Abstract: Tissue engineering combines artificial scaffolds and living cells in order to reconstruct damaged tissues and organs. The biodegradable scaffolds should maintain their mechanical properties during first stages of the regeneration. The aim of this study was to investigate the extent the degradation affects the mechanical stability of novel biodegradable composite scaffolds in relation to their composition. The scaffolds were made using fused deposition modeling. They were composed of ternary composites containing poly(epsilon-caprolactone) (PCL), 5 wt% of tricalcium phosphate (TCP) and 5, 15, and 25 wt% of poly(lactide-co-glycolide) (PLGA). Scaffolds made of pristine PCL and binary composite PCL-TCP were tested as reference samples. The degradation experiment was carried out in simulated body fluid at 37 degrees C for 12 weeks. Mechanical tests were carried out in a mechanical tester. Strain was measured using digital image correlation and crossbar displacement. Chemical composition had a significant effect on initial mechanical properties and their changes during degradation. The initial apparent Young's modulus of ternary composite scaffolds was two times higher than that of PCL-TCP. Higher PLGA concentration yielded faster decrease of the mechanical properties. At the end of the experiment, there were no significant differences of the modulus among all tested materials although degradation of the ternary composite scaffolds was significantly advanced. (C) 2015 Society of Plastics Engineers

Abstract: Electrospinning is a versatile technique for the fabrication of polymer-based nano/microfibers. Both physical and chemical characteristics of pre-electrospinning polymer solutions affect the morphology and chemistry of electrospun nanofibers. An atmospheric-pressure plasma jet has previously been shown to induce physical modifications in polylactic acid (PLA) solutions. This work aims at investigating the plasma-induced chemistry in organic solutions of PLA, and their effects on the resultant PLA nanofibers. Therefore, very broad range of gas, liquid, and solid (nanofiber) analyzing techniques has been applied. Plasma alters the acidity of the solutions. SEM studies illustrated that complete fiber morphology enhancement only occurred when both PLA and solvent molecules were exposed to preelectrospinning plasma treatment.
Additionally, the surface
chemistry of the PLA nanofibers
was mostly preserved.

Abstract: A crystal structure investigation of the low temperature Li2SnO3 modification has been carried out. X-ray, neutron powder and electron diffraction data showed that this compound crystallizes in a monoclinic unit cell with parameters: a = 5.3033(2)Å, b = 9.1738(3)Å, c = 10.0195(2)Å, β ~ 100.042(2)º and has stacking disorder along the c-axis. Simulation of diffraction patterns with different stacking faults mainly reveal the presence of rotational stacking faults with a probability of about 40% .

Abstract: A systematic investigation of voltage effect on the plasma parameters, especially the species densities and chemical reaction mechanisms, in the capacitive N-2 discharges is performed by employing a two-dimensional self-consistent fluid model. The validity of the numerical model is first demonstrated by the qualitative agreement of the calculated and experimental results. Then, the densities, production mechanisms, and loss mechanisms of species from simulation are examined at various voltages. It is found that all the species densities increase monotonically with the voltage, whereas their spatial profiles at lower voltages are quite different from those at higher voltages. The electrons and Nthorn 2 ions are mainly generated by the electron impact ionization of N-2 gas, while the Nthorn ions, whose density is one or two orders of magnitude lower, are mostly formed by the ionization of N atoms. The electron impact dissociation of N-2 gas dominates the generation of N atoms, which are mostly destroyed for the Nthorn ion production. As for the excited N-2 levels, the level conversion processes play a very important role in their production and depletion mechanisms, except for the electron impact excitation of the ground state N-2 molecules. Published under license by AIP Publishing.

Abstract: In this study we quantitatively investigate for the first time the plasma characteristics of an argon gliding arc with a 3D model. The model is validated by comparison with available experimental data from literature and a reasonable agreement is obtained for the calculated gas temperature and electron density. A complete arc cycle is modeled from initial ignition to arc decay. We investigate how the plasma characteristics, i.e., the electron temperature, gas temperature,
reduced electric field, and the densities of electrons, Ar+ and Ar2+ ions and Ar(4s) excited states, vary over one complete arc cycle, including their behavior in the discharge and post-discharge. These plasma characteristics exhibit a different evolution over one arc cycle, indicating that either the active discharge stage or the post-discharge stage can be beneficial for certain applications.

Abstract: The structure of beta-SiC formed by carbon implantation into Si at high temperatures (850-950 degrees C) at doses ranging between 0.2 X 10(18) to 1 X 10(18) cm(-2) at 200 keV, was studied by combined cross section and high resolution transmission electron microscopy (XTEM and HRTEM). Implantation was performed on (001) and (111) Si wafers. In both cases a buried beta-SiC layer was formed having the same orientation as the Si matrix.

Abstract: Previous reports on Poisson-Nernst-Planck (PNP) simulations of solid-state nanopores have focused on steady state behaviour under simplified boundary conditions. These are Neumann boundary conditions for the voltage at the pore walls, and in some cases also Donnan equilibrium boundary conditions for concentrations and voltages at both entrances of the nanopore. In this paper, we report time-dependent and steady state PNP simulations under less restrictive boundary conditions, including Neumann boundary conditions applied throughout the membrane relatively far away from the nanopore. We simulated ion currents through cylindrical and conical nanopores with several surface charge configurations, studying the spatial and temporal dependence of the currents contributed by each ion species. This revealed that, due to slow co-diffusion of oppositely charged ions, steady state is generally not reached in simulations or in practice. Furthermore, it is shown that ion concentration polarization is responsible for the observed limiting conductances and ion current rectification in nanopores with asymmetric surface charges or shapes. Hence, after more than a decade of collective research attempting to understand the nature of ion current rectification in solid-state nanopores, a relatively intuitive model is retrieved. Moreover, we measured and simulated current-voltage characteristics of rectifying silicon nitride nanopores presenting overlimiting conductances. The similarity between measurement and simulation shows that overlimiting conductances can result from the increased conductance of the electric double-layer at the membrane surface at the depletion side due to voltage-induced polarization charges.

Abstract: The experiments conducted are focused on natural organic substances, removal from water in ion-exchange process, ultrafiltration process and ion exchange-ultrafiltration integrated process. The water from the Odra River and model solution were investigated. In treatment processes, various doses of 5 anion-exchange resins as well as polyethersulphone membranes with different cut-offs were used. The efficiency of process was determined by measuring a decrease both in the colour intensity and the UV 254 nm absorbance. The results show that separation efficiency in integrated process depends on resin dose added to water before ultrafiltration and on the membrane cut-off as well. Among the resins tested the most efficient was MIEX (R) resin. The ion-exchange process carried out prior to the ultrafiltration increased, especially for high cut-off membranes, NOM retention and resulted in the decrease of membrane fouling intensity.

Abstract: We analyzed ultra-thin ZrO2/SiO2/Si gate dielectrics under post-deposition anneals in dry O-2 at temperatures from 500 to 700 degreesC. TOF-SIMS profiling of ZrO2/SiO2/Si stacks is hampered by many sputter induced artifacts. The depletion of oxygen leads to a decrease in SIMS intensities. However, preferential sputtering is accompanied by transport of the depleted species towards the surface. Due to recoil implantation oxygen gets piled-up near the ZrO2/SiO2 interface. Either normal or radiation-enhanced diffusion transports oxygen back to the surface. Simultaneously also segregation of zirconium towards and through the interface is observed, resulting in a large zirconium tail in the underlying silicon substrate. (C) 2002 Elsevier Science B.V. All rights reserved.

Abstract: When confined between graphene layers, water behaves differently from the bulk and exhibits unusual properties such as fast water flow and ordering into a crystal. The hydrogen-bonded network is affected by the limited space and by the characteristics of the confining walls. The presence of an extraordinary number of hydronium and hydroxide ions in narrow channels has the following effects: (i) they affect water permeation through the channel, (ii) they may interact with functional groups on the graphene oxide surface and on the edges, and (iii) they change the thermochemistry of water, which are fundamentally important to understand, especially when confined water is subjected to an external electric field. Here we study the physical properties of water when confined between two graphene sheets and containing hydronium and hydroxide. We found that: (i) there is a disruption in the solvation structure of the ions, which is also affected by the layered structure of confined water, (ii) hydronium and hydroxide occupy specific regions inside the nanochannel, with a prevalence of hydronium (hydroxide) ions at the edges (interior), and (iii) ions recombine more slowly in confined systems than in bulk water, with the recombination process depending on the channel height and commensurability between the size of the molecules and the nanochannel height – a decay of 20% (40%) in the number of ions in 8 ps is observed for a channel height of h = 7 angstrom (bulk water). Our work reveals distinctive properties of water confined in a nanocapillary in the presence of additional hydronium and hydroxide ions.

Abstract: Iron (Fe) sources available for plants in the rhizospheric solution are mainly a mixture of complexes between Fe and organic ligands, including phytosiderophores (PS) and water-extractable humic substances (WEHS). In comparison with the other Fe sources, Fe-WEHS are more efficiently used by plants, and experimental evidences show that Fe translocation contributes to this better response. On the other hand, very little is known on the mechanisms involved in Fe allocation in leaves. In this work, physiological and molecular processes involved in Fe distribution in leaves of Fe-deficient Cucumis sativus supplied with Fe-PS or Fe-WEHS up to 5days were studied combining different techniques, such as radiochemical experiments, synchrotron micro X-ray fluorescence, real-time reverse transcription polymerase chain reaction and in situ hybridization. In Fe-WEHS-fed plants, Fe was rapidly (1day) allocated into the leaf veins, and after 5days, Fe was completely transferred into interveinal cells; moreover, the amount of accumulated Fe was much higher than with Fe-PS. This redistribution in Fe-WEHS plants was associated with an upregulation of genes encoding a ferric(III)-chelate reductase (FRO), a Fe2+ transporter (IRT1) and a natural resistance-associated macrophage protein (NRAMP). The localization of FRO and IRT1 transcripts next to the midveins, beside that of NRAMP in the interveinal area, may suggest a rapid and efficient response induced by the presence of Fe-WEHS in the extra-radical solution for the allocation in leaves of high amounts of Fe. In conclusion, Fe is more efficiently used when chelated to WEHS than PS and seems to involve Fe distribution and gene regulation of Fe acquisition mechanisms operating in leaves.

Abstract: Problematic microfossils dominate the palaeontological record between the Great Oxidation Event 2.4 billion years ago (Ga) and the last Palaeoproterozoic iron formations, deposited 500–600 million years later. These fossils are often associated with iron-rich sedimentary rocks, but their affinities, metabolism, and, hence, their contributions to Earth surface oxidation and Fe deposition remain unknown. Here we show that specific microfossil populations of the 1.88 Ga Gunflint Iron Formation contain Fe-silicate and Fe-carbonate nanocrystal concentrations in cell interiors. Fe minerals are absent in/on all organically preserved cell walls. These features are consistent with in vivo intracellular Fe biomineralization, with subsequent in situ recrystallization, but contrast with known patterns of post-mortem Fe mineralization. The Gunflint populations that display relatively large cells (thick-walled spheres, filament-forming rods) and intra-microfossil Fe minerals are consistent with oxygenic photosynthesizers but not with other Fe-mineralizing microorganisms studied so far. Fe biomineralization may have protected oxygenic photosynthesizers against Fe2+ toxicity during the Palaeoproterozoic.

Abstract: Energy-dispersive X-ray fluorescence was used for the analysis of hair samples from three different age groups of the Sudanese population. Hair samples were digested in a mixture of nitric and perchloric acids and the metals were then precipitated with ammonium pyrrolidine dithiocarbamate. The variations of the Fe, Cu, Zn and Pb content of hair with age were investigated. The averages of the elemental concentrations in each age group were compared with the other age groups and with literature values. The correlation of each pair of elements in the hair samples was also investigated.