocomposite decreases the surface area as shown by the BET results. Moreover, the poor adsorptive properties of the BiVO4 photocatalyst also affect the photocatalytic performance, in particular at higher BiVO4 content. The present work demonstrates that BiVO4/3DOM TiO2 is a very promising heterojunction system for visible light photocatalytic applications.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.446
Times cited: 52
DOI: 10.1016/j.apcatb.2016.12.019
|
|
|
“Art, science and sustainability = Kunst, wetenschap en duurzaamheid”. Van Tendeloo G Vrienden van het M HKA, Antwerpen, page 24 (2016).
Keywords: H2 Book chapter; Art; Electron microscopy for materials research (EMAT)
|
|
|
“Heterogeneous conjugation of vegetable oil with alkaline treated highly dispersed Ru/USY catalysts”. Van Aelst J, Philippaerts A, Turner S, Van Tendeloo G, Jacobs P, Sels B, Applied catalysis : A : general 526, 172 (2016). http://doi.org/10.1016/J.APCATA.2016.08.026
Abstract: Heterogeneous metal catalysts enable the direct conjugation of linoleic acid tails in vegetable oil to their conjugated linoleic acid (CIA) isomers. CIA-enriched oils are useful as renewable feedstock for the chemical industry and as nutraceutical. Up to now, a solvent-free process for conjugated oils without significant formation of undesired hydrogenation products was not existing. This work shows the design of Ru/USY catalysts able to directly conjugate highly unsaturated vegetable oils such as safflower oil in absence of solvent and hydrogen. Key is fast molecular transport of the bulky reagent and reactive product triglycerides in the zeolite crystal. A two-step zeolite post-synthetic treatment (with NH4OH and acetate salt) was applied to create the necessary mesoporosity. More open zeolite structures allow for a faster conjugation reaction, while securing a fast removal of the reactive conjugated triglycerides, otherwise rapidly deactivating through fouling and pore blockage by polymers. The best Ru/USY catalyst in this contribution is capable of producing exceptionally high yields of conjugated oils, containing up to almost 30 wt% conjugated fatty acid tails in safflower oil, at an initial production rate of 328 g(CLA) mL(-1) h(-1) per gram metal catalyst. (C) 2016 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.339
Times cited: 1
DOI: 10.1016/J.APCATA.2016.08.026
|
|
|
“Iron-titanium oxide nanocomposites functionalized with gold particles : from design to solar hydrogen production”. Barreca D, Carraro G, Gasparotto A, Maccato C, Warwick MEA, Toniato E, Gombac V, Sada C, Turner S, Van Tendeloo G, Fornasiero P;, Advanced Materials Interfaces 3, 1600348 (2016). http://doi.org/10.1002/ADMI.201600348
Abstract: Hematite-titania nanocomposites, eventually functionalized with gold nanoparticles (NPs), are designed and developed by a plasma-assisted strategy, consisting in: (i) the plasma enhanced-chemical vapor deposition of -Fe2O3 on fluorine-doped tin oxide substrates; the radio frequency-sputtering of (ii) TiO2, and (iii) Au in controlled amounts. A detailed chemicophysical characterization, carried out through a multitechnique approach, reveals that the target materials are composed by interwoven -Fe2O3 dendritic structures, possessing a high porosity and active area. TiO2 introduction results in the formation of an ultrathin titania layer uniformly covering Fe2O3, whereas Au sputtering yields a homogeneous dispersion of low-sized gold NPs. Due to the intimate and tailored interaction between the single constituents and their optical properties, the resulting composite materials are successfully exploited for solar-driven applications. In particular, promising photocatalytic performances in H-2 production by reforming of water-ethanol solutions under simulated solar illumination are obtained. The related insights, presented and discussed in this work, can yield useful guidelines to boost the performances of nanostructured photocatalysts for energy-related applications.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.279
Times cited: 15
DOI: 10.1002/ADMI.201600348
|
|
|
“PDMS membranes containing ZIF-coated mesoporous silica spheres for efficient ethanol recovery via pervaporation”. Naik PV, Wee LH, Meledina M, Turner S, Li Y, Van Tendeloo G, Martens JA, Vankelecom IFJ, Journal of materials chemistry A : materials for energy and sustainability 4, 12790 (2016). http://doi.org/10.1039/C6TA04700A
Abstract: The design of functional micro- and mesostructured composite materials is significantly important for separation processes. Mesoporous silica is an attractive material for fast diffusion, while microporous zeolitic imidazolate frameworks (ZIFs) are beneficial for selective adsorption and diffusion. In this work, ZIF-71 and ZIF-8 nanocrystals were grown on the surface of mesoporous silica spheres (MSS) via the seeding and regrowth approach in order to obtain monodispersed MSS-ZIF-71 and MSS-ZIF-8 spheres with a particle size of 2-3 mm. These MSS-ZIF spheres were uniformly dispersed into a polydimethylsiloxane (PDMS) matrix to prepare mixed matrix membranes (MMMs). These MMMs were evaluated for the separation of ethanol from water via pervaporation. The pervaporation results reveal that the MSS-ZIF filled MMMs substantially improve the ethanol recovery in both aspects viz. flux and separation factor. These MMMs outperforms the unfilled PDMS membranes and the conventional carbon and zeolite filled MMMs. As expected, the mesoporous silica core allows very fast flow of the permeating compound, while the hydrophobic ZIF coating enhances the ethanol selectivity through its specific pore structure, hydrophobicity and surface chemistry. It can be seen that ZIF-8 mainly has a positive impact on the selectivity, while ZIF-71 enhances fluxes more significantly.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 8.867
Times cited: 26
DOI: 10.1039/C6TA04700A
|
|
|
“The mechanical behavior during (de)lithiation of coated silicon nanoparticles as anode material for lithium-ion batteries studied by InSitu transmission electron microscopy”. Van Havenbergh K, Turner S, Marx N, Van Tendeloo G, Energy technology 4, 1005 (2016). http://doi.org/10.1002/ENTE.201600057
Abstract: One approach to cope with the continuous irreversible capacity loss in Si-based electrodes, attributed to lithiation-induced volume changes and the formation of a solid-electrolyte interface (SEI), is by coating silicon nanoparticles. A coating can improve the conductivity of the electrode, form a chemical shield against the electrolyte, or provide mechanical confinement to reduce the volume increase. The influence of such a coating on the mechanical behavior of silicon nanoparticles during Li insertion and Li extraction was investigated by insitu transmission electron microscopy. The type of coating was shown to influence the size of the unreacted core that remains after reaction of silicon with lithium. Furthermore, two mechanisms to relieve the stress generated during volume expansion are reported: the initiation of cracks and the formation of nanovoids. Both result in a full reaction of the silicon nanoparticles, whereas with the formation of cracks, additional surface area is created, on which an SEI can be formed.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 2.789
Times cited: 6
DOI: 10.1002/ENTE.201600057
|
|
|
“Evaluation of mesoporous carbon aerogels as carriers of the non-steroidal anti-inflammatory drug ibuprofen”. Eleftheriadis GK, Filippousi M, Tsachouridou V, Darda M-A, Sygellou L, Kontopoulou I, Bouropoulos N, Steriotis T, Charalambopoulou G, Vizirianakis IS, Van Tendeloo G, Fatouros DG, International journal of pharmaceutics 515, 262 (2016). http://doi.org/10.1016/J.IJPHARM.2016.10.008
Abstract: Towards the development of novel drug carriers for oral delivery of poorly soluble drugs mesoporous aerogel carbons (CAs), namely CA10 and CA20 with different pore sizes (10 and 20 nm, respectively), were evaluated. The non-steroidal anti-inflammatory lipophilic compound ibuprofen was incorporated via passive loading. The drug loaded carbon aerogels were systemically investigated by means of High-Resolution Transmission Electron Microscopy (HR-TEM), Nitrogen physisorption studies, X-ray diffraction (XRD), Differential Scanning Calorimetry (DSC), X-ray photon electron spectroscopy (XPS) and zeta-potential studies. In vitro release studies were performed in simulated intestinal fluids reflecting both fasted (FaSSIF) and fed (FeSSIF) state conditions. Cytotoxicity studies were conducted with human intestinal cells (Caco-2). Drug was in an amorphous state in the pores of the carbon carrier as shown from the physicochemical characterization studies. The results showed marked differences in the release profiles for ibuprofen from the two aerogels in the media tested whereas in vitro toxicity profiles appear to be compatible with potential therapeutic applications at low concentrations. (C) 2016 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Pharmacology. Therapy; Electron microscopy for materials research (EMAT)
Impact Factor: 3.649
Times cited: 7
DOI: 10.1016/J.IJPHARM.2016.10.008
|
|
|
“Fe3O4@MIL-101-A selective and regenerable adsorbent for the removal of as species from water”. Folens K, Leus K, Nicomel NR, Meledina M, Turner S, Van Tendeloo G, Du Laing G, Van Der Voort P, European journal of inorganic chemistry 2016, 4395 (2016). http://doi.org/10.1002/EJIC.201600160
Abstract: The chromium-based metal organic framework MIL-101(Cr) served as a host for the in situ synthesis of Fe3O4 nano particles. This hybrid nanomaterial was tested as an adsorbent for arsenite and arsenate species in groundwater and surface water and showed excellent affinity towards As-III and As-V species. The adsorption capacities of 121.5 and 80.0 mg g(-1) for arsenite and arsenate species, respectively, are unprecedented. The presence of Ca2+, Mg2+, and phosphate ions and natural organic matter does not affect the removal efficiency or the selectivity. The structural integrity of the hybrid nanomaterial was maintained during the adsorption process and even after desorption through phosphate elution. Additionally, no significant leaching of Cr or Fe species was observed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.444
Times cited: 27
DOI: 10.1002/EJIC.201600160
|
|
|
“Diatom silica-titania photocatalysts for air purification by bio-accumulation of different titanium sources”. Van Eynde E, Hu Z-Y, Tytgat T, Verbruggen SW, Watte J, Van Tendeloo G, Van Driessche I, Blust R, Lenaerts S, Environmental science : nano 3, 1052 (2016). http://doi.org/10.1039/C6EN00163G
Abstract: We present a green, biological production route for silica-titania photocatalysts using diatom microalgae. Diatoms are single-celled, eukaryotic microalgae (2-2000 mu m) that self-assemble soluble silicon (Si(OH)(4)) into intricate silica cell walls, called frustules. These diatom frustules are formed under ambient conditions and consist of hydrated silica with specific 3D morphologies and micro-meso or macroporosity. A remarkable characteristic of diatoms is their ability to bioaccumulate soluble titanium from cell culture medium and incorporate them into their nanostructured silica cell wall. Controlled cultivation of the diatom Pinnularia sp. on soluble titanium in a batch process resulted in the biological immobilisation of titanium dioxide in the porous 3D architecture of the frustules. Six different titanium sources are tested. The silica-titania frustules were isolated by treating the harvested Pinnularia cells with nitric acid (65%) or by high temperature treatment. Thermal annealing converted the amorphous titania into crystalline titania. The produced silica-titania material is evaluated towards photocatalytic activity for acetaldehyde (C2H4O) abatement. Frustules cultivated with TiBaldH showed the highest photocatalytic performance. Comparison of the photocatalytic activity with P25 reveals that P25 has a 4 fold higher photocatalytic activity, but when photocatalytic activity is normalized for titania content, the frustules show double activity. Further material characterization (morphology, crystallinity, surface area and elemental distribution) of the TiBaldH silica-titania frustules provides additional insight into their structure-activity relationship. These natural biosilicatitania materials have excellent properties for photocatalytic purposes, including high surface area (108 m(2) g(-1)) and good porosity, and show reliable immobilization of TiO2 in the ordered structure of the diatom frustule.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Sustainable Energy, Air and Water Technology (DuEL)
Impact Factor: 6.047
Times cited: 7
DOI: 10.1039/C6EN00163G
|
|
|
“Size-Induced Switching of Nanowire Growth Direction: a New Approach Toward Kinked Nanostructures”. Shen Y, Lebedev OI, Turner S, Van Tendeloo G, Song X, Yu X, Wang Q, Chen H, Dayeh SA, Wu T, Advanced functional materials 26, 3687 (2016). http://doi.org/10.1002/ADFM.201600142
Abstract: Exploring self-assembled nanostructures with controllable architectures has been a central theme in nanoscience and nanotechnology because of the tantalizing perspective of directly integrating such bottom-up nanostructures into functional devices. Here, the growth of kinked single-crystal In2O3 nanostructures consisting of a nanocone base and a nanowire tip with an epitaxial and defect-free transition is demonstrated for the first time. By tailoring the growth conditions, a reliable switching of the growth direction from [111] to [110] or [112] is observed when the Au catalyst nanoparticles at the apexes of the nanocones shrink below approximate to 100 nm. The natural formation of kinked nanoarchitectures at constant growth pressures is related to the size-dependent free energy that changes for different orientations of the nanowires. The results suggest that the mechanism of forming such kinked nanocone-nanowire nanostructures in well-controlled growth environment may be universal for a wide range of functional materials.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.124
Times cited: 2
DOI: 10.1002/ADFM.201600142
|
|
|
“Investigating lattice strain in Au nanodecahedrons”. Goris B, De Beenhouwer J, de Backer A, Zanaga D, Batenburg J, Sanchez-Iglesias A, Liz-Marzan L, Van Aert S, Sijbers J, Van Tendeloo G, Bals S, , 11 (2016). http://doi.org/10.1002/9783527808465.EMC2016.5519
Keywords: P1 Proceeding; Electron microscopy for materials research (EMAT); Vision lab
DOI: 10.1002/9783527808465.EMC2016.5519
|
|
|
“Air- and water-resistant noble metal coated ferromagnetic cobalt nanorods”. Lentijo-Mozo S, Tan RP, Garcia-Marcelot C, Altantzis T, Fazzini PF, Hungria T, Cormary B, Gallagher JR, Miller JT, Martinez H, Schrittwieser S, Schotter J, Respaud M, Bals S, Van Tendeloo G, Gatel C, Soulantica K, ACS nano 9, 2792 (2015). http://doi.org/10.1021/nn506709k
Abstract: Cobalt nanorods possess ideal magnetic properties for applications requiring magnetically hard nanoparticles. However, their exploitation is undermined by their sensitivity toward oxygen and water, which deteriorates their magnetic properties. The development of a continuous metal shell inert to oxidation could render them stable, opening perspectives not only for already identified applications but also for uses in which contact with air and/or aqueous media is inevitable. However, the direct growth of a conformal noble metal shell on magnetic metals is a challenge. Here, we show that prior treatment of Co nanorods with a tin coordination compound is the crucial step that enables the subsequent growth of a continuous noble metal shell on their surface, rendering them air- and water-resistant, while conserving the monocrystallity, metallicity and the magnetic properties of the Co core. Thus, the as-synthesized coreshell ferromagnetic nanorods combine high magnetization and strong uniaxial magnetic anisotropy, even after exposure to air and water, and hold promise for successful implementation in in vitro biodiagnostics requiring probes of high magnetization and anisotropic shape.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 13.942
Times cited: 25
DOI: 10.1021/nn506709k
|
|
|
“Au@UiO-66 : a base free oxidation catalyst”. Leus K, Concepcion P, Vandichel M, Meledina M, Grirrane A, Esquivel D, Turner S, Poelman D, Waroquier M, Van Speybroeck V, Van Tendeloo G, García H, Van Der Voort P;, RSC advances 5, 22334 (2015). http://doi.org/10.1039/c4ra16800c
Abstract: We present the in situ synthesis of Au nanoparticles within the Zr based Metal Organic Framework, UiO-66. The resulting Au@UiO-66 materials were characterized by means of N-2 sorption, XRPD, UV-Vis, XRF, XPS and TEM analysis. The Au nanoparticles (NP) are homogeneously distributed along the UiO-66 host matrix when using NaBH4 or H-2 as reducing agents. The Au@UiO-66 materials were evaluated as catalysts in the oxidation of benzyl alcohol and benzyl amine employing O-2 as oxidant. The Au@MOF materials exhibit a very high selectivity towards the ketone (up to 100%). Regenerability and stability tests demonstrate that the Au@UiO-66 catalyst can be recycled with a negligible loss of Au species and no loss of crystallinity. In situ IR measurements of UiO-66 and Au@UiO-66-NaBH4, before and after treatment with alcohol, showed an increase in IR bands that can be assigned to a combination of physisorbed and chemisorbed alcohol species. This was confirmed by velocity power spectra obtained from the molecular dynamics simulations. Active peroxo and oxo species on Au could be visualized with Raman analysis.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.108
Times cited: 38
DOI: 10.1039/c4ra16800c
|
|
|
“Boron-rich inclusions and boron distribution in HPHT polycrystalline superconducting diamond”. Lu Y-G, Turner S, Ekimov EA, Verbeeck J, Van Tendeloo G, Carbon 86, 156 (2015). http://doi.org/10.1016/j.carbon.2015.01.034
Abstract: Polycrystalline boron-doped superconducting diamond, synthesized at high pressure and high temperature (HPHT) via a reaction of a single piece of crystalline boron with monolithic graphite, has been investigated by analytical transmission electron microscopy. The local boron distribution and boron environment have been studied by a combination of (scanning) transmission electron microscopy ((S)TEM) and spatially resolved electron energy-loss spectroscopy (EELS). High resolution TEM imaging and EELS elemental mapping have established, for the first time, the presence of largely crystalline diamond-diamond grain boundaries within the material and have evidenced the presence of substitutional boron dopants within individual diamond grains. Confirmation of the presence of substitutional B dopants has been obtained through comparison of acquired boron K-edge EELS fine structures with known references. This confirmation is important to understand the origin of superconductivity in polycrystalline B-doped diamond. In addition to the substitutional boron doping, boron-rich inclusions and triple-points, both amorphous and crystalline, with chemical compositions close to boron carbide B4C, are evidenced. (C) 2015 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.337
Times cited: 20
DOI: 10.1016/j.carbon.2015.01.034
|
|
|
“Cation exchange mediated elimination of the Fe-antisites in the hydrothermal synthesis of LiFePO4”. Paolella A, Bertoni G, Hovington P, Feng Z, Flacau R, Prato M, Colombo M, Marras S, Manna L, Turner S, Van Tendeloo G, Guerfi A, Demopoulos GP, Zaghib K;, Nano energy 16, 256 (2015). http://doi.org/10.1016/j.nanoen.2015.06.005
Abstract: In this work we elucidate the elimination of mechanism Fe-antisite defects in lithium iron phosphate (LiFePO4) during the hydrothermal synthesis. Compelling evidence of this effect is provided by combining Neutron Powder Diffraction (NPD), High Resolution (Scanning) Transmission Electron Microscopy (HR-(S)TEM), Electron Energy Loss Spectroscopy (EELS), X-Ray Photoelectron Spectroscopy (XPS) and calculations. We found: i) the first intermediate vivianite inevitably creates Fe-antisite defects in LiFePO4; ii) the removal of these antisite defects by cation exchange is assisted by a nanometer-thick amorphous layer, rich in Li, that enwraps the LiFePO4 crystals.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.343
Times cited: 27
DOI: 10.1016/j.nanoen.2015.06.005
|
|
|
“Chabazite : stable cation-exchanger in hyper alkaline concrete pore water”. Van Tendeloo L, Wangermez W, Kurttepeli M, de Blochouse B, Bals S, Van Tendeloo G, Martens JA, Maes A, Kirschhock CEA, Breynaert E, Environmental science and technology 49, 2358 (2015). http://doi.org/10.1021/es505346j
Abstract: To avoid impact on the environment, facilities for permanent disposal of hazardous waste adopt multibarrier design schemes. As the primary barrier very often consists of cement-based materials, two distinct aspects are essential for the selection of suitable complementary barriers: (1) selective sorption of the contaminants in the repository and (2) long-term chemical stability in hyperalkaline concrete-derived media. A multidisciplinary approach combining experimental strategies from environmental chemistry and materials science is therefore essential to provide a reliable assessment of potential candidate materials. Chabazite is typically synthesized in 1 M KOH solutions but also crystallizes in simulated young cement pore water, a pH 13 aqueous solution mainly containing K+ and Na+ cations. Its formation and stability in this medium was evaluated as a function of temperature (60 and 85 °C) over a timeframe of more than 2 years and was also asessed from a mechanistic point of view. Chabazite demonstrates excellent cation-exchange properties in simulated young cement pore water. Comparison of its Cs+ cation exchange properties at pH 8 and pH 13 unexpectedly demonstrated an increase of the KD with increasing pH. The combined results identify chabazite as a valid candidate for inclusion in engineered barriers for concrete-based waste disposal.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.198
Times cited: 13
DOI: 10.1021/es505346j
|
|
|
“Competing forces in the self-assembly of coupled ZnO nanopyramids”. Javon E, Gaceur M, Dachraoui W, Margeat O, Ackermann J, Ilenia Saba M, Delugas P, Mattoni A, Bals S, Van Tendeloo G, ACS nano 9, 3685 (2015). http://doi.org/10.1021/acsnano.5b00809
Abstract: Self-assembly (SA) of nanostructures has recently gained increasing interest. A clear understanding of the process is not straightforward since SA of nanoparticles is a complex multiscale phenomenon including different driving forces. Here, we study the SA between aluminum doped ZnO nanopyramids into couples by combining inorganic chemistry and advanced electron microscopy techniques with atomistic simulations. Our results show that the SA of the coupled nanopyramids is controlled first by morphology, as coupling only occurs in the case of pyramids with well-developed facets of the basal planes. The combination of electron microscopy and atomistic modeling reveals that the coupling is further driven by strong ligandligand interaction between the bases of the pyramids as dominant force, while screening effects due to Al doping or solvent as well as corecore interaction are only minor contributions. Our combined approach provides a deeper understanding of the complex interplay between the interactions at work in the coupled SA of ZnO nanopyramids.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 13.942
Times cited: 21
DOI: 10.1021/acsnano.5b00809
|
|
|
“Direct observation and structural characterization of natural and metal ion-exchanged HEU-type zeolites”. Filippousi M, Turner S, Katsikini M, Pinakidou F, Zamboulis D, Pavlidou E, Van Tendeloo G, Microporous and mesoporous materials: zeolites, clays, carbons and related materials 210, 185 (2015). http://doi.org/10.1016/j.micromeso.2015.01.043
Abstract: The atomic structure of natural HEU-type zeolite and two ion-exchanged variants of the zeolite, Ag+ (Ag-HEU) and Zn2+ (Zn-HEU) ion exchanged HEU-type zeolites, are investigated using advanced transmission electron microscopy techniques in combination with X-ray powder diffraction and X-ray absorption fine structure measurements. In both ion-exchanged materials, loading of the natural HEU zeolite is confirmed. Using low-voltage, aberration-corrected transmission electron microscopy at low-dose conditions, the local crystal structure of natural HEU-type zeolite is determined and the interaction of the ion-exchanged natural zeolites with the Ag+ and Zn2+ ions is studied. In the case of Ag-HEU, the presence of Ag+ ions and clusters at extra-framework sites as well as Ag nanoparticles has been confirmed. The Ag nanoparticles are preferentially positioned at the zeolite surface. For Zn-HEU, no large Zn(O) nanopartides are present, instead, the HEU channels are evidenced to be decorated by small Zn(O) clusters. (c) 2015 Elsevier Inc. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.615
Times cited: 5
DOI: 10.1016/j.micromeso.2015.01.043
|
|
|
“Effect of clay modification on structureproperty relationships and thermal degradation kinetics of \beta-polypropylene/clay composite materials”. Papageorgiou DG, Filippousi M, Pavlidou E, Chrissafis K, Van Tendeloo G, Bikiaris D, Journal of thermal analysis and calorimetry 122, 393 (2015). http://doi.org/10.1007/s10973-015-4705-y
Abstract: The influence of neat and organically modified montmorillonite on the structureproperty relationships of a β-nucleated polypropylene matrix has been thoroughly investigated. High-angle annular dark field scanning transmission electron microscopy revealed that the organic modification of clay facilitated the dispersion of the clay, while X-ray diffractograms showed the α-nucleating effect of the clays on the β-nucleated matrix. The results from tensile tests showed that the organic modification of MMT affected profoundly only the tensile strength at yield and at break. The effect of the organic modification of the clay on the thermal stability of the composites was finally evaluated by thermogravimetric analysis, where the samples filled with oMMT decomposed faster than the ones filled with neat MMT, due to the decomposition of the organic salts that were initially used for the modification of MMT. A kinetics study of the thermal degradation of the composites was also performed, in order to export additional conclusions on the activation energy of the samples.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.953
Times cited: 7
DOI: 10.1007/s10973-015-4705-y
|
|
|
“Self-Assembly of Pluronic F127—Silica Spherical Core–Shell Nanoparticles in Cubic Close-Packed Structures”. Kerkhofs S, Willhammar T, Van Den Noortgate H, Kirschhock CEA, Breynaert E, Van Tendeloo G, Bals S, Martens JA, Chemistry of materials 27, 5161 (2015). http://doi.org/10.1021/acs.chemmater.5b01772
Abstract: A new ordered mesoporous silica material (COK-19) with cubic symmetry is synthesized by silicate polycondensation in a citric acid/citrate buffered micellar solution of Pluronic F127 triblock copolymer near neutral pH. SAXS, nitrogen adsorption, TEM, and electron tomography reveal the final material has a cubic close packed symmetry (Fm3̅m) with isolated spherical mesopores interconnected through micropores. Heating of the synthesis medium from room temperature to 70 °C results in a mesopore size increase from 7.0 to 11.2 nm. Stepwise addition of the silicate source allows isolation of a sequence of intermediates that upon characterization with small-angle X-ray scattering uncovers the formation process via formation and aggregation of individual silica-covered Pluronic micelles.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 39
DOI: 10.1021/acs.chemmater.5b01772
|
|