Abstract: Cerium-doped manganite thin films were grown epitaxially by pulsed laser deposition at 720 °C and oxygen pressure pO2=125 Pa and were subjected to different annealing steps. According to x-ray diffraction (XRD) data, the formation of CeO2 as a secondary phase could be avoided for pO28 Pa. However, transmission electron microscopy shows the presence of CeO2 nanoclusters even in those films which appear to be single phase in XRD. With O2 annealing, the metal-to-insulator transition temperature increases, while the saturation magnetization decreases and stays well below the theoretical value for electron-doped La0.7Ce0.3MnO3 with mixed Mn3+/Mn2+ valences. The same trend is observed with decreasing film thickness from 100 to 20 nm, indicating a higher oxygen content for thinner films. Hall measurements on a film which shows a metal-to-insulator transition clearly reveal holes as dominating charge carriers. Combining data from x-ray photoemission spectroscopy, for determination of the oxygen content, and x-ray absorption spectroscopy (XAS), for determination of the hole concentration and cation valences, we find that with increasing oxygen content the hole concentration increases and Mn valences are shifted from 2+ to 4+. The dominating Mn valences in the films are Mn3+ and Mn4+, and only a small amount of Mn2+ ions can be observed by XAS. Mn2+ and Ce4+ XAS signals obtained in surface-sensitive total electron yield mode are strongly reduced in the bulk-sensitive fluorescence mode, which indicates hole-doping in the bulk for those films which do show a metal-to-insulator transition.

Abstract: We present a time-dependent parametric model for reactive HiPIMS deposition of films. Specific features of HiPIMS discharges and a possible increase in the density of the reactive gas in front of the reactive gas inlets placed between the target and the substrate are considered in the model. The model makes it possible to calculate the compound fractions in two target layers and in one substrate layer, and the deposition rate of films at fixed partial pressures of the reactive and inert gas. A simplified relation for the deposition rate of films prepared using a reactive HiPIMS is presented. We used the model to simulate controlled reactive HiPIMS depositions of stoichiometric ZrO2 films, which were recently carried out in our laboratories with two different configurations of the O2 inlets in front of the sputtered target. The repetition frequency was 500 Hz at the deposition-averaged target power densities of 5 Wcm−2 and 50 Wcm−2 with a pulse-averaged target power density up to 2 kWcm−2. The pulse durations were 50 μs and 200 μs. Our model calculations show that the to-substrate O2 inlet provides systematically lower compound fractions in the target surface layer and higher compound fractions in the substrate surface layer, compared with the to-target O2 inlet. The low compound fractions in the target surface layer (being approximately 10% at the depositionaveraged target power density of 50 Wcm−2 and the pulse duration of 200 μs) result in high deposition rates of the films produced, which are in agreement with experimental values.

Abstract: The deactivation of Sn-Beta zeolite catalyst during retro-aldolization and isomerization of glucose is investigated. Confocal fluorescence microscopy reveals that retro-aldolization of glucose in CH3OH at 160 degrees C is accompanied with the build-up of insoluble oligomeric deposits in the micropores, resulting in a rapid catalyst deactivation. These deposits accumulate predominantly in the outer regions of the zeolite crystals, which points to mass transport limitations. Glucose isomerization in water is not only accompanied by the formation of insoluble deposits in the micropores, but also by the structural degradation of the zeolite due to desilication and destannation. Enhanced and sustained catalytic performance can be achieved by using ethanol/water mixtures as the reaction solvent instead of water.

Abstract: Because of high electrocatalytic activity, Pt based metal nanospheres (NSs) have attracted a lot of attention. Hence, multi-particle nano-single crystal coalesced PtCu NSs are designed and successfully synthesized by a cost-effective aqueous solution method. The formed PtCu NS catalyst exhibits a superior hydrogen evolution reaction (HER) electrocatalytic activity with an ultralow onset potential of 18 mV at the current density of 2 mA/cm(2) and high mass activity of 1.08 A/mg(pt) (7.2 times higher than that of commercial Pt/C catalysts). Also, it shows an enhancement of 3.2 and 2.7 times in the mass and specific activities toward oxygen reduction reaction (ORR) compared to that of Pt/C. Moreover, it possesses an excellent catalytic durability for both ORR and HER. Even after 10,000 cycles, its ORR mass activity retains 87% of its initial value. The density functional theory (DFT) calculations demonstrate that by introducing Cu atoms into the Pt lattice, a downshift of the D-band center and favorable hydrogen adsorption free energy of approaching to zero (Delta G) occur, indicating the increased electrocatalytic activity of Pt electrocatalysts. (C) 2019 Elsevier Inc. All rights reserved.

Abstract: Ultrafast laser irradiation can induce morphological and structural changes in plasmonic nanoparticles. Gold nanorods (Au NRs), in particular, can be welded together upon irradiation with femtosecond laser pulses, leading to dimers and trimers through the formation of necks between individual nanorods. We used electron tomography to determine the 3D (atomic) structure at such necks for representative welding geometries and to characterize the induced defects. The spatial distribution of localized surface plasmon modes for different welding configurations was assessed by electron energy loss spectroscopy. Additionally, we were able to directly compare the plasmon line width of single-crystalline and welded Au NRs with single defects at the same resonance energy, thus making a direct link between the structural and plasmonic properties. In this manner, we show that the occurrence of (single) defects results in significant plasmon broadening.

Abstract: Lead halide perovskites have been widely explored
in the field of photovoltaics, light-emitting diodes, and lasers due to
their outstanding linear and nonlinear optical (NLO) properties.
But, the presence of lead toxicity and low chemical stability remain
serious concerns. Lead-free double perovskite with excellent
optical properties and chemical stability could be an alternative.
However, proper examination of the NLO properties of such a
material is crucial to identify their utility for future nonlinear device
applications. Herein, we have made use of femtosecond (fs) Z-scan
technique to explore the NLO properties of Cs2AgIn0.9Bi0.1Cl6
nanocrystals (NCs). Our measurements suggest that under
nonresonant fs excitation, perovskite NCs exhibit strong twophoton
absorption (TPA). The observed saturation of TPA at high
light intensities has been explained by a customized model. Furthermore, we have demonstrated a change in the nonlinear refractive
index of the NCs under varying input intensities. The strong TPA absorption of lead-free double perovskite NCs could be used for
Kerr nonlinearity-based nonlinear applications such as optical shutters for picosecond lasers.

Abstract: The combination of AgNO3 with NaH results in Ag nanoparticles that can selectively perform alcohol aminations under mild reaction conditions (110 °C). NaH not only serves as a reducing agent for the Ag salt, but also activates the alcohol for dehydrogenation to the corresponding ketone/aldehyde. The stability of the particles can be improved by immobilizing them onto mixed Al2O3Ga2O3 supports; the combination of Ga and Al provides materials with stronger Lewis acidic sites compared to pure alumina or gallium oxide supports. This leads to catalysts with enhanced activities, without the necessity of adding external Lewis acids. Detailed TEM characterization also reveals a close interaction between the Ag NPs and the gallium oxide phase. The obtained catalysts are recyclable and show activity for the alcohol amination using a variety of aliphatic and aromatic amines under mild conditions.

Abstract: The R-2(MoO4)(3) (R = rare earth elements) molybdates doped with Eu3+ cations are interesting red-emitting materials for display and solid-state lighting applications. The structure and luminescent properties of the R2-xEux(MoO4)(3) (R = Gd, Sm) solid solutions have been investigated as a function of chemical composition and preparation conditions. Monoclinic (alpha) and orthorhombic (beta') R2-xEux(MoO4)(3) (R = Gd, Sm; 0 <= x <= 2) modifications were prepared by solid-state reaction, and their structures were investigated using synchrotron powder X-ray diffraction and transmission electron microscopy. The pure orthorhombic beta'-phases could be synthesized only by quenching from high temperature to room temperature for Gd2-xEux(MoO4)(3) in the Eu3+-rich part (x > 1) and for all Sm2-xEux(MoO4)(3) solid solutions. The transformation from the alpha-phase to the beta'-phase results in a notable increase (similar to 24%) of the unit cell volume for all R2-xEux(MoO4)(3) (R = Sm, Gd) solid solutions. The luminescent properties of all R2-xEux(MoO4)(3) (R = Gd, Sm; 0 <= x <= 2) solid solutions were measured, and their optical properties were related to their structural properties. All R2-xEux(MoO4)(3) (R = Gd, Sm; 0 <= x <= 2) phosphors emit intense red light dominated by the D-5(0)-> F-7(2) transition at similar to 616 nm. However, a change in the multiplet splitting is observed when switching from the monoclinic to the orthorhombic structure, as a consequence of the change in coordination polyhedron of the luminescent ion from RO8 to RO7 for the alpha- and beta'-modification, respectively. The Gd2-xEux(MoO4)(3) solid solutions are the most efficient emitters in the range of 0 < x < 1.5, but their emission intensity is comparable to or even significantly lower than that of Sm2-xEux(MoO4)(3) for higher Eu3+ concentrations (1.5 <= x <= 1.75). Electron energy loss spectroscopy (EELS) measurements revealed the influence of the structure and element content on the number and positions of bands in the ultraviolet-visible-infrared regions of the EELS spectrum.

Abstract: A polycrystalline sample of LuFe2O4 has been investigated by means of powder synchrotron x-ray and neutron diffraction and transmission electron microscopy (TEM), along with Mössbauer spectroscopy and transport and magnetic properties. A monoclinic distortion is unambiguously evidenced, and the crystal structure is refined in the monoclinic C2/m space group [aM = 5.9563(1) Å, bM = 3.4372(1) Å, cM = 8.6431(1) Å, β = 103.24(1)°]. Along with the previously reported modulations distinctive of the charge-ordering (CO) of the iron species, a new type of incommensurate order is observed, characterized by a vector q⃗1 = α1a⃗M* + γ1c⃗M* (with α1 ≅ 0.55, γ1 ≅ 0.13). In situ heating TEM observations from 300 to 773 K confirm that the satellites associated with q⃗1 vanish completely, only at a temperature significantly higher than the CO temperature. This incommensurate modulation has a displacive character and corresponds primarily to a transverse displacive modulation wave of the Lu cations position, as revealed by the high resolution, high angle annular dark field scanning TEM images and in agreement with synchrotron data refinements. Analyses of vacuum-annealed samples converge toward the hypothesis of a new ordering mechanism, associated with a tiny oxygen deviation from the O4 stoichiometry.

Abstract: In this study of the changes induced by exposing MWCNTs to a nitrogen plasma, it was found by HRTEM that the atomic nitrogen exposure does not significantly etch the surface of the carbon nanotube (CNT). Nevertheless, the atomic nitrogen generated by a microwave plasma effectively grafts amine, nitrile, amide, and oxime groups onto the CNT surface, as observed by XPS, altering the density of valence electronic states, as seen in UPS. (C) 2008 Elsevier Ltd. All fights reserved.

Abstract: This report describes the effect of light irradiation on the synthesis of silver nanowires by the well-known polyol method. High quality nanowires are produced in high yields when the reaction suspension is irradiated with 400500 nm light during the nucleation stage. These studies suggest that light accelerates the formation of the nanoparticle seeds most appropriate for nanowire growth.

Abstract: MOF-5 nanoparticles were prepared by mixing a solution of [Zn4O(C6H5COO)(6)] with a solution of benzene-1,4-dicarboxylic acid in DMF at ambient conditions. The former species mimics as a secondary building unit (SBU), and the latter acts as linker. Mixing of the two solutions induced the formation of MOF-5 nanoparticles in dilute suspension. The applied conditions were identified as suitable for a closer investigation of the particle formation process by combined light and small angle neutron scattering (SANS). Scattering analysis revealed a significant impact of the molar ratio of the two components in the reaction mixture. Excessive use of the building unit slowed down the process. A similar effect was observed upon addition of 4n-decylbenzoic acid, which is supposed to act as a modulator. The formation mechanism leads to initial intermediates, which turn into cubelike nanoparticles with a diameter of about 60-80 nm. This initial stage is followed by an extended formation period, where nucleation proceeds over hours, leading to an increasing number of nanoparticles with the same final size of 60-80 nm.

Abstract: A generalization of the real-space Greens-function approach is presented for ab initio calculations of relativistic electron energy loss spectra (EELS) which are particularly important in anisotropic materials. The approach incorporates relativistic effects in terms of the transition tensor within the dipole-selection rule. In particular, the method accounts for relativistic corrections to the magic angle in orientation resolved EELS experiments. The approach is validated by a study of the graphite C  K edge, for which we present an accurate magic angle measurement consistent with the predicted value.