“Annular dark-field transmission electron microscopy for low contrast materials”. Leroux F, Bladt E, Timmermans J-P, Van Tendeloo G, Bals S, Microscopy and microanalysis 19, 629 (2013). http://doi.org/10.1017/S1431927613000020
Abstract: Imaging soft matter by transmission electron microscopy (TEM) is anything but straightforward. Recently, interest has grown in developing alternative imaging modes that generate contrast without additional staining. Here, we present a dark-field TEM technique based on the use of an annular objective aperture. Our experiments demonstrate an increase in both contrast and signal-to-noise ratio in comparison to conventional bright-field TEM. The proposed technique is easy to implement and offers an alternative imaging mode to investigate soft matter.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.891
Times cited: 5
DOI: 10.1017/S1431927613000020
|
|
|
“Atomic resolution mapping using quantitative high-angle annular dark field scanning transmission electron microscopy”. Van Aert S, Verbeeck J, Bals S, Erni R, van Dyck D, Van Tendeloo G, Microscopy and microanalysis 15, 464 (2009). http://doi.org/10.1017/S1431927609093957
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 1.891
Times cited: 1
DOI: 10.1017/S1431927609093957
|
|
|
“Chemical microcharacterization of ultrathin iodide conversion layers and adsorbed thiocyanate surface layers on silver halide microcrystals with time-of-flight SIMS”. Verlinden G, Gijbels R, Geuens I, Microscopy and microanalysis 8, 216 (2002). http://doi.org/10.1017/S1431927602020159
Abstract: The technique of imaging time-of-flight secondary ion mass spectrometry (TOF-SIMS) and dual beam depth,profiling has been used to study the composition of the surface of tabular silver halide microcrystals. Analysis of individual microcrystals with a size well below 1 mum from a given emulsion is possible. The method is successfully applied for the characterization of silver halide microcrystals with subpercent global iodide concentrations confined in surface layers with a thickness below 5 nm. The developed TOF-SIMS analytical procedure is explicitly demonstrated for the molecular imaging of adsorbed thiocyanate layers (SCN) at crystal surfaces of individual crystals and for the differentiation of iodide conversion layers synthesized with KI and with AgI micrates (nanocrystals with a size between 10 and 50 nm). It can be concluded that TOF-SIMS as a microanalytical, surface-sensitive technique has some unique properties over other analytical techniques for the study of complex structured surface layers of silver halide microcrystals. This offers valuable information to support the synthesis of future photographic emulsions.
Keywords: A1 Journal article; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 1.891
Times cited: 1
DOI: 10.1017/S1431927602020159
|
|
|
“Computational aspects in quantitative EELS”. Verbeeck J, Van Aert S, Zhang L, Haiyan T, Schattschneider P, Rosenauer A, Microscopy and microanalysis 16, 240 (2010). http://doi.org/10.1017/S143192761005511X
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.891
DOI: 10.1017/S143192761005511X
|
|
|
“EELS investigations of different niobium oxide phases”. Bach D, Störmer H, Schneider R, Gerthsen D, Verbeeck J, Microscopy and microanalysis 12, 416 (2006). http://doi.org/10.1017/S1431927606060521
Abstract: Electron energy loss spectra in conjunction with near-edge fine structures of purely stoichiometric niobium monoxide (NbO) and niobium pentoxide (Nb2O5) reference materials were recorded. The structures of the niobium oxide reference materials were checked by selected area electron diffraction to ensure a proper assignment of the fine structures. NbO and Nb2O5 show clearly different energy loss near-edge fine structures of the Nb-M-4,M-5 and -M-2,M-3 edges and of the O-K edge, reflecting the specific local environments of the ionized atoms. To distinguish the two oxides in a quantitative manner, the intensities under the Nb-M-4,M-5 as well as Nb-M-2,M-3 edges and the O-K edge were measured and their ratios calculated. k-factors were also derived from these measurements.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.891
Times cited: 50
DOI: 10.1017/S1431927606060521
|
|
|
“EELS of niobium and stoichiometric niobium-oxide phases: part 1: plasmon and Near-edges fine structure”. Bach D, Schneider R, Gerthsen D, Verbeeck J, Sigle W, Microscopy and microanalysis 15, 505 (2009). http://doi.org/10.1017/S143192760999105X
Abstract: A comprehensive electron energy-loss spectroscopy study of niobium (Nb) and stable Nb-oxide phases (NbO, NbO2, Nb2O5) was carried out. In this work (Part I), the plasmons and energy-loss near-edge structures (ELNES) of all relevant Nb edges (Nb-N2,3, Nb-M4,5, Nb-M2,3, Nb-M1, and Nb-L2,3) up to energy losses of about 2600 eV and the O-K edge are analyzed with respect to achieving characteristic fingerprints of Nb in different formal oxidation states (0 for metallic Nb, +2 for NbO, +4 for NbO2, and +5 for Nb2O5). Chemical shifts of the Nb-N2,3, Nb-M4,5, Nb-M2,3, and Nb-L2,3 edges are extracted from the spectra that amount to about 4 eV as the oxidation state increases from 0 for Nb to +5 for Nb2O5. Four different microscopes, including a 200 keV ZEISS Libra with monochromator, were used. The corresponding wide range of experimental parameters with respect to the primary electron energy, convergence, and collection semi-angles as well as energy resolution allows an assessment of the influence of the experimental setup on the ELNES of the different edges. Finally, the intensity of the Nb-L2,3 white-line edges is correlated with niobium 4d-state occupancy in the different reference materials.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.891
Times cited: 55
DOI: 10.1017/S143192760999105X
|
|
|
“Fully automated measurement of the modulation transfer function of charge-coupled devices above the Nyquist frequency”. van den Broek W, Van Aert S, van Dyck D, Microscopy and microanalysis 18, 336 (2012). http://doi.org/10.1017/S1431927611012633
Abstract: The charge-coupled devices used in electron microscopy are coated with a scintillating crystal that gives rise to a severe modulation transfer function (MTF). Exact knowledge of the MTF is imperative for a good correspondence between image simulation and experiment. We present a practical method to measure the MTF above the Nyquist frequency from the beam blocker's shadow image. The image processing has been fully automated and the program is made public. The method is successfully tested on three cameras with various beam blocker shapes.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 1.891
Times cited: 15
DOI: 10.1017/S1431927611012633
|
|
|
“High-quality sample preparation by low kV FIB thinning for analytical TEM measurements”. Bals S, Tirry W, Geurts R, Yang Z, Schryvers D, Microscopy and microanalysis 13, 80 (2007). http://doi.org/10.1017/S1431927607070018
Abstract: Focused ion beam specimen preparation has been used for NiTi samples and SrTiO(3)/SrRuO(3) multilayers with prevention of surface amorphization and Ga implantation by a 2-kV cleaning procedure. Transmission electron microscopy techniques show that the samples are of high quality with a controlled thickness over large scales. Furthermore, preferential thinning effects in multicompounds are avoided, which is important when analytical transmission electron microscopy measurements need to be interpreted in a quantitative manner. The results are compared to similar measurements acquired for samples obtained using conventional preparation techniques such as electropolishing for alloys and ion milling for oxides.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.891
Times cited: 82
DOI: 10.1017/S1431927607070018
|
|
|
“Intergrowth of components and ramps in coffin-shaped ZSM-5 zeolite crystals unraveled by focused ion beam-assisted transmission electron microscopy”. Lu J, Roeffaers MBJ, Bartholomeeusen E, Sels BF, Schryvers D, Microscopy and microanalysis 20, 42 (2014). http://doi.org/10.1017/S1431927613013731
Abstract: Scanning electron microscopy, focused ion beam (FIB), and transmission electron microscopy are combined to study the intergrowth of 90 degrees rotational components and of ramps in coffin-shaped ZSM-5 crystals. The 90 degrees rotational boundaries with local zig-zag features between different intergrowth components are observed in the main part of crystal. Also a new kind of displacement boundary is described. At the displacement boundary there is a shift of the unit cells along the boundary without a change in orientation. Based on lamellae prepared with FIB from different positions of the ramps and crystal, the orientation relationships between ramps and the main part of the crystal are studied and the three-dimensional morphology and growth mechanism of the ramp are illustrated.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.891
Times cited: 7
DOI: 10.1017/S1431927613013731
|
|
|
“Microstructure of surface and subsurface layers of a Ni-Ti shape memory microwire”. Tian H, Schryvers D, Shabalovskaya S, van Humbeeck J, Microscopy and microanalysis 15, 62 (2009). http://doi.org/10.1017/S1431927609090059
Abstract: The microstructure of a 55 Êm diameter, cold-worked Ni-Ti microwire is investigated by different transmission electron microscopy techniques. The surface consists of a few hundred nanometer thick oxide layer composed of TiO and TiO2 with a small fraction of inhomogeneously distributed Ni. The interior of the wire has a core-shell structure with primarily B2 grains in the 1 Êm thick shell, and heavily twinned B19 martensite in the core. This core-shell structure can be explained by a concentration gradient of the alloying elements resulting in a structure separation due to the strong temperature dependence of the martensitic start temperature. Moreover, in between the B2 part of the metallic core-shell and the oxide layer, a Ni3Ti interfacial layer is detected.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.891
Times cited: 15
DOI: 10.1017/S1431927609090059
|
|
|
“Optimal sample preparation to characterize corrosion in historical photographs with analytical TEM”. Grieten E, Caen J, Schryvers D, Microscopy and microanalysis 20, 1585 (2014). http://doi.org/10.1017/S1431927614012860
Abstract: An alternative focused ion beam preparation method is used for sampling historical photographs containing metallic nanoparticles in a polymer matrix. We use the preparation steps of classical ultra-microtomy with an alternative final sectioning with a focused ion beam. Transmission electron microscopy techniques show that the lamella has a uniform thickness, which is an important factor for analytical transmission electron microscopy. Furthermore, the method maintains the spatial distribution of nanoparticles in the soft matrix. The results are compared with traditional preparation techniques such as ultra-microtomy and classical focused ion beam milling.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Antwerp Cultural Heritage Sciences (ARCHES)
Impact Factor: 1.891
DOI: 10.1017/S1431927614012860
|
|
|
“Physical limits on atomic resolution”. van Dyck D, Van Aert S, den Dekker AJ, Microscopy and microanalysis 10, 153 (2004). http://doi.org/10.1017/S143192760404036X
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 1.891
Times cited: 14
DOI: 10.1017/S143192760404036X
|
|
|
“Point defect clusters and dislocations in FIB irradiated nanocrystalline aluminum films : an electron tomography and aberration-corrected high-resolution ADF-STEM study”. Idrissi H, Turner S, Mitsuhara M, Wang B, Hata S, Coulombier M, Raskin J-P, Pardoen T, Van Tendeloo G, Schryvers D, Microscopy and microanalysis 17, 983 (2011). http://doi.org/10.1017/S143192761101213X
Abstract: Focused ion beam (FIB) induced damage in nanocrystalline Al thin films has been characterized using advanced transmission electron microscopy techniques. Electron tomography was used to analyze the three-dimensional distribution of point defect clusters induced by FIB milling, as well as their interaction with preexisting dislocations generated by internal stresses in the Al films. The atomic structure of interstitial Frank loops induced by irradiation, as well as the core structure of Frank dislocations, has been resolved with aberration-corrected high-resolution annular dark-field scanning TEM. The combination of both techniques constitutes a powerful tool for the study of the intrinsic structural properties of point defect clusters as well as the interaction of these defects with preexisting or deformation dislocations in irradiated bulk or nanostructured materials.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.891
Times cited: 25
DOI: 10.1017/S143192761101213X
|
|
|
“Structural, chemical and electronic characterization of ceramic materials using quantitative (scanning) transmission electron microscopy”. Bals S, Van Aert S, Verbeeck J, Van Tendeloo G, Microscopy and microanalysis 13, 332 (2007). http://doi.org/10.1017/S1431927607081664
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.891
DOI: 10.1017/S1431927607081664
|
|
|
“TEM annular objective apertures fabricated by FIB”. Bals S, Radmilovic V, Kisielowski C, Microscopy and microanalysis 10, 1148 (2004). http://doi.org/10.1017/S1431927604881765
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.891
DOI: 10.1017/S1431927604881765
|
|
|
“Three-dimensional analysis of carbon nanotube networks in interconnects by electron tomography without missing wedge artifacts”. Ke X, Bals S, Cott D, Hantschel T, Bender H, Van Tendeloo G, Microscopy and microanalysis 16, 210 (2010). http://doi.org/10.1017/S1431927609991371
Abstract: The three-dimensional (3D) distribution of carbon nanotubes (CNTs) grown inside semiconductor contact holes is studied by electron tomography. The use of a specialized tomography holder results in an angular tilt range of ±90°, which means that the so-called missing wedge is absent. The transmission electron microscopy (TEM) sample for this purpose consists of a micropillar that is prepared by a dedicated procedure using the focused ion beam (FIB) but keeping the CNTs intact. The 3D results are combined with energy dispersive X-ray spectroscopy (EDS) to study the relation between the CNTs and the catalyst particles used during their growth. The reconstruction, based on the full range of tilt angles, is compared with a reconstruction where a missing wedge is present. This clearly illustates that the missing wedge will lead to an unreliable interpretation and will limit quantitative studies
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.891
Times cited: 42
DOI: 10.1017/S1431927609991371
|
|
|
“Towards quantitative EDX results in 3 dimensions”. Goris B, Freitag B, Zanaga D, Bladt E, Altantzis T, Ringnalda J, Bals S, Microscopy and microanalysis 20, 766 (2014). http://doi.org/10.1017/S1431927614005558
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.891
DOI: 10.1017/S1431927614005558
|
|
|
“Ultra-high resolution electron tomography for materials science : a roadmap”. Batenburg KJ, Bals S, Van Aert S, Roelandts T, Sijbers J, Microscopy and microanalysis 17, 934 (2011). http://doi.org/10.1017/S143192761100554X
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 1.891
DOI: 10.1017/S143192761100554X
|
|
|
“Wet-STEM tomography : principles, potentialities and limitations”. Masenelli-Varlot K, Malchere A, Ferreira J, Heidari Mezerji H, Bals S, Messaoudi C, Garrido SM, Microscopy and microanalysis 20, 366 (2014). http://doi.org/10.1017/S1431927614000105
Abstract: The characterization of biological and inorganic materials by determining their three-dimensional structure in conditions closer to their native state is a major challenge of technological research. Environmental scanning electron microscopy (ESEM) provides access to the observation of hydrated samples in water environments. Here, we present a specific device for ESEM in the scanning transmission electron microscopy mode, allowing the acquisition of tilt-series suitable for tomographic reconstructions. The resolution which can be obtained with this device is first determined. Then, we demonstrate the feasibility of tomography on wet materials. The example studied here is hydrophilic mesoporous silica (MCM-41). Finally, the minimum thickness of water which can be detected is calculated from Monte Carlo simulations and compared with the resolution expected in the tomograms.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.891
Times cited: 9
DOI: 10.1017/S1431927614000105
|
|
|
“The incorporation of nanoparticles into conventional glass-ionomer dental restorative cements”. Gjorgievska E, Van Tendeloo G, Nicholson JW, Coleman NJ, Slipper IJ, Booth S, Microscopy and microanalysis 21, 392 (2015). http://doi.org/10.1017/S1431927615000057
Abstract: Conventional glass-ionomer cements (GICs) are popular restorative materials, but their use is limited by their relatively low mechanical strength. This paper reports an attempt to improve these materials by incorporation of 10 wt% of three different types of nanoparticles, aluminum oxide, zirconium oxide, and titanium dioxide, into two commercial GICs (ChemFil((R)) Rock and EQUIA (TM) Fil). The results indicate that the nanoparticles readily dispersed into the cement matrix by hand mixing and reduced the porosity of set cements by filling the empty spaces between the glass particles. Both cements showed no significant difference in compressive strength with added alumina, and ChemFil((R)) Rock also showed no significant difference with zirconia. By contrast, ChemFil((R)) Rock showed significantly higher compressive strength with added titania, and EQUIA (TM) Fil showed significantly higher compressive strength with both zirconia and titania. Fewer air voids were observed in all nanoparticle-containing cements and this, in turn, reduced the development of cracks within the matrix of the cements. These changes in microstructure provide a likely reason for the observed increases in compressive strength, and overall the addition of nanoparticles appears to be a promising strategy for improving the physical properties of GICs.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.891
Times cited: 15
DOI: 10.1017/S1431927615000057
|
|
|
“Melamine–Formaldehyde Microcapsules: Micro- and Nanostructural Characterization with Electron Microscopy”. Heidari H, Rivero G, Idrissi H, Ramachandran D, Cakir S, Egoavil R, Kurttepeli M, Crabbé, AC, Hauffman T, Terryn H, Du Prez F, Schryvers D, Microscopy and microanalysis 22, 1222 (2016). http://doi.org/10.1017/S1431927616012484
Abstract: A systematic study has been carried out to compare the surface morphology, shell thickness, mechanical properties, and binding behavior of melamine–formaldehyde microcapsules of 5–30 μm diameter size with various amounts of core content by using scanning and transmission electron microscopy including electron tomography, in situ nanomechanical tensile testing, and electron energy-loss spectroscopy. It is found that porosities are present on the outside surface of the capsule shell, but not on the inner surface of the shell. Nanomechanical tensile tests on the capsule shells reveal that Young’s modulus of the shell material is higher than that of bulk melamine–formaldehyde and that the shells exhibit a larger fracture strain compared with the bulk. Core-loss elemental analysis of microcapsules embedded in epoxy indicates that during the curing process, the microcapsule-matrix interface remains uniform and the epoxy matrix penetrates into the surface micro-porosities of the capsule shells.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.891
Times cited: 2
DOI: 10.1017/S1431927616012484
|
|
|
“Getting the best from an imperfect detector : an alternative normalisation procedure for quantitative HAADF STEM”. Jones L, Martinez GT, Béché, A, Van Aert S, Nellist PD, Microscopy and microanalysis 20, 126 (2014). http://doi.org/10.1017/S1431927614002359
Keywords: A1 Journal article; Engineering Management (ENM); Electron microscopy for materials research (EMAT)
Impact Factor: 1.891
DOI: 10.1017/S1431927614002359
|
|
|
“Microanalysis (micro-XRF, micro-XANES, and micro-XRD) of a tertiary sediment using microfocused synchrotron radiation”. Denecke MA, Somogyi A, Janssens K, Simon R, Dardenne K, Noseck U, Microscopy and microanalysis 13, 165 (2007). http://doi.org/10.1017/S1431927607070316
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 1.891
Times cited: 31
DOI: 10.1017/S1431927607070316
|
|
|
“PXRF, \mu-XRF, vacuum \mu-XRF, and EPMA analysis of Email Champlevé, objects present in Belgian museums”. van der Linden V, Meesdom E, Devos A, van Dooren R, Nieuwdorp H, Janssen E, Balace S, Vekemans B, Vincze L, Janssens K, Microscopy and microanalysis 17, 674 (2011). http://doi.org/10.1017/S1431927611011950
Abstract: The enamel of 20 Email Champlevé objects dating between the 12th and 19th centuries was investigated by means of microscopic and portable X-ray fluorescence analysis (μ-XRF and PXRF). Seven of these objects were microsampled and the fragments were analyzed with electron probe microanalysis (EPMA) and vacuum μ-XRF to obtain quantitative data about the composition of the glass used to produce these enameled objects. As a result of the evolution of the raw materials employed to produce the base glass, three different compositional groups could be discriminated. The first group consisted of soda-lime-silica glass with a sodium source of mineral origin (with low K content) that was opacified by addition of calcium antimonate crystals. This type of glass was only used in objects made in the 12th century. Email Champlevé objects from the beginning of the 13th century onward were enameled with soda-lime-silica glass with a sodium source of vegetal origin. This type of glass, which has a higher potassium content, was opacified with SnO2 crystals. The glass used for 19th century Email Champlevé artifacts was produced with synthetic and purified components resulting in a different chemical composition compared to the other groups. Although the four analytical techniques employed in this study have their own specific characteristics, they were all found to be suitable for classifying the objects into the different chronological categories.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 1.891
Times cited: 9
DOI: 10.1017/S1431927611011950
|
|
|
“Efficient Phase Contrast Imaging via Electron Ptychography, a Tutorial”. Pennycook TJ, Martinez GT, O'Leary CM, Yang H, Nellist PD, Microscopy and microanalysis 25, 2684 (2019). http://doi.org/10.1017/S1431927619014156
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
DOI: 10.1017/S1431927619014156
|
|
|
“Fast pixelated detectors in scanning transmission electron microscopy. Part I: data acquisition, live processing, and storage”. Nord M, Webster RWH, Paton KA, McVitie S, McGrouther D, MacLaren I, Paterson GW, Microscopy And Microanalysis 26, Pii S1431927620001713 (2020). http://doi.org/10.1017/S1431927620001713
Abstract: The use of fast pixelated detectors and direct electron detection technology is revolutionizing many aspects of scanning transmission electron microscopy (STEM). The widespread adoption of these new technologies is impeded by the technical challenges associated with them. These include issues related to hardware control, and the acquisition, real-time processing and visualization, and storage of data from such detectors. We discuss these problems and present software solutions for them, with a view to making the benefits of new detectors in the context of STEM more accessible. Throughout, we provide examples of the application of the technologies presented, using data from a Medipix3 direct electron detector. Most of our software are available under an open source licence, permitting transparency of the implemented algorithms, and allowing the community to freely use and further improve upon them.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.8
Times cited: 4
DOI: 10.1017/S1431927620001713
|
|
|
“Fast pixelated detectors in scanning transmission electron microscopy. part II : post-acquisition data processing, visualization, and structural characterization”. Paterson GW, Webster RWH, Ross A, Paton KA, Macgregor TA, McGrouther D, MacLaren I, Nord M, Microscopy And Microanalysis 26, 944 (2020). http://doi.org/10.1017/S1431927620024307
Abstract: Fast pixelated detectors incorporating direct electron detection (DED) technology are increasingly being regarded as universal detectors for scanning transmission electron microscopy (STEM), capable of imaging under multiple modes of operation. However, several issues remain around the post-acquisition processing and visualization of the often very large multidimensional STEM datasets produced by them. We discuss these issues and present open source software libraries to enable efficient processing and visualization of such datasets. Throughout, we provide examples of the analysis methodologies presented, utilizing data from a 256 x 256 pixel Medipix3 hybrid DED detector, with a particular focus on the STEM characterization of the structural properties of materials. These include the techniques of virtual detector imaging; higher-order Laue zone analysis; nanobeam electron diffraction; and scanning precession electron diffraction. In the latter, we demonstrate a nanoscale lattice parameter mapping with a fractional precision <= 6 x 10(-4) (0.06%).
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.8
Times cited: 3
DOI: 10.1017/S1431927620024307
|
|
|
“Optimizing Experimental Conditions for Accurate Quantitative Energy-Dispersive X-ray Analysis of Interfaces at the Atomic Scale”. MacArthur KE, Yankovich AB, Béché, A, Luysberg M, Brown HG, Findlay SD, Heggen M, Allen LJ, Microscopy And Microanalysis , 1 (2021). http://doi.org/10.1017/S1431927621000246
Abstract: The invention of silicon drift detectors has resulted in an unprecedented improvement in detection efficiency for energy-dispersive X-ray (EDX) spectroscopy in the scanning transmission electron microscope. The result is numerous beautiful atomic-scale maps, which provide insights into the internal structure of a variety of materials. However, the task still remains to understand exactly where the X-ray signal comes from and how accurately it can be quantified. Unfortunately, when crystals are aligned with a low-order zone axis parallel to the incident beam direction, as is necessary for atomic-resolution imaging, the electron beam channels. When the beam becomes localized in this way, the relationship between the concentration of a particular element and its spectroscopic X-ray signal is generally nonlinear. Here, we discuss the combined effect of both spatial integration and sample tilt for ameliorating the effects of channeling and improving the accuracy of EDX quantification. Both simulations and experimental results will be presented for a perovskite-based oxide interface. We examine how the scattering and spreading of the electron beam can lead to erroneous interpretation of interface compositions, and what approaches can be made to improve our understanding of the underlying atomic structure.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.891
DOI: 10.1017/S1431927621000246
|
|
|
“Fast electron low dose tomography for beam sensitive materials”. Esteban DA, Vanrompay H, Skorikov A, Béché, A, Verbeeck J, Freitag B, Bals S, Microscopy And Microanalysis 27, 2116 (2021). http://doi.org/10.1017/S1431927621007649
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.891
DOI: 10.1017/S1431927621007649
|
|
|
“Novel thin film lift-off process for in situ TEM tensile characterization”. Neelisetty KK, Kumar CN S, Kashiwar A, Scherer T, Chakravadhanula VSK, Kuebel C, Microscopy And Microanalysis 27, 216 (2021). http://doi.org/10.1017/S1431927621001367
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 1.891
DOI: 10.1017/S1431927621001367
|
|