“Nucleation and growth of the Ni5Al3 phase in Ni-Al austenite and martensite”. Schryvers D, Toth L, Ma Y, Tanner L, Journal de physique: 4
T2 –, IIIrd European Symposium on Martensitic Transformations (ESOMAT 94), SEP 14-16, 1994, BARCELONA, SPAIN 5, 299 (1995). http://doi.org/10.1051/jp4:1995246
Abstract: The nucleation and growth mechanisms of Ni5Al3 precipitates and microtwinned plates in B2 austenite and 2M (3R) martensite phases are described on the basis of conventional and high resolution electron microscopy. In the Ni62.5Al37.5 B2 austenite matrix short annealings at 550 degrees C introduce three-pointed star shaped precipitates consisting of twin related parts of different variants of the Ni5Al3 structure. Longer annealings result in plates growing separately from these wings and developing microtwinning in order to accommodate stress built-up at the interfaces with the surrounding matrix. Annealing of Ni65Al35 2M martensite plates induces simple reordering into the Ni5Al3 phase, increasing the fct c/a ratio by about 1%. As a result stracking faults are introduced in the smallest twin variants.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 3
DOI: 10.1051/jp4:1995246
|
|
|
“Special microstructures and twin features in Ti50Ni50-x(Pd,Au)x at small hysteresis”. Delville R, Shi H, James RD, Schryvers D, Diffusion and defect data : solid state data : part B : solid state phenomena 172/174, 105 (2011). http://doi.org/10.4028/www.scientific.net/SSP.172-174.105
Abstract: The breaking of symmetry due to atomic displacements in the austenite-martensite phase transformation generally leads to their crystallographic incompatibility. Energy minimizing accommodation mechanisms such as martensite twinning have been recently shown to be a source of hysteresis and irreversible plastic deformation. Compatibility between the two phases can however be achieved by carefully tuning lattice parameters through composition change. A dramatic drop in hysteresis and novel microstructures such as a lowering of the amount of twin lamella are then observed. Related theoretical and simulation works also support the existence of such microstructures including peculiar self-accommodating configurations at near-compatibility. We present the transmission electron microscopy (TEM) study of these novel microstructures for the alloy systems Ti50Ni50-xPdx and Ti50Ni50-xAux where the composition was systemically tuned to approach perfect compatibility. High resolution imaging of the interface between austenite and martensite supplies evidences of compatibility at the atomic level.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 3
DOI: 10.4028/www.scientific.net/SSP.172-174.105
|
|
|
“A temperature study of mixed AgBr-AgBrI tabular crystals”. Goessens C, Schryvers D, van Landuyt J, Geuens I, Gijbels R, Jacob W, de Keyzer R Hawaii, page 70 (1995).
Keywords: H1 Book chapter; Electron microscopy for materials research (EMAT); Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Times cited: 3
|
|
|
“Transmission electron microscopy study of low-hysteresis shape memory alloys”. Delville R, James RD, Salman U, Finel A, Schryvers D, , 02005 (2009). http://doi.org/10.1051/esomat/200902005
Abstract: Recent findings have linked low hysteresis in shape memory alloys with phase compatibility between austenite and martensite. In order to investigate the evolution of microstructure as the phase compatibility increases and the hysteresis is reduced, transmission electron microscopy was used to study the alloy system Ti50Ni50-xPdx where the composition is systemically tuned to approach perfect compatibility. Changes in morphology, twinning density and twinning modes are reported along with special microstructures occurring when the compatibility is achieved. In addition, the interface between austenite and a single variant of martensite was studied by high-resolution and conventional electron microscopy. The atomically sharp, defect free, low energy configuration of the interface suggests that it plays an important role in the lowering of hysteresis. Finally, dynamical modeling of the martensitic transformation using the phase-field micro-elasticity model within the geometrically linear theory succeeded in reproducing the change in microstructure as the compatibility condition is satisfied. Latest results on the extension of these findings in other Ni-Ti based ternary/quaternary systems are also reported.
Keywords: P1 Proceeding; Electron microscopy for materials research (EMAT)
Times cited: 3
DOI: 10.1051/esomat/200902005
|
|
|
“Transmission electron microscopy study of microstructural evolution in nanograined Ni-Ti microwires heat treated by electric pulse”. Delville R, Malard B, Pilch J, Sittner P, Schryvers D, Diffusion and defect data : solid state data : part B : solid state phenomena 172/174, 682 (2011). http://doi.org/10.4028/www.scientific.net/SSP.172-174.682
Abstract: Transmission electron microscopy and mechanical testing were employed to investigate the evolution of microstructure and functional superelastic properties of 0.1mm diameter as-drawn Ni-Ti wires subjected to a non-conventional heat treatment by controlled electric pulse current. This method enables a finer control of the recovery and recrystallisation processes taking place during the heat treatment and accordingly a better control on the final microstructure. The best functional properties were obtained for heat-treated Ni-Ti wires having a nanograined microstructure (20-50 nm) partially recovered through polygonization and partially recrystallized. Such microstructure is highly resistant against dislocation slip upon cycling, while microstructures annealed for longer time and showing mostly recrystallized grains were prone to dislocation slip, particularly as the grain size exceeds 100 nm. The density of dislocation defects increased significantly with increasing grain size of the microstructure. The activity of three <100>/{011} slip systems was identified in the largest grains of 500-1200 nm. An additional mode of plastic deformation, {114} compound austenite twinning, was observed in the largest grains of fully recrystallized microstructures. It is proposed that dislocation slip (and possibly deformation twinning) occurring in superelastic cycling is coupled with the stress-induced martensitic transformation.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 3
DOI: 10.4028/www.scientific.net/SSP.172-174.682
|
|
|
“Microstructure and phase composition characterization in a Co38Ni33Al29 ferromagnetic shape memory alloy”. Lu JB, Schryvers D, Materials characterization 118, 9 (2016). http://doi.org/10.1016/j.matchar.2016.04.028
Abstract: Transmission electron microscopy was performed to investigate the microstructures of a secondary phase and its surrounding matrix in a Co38Ni33Al29 ferromagnetic shape memory alloy. The secondary phase shows a γ′ L12 structure exhibiting a dendritic morphology with enclosed B2 austenite regions while the matrix shows the L10 martensitic structure. A secondary phase-austenite-martensite sandwich structure with residual austenite ranging from several hundred nanometers to several micrometers wide is observed at the secondary phase-martensite interface due to the depletion of Co and enrichment of Al in the chemical gradient zone and the effect of the strong martensitic start temperature dependency of the element concentrations. The crystallographic orientation relationship of the secondary phase and the B2 austenite fits the Kurdjumov-Sachs relationship.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 2.714
Times cited: 3
DOI: 10.1016/j.matchar.2016.04.028
|
|
|
“Influence of M23C6 dissolution on the kinetics of ferrite to austenite transformation in Fe-11Cr-0.06C stainless steel”. Miotti Bettanini A, Ding L, Mithieux J-D, Parrens C, Idrissi H, Schryvers D, Delannay L, Pardoen T, Jacques PJ, Materials &, design 162, 362 (2019). http://doi.org/10.1016/j.matdes.2018.12.005
Abstract: The design of high-strength martensitic stainless steels requires an accurate control over the stability of undesired phases, like carbides and ferrite, which can hamper strength and ductility. Here, the ferrite to austenite transformation in Fe-11Cr-0.06C has been studied with a combined experimental-modelling approach. Experimental observations of the austenization process indicate that austenite growth proceeds in multiple steps, each one characterized by a different transformation rate. DICTRA based modelling reveals that the dissolution of the M23C6 Cr-rich carbides leads to Cr partitioning between austenite and parent phases, which controls the rate of transformation through (i) a soft-impingement effect and (ii) consequent stabilization of the ferrite, which remains untransformed inside chromium-enriched-zones even after prolonged austenization stage. Slow heating rate and smaller initial particle sizes allow the design of ferrite-free microstructure.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.364
Times cited: 3
DOI: 10.1016/j.matdes.2018.12.005
|
|
|
“Orientation relationship of the austenite-to-ferrite transformation in austenitic stainless steels due to dissolution corrosion in contact with liquid Pb-Bi eutectic”. Charalampopoulou E, Cautaerts N, Van der Donck T, Schryvers D, Lambrinou K, Delville R, Scripta materialia 167, 66 (2019). http://doi.org/10.1016/J.SCRIPTAMAT.2019.03.035
Abstract: The orientation relationship of an austenite-to-ferrite phase transformation in 316L stainless steels induced by the loss of austenite stabilizers resulting from the steel dissolution corrosion in liquid Pb-Bi eutectic was studied by means of electron backscatter diffraction. The misorientations at the austenite/ferrite interface were compared to the prevailing orientation relationship models in steels. The Pitsch orientation relationship model was found to be predominant, which is unusual for austenite-to-ferrite bulk transformations in steels. The nature of this particular transformation, which involves loss of steel alloying elements and the presence of an interfacial liquid metal layer, is discussed to explain this finding. (C) 2019 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.747
Times cited: 3
DOI: 10.1016/J.SCRIPTAMAT.2019.03.035
|
|
|
“A comparative investigation of replication techniques used for the study of (S+Au) sensitized AgBr microcrystals”. Buschmann V, Schryvers D, van Landuyt J, van Roost C, de Keyzer R, The journal of imaging science and technology 40, 189 (1996)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.349
Times cited: 4
|
|
|
“Dynamic shear localization in Ti6Al4V”. Peirs J, Verleysen P, Tirry W, Rabet L, Schryvers D, Degrieck J, Procedia Engineering
T2 –, 11th International Conference on the Mechanical Behavior of Materials, (ICM), 2011, Como, ITALY (ICM11) , 1 (2011). http://doi.org/10.1016/j.proeng.2011.04.386
Abstract: The alloy Ti6Al4V is known to be prone to the formation of adiabatic shear bands when dynamically loaded in shear. This causes a catastrophic decrease of the load carrying capacity and is usually followed by fracture. Although, the main mechanism is recognized to be the competition between strain hardening and thermal softening, a detailed understanding of the role of microstructural plasticity mechanisms and macroscopic loading conditions does not exist yet. To study strain localization and shear fracture, different high strain rate shear tests have been carried out: compression of hat-shaped specimens, torsion of thin walled tubular specimens and in-plane shear tests. The value of the three techniques in studying shear localization is evaluated. Post-mortem analysis of the fracture surface and the materials' microstructure is performed with optical and electron microscopy. In all cases a ductile fracture is observed. SEM and TEM techniques are used to study the local microstructure and composition in the shear band and as such the driving mechanism for the ASB formation. (C) 2011 Published by Elsevier Ltd. Selection and/or peer-review under responsibility of ICM11
Keywords: P1 Proceeding; Electron microscopy for materials research (EMAT)
Times cited: 4
DOI: 10.1016/j.proeng.2011.04.386
|
|
|
“Review of phonon behaviour and microstructural development leading to martensitic transformations in NixAl100-x alloys”. Tanner LE, Shapiro SM, Schryvers D, Noda Y, Shape memory materials and phenomena: fundamental aspects and applications 246, 265 (1992)
Keywords: A3 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 4
|
|
|
“Internal architecture of coffin-shaped ZSM-5 zeolite crystals with hourglass contrast unravelled by focused ion beam-assisted transmission electron microscopy: INTERNAL ARCHITECTURE OF COFFIN-SHAPED”. Lu J, Bartholomeeusen E, Sels BF, Schryvers D, Journal of microscopy 265, 27 (2017). http://doi.org/10.1111/jmi.12459
Abstract: Optical microscopy, focused ion beam and transmission electron microscopy are combined to study the internal architecture in a coffin-shaped ZSM-5 crystal showing an hourglass contrast in optical microscopy. Based on parallel lamellas from different positions in the crystal, the orientation relationships between the intergrowth components of the crystal are studied and the internal architecture and growth mechanism are illustrated. The crystal is found to contain two pyramid-like components aside from a central component. Both pyramid-like components are rotated by 90 degrees along the common c-axis and with respect to the central component while the interfaces between the components show local zig-zag feature, the latter indicating variations in relative growth velocity of the two components. The pyramid-like intergrowth components are larger and come closer to one another in the middle of the crystal than at the edges, but they do not connect. A model of multisite nucleation and growth of 90 degrees intergrowth components is proposed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.692
Times cited: 4
DOI: 10.1111/jmi.12459
|
|
|
“Ni cluster formation in low temperature annealed Ni50.6Ti49.4”. Pourbabak S, Wang X, Van Dyck D, Verlinden B, Schryvers D, Functional materials letters 10, 1740005 (2017). http://doi.org/10.1142/S1793604717400057
Abstract: Various low temperature treatments of Ni50.6Ti49.4 have shown an unexpected effect on the martensitic start temperature. Periodic diffuse intensity distributions in reciprocal space indicate the formation of short pure Ni strings along the <111> directions in the B2 ordered lattice, precursing the formation of Ni4Ti3 precipitates formed at higher annealing temperatures.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 1.234
Times cited: 4
DOI: 10.1142/S1793604717400057
|
|
|
“Enhancement of toughness of Al-to-steel Friction Melt Bonded welds via metallic interlayers”. Jimenez-Mena N, Jacques PJ, Ding L, Gauquelin N, Schryvers D, Idrissi H, Delannay F, Simar A, Materials science and engineering: part A: structural materials: properties, microstructure and processing 740-741, 274 (2019). http://doi.org/10.1016/j.msea.2018.10.101
Abstract: The toughness of Al-to-steel welds decreases with increasing thickness of the intermetallic (IM) layer formed at the interface. Co plating has been added as interlayer in Al-to-steel Friction Melt Bonded (FMB) welds to control the nature and thickness of the IM layer. In comparison to a weld without interlayer, Co plating brings about a reduction of the thickness of the IM layer by 70%. The critical energy release rate of the crack propagating in the weld is used as an indicator of toughness. It is evaluated via an adapted crack propagation test using an energy conservation criterion. For a weld without interlayer, critical energy release rate is found to increase when the thickness of the intermetallic layer decreases. When the intermetallic layer is thick, the crack propagates in a brittle manner through the intermetallic whereas, at low layer thickness, the crack deviates and partially propagates through the Al plate, which causes an increase of toughness. The use of a Co interlayer brings about an increase of toughness by causing full deviation of the crack towards the Al plate.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 4
DOI: 10.1016/j.msea.2018.10.101
|
|
|
“Decomposition of a metastable bcc phase in rapidly solidified Ni-9 at.% Zr and Ni-8 at.%X alloys”. Chandrasekaran M, Ghosh G, Schryvers D, de Graef M, Delaey L, Van Tendeloo G, Philosophical magazine: A: physics of condensed matter: defects and mechanical properties 75, 677 (1997)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 5
|
|
|
“Effect of annealing on the transformation behavior and mechanical properties of two nanostructured Ti-50.8at.%Ni thin wires produced by different methods”. Wang X, Amin-Ahmadi B, Schryvers D, Verlinden B, Van Humbeeck J, Materials science forum 738/739, 306 (2013). http://doi.org/10.4028/www.scientific.net/MSF.738-739.306
Abstract: A Ti-50.8at.%Ni wire produced using a co-drawing method and a commercial Ti-50.8at.%Ni wire were annealed at different temperatures between 450°C and 700°C. Grains with diameter less than 100nm were revealed by transmission electron microscopy for both wires before annealing treatment. However, the microstructural heterogeneity of the co-drawn wire is more obvious than that of the commercial wire. Multi-stage martensitic transformation was observed in the co-drawn wire, compared with the one-stage A↔M transformation in the commercial wire after annealing at 600°C for 30min. The differences of total elongation, plateau strain and pseudoelastic recoverable strain between the commercial wire and the co-drawn wire were also observed. The differences of the transformation behavior and mechanical properties between the commercial wire and the co-drawn wire are attributed to the microstructural difference between these two wires.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 5
DOI: 10.4028/www.scientific.net/MSF.738-739.306
|
|
|
“Electron microscopy of stress-induced martensite and pretransition microstructures in Ni62.5Al37.5”. Schryvers D, Tanner LE, Shape memory materials and phenomena: fundamental aspects and applications 246, 33 (1992)
Keywords: A3 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 5
|
|
|
“Functional twin boundaries”. Van Aert S, Turner S, Delville R, Schryvers D, Van Tendeloo G, Ding X, Salje EKH, Phase transitions 86, 1052 (2013). http://doi.org/10.1080/01411594.2012.748909
Abstract: Functional interfaces are at the core of research in the emerging field of domain boundary engineering where polar, conducting, chiral, and other interfaces and twin boundaries have been discovered. Ferroelectricity was found in twin walls of paraelectric CaTiO3. We show that the effect of functional interfaces can be optimized if the number of twin boundaries is increased in densely twinned materials. Such materials can be produced by shear in the ferroelastic phase rather than by rapid quench from the paraelastic phase.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.06
Times cited: 5
DOI: 10.1080/01411594.2012.748909
|
|
|
“In-situ TEM study of the Ni5Al3 to B2 + L12 decomposition in Ni65Al35”. Schryvers D, Ma Y, Materials letters 23, 105 (1995). http://doi.org/10.1016/0167-577X(95)00030-5
Abstract: Homogenised and quenched Ni65Al35 samples were heated and studied in situ in a CM20 electron microscope up to 900 degrees C. The Ni5Al3 phase first forming around 550 degrees C in the quenched L1(0) microtwinned martensite starts to decompose around 800 degrees C yielding B2 precipitates in a twinned L1(2) matrix. The latter twinning is a remainder of the microtwinning in the original room temperature martensite. Also the crystallographic relations between precipitates and matrix can be traced back to the original formation of twinned martensite plates within the austenite. Some aspects of the dynamics of the process are discussed on the basis of snap shots and video recordings.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.489
Times cited: 5
DOI: 10.1016/0167-577X(95)00030-5
|
|
|
“Morphological characterization and distribution of autocatalytic-grown Ni4Ti3 precipitates in a Ni-Ti single crystal”. Cao S, Ke CB, Zhang XP, Schryvers D, Journal of alloys and compounds 577, 215 (2013). http://doi.org/10.1016/j.jallcom.2012.02.013
Abstract: The 3D size, morphology and distribution of autocatalytic-grown Ni4Ti3 precipitates in a Ni51Ti49 single crystal were characterized via a FIB/SEM Slice-and-View procedure and phase-field simulation. Important parameters on size and shape of the precipitates were measured. The pair distribution function and the minimum distance between two precipitates from different variants were calculated to describe the 3D distribution of the autocatalytic-grown Ni4Ti3 precipitates in single crystal Ni-Ti, with a comparison to the polycrystalline Ni50.8Ti49.2 alloy. Phase-field simulation was conducted to study the nucleation behavior of precipitates in the single crystal Ni-Ti. (C) 2012 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.133
Times cited: 5
DOI: 10.1016/j.jallcom.2012.02.013
|
|
|
“Structure of multi-grain spherical particles in an amorphous Ti50Ni25Cu25 melt-spun ribbon”. Santamarta R, Schryvers D, Materials science and engineering: part A: structural materials: properties, microstructure and processing 378, 143 (2004). http://doi.org/10.1016/j.msea.2003.11.060
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 5
DOI: 10.1016/j.msea.2003.11.060
|
|
|
“Mechanical behavior of ultrathin sputter deposited porous amorphous Al2O3 films”. van der Rest A, Idrissi H, Henry F, Favache A, Schryvers D, Proost J, Raskin J-P, Van Overmeere Q, Pardoen T, Acta materialia 125, 27 (2017). http://doi.org/10.1016/j.actamat.2016.11.037
Abstract: The determination of the mechanical properties of porous amorphous Al2O3 thin films is essential to address reliability issues in wear-resistant, optical and electronic coating applications. Testing the mechanical properties of Al2O3 films thinner than 200 nm is challenging, and the link between the mechanical behavior and the microstructure of such films is largely unknown. Herein, we report on the elastic and viscoplastic mechanical properties of amorphous Al2O3 thin films synthesized by reactive magnetron sputtering using a combination of internal stress, nanoindentation, and on-chip uniaxial tensile testing, together with mechanical homogenization models to separate the effect of porosity from intrinsic variations of the response of the sound material. The porosity is made of voids with 2e30 nm diameter. The Young's modulus and hardness of the films decrease by a factor of two when the deposition pressure increases from 1.2 to 8 mTorr. The contribution of porosity was found to be small, and a change in the atomic structure of the amorphous Al2O3 matrix is hypothesized to be the main contributing factor. The activation volume associated to the viscoplastic deformation mechanism is around 100 Å3. Differences in the atomic structure of the films could not be revealed by electron diffraction, pointing to a minute effect of atomic arrangement on the elastic properties.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 5.301
Times cited: 5
DOI: 10.1016/j.actamat.2016.11.037
|
|
|
“Towards biolubricant compatible vegetable oils by pore mouth hydrogenation with shape-selective Pt/ZSM-5 catalysts”. Van Aelst J, Philippaerts A, Bartholomeeusen E, Fayad E, Thibault-Starzyk F, Lu J, Schryvers D, Ooms R, Verboekend D, Jacobs P, Sels B, Catalysis science &, technology 6, 2820 (2016). http://doi.org/10.1039/C6CY00498A
Abstract: Pt/ZSM-5 catalysts with various crystal sizes were prepared via competitive ion-exchange, followed by a slow activation procedure. Even when using very large ZSM-5 crystals, highly dispersed Pt nano-clusters were contained within the zeolite crystal's voids, as ascertained by 2D pressure-jump IR spectroscopy of adsorbed CO and focussed ion-beam transmission electron microscopy. The shape-selective properties of the Pt/ZSM-5 catalysts were evaluated in the partial hydrogenation of soybean oil. Unique hydrogenation selectivities were observed, as the fatty acids located at the central position of the triacylglycerol (TAG) molecules were preferentially hydrogenated. The resulting oil has therefore high levels of intermediately melting TAGs, which are compatible with biolubricants due to their improved oxidative stability and still appropriate low-temperature fluidity. The TAG distribution in the partially hydrogenated soybean oil samples was independent from the zeolite crystal size, while the hydrogenation activity linearly increases with the crystal's external surface area. This trend was confirmed with a Pt loaded mesoporous ZSM-5 zeolite, obtained via a mild alkaline treatment. These observations imply and confirm a genuine pore mouth catalysis mechanism, in which only one fatty acid chain of the TAG is able to enter the micropores of ZSM-5, where the double bonds are hydrogenated by the crystal encapsulated Pt-clusters.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.773
Times cited: 5
DOI: 10.1039/C6CY00498A
|
|
|
“Transmission electron microscopy study of complex oxide scales on DIN 1.4970 steel exposed to liquid Pb-Bi eutectic”. Charalampopoulou E, Delville R, Verwerft M, Lambrinou K, Schryvers D, Corrosion science 147, 22 (2019). http://doi.org/10.1016/j.corsci.2018.10.018
Abstract: The deployment of Gen-IV lead-cooled fast reactors requires a good compatibility between the selected structural/cladding steels and the inherently corrosive heavy liquid metal coolant. An effective liquid metal corrosion mitigation strategy involves the in-situ steel passivation in contact with the oxygen-containing Pb-alloy coolant. Transmission electron microscopy was used in this work to study the multi-layered oxide scales forming on an austenitic stainless steel fuel cladding exposed to oxygen-containing (CO ≈ 10−6 mass%) static liquid leadbismuth eutectic (LBE) for 1000 h between 400 and 500 °C. The oxide scale constituents were analyzed, including the intertwined phases comprising the innermost biphasic layer.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Times cited: 5
DOI: 10.1016/j.corsci.2018.10.018
|
|
|
“On the formation mechanisms of intragranular shear bands in olivine by stress-induced amorphization”. Idrissi H, Béché, A, Gauquelin N, Ul-Haq I, Bollinger C, Demouchy S, Verbeeck J, Pardoen T, Schryvers D, Cordier P, Acta materialia 239, 118247 (2022). http://doi.org/10.1016/J.ACTAMAT.2022.118247
Abstract: Intragranular amorphization shear lamellae are found in deformed olivine aggregates. The detailed trans-mission electron microscopy analysis of intragranular lamella arrested in the core of a grain provides novel information on the amorphization mechanism. The deformation field is complex and heteroge-neous, corresponding to a shear crack type instability involving mode I, II and III loading components. The formation and propagation of the amorphous lamella is accompanied by the formation of crystal defects ahead of the tip. These defects are geometrically necessary [001] dislocations, characteristics of high-stress deformation in olivine, and rotational nanodomains which are tentatively interpreted as disclinations. We show that these defects play an important role in dictating the path followed by the amorphous lamella. Stress-induced amorphization in olivine would thus result from a direct crystal-to -amorphous transformation associated with a shear instability and not from a mechanical destabilization due to the accumulation of high number of defects from an intense preliminary deformation. The pref-erential alignment of some lamellae along (010) is a proof of the lower ultimate mechanical strength of these planes.(c) 2022 The Authors. Published by Elsevier Ltd on behalf of Acta Materialia Inc. This is an open access article under the CC BY license ( http://creativecommons.org/licenses/by/4.0/ )
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 9.4
Times cited: 5
DOI: 10.1016/J.ACTAMAT.2022.118247
|
|
|
“Acquisition of the EELS data cube by tomographic reconstruction”. van den Broek W, Verbeeck J, de Backer S, Scheunders P, Schryvers D, Ultramicroscopy 106, 269 (2006). http://doi.org/10.1016/j.ultramic.2005.09.001
Abstract: Energy filtered TEM, EFTEM, provides three-dimensional data, two spatial and one spectral dimension. We propose to acquire these data by measuring a series of images with a defocused energy filter. It will be shown that each image is a projection of the data on the detector and that reconstruction of the data out of a sufficient number of such projections using a tomographic reconstruction algorithm is possible. This technique uses only a fraction of the electron dose an energy filtered series (EFS) needs for the same spectral and spatial resolution and the same mean signal-to-noise ratio. (c) 2005 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 2.843
Times cited: 6
DOI: 10.1016/j.ultramic.2005.09.001
|
|
|
“Advanced three-dimensional electron microscopy techniques in the quest for better structural and functional materials”. Schryvers D, Cao S, Tirry W, Idrissi H, Van Aert S, Science and technology of advanced materials 14, 014206 (2013). http://doi.org/10.1088/1468-6996/14/1/014206
Abstract: After a short review of electron tomography techniques for materials science, this overview will cover some recent results on different shape memory and nanostructured metallic systems obtained by various three-dimensional (3D) electron imaging techniques. In binary NiTi, the 3D morphology and distribution of Ni4Ti3 precipitates are investigated by using FIB/SEM slice-and-view yielding 3D data stacks. Different quantification techniques will be presented including the principal ellipsoid for a given precipitate, shape classification following a Zingg scheme, particle distribution function, distance transform and water penetration. The latter is a novel approach to quantifying the expected matrix transformation in between the precipitates. The different samples investigated include a single crystal annealed with and without compression yielding layered and autocatalytic precipitation, respectively, and a polycrystal revealing different densities and sizes of the precipitates resulting in a multistage transformation process. Electron tomography was used to understand the interaction between focused ion beam-induced Frank loops and long dislocation structures in nanobeams of Al exhibiting special mechanical behaviour measured by on-chip deposition. Atomic resolution electron tomography is demonstrated on Ag nanoparticles in an Al matrix.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.798
Times cited: 6
DOI: 10.1088/1468-6996/14/1/014206
|
|
|
“Applications of advanced transmission electron microscopic techniques to Ni-Ti based shape memory materials”. Schryvers D, Potapov P, Santamarta R, Tirry W, Materials science and engineering: part A: structural materials: properties, microstructure and processing 378, 11 (2004). http://doi.org/10.1016/j.msea.2003.10.325
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 6
DOI: 10.1016/j.msea.2003.10.325
|
|
|
“Martensitic transformations and microstructures in splat-cooled Ni-Al”. Schryvers D, Holland-Moritz D, Materials science and engineering: part A: structural materials: properties, microstructure and processing 273/275, 697 (1999). http://doi.org/10.1016/S0921-5093(99)00399-8
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 6
DOI: 10.1016/S0921-5093(99)00399-8
|
|
|
“Electron-diffraction evidence for ordering of interstitial silver ions in silver bromide microcrystals”. Goessens C, Schryvers D, van Dyck D, van Landuyt J, de Keyzer R, Physica status solidi: A 143, 277 (1994). http://doi.org/10.1002/pssa.2211430211
Abstract: The occurrence and origin of diffuse intensity contours in electron micrographs of AgBr crystals are investigated. The observations are interpreted in terms of a model, which attributes diffuse scattering to the presence of predominant atom or vacancy clusters of a particular polyhedral type. It is shown that irrespective of the crystal morphology, interstitial Ag ions order in AgBr material in clusters of finite size along 001 type planes. A different geometry of the diffuse intensity locus observed for triangular and hexagonal tabular grains is explained in terms of the different twin plane morphology of these grains.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Times cited: 7
DOI: 10.1002/pssa.2211430211
|
|