“Highly-translucent, strong and aging-resistant 3Y-TZP ceramics for dental restoration by grain boundary segregation”. Zhang F, Vanmeensel K, Batuk M, Hadermann J, Inokoshi M, Van Meerbeek B, Naert I, Vleugels J, Acta biomaterialia 16, 215 (2015). http://doi.org/10.1016/j.actbio.2015.01.037
Abstract: Latest trends in dental restorative ceramics involve the development of full-contour 3Y-TZP ceramics which can avoid chipping of veneering porcelains. Among the challenges are the low translucency and the hydrothermal stability of 3Y-TZP ceramics. In this work, different trivalent oxides (Al2O3, Sc2O3, Nd2O3 and La2O3) were selected to dope 3Y-TZP ceramics. Results show that dopant segregation was a key factor to design hydrothermally stable and high-translucent 3Y-TZP ceramics and the cation dopant radius could be used as a controlling parameter. A large trivalent dopant, oversized as compared to Zr4+, exhibiting strong segregation at the ZrO2 grain boundary was preferred. The introduction of 0.2 mol% La2O3 in conventional 0.10.25 wt.% Al2O3-doped 3Y-TZP resulted in an excellent combination of high translucency and superior hydrothermal stability, while retaining excellent mechanical properties.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.319
Times cited: 54
DOI: 10.1016/j.actbio.2015.01.037
|
|
|
“Sub-ppm H2S sensing by tubular ZnO-Co3O4 nanofibers”. Rumyantseva MN, Vladimirova SA, Platonov VB, Chizhov AS, Batuk M, Hadermann J, Khmelevsky NO, Gaskov AM, Sensors And Actuators B-Chemical 307, 127624 (2020). http://doi.org/10.1016/j.snb.2019.127624
Abstract: Tubular ZnO – Co3O4 nanofibers were co-electrospun from polymer solution containing zinc and cobalt acetates. Phase composition, cobalt electronic state and element distribution in the fibers were investigated by XRD, SEM, HRTEM, HAADF-STEM with EDX mapping, and XPS. Bare ZnO has high selective sensitivity to NO and NO2, while ZnO-Co3O4 composites demonstrate selective sensitivity to H2S in dry and humid air. This effect is discussed in terms of transformation of cobalt oxides into cobalt sulfides and change in the acidity of ZnO oxide surface upon cobalt doping. Reduction in response and recovery time is attributed to the formation of a tubular structure facilitating gas transport through the sensitive layer.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.401
DOI: 10.1016/j.snb.2019.127624
|
|
|
“Tuning the crystal structure of A2CoPO4F(A=Li,Na) fluoride-phosphates : a new layered polymorph of LiNaCoPO4F”. Fedotov SS, Aksyonov DA, Samarin AS, Karakulina OM, Hadermann J, Stevenson KJ, Khasanova NR, Abakumov AM, Antipov E V, European journal of inorganic chemistry 2019, 4365 (2019). http://doi.org/10.1002/EJIC.201900660
Abstract: Co-containing fluoride-phosphates are of interest in sense of delivering high electrode potentials and attractive specific energy values as positive electrode materials for rechargeable batteries. In this paper we report on a new Co-based fluoride-phosphate, LiNaCoPO4F, with a layered structure (2D), which was Rietveld-refined based on X-ray powder diffraction data [P2(1)/c, a = 6.83881(4) angstrom, b = 11.23323(5) angstrom, c = 5.07654(2) angstrom, beta = 90.3517(5) degrees, V = 389.982(3) angstrom(3)] and validated by electron diffraction and high-resolution scanning transmission electron microscopy. The differential scanning calorimetry measurements revealed that 2D-LiNaCoPO4F forms in a narrow temperature range of 520-530 degrees C and irreversibly converts to the known 3D-LiNaCoPO4F modification (Pnma) above 530 degrees C. The non-carbon-coated 2D-LiNaCoPO4F shows reversible electrochemical activity in Li-ion cell in the potential range of 3.0-4.9 V vs. Li/Li+ with an average potential of approximate to 4.5 V and in Na-ion cell in the range of 3.0-4.5 V vs. Na/Na+ exhibiting a plateau profile centered around 4.2 V, in agreement with the calculated potentials by density functional theory. The energy barriers for both Li+ and Na+ migration in 2D-LiNaCoPO4F amount to 0.15 eV along the [001] direction rendering 2D-LiNaCoPO4F as a viable electrode material for high-power Li- and Na-ion rechargeable batteries. The discovery and stabilization of the 2D-LiNaCoPO4F polymorph indicates that temperature influence on the synthesis of A(2)MPO(4)F fluoride-phosphates needs more careful examination with perspective to unveil new structures.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.444
DOI: 10.1002/EJIC.201900660
|
|
|
“Disproportionation of Co2+ in the topochemically reduced oxide LaSrCoRuO₅”. Liang Z, Batuk M, Orlandi F, Manuel P, Hadermann J, Hayward MA, Angewandte Chemie: international edition in English 63, e202313067 (2024). http://doi.org/10.1002/ANIE.202313067
Abstract: Complex transition-metal oxides exhibit a wide variety of chemical and physical properties which are a strong function the local electronic states of the transition-metal centres, as determined by a combination of metal oxidation state and local coordination environment. Topochemical reduction of the double perovskite oxide, LaSrCoRuO6, using Zr, yields LaSrCoRuO5. This reduced phase contains an ordered array of apex-linked square-based pyramidal Ru3+O5, square-planar Co1+O4 and octahedral Co3+O6 units, consistent with the coordination-geometry driven disproportionation of Co2+. Coordination-geometry driven disproportionation of d(7) transition-metal cations (e.g. Rh2+, Pd3+, Pt3+) is common in complex oxides containing 4d and 5d metals. However, the weak ligand field experienced by a 3d transition-metal such as cobalt leads to the expectation that d(7+) Co2+ should be stable to disproportionation in oxide environments, so the presence of Co1+O4 and Co3+O6 units in LaSrCoRuO5 is surprising. Low-temperature measurements indicate LaSrCoRuO5 adopts a ferromagnetically ordered state below 120 K due to couplings between S=(1)/(2) Ru3+ and S=1 Co1+.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 16.6
DOI: 10.1002/ANIE.202313067
|
|
|
“Computationally Driven Discovery of a Family of Layered LiNiB Polymorphs”. Gvozdetskyi V, Bhaskar G, Batuk M, Zhao X, Wang R, Carnahan SL, Hanrahan MP, Ribeiro RA, Canfield PC, Rossini AJ, Wang C-Z, Ho K-M, Hadermann J, Zaikina JV, Angewandte Chemie: international edition in English 58, 15855 (2019). http://doi.org/10.1002/anie.201907499
Abstract: Two novel lithium nickel boride polymorphs RT-LiNiB and HT-LiNiB with layered crystal structures are reported. This family of compounds was theoretically predicted by using the adaptive genetic algorithm (AGA) and subsequently synthesized via a hydride route with LiH precursor as a lithium source. Being unique among the known ternary transition metal borides, the LiNiB structures feature Li layers alternating with nearly planar [NiB] layers, composed of Ni hexagonal rings centered by B-B pairs. A comprehensive study using a combination of single crystal/synchrotron powder X-ray diffraction data, solid-state 7Li and 11B NMR, scanning transmission electron microscopy, quantum chemistry calculations, and magnetism has shed light on the intrinsic features of these polymorphic compounds. The unique layered structures of LiNiB compounds make them ultimate precursors to further study their exfoliation, paving a way toward two-dimensional transition metal borides, MBenes.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 11.994
DOI: 10.1002/anie.201907499
|
|
|
“A Chemical Approach to Raise Cell Voltage and Suppress Phase Transition in O3 Sodium Layered Oxide Electrodes”. Sathiya M, Jacquet Q, Doublet ML, Karakulina OM, Hadermann J, Tarascon J-M, Advanced energy materials (2018). http://doi.org/10.1002/aenm.201702599
Abstract: Sodium ion batteries (NIBs) are one of the versatile technologies for lowcost rechargeable batteries. O3-type layered sodium transition metal oxides (NaMO2, M = transition metal ions) are one of the most promising positive electrode materials considering their capacity. However, the use of O3 phases is limited due to their low redox voltage and associated multiple phase transitions which are detrimental for long cycling. Herein, a simple strategy is proposed to successfully combat these issues. It consists of the introduction of a larger, nontransition metal ion Sn4+ in NaMO2 to prepare a series of NaNi0.5Mn0.5−y SnyO2 (y = 0–0.5) compositions with attractive electrochemical performances, namely for y = 0.5, which shows a single-phase transition from O3 ⇔ P3 at the very end of the oxidation process. Na-ion NaNi0.5Sn0.5O2/C coin cells are shown to deliver an average cell voltage of 3.1 V with an excellent capacity retention as compared to an average stepwise voltage of ≈2.8 V and limited capacity retention for the pure NaNi0.5Mn0.5O2 phase. This study potentially shows the way to manipulate the O3 NaMO2 for facilitating their practical use in NIBs.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 21.875
Times cited: 28
DOI: 10.1002/aenm.201702599
|
|
|
“Enhancing the hydrogen evolution properties of kesterite absorber by Si-doping in the surface of CZTS thin film”. Vishwakarma M, Kumar M, Hendrickx M, Hadermann J, Singh AP, Batra Y, Mehta BR, Advanced Materials Interfaces , 2002124 (2021). http://doi.org/10.1002/ADMI.202002124
Abstract: In this work, the effects of Si-doping in Cu2ZnSnS4 are examined computationally and experimentally. The density functional theory calculations show that an increasing concentration of Si (from x = 0 to x = 1) yields a band gap rise due to shifting of the conduction band minimum towards higher energy states in the Cu2Zn(Sn1-xSix)S-4. CZTSiS thin film prepared by co-sputtering process shows Cu2Zn(Sn1-xSix)S-4 (Si-rich) and Cu2ZnSnS4 (S-rich) kesterite phases on the surface and in the bulk of the sample, respectively. A significant change in surface electronic properties is observed in CZTSiS thin film. Si-doping in CZTS inverts the band bending at grain-boundaries from downward to upward and the Fermi level of CZTSiS shifts upward. Further, the coating of the CdS and ZnO layer improves the photocurrent to approximate to 5.57 mA cm(-2) at -0.41 V-RHE in the CZTSiS/CdS/ZnO sample, which is 2.39 times higher than that of pure CZTS. The flat band potential increases from CZTS approximate to 0.43 V-RHE to CZTSiS/CdS/ZnO approximate to 1.31 V-RHE indicating the faster carrier separation process at the electrode-electrolyte interface in the latter sample. CdS/ZnO layers over CZTSiS significantly reduce the charge transfer resistance at the semiconductor-electrolyte interface.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.279
DOI: 10.1002/ADMI.202002124
|
|
|
“Trapping of Oxygen Vacancies at Crystallographic Shear Planes in Acceptor-Doped Pb-Based Ferroelectrics”. Batuk D, Batuk M, Tsirlin AA, Hadermann J, Abakumov AM, Angewandte Chemie: international edition in English 54, 14787 (2015). http://doi.org/10.1002/anie.201507729
Abstract: The defect chemistry of the ferroelectric material PbTiO3 after doping with Fe(III) acceptor ions is reported. Using advanced transmission electron microscopy and powder X-ray and neutron diffraction, we demonstrate that even at concentrations as low as circa 1.7% (material composition approximately ABO2.95), the oxygen vacancies are trapped into extended planar defects, specifically crystallographic shear planes. We investigate the evolution of these defects upon doping and unravel their detailed atomic structure using the formalism of superspace crystallography, thus unveiling their role in nonstoichiometry in the Pb-based perovskites.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 11.994
Times cited: 3
DOI: 10.1002/anie.201507729
|
|
|
“Achieving independent control of core diameter and carbon shell thickness in Pd-C core–shell nanoparticles by gas phase synthesis”. Singh V, Mehta BR, Sengar SK, Karakulina OM, Hadermann J, Kaushal A, Nanotechnology 28, 295603 (2017). http://doi.org/10.1088/1361-6528/aa7660
Abstract: Pd-C core–shell nanoparticles with independently controllable core size and shell thickness are grown by gas phase synthesis. First, the core size is selected by electrical mobility values of charged particles, and second, the shell thickness is controlled by the concentration of carbon precursor gas. The carbon shell grows by adsorption of carbon precursor gas molecules on the surface of nanoparticles, followed by sintering. The presence of a carbon shell on Pd nanoparticles is potentially important in hydrogen-related applications operating at high temperatures or in catalytic reactions in acidic/aqueous environments.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.44
Times cited: 1
DOI: 10.1088/1361-6528/aa7660
|
|
|
“Site-specific mapping of transition metal oxygen coordination in complex oxides”. Turner S, Egoavil R, Batuk M, Abakumov AA, Hadermann J, Verbeeck J, Van Tendeloo G, Applied physics letters 101, 241910 (2012). http://doi.org/10.1063/1.4770512
Abstract: We demonstrate site-specific mapping of the oxygen coordination number for transition metals in complex oxides using atomically resolved electron energy-loss spectroscopy in an aberration-corrected scanning transmission electron microscope. Pb2Sr2Bi2Fe6O16 contains iron with a constant Fe3+ valency in both octahedral and tetragonal pyramidal coordination and is selected to demonstrate the principle of site-specific coordination mapping. Analysis of the site-specific Fe-L2,3 data reveals distinct variations in the fine structure that are attributed to Fe in a six-fold (octahedron) or five-fold (distorted tetragonal pyramid) oxygen coordination. Using these variations, atomic resolution coordination maps are generated that are in excellent agreement with simulations.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 12
DOI: 10.1063/1.4770512
|
|
|
“Complex Microstructure and Magnetism in Polymorphic CaFeSeO”. Cassidy SJ, Batuk M, Batuk D, Hadermann J, Woodruff DN, Thompson AL, Clarke SJ, Inorganic chemistry 55, 10714 (2016). http://doi.org/10.1021/acs.inorgchem.6b01951
Abstract: The structural complexity of the antiferromagnetic oxide selenide CaFeSeO is described. The compound contains puckered FeSeO layers composed of FeSe2O2 tetrahedra sharing all their vertexes. Two polymorphs coexist that can be derived from an archetype BaZnSO structure by cooperative tilting of the FeSe2O2 tetrahedra. The polymorphs differ in the relative arrangement of the puckered layers of vertex-linked FeSe2O2 tetrahedra. In a noncentrosymmetric Cmc21 polymorph (a = 3.89684(2) A, b = 13.22054(8) A, c = 5.93625(2) A) the layers are related by the C-centering translation, while in a centrosymmetric Pmcn polymorph, with a similar cell metric (a = 3.89557(6) A, b = 13.2237(6) A, c = 5.9363(3) A), the layers are related by inversion. The compound shows long-range antiferromagnetic order below a Neel temperature of 159(1) K with both polymorphs showing antiferromagnetic coupling via Fe-O-Fe linkages and ferromagnetic coupling via Fe-Se-Fe linkages within the FeSeO layers. The magnetic susceptibility also shows evidence for weak ferromagnetism which is modeled in the refinements of the magnetic structure as arising from an uncompensated spin canting in the noncentrosymmetric polymorph. There is also a spin glass component to the magnetism which likely arises from the disordered regions of the structure evident in the transmission electron microscopy.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 6
DOI: 10.1021/acs.inorgchem.6b01951
|
|
|
“Bi(3n+1)Ti7Fe(3n-3)O(9n+11) Homologous Series: Slicing Perovskite Structure with Planar Interfaces Containing Anatase-like Chains”. Batuk D, Tsirlin AA, Filimonov DS, Zakharov KV, Volkova OS, Vasiliev A, Hadermann J, Abakumov AM, Inorganic chemistry 55, 1245 (2016). http://doi.org/10.1021/acs.inorgchem.5b02465
Abstract: The n = 3-6 members of a new perovskite-based homologous series Bi(3n+1)Ti7Fe(3n-3)O(9n+11) are reported. The crystal structure of the n = 3 Bi10Ti7Fe6O38 member is refined using a combination of X-ray and neutron powder diffraction data (a = 11.8511(2) A, b = 3.85076(4) A, c = 33.0722(6) A, S.G. Immm), unveiling the partially ordered distribution of Ti(4+) and Fe(3+) cations and indicating the presence of static random displacements of the Bi and O atoms. All Bi(3n+1)Ti7Fe(3n-3)O(9n+11) structures are composed of perovskite blocks separated by translational interfaces parallel to the (001)p perovskite planes. The thickness of the perovskite blocks increases with n, while the atomic arrangement at the interfaces remains the same. The interfaces comprise chains of double edge-sharing (Fe,Ti)O6 octahedra connected to the octahedra of the perovskite blocks by sharing edges and corners. This configuration shifts the adjacent perovskite blocks relative to each other over a vector (1/2)[110]p and creates S-shaped tunnels along the [010] direction. The tunnels accommodate double columns of the Bi(3+) cations, which stabilize the interfaces owing to the stereochemical activity of their lone electron pairs. The Bi(3n+1)Ti7Fe(3n-3)O(9n+11) structures can be formally considered either as intergrowths of perovskite modules and polysynthetically twinned modules of the Bi2Ti4O11 structure or as intergrowths of the 2D perovskite and 1D anatase fragments. Transmission electron microscopy (TEM) on Bi10Ti7Fe6O38 reveals that static atomic displacements of Bi and O inside the perovskite blocks are not completely random; they are cooperative, yet only short-range ordered. According to TEM, the interfaces can be laterally shifted with respect to each other over +/-1/3a, introducing an additional degree of disorder. Bi10Ti7Fe6O38 is paramagnetic in the 1.5-1000 K temperature range due to dilution of the magnetic Fe(3+) cations with nonmagnetic Ti(4+). The n = 3, 4 compounds demonstrate a high dielectric constant of 70-165 at room temperature.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 3
DOI: 10.1021/acs.inorgchem.5b02465
|
|
|
“Luminescence Property Upgrading via the Structure and Cation Changing in AgxEu(2–x)/3WO4and AgxGd(2–x)/3–0.3Eu0.3WO4”. Morozov VA, Batuk D, Batuk M, Basovich OM, Khaikina EG, Deyneko DV, Lazoryak BI, Leonidov II, Abakumov AM, Hadermann J, Chemistry of materials 29, 8811 (2017). http://doi.org/10.1021/acs.chemmater.7b03155
Abstract: The creation and ordering of A-cation vacancies and the effect of cation substitutions in the scheelite-type framework are investigated as a factor for controlling the scheelite-type structure and luminescence properties. AgxEu3+(2−x)/3□(1−2x)/3WO4 and AgxGd(2−x)/3−0.3Eu3+0.3□(1−2x)/3WO4 (x = 0.5−0) scheelite-type phases were synthesized by a solid state method, and their structures were investigated using a combination of transmission electron microscopy techniques and powder synchrotron X-ray diffraction. Transmission electron microscopy also revealed the (3 + 1)D incommensurately modulated character of AgxEu3+(2−x)/3□(1−2x)/3WO4 (x = 0.286, 0.2) phases. The crystal structures of the scheelite-based AgxEu3+(2−x)/3□(1−2x)/3WO4 (x = 0.5, 0.286, 0.2) red phosphors have been refined from high resolution synchrotron powder X-ray diffraction data. The luminescence properties of all phases under near-ultraviolet (n-UV) light have been investigated. The excitation spectra of AgxEu3+(2−x)/3□(1−2x)/3WO4 (x = 0.5, 0.286,0.2) phosphors show the strongest absorption at 395 nm, which matches well with the commercially available n-UV-emitting GaN-based LED chip. The excitation spectra of the Eu2/3□1/3WO4 and Gd0.367Eu0.30□1/3WO4 phases exhibit the highest contribution of the charge transfer band at 250 nm and thus the most efficient energy transfer mechanism between the host and the luminescent ion as compared to direct excitation. The emission spectra of all samples indicate an intense red emission due to the 5D0 → 7F2 transition of Eu3+. Concentration dependence of the 5D0 → 7F2 emission for AgxEu(2−x)/3□(1−2x)/3WO4 samples differs from the same dependence for the earlier studied NaxEu3+(2−x)/3□(1−2x)/3MoO4 (0 ≤ x ≤ 0.5) phases. The intensity of the 5D0 → 7F2 emission is reduced almost 7 times with decreasing x from 0.5 to 0, but it practically does not change in the range from x = 0.286 to x = 0.200. The emission spectra of Gd-containing samples show a completely different trend as compared to only Eu-containing samples. The Eu3+ emission under excitation of Eu3+(5L6) level (λex = 395 nm) increases more than 2.5 times with the increasing Gd3+ concentration from 0.2 (x = 0.5) to 0.3 (x = 0.2) in the AgxGd(2−x)/3−0.3Eu3+0.3□(1−2x)/3WO4, after which it remains almost constant for higher Gd3+ concentrations.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 7
DOI: 10.1021/acs.chemmater.7b03155
|
|
|
“Crystal structure study of manganese and titanium substituted BaLaFe2O6-δ”. Ben Hafsia A, Hendrickx M, Batuk M, Khitouni M, Hadermann J, Greneche J-M, Rammeh N, Journal of solid state chemistry 251, 186 (2017). http://doi.org/10.1016/j.jssc.2017.04.019
Abstract: Barium lanthanum ferrite and four Mn/Ti substituted materials were synthesized by the sol-gel method. The crystal structure of the materials was studied by a combination of X-ray powder diffraction, electron diffraction, scanning transmission electron microscopy and 57Fe Mössbauer spectrometry. BaLaFe2O6-δ has a cubic perovskite structure and Ba0.7La1.3FeMnO6-δ is distorted perovskite with the R-3c symmetry, both from electron diffraction and X-ray powder diffraction. However, according to transmission electron microscopy, the crystals of BaLaFeTiO6-δ, BaLaFeTi0.5Mn0.5O6-δ, and BaLaFe0.5Ti0.5MnO6-δ consist of nanodomains with different symmetries (Pm3m next to R-3c due to octahedral tilts), whereas the bulk X-ray powder diffraction patterns for these compounds correspond to the simple cubic structure. 57Fe Mössbauer spectrometry confirms that all materials contain high spin state Fe3+ ions which are strongly influenced by the chemical disorder
resulting from various cationic environments.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
DOI: 10.1016/j.jssc.2017.04.019
|
|
|
“Strength, toughness and aging stability of highly-translucent Y-TZP ceramics for dental restorations”. Zhang F, Inokoshi M, Batuk M, Hadermann J, Naert I, Van Meerbeek B, Vleugels J, Dental Materials 32, e327 (2016). http://doi.org/10.1016/j.dental.2016.09.025
Abstract: OBJECTIVE: The aim was to evaluate the optical properties, mechanical properties and aging stability of yttria-stabilized zirconia with different compositions, highlighting the influence of the alumina addition, Y2O3 content and La2O3 doping on the translucency. METHODS: Five different Y-TZP zirconia powders (3 commercially available and 2 experimentally modified) were sintered under the same conditions and characterized by X-ray diffraction with Rietveld analysis and scanning electron microscopy (SEM). Translucency (n=6/group) was measured with a color meter, allowing to calculate the translucency parameter (TP) and the contrast ratio (CR). Mechanical properties were appraised with four-point bending strength (n=10), single edge V-notched beam (SEVNB) fracture toughness (n=8) and Vickers hardness (n=10). The aging stability was evaluated by measuring the tetragonal to monoclinic transformation (n=3) after accelerated hydrothermal aging in steam at 134 degrees C, and the transformation curves were fitted by the Mehl-Avrami-Johnson (MAJ) equation. Data were analyzed by one-way ANOVA, followed by Tukey's HSD test (alpha=0.05). RESULTS: Lowering the alumina content below 0.25wt.% avoided the formation of alumina particles and therefore increased the translucency of 3Y-TZP ceramics, but the hydrothermal aging stability was reduced. A higher yttria content (5mol%) introduced about 50% cubic zirconia phase and gave rise to the most translucent and aging-resistant Y-TZP ceramics, but the fracture toughness and strength were considerably sacrificed. 0.2mol% La2O3 doping of 3Y-TZP tailored the grain boundary chemistry and significantly improved the aging resistance and translucency. Although the translucency improvement by La2O3 doping was less effective than for introducing a substantial amount of cubic zirconia, this strategy was able to maintain the mechanical properties of typical 3Y-TZP ceramics. SIGNIFICANCE: Three different approaches were compared to improve the translucency of 3Y-TZP ceramics.
Keywords: A1 Journal article; Electron Microscopy for Materials Science (EMAT);
Impact Factor: 4.07
DOI: 10.1016/j.dental.2016.09.025
|
|
|
“Effect of cation dopant radius on the hydrothermal stability of tetragonal zirconia: Grain boundary segregation and oxygen vacancy annihilation”. Zhang F, Batuk M, Hadermann J, Manfredi G, Mariën A, Vanmeensel K, Inokoshi M, Van Meerbeek B, Naert I, Vleugels J, Acta materialia 106, 48 (2016). http://doi.org/10.1016/j.actamat.2015.12.051
Abstract: The hydrothermal aging stability of 3Y-TZP-xM2O3 (M = La, Nd, Sc) was investigated as a function of 0.02–5 mol% M2O3 dopant content and correlated to the overall phase content, t-ZrO2 lattice parameters, grain size distribution, grain boundary chemistry and ionic conductivity.
The increased aging stability with increasing Sc2O3 content and the optimum content of 0.4–0.6 mol% Nd2O3 or 0.2–0.4 mol% La2O3, resulting in the highest aging resistance, could be directly related to the constituent phases and the lattice parameters of the remaining tetragonal zirconia.
At low M2O3 dopant contents ≤0.4 mol%, the different aging behavior of tetragonal zirconia was attributed to the defect structure of the zirconia grain boundary which was influenced by the dopant cation radius. It was observed that the grain boundary ionic resistivity and the aging resistance followed the same trend: La3+ > Nd3+ > Al3+ > Sc3+, proving that hydrothermal aging is driven by the diffusion of water-derived mobile species through the oxygen vacancies. Accordingly, we elucidated the underlying mechanism by which a larger trivalent cation segregating at the zirconia grain boundary resulted in a higher aging resistance.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 5.301
Times cited: 37
DOI: 10.1016/j.actamat.2015.12.051
|
|
|
“CO₂, electrochemical reduction with Zn-Al layered double hydroxide-loaded gas-diffusion electrode”. Nakazato R, Matsumoto K, Yamaguchi N, Cavallo M, Crocella V, Bonino F, Quintelier M, Hadermann J, Rosero-navarro NC, Miura A, Tadanaga K, Electrochemistry 91, 097003 (2023). http://doi.org/10.5796/ELECTROCHEMISTRY.23-00080
Abstract: Carbon dioxide electrochemical reduction (CO2ER) has attracted considerable attention as a technology to recycle CO2 into raw materials for chemicals using renewable energies. We recently found that Zn-Al layered double hydroxides (Zn-Al LDH) have the CO-forming CO2ER activity. However, the activity was only evaluated by using the liquid-phase CO2ER. In this study, Ni-Al and Ni-Fe LDHs as well as Zn-Al LDH were synthesized using a facile coprecipitation process and the gas-phase CO2ER with the LDH-loaded gas-diffusion electrode (GDE) was examined. The products were characterized by XRD, STEM-EDX, BF-TEM and ATR-IR spectroscopy. In the ATR-IR results, the interaction of CO2 with Zn-Al LDH showed a different carbonates evolution with respect to other LDHs, suggesting a different electrocatalytic activity. The LDH-loaded GDE was prepared by simple drop-casting of a catalyst ink onto carbon paper. For gas-phase CO2ER, only Zn-Al LDH exhibited the CO2ER activity for carbon monoxide (CO) formation. By using different potassium salt electrolytes affording neutral to strongly basic conditions, such as KCl, KHCO3 and KOH, the gas-phase CO2ER with Zn-Al LDH-loaded GDE showed 1.3 to 2.1 times higher partial current density for CO formation than the liquid-phase CO2ER.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
DOI: 10.5796/ELECTROCHEMISTRY.23-00080
|
|
|
Nakazato R, Matsumoto K, Yamaguchi N, Cavallo M, Crocella V, Bonino F, Quintelier M, Hadermann J, Rosero-Navarro NC, Miura A, Tadanaga K (2023) CO2 Electrochemical Reduction with Zn-Al Layered Double Hydroxide-Loaded Gas-Diffusion Electrode (Supporting Information)
Abstract: Carbon dioxide electrochemical reduction (CO2ER) has attracted considerable attention as a technology to recycle CO2 into raw materials for chemicals using renewable energies. We recently found that Zn-Al layered double hydroxides (Zn-Al LDH) have the CO-forming CO2ER activity. However, the activity was only evaluated by using the liquid-phase CO2ER. In this study, Ni-Al and Ni-Fe LDHs as well as Zn-Al LDH were synthesized using a facile coprecipitation process and the gas-phase CO2ER with the LDH-loaded gas-diffusion electrode (GDE) was examined. The products were characterized by XRD, STEM-EDX, BF-TEM and ATR-IR spectroscopy. In the ATR-IR results, the interaction of CO2 with Zn-Al LDH showed a different carbonates evolution with respect to other LDHs, suggesting a different electrocatalytic activity. The LDH-loaded GDE was prepared by simple drop-casting of a catalyst ink onto carbon paper. For gas-phase CO2ER, only Zn-Al LDH exhibited the CO2ER activity for carbon monoxide (CO) formation. By using different potassium salt electrolytes affording neutral to strongly basic conditions, such as KCl, KHCO3 and KOH, the gas-phase CO2ER with Zn-Al LDH-loaded GDE showed 1.3 to 2.1 times higher partial current density for CO formation than the liquid-phase CO2ER.
Keywords: Dataset; Electron microscopy for materials research (EMAT)
DOI: 10.50892/DATA.ELECTROCHEMISTRY.24069993
|
|
|
“The influence of synthesis method on the local structure and electrochemical properties of Li-rich/Mn-rich NMC cathode materials for Li-Ion batteries”. Hendrickx M, Paulus A, Kirsanova MA, Van Bael MK, Abakumov AM, Hardy A, Hadermann J, Nanomaterials 12, 2269 (2022). http://doi.org/10.3390/NANO12132269
Abstract: Electrochemical energy storage plays a vital role in combating global climate change. Nowadays lithium-ion battery technology remains the most prominent technology for rechargeable batteries. A key performance-limiting factor of lithium-ion batteries is the active material of the positive electrode (cathode). Lithium- and manganese-rich nickel manganese cobalt oxide (LMR-NMC) cathode materials for Li-ion batteries are extensively investigated due to their high specific discharge capacities (>280 mAh/g). However, these materials are prone to severe capacity and voltage fade, which deteriorates the electrochemical performance. Capacity and voltage fade are strongly correlated with the particle morphology and nano- and microstructure of LMR-NMCs. By selecting an adequate synthesis strategy, the particle morphology and structure can be controlled, as such steering the electrochemical properties. In this manuscript we comparatively assessed the morphology and nanostructure of LMR-NMC (Li1.2Ni0.13Mn0.54Co0.13O2) prepared via an environmentally friendly aqueous solution-gel and co-precipitation route, respectively. The solution-gel (SG) synthesized material shows a Ni-enriched spinel-type surface layer at the {200} facets, which, based on our post-mortem high-angle annual dark-field scanning transmission electron microscopy and selected-area electron diffraction analysis, could partly explain the retarded voltage fade compared to the co-precipitation (CP) synthesized material. In addition, deviations in voltage fade and capacity fade (the latter being larger for the SG material) could also be correlated with the different particle morphology obtained for both materials.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 5.3
DOI: 10.3390/NANO12132269
|
|
|
“Crystal structure of the group of optical materials Ln2MeGe4O12 (Me = Ca, Mn)”. Tarakina NV, Zubkov VG, Leonidov II, Tyutunnik AP, Surat LL, Hadermann J, Van Tendeloo G, Zeitschrift für Kristallographie , 401 (2009). http://doi.org/10.1524/zksu.2009.0059
Abstract: The crystal structure of the group of optical materials Ln2MeGe4O12, Ln = Eu, Gd, Dy-Lu, Y; Me = Ca, Mn and of the solid solution (Y1-xErx)2CaGe4O12 (x = 0 – 1), promising materials for photonics, has been studied in detail. The crystal structure of all compounds exhibit two alternating layers: one formed by Ln and Me atoms and another by cyclic [Ge4O12]8- anions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 7
DOI: 10.1524/zksu.2009.0059
|
|
|
“Grain-boundary engineering for aging and slow-crack-growth resistant zirconia”. Zhang F, Chevalier J, Olagnon C, Batuk M, Hadermann J, Van Meerbeek B, Vleugels J, Journal of dental research 96, 774 (2017). http://doi.org/10.1177/0022034517698661
Abstract: Ceramic materials are prone to slow crack growth, resulting in strength degradation over time. Although yttria-stabilized zirconia (Y-TZP) ceramics have higher crack resistance than other dental ceramics, their aging susceptibility threatens their long-term performance in aqueous environments such as the oral cavity. Unfortunately, increasing the aging resistance of Y-TZP ceramics normally reduces their crack resistance. Our recently conducted systematic study of doping 3Y-TZP with various trivalent cations revealed that lanthanum oxide (La2O3) and aluminum oxide (Al2O3) have the most potent effect to retard the aging kinetics of 3Y-TZP. In this study, the crack-propagation behavior of La2O3 and Al2O3 co-doped 3Y-TZP ceramics was investigated by double-torsion methods. The grain boundaries were examined using scanning transmission electron microscopy and energy-dispersive spectroscopy (STEM-EDS). Correlating these analytic data with hydrothermal aging studies using different doping systems, a strategy to strongly bind the segregated dopant cations with the oxygen vacancies at the zirconia-grain boundary was found to improve effectively the aging resistance of Y-TZP ceramics without affecting the resistance to crack propagation.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.755
Times cited: 3
DOI: 10.1177/0022034517698661
|
|
|
“Lanthanum-strontium cuprate as a promising cathodic matreila for solid oxide fuel cells”. Mazo GN, Savvin SN, Abakumov AM, Hadermann J, Dobrovol'skii YA, Leonova LS, Russian journal of electrochemistry 43, 436 (2007). http://doi.org/10.1134/S1023193507040106
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.828
Times cited: 8
DOI: 10.1134/S1023193507040106
|
|
|
“The synthesis and thermodynamic properties of strontium fluoromanganite Sr2.5Mn6O12.5-\deltaF2”. Kovba ML, Skolis YY, Abakumov AM, Hadermann J, Sukhushina IS, Russian journal of physical chemistry A 84, 2033 (2010). http://doi.org/10.1134/S0036024410120046
Abstract: The existence of the [SrF(0.8)O(0.1)](2.5)[Mn(6)O(12)] = Sr(2.5)Mn(6)O(12.5 – delta)F(2) compound was established in the SrO-Mn(2)O(3)-SrF(2) system at 900A degrees C and p(O(2)) = 1 atm. The crystal structure of strontium fluoromanganite was determined from the X-ray powder diffraction data, electron diffraction, and high-resolution electron microscopy. It can be described in the monoclynic system with four Miller hklm indices: hklm: H = h a* + k b* + l c (1) (*) + m q (1), q (1), q (1) = c (2) (*) = gamma c (1) (*) , gamma a parts per thousand 0.632, a a parts per thousand a a parts per thousand 9.72 , b a parts per thousand 9.55 , c (1) a parts per thousand 2.84 , c (2) a parts per thousand 4.49 , monoclinic angle gamma a parts per thousand 95.6A degrees. The electromotive force method with a solid fluorine ion electrolyte was used to refine the composition of fluoromanganite and determine the thermodynamic functions of its formation from phases neighboring in the phase diagram (SrMn(3)O(6), Mn(2)O(3), SrF(2), and oxygen), Delta GA degrees, kJ/mol = -(111.7 +/- 1.9) + (89.5 +/- 1.5) x 10(-3) T.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.581
Times cited: 1
DOI: 10.1134/S0036024410120046
|
|
|
“Effect of Bimetallic Pd/Pt Clusters on the Sensing Properties of Nanocrystalline SnO2 in the Detection of CO”. Malkov I V, Krivetskii VV, Potemkin D I, Zadesenets A V, Batuk MM, Hadermann J, Marikutsa A V, Rumyantseva MN, Gas'kov AM, Russian journal of inorganic chemistry 63, 1007 (2018). http://doi.org/10.1134/S0036023618080168
Abstract: Nanocrystalline tin dioxide modified by Pd and Pt clusters or by bimetallic PdPt nanoparticles was synthesized. Distribution of the modifers on the SnO2 surface was studied by high-resolution transmission electron microscopy and energy dispersive X-ray microanalysis with element distribution mapping. It was shown that the Pd/Pt ratio in bimetallic particles varies over a broad range and does not depend on the particle diameter. The effect of platinum metals on the reducibility of nanocrystalline SnO2 by hydrogen was determined. The sensing properties of the resulting materials towards 6.7 ppm CO in air were estimated in situ by electrical conductivity measurements. The sensor response of SnO2 modified with bimetallic PdPt particles was a superposition of the signals of samples with Pt and Pd clusters.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.787
Times cited: 3
DOI: 10.1134/S0036023618080168
|
|
|
“Chemistry and structure of anion-deficient perovskites with translational interfaces”. Abakumov AM, Hadermann J, Van Tendeloo G, Antipov EV, Journal of the American Ceramic Society 91, 1807 (2008). http://doi.org/10.1111/j.1551-2916.2008.02351.x
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.841
Times cited: 39
DOI: 10.1111/j.1551-2916.2008.02351.x
|
|
|
“Structure solution and refinement of metal-ion battery cathode materials using electron diffraction tomography”. Hadermann J, Abakumov AM, And Materials 75, 485 (2019). http://doi.org/10.1107/S2052520619008291
Abstract: The applicability of electron diffraction tomography to the structure solution and refinement of charged, discharged or cycled metal-ion battery positive electrode (cathode) materials is discussed in detail. As these materials are often only available in very small amounts as powders, the possibility of obtaining single-crystal data using electron diffraction tomography (EDT) provides unique access to crucial information complementary to X-ray diffraction, neutron diffraction and high-resolution transmission electron microscopy techniques. Using several examples, the ability of EDT to be used to detect lithium and refine its atomic position and occupancy, to solve the structure of materials ex situ at different states of charge and to obtain in situ data on structural changes occurring upon electrochemical cycling in liquid electrolyte is discussed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 2
DOI: 10.1107/S2052520619008291
|
|
|
“Transmission electron microscopy and structural phase transitions in anion-deficient perovskite-based oxides”. Hadermann J, Van Tendeloo G, Abakumov AM, Acta crystallographica: section A: foundations of crystallography 61, 77 (2005). http://doi.org/10.1107/S0108767304023013
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.725
Times cited: 18
DOI: 10.1107/S0108767304023013
|
|
|
“Crystal structure, phase transition, and magnetic ordering in perovskitelike Pb2-xBaxFe2O5 solid solutions”. Nikolaev IV, d' Hondt H, Abakumov AM, Hadermann J, Balagurov AM, Bobrikov IA, Sheptyakov DV, Pomjakushin VY, Pokholok KV, Filimonov DS, Van Tendeloo G, Antipov EV, Physical review : B : condensed matter and materials physics 78, 024426 (2008). http://doi.org/10.1103/PhysRevB.78.024426
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 29
DOI: 10.1103/PhysRevB.78.024426
|
|
|
“Spin ladder compound Pb0.55Cd0.45V2O5: synthesis and investigation”. Tsirlin AA, Shpanchenko RV, Antipov EV, Bougerol C, Hadermann J, Van Tendeloo G, Schnelle W, Rosner H, Physical review : B : condensed matter and materials physics 76, 104429 (2007). http://doi.org/10.1103/PhysRevB.76.104429
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 1
DOI: 10.1103/PhysRevB.76.104429
|
|
|
“Anisotropic magnetism and spin-dependent transport in Co nanoparticle embedded ZnO thin films”. Li DY, Zeng YJ, Pereira LMC, Batuk D, Hadermann J, Zhang YZ, Ye ZZ, Temst K, Vantomme A, Van Bael MJ, Van Haesendonck C;, Journal of applied physics 114, 033909 (2013). http://doi.org/10.1063/1.4815877
Abstract: Oriented Co nanoparticles were obtained by Co ion implantation in crystalline ZnO thin films grown by pulsed laser deposition. Transmission electron microscopy revealed the presence of elliptically shaped Co precipitates with nanometer size, which are embedded in the ZnO thin films, resulting in anisotropic magnetic behavior. The low-temperature resistance of the Co-implanted ZnO thin films follows the Efros-Shklovskii type variable-range-hopping. Large negative magnetoresistance (MR) exceeding 10% is observed in a magnetic field of 1 T at 2.5K and the negative MR survives up to 250K (0.3%). The negative MR reveals hysteresis as well as anisotropy that correlate well with the magnetic properties, clearly demonstrating the presence of spin-dependent transport. (C) 2013 AIP Publishing LLC.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.068
Times cited: 10
DOI: 10.1063/1.4815877
|
|