Abstract: The morphology and structure of diamond films, deposited on cubic boron nitride (c-BN) crystals by microwave-plasma-enhanced chemical vapor deposition, is studied by high-resolution scanning electron microscopy and micro-Raman spectroscopy. The c-BN crystals, with sizes of 200 to 350 mu m and grown by a high-temperature/high-pressure technique, were embedded in a copper holder, and used as substrates in deposition runs of 15 min to 5 h. The nucleation centers for diamond appear as well-shaped cuboctahedral crystallites, having diameters of approximately 100 nm. With increasing deposition time the diamond crystallites grew larger, forming islands on the c-BN faces. In some cases, epitaxial growth was observed on the (111) c-BN faces where coalesced particles gave rise to very smooth regions. A number of diamond crystals with peculiar shapes are observed, such as a pseudo five-fold symmetry due to multiple twinning. Moreover, both randomly distributed carbon tubes, about 100 nn in diameter and 1 mu m in length, and spherically shaped features are observed in samples prepared under the typical conditions of diamond deposition, this effect being ascribed to the influence of plasma-sputtered copper contamination. Quite unusual diamond crystals with a deep, pyramidal-shaped hole in the middle grew on the copper substrate between the c-BN crystals. (C) 2000 Elsevier Science S.A. All rights reserved.

Abstract: Pure and Nb-doped TiO2 thick-films were prepared by screen-printing, starting from nanosized powders. Grain growth and crystalline phase modification occurred as consequence of firing at high temperature. It has been shown that niobium addition inhibits grain coarsening and hinders anatase-to-rutile phase transition. These semiconducting films exhibited n-type behavior, while Nb acted as donor-dopant. Gas measurements demonstrated that the films are suitable for CO or NO2 sensing. Microstructural characterization by electron microscopy and differential thermal analysis (DTA) highlights the dependence of gas-sensing behavior on film's properties. (C) 2000 Elsevier Science S.A. All rights reserved.

Abstract: In this work we present for the first time, to our knowledge, the CVD epitaxial growth of beta -SiC using an ion beam synthesized (IBS) beta -SiC layer as seed, which has been formed by multiple implantation into Si wafers at 500 degreesC. The ion beam synthesized continuous layer is constituted by beta -SiC nanocrystals that are well oriented relative to the silicon substrate. Comparison of the epitaxial growth on these samples with that on silicon test samples, both on and off-axis, is performed. The results show that the epitaxial growth can be achieved on the IBS samples without the need of the carbonization step and that the structural quality of the CVD layer is comparable to that obtained on a carbonized silicon sample. Improvement of the quality of the deposited layer is proposed.

Abstract: In situ HREM irradiation of (110) FZ-Si crystals covered with thin Si3N4 films was carried out in a JEOL-4000EX microscope, operated at 400 keV at room temperature. It is found that clustering of vacancies on (113) planes is realised in a Si layer close to the Si-Si3N4 interface at the initial stage of irradiation. Further aggregation of self-interstitials inside vacancy clusters is considered as an alternative way of point defect recombination in extended shape, to be accomplished with the formation of the extended defects of interstitial type upon interstitial supersaturation.

Abstract: The use of an energy-filtering held emission gun transmission electron microscope (CM30 FEG Ultratwin) allows, apart from imaging morphologies down to nanometer scale, the fast acquisition of high-resolution element distributions. Electrons that have lost energy corresponding to characteristic inner-shell loss edges are used to form the element maps. The production of Ultra Large-Scale Integration (ULSI) devices with dimensions below 0.25 mum requires among others the formation of a multilayer metallization scheme by means of repeatedly applying the deposition and etching of dielectrics and metals. In this work the evolution of the surface chemical species on etched Al lines in a post-etch cleaning process has been investigated by energy filtering transmission electron microscopy, with the aim to understand the role of each process step on the removal of the etching residues. (C) 2001 Elsevier Science Ltd. All rights reserved.

Abstract: The morphology and structure of hexagonal graphitic BN (h-BN) powders with graphitization indices GI <5, used as precursors for the synthesis of cubic BN (c-BN) crystals, has been investigated by transmission electron microscopy in diffraction contrast and high resolution. We show that besides the GI, which is a general parameter for controlling the structural quality of h-EN ponders, some other microstructural features strongly influence the synthesis of c-BN. In our opinion, the high reactivity of some h-BN powders results from the presence of some nucleation centers for c-BN, observed at the edges of the h-BN particles. They are formed by a rearrangement of the graphitic (0002) planes by bending back, joining in pairs and forming locally nanoarches (half nanotubes). In these particular places, the nature of bonding locally turns towards sp(3), as in the case of c-BN, (C) 2001 Elsevier Science B.V. All rights reserved.

Abstract: Convergent beam electron diffraction (CBED) is used in this study to investigate the stress distribution around shallow trench isolation (STI) structures. Attention is given to the influence of the different processing parameters and the width and spacing of the structures. The use of a wet or a dry pregate oxidation is found to have a strong influence on the stress behavior. Isolated lines show more stress, leading to the formation of defects in the silicon substrate if a wet pregate oxidation is used. The CBED analyses are compared with micro-Raman and bright-field transmission electron microscopy measurements. (C) 2001 The Electrochemical Society.

Abstract: Infrared absorption spectra of polyhedral and platelet oxygen precipitates in silicon are analyzed using a modified Day-Thorpe approach [J. Phys.: Condens. Matter 11, 2551 (1999)]. The aspect ratio of the precipitates is determined by transmission electron microscopy analysis. The reduced spectral function and the stoichiometry of the precipitate are extracted from the absorption spectra and the amount of precipitated interstitial oxygen. The experimental absorption spectra can be divided in a set with a Frohlich frequency of around 1100 cm(-1) and in a set with a Frohlich frequency between 1110 and 1120 cm(-1). It is shown that the shift in the Frohlich frequency is not due to a differing stoichiometry, but to the detailed structure of the reduced spectral function. Inverse modeling of the spectra suggests that the oxide precipitates consist of substoichiometric SiOgamma with gamma=1.17+/-0.14. (C) 2002 American Institute of Physics.

Abstract: High-resolution electron microscopy (HREM) studies of the microstructure and specific defects in hexagonal boron nitride (h-BN) precursors and cubic boron nitride (c-BN) crystals made under high-pressure high-temperature conditions revealed the presence of half-nanotubes at the edges of the h-BN particles. Their sp(3) bonding tendency could strongly influence the nucleation rates of c-BN. The atomic resolution at extended dislocations was insufficient to allow us to determine the stacking fault energy in the c-BN crystals. Its mean value of 191 +/- 15 mJ m(-2) is of the same order of magnitude as that of diamond. High-frequency (94 GHz) electron paramagnetic resonance studies on c-BN single crystals have produced new data on the D1 centres associated with the boron species. Ion-beam-induced luminescence measurements have indicated that c-BN is a very interesting luminescent material, which is characterized by four luminescence bands and exhibits a better resistance to ionizing radiation than CVD diamond.

Abstract: An alternative pathway to assemble mesoporous molecular sieve silicas is developed using nonionic alkylamines and N,N-dimethylalkylamines (SO) as structure-directing agents in acidic conditions. The synthesized mesostructures possess wormhole-like frameworks with pore sizes and pore volumes in the range of 20-90 Angstrom and 0.5-1.3 cm(3)/g, respectively. The formation of the mesophase is controlled by a counterion-mediated mechanism of the type (S(0)H(+))(X(-)I(+)), where S(0)H(+) are protonated water molecules that are hydrogen bonded to the lone electron pairs on the amine surfactant headgroups (S(0)H(+)), X(-) is the counteranion originating from the acid, and I(+) are the positively charged (protonated) silicate species. We found that the stronger the ion X(-) is bonded to S(0)H(+), the more it catalyzes the silica condensation into (S(0)H(+))(X(-)I(+)). Br(-) is shown to be a strong binding anion and therefore a fast silica polymerization promoter compared to Cl(-) resulting in the formation of a higher quality mesophase for the Br(-) syntheses. We also showed that the polymerization rate of the silica, dictated by the counterion, controls the morphology of the mesostructures from nonuniform agglomerated blocks in the case of Br(-) syntheses to spherical particles for the Cl(-) syntheses. Next to many benefits such as low temperature, short synthesis time, and the use of inexpensive, nontoxic, and easily extractable amine templates, the developed materials have a remarkable higher thermal and hydrothermal stability compared to hexagonal mesoporous silica, which is also prepared with nonionic amines but formed through the S(0)I(0) mechanism.

Abstract: Multishell tabular grains have a higher speed than pure AgBr tabular grains. Usually the shells differ in size and iodide content, but also the precipitation method for the iodide containing shells has an influence on the iodide incorporation. A TEM investigation was performed to determine the defect structure of multishell AgBr (111) tabular crystals containing a shell with a low iodide concentration and one with a high iodide concentration. The twins that induce tabular growth and stacking fault contrast in the region of the iodide shells have been observed, similar to previously studied AgBr/Ag(Br,I) coreshell crystals. Moreover in some of the crystals dislocations have been observed, sometimes even an entire network. The number of dislocations formed varies for the different methods of iodide addition. Also variations in average thickness between the different iodide addition methods have been observed. A higher number of dislocations and thicker crystals point towards a higher local concentration of iodide. These observations allow deciding which iodide incorporation method is most useful for a preferred dislocation pattern.

Abstract: Infrared absorption spectra of oxygen precipitates in boron-doped silicon with a boron concentration between 10(17) and 10(19) cm(-3) are analyzed, applying the spectral function representation of composite materials. The aspect ratio of the platelet precipitates is determined by transmission electron microscopy measurements. The analysis shows that in samples with moderate doping levels (<10(18) B cm(-3)) SiOγ precipitates are formed with the same composition as in the lightly doped case. In the heavily boron-doped (>10(18) cm(-3)) samples, however, the measured spectra of the precipitates are consistent with a mixture of SiO2 and B2O3, with a volume fraction of B2O3 as high as 0.41 in the most heavily doped case. (C) 2004 The Electrochemical Society.