“Nitrogen and luminescent nitrogen-vacancy defects in detonation nanodiamond”. Vlasov II, Shenderova O, Turner S, Lebedev OI, Basov AA, Sildos I, Rähn M, Shiryaev AA, Van Tendeloo G, Small 6, 687 (2010). http://doi.org/10.1002/smll.200901587
Abstract: An efficient method to investigate the microstructure and spatial distribution of nitrogen and nitrogen-vacancy (N-V) defects in detonation nanodiamond (DND) with primary particle sizes ranging from approximately 3 to 50 nm is presented. Detailed analysis reveals atomic nitrogen concentrations as high as 3 at% in 50% of diamond primary particles with sizes smaller than 6 nm. A non-uniform distribution of nitrogen within larger primary DND particles is also presented, indicating a preference for location within the defective central part or at twin boundaries. A photoluminescence (PL) spectrum with well-pronounced zero-phonon lines related to the N-V centers is demonstrated for the first time for electron-irradiated and annealed DND particles at continuous laser excitation. Combined Raman and PL analysis of DND crystallites dispersed on a Si substrate leads to the conclusion that the observed N-V luminescence originates from primary particles with sizes exceeding 30 nm. These findings demonstrate that by manipulation of the size/nitrogen content in DND there are prospects for mass production of nanodiamond photoemitters based on bright and stable luminescence from nitrogen-related defects.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 8.643
Times cited: 84
DOI: 10.1002/smll.200901587
|
|
|
“Surface-Facet-Dependent Phonon Deformation Potential in Individual Strained Topological Insulator Bi2Se3 Nanoribbons”. Yan Y, Zhou X, Jin H, Li C-Z, Ke X, Van Tendeloo G, Liu K, Yu D, Dressel M, Liao Z-M, ACS nano 9, 10244 (2015). http://doi.org/10.1021/acsnano.5b04057
Abstract: Strain is an important method to tune the properties of topological insulators. For example, compressive strain can induce superconductivity in Bi2Se3 bulk material. Topological insulator nanostructures are the superior candidates to utilize the unique surface states due to the large surface to volume ratio. Therefore, it is highly desirable to monitor the local strain effects in individual topological insulator nanostructures. Here, we report the systematical micro-Raman spectra of single strained Bi2Se3 nanoribbons with different thicknesses and different surface facets, where four optical modes are resolved in both Stokes and anti-Stokes Raman spectral lines. A striking anisotropy of the strain dependence is observed in the phonon frequency of strained Bi2Se3 nanoribbons grown along the ⟨112̅0⟩ direction. The frequencies of the in-plane Eg2 and out-of-plane A1g1 modes exhibit a nearly linear blue-shift against bending strain when the nanoribbon is bent along the ⟨112̅0⟩ direction with the curved {0001} surface. In this case, the phonon deformation potential of the Eg2 phonon for 100 nm-thick Bi2Se3 nanoribbon is up to 0.94 cm–1/%, which is twice of that in Bi2Se3 bulk material (0.52 cm–1/%). Our results may be valuable for the strain modulation of individual topological insulator nanostructures.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 13.942
Times cited: 14
DOI: 10.1021/acsnano.5b04057
|
|
|
“Nitrogen control in nanodiamond produced by detonation shock-wave-assisted synthesis”. Shenderova OA, Vlasov II, Turner S, Van Tendeloo G, Orlinskii SB, Shiryaev AA, Khomich AA, Sulyanov SN, Jelezko F, Wrachtrup J, The journal of physical chemistry: C : nanomaterials and interfaces 115, 14014 (2011). http://doi.org/10.1021/jp202057q
Abstract: Development of efficient production methods of nanodiamond (ND) particles containing substitutional nitrogen and nitrogen-vacancy (NV) complexes remains an important goal in the nanodiamond community. ND synthesized from explosives is generally not among the preferred candidates for imaging applications owing to lack of optically active particles containing NV centers. In this paper, we have systematically studied representative classes of NDs produced by detonation shock wave conversion of different carbon precursor materials, namely, graphite and a graphite/hexogen mixture into ND, as well as ND produced from different combinations of explosives using different cooling methods (wet or dry cooling). We demonstrate that (i) the N content in nanodiamond particles can be controlled through a correct selection of the carbon precursor material (addition of graphite, explosives composition); (ii) particles larger than approximately 20 nm may contain in situ produced optically active NV centers, and (iii) in ND produced from explosives, NV centers are detected only in ND produced by wet synthesis. ND synthesized from a mixture of graphite/explosive contains the largest amount of NV centers formed during synthesis and thus deserves special attention.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.536
Times cited: 54
DOI: 10.1021/jp202057q
|
|
|
“Non-ionic surfactant (C13EOm, m=6, 12 and 18) for large pore mesoporous molecular sieves preparation”. Blin JL, Becue A, Pauwels B, Van Tendeloo G, Su BL, Microporous and mesoporous materials 44/45, 41 (2001). http://doi.org/10.1016/S1387-1811(01)00167-6
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.615
Times cited: 27
DOI: 10.1016/S1387-1811(01)00167-6
|
|
|
“Nonlinear optical properties of Ag nanoclusters and nanoparticles dispersed in a glass host”. Mai HH, Kaydashev VE, Tikhomirov VK, Janssens E, Shestakov MV, Meledina M, Turner S, Van Tendeloo G, Moshchalkov VV, Lievens P, The journal of physical chemistry: C : nanomaterials and interfaces 118, 15995 (2014). http://doi.org/10.1021/jp502294u
Abstract: The nonlinear absorption of Ag atomic clusters and nanoparticles dispersed in a transparent oxyfluoride glass host has been studied. The as-prepared glass, containing 0.15 atom % Ag, shows an absorption band in the UV/violet attributed to the presence of amorphous Ag atomic nanoclusters with an average size of 1.2 nm. Upon heat treatment the Ag nanoclusters coalesce into larger nanoparticles that show a surface plasmon absorption band in the visible. Open aperture z-scan experiments using 480 nm nanosecond laser pulses demonstrated nonsaturated and saturated nonlinear absorption with large nonlinear absorption indices for the Ag nanoclusters and nanoparticles, respectively. These properties are promising, e.g., for applications in optical limiting and objects contrast enhancement.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.536
Times cited: 43
DOI: 10.1021/jp502294u
|
|
|
“Nonvolatile resistive switching in Pt/LaAlO3/SrTiO3 heterostructures”. Wu S, Luo X, Turner S, Peng H, Lin W, Ding J, David A, Wang B, Van Tendeloo G, Wang J, Wu T;, Physical review X 3, 041027 (2013). http://doi.org/10.1103/PhysRevX.3.041027
Abstract: Resistive switching heterojunctions, which are promising for nonvolatile memory applications, usually share a capacitorlike metal-oxide-metal configuration. Here, we report on the nonvolatile resistive switching in Pt/LaAlO3/SrTiO3 heterostructures, where the conducting layer near the LaAlO3/SrTiO3 interface serves as the unconventional bottom electrode although both oxides are band insulators. Interestingly, the switching between low-resistance and high-resistance states is accompanied by reversible transitions between tunneling and Ohmic characteristics in the current transport perpendicular to the planes of the heterojunctions. We propose that the observed resistive switching is likely caused by the electric-field-induced drift of charged oxygen vacancies across the LaAlO3/SrTiO3 interface and the creation of defect-induced gap states within the ultrathin LaAlO3 layer. These metal-oxide-oxide heterojunctions with atomically smooth interfaces and defect-controlled transport provide a platform for the development of nonvolatile oxide nanoelectronics that integrate logic and memory devices.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 12.789
Times cited: 77
DOI: 10.1103/PhysRevX.3.041027
|
|
|
“Novel complex stacking of fully-ordered transition metal layers in Li4FeSbO6 materials”. McCalla E, Abakumov A, Rousse G, Reynaud M, Sougrati MT, Budic B, Mahmoud A, Dominko R, Van Tendeloo G, Hermann RP, Tarascon JM;, Chemistry of materials 27, 1699 (2015). http://doi.org/10.1021/cm504500a
Abstract: As part of a broad project to explore Li4MM'O-6 materials (with M and M' being selected from a wide variety of metals) as positive electrode materials for Li-ion batteries, the structures of Li4FeSbO6 materials with both stoichiometric and slightly deficient lithium contents are studied here. For lithium content varying from 3.8 to 4.0, the color changes from yellow to black and extra superstructure peaks are seen in the XRD patterns. These extra peaks appear as satellites around the four superstructure peaks affected by the stacking of the transition metal atoms. Refinements of both XRD and neutron scattering patterns show a nearly perfect ordering of Li, Fe, and Sb in the transition metal layers of all samples, although these refinements must take the stacking faults into account in order to extract information about the structure of the TM layers. The structure of the most lithium rich sample, where the satellite superstructure peaks are seen, was determined with the help of HRTEM, XRD, and neutron scattering. The satellites arise due to a new stacking sequence where not all transition metal layers are identical but instead two slightly different compositions stack in an AABB sequence giving a unit cell that is four times larger than normal for such monoclinic layered materials. The more lithium deficient samples are found to contain metal site vacancies based on elemental analysis and Mossbauer spectroscopy results. The significant changes in physical properties are attributed to the presence of these vacancies. This study illustrates the great importance of carefully determining the final compositions in these materials, as very small differences in compositions may have large impacts on structures and properties.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 22
DOI: 10.1021/cm504500a
|
|
|
“Novel coreshell magnetic nanoparticles for Taxol encapsulation in biodegradable and biocompatible block copolymers : preparation, characterization and release properties”. Filippousi M, Papadimitriou SA, Bikiaris DN, Pavlidou E, Angelakeris M, Zamboulis D, Tian H, Van Tendeloo G, International journal of pharmaceutics 448, 221 (2013). http://doi.org/10.1016/j.ijpharm.2013.03.025
Abstract: Theranostic polymeric nanocarriers loaded with anticancer drug Taxol and superparamagnetic iron oxide nanocrystals have been developed for possible magnetic resonance imaging (MRI) use and cancer therapy. Multifunctional nanocarriers with a coreshell structure have been prepared by coating superparamagnetic Fe3O4 nanoparticles with block copolymer of poly(ethylene glycol)-b-poly(propylene succinate) with variable molecular weights of the hydrophobic block poly(prolylene succinate). The multifunctional polymer nano-vehicles were prepared using a nanoprecipitation method. Scanning transmission electron microscopy revealed the encapsulation of magnetic nanoparticles inside the polymeric matrix. Energy dispersive X-ray spectroscopy and electron energy loss spectroscopy mapping allowed us to determine the presence of the different material ingredients in a quantitative way. The diameter of the nanoparticles is below 250 nm yielding satisfactory encapsulation efficiency. The nanoparticles exhibit a biphasic drug release pattern in vitro over 15 days depending on the molecular weight of the hydrophobic part of the polymer matrix. These new systems where anti-cancer therapeutics like Taxol and iron oxide nanoparticles (IOs) are co-encapsulated into new facile polymeric nanoparticles, could be addressed as potential multifunctional vehicles for simultaneous drug delivery and targeting imaging as well as real time monitoring of therapeutic effects.
Keywords: A1 Journal article; Pharmacology. Therapy; Electron microscopy for materials research (EMAT)
Impact Factor: 3.649
Times cited: 29
DOI: 10.1016/j.ijpharm.2013.03.025
|
|
|
“Novel hybrid materials for gas sensing applications made of metal-decorated MWCNTs dispersed on nano-particle metal oxides”. Ionescu R, Espinosa EH, Leghrib R, Felten A, Pireaux J-J, Erni R, Van Tendeloo G, Bittencourt C, Canellas N, Llobet E, Sensors and actuators : B : chemical 131, 174 (2008). http://doi.org/10.1016/j.snb.2007.11.001
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.401
Times cited: 47
DOI: 10.1016/j.snb.2007.11.001
|
|
|
“Novel poly(butylene succinate) nanocomposites containing strontium hydroxyapatite nanorods with enhanced osteoconductivity for tissue engineering applications”. Nerantzaki M, Filippousi M, Van Tendeloo G, Terzopoulou Z, Bikiaris D, Goudouri OM, Detsch R, Grueenewald A, Boccaccini AR, Express polymer letters 9, 773 (2015). http://doi.org/10.3144/expresspolymlett.2015.73
Abstract: Three series of poly(butylene succinate) (PBSu) nanocomposites containing 0.5, 1 and 2.5 wt% strontium hydroxyapatite [Sr-5(PO4)(3)OH] nanorods (SrHAp nrds) were prepared by in situ polymerisation. The structural effects of Sr-5(PO4)(3)OH nanorods, for the different concentrations, inside the polymeric matrix (PBSu), were studied through high angle annular dark field scanning transmission electron microscopy (HAADF-STEM). HAADF-STEM measurements revealed that the SrHAp nanorods at low concentrations are dispersed inside the polymeric PBSu matrix while in 1 wt% some aggregates are formed. These aggregations affect the mechanical properties giving an enhancement for the concentration of 0.5 wt% SrHAp nrds in tensile strength, while a reduction is recorded for higher loadings of the nanofiller. Studies on enzymatic hydrolysis revealed that all nanocomposites present higher hydrolysis rates than neat PBSu, indicating that nanorods accelerate the hydrolysis degradation process. In vitro bioactivity tests prove that SrHAp nrds promote the formation of hydroxyapatite on the PBSu surface. All nanocomposites were tested also in relevant cell culture using osteoblast-like cells (MG-63) to demonstrate their biocompatibility showing SrHAp nanorods support cell attachment.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.983
Times cited: 21
DOI: 10.3144/expresspolymlett.2015.73
|
|
|
“Nucleation of metal clusters on plasma treated multi wall carbon nanotubes”. Felten A, Bittencourt C, Colomer J-F, Van Tendeloo G, Pireaux J-J, Carbon 45, 110 (2007). http://doi.org/10.1016/j.carbon.2006.07.023
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.337
Times cited: 40
DOI: 10.1016/j.carbon.2006.07.023
|
|
|
“The “oblique&rdquo, zone imaging of the superlattice in complex crystal structure”. Milat O, Krekels T, Van Tendeloo G, Amelinckx S, Icem 13, 859 (1994)
Keywords: A3 Journal article; Electron microscopy for materials research (EMAT)
|
|
|
“Observation of Co/CoO nanoparticles below the critical size for exchange bias”. Dobrynin AN, Temst K, Lievens P, Margueritat J, Gonzalo J, Afonso CN, Piscopiello E, Van Tendeloo G, Journal of applied physics 101, 113913 (2007). http://doi.org/10.1063/1.2736303
Abstract: We compare the magnetic properties of pure and oxidized Co nanoparticles embedded in an amorphous Al2O3 matrix. Nanoparticles with diameters of 2 or 3 nm were prepared by alternate pulsed laser deposition in high vacuum conditions, and some of them were exposed to O-2 after production and before being embedded. The nanoparticles are organized in layers, the effective edge-to-edge in-depth separation being 5 or 10 nm. The lower saturation magnetizations per Co atom for the samples containing oxidized nanoparticles provide evidence for the formation of antiferromagnetic CoO shells in the nanoparticles. None of the samples with Co/CoO nanoparticles show exchange bias, while vertical hysteresis loop shifts and enhanced coercivities (as compared to samples with pure Co nanoparticles) are observed. This constitutes evidence for the nanoparticles size being in all cases smaller than the critical size for exchange bias. The difference in coercivity versus temperature dependences for the samples with pure and oxidized Co nanoparticles shows that the exchange anisotropy in Co/CoO nanoparticles appears at temperatures lower than 50 K. (c) 2007 American Institute of Physics.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.068
Times cited: 27
DOI: 10.1063/1.2736303
|
|
|
“Observation of nanostripes and -clusters in (Nd, EuGd)Ba2Cu3Ox superconductors”. Koblischka MR, Winter M, Das P, Koblischka-Veneva A, Muralidhar M, Wolf T, Babu NH, Turner S, Van Tendeloo G, Hartmann U, Physica: C : superconductivity 469, 168 (2009). http://doi.org/10.1016/j.physc.2009.01.007
Abstract: Nanostripes are observed in melt-textured and single-crystalline samples of the ternary light rare earth (LRE)-compound (Nd0.33Eu0.33Gd0.33)Ba2Cu3Ox (NEG) by means of atomic force microscopy, scanning tunnelling microscopy at ambient conditions, combined with transmission electron microscopy and electron backscatter diffraction. This enables the observation of several important features: The nanostripes are formed by chains of nanoclusters, representing the LRE/Ba substitution. The dimensions of the nanostripes are similar for both types of NEG samples. The periodicity of the nanostripes is found to range between 40 and 60 nm; the shape of the nanoclusters is elliptic with a major axis length between 300 and 500 nm and a minor axis length of about 30150 nm. The stripes are filling effectively the space in between the twin boundaries. Concerning the flux pinning, the nanoclusters are the important pinning sites, not the nanostripes themselves.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.404
Times cited: 6
DOI: 10.1016/j.physc.2009.01.007
|
|
|
“Observation of superconductivity (Tc = 50K) in a new tetragonal alkaline-earth cuprate Sr0.8Ba1.2CuO3+\delta synthesised at ambient pressure”. Hodges JP, Slater PR, Edwards PP, Greaves C, Slaski M, Van Tendeloo G, Amelinckx S, Physica: C : superconductivity 260, 249 (1996). http://doi.org/10.1016/0921-4534(96)00118-9
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.942
Times cited: 7
DOI: 10.1016/0921-4534(96)00118-9
|
|
|
“Observations of intermetallic compound formation of hot dip aluminized steel”. Kee-Hyun K, van Daele B, Van Tendeloo G, Jong-Kyu Y, Aluminium alloys: part 1-2 519-521, 1871 (2006)
Abstract: A hot dip aluminizing process to simulate the continuous galvanizing line (CGL) was carried out in three successive steps by a hot dip simulator: the pre-treatment for removing scales on the 200 x 250 mm(2) and 1mm in thickness cold rolled steel sheet, the dipping in 660 degrees C Al-Si melt for 3s and the cooling. In a pre-treatment, the steel specimen was partly coated by Au to confirm the mechanism of intermetallic compound (IMC) formation. Scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDX), and transmission electron microscopy (TEM) analyses were followed to observe the cross-section and the distribution of the elements. The specimen was analyzed in the boundary of the dipped-undipped part to see the formation mechanism of the aluminized steel. An intermetallic compound (IMC) is rapidly developed and grown in the steel-liquid interface. It has been usually reported that the IMC was formed by the dissolution of iron in the steel substrate toward the melt and the diffusion of aluminum in an opposite direction. The specimen is covered with aluminum-10 wt.% silicon, forms the IMC in the part that was not Au coated. However, IMC is not formed in the Au-coated part. The interface of the dipped-undipped is also analyzed by EDX. At the interface of the steel-IMC, it is clearly shown that the IMC is only formed in the dipped part and exists in the steel substrate as well, and contributes by iron, aluminum and silicon. The result clearly shows that only aluminum diffuses into the steel substrate without the dissolution of iron and forms the IMC between the steel substrate and the melt. Au coating and the short dipping time prevent the iron from dissolving into the aluminum melt. By TEM combined with focused ion beam (FIB) sample preparation, the IMC is confirmed as Fe2SiAl8, a hexagonal structure with space group P6(3)/mmc.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
|
|
|
“Off-stoichiometry effects on the crystalline and defect structure of hexagonal manganite REMnO3 films (RE = Y, Er, Dy)”. Gélard J, Jehanathan N, Roussel H, Gariglio S, Lebedev OI, Van Tendeloo G, Dubourdieu C, Chemistry of materials 23, 1232 (2011). http://doi.org/10.1021/cm1029358
Abstract: The crystalline and defect structure of epitaxial hexagonal RExMnyO3 (RE = Er, Dy) films with varying cationic composition was investigated by X-ray diffraction and transmission electron microscopy. The films are composed of a strained layer at the interface with the substrate and of a relaxed layer on top of it. The critical thickness is of 10 to 25 nm. For Mn-rich films (or RE deficient), an off-stoichiometric composition maintaining the hexagonal LuMnO3-type structure is stabilized over a large range of the RE/Mn ratio (0.72−1.00), with no Mn-rich secondary phases observed. A linear dependence of the out-of-plane lattice parameter with RE/Mn is observed in this range. Out-of-phase boundary (OPB) extended defects are observed in all films and exhibit a local change in stoichiometry. Such a large solubility limit in the RE deficient region points toward the formation of vacancies on the RE site (RExMnO3−δ, with 0.72 ≤ x < 1), a phenomenon that is encountered in perovskite manganites such as LaxMnO3−δ (x < 1) and that may strongly impact the physical properties of hexagonal manganites.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 17
DOI: 10.1021/cm1029358
|
|
|
“On the asymmetric next-nearest-neighbor ising model of oxygen ordering in YBa2Cu3Oz”. de Fontaine D, Asta M, Ceder G, McCormack R, Van Tendeloo G, Europhysics letters 19, 229 (1992). http://doi.org/10.1209/0295-5075/19/3/013
Abstract: Basic results concerning oxygen ordering in the superconducting compound YBa2Cu3Oz are briefly summarized. It is shown that, at equilibrium, only infinite-chain structures can be stabilized and those models based on hypothetical (and actually nonphysical) screened Coulomb interactions cannot produce stable ground states. It is suggested that diffraction data (neutrons, X-rays, electrons) from oxygen-lean samples are indicative of metastable displacive transformations, and are not directly related to oxygen ordering.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.095
Times cited: 33
DOI: 10.1209/0295-5075/19/3/013
|
|
|
“On the interpretation of HREM images of partially ordered alloys”. De Meulenaere P, Van Tendeloo G, van Landuyt J, van Dyck D, Ultramicroscopy 60, 265 (1995). http://doi.org/10.1016/0304-3991(95)00065-9
Abstract: The ordering for 11/20 alloys has been studied by high-resolution electron microscopy (HREM). The distribution of the intensity maxima in the HREM image have been statistically examined, which provides a profound basis for the image interpretation. Processing of the HREM images allows ''dark-field'' images to be obtained, exhibiting a two-dimensional distribution of those columns which contain the most information in order to interpret the short-range order correlations. Pair correlations and higher cluster correlations between projected columns can be visualised, providing unique information about the ordering as retrieved from an experimental result without any other assumption. The method has been applied to Au4Cr and to Au4Mn to interpret the quenched short-range order state and the transition to long-range order.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 2.436
Times cited: 20
DOI: 10.1016/0304-3991(95)00065-9
|
|
|
“On the relationship between morphology, composition and structure of Al-Cu-Fe crystals and quasicrystals”. Balzuweit K, Meekes H, Van Tendeloo G, de Boer JL, Philosophical magazine: B: physics of condensed matter: electronic, optical and magnetic properties 67, 513 (1993). http://doi.org/10.1080/13642819308207689
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 10
DOI: 10.1080/13642819308207689
|
|
|
Kirschhock CEA, Liang D, Aerts A, Aerts CA, Kremer SPB, Jacobs PA, Van Tendeloo G, Martens JA (2004) On the TEM and AFM evidence of zeosil nanoslabs present during the synthesis of silicalite-1 : reply. Weinheim, 4562–4564
Keywords: L1 Letter to the editor; Electron microscopy for materials research (EMAT)
Impact Factor: 11.994
DOI: 10.1002/anie.200460541
|
|
|
“One particle@one cell : highly monodispersed PtPd bimetallic nanoparticles for enhanced oxygen reduction reaction”. Ying J, Yang X-Y, Hu Z-Y, Mu S-C, Janiak C, Geng W, Pan M, Ke X, Van Tendeloo G, Su B-L, Nano energy 8, 214 (2014). http://doi.org/10.1016/j.nanoen.2014.06.010
Abstract: Highly monodispersed platinum-based nanoalloys are the best-known catalysts for the oxygen reduction reaction. Although certainly promising, the durability and stability are among the main requirements for commercializing fuel cell electrocatalysts in practical applications. Herein, we synthesize highly stable, durable and catalytic active monodispersed PtPd nano-particles encapsulated in a unique one particle@one cell structure by adjusting the viscosity of solvents using mesocellular foam. PtPd nanoparticles in mesocellular carbon foam exhibit an excellent electrocatalytic activity (over 4 times mass and specific activities than the commercial Pt/C catalyst). Most importantly, this nanocatalyst shows no obvious change of structure and only a 29.5% loss in electrochemically active surface area after 5000 potential sweeps between 0.6 and 1.1 V versus reversible hydrogen electrode cycles. (C) 2014 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.343
Times cited: 40
DOI: 10.1016/j.nanoen.2014.06.010
|
|
|
“One-pot synthesis of catalytically stable and active nanoreactors: encapsulation of size-controlled nanoparticles within a hierarchically macroporous core@ordered mesoporous shell system”. Yang X-Y, Li Y, Van Tendeloo G, Xiao F-S, Su B-L, Advanced materials 21, 1368 (2009). http://doi.org/10.1002/adma.200802914
Abstract: Size-controlled, catalytically active nanoparticles are successfully encapsulated in a one-pot synthesis to form novel hierarchical macroporous core@mesoporous shell structures, where macroporous cores are connected by uniform and ordered mesoporous channels. Most importantly, the encapsulated nanoparticles can be used as nanoreactors, with high activities and excellent long-term recycling stability.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 19.791
Times cited: 61
DOI: 10.1002/adma.200802914
|
|
|
“One-step synthesis of shelled PbS nanoparticles in a layered double hydroxide matrix”. Lukashin AV, Eliseev AA, Zhuravleva NG, Vertegel AA, Tretyakov YD, Lebedev OI, Van Tendeloo G, Mendeleev communications , 174 (2004). http://doi.org/10.1070/MC2004v014n04ABEH001973
Abstract: The one-step preparation of capped PbS nanoparticles in an inorganic matrix via UV-induced decomposition of lead thiosulfate complexes intercalated into a hydrotalcite-type layered double hydroxide is reported.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.741
Times cited: 9
DOI: 10.1070/MC2004v014n04ABEH001973
|
|
|
“Optimisation of superconducting thin films by TEM”. Bals S, Van Tendeloo G, Rijnders G, Blank DHA, Leca V, Salluzzo M, Physica: C : superconductivity 372/376, 711 (2002). http://doi.org/10.1016/S0921-4534(02)00838-9
Abstract: High-resolution electron microscopy is used to study the initial growth of different REBa2CU3O7-5 thin films. In DyBa2CU3O7-5 ultra-thin films, deposited on TiO2 terminated SrTiO3, two different types of interface arrangements occur: bulk-SrO-TiO2-BaO-CuO-BaO-CuO2-Dy-CuO2-BaO-bulk and bulk-SrO-TiO2-BaO-CuO2-Dy-CuO2-BaO-CuO-BaO-bulk. This variable growth sequence is the origin of the presence of antiphase boundaries. In Nd1+xBa2-xCu3O7-5 thin films, antiphase boundaries tend to annihilate by the insertion of extra Nd-layers. This annihilation is correlated with the flat morphology of the film and the absence of growth spirals at the surface of the Nd-rich films. (C) 2002 Elsevier Science B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.404
Times cited: 6
DOI: 10.1016/S0921-4534(02)00838-9
|
|
|
“Optimization of the amount of catalyst and reaction time in single wall nanotube production”. Horvath ZE, Biro LP, Van Tendeloo G, Tondeur C, Bister G, Pierard N, Fonseca A, Nagy JB, Diffusion and defect data : solid state data : part B : solid state phenomena 94, 271 (2003)
Abstract: The influence of the amount of catalyst and the reaction time on the quantity and quality of catalytically grown single wall carbon nanotubes (SWNT) was investigated. The aim was to optimize some of the SWNT growth parameters using TEM and HRTEM. The thickness of catalyst layer influences the synthesis of the nanotube because the gas composition can differ between top and bottom. Microscopic investigation of the grown SWNT samples showed that the thicker the catalyst layer the lower relative nanotube content, so the deeper parts of the catalyst layer are less effective: The optimum time for the reaction was found to be 10 minutes. This may be understood assuming that nanotube growth needs an initial incubation time while the activity of the catalyst decreases steadily until the nariotube growth stops.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
|
|
|
“Optimized fabrication of high-quality La0.67Sr0.33MnO3 thin films considering all essential characteristics”. Boschker H, Huijben M, Vailinois A, Verbeeck J, Van Aert S, Luysberg M, Bals S, Van Tendeloo G, Houwman EP, Koster G, Blank DHA, Rijnders G, Journal of physics: D: applied physics 44, 205001 (2011). http://doi.org/10.1088/0022-3727/44/20/205001
Abstract: In this paper, an overview of the fabrication and properties of high-quality La0.67Sr0.33MnO3 (LSMO) thin films is given. A high-quality LSMO film combines a smooth surface morphology with a large magnetization and a small residual resistivity, while avoiding precipitates and surface segregation. In the literature, typically only a few of these issues are adressed. We therefore present a thorough characterization of our films, which were grown by pulsed laser deposition. The films were characterized with reflection high energy electron diffraction, atomic force microscopy, x-ray diffraction, magnetization and transport measurements, x-ray photoelectron spectroscopy and scanning transmission electron microscopy. The films have a saturation magnetization of 4.0 µB/Mn, a Curie temperature of 350 K and a residual resistivity of 60 µΩ cm. These results indicate that high-quality films, combining both large magnetization and small residual resistivity, were realized. A comparison between different samples presented in the literature shows that focussing on a single property is insufficient for the optimization of the deposition process. For high-quality films, all properties have to be adressed. For LSMO devices, the thin-film quality is crucial for the device performance. Therefore, this research is important for the application of LSMO in devices.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.588
Times cited: 99
DOI: 10.1088/0022-3727/44/20/205001
|
|
|
“Optimizing Er/Yb ratio and content in Er-Yb co-doped glass-ceramics for enhancement of the up- and down-conversion luminescence”. Tikhomirov VK, Rodríguez VD, Méndez-Ramos J, del- Castillo J, Kirilenko D, Van Tendeloo G, Moshchalkov VV, Solar energy materials and solar cells 100, 209 (2012). http://doi.org/10.1016/j.solmat.2012.01.019
Abstract: Er3+Yb3+ co-doped transparent glass-ceramics with varying Er/Yb content and ratio have been prepared. High quantum yields for up- and down-conversion luminescence by energy transfer from Yb3+ to Er3+ and from Er3+ to Yb3+, respectively, have been detected and optimized with respect to the Er/Yb content and ratio, and proposed in particular for up- and down-conversion of solar spectrum for enhancement of the efficiency of solar cells. The rise and decay kinetics for the population of the excited levels of Er3+ and Yb3+ have been studied and fit. Based on these experimental data, the mechanisms for the energy transfers have been suggested with emphasis on the optimized Er/Yb content and ratio for enhancement of the efficiency of the Er3+↔Yb3+ energy transfers.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.784
Times cited: 66
DOI: 10.1016/j.solmat.2012.01.019
|
|
|
“Order and disorder in (Nd,Ce)nO2nSr2GaCu2O5 and YSr2CoCu2O7”. Krekels T, Milat O, Van Tendeloo G, Amelinckx S, Babu TGN, Wright AJ, Greaves C, Journal of solid state chemistry 105, 313 (1993). http://doi.org/10.1006/jssc.1993.1222
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.133
Times cited: 50
DOI: 10.1006/jssc.1993.1222
|
|
|
“Order and twining in Sb2W0.75Mo0.25O6”. Enjalbert R, Galy J, Castro A, Lidin S, Withers R, Van Tendeloo G, Solid state sciences 5, 721 (2003). http://doi.org/10.1016/S1293-2558(03)00093-1
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.811
Times cited: 3
DOI: 10.1016/S1293-2558(03)00093-1
|
|