Abstract: We present a detailed analysis of the point-defect clustering in strained Si/Si(1-x)Ge(x)/(001)Si structures, including the interaction of the point defects with the strained interfaces and the sample surface during 400 kV electron irradiation at room temperature. Point-defect cluster formation is very sensitive to the type and magnitude of the strain in the Si and Si(1-x)Ge(x) layers. A small compressive strain (-0.3%) in the SiGe alloy causes an aggregation of vacancies in the form of metastable [110]-oriented chains. They are located on {113} planes and further recombine with interstitials. Tensile strain in the Si layer causes an aggregation of interstitial atoms in the forms of additional [110] rows which are inserted on {113} planes with [001]-split configurations. The chainlike configurations are characterized by a large outward lattice relaxation for interstitial rows (0.13 +/-0.01 nm) and a very small inward relaxation for vacancy chains (0.02+/-0.01 nm). A compressive strain higher than -0.5% strongly decreases point-defect generation inside the strained SiGe alloy due to the large positive value of the formation volume of a Frenkel pair. This leads to the suppression of point-defect clustering in a strained SiGe alloy so that SiGe relaxes via a diffusion of vacancies from the Si layer, giving rise to an intermixing at the Si/SiGe interface. In material with a 0.9% misfit a strongly increased flow of vacancies from the Si layer to the SiGe layer and an increased biaxial strain in SiGe bath promote the preferential aggregation of vacancies in the (001) plane, which relaxes to form intrinsic 60 degrees dislocation loops.

Abstract: High-resolution electron microscopy (HREM) studies of the microstructure and specific defects in hexagonal boron nitride (h-BN) precursors and cubic boron nitride (c-BN) crystals made under high-pressure high-temperature conditions revealed the presence of half-nanotubes at the edges of the h-BN particles. Their sp(3) bonding tendency could strongly influence the nucleation rates of c-BN. The atomic resolution at extended dislocations was insufficient to allow us to determine the stacking fault energy in the c-BN crystals. Its mean value of 191 +/- 15 mJ m(-2) is of the same order of magnitude as that of diamond. High-frequency (94 GHz) electron paramagnetic resonance studies on c-BN single crystals have produced new data on the D1 centres associated with the boron species. Ion-beam-induced luminescence measurements have indicated that c-BN is a very interesting luminescent material, which is characterized by four luminescence bands and exhibits a better resistance to ionizing radiation than CVD diamond.

Abstract: The results of an in situ transmission electron microscopy study of the formation of Co-silicides on patterned (001) Si substrates are discussed. It is shown that the results of the in situ heating experiments agreed very well with the data based on standard rapid thermal annealing experiments. Fast heating rates resulted in better definition of the silicide lines. Also, better lines were obtained for samples that received already a low-temperature ex situ anneal. A Ti cap layer gave rise to a higher degree of epitaxy in the CoSi2 silicide.

Abstract: Results are presented of in situ studies of 1 MeV electron irradiation induced (113) defect generation in silicon containing different types and concentrations of extrinsic point defects. A semiquantitative model is developed describing the influence of interfaces and stress fields and of extrinsic point defects on the (113) defect generation in silicon during irradiation. The theoretical results obtained are correlated with experimental data obtained on silicon uniformly doped with boron and phosphorus and with observations obtained by irradiating cross-sectional samples of wafers with highly doped surface layers. It is shown that in situ irradiation in a high voltage election microscope is a powerful tool for studying local point defect reactions in silicon. (C) 1995 The Institute of Materials.

Abstract: Convergent beam electron diffraction (CBED) is used in this study to investigate the stress distribution around shallow trench isolation (STI) structures. Attention is given to the influence of the different processing parameters and the width and spacing of the structures. The use of a wet or a dry pregate oxidation is found to have a strong influence on the stress behavior. Isolated lines show more stress, leading to the formation of defects in the silicon substrate if a wet pregate oxidation is used. The CBED analyses are compared with micro-Raman and bright-field transmission electron microscopy measurements. (C) 2001 The Electrochemical Society.

Abstract: Twin-domains of a b.c.c. crystalline phase with a = 0.29 nm have been found in a surface layer on surfaces of Al-Co decagonal quasicrystals and the coexisting tau(2)-Al13Co4 crystalline approximant. These surface layer domains are introduced during the preparation of electron microscopy thin films by ion milling.

Abstract: Multishell carbon nanotubules are studied by means of diffraction contrast dark field images. This results in an electron microscopy method for the determination of the sign of the chiral angles in carbon nanotubes. The method is justified by a reasoning either in direct space or in diffraction space. We also investigate a carbon nanotubule exhibiting a bend and we confront the observations with the heptagon-pentagon pair model.

Abstract: Infrared absorption spectra of polyhedral and platelet oxygen precipitates in silicon are analyzed using a modified Day-Thorpe approach [J. Phys.: Condens. Matter 11, 2551 (1999)]. The aspect ratio of the precipitates is determined by transmission electron microscopy analysis. The reduced spectral function and the stoichiometry of the precipitate are extracted from the absorption spectra and the amount of precipitated interstitial oxygen. The experimental absorption spectra can be divided in a set with a Frohlich frequency of around 1100 cm(-1) and in a set with a Frohlich frequency between 1110 and 1120 cm(-1). It is shown that the shift in the Frohlich frequency is not due to a differing stoichiometry, but to the detailed structure of the reduced spectral function. Inverse modeling of the spectra suggests that the oxide precipitates consist of substoichiometric SiOgamma with gamma=1.17+/-0.14. (C) 2002 American Institute of Physics.

Abstract: The reaction of a Ti (8 nm) capped Co film (15 nm) with a Si3N4 layer (150 nm) is studied after rapid thermal annealing at 660 degreesC for 120 s in a N-2 ambient. X-ray photoelectron spectroscopy, transmission electron microscopy, electron energy-loss spectroscopy, and Auger electron spectroscopy are used to study the reaction products. Combining the results of the different analyses yields a layer stack consisting of: TiO2/TiO/unreacted Co/(Ti,Co)(2)N/Co2Si, followed by amorphous Si3N4. The reaction mechanisms are discussed. Conclusions concerning the risk for degradation of nitride spacers in advanced devices are drawn. (C) 2000 American Institute of Physics. [S0003-6951(00)05248-7].

Abstract: A method has been developed to determine the interstitial and precipitated oxygen concentration in highly doped n- and p-type silicon. 10-30-mu m-thin silicon samples in a mechanical stress-free state and without alteration of the thermal history are prepared and measured with Fourier transform infrared spectroscopy at 5.5-6 K. The measured oxygen contents in the as-grown Si samples agree well with those obtained with gas fusion analysis. In the highly boron-doped samples, the interstitial oxygen can be determined down to 10(17) cm(-3). (C) 1999 American Institute of Physics. [S0034-6748(99)04909-6].