Abstract: Synthetic electrochemistry agrees well with the principles of sustainable chemistry, therefore it is considered as a more environmentally friendly approach than some current synthetic methods Here, we present a new strategy for the chemoselective oxidation of vicinal diols, viz. the integration of neocuproine palladium catalysts and electrosynthesis. Benzoquinones are used as an effective mediator as the reduced species (hydroquinones) can be easily reoxidized at relative low potentials at an electrode surface. NeocuproinePd(OAc)2 efficiently works as a catalyst in an electrolysis reaction for vicinal diols at room temperature. This is a remarkable observation given the fact that aerobic oxidation reactions of alcohols typically need a more complex catalyst, i.e. [neocuproinePdOAc]2[OTf]2. In this article we describe the optimization of the electrolysis conditions for the neocuproinePd(OAc)2 catalyst to selectively oxidize diols. The suggested approach leads to conversion of alcohols with high yields and provides an interesting alternative to perform oxidation reactions under mild conditions by the aid of electrochemistry.

Abstract: Barium lanthanum ferrite and four Mn/Ti substituted materials were synthesized by the sol-gel method. The crystal structure of the materials was studied by a combination of X-ray powder diffraction, electron diffraction, scanning transmission electron microscopy and 57Fe Mössbauer spectrometry. BaLaFe2O6-δ has a cubic perovskite structure and Ba0.7La1.3FeMnO6-δ is distorted perovskite with the R-3c symmetry, both from electron diffraction and X-ray powder diffraction. However, according to transmission electron microscopy, the crystals of BaLaFeTiO6-δ, BaLaFeTi0.5Mn0.5O6-δ, and BaLaFe0.5Ti0.5MnO6-δ consist of nanodomains with different symmetries (Pm3m next to R-3c due to octahedral tilts), whereas the bulk X-ray powder diffraction patterns for these compounds correspond to the simple cubic structure. 57Fe Mössbauer spectrometry confirms that all materials contain high spin state Fe3+ ions which are strongly influenced by the chemical disorder
resulting from various cationic environments.

Abstract: A polycrystalline sample of Ba3Fe2TeO9 having the 6H perovskite structure has been prepared in a solid-state reaction and studied by a combination of electron microscopy, Mossbauer spectroscopy, magnetometry, X-ray diffraction and neutron diffraction. Partial ordering of Fe3+ and Te6+ cations occurs over the six-coordinate sites; the corner-sharing octahedra are predominantly occupied by the former and the face-sharing octahedra by a 1:1 mixture of the two. On cooling through the temperature range 18 < T/K < 295 an increasing number of spins join an antiferromagnetic backbone running through the structure while the remainder show complex relaxation effects. At 3 K an antiferromagnetic phase and a spin glass coexist.

Abstract: Quantum electron transport in side-gated graphene Hall bars is investigated in the presence of quantizing external magnetic fields. The asymmetric potential of four side-gates distorts the otherwise flat bands of the relativistic Landau levels, and creates new propagating states in the Landau spectrum (i.e. snake states). The existence of these new states leads to an interesting modification of the bend and Hall resistances, with new quantizing plateaus appearing in close proximity of the Landau levels. The electron guiding in this system can be understood by studying the current density profiles of the incoming and outgoing modes. From the fact that guided electrons fully transmit without any backscattering (similarly to edge states), we are able to analytically predict the values of the quantized resistances, and they match the resistance data we obtain with our numerical (tight-binding) method. These insights in the electron guiding will be useful in predicting the resistances for other side-gate configurations, and possibly in other system geometries, as long as there is no backscattering of the guided states.

Abstract: <script type='text/javascript'>document.write(unpmarked('The crystal and defect structure of SnS crystals grown using chemical vapour deposition for application in electronic devices are investigated. The structural analysis shows the presence of two distinct crystal morphologies, that is thin flakes with lateral sizes up to 50 m and nanometer scale thickness, and much thicker but smaller crystallites. Both show similar Raman response associated with SnS. The structural analysis with transmission electron microscopy shows that the flakes are single crystals of -SnS with [010] normal to the substrate. Parallel with the surface of the flakes, lamellae with varying thickness of a new SnS phase are observed. High-resolution transmission electron microscopy (TEM), scanning transmission electron microscopy (STEM), first-principles simulations (DFT) and nanobeam diffraction (NBD) techniques are employed to characterise this phase in detail. DFT results suggest that the phase is a strain stabilised \u0027 one grown epitaxially on the -SnS crystals. TEM analysis shows that the crystallites are also -SnS with generally the [010] direction orthogonal to the substrate. Contrary to the flakes the crystallites consist of two to four grains which are tilted up to 15 degrees relative to the substrate. The various grain boundary structures and twin relations are discussed. Under high-dose electron irradiation, the SnS structure is reduced and -Sn formed. It is shown that this damage only occurs for SnS in direct contact with SiO2. Lay description SnS is a p-type semiconductor, which has attracted significant interest for electronic devices due to its unique properties, low-toxicity and abundance of Sn in nature. Although in the past it has been most extensively studied as the absorber material in solar cells, it has recently garnered interest for application as a p-type two-dimensional semiconductor in nanoelectronic devices due to its anisotropic layered structure similar to the better known phosphorene. Tin sulphide can take the form of several phases and the electronic properties of the material depend strongly on its crystal structure. It is therefore crucial to study the crystal structure of the material in order to predict the electronic properties and gain insight into the growth mechanism. In this work, SnS crystals deposited using a chemical vapour deposition technique are investigated extensively for their crystal and defect structure using transmission electron microscopy (TEM) and related techniques. We find the presence of two distinct crystal morphologies, that is thin flakes with lateral sizes up to 50 m and nm scale thickness, and much thicker but smaller crystallites. The flakes are single crystals of -SnS and contain lamellae with varying thickness of a different phase which appear to be -SnS at first glance. High-resolution scanning transmission electron microscopy is used to characterise these lamellae where the annular bright field (ABF) mode better reveals the position of the sulphur columns. The sulphur columns in the lamellae are found to be shifted relative to the -SnS structure which indicates the formation of a new phase which is a distorted version of the phase which we tentatively refer to as \u0027-SnS. Simulations based on density functional theory (DFT) are used to model the interface and a similar shift of sulphur columns in the -SnS layer is observed which takes place as a result of strong interaction at the interface between the two phases resulting in strain transfer. Nanobeam electron diffraction (NBD) is used to map the lattice mismatch in the thickness of the flakes which reveals good in-plane matching and some expansion out-of-plane in the lamellae. Contrary to the flakes the crystallites are made solely of -SnS and consist of two to four grains which are tilted up to 15 degrees relative to the substrate. The various grain boundary structures and twin relations are discussed. At high electron doses, SnS is reduced to -Sn, however the damage occurs only for SnS in direct contact with SiO2.'));

Abstract: In-situ fabrication of palladium(0) nanoparticles inside zeolitic imidazolate frameworks (ZIF-8) has been established via one-step facile spray-dry technique. Crystal structures and morphologies of the Pd@ZIF-8 samples are investigated by powder XRD, TEM, SAED, STEM, and EDX techniques. High angle annular dark field scanning transmission electron microscopy (HAAD-STEM) and 3D tomographic analysis confirm the presence of palladium nanoparticles inside the ZIF-8 structure. The porosity, surface area and N-2 physisorption properties are evaluated for Pd@ZIF-8 with various palladium contents. Furthermore, Pd@ZIF-8 samples are effectively applied as heterogeneous catalysts in alkenes hydrogenation. This straightforward method is able to speed up the synthesis of encapsulation of metal nanoparticles in metal organic frameworks. (C) 2017 Elsevier B.V. All rights reserved.

Abstract: Plasma catalysis is gaining increasing interest for CO2 conversion, but the interaction between the plasma and catalyst is still poorly understood. This is caused by limited systematic materials research, since most works combine a plasma with commercial supported catalysts and packings. In the present paper, we study the influence of specific material and reactor properties, as well as reactor/bead configuration, on the conversion and energy efficiency of CO2 dissociation in a packed bed dielectric barrier discharge (DBD) reactor. Of the various packing materials investigated, BaTiO3 yields the highest conversion and energy efficiency, i.e., 25% and 4.5%.
Our results show that, when evaluating the influence of catalysts, the impact of the packing (support) material itself cannot be neglected, since it can largely affect the conversion and energy efficiency. This shows the large potential for further improvement of packed bed plasma reactors for CO2 conversion and other chemical conversion reactions by adjusting both packing (support) properties and catalytically active sites. Moreover, we clearly prove that comparison of results obtained in different reactor setups should be done with care, since there is a large effect of the reactor setup and reactor/bead configuration.

Abstract: Mesoporous MIL-101(Cr) is used as host for a ship-in-a-bottle type adsorbent for selective U(VI) recovery from aqueous environments. The acid-resistant cage-type MOF is built in-situ around N,N-Diisobutyl-2-(octylphenylphosphoryl)acetamide (CMPO), a sterically demanding ligand with high U(VI) affinity. This one-step procedure yields an adsorbent which is an ideal compromise between homogeneous and heterogeneous systems, where the ligand can act freely within the pores of MIL-101, without leaching, while the adsorbent is easy separable and reusable. The adsorbent was characterized by XRD, FTIR spectroscopy, nitrogen adsorption, XRF, ADF-STEM and EDX, to confirm and quantify the successful encapsulation of the CMPO in MIL-101, and the preservation of the host. Adsorption experiments with a central focus on U(VI) recovery were performed. Very high selectivity for U(VI) was observed, while competitive metal adsorption (rare earths, transition metals...) was almost negligible. The adsorption capacity was calculated at 5.32 mg U/g (pH 3) and 27.99 mg U/g (pH 4), by fitting equilibrium data to the Langmuir model. Adsorption kinetics correlated to the pseudo-second-order model, where more than 95% of maximum uptake is achieved within 375 min. The adsorbed U(VI) is easily recovered by desorption in 0.1 M HNO3. Three adsorption/desorption cycles were performed. (C) 2017 Elsevier B.V. All rights reserved.

Abstract: The Wigner-Liouville equation is reformulated using a spectral decomposition of the classical force field instead of the potential energy. The latter is shown to simplify the Wigner-Liouville kernel both conceptually and numerically as the spectral force Wigner-Liouville equation avoids the numerical evaluation of the highly oscillatory Wigner kernel which is nonlocal in both position and momentum. The quantum mechanical evolution is instead governed by a term local in space and non-local in momentum, where the non locality in momentum has only a limited range. An interpretation of the time evolution in terms of two processes is presented; a classical evolution under the influence of the averaged driving field, and a probability-preserving quantum-mechanical generation and annihilation term. Using the inherent stability and reduced complexity, a direct deterministic numerical implementation using Chebyshev and Fourier pseudo-spectral methods is detailed. For the purpose of illustration, we present results for the time evolution of a one-dimensional resonant tunneling diode driven out of equilibrium. (C) 2017 Elsevier Inc. All rights reserved.

Abstract: The response of electron systems to electrodynamic fields that change rapidly in space is endowed by unique features, including an exquisite spatial nonlocality. This can reveal much about the materials' electronic structure that is invisible in standard probes that use gradually varying fields. Here, we use graphene plasmons, propagating at extremely slow velocities close to the electron Fermi velocity, to probe the nonlocal response of the graphene electron liquid. The near-field imaging experiments reveal a parameter-free match with the full quantum description of the massless Dirac electron gas, which involves three types of nonlocal quantum effects: single-particle velocity matching, interaction-enhanced Fermi velocity, and interaction-reduced compressibility. Our experimental approach can determine the full spatiotemporal response of an electron system.

Abstract: A new electrocatalytic conversion of alcohols to ketones and aldehydes was developed based on an electrochemical study of Shvos complex. The oxidation of secondary alcohols was efficiently performed under mild conditions using a catalytic amount of Shvos catalyst, in combination with a sub-stoichiometric amount of 2,6-dimethoxy-1,4- benzoquinone in N,N-dimethylformamide at 80 8C. The hydroquinone thus formed is continuously reoxidized with the aid of an electrochemical device. Excellent yields for different ketones, aromatic as well as aliphatic and a,b-unsaturated ketones, are obtained. In addition, chemoselectivity towards oxidation of the secondary alcohol is achieved when converting vicinal diols such as 1,2-octanediol and 1,2-decanediol.

Abstract: This work addresses the dissolution corrosion behaviour of 316L austenitic stainless steels. For this purpose, solution-annealed and cold-deformed 316L steels were simultaneously exposed to oxygen-poor (<10-8 mass%) static liquid lead-bismuth eutectic (LBE) for 253e3282 h at 500 °C. Corrosion was consistently more severe for the cold-drawn steels than the solution-annealed steel, indicating the importance of the steel thermomechanical state. The thickness of the dissolution-affected zone was nonuniform, and sites of locally-enhanced dissolution were occasionally observed. The progress of LBE dissolution attack was promoted by the interplay of certain steel microstructural features (grain boundaries, deformation twin laths, precipitates) with the dissolution corrosion process. The identified dissolution mechanisms were selective leaching leading to steel ferritization, and non-selective leaching; the latter was mainly observed in the solution-annealed steel. The maximum corrosion rate decreased with exposure time and was found to be inversely proportional to the depth of dissolution attack.

Abstract: In a mesoscopic sample of a chiral p-wave superconductor, novel states comprising skyrmions and edge states have been stabilized in out-of-plane applied magnetic field. Using the time-dependent Ginzburg-Landau equations we shed light on the dynamic response of such states to an external applied current. Three different regimes are obtained, namely, the superconducting (stationary), resistive (non-stationary) and normal regime, similarly to conventional s-wave superconductors. However, in the resistive regime and depending on the external current, we found that moving skyrmions and the edge state behave distinctly different from the conventional kinematic vortex, thereby providing new fingerprints for identification of p-wave superconductivity. (C) 2016 Elsevier B.V. All rights reserved.

Abstract: The ability of urban wastewater systems to adapt and transform as a response to change is an integral part of sustainable development. This requires technology and infrastructure that can be adapted to new operational challenges. In this study the adaptive capacity of urban wastewater systems is evaluated by assessing the interdependencies between system components. In interdependent and therefore tightly coupled systems, changes to one systems component will require alteration elsewhere in the system, therefore impairing the capacity of these systems to be changed. The aim of this paper is to develop a methodology to evaluate the adaptive capacity of urban wastewater systems by assessing how change drivers and innovation affect existing wastewater technology and infrastructure. The methodology comprises 7 steps and applies a change impact table and a design structure matrix that are completed by experts during workshops. Change impact tables quantify where change drivers, such as energy neutrality and resource recovery, require innovation in a system. The design structure matrix is a tool to quantify emerging changes that are a result of the innovation. The method is applied for the change driver of energy neutrality and shown for two innovations: a decentralised upflow anaerobic sludge blanket reactor followed by an anammox process and a conventional activated sludge treatment with enhanced chemical precipitation and high temperature-high pressure hydrolysis. The results show that the energy neutrality of wastewater systems can be address by either innovation in the decentralised or centralised treatment. The quantification of the emerging changes for both innovations indicates that the decentralised treatment is more disruptive, or in other words, the system needs to undergo more adaptation. It is concluded that the change impact and change propagation method can be used to characterise and quantify the technological or infrastructural transformations. In addition, it provides insight into the stakeholders affected by change.

Abstract: SmFe8.75 Si-0.25 C/alpha-Fe nanocomposites have been successfully synthesized using high energy milling, followed by annealing at 750 degrees C. The crystal structure of these compounds was characterized by the Rietveld method using powder X-ray diffraction data. By increasing the concentration of Sm, we observed a decrease in the amount of alpha-Fe phase. The morphology of the samples was determined by scanning and transmission electron microscopy. The average grain size is about 20 nm. The magnetic properties were investigated at room temperature and at 10 K. A ferromagnetic behavior was observed in all samples at both temperatures. An increase of the soft magnetic phase alpha-Fe induced an increase in the magnetization and a decrease in coercivity. (C) 2016 Elsevier B.V. All rights reserved.