“Addition of yttrium into HfO2 films: microstructure and electrical properties”. Dubourdieu C, Rauwel E, Roussel H, Ducroquet F, Hollaender B, Rossell M, Van Tendeloo G, Lhostis S, Rushworth S, Journal of vacuum science and technology: A: vacuum surfaces and films 27, 503 (2009). http://doi.org/10.1116/1.3106627
Abstract: The cubic phase of HfO2 was stabilized by addition of yttrium in thin films grown on Si/SiO2 by metal-organic chemical vapor deposition. The cubic phase was obtained for contents of 6.5 at. % Y or higher at a temperature as low as 470 °C. The complete compositional range (from 1.5 to 99.5 at. % Y) was investigated. The crystalline structure of HfO2 was determined from x-ray diffraction, electron diffraction, and attenuated total-reflection infrared spectroscopy. For cubic films, the continuous increase in the lattice parameter indicates the formation of a solid-solution HfO2Y2O3. As shown by x-ray photoelectron spectroscopy, yttrium silicate is formed at the interface with silicon; the interfacial layer thickness increases with increasing yttrium content and increasing film thickness. The dependence of the intrinsic relative permittivity r as a function of Y content was determined. It exhibits a maximum of ~30 for ~8.8 at. % Y. The cubic phase is stable upon postdeposition high-temperature annealing at 900 °C under NH3.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.374
Times cited: 29
DOI: 10.1116/1.3106627
|
|
|
“Adsorption of potassium and oxygen on graphite: a theoretical study”. Lamoen D, Persson BNJ, Journal Of Chemical Physics 108, 3332 (1998). http://doi.org/10.1063/1.475732
Keywords: A1 Journal article; Electron Microscopy for Materials Science (EMAT);
Impact Factor: 2.965
Times cited: 91
DOI: 10.1063/1.475732
|
|
|
“Adsorption of sulfur onto a surface of silver nanoparticles stabilized with sago starch biopolymer”. Djoković, V, Krsmanović, R, Božanić, DK, McPherson M, Van Tendeloo G, Nair PS, Georges MK, Radhakrishnan T, Colloids and surfaces: B : biointerfaces 73, 30 (2009). http://doi.org/10.1016/j.colsurfb.2009.04.022
Abstract: Adsorption of sulfide ions onto a surface of starch capped silver nanoparticles upon addition of thioacetamide was investigated. UVvis absorption spectroscopy revealed that the adsorption of the sulfide ion on the surface of the silver nanoparticles induced damping as well as blue shift of the silver surface plasmon resonance band. Further increase in thioacetamide concentration led to shift of the resonance band toward higher wavelengths indicating the formation of the continuous Ag2S layer on the silver surface. Thus fabricated nanoparticles were investigated using electron microscopy techniques (TEM, HRTEM, and HAADF-STEM) and X-ray photoelectron spectroscopy (XPS), which confirmed their coreshell structure.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.887
Times cited: 41
DOI: 10.1016/j.colsurfb.2009.04.022
|
|
|
“Advanced electron microscopy and its possibilities to solve complex structures: application to transition metal oxides”. Van Tendeloo G, Hadermann J, Abakumov AM, Antipov EV, Journal of materials chemistry 19, 2660 (2009). http://doi.org/10.1039/b817914j
Abstract: Design and optimization of materials properties can only be performed through a thorough knowledge of the structure of the compound. In this feature article we illustrate the possibilities of advanced electron microscopy in materials science and solid state chemistry. The different techniques are briefly discussed and several examples are given where the structures of complex oxides, often with a modulated structure, have been solved using electron microscopy.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 9
DOI: 10.1039/b817914j
|
|
|
“Advanced electron microscopy characterisation of important precipitation and ordering phenomena in shape memory systems”. Schryvers D, Shape memory and superelasticity 1, 78 (2015). http://doi.org/10.1007/s40830-015-0006-3
Abstract: The present paper discusses some important aspects of precipitation and ordering in alloy systems that show a martensitic transformation and can or are used as shape memory or superelastic metallic systems. The precipitates are investigated by a variety of conventional and advanced electron microscopy techniques, including atomic resolution, 3D slice-and-view, energy loss spectroscopy etc. Depending on the system, such secondary phases can decrease the probability of a displacive transformation by changing the phase stability in the system, such as in the case of NiAl or NiTiPd, or can mechanically hinder the passage of the transformation interface, as in NiTiNb. On the other hand, properly controlling the nucleation and growth of some precipitates can strongly improve the properties of some types of materials, as is the case for the well-known Ni4Ti3 precipitates.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
DOI: 10.1007/s40830-015-0006-3
|
|
|
“Advanced electron microscopy for advanced materials”. Van Tendeloo G, Bals S, Van Aert S, Verbeeck J, van Dyck D, Advanced materials 24, 5655 (2012). http://doi.org/10.1002/adma.201202107
Abstract: The idea of this Review is to introduce newly developed possibilities of advanced electron microscopy to the materials science community. Over the last decade, electron microscopy has evolved into a full analytical tool, able to provide atomic scale information on the position, nature, and even the valency atoms. This information is classically obtained in two dimensions (2D), but can now also be obtained in 3D. We show examples of applications in the field of nanoparticles and interfaces.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 19.791
Times cited: 107
DOI: 10.1002/adma.201202107
|
|
|
Goris B (2014) Advanced electron tomography : 3 dimensional structural characterisation of nanomaterials down to the atomic scale. Antwerpen
Keywords: Doctoral thesis; Electron microscopy for materials research (EMAT)
|
|
|
“Advanced reconstruction algorithms for electron tomography : from comparison to combination”. Goris B, Roelandts T, Batenburg KJ, Heidari Mezerji H, Bals S, Ultramicroscopy 127, 40 (2013). http://doi.org/10.1016/j.ultramic.2012.07.003
Abstract: In this work, the simultaneous iterative reconstruction technique (SIRT), the total variation minimization (TVM) reconstruction technique and the discrete algebraic reconstruction technique (DART) for electron tomography are compared and the advantages and disadvantages are discussed. Furthermore, we describe how the result of a three dimensional (3D) reconstruction based on TVM can provide objective information that is needed as the input for a DART reconstruction. This approach results in a tomographic reconstruction of which the segmentation is carried out in an objective manner.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 2.843
Times cited: 63
DOI: 10.1016/j.ultramic.2012.07.003
|
|
|
“Advanced TEM and SEM methods applied to 3D nano- and microstructural investigations of Ni4Ti3 precipitates in Ni-Ti (SMA)”. Schryvers D, Tirry W, Cao S, Diffusion and defect data : solid state data : part B : solid state phenomena 172/174, 229 (2011). http://doi.org/10.4028/www.scientific.net/SSP.172-174.229
Abstract: Two different kinds of experimental approaches yielding three-dimensional structural information on metastable semi-coherent precipitates are demonstrated. By combining high-resolution images from two independent viewing directions a full description of the strain field surrounding a nano-sized Ni4Ti3 precipitate in Ni-Ti can be obtained. The principal axes and strains correlate well with the transformation strain of the observed R-phase transformation close to the precipitate. Using a slice-and-view procedure in a FIB/SEM dual-beam instrument, a three-dimensional voxel dataset is produced from which morphological and distributional information on the same precipitates can be obtained yielding new insight into the particular transformation paths of these alloys, relevant for their functional behaviour.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
DOI: 10.4028/www.scientific.net/SSP.172-174.229
|
|
|
“Advanced TEM investigation of the plasticity mechanisms in nanocrystalline freestanding palladium films with nanoscale twins”. Wang B, Idrissi H, Galceran M, Colla MS, Turner S, Hui S, Raskin JP, Pardoen T, Godet S, Schryvers D, International journal of plasticity 37, 140 (2012). http://doi.org/10.1016/j.ijplas.2012.04.003
Abstract: Nanocrystalline palladium thin films deposited by electron-beam evaporation and deformed by on-chip tensile testing reveal a surprisingly large strain hardening capacity when considering the small similar to 25 nm grain size. The as-grown films contain several coherent single and multifold twin boundaries. The coherency of the twin boundaries considerably decreases with deformation due to dislocation/twin boundary interactions. These reactions are described based on a detailed analysis of the number and the type of dislocations located at the twin boundaries using high-resolution TEM, including aberration corrected microscopy. Sessile Frank dislocations were observed at the twin/matrix interfaces, explaining the loss of the TB coherency due to the Burgers vector pointing out of the twinning plane. Grain boundary mediated processes were excluded as a mechanism dominating the plastic deformation based on the investigation of the grain size distribution as well as the crystallographic texture using Automated Crystallographic Orientation Indexation TEM. Other factors influencing the plastic deformation such as impurities and the presence of a native passivation oxide layer at the surface of the films were investigated using analytical TEM. The twin boundaries observed in the present work partly explain the high strain hardening capacity by providing both increasing resistance to dislocation motion with deformation and a source for dislocation multiplication. (C) 2012 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.702
Times cited: 44
DOI: 10.1016/j.ijplas.2012.04.003
|
|
|
“Advanced TEM investigations on Ni-Ti shape memory material: strain and concentration gradients surrounding Ni4Ti3 precipitates”. Schryvers D, Tirry W, Yang Z, , 329 (2005)
Abstract: Lattice deformations and concentration gradients surrounding Ni4Ti3 precipitates grown by appropriate annealing in a Ni51Ti49 B2 austenite matrix are determined by a combination of TEM techniques. Quantitative Fourier analysis of HRTEM images reveals a deformed nanoscale region with lattice deformations up to 2% while EELS and EDX indicate a Ni depleted zone up to 150 nm away from the matrix-precipitate interface.
Keywords: P1 Proceeding; Electron microscopy for materials research (EMAT)
|
|
|
“Advanced TEM studies of martensite and related phase transformations”. Schryvers D s.l., page 947 (1999).
Keywords: H1 Book chapter; Electron microscopy for materials research (EMAT)
|
|
|
“Advanced three-dimensional electron microscopy techniques in the quest for better structural and functional materials”. Schryvers D, Cao S, Tirry W, Idrissi H, Van Aert S, Science and technology of advanced materials 14, 014206 (2013). http://doi.org/10.1088/1468-6996/14/1/014206
Abstract: After a short review of electron tomography techniques for materials science, this overview will cover some recent results on different shape memory and nanostructured metallic systems obtained by various three-dimensional (3D) electron imaging techniques. In binary NiTi, the 3D morphology and distribution of Ni4Ti3 precipitates are investigated by using FIB/SEM slice-and-view yielding 3D data stacks. Different quantification techniques will be presented including the principal ellipsoid for a given precipitate, shape classification following a Zingg scheme, particle distribution function, distance transform and water penetration. The latter is a novel approach to quantifying the expected matrix transformation in between the precipitates. The different samples investigated include a single crystal annealed with and without compression yielding layered and autocatalytic precipitation, respectively, and a polycrystal revealing different densities and sizes of the precipitates resulting in a multistage transformation process. Electron tomography was used to understand the interaction between focused ion beam-induced Frank loops and long dislocation structures in nanobeams of Al exhibiting special mechanical behaviour measured by on-chip deposition. Atomic resolution electron tomography is demonstrated on Ag nanoparticles in an Al matrix.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.798
Times cited: 6
DOI: 10.1088/1468-6996/14/1/014206
|
|
|
“Aerosol synthesis of fullerene nanocrystals in controlled flow reactor conditions”. Joutsensaari J, Ahonen PP, Kauppinen EI, Brown DP, Lehtinen KEJ, Jokiniemi JK, Pauwels B, Van Tendeloo G, Journal of nanoparticle research 2, 53 (2000)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.02
Times cited: 5
|
|
|
“Aerosol synthesis of nanostructured, ultrafine fullerene particles”. Joutsensaari J, Ahonen PP, Tapper U, Kauppinen EI, Pauwels B, Amelinckx S, Van Tendeloo G, (1999)
Keywords: P3 Proceeding; Electron microscopy for materials research (EMAT)
|
|
|
“Ag nanoparticles on mixed Al2O3-Ga2O3 supports as catalysts for the N-alkylation of amines with alcohols”. Geukens I, Vermoortele F, Meledina M, Turner S, Van Tendeloo G, De Vos DE, Applied catalysis : A : general 469, 373 (2014). http://doi.org/10.1016/j.apcata.2013.09.044
Abstract: The combination of AgNO3 with NaH results in Ag nanoparticles that can selectively perform alcohol aminations under mild reaction conditions (110 °C). NaH not only serves as a reducing agent for the Ag salt, but also activates the alcohol for dehydrogenation to the corresponding ketone/aldehyde. The stability of the particles can be improved by immobilizing them onto mixed Al2O3Ga2O3 supports; the combination of Ga and Al provides materials with stronger Lewis acidic sites compared to pure alumina or gallium oxide supports. This leads to catalysts with enhanced activities, without the necessity of adding external Lewis acids. Detailed TEM characterization also reveals a close interaction between the Ag NPs and the gallium oxide phase. The obtained catalysts are recyclable and show activity for the alcohol amination using a variety of aliphatic and aromatic amines under mild conditions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.339
Times cited: 24
DOI: 10.1016/j.apcata.2013.09.044
|
|
|
“Air- and water-resistant noble metal coated ferromagnetic cobalt nanorods”. Lentijo-Mozo S, Tan RP, Garcia-Marcelot C, Altantzis T, Fazzini PF, Hungria T, Cormary B, Gallagher JR, Miller JT, Martinez H, Schrittwieser S, Schotter J, Respaud M, Bals S, Van Tendeloo G, Gatel C, Soulantica K, ACS nano 9, 2792 (2015). http://doi.org/10.1021/nn506709k
Abstract: Cobalt nanorods possess ideal magnetic properties for applications requiring magnetically hard nanoparticles. However, their exploitation is undermined by their sensitivity toward oxygen and water, which deteriorates their magnetic properties. The development of a continuous metal shell inert to oxidation could render them stable, opening perspectives not only for already identified applications but also for uses in which contact with air and/or aqueous media is inevitable. However, the direct growth of a conformal noble metal shell on magnetic metals is a challenge. Here, we show that prior treatment of Co nanorods with a tin coordination compound is the crucial step that enables the subsequent growth of a continuous noble metal shell on their surface, rendering them air- and water-resistant, while conserving the monocrystallity, metallicity and the magnetic properties of the Co core. Thus, the as-synthesized coreshell ferromagnetic nanorods combine high magnetization and strong uniaxial magnetic anisotropy, even after exposure to air and water, and hold promise for successful implementation in in vitro biodiagnostics requiring probes of high magnetization and anisotropic shape.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 13.942
Times cited: 25
DOI: 10.1021/nn506709k
|
|
|
“ALN nanoparticles XANES analysis: local atomic and electronic structure”. Soldatov A, Yalovega G, Smolentsev G, Kravtsova A, Lamoen D, Balasubramanian C, Marcelli A, Cinque G, Bellucci S, Nuclear Instruments &, Methods In Physics Research Section A-Accelerators Spectrometers Detectors And Associated Equipment 575, 85 (2007). http://doi.org/10.1016/j.nima.2007.01.031
Keywords: A1 Journal article; Electron Microscopy for Materials Science (EMAT);
Impact Factor: 1.362
Times cited: 3
DOI: 10.1016/j.nima.2007.01.031
|
|
|
“An alternative approach to determine attainable resolution directly from HREM images”. Wang A, Turner S, Van Aert S, van Dyck D, Ultramicroscopy 133, 50 (2013). http://doi.org/10.1016/j.ultramic.2013.05.008
Abstract: The concept of resolution in high-resolution electron microscopy (HREM) is the power to resolve neighboring atoms. Since the resolution is related to the width of the point spread function of the microscope, it could in principle be determined from the image of a point object. However, in electron microscopy there are no ideal point objects. The smallest object is an individual atom. If the width of an atom is much smaller than the resolution of the microscope, this atom can still be considered as a point object. As the resolution of the microscope enters the sub-Å regime, information about the microscope is strongly entangled with the information about the atoms in HREM images. Therefore, we need to find an alternative method to determine the resolution in an object-independent way. In this work we propose to use the image wave of a crystalline object in zone axis orientation. Under this condition, the atoms of a column act as small lenses so that the electron beam channels through the atom column periodically. Because of this focusing, the image wave of the column can be much more peaked than the constituting atoms and can thus be a much more sensitive probe to measure the resolution. Our approach is to use the peakiness of the image wave of the atom column to determine the resolution. We will show that the resolution can be directly linked to the total curvature of the atom column wave. Moreover, we can then directly obtain the resolution of the microscope given that the contribution from the object is known, which is related to the bounding energy of the atom. The method is applied on an experimental CaTiO3 image wave.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 2.843
DOI: 10.1016/j.ultramic.2013.05.008
|
|
|
“Aluminum incorporation into MCM-48 toward the creation of Brønsted acidity”. Collart O, Cool P, van der Voort P, Meynen V, Vansant EF, Houthoofd KJ, Grobet PJ, Lebedev OI, Van Tendeloo G, The journal of physical chemistry : B : condensed matter, materials, surfaces, interfaces and biophysical 108, 13905 (2004). http://doi.org/10.1021/jp049837x
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 3.177
Times cited: 13
DOI: 10.1021/jp049837x
|
|
|
“An accurate parameterization for scattering factors, electron densities and electrostatic potentials for neutral atoms that obey all physical constraints”. Lobato Hoyos IP, van Dyck D, Acta crystallographica: section A: foundations of crystallography 70, 636 (2014). http://doi.org/10.1107/S205327331401643X
Abstract: An efficient procedure and computer program are outlined for fitting numerical X-ray and electron scattering factors with the correct inclusion of all physical constraints. The numerical electron scattering factors have been parameterized using five analytic non-relativistic hydrogen electron scattering factors as basis functions for 103 neutral atoms of the periodic table. The inclusion of the correct physical constraints in the electron scattering factor and its derived quantities allows the use of the new parameterization in different fields. In terms of quality of the fit, the proposed parameterization of the electron scattering factor is one order of magnitude better than the previous analytic fittings.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 5.725
Times cited: 19
DOI: 10.1107/S205327331401643X
|
|
|
“An oxysulfate Fe2O(SO4)2 electrode for sustainable Li-based batteries”. Sun M, Rousse G, Abakumov AM, Van Tendeloo G, Sougrati M-T, Courty M, Doublet M-L, Tarascon J-M, Journal of the American Chemical Society 136, 12658 (2014). http://doi.org/10.1021/ja505268y
Abstract: High-performing Fe-based electrodes for Li-based batteries are eagerly pursued because of the abundance and environmental benignity of iron, with especially great interest in polyanionic compounds because of their flexibility in tuning the Fe3+/Fe2+ redox potential. We report herein the synthesis and structure of a new Fe-based oxysulfate phase, Fe2O(SO4)(2), made at low temperature from abundant elements, which electrochemically reacts with nearly 1.6 Li atoms at an average voltage of 3.0 V versus Li+/Li, leading to a sustained reversible capacity of similar to 125 mAh/g. The Li insertiondeinsertion process, the first ever reported in any oxysulfate, entails complex phase transformations associated with the position of iron within the FeO6 octahedra. This finding opens a new path worth exploring in the quest for new positive electrode materials.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 13.858
Times cited: 11
DOI: 10.1021/ja505268y
|
|
|
“Analytical TEM investigations on concentration gradients surrounding Ni4Ti3 precipitates in Ni-Ti shape memory material”. Yang Z, Tirry W, Schryvers D, Scripta materialia 52, 1129 (2005). http://doi.org/10.1016/j.scriptamat.2005.02.013
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.747
Times cited: 49
DOI: 10.1016/j.scriptamat.2005.02.013
|
|
|
“Analytical TEM study of CVD diamond growth on TiO2 sol-gel layers”. Lu Y-G, Verbeeck J, Turner S, Hardy A, Janssens SD, De Dobbelaere C, Wagner P, Van Bael MK, Van Tendeloo G, Diamond and related materials 23, 93 (2012). http://doi.org/10.1016/j.diamond.2012.01.022
Abstract: The early growth stages of chemical vapor deposition (CVD) diamond on a solgel TiO2 film with buried ultra dispersed diamond seeds (UDD) have been studied. In order to investigate the diamond growth mechanism and understand the role of the TiO2 layer in the growth process, high resolution transmission electron microscopy (HRTEM), energy-filtered TEM and electron energy loss spectroscopy (EELS) techniques were applied to cross sectional diamond film samples. We find evidence for the formation of TiC crystallites inside the TiO2 layer at different diamond growth stages. However, there is no evidence that diamond nucleation starts from these crystallites. Carbon diffusion into the TiO2 layer and the chemical bonding state of carbon (sp2/sp3) were both extensively investigated. We provide evidence that carbon diffuses through the TiO2 layer and that the diamond seeds partially convert to amorphous carbon during growth. This carbon diffusion and diamond to amorphous carbon conversion make the seed areas below the TiO2 layer grow and bend the TiO2 layer upwards to form the nucleation center of the diamond film. In some of the protuberances a core of diamond seed remains, covered by amorphous carbon. It is however unlikely that the remaining seeds are still active during the growth process.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.561
Times cited: 16
DOI: 10.1016/j.diamond.2012.01.022
|
|
|
“Andreev-type states induced by quantum confinement”. Shanenko AA, Croitoru MD, Mints RG, Peeters FM, Journal of Surface Investigation. X-ray, Synchrotron and Neutron Techniques 2, 611 (2008). http://doi.org/10.1134/S1027451008040216
Abstract: The properties of a clean superconductor with nanoscale dimensions are governed by quantum confinement of the electrons. This results in a spatially inhomogeneous superconducting condensate and in the formation of new Andreev-type quasiparticle states. These states are mainly located beyond regions where the superconducting condensate is enhanced. A numerical self-consistent solution of the Bogoliubov-de Gennes equations for a cylindrical metallic nanowire shows that these new Andreev-type states decrease the ratio of the energy gap to the critical temperature.
Keywords: A1 Journal article; Condensed Matter Theory (CMT); Electron microscopy for materials research (EMAT)
Times cited: 1
DOI: 10.1134/S1027451008040216
|
|
|
“Anion ordering and defect structure in Ruddlesden-Popper strontium niobium oxynitrides”. Tobías G, Beltrán-Porter D, Lebedev OI, Van Tendeloo G, Rodríguez-Carvajal J, Fuertes A, Inorganic chemistry 43, 8010 (2004). http://doi.org/10.1021/ic049236k
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 31
DOI: 10.1021/ic049236k
|
|
|
“Anion ordering in fluorinated La2CuO4”. Abakumov AM, Hadermann J, Van Tendeloo G, Shpanchenko RV, Oleinikov PN, Antipov EV, Journal of solid state chemistry 142, 311 (1999). http://doi.org/10.1006/jssc.1998.8064
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 20
DOI: 10.1006/jssc.1998.8064
|
|
|
“Anion ordering in fluorinated La2CuO4”. Hadermann J, Abakumov AM, Van Tendeloo G, Shpanchenko RV, Oleinikov PN, Antipov EV s.l., page 133 (1999).
Keywords: H1 Book chapter; Electron microscopy for materials research (EMAT)
|
|
|
“Anion rearrangements in fluorinated Nd2CuO3.5”. Corbel G, Attfield JP, Hadermann J, Abakumov AM, Alekseeva AM, Rozova MG, Antipov EV, Chemistry of materials 15, 189 (2003). http://doi.org/10.1021/cm021102m
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 9
DOI: 10.1021/cm021102m
|
|
|
“Anisotropic cation exchange in PbSe/CdSe core/shell nanocrystals of different geometry”. Casavola M, van Huis MA, Bals S, Lambert K, Hens Z, Vanmaekelbergh D, Chemistry of materials 24, 294 (2012). http://doi.org/10.1021/cm202796s
Abstract: We present a study of Cd2+-for-Pb2+ exchange in PbSe nanocrystals (NCs) with cube, star, and rod shapes. Prolonged temperature-activated cation exchange results in PbSe/CdSe heterostructured nanocrystals (HNCs) that preserve their specific overall shape, whereas the PbSe core is strongly faceted with dominance of {111} facets. Hence, cation exchange proceeds while the Se anion lattice is preserved, and well-defined {111}/{111} PbSe/CdSe interfaces develop. Interestingly, by quenching the reaction at different stages of the cation exchange new structures have been isolated, such as coreshell nanorods, CdSe rods that contain one or two separated PbSe dots and fully zinc blende CdSe nanorods. The crystallographically anisotropic cation exchange has been characterized by a combined HRTEM/HAADF-STEM study of heterointerface evolution over reaction time and temperature. Strikingly, Pb and Cd are only intermixed at the PbSe/CdSe interface. We propose a plausible model for the cation exchange based on a layer-by-layer replacement of Pb2+ by Cd2+ enabled by a vacancy-assisted cation migration mechanism.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 136
DOI: 10.1021/cm202796s
|
|