“Mechanical resonance of the austenite/martensite interface and the pinning of the martensitic microstructures by dislocations in Cu74.08Al23.13Be2.79”. Salje EKH, Zhang H, Idrissi H, Schryvers D, Carpenter MA, Moya X, Planes A, Physical review: B: condensed matter and materials physics 80, 134114 (2009). http://doi.org/10.1103/PhysRevB.80.134114
Abstract: A single crystal of Cu74.08Al23.13Be2.79 undergoes a martensitic phase transition at 246 and 232 K under heating and cooling, respectively. The phase fronts between the austenite and martensite regions of the sample are weakly mobile with a power-law resonance under external stress fields. Surprisingly, the martensite phase is elastically much harder than the austenite phase showing that interfaces between various crystallographic variants are strongly pinned and cannot be moved by external stress while the phase boundary between the austenite and martensite regions in the sample remains mobile. This unusual behavior was studied by dynamical mechanical analysis (DMA) and resonant ultrasound spectroscopy. The remnant strain, storage modulus, and internal friction were recorded simultaneously for different applied forces in DMA. With increasing forces, the remnant strain increases monotonously while the internal friction peak height shows a minimum at 300 mN. Transmission electron microscopy shows that the pinning is generated by dislocations which are inherited from the austenite phase.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 38
DOI: 10.1103/PhysRevB.80.134114
|
|
|
“Mechanical switching of nanoscale multiferroic phase boundaries”. Li YJ, Wang JJ, Ye JC, Ke XX, Gou GY, Wei Y, Xue F, Wang J, Wang CS, Peng RC, Deng XL, Yang Y, Ren XB, Chen LQ, Nan CW, Zhang JX;, Advanced functional materials 25, 3405 (2015). http://doi.org/10.1002/adfm.201500600
Abstract: Tuning the lattice degree of freedom in nanoscale functional crystals is critical to exploit the emerging functionalities such as piezoelectricity, shape-memory effect, or piezomagnetism, which are attributed to the intrinsic lattice-polar or lattice-spin coupling. Here it is reported that a mechanical probe can be a dynamic tool to switch the ferroic orders at the nanoscale multiferroic phase boundaries in BiFeO3 with a phase mixture, where the material can be reversibly transformed between the soft tetragonal-like and the hard rhombohedral-like structures. The microscopic origin of the nonvolatile mechanical switching of the multiferroic phase boundaries, coupled with a reversible 180 degrees rotation of the in-plane ferroelectric polarization, is the nanoscale pressure-induced elastic deformation and reconstruction of the spontaneous strain gradient across the multiferroic phase boundaries. The reversible control of the room-temperature multiple ferroic orders using a pure mechanical stimulus may bring us a new pathway to achieve the potential energy conversion and sensing applications.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.124
Times cited: 23
DOI: 10.1002/adfm.201500600
|
|
|
“Mechanical synthesis of high purity Cu-In-Se alloy nanopowder as precursor for printed CISe thin film solar cells”. Zaghi AE, Buffière M, Brammertz G, Batuk M, Lenaers N, Kniknie B, Hadermann J, Meuris M, Poortmans J, Vleugels J, Advanced powder technology 25, 1254 (2014). http://doi.org/10.1016/j.apt.2014.03.003
Abstract: Mechanical alloying and ball milling are low cost, up-scalable techniques for the preparation of high purity chalcogenide nanopowders to be used as precursor material for printing thin film solar cells. In this study, high purity copper indium selenium (Cu-In-Se) alloy nanopowders with 20-200 nm particle size were synthesized from macroscopic elemental Cu, In and Se powders via mechanical alloying and planetary ball milling. The particle size distribution, morphology, composition, and purity level of the synthesized Cu-In-Se alloy nanopowders were investigated. Thin Cu-In-Se alloy nanopowder ink coatings, deposited on Mo-coated glass substrates by doctor blading, were converted into a CuInSe2 semiconductor film by selenization heat treatment in Se vapor. The CuInSe2 film showed semiconducting band gap around 1 eV measured by photoluminescence spectroscopy. CuInSe2 absorber layer based thin film solar cell devices were fabricated to assess their performance. The solar cell device showed a total efficiency of 4.8%, as measured on 0.25 cm(2) area cell. (c) 2014 The Society of Powder Technology Japan. Published by Elsevier B.V. and The Society of Powder Technology Japan. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.659
Times cited: 10
DOI: 10.1016/j.apt.2014.03.003
|
|
|
“Mechanism for Ohmic contact formation on Si3N4 passivated AlGaN/GaN high-electron-mobility transistors”. Van Daele B, Van Tendeloo G, Derluyn J, Shrivastava P, Lorenz A, Leys MR, Germain M;, Applied physics letters 89, Artn 201908 (2006). http://doi.org/10.1063/1.2388889
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 15
DOI: 10.1063/1.2388889
|
|
|
“Mechanism of preferential orientation in sputter deposited titanium nitride and yttria-stabilized zirconia layers”. Mahieu S, Ghekiere P, de Winter G, Heirwegh S, Depla D, de Gryse R, Lebedev OI, Van Tendeloo G, Journal of crystal growth 279, 100 (2005). http://doi.org/10.1016/j.jcrysgro.2005.02.014
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.751
Times cited: 41
DOI: 10.1016/j.jcrysgro.2005.02.014
|
|
|
“A memory efficient method for fully three-dimensional object reconstruction with HAADF STEM”. Van den Broek W, Rosenauer A, Van Aert S, Sijbers J, van Dyck D, Ultramicroscopy 141, 22 (2014). http://doi.org/10.1016/j.ultramic.2014.03.008
Abstract: The conventional approach to object reconstruction through electron tomography is to reduce the three-dimensional problem to a series of independent two-dimensional slice-by-slice reconstructions. However, at atomic resolution the image of a single atom extends over many such slices and incorporating this image as prior knowledge in tomography or depth sectioning therefore requires a fully three-dimensional treatment. Unfortunately, the size of the three-dimensional projection operator scales highly unfavorably with object size and readily exceeds the available computer memory. In this paper, it is shown that for incoherent image formation the memory requirement can be reduced to the fundamental lower limit of the object size, both for tomography and depth sectioning. Furthermore, it is shown through multislice calculations that high angle annular dark field scanning transmission electron microscopy can be sufficiently incoherent for the reconstruction of single element nanocrystals, but that dynamical diffraction effects can cause classification problems if more than one element is present. (C) 2014 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 2.843
Times cited: 6
DOI: 10.1016/j.ultramic.2014.03.008
|
|
|
“A mercury-based “1201-0201&rdquo, intergrowth HgBa2La2Cu2O8+x: a 53K superconductor”. Huvé, M, Martin C, Van Tendeloo G, Maignan A, Michel C, Hervieu M, Raveau B, Solid state communications 90, 37 (1994)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.897
Times cited: 7
|
|
|
“A mercury based cuprate with the “2212&rdquo, structure: Hg2-x(Cu,Pr)xBa2PrCu2O8-\delta”. Martin C, Hervieu M, Van Tendeloo G, Goutenoire F, Michel C, Maignan A, Raveau B, Solid state communications 93, 53 (1995)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.897
Times cited: 6
|
|
|
“A mercury based superconducting cuprate, intergrowth of the 2201 and 1201 structures Tl2HgBa4Cu2O10+y”. Martin C, Huvé, M, Van Tendeloo G, Maignan A, Michel C, Hervieu M, Raveau B, Physica: C : superconductivity 212, 274 (1993)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.942
Times cited: 21
|
|
|
“The merging of silica-surfactant microspheres under hydrothermal conditions”. Liu S, Lebedev OI, Mertens M, Meynen V, Cool P, Van Tendeloo G, Vansant EF, Microporous and mesoporous materials: zeolites, clays, carbons and related materials 116, 141 (2008). http://doi.org/10.1016/j.micromeso.2008.03.034
Abstract: Post-synthesis hydrothermal treatments have been used to improve the quality of MCM-41 materials. In our latest work, merging of surfactant-containing silica microspheres during the hydrothermal treatments was observed. Mechanistic insights and the different stages that are involved in the merging process can be summarized as follows. First, the surfaces of the starting microspheres open up due to the dissolution of silica. Then the dissolved silica species provide mass source for the formation of particle necks connecting two neighboring microspheres. Gradually, surfaces of the starting microspheres are flattened to meet the needs of further growth of the necks. Finally, some chain-like highly-ordered mesoporous structures up to several micrometers are formed. The observed merging of the surfactant-containing microspheres is a re-assembling process, which is under the control of electrostatic force between the dissolved silica species and the surfactant cations. The occluded surfactant cations in the precursor spheres play important roles in the merging process.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 3.615
Times cited: 5
DOI: 10.1016/j.micromeso.2008.03.034
|
|
|
“Mesoporous material formed by acidic hydrothermal assembly of silicalite-1 precursor nanoparticles in the absence of meso-templates”. Stevens WJJ, Meynen V, Bruijn E, Lebedev OI, Van Tendeloo G, Cool P, Vansant EF, Microporous and mesoporous materials: zeolites, clays, carbons and related materials 110, 77 (2008). http://doi.org/10.1016/j.micromeso.2007.09.007
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 3.615
Times cited: 21
DOI: 10.1016/j.micromeso.2007.09.007
|
|
|
“Mesoseopic ordering in the 0.9 Pb(Mg1/3Nb2/3)O3-0.1 PbTiO3 relaxor ferroelectric : a HRTEM study”. Nistor LC, Ghica C, Van Tendeloo G, Physica status solidi: C: conferences and critical reviews 4, 736 (2007). http://doi.org/10.1002/pssc.200673753
Abstract: We report a microstructural and compositional study of a 90% Pb(Mg1/3Nb2/3)O-3 – 10% PbTiO3 ceramic sample. High resolution transmission electron microscopy (HRTEM) revealed the presence of compositional ordered nano-domains (1 – 4 mn), observable in two specific orientations, [0 (1) over bar 1] and [1 1 (2) over bar]. However, the visibility and the ordering degree of the nano-domains on the HRTEM images are not at all obvious. Fourier filtering of the images clearly revealed the ordered domains. Antiphase boundaries lying in the (111) planes separate them, while (100) and (111) facets separate the ordered domains from the disordered matrix. Their shape is plate-like, not uniformly spread in the disordered matrix. Their average size varies in different regions of the sample, most probably due to a non-uniform distribution of Ti, as observed by energy dispersive X-ray spectroscopy. (c) 2007 WILEY-VCH Verlag GmbH Co. KGaA, Weinheim.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 2
DOI: 10.1002/pssc.200673753
|
|
|
“Metal and composite nanocluster precipitate formation in silicon dioxide implanted with Sb+ ions”. Ignatova VA, Lebedev OI, Watjen U, van Vaeck L, van Landuyt J, Gijbels R, Adams F, Journal of applied physics 92, 4336 (2002). http://doi.org/10.1063/1.1508425
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 2.068
Times cited: 5
DOI: 10.1063/1.1508425
|
|
|
“Metal@COFs : covalent organic frameworks as templates for Pd nanoparticles and hydrogen storage properties of Pd@COF-102 hybrid material”. Kalidindi SB, Hyunchul O, Hirscher M, Esken D, Wiktor C, Turner S, Van Tendeloo G, Fischer RA, Chemistry: a European journal 18, 10848 (2012). http://doi.org/10.1002/chem.201201340
Abstract: Three-dimensional covalent organic frameworks (COFs) have been demonstrated as a new class of templates for nanoparticles. Photodecomposition of the [Pd(eta 3-C3H5)(eta 5-C5H5)]@COF-102 inclusion compound (synthesized by a gas-phase infiltration method) led to the formation of the Pd@COF-102 hybrid material. Advanced electron microscopy techniques (including high-angle annular dark-field scanning transmission electron microscopy and electron tomography) along with other conventional characterization techniques unambiguously showed that highly monodisperse Pd nanoparticles ((2.4 +/- 0.5) nm) were evenly distributed inside the COF-102 framework. The Pd@COF-102 hybrid material is a rare example of a metal-nanoparticle-loaded porous crystalline material with a very narrow size distribution without any larger agglomerates even at high loadings (30 wt %). Two samples with moderate Pd content (3.5 and 9.5 wt %) were used to study the hydrogen storage properties of the metal-decorated COF surface. The uptakes at room temperature from these samples were higher than those of similar systems such as Pd@metalorganic frameworks (MOFs). The studies show that the H2 capacities were enhanced by a factor of 2-3 through Pd impregnation on COF-102 at room temperature and 20 bar. This remarkable enhancement is not just due to Pd hydride formation and can be mainly ascribed to hydrogenation of residual organic compounds, such as bicyclopentadiene. The significantly higher reversible hydrogen storage capacity that comes from decomposed products of the employed organometallic Pd precursor suggests that this discovery may be relevant to the discussion of the spillover phenomenon in metal/MOFs and related systems.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.317
Times cited: 88
DOI: 10.1002/chem.201201340
|
|
|
“Metal-decorated multi-wall carbon nanotubes for low temperature gas sensing”. Espinosa EH, Lonescu R, Bittencourt C, Felten A, Erni R, Van Tendeloo G, Pireaux J-J, Llobet E, Thin solid films : an international journal on the science and technology of thin and thick films 515, 8322 (2007). http://doi.org/10.1016/j.tsf.2007.03.017
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.879
Times cited: 86
DOI: 10.1016/j.tsf.2007.03.017
|
|
|
“Metal to insulator transition in the n-type hollandite vanadate Pb1.6V8O16”. Maignan A, Lebedev OI, Van Tendeloo G, Martin C, Hebert S, Physical review : B : condensed matter and materials physics 82, 035122 (2010). http://doi.org/10.1103/PhysRevB.82.035122
Abstract: The transport and magnetic measurements of polycrystalline Pb1.6V8O16 hollandite reveal a concomitant metal to insulator and antiferromagnetic transition at TMI≈140 K. A clear localization is found below TMI, evidenced by a rapid increase in the absolute value of the negative Seebeck coefficient. The structural study by x-ray and transmission electron microscopy confirms the hollandite structure and shows that no structural transition occurs at TMI, ruling out a possible charge orbital ordering. The negative Seebeck coefficient observed from 50 K up to 900 K, with values reaching S=−38 μV K−1 at 900 K, is explained by the electron doping of ∼1.4e− in the V empty t2g orbitals responsible for the bad metal resistivity (ρ900 K∼2 mΩ cm). As this S value is close to that obtained by considering only the spin and orbital degeneracies, it is expected that |S| for such vanadates will not be sensitive at high temperature to the t2g band filling
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 10
DOI: 10.1103/PhysRevB.82.035122
|
|
|
“Metallic nanoparticles on plasma treated carbon nanotubes : $Nano2hybrids$”. Bittencourt C, Felten A, Douhard B, Colomer J-F, Van Tendeloo G, Drube W, Ghijsen J, Pireaux J-J, Surface science : a journal devoted to the physics and chemistry of interfaces
T2 –, International Conference on NANO-Structures Self Assembling, JUL 02-06, 2006, Aix en Provence, FRANCE 601, 2800 (2007). http://doi.org/10.1016/j.susc.2006.12.045
Abstract: Multi-wall carbon nanotubes (MWCNTs) were decorated with metal clusters by thermal evaporation. Transmission electron microscopy (TEM) shows that the nature and extent of metal coverage can be varied by plasma treating the MWCNT surface. The metal clusters on oxygen plasma treated arc-discharge MWCNTs have a more dense distribution than the clusters evaporated on as-synthesized are-discharge MWCNTs. In contrast, the plasma treatment did not affect the cluster distribution on CVD MWCNTs. Analyses of the valence band and the core levels by X-ray photoelectron spectroscopy suggest poor charge transfer between gold clusters and MWCNTs; on the contrary suggest good charge transfer between Ni clusters and MWCNTs. (c) 2007 Elsevier B. V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.062
Times cited: 44
DOI: 10.1016/j.susc.2006.12.045
|
|
|
“Metals@MOFs –, loading MOFs with metal nanoparticles for hybrid functions”. Meilikhov M, Yusenko K, Esken D, Turner S, Van Tendeloo G, Fischer RA, European journal of inorganic chemistry 2010, 3701 (2010). http://doi.org/10.1002/ejic.201000473
Abstract: Metalorganic frameworks (MOFs) as well as porous coordination polymers (PCPs) are porous, organicinorganic hybrid solids with zeolite-like structures and properties. Due to their extraordinarily high surface area and well defined pore structure MOFs can be used for the stabilization of metal nanoparticles with adjustable size. The embedded metal nanoparticles are still accessible for other reagents due to the high porosity of the MOF systems. This fact makes metal@MOF systems especially interesting for heterogeneous catalysis, gas storage and chemical sensing. This review compiles the cases of metal nanoparticles supported by or embedded into MOFs reported so far and the main aspects and problems associated with these novel nanocomposite systems. The determination of the dispersion and the location of the particles at the MOF support, the control of the loading degree and its effect on the catalytic activity of the system are discussed as well as the partial degradation of the MOF structure upon particle formation. Examples of the introduction of stabilizing groups into the MOF network that direct the loading and can influence the size and shape of the embedded particles are still rare and point into the possible direction of future investigations. Finally, the formation of bimetallic nanoparticles, which are stabilized and supported by a MOF network, will also be reviewed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.444
Times cited: 366
DOI: 10.1002/ejic.201000473
|
|
|
“The metastable Ni7\pm xS6 and mixed Ni6\pm x(S1-ySey)5 phases”. Liu Y, Norén L, Withers RL, Hadermann J, Van Tendeloo G, Garcia-Garcia J, Journal of solid state chemistry 170, 351 (2003). http://doi.org/10.1016/S0022-4596(02)00123-8
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 5
DOI: 10.1016/S0022-4596(02)00123-8
|
|
|
“A method to determine the local surface profile from reconstructed exit waves”. Wang A, Chen FR, Van Aert S, van Dyck D, Ultramicroscopy 111, 1352 (2011). http://doi.org/10.1016/j.ultramic.2011.04.005
Abstract: Reconstructed exit waves are useful to quantify unknown structure parameters such as the position and composition of the atom columns at atomic scale. Existing techniques provide a complex wave in a flat plane which is close to the plane where the electrons leave the atom columns. However, due to local deviation in the flatness of the exit surface, there will be an offset between the plane of reconstruction and the actual exit of a specific atom column. Using the channelling theory, it has been shown that this defocus offset can in principle be determined atom column-by-atom column. As such, the surface roughness could be quantified at atomic scale. However, the outcome strongly depends on the initial plane of reconstruction especially in a crystalline structure. If this plane is further away from the true exit, the waves of the atom columns become delocalized and interfere mutually which strongly complicates the interpretation of the exit wave in terms of the local structure. In this paper, we will study the delocalization with defocus using the channelling theory in a more systematic way.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 2.843
Times cited: 3
DOI: 10.1016/j.ultramic.2011.04.005
|
|
|
“Microscopic origin of dimerization in the CuO2 chains in Sr14Cu24O41”. Hiroi Z, Amelinckx S, Van Tendeloo G, Kobayashi N, Physical review : B : condensed matter and materials physics 54, 849 (1996). http://doi.org/10.1103/PhysRevB.54.15849
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.736
Times cited: 33
DOI: 10.1103/PhysRevB.54.15849
|
|
|
“Microstructural analysis of 9.7% efficient Cu2ZnSnSe4 thin film solar cells”. Buffière M, Brammertz G, Batuk M, Verbist C, Mangin D, Koble C, Hadermann J, Meuris M, Poortmans J, Applied physics letters 105, 183903 (2014). http://doi.org/10.1063/1.4901401
Abstract: This work presents a detailed analysis of the microstructure and the composition of our record Cu 2ZnSnSe4 (CZTSe)-CdS-ZnO solar cell with a total area efficiency of 9.7%. The average composition of the CZTSe crystallites is Cu 1.94 Zn 1.12Sn0.95Se3.99. Large crystals of ZnSe secondary phase (up to 400 nm diameter) are observed at the voids between the absorber and the back contact, while smaller ZnSe domains are segregated at the grain boundaries and close to the surface of the CZTSe grains. An underlying layer and some particles of Cu xSe are observed at the Mo-MoSe2-Cu2ZnSnSe4 interface. The free surface of the voids at the back interface is covered by an amorphous layer containing Cu, S, O, and C, while the presence of Cd, Na, and K is also observed in this region.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 17
DOI: 10.1063/1.4901401
|
|
|
“Microstructural and physical properties of layered manganite oxides related to the magnetoresistive perovskites”. Laffez P, Van Tendeloo G, Seshadri R, Hervieu M, Martin C, Maignan A, Raveau B, Journal of applied physics 80, 5850 (1996). http://doi.org/10.1063/1.363578
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.183
Times cited: 36
DOI: 10.1063/1.363578
|
|
|
“Microstructural aspects of the degradation behavior of SnO2-based anodes for aluminum electrolysis”. Vassiliev SY, Laurinavichute VK, Abakumov AM, Govorov VA, Bendovskii EB, Turner S, Filatov AY, Tarasovskii VP, Borzenko AG, Alekseeva AM, Antipov EV, Journal of the electrochemical society 157, C178 (2010). http://doi.org/10.1149/1.3327903
Abstract: The performance of SnO2 ceramic anodes doped with copper and antimony oxides was examined in cryolite alumina melts under anodic polarization at different cryolite ratios, temperatures, times, and current densities. The corroded part consists of a narrow strong corrosion zone at the anode surface with damage of the intergrain contacts and a large increase in porosity, a wider moderate corrosion zone with a smaller porosity increase, and a Cu depletion zone, where the ceramic retains its initial microstructure and a slight porosity increase occurs due to the removal of the Cu-rich inclusions. Mechanical destruction of the anode was never observed in the 10100 h tests. A microstructural model of the ceramic was suggested, consisting of grains with an Sb-doped SnO2 grain core surrounded by an ~200 to 500 nm grain shell where SnO2 was simultaneously doped with Sb and Mn+ (M=Cu2+,Fe3+,Al3+). The grains were separated by a few nanometers thick Cu-enriched grain boundaries. Different secondary charge carrier (holes) concentrations and electric conductivities in the grain core and grain shell result in a higher current density at the intergrain regions that leads to their profound degradation, especially in the low temperature acidic melt.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.259
Times cited: 3
DOI: 10.1149/1.3327903
|
|
|
“Microstructural characterization of diamond films deposited on c-BN crystals”. Nistor L, Buschmann V, Ralchenko V, Dinca G, Vlasov I, van Landuyt J, Fuess H, Diamond and related materials
T2 –, 10th European Conference on Diamond, Diamond-Like Materials, Nitrides, and Silicon Carbide (Diamond 1999), SEP 12-17, 1999, PRAGUE, CZECH REPUBLIC 9, 269 (2000). http://doi.org/10.1016/S0925-9635(99)00246-0
Abstract: The morphology and structure of diamond films, deposited on cubic boron nitride (c-BN) crystals by microwave-plasma-enhanced chemical vapor deposition, is studied by high-resolution scanning electron microscopy and micro-Raman spectroscopy. The c-BN crystals, with sizes of 200 to 350 mu m and grown by a high-temperature/high-pressure technique, were embedded in a copper holder, and used as substrates in deposition runs of 15 min to 5 h. The nucleation centers for diamond appear as well-shaped cuboctahedral crystallites, having diameters of approximately 100 nm. With increasing deposition time the diamond crystallites grew larger, forming islands on the c-BN faces. In some cases, epitaxial growth was observed on the (111) c-BN faces where coalesced particles gave rise to very smooth regions. A number of diamond crystals with peculiar shapes are observed, such as a pseudo five-fold symmetry due to multiple twinning. Moreover, both randomly distributed carbon tubes, about 100 nn in diameter and 1 mu m in length, and spherically shaped features are observed in samples prepared under the typical conditions of diamond deposition, this effect being ascribed to the influence of plasma-sputtered copper contamination. Quite unusual diamond crystals with a deep, pyramidal-shaped hole in the middle grew on the copper substrate between the c-BN crystals. (C) 2000 Elsevier Science S.A. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.561
Times cited: 9
DOI: 10.1016/S0925-9635(99)00246-0
|
|
|
“Microstructural dependence on middle eigenvalue in Ti-Ni-Au”. Shi H, Delville R, Srivastava V, James RD, Schryvers D, Journal of alloys and compounds 582, 703 (2013). http://doi.org/10.1016/j.jallcom.2013.08.132
Abstract: The microstructure of various compounds of the Ti-Ni-Au alloy system is investigated by transmission electron microscopy in relation with changing lattice parameters improving the compatibility conditions between austenite and martensite expressed by the lambda(2) = 1 equation based on the Geometrically NonLinear Theory of Martensite (GNLTM). Although local differences in microstructure are observed, when increasing the gold content compound twins are replaced by Type I twins, while twinned lamellar structures are replaced by untwinned plates and self-accommodating structures when lambda(2) = 1 is approached, all confirming the predictions of the GNLTM. (c) 2013 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.133
Times cited: 8
DOI: 10.1016/j.jallcom.2013.08.132
|
|
|
“Microstructural investigation of BaTiO3 thin films deposited on (001) MgO”. Lei CH, Van Tendeloo G, Siegert M, Schubert J, Journal of materials research 17, 1923 (2002). http://doi.org/10.1557/JMR.2002.0285
Abstract: The microstructure of BaTiO3 thin films, epitaxially deposited on (001) MgO by pulsed laser ablation, has been investigated by transmission electron microscopy. The films are always c-axis-orientated, but dislocations, {111} stacking faults, and antiphase boundaries are frequently observed. Conventional TEM and high-resolution microscopy allow one to deduce the Burgers vectors of dislocations as b(1) = <100> or b(2) = <110>, both being perfect dislocations. Most extrinsic stacking faults are ending at 1/3<112> or 1/3<111> partial dislocations; the displacement vector of the antiphase boundaries is 1/2<101>. Studying the interfacial structure by means of zone images taken along [100] and [110] shows that the misfit is mainly released by dislocations with Burgers vectors of 1/2<110> and 1/2<101>.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.673
Times cited: 8
DOI: 10.1557/JMR.2002.0285
|
|
|
“Microstructural mechanism of development in photothermographic materials”. Potapov PL, Schryvers D, Strijckers H, van Roost C, The journal of imaging science and technology 47, 115 (2003)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.348
|
|
|
“Microstructural study of equiatomic PtTi martensite and the discovery of a new long-period structure”. Rotaru G-M, Tirry W, Sittner P, van Humbeeck J, Schryvers D, Acta materialia 55, 4447 (2007). http://doi.org/10.1016/j.actamat.2007.04.010
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.301
Times cited: 7
DOI: 10.1016/j.actamat.2007.04.010
|
|
|
“A microstructural study of the thermal stability of atomic layer deposited Al2O3 thin films”. Nistor LC, Richard O, Zhao O, Bender H, Stesmans A, Van Tendeloo G, Institute of physics conference series
T2 –, Microscopy of semiconducting materials , 397 (2003)
Abstract: The thermal stability of amorphous Al2O3 films (similar to8 and 80 nut thick) deposited by atomic layer deposition on HF-last and thin SiO2 covered (001) Si substrates is studied by transmission electron microscopy. The layers are in- and ex-situ annealed in the same temperature range.