“Pr/ZrO2 prepared by atomic trapping : an efficient catalyst for the conversion of glycerol to lactic acid with concomitant transfer hydrogenation of cyclohexene”. Tang Z, Liu P, Cao H, Bals S, Heeres HJ, Pescarmona PP, ACS catalysis 9, 9953 (2019). http://doi.org/10.1021/ACSCATAL.9B02139
Abstract: A series of heterogeneous catalysts consisting of highly dispersed Pt nanoparticles supported on nanosized ZrO2 (20 to 60 nm) was synthesized and investigated for the one-pot transfer hydrogenation between glycerol and cyclohexene to produce lactic acid and cyclohexane, without any additional H-2. Different preparation methods were screened, by varying the calcination and reduction procedures with the purpose of optimizing the dispersion of Pt species (i.e., as single-atom sites or extra-fine Pt nanoparticles) on the ZrO2 support. The Pt/ZrO2 catalysts were characterized by means of transmission electron microscopy techniques (HAADF-STEM, TEM), elemental analysis (ICP-OES, EDX mapping), N-2-physisorption, H-2 temperature-programmed-reduction (H-2-TPR), X-ray photoelectron spectroscopy (XPS), and X-ray diffraction (XRD). Based on this combination of techniques it was possible to correlate the temperature of the calcination and reduction treatments with the nature of the Pt species. The best catalyst consisted of subnanometer Pt clusters (<1 nm) and atomically dispersed Pt (as Pt2+ and Pt4+) on the ZrO2 support, which were converted into extra-fine Pt nanoparticles (average size = 1.4 nm) upon reduction. These nanoparticles acted as catalytic species for the transfer hydrogenation of glycerol with cyclohexene, which gave an unsurpassed 95% yield of lactic acid salt at 96% glycerol conversion (aqueous glycerol solution, NaOH as promoter, 160 degrees C, 4.5 h, at 20 bar N-2). This is the highest yield and selectivity of lactic acid (salt) reported in the literature so far. Reusability experiments showed a partial and gradual loss of activity of the Pt/ZrO2 catalyst, which was attributed to the experimentally observed aggregation of Pt nanoparticles.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 10.614
Times cited: 46
DOI: 10.1021/ACSCATAL.9B02139
|
|
|
“Postsynthetic high-alumina zeolite crystal engineering in organic free hyper-alkaline media”. Van Tendeloo L, Wangermez W, Vandekerkhove A, Willhammar T, Bals S, Maes A, Martens JA, Kirschhock CEA, Breynaert E, Chemistry of materials 29, 629 (2017). http://doi.org/10.1021/ACS.CHEMMATER.6B04052
Abstract: Postsynthetic modification of high -alumina zeolites in hyper alkaline media can be tailored toward alteration of framework topology, crystal size and morphology, or desired Si/A1 ratio. FAU, EMT, MAZ, KFI, HEU, and LTA starting materials were treated with 1.2 M MOH (M = Na, K, RE, or Cs), leading to systematic ordered porosity or fully transformed frameworks with new topology and adjustable Si/Al ratio. In addition to the versatility of this tool for zeolite crystal engineering, these alterations improve understanding of the crystal chemistry. Such knowledge can guide further development in zeolite crystal engineering. Postsynthetic alteration also provides insight on the long-term stability of aluminosilicate zeolites that are used as a sorption sink in concrete -based waste disposal facilities in harsh alkaline conditions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 16
DOI: 10.1021/ACS.CHEMMATER.6B04052
|
|
|
“Post-synthesis deposition of V-Zeolitic nanoparticles in SBA-15”. Meynen V, Beyers E, Cool P, Vansant EF, Mertens M, Weyten H, Lebedev OI, Van Tendeloo G, Chemical communications , 898 (2004). http://doi.org/10.1039/b400636d
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 6.319
Times cited: 22
DOI: 10.1039/b400636d
|
|
|
“Post-synthesis bromination of benzene bridged PMO as a way to create a high potential hybrid material”. Huybrechts W, Mali G, Kuśtrowski P, Willhammar T, Mertens M, Bals S, Van Der Voort P, Cool P, Microporous and mesoporous materials: zeolites, clays, carbons and related materials 236, 244 (2016). http://doi.org/10.1016/j.micromeso.2016.09.003
Abstract: Periodic mesoporous organosilicas provide the best of two worlds: the strength and porosity of an inorganic framework combined with the infinite possibilities created by the organic bridging unit. In this work we focus on post-synthetical modification of benzene bridged PMO, in order to create bromobenzene PMO. In the past, this proved to be very challenging due to unwanted structural deterioration. However, now we have found a way to brominate this material whilst keeping the structure intact. In-depth structural analysis by solid state NMR and XPS shows both vast progress over previous attempts as well as potential for improvement.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 3.615
Times cited: 7
DOI: 10.1016/j.micromeso.2016.09.003
|
|
|
“Possibilities and limitations of advanced transmission electron microscopy for carbon-based nanomaterials”. Ke X, Bittencourt C, Van Tendeloo G, Beilstein journal of nanotechnology 6, 1541 (2015). http://doi.org/10.3762/bjnano.6.158
Abstract: A major revolution for electron microscopy in the past decade is the introduction of aberration correction, which enables one to increase both the spatial resolution and the energy resolution to the optical limit. Aberration correction has contributed significantly to the imaging at low operating voltages. This is crucial for carbon-based nanomaterials which are sensitive to electron irradiation. The research of carbon nanomaterials and nanohybrids, in particular the fundamental understanding of defects and interfaces, can now be carried out in unprecedented detail by aberration-corrected transmission electron microscopy (AC-TEM). This review discusses new possibilities and limits of AC-TEM at low voltage, including the structural imaging at atomic resolution, in three dimensions and spectroscopic investigation of chemistry and bonding. In situ TEM of carbon-based nanomaterials is discussed and illustrated through recent reports with particular emphasis on the underlying physics of interactions between electrons and carbon atoms.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.127
Times cited: 10
DOI: 10.3762/bjnano.6.158
|
|
|
“Positron annihilation study of nanocrystalline Ni3Al : simulations and measurements”. Kuriplach J, van Petegem S, Hou M, Van Tendeloo G, Schryvers D, et al, Materials science forum
T2 –, 12th International Conference on Positron Annihilation (ICPA-12), AUG 06-12, 2000, UNIV BUNDERSWEHR MUNCHEN, NEUBIBERG, GERMANY 363-3, 94 (2001)
Abstract: A positron lifetime experiment is performed on samples produced by the compaction of nanocrystalline Ni3Al powder synthesized by the inert-gas condensation technique. In the lifetime spectrum we observe two components corresponding to defects. Computer (virtual) samples of n-Ni3Al are obtained using molecular dynamics combined with the Metropolis Monte Carlo technique. Positron lifetime calculations are then performed on selected regions of simulated samples. For this purpose, a new computational technique based on a generalization of the atomic superposition method for non-periodic systems was developed. Lifetimes calculated in this way are compared to experiment.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
|
|
|
Tavernier S, op de Beeck W, Ghekiere J-P, Van Tendeloo G (1996) Positively charged toner for use in electrostatography : US5532097 : 07/02/1996
Keywords: Patent; Electron microscopy for materials research (EMAT)
|
|
|
“Positive graphene by chemical design : tuning supramolecular strategies for functional surfaces”. Hadad C, Ke X, Carraro M, Sartorel A, Bittencourt C, Van Tendeloo G, Bonchio M, Quintana M, Prato M, Chemical communications 50, 885 (2014). http://doi.org/10.1039/c3cc47056c
Abstract: A diazonium based-arylation reaction was efficiently used for the covalent addition of 4-amino-N,N,N-trimethylbenzene ammonium to stable dispersions of few layer graphene (FLG) yielding an innovative FLG platform with positive charges to immobilize inorganic polyanions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.319
Times cited: 19
DOI: 10.1039/c3cc47056c
|
|
|
“Positional and orientational disorder in a solid solution of Sr9-xNi1.5-x(PO4)7 (x=0.3)”. Belik A, Izumi F, Ikeda T, Morozov VA, Dilanian R, Torii S, Kopnin E, Lebedev OI, Van Tendeloo G, Lazoryak BI, Chemistry and materials 14, 4464 (2002). http://doi.org/10.1021/cm0206901
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 28
DOI: 10.1021/cm0206901
|
|
|
“Porous nanostructured metal oxides synthesized through atomic layer deposition on a carbonaceous template followed by calcination”. Deng S, Kurttepeli M, Cott DJ, Bals S, Detavernier C, Journal of materials chemistry A : materials for energy and sustainability 3, 2642 (2015). http://doi.org/10.1039/C4TA05165C
Abstract: Porous metal oxides with nano-sized features attracted intensive interest in recent decades due to their high surface area which is essential for many applications, e.g. Li ion batteries, photocatalysts, fuel cells and dye-sensitized solar cells. Various approaches have so far been investigated to synthesize porous nanostructured metal oxides, including self-assembly and template-assisted synthesis. For the latter approach, forests of carbon nanotubes are considered as particularly promising templates, with respect to their one-dimensional nature and the resulting high surface area. In this work, we systematically investigate the formation of porous metal oxides (Al2O3, TiO2, V2O5 and ZnO) with different morphologies using atomic layer deposition on multi-walled carbon nanotubes followed by post-deposition calcination. X-ray diffraction, scanning electron microscopy accompanied by X-ray energy dispersive spectroscopy and transmission electron microscopy were used for the investigation of morphological and structural transitions at the micro- and nano-scale during the calcination process. The crystallization temperature and the surface coverage of the metal oxides and the oxidation temperature of the carbon nanotubes were found to produce significant influence on the final morphology.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 8.867
Times cited: 23
DOI: 10.1039/C4TA05165C
|
|
|
“Pore REconstruction and Segmentation (PORES) method for improved porosity quantification of nanoporous materials”. Van Eyndhoven G, Kurttepeli M, van Oers CJ, Cool P, Bals S, Batenburg KJ, Sijbers J, Ultramicroscopy 148, 10 (2015). http://doi.org/10.1016/j.ultramic.2014.08.008
Abstract: Electron tomography is currently a versatile tool to investigate the connection between the structure and properties of nanomaterials. However, a quantitative interpretation of electron tomography results is still far from straightforward. Especially accurate quantification of pore-space is hampered by artifacts introduced in all steps of the processing chain, i.e., acquisition, reconstruction, segmentation and quantification. Furthermore, most common approaches require subjective manual user input. In this paper, the PORES algorithm POre REconstruction and Segmentation is introduced; it is a tailor-made, integral approach, for the reconstruction, segmentation, and quantification of porous nanomaterials. The PORES processing chain starts by calculating a reconstruction with a nanoporous-specific reconstruction algorithm: the Simultaneous Update of Pore Pixels by iterative REconstruction and Simple Segmentation algorithm (SUPPRESS). It classifies the interior region to the pores during reconstruction, while reconstructing the remaining region by reducing the error with respect to the acquired electron microscopy data. The SUPPRESS reconstruction can be directly plugged into the remaining processing chain of the PORES algorithm, resulting in accurate individual pore quantification and full sample pore statistics. The proposed approach was extensively validated on both simulated and experimental data, indicating its ability to generate accurate statistics of nanoporous materials.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab; Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 2.843
Times cited: 7
DOI: 10.1016/j.ultramic.2014.08.008
|
|
|
“Pore Chemistry of Metal–Organic Frameworks”. Ji Z, Wang H, Canossa S, Wuttke S, Yaghi OM, Advanced Functional Materials 30, 2000238 (2020). http://doi.org/10.1002/adfm.202000238
Abstract: The pores in metal–organic frameworks (MOFs) can be functionalized by placing chemical entities along the backbone and within the backbone. This chemistry is enabled by the architectural, thermal, and chemical robustness of the frameworks and the ability to characterize them by many diffraction and spectroscopic techniques. The pore chemistry of MOFs is articulated in terms of site isolation, coupling, and cooperation and relate that to their functions in guest recognition, catalysis, ion and electron transport, energy transfer, pore‐dynamic modulation, and interface construction. It is envisioned that the ultimate control of pore chemistry requires arranging functionalities into defined sequences and developing techniques for reading and writing such sequences within the pores.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 19
DOI: 10.1002/adfm.202000238
|
|
|
“Polytypism in mcalpineite : a study of natural and synthetic Cu₃TeO₆”. Missen OP, Mills SJ, Canossa S, Hadermann J, Nenert G, Weil M, Libowitzky E, Housley RM, Artner W, Kampf AR, Rumsey MS, Spratt J, Momma K, Dunstan MA, Acta Crystallographica. Section B: Structural Science, Crystal Engineering and Materials (Online) 78 (2022). http://doi.org/10.1107/S2052520621013032
Abstract: Synthetic and naturally occurring forms of tricopper orthotellurate, (Cu3TeO6)-Te-II-O-IV (the mineral mcalpineite) have been investigated by 3D electron diffraction (3D ED), X-ray powder diffraction (XRPD), Raman and infrared (IR) spectroscopic measurements. As a result of the diffraction analyses, (Cu3TeO6)-Te-II-O-IV is shown to occur in two polytypes. The higher-symmetric (Cu3TeO6)-Te-II-O-IV-1C polytype is cubic, space group 1a (3) over bar, with a = 9.537 (1) angstrom and V = 867.4 (3) angstrom(3) as reported in previous studies. The 1C polytype is a well characterized structure consisting of alternating layers of (CuO6)-O-II octahedra and both (CuO6)-O-II and (TeO6)-O-VI octahedra in a patchwork arrangement. The structure of the lower-symmetric orthorhombic (Cu3TeO6)-Te-II-O-IV-2O polytype was determined for the first time in this study by 3D ED and verified by Rietveld refinement. The 2O polytype crystallizes in space group Pcca, with a = 9.745 (3) angstrom, b = 9.749 (2) angstrom, c = 9.771 (2) angstrom and V = 928.3 (4) angstrom(3) . High-precision XRPD data were also collected on (Cu3TeO6)-Te-II-O-IV-2O to verify the lower-symmetric structure by performing a Rietveld refinement. The resultant structure is identical to that determined by 3D ED, with unit-cell parameters a = 9.56157 (19) angstrom, b = 9.55853 (11) angstrom, c = 9.62891 (15) angstrom and V = 880.03 (2) angstrom(3) . The lower symmetry of the 2O polytype is a consequence of a different cation ordering arrangement, which involves the movement of every second (CuO6)-O-II and (TeO6)-O-VI octahedral layer by (1/4, 1/4, 0), leading to an offset of (TeO6)-O-VI and (CuO6)-O-II octahedra in every second layer giving an ABAB* stacking arrangement. Syntheses of (Cu3TeO6)-Te-II-O-IV showed that low-temperature (473 K) hydrothermal conditions generally produce the 2O polytype. XRPD measurements in combination with Raman spectroscopic analysis showed that most natural mcalpineite is the orthorhombic 2O polytype. Both XRPD and Raman spectroscopy measurements may be used to differentiate between the two polytypes of (Cu3TeO6)-Te-II-O-IV. In Raman spectroscopy, (Cu3TeO6)-Te-II-O-IV-1C has a single strong band around 730 cm(-1), whereas (Cu3TeO6)-Te-II-O-IV-2O shows a broad double maximum with bands centred around 692 and 742 cm(-1).
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.9
DOI: 10.1107/S2052520621013032
|
|
|
“Polyoxocationic antimony oxide cluster with acidic protons”. Watanabe Y, Hyeon-Deuk K, Yamamoto T, Yabuuchi M, Karakulina OM, Noda Y, Kurihara T, Chang I-Y, Higashi M, Tomita O, Tassel C, Kato D, Xia J, Goto T, Brown CM, Shimoyama Y, Ogiwara N, Hadermann J, Abakumov AM, Uchida S, Abe R, Kageyama H, Science Advances 8, eabm5379 (2022). http://doi.org/10.1126/SCIADV.ABM5379
Abstract: The success and continued expansion of research on metal-oxo clusters owe largely to their structural richness and wide range of functions. However, while most of them known to date are negatively charged polyoxometalates, there is only a handful of cationic ones, much less functional ones. Here, we show an all-inorganic hydroxyiodide [H(10.)7Sb(32.1)O(44)][H2.1Sb2.1I8O6][Sb0.76I6](2)center dot 25H(2)O (HSbOI), forming a face-centered cubic structure with cationic Sb32O44 clusters and two types of anionic clusters in its interstitial spaces. Although it is submicrometer in size, electron diffraction tomography of HSbOI allowed the construction of the initial structural model, followed by powder Rietveld refinement to reach the final structure. The cationic cluster is characterized by the presence of acidic protons on its surface due to substantial Sb3+ deficiencies, which enables HSbOI to serve as an excellent solid acid catalyst. These results open up a frontier for the exploration and functionalization of cationic metal-oxo clusters containing heavy main group elements.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 13.6
DOI: 10.1126/SCIADV.ABM5379
|
|
|
“Polyhedral iron oxide coreshell nanoparticles in a biodegradable polymeric matrix : preparation, characterization and application in magnetic particle hyperthermia and drug delivery”. Filippousi M, Altantzis T, Stefanou G, Betsiou M, Bikiaris DN, Angelakeris M, Pavlidou E, Zamboulis D, Van Tendeloo G, RSC advances 3, 24367 (2013). http://doi.org/10.1039/c3ra43747g
Abstract: Polyhedral magnetic iron oxide nanocrystals with multiple facets have been embedded in biocompatible and biodegradable polymeric matrices in order to study their structural, magnetic features and alternating-current (AC) magnetic heating efficiency. The encapsulation of iron oxide nanoparticles into a polymer matrix was confirmed by transmission electron microscopy and further corroborated by high angle annular dark field scanning transmission electron microscopy (HAADF-STEM). HAADF-STEM tomography proved that the iron oxide nanocrystals consist of well-defined polyhedral structures with multiple facets. The magnetic features were found to be in good agreement with the structural and morphological features and are maintained even after encapsulation. Furthermore, the magnetic nanoparticles inside these matrices may be considered as good candidates for biomedical applications in hyperthermia treatments because of their high heating capacity exhibited under an alternating magnetic field. The anticancer Taxol drug was encapsulated in these nanoparticles and its physical state and release rate at 37 and 42 °C was studied.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.108
Times cited: 19
DOI: 10.1039/c3ra43747g
|
|
|
“Polyethylene glycol conjugated polymeric nanocapsules for targeted delivery of quercetin to folate-expressing cancer cells in vitro and in vivo”. El-Gogary RI, Rubio N, Wang JTW, Al-Jamal WT, Bourgognon M, Kafa H, Naeem M, Klippstein R, Abbate V, Leroux F, Bals S, Van Tendeloo G, Kamel AO, Awad GAS, Mortada ND, Al-Jamal KT;, ACS nano 8, 1384 (2014). http://doi.org/10.1021/nn405155b
Abstract: In this work we describe the formulation and characterization of chemically modified polymeric nanocapsules incorporating the anticancer drug, quercetin, for the passive and active targeting to tumors. Folic acid was conjugated to poly(lactide-co-glycolide) (PLGA) polymer to facilitate active targeting to cancer cells. Two different methods for the conjugation of PLGA to folic acid were employed utilizing polyethylene glycol (PEG) as a spacer. Characterization of the conjugates was performed using FTIR and H-1 NMR studies. The PEG and folk acid content was independent of the conjugation methodology employed. PEGylation has shown to reduce the size of the nanocapsule; moreover, zeta-potential was shown to be polymer-type dependent. Comparative studies on the cytotoxicity and cellular uptake of the different formulations by He La cells, in the presence and absence of excess folic acid, were carried out using MTT assay and Confocal Laser Scanning Microscopy, respectively. Both results confirmed the selective uptake and cytotoxicity of the folic acid targeted nanocapsules to the folate enriched cancer cells in a folate-dependent manner. Finally, the passive tumor accumulation and the active targeting of the nanocapsules to folate-expressing cells were confirmed upon intravenous administration in He La or IGROV-1 tumor-bearing mice. The developed nanocapsules provide a system for targeted delivery of a range of hydrophobic anticancer drugs in vivo.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 13.942
Times cited: 144
DOI: 10.1021/nn405155b
|
|
|
“Polydopamine nanocoated whole-cell asymmetric biocatalysts”. Wang L, Hu Z-Y, Yang X-Y, Zhang B-B, Geng W, Van Tendeloo G, Su B-L, Chemical communications 53, 6617 (2017). http://doi.org/10.1039/C7CC01283G
Abstract: Our whole-cell biocatalyst with a polydopamine nanocoating shows high catalytic activity (5 times better productivity than the native cell) and reusability (84% of the initial yield after 5 batches, 8 times higher than the native cell) in asymmetric reduction. It also integrates with titania, silica, and magnetic nanoparticles for multi-functionalization.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.319
Times cited: 15
DOI: 10.1039/C7CC01283G
|
|
|
“Polar and magnetic Mn2FeMO6 (M=Nb, Ta) with LiNbO3-type structure : high-pressure synthesis”. Li MR, Walker D, Retuerto M, Sarkar T, Hadermann J, Stephens PW, Croft M, Ignatov A, Grams CP, Hemberger J, Nowik I, Halasyamani PS, Tran TT, Mukherjee S, Dasgupta TS, Greenblatt M;, Angewandte Chemie: international edition in English 52, 8406 (2013). http://doi.org/10.1002/anie.201302775
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 11.994
Times cited: 53
DOI: 10.1002/anie.201302775
|
|
|
“Polar and magnetic layered A-site and rock salt B-site-ordered NaLnFeWO6 (Ln = La, Nd) perovskites”. Retuerto M, Li MR, Ignatov A, Croft M, Ramanujachary KV, Chi S, Hodges JP, Dachraoui W, Hadermann J, Tran TT, Halasyamani PS, Grams CP, Hemberger J, Greenblatt M;, Inorganic chemistry 52, 12482 (2013). http://doi.org/10.1021/ic401491y
Abstract: We have expanded the double perovskite family of materials with the unusual combination of layered order in the A sublattice and rock salt order over the B sublattice to compounds NaLaFeWO6 and NaNdFeWO6. The materials have been synthesized and studied by powder X-ray diffraction, neutron diffraction, electron diffraction, magnetic measurements, X-ray absorption spectroscopy, dielectric measurements, and second harmonic generation. At room temperature, the crystal structures of both compounds can be defined in the noncentrosymmetric monoclinic P2(1) space group resulting from the combination of ordering both in the A and B sublattices, the distortion of the cell due to tilting of the octahedra, and the displacement of certain cations. The magnetic studies show that both compounds are ordered antiferromagnetically below T-N approximate to 25 K for NaLaFeWO6 and at similar to 21 K for NaNdFeWO6. The magnetic structure of NaNdFeWO6 has been solved with a propagation vector k = (1/2 0 1/2) as an antiferromagnetic arrangement of Fe and Nd moments. Although the samples are potential multiferroics, the dielectric measurements do not show a ferroelectric response.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 17
DOI: 10.1021/ic401491y
|
|
|
“Point defect reactions in silicon studies in situ by high flux electron irradiation in high voltage transmission electron microscope”. Vanhellemont J, Romano-Rodriguez A, Fedina L, van Landuyt J, Aseev A, Materials science and technology 11, 1194 (1995)
Keywords: A3 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 7
|
|
|
“Point defect reactions in silicon studied in situ by high flux electron irradiation in high voltage transmission electron microscope”. Vanhellemont J, Romano Rodriguez A, Fedina L, van Landuyt J, Aseev A, Materials science and technology 11, 1194 (1995). http://doi.org/10.1179/mst.1995.11.11.1194
Abstract: Results are presented of in situ studies of 1 MeV electron irradiation induced (113) defect generation in silicon containing different types and concentrations of extrinsic point defects. A semiquantitative model is developed describing the influence of interfaces and stress fields and of extrinsic point defects on the (113) defect generation in silicon during irradiation. The theoretical results obtained are correlated with experimental data obtained on silicon uniformly doped with boron and phosphorus and with observations obtained by irradiating cross-sectional samples of wafers with highly doped surface layers. It is shown that in situ irradiation in a high voltage election microscope is a powerful tool for studying local point defect reactions in silicon. (C) 1995 The Institute of Materials.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 0.995
Times cited: 7
DOI: 10.1179/mst.1995.11.11.1194
|
|
|
“Point defect clusters and dislocations in FIB irradiated nanocrystalline aluminum films : an electron tomography and aberration-corrected high-resolution ADF-STEM study”. Idrissi H, Turner S, Mitsuhara M, Wang B, Hata S, Coulombier M, Raskin J-P, Pardoen T, Van Tendeloo G, Schryvers D, Microscopy and microanalysis 17, 983 (2011). http://doi.org/10.1017/S143192761101213X
Abstract: Focused ion beam (FIB) induced damage in nanocrystalline Al thin films has been characterized using advanced transmission electron microscopy techniques. Electron tomography was used to analyze the three-dimensional distribution of point defect clusters induced by FIB milling, as well as their interaction with preexisting dislocations generated by internal stresses in the Al films. The atomic structure of interstitial Frank loops induced by irradiation, as well as the core structure of Frank dislocations, has been resolved with aberration-corrected high-resolution annular dark-field scanning TEM. The combination of both techniques constitutes a powerful tool for the study of the intrinsic structural properties of point defect clusters as well as the interaction of these defects with preexisting or deformation dislocations in irradiated bulk or nanostructured materials.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.891
Times cited: 25
DOI: 10.1017/S143192761101213X
|
|
|
“Platinumcarbon nanotube interaction”. Bittencourt C, Hecq M, Felten A, Pireaux JJ, Ghijsen J, Felicissimo MP, Rudolf P, Drube W, Ke X, Van Tendeloo G, Chemical physics letters 462, 260 (2008). http://doi.org/10.1016/j.cplett.2008.07.082
Abstract: The interaction between evaporated Pt and pristine or oxygen-plasma-treated multiwall carbon nanotubes (CNTs) is investigated. Pt is found to nucleate at defect sites, whether initially present or introduced by oxygen plasma treatment. The plasma treatment induces a uniform dispersion of Pt nanoparticles at the CNT surface. The absence of additional features in the C 1s core level spectrum indicates that no mixed PtC phase is formed. The formation of COPt bonds at the cluster-CNT interface is suggested to reduce the electronic interaction between Pt nanoparticles and the CNT surface.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.815
Times cited: 62
DOI: 10.1016/j.cplett.2008.07.082
|
|
|
“Platinum particle size and support effects in NOx mediated carbon oxidation over platinum catalysts”. Villani K, Vermandel W, Smets K, Liang D, Van Tendeloo G, Martens JA, Environmental science &, technology 40, 2727 (2006). http://doi.org/10.1021/es051871h
Abstract: Platinum metal was dispersed on microporous, mesoporous, and nonporous support materials including the zeolites Na-Y, Ba-Y, Ferrierite, ZSM-22, ETS-10, and AlPO-11, alumina, and titania. The oxidation of carbon black loosely mixed with catalyst powder was monitored gravimetrically in a gas stream containing nitric oxide, oxygen, and water. The carbon oxidation activity of the catalysts was found to be uniquely related to the Pt dispersion and little influenced by support type. The optimum dispersion is around 3-4% corresponding to relatively large Pt particle sizes of 2040 nm. The carbon oxidation activity reflects the NO oxidation activity of the platinum catalyst, which reaches an optimum in the 20-40 nm Pt particle size range. The lowest carbon oxidation temperatures were achieved with platinum loaded ZSM-22 and AlPO-11 zeolite crystallites bearing platinum of optimum dispersion on their external surfaces.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.198
Times cited: 29
DOI: 10.1021/es051871h
|
|
|
“Platinum and palladium on carbon nanotubes : experimental and theoretical studies”. Adjizian JJ, De Marco P, Suarez-Martinez I, El Mel AA, Snyders R, Gengler RYN, Rudolf P, Ke X, Van Tendeloo G, Bittencourt C, Ewels CP;, Chemical physics letters 571, 44 (2013). http://doi.org/10.1016/j.cplett.2013.03.079
Abstract: Pristine and oxygen plasma functionalised carbon nanotubes (CNTs) were studied after the evaporation of Pt and Pd atoms. High resolution transmission electron microscopy shows the formation of metal nanoparticles at the CNT surface. Oxygen functional groups grafted by the plasma functionalization act as nucleation sites for metal nanoparticles. Analysis of the C1s core level spectra reveals that there is no covalent bonding between the Pt or Pd atoms and the CNT surface. Unlike other transition metals such as titanium and copper, neither Pd nor Pt show strong oxygen interaction or surface oxygen scavenging behaviour.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.815
Times cited: 23
DOI: 10.1016/j.cplett.2013.03.079
|
|
|
“Plasticity mechanisms in ultrafine grained freestanding aluminum thin films revealed by in-situ transmission electron microscopy nanomechanical testing”. Idrissi H, Kobler A, Amin-Ahmadi B, Coulombier M, Galceran M, Raskin J-P, Godet S, Kuebel C, Pardoen T, Schryvers D, Applied physics letters 104, 101903 (2014). http://doi.org/10.1063/1.4868124
Abstract: In-situ bright field transmission electron microscopy (TEM) nanomechanical tensile testing and in-situ automated crystallographic orientation mapping in TEM were combined to unravel the elementary mechanisms controlling the plasticity of ultrafine grained Aluminum freestanding thin films. The characterizations demonstrate that deformation proceeds with a transition from grain rotation to intragranular dislocation glide and starvation plasticity mechanism at about 1% deformation. The grain rotation is not affected by the character of the grain boundaries. No grain growth or twinning is detected. (C) 2014 AIP Publishing LLC.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 24
DOI: 10.1063/1.4868124
|
|
|
“Plasmonic ‘rainbow&rsquo, photocatalyst with broadband solar light response for environmental applications”. Verbruggen SW, Keulemans M, Goris B, Blommaerts N, Bals S, Martens JA, Lenaerts S, Applied catalysis : B : environmental 188, 147 (2016). http://doi.org/10.1016/j.apcatb.2016.02.002
Abstract: We propose the concept of a ‘rainbow’ photocatalyst that consists of TiO2 modified with gold-silver alloy nanoparticles of various sizes and compositions, resulting in a broad plasmon absorption band that covers the entire UV–vis range of the solar spectrum. It is demonstrated that this plasmonic ‘rainbow’ photocatalyst is 16% more effective than TiO2 P25 under both simulated and real solar light for pollutant degradation at the solid-gas interface. With this we provide a promising strategy to maximize the spectral response for solar to chemical energy conversion.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Sustainable Energy, Air and Water Technology (DuEL)
Impact Factor: 9.446
Times cited: 47
DOI: 10.1016/j.apcatb.2016.02.002
|
|
|
“Plasmonic nanodiamonds : targeted coreshell type nanoparticles for cancer cell thermoablation”. Rehor I, Lee KL, Chen K, Hajek M, Havlik J, Lokajova J, Masat M, Slegerova J, Shukla S, Heidari H, Bals S, Steinmetz NF, Cigler P, Advanced healthcare materials 4, 460 (2015). http://doi.org/10.1002/adhm.201400421
Abstract: Targeted biocompatible nanostructures with controlled plasmonic and morphological parameters are promising materials for cancer treatment based on selective thermal ablation of cells. Here, coreshell plasmonic nanodiamonds consisting of a silica-encapsulated diamond nanocrystal coated in a gold shell are designed and synthesized. The architecture of particles is analyzed and confirmed in detail using electron tomography. The particles are biocompatibilized using a PEG polymer terminated with bioorthogonally reactive alkyne groups. Azide-modified transferrin is attached to these particles, and their high colloidal stability and successful targeting to cancer cells overexpressing the transferrin receptor are demonstrated. The particles are nontoxic to the cells and they are readily internalized upon binding to the transferrin receptor. The high plasmonic cross section of the particles in the near-infrared region is utilized to quantitatively ablate the cancer cells with a short, one-minute irradiation by a pulse 750-nm laser.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.11
Times cited: 30
DOI: 10.1002/adhm.201400421
|
|
|
“Plasmonic goldsilver alloy on TiO2 photocatalysts with tunable visible light activity”. Verbruggen SW, Keulemans M, Filippousi M, Flahaut D, Van Tendeloo G, Lacombe S, Martens JA, Lenaerts S, Applied catalysis : B : environmental 156, 116 (2014). http://doi.org/10.1016/j.apcatb.2014.03.027
Abstract: Adaptation of the photoresponse of anatase TiO2 to match the solar spectrum is an important scientific challenge. Modification of TiO2 with noble metal nanoparticles displaying surface plasmon resonance effects is one of the promising approaches. Surface plasmon resonance typically depends on chemical composition, size, shape and spatial organization of the metal nanoparticles in contact with TiO2. AuxAg(1 − x) alloy nanoparticles display strong composition-dependent surface plasmon resonance in the visible light region of the spectrum. In this work, a general strategy is presented to prepare plasmonic TiO2-based photocatalysts with a visible light response that can be accurately tuned over a broad range of the spectrum. The application as self-cleaning material toward the degradation of stearic acid is demonstrated for a plasmonic TiO2 photocatalyst displaying visible light photoactivity at the intensity maximum of solar light around 490 nm.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Sustainable Energy, Air and Water Technology (DuEL)
Impact Factor: 9.446
Times cited: 84
DOI: 10.1016/j.apcatb.2014.03.027
|
|
|
“Plasmonic gold-embedded TiO2 thin films as photocatalytic self-cleaning coatings”. Peeters H, Keulemans M, Nuyts G, Vanmeert F, Li C, Minjauw M, Detavernier C, Bals S, Lenaerts S, Verbruggen SW, Applied Catalysis B-Environmental 267, 118654 (2020). http://doi.org/10.1016/j.apcatb.2020.118654
Abstract: Transparent photocatalytic TiO2 thin films hold great potential in the development of self-cleaning glass sur-
faces, but suffer from a poor visible light response that hinders the application under actual sunlight. To alleviate this problem, the photocatalytic film can be modified with plasmonic nanoparticles that interact very effectively with visible light. Since the plasmonic effect is strongly concentrated in the near surroundings of the nano- particle surface, an approach is presented to embed the plasmonic nanostructures in the TiO2 matrix itself, rather than deposit them loosely on the surface. This way the interaction interface is maximised and the plasmonic effect can be fully exploited. In this study, pre-fabricated gold nanoparticles are made compatible with the organic medium of a TiO2 sol-gel coating suspension, resulting in a one-pot coating suspension. After spin coating, homogeneous, smooth, highly transparent and photoactive gold-embedded anatase thin films are ob- tained.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation); Sustainable Energy, Air and Water Technology (DuEL)
Impact Factor: 22.1
Times cited: 57
DOI: 10.1016/j.apcatb.2020.118654
|
|