“Energy Level Alignment and Cation Charge States at the LaFeO3/LaMnO3(001) Heterointerface”. Smolin SY, Choquette AK, Wilks RG, Gauquelin N, Félix R, Gerlach D, Ueda S, Krick AL, Verbeeck J, Bär M, Baxter JB, May SJ, Advanced Materials Interfaces 4, 1700183 (2017). http://doi.org/10.1002/admi.201700183
Abstract: The electronic properties of LaFeO 3 /LaMnO 3 epitaxial heterojunctions are investigated to determine the valence and conduction band offsets and the nominal Mn and Fe valence states at the interface. Studying a systematic series of (LaFeO 3 ) n /(LaMnO 3 ) m bilayers (m ≈ 50) epitaxially grown in the (001) orientation using molecular beam epitaxy, layer-resolved electron energy loss spectroscopy reveals a lack of significant interfacial charge transfer, with a nominal 3+ valence state observed for both Mn and Fe across the interface. Through a combination of variable angle spectroscopic ellipsometry and hard X-ray photoelectron spectroscopy, type I energy level alignments are obtained at the LaFeO 3 /LaMnO 3 interface with positive valence and conduction band offsets of (1.20 ± 0.07) eV and (0.5–0.7 ± 0.3) eV, respectively, with minimal band bending. Variable temperature resistivity measurements reveal that the bilayers remain insulating and that the presence of the heterojunction does not result in a conducting interface.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.279
Times cited: 14
DOI: 10.1002/admi.201700183
|
|
|
“Determining oxygen relaxations at an interface: A comparative study between transmission electron microscopy techniques”. Gauquelin N, van den Bos KHW, Béché, A, Krause FF, Lobato I, Lazar S, Rosenauer A, Van Aert S, Verbeeck J, Ultramicroscopy 181, 178 (2017). http://doi.org/10.1016/j.ultramic.2017.06.002
Abstract: Nowadays, aberration corrected transmission electron microscopy (TEM) is a popular method to characterise nanomaterials at the atomic scale. Here, atomically resolved images of nanomaterials are acquired, where the contrast depends on the illumination, imaging and detector conditions of the microscope. Visualization of light elements is possible when using low angle annular dark field (LAADF) STEM, annular bright field (ABF) STEM, integrated differential phase contrast (iDPC) STEM, negative spherical aberration imaging (NCSI) and imaging STEM (ISTEM). In this work, images of a NdGaO3-La0.67Sr0.33MnO3 (NGO-LSMO) interface are quantitatively evaluated by using statistical parameter estimation theory. For imaging light elements, all techniques are providing reliable results, while the techniques based on interference contrast, NCSI and ISTEM, are less robust in terms of accuracy for extracting heavy column locations. In term of precision, sample drift and scan distortions mainly limits the STEM based techniques as compared to NCSI. Post processing techniques can, however, partially compensate for this. In order to provide an outlook to the future, simulated images of NGO, in which the unavoidable presence of Poisson noise is taken into account, are used to determine the ultimate precision. In this future counting noise limited scenario, NCSI and ISTEM imaging will provide more precise values as compared to the other techniques, which can be related to the mechanisms behind the image recording.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.843
Times cited: 34
DOI: 10.1016/j.ultramic.2017.06.002
|
|
|
“One step toward a new generation of C-MOS compatible oxide p-n junctions: Structure of the LSMO/ZnO interface elucidated by an experimental and theoretical synergic work”. Pullini D, Sgroi M, Mahmoud A, Gauquelin N, Maschio L, Lorenzo-Ferrari AM, Groenen R, Damen C, Rijnders G, van den Bos KHW, Van Aert S, Verbeeck J, ACS applied materials and interfaces 9, 20974 (2017). http://doi.org/10.1021/acsami.7b04089
Abstract: Heterostructures formed by La0.7Sr0.3MnO3/ZnO (LSMO/ZnO) interfaces exhibit extremely interesting electronic properties making them promising candidates for novel oxide p–n junctions, with multifunctional features. In this work, the structure of the interface is studied through a combined experimental/theoretical approach. Heterostructures were grown epitaxially and homogeneously on 4″ silicon wafers, characterized by advanced electron microscopy imaging and spectroscopy and simulated by ab initio density functional theory calculations. The simulation results suggest that the most stable interface configuration is composed of the (001) face of LSMO, with the LaO planes exposed, in contact with the (112̅0) face of ZnO. The ab initio predictions agree well with experimental high-angle annular dark field scanning transmission electron microscopy images and confirm the validity of the suggested structural model. Electron energy loss spectroscopy confirms the atomic sharpness of the interface. From statistical parameter estimation theory, it has been found that the distances between the interfacial planes are displaced from the respective ones of the bulk material. This can be ascribed to the strain induced by the mismatch between the lattices of the two materials employed
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 7.504
Times cited: 4
DOI: 10.1021/acsami.7b04089
|
|
|
“Reclaiming the image of daguerreotypes: Characterization of the corroded surface before and after atmospheric plasma treatment”. Grieten E, Schalm O, Tack P, Bauters S, Storme P, Gauquelin N, Caen J, Patelli A, Vincze L, Schryvers D, Journal of cultural heritage (2017). http://doi.org/10.1016/j.culher.2017.05.008
Abstract: Technological developments such as atmospheric plasma jets for industry can be adapted for the conservation of cultural heritage. This application might offer a potential method for the removal or transformation of the corrosion on historical photographs. We focus on daguerreotypes and present an in-depth study of the induced changes by a multi-analytical approach using optical microscopy, scanning electron microscopy, different types of transmission electron microscopy and X-ray absorption fine structure. The H2-He afterglow removes S from an Ag2S or Cu2S layer which results in a nano-layer of metallic Ag or Cu on top of the deteriorated microstructure. In case the corrosion layer is composed of Cu-Ag-S compounds, our proposed setup can be used to partially remove the corrosion. These alterations of the corrosion results in an improvement in the readability of the photographic image.
Keywords: A1 Journal article; Art; History; Electron microscopy for materials research (EMAT); Antwerp Cultural Heritage Sciences (ARCHES)
Impact Factor: 1.838
Times cited: 9
DOI: 10.1016/j.culher.2017.05.008
|
|
|
“Interplay of strain and indium incorporation in InGaN/GaN dot-in-a-wire nanostructures by scanning transmission electron microscopy”. Woo SY, Gauquelin N, Nguyen HPT, Mi Z, Botton GA, Nanotechnology 26, 344002 (2015). http://doi.org/10.1088/0957-4484/26/34/344002
Abstract: The interplay between strain and composition is at the basis of heterostructure design to engineer new properties. The influence of the strain distribution on the incorporation of indium during the formation of multiple InGaN/GaN quantum dots (QDs) in nanowire (NW) heterostructures has been investigated, using the combined techniques of geometric phase analysis of atomic-resolution images and quantitative elemental mapping from core-loss electron energy-loss spectroscopy within scanning transmission electron microscopy. The variation in In-content between successive QDs within individual NWs shows a dependence on the magnitude of compressive strain along the growth direction within the underlying GaN barrier layer, which affects the incorporation of In-atoms to minimize the local effective strain energy. Observations suggest that the interfacial misfit between InGaN/GaN within the embedded QDs is mitigated by strain partitioning into both materials, and results in normal stresses inflicted by the presence of the surrounding GaN shell. These experimental measurements are linked to the local piezoelectric polarization fields for individual QDs, and are discussed in terms of the photoluminescence from an ensemble of NWs.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.44
Times cited: 19
DOI: 10.1088/0957-4484/26/34/344002
|
|
|
“Epitaxial stress-free growth of high crystallinity ferroelectric PbZr0.52Ti0.48O3 on GaN/AlGaN/Si(111) substrate”. Li L, Liao Z, Gauquelin N, Minh Duc Nguyen, Hueting RJE, Gravesteijn DJ, Lobato I, Houwman EP, Lazar S, Verbeeck J, Koster G, Rijnders G, Advanced Materials Interfaces 5, 1700921 (2018). http://doi.org/10.1002/ADMI.201700921
Abstract: <script type='text/javascript'>document.write(unpmarked('Due to its physical properties gallium-nitride (GaN) is gaining a lot of attention as an emerging semiconductor material in the field of high-power and high-frequency electronics applications. Therefore, the improvement in the performance and/or perhaps even extension in functionality of GaN based devices would be highly desirable. The integration of ferroelectric materials such as lead-zirconate-titanate (PbZrxTi1-xO3) with GaN has a strong potential to offer such an improvement. However, the large lattice mismatch between PZT and GaN makes the epitaxial growth of Pb(Zr1-xTix)O-3 on GaN a formidable challenge. This work discusses a novel strain relaxation mechanism observed when MgO is used as a buffer layer, with thicknesses down to a single unit cell, inducing epitaxial growth of high crystallinity Pb(Zr0.52Ti0.48)O-3 (PZT) thin films. The epitaxial PZT films exhibit good ferroelectric properties, showing great promise for future GaN device applications.'));
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.279
Times cited: 15
DOI: 10.1002/ADMI.201700921
|
|
|
“Spin-orbit semimetal SrIrO3 in the two-dimensional limit”. Groenendijk DJ, Autieri C, Girovsky J, Martinez-Velarte MC, Manca N, Mattoni G, Monteiro AMRVL, Gauquelin N, Verbeeck J, Otte AF, Gabay M, Picozzi S, Caviglia AD, Physical review letters 119, 256403 (2017). http://doi.org/10.1103/PHYSREVLETT.119.256403
Abstract: <script type='text/javascript'>document.write(unpmarked('We investigate the thickness-dependent electronic properties of ultrathin SrIrO3 and discover a transition from a semimetallic to a correlated insulating state below 4 unit cells. Low-temperature magnetoconductance measurements show that spin fluctuations in the semimetallic state are significantly enhanced while approaching the transition point. The electronic properties are further studied by scanning tunneling spectroscopy, showing that 4 unit cell SrIrO(3)d is on the verge of a gap opening. Our density functional theory calculations reproduce the critical thickness of the transition and show that the opening of a gap in ultrathin SrIrO3 requires antiferromagnetic order.'));
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 8.462
Times cited: 79
DOI: 10.1103/PHYSREVLETT.119.256403
|
|
|
“Synthesis of high-oxidation Y-Ba-Cu-O phases in superoxygenated thin films”. Zhang H, Gauquelin N, McMahon C, Hawthorn DG, Botton GA, Wei JYT, Physical review materials 2, 033803 (2018). http://doi.org/10.1103/PHYSREVMATERIALS.2.033803
Abstract: It is known that solid-state reaction in high-pressure oxygen can stabilize high-oxidation phases of Y-Ba-Cu-O superconductors in powder form. We extend this superoxygenation concept of synthesis to thin films which, due to their large surface-to-volume ratio, are more reactive thermodynamically. Epitaxial thin films of YBa2Cu3O7-delta grown by pulsed laser deposition are annealed at up to 700 atm O-2 and 900 degrees C, in conjunction with Cu enrichment by solid-state diffusion. The films show the clear formation of Y2Ba4Cu7O15-delta and Y2Ba4Cu8O16 as well as regions of YBa2Cu5O9-delta and YBa2Cu6O10-delta phases, according to scanning transmission electron microscopy, x-ray diffraction, and x-ray absorption spectroscopy. Similarly annealed YBa2Cu3O7-delta powders show no phase conversion. Our results demonstrate a route of synthesis towards discovering more complex phases of cuprates and other superconducting oxides.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 2
DOI: 10.1103/PHYSREVMATERIALS.2.033803
|
|
|
“Atomic-scale identification of novel planar defect phases in heteroepitaxial YBa2Cu3O7-\delta thin films”. Gauquelin N, Zhang H, Zhu G, Wei JYT, Botton GA, AIP advances 8, 055022 (2018). http://doi.org/10.1063/1.5011761
Abstract: We have discovered two novel types of planar defects that appear in heteroepitaxial YBa2Cu3O7-delta(YBCO123) thin films, grown by pulsed-laser deposition (PLD) either with or without a La2/3Ca1/3MnO3 (LCMO) overlayer, using the combination of highangle annular dark-field scanning transmission electron microscopy (HAADF-STEM) imaging and electron energy loss spectroscopy (EELS) mapping for unambiguous identification. These planar lattice defects are based on the intergrowth of either a BaO plane between two CuO chains or multiple Y-O layers between two CuO2 planes, resulting in non-stoichiometric layer sequences that could directly impact the high-Tc superconductivity. (C) 2018 Author(s).
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 1.568
Times cited: 1
DOI: 10.1063/1.5011761
|
|
|
“Orthorhombic vs. hexagonal epitaxial SrIrO3 thin films : structural stability and related electrical transport properties”. Bhat SG, Gauquelin N, Sebastian NK, Sil A, Béché, A, Verbeeck J, Samal D, Kumar PSA, Europhysics letters 122, 28003 (2018). http://doi.org/10.1209/0295-5075/122/28003
Abstract: Metastable orthorhombic SrIrO3 (SIO) is an arch-type spin-orbit coupled material. We demonstrate here a controlled growth of relatively thick (200 nm) SIO films that transform from bulk “6H-type” structure with monoclinic distortion to an orthorhombic lattice by controlling growth temperature. Extensive studies based on high-resolution X-ray diffraction and transmission electron microscopy infer a two distinct structural phases of SIO. Electrical transport reveals a weak temperature-dependent semi-metallic character for both phases. However, the temperature-dependent Hall-coefficient for the orthorhombic SIO exhibits a prominent sign change, suggesting a multiband character in the vicinity of E-F. Our findings thus unravel the subtle structure-property relation in SIO epitaxial thin films. Copyright (C) EPLA, 2018
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.957
Times cited: 4
DOI: 10.1209/0295-5075/122/28003
|
|
|
“Small-moment paramagnetism and extensive twinning in the topochemically reduced phase Sr2ReLiO5.5”. Hasanli N, Gauquelin N, Verbeeck J, Hadermann J, Hayward MA, Journal of the Chemical Society : Dalton transactions 47, 15783 (2018). http://doi.org/10.1039/C8DT03463J
Abstract: Reaction of the cation-ordered double perovskite Sr2ReLiO6 with dilute hydrogen at 475 degrees C leads to the topochemical deintercalation of oxide ions from the host lattice and the formation of a phase of composition Sr2ReLiO5.5, as confirmed by thermogravimetric and EELS data. A combination of neutron and electron diffraction data reveals the reduction process converts the -Sr2O2-ReLiO4-Sr2O2-ReLiO4- stacking sequence of the parent phase into a -Sr2O2-ReLiO3-Sr2O2-ReLiO4-, partially anion-vacant ordered sequence. Furthermore a combination of electron diffraction and imaging reveals Sr2ReLiO5.5 exhibits extensive twinning – a feature which can be attributed to the large, anisotropic volume expansion of the material on reduction. Magnetisation data reveal a strongly reduced moment of (eff) = 0.505(B) for the d(1) Re6+ centres in the phase, suggesting there remains a large orbital component to the magnetism of the rhenium centres, despite their location in low symmetry coordination environments.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.029
DOI: 10.1039/C8DT03463J
|
|
|
“Enhancement of toughness of Al-to-steel Friction Melt Bonded welds via metallic interlayers”. Jimenez-Mena N, Jacques PJ, Ding L, Gauquelin N, Schryvers D, Idrissi H, Delannay F, Simar A, Materials science and engineering: part A: structural materials: properties, microstructure and processing 740-741, 274 (2019). http://doi.org/10.1016/j.msea.2018.10.101
Abstract: The toughness of Al-to-steel welds decreases with increasing thickness of the intermetallic (IM) layer formed at the interface. Co plating has been added as interlayer in Al-to-steel Friction Melt Bonded (FMB) welds to control the nature and thickness of the IM layer. In comparison to a weld without interlayer, Co plating brings about a reduction of the thickness of the IM layer by 70%. The critical energy release rate of the crack propagating in the weld is used as an indicator of toughness. It is evaluated via an adapted crack propagation test using an energy conservation criterion. For a weld without interlayer, critical energy release rate is found to increase when the thickness of the intermetallic layer decreases. When the intermetallic layer is thick, the crack propagates in a brittle manner through the intermetallic whereas, at low layer thickness, the crack deviates and partially propagates through the Al plate, which causes an increase of toughness. The use of a Co interlayer brings about an increase of toughness by causing full deviation of the crack towards the Al plate.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 4
DOI: 10.1016/j.msea.2018.10.101
|
|
|
“Metal–insulator-transition engineering by modulation tilt-control in perovskite nickelates for room temperature optical switching”. Liao Z, Gauquelin N, Green RJ, Müller-Caspary K, Lobato I, Li L, Van Aert S, Verbeeck J, Huijben M, Grisolia MN, Rouco V, El Hage R, Villegas JE, Mercy A, Bibes M, Ghosez P, Sawatzky GA, Rijnders G, Koster G, America 115, 9515 (2018). http://doi.org/10.1073/pnas.1807457115
Abstract: In transition metal perovskites ABO3 the physical properties are largely driven by the rotations of the BO6 octahedra, which can be tuned in thin films through strain and dimensionality control. However, both approaches have fundamental and practical limitations due to discrete and indirect variations in bond angles, bond lengths and film symmetry by using commercially available substrates. Here, we introduce modulation tilt control as a new approach to tune the ground state of perovskite oxide thin films by acting explicitly on the oxygen octahedra rotation modes, i.e. directly on the bond angles. By intercalating the prototype SmNiO3 target material with a tilt-control layer, we cause the system to change the natural amplitude of a given rotation mode without affecting the interactions. In contrast to strain and dimensionality engineering, our method enables a continuous fine-tuning of the materials properties. This is achieved through two independent adjustable parameters: the nature of the tilt-control material (through its symmetry, elastic constants and oxygen rotation angles) and the relative thicknesses of the target and tilt-control materials. As a result, a magnetic and electronic phase diagram can be obtained, normally only accessible by A-site element substitution, within the single SmNiO3 compound. With this unique approach, we successfully adjusted the metal-insulator transition (MIT) to room temperature to fulfill the desired conditions for optical switching applications.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 9.661
Times cited: 50
DOI: 10.1073/pnas.1807457115
|
|
|
“Nanoscale investigation by TEM and STEM-EELS of the laser induced yellowing”. Godet M, Vergès-Belmin V, Gauquelin N, Saheb M, Monnier J, Leroy E, Bourgon J, Verbeeck J, Andraud C, Micron 115, 25 (2018). http://doi.org/10.1016/j.micron.2018.08.006
Abstract: Nd-YAG QS laser cleaning of soiled stone at 1064 nm can sometimes result in a more yellow appearance compared to other cleaning techniques. Especially in France, this yellowing effect is still considered as a major aesthetic issue by the architects and conservators. One explanation states that the yellowing is linked to the formation of iron-rich nanophase(s) through the laser beam interaction with black crusts that would re-deposit on the cleaned substrate after irradiation. To characterize these nanophases, a model crust containing hematite was elaborated and laser irradiated using a Nd-YAG QS laser. The color of the sample shifted instantaneously from red to a bright yellow and numerous particles were ablated in a visible smoke. Transmission electron microscopy (TEM) was used to examine the morphology and the crystallinity of the neo-formed compounds, both on the surface of the samples and in the ablated materials. In addition, an investigation of the chemical and structural properties of the nanophases was conducted by X-ray dispersive energy (EDX) and electron energy loss (EELS) spectroscopies. It was found that both the surface of the sample and the ablated materials are covered by crystallized nano-spheres and nano-residues, all containing iron and oxygen, sometimes along with calcium and sulfur. In particular an interfacial area containing the four elements was evidenced between some nanostructures and the substrate. Magnetite Fe3O4 was also identified at the nanoscale. This study demonstrates that the laser yellowing of a model crust is linked to the presence of iron-rich nanophases including CaxFeySzOδ nanostructures and magnetite Fe3O4 at the surface after irradiation.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.98
Times cited: 9
DOI: 10.1016/j.micron.2018.08.006
|
|
|
“Electrical Polarization in AlN/GaN Nanodisks Measured by Momentum-Resolved 4D Scanning Transmission Electron Microscopy”. Müller-Caspary K, Grieb T, Müßener J, Gauquelin N, Hille P, Schörmann J, Verbeeck J, Van Aert S, Eickhoff M, Rosenauer A, Physical review letters 122, 106102 (2019). http://doi.org/10.1103/PhysRevLett.122.106102
Abstract: We report the mapping of polarization-induced internal electric fields in AlN/GaN nanowire heterostructures at unit cell resolution as a key for the correlation of optical and structural phenomena in semiconductor optoelectronics. Momentum-resolved aberration-corrected scanning transmission electron microscopy is employed as a new imaging mode that simultaneously provides four-dimensional data in real and reciprocal space. We demonstrate how internal mesoscale and atomic electric fields can be separated in an experiment, which is verified by comprehensive dynamical simulations of multiple electron scattering. A mean difference of 5.3 +- 1.5 MV/cm is found for the polarization-induced electric fields in AlN and GaN, being in accordance with dedicated simulations and photoluminescence measurements in previous publications.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 8.462
Times cited: 26
DOI: 10.1103/PhysRevLett.122.106102
|
|
|
“Controlling the interfacial conductance in LaAlO3/SrTiO3 in 90 degrees off-axis sputter deposition”. Yin C, Krishnan D, Gauquelin N, Verbeeck J, Aarts J, Physical review materials 3, 034002 (2019). http://doi.org/10.1103/PHYSREVMATERIALS.3.034002
Abstract: We report on the fabrication of conducting interfaces between LaAlO3 and SrTiO3 by 90 degrees off-axis sputtering in an Ar atmosphere. At a growth pressure of 0.04 mbar the interface is metallic, with a carrier density of the order of 1 x 10(13) cm(-2) at 3 K. By increasing the growth pressure, we observe an increase of the out-of-plane lattice constants of the LaAlO3 films while the in-plane lattice constants do not change. Also, the low-temperature sheet resistance increases with increasing growth pressure, leading to an insulating interface when the growth pressure reaches 0.10 mbar. We attribute the structural variations to an increase of the La/Al ratio, which also explains the transition from metallic behavior to insulating behavior of the interfaces. Our research shows that the control which is furnished by the Ar pressure makes sputtering as versatile a process as pulsed laser deposition, and emphasizes the key role of the cation stoichiometry of LaAlO3 in the formation of the conducting interface.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.926
Times cited: 4
DOI: 10.1103/PHYSREVMATERIALS.3.034002
|
|
|
“Diluted oxide interfaces with tunable ground states”. Gan Y, Christensen DV, Zhang Y, Zhang H, Krishnan D, Zhong Z, Niu W, Carrad DJ, Norrman K, von Soosten M, Jespersen TS, Shen B, Gauquelin N, Verbeeck J, Sun J, Pryds N, Chen Y, Advanced materials 31, 1805970 (2019). http://doi.org/10.1002/ADMA.201805970
Abstract: The metallic interface between two oxide insulators, such as LaAlO3/SrTiO3 (LAO/STO), provides new opportunities for electronics and spintronics. However, due to the presence of multiple orbital populations, tailoring the interfacial properties such as the ground state and metal-insulator transitions remains challenging. Here, an unforeseen tunability of the phase diagram of LAO/STO is reported by alloying LAO with a ferromagnetic LaMnO3 insulator without forming lattice disorder and at the same time without changing the polarity of the system. By increasing the Mn-doping level, x, of LaAl1-xMnxO3/STO (0 <= x <= 1), the interface undergoes a Lifshitz transition at x = 0.225 across a critical carrier density of n(c) = 2.8 x 10(13) cm(-2), where a peak T-SC approximate to 255 mK of superconducting transition temperature is observed. Moreover, the LaAl1-xMnxO3 turns ferromagnetic at x >= 0.25. Remarkably, at x = 0.3, where the metallic interface is populated by only d(xy) electrons and just before it becomes insulating, a same device with both signatures of superconductivity and clear anomalous Hall effect (7.6 x 10(12) cm(-2) < n(s) <= 1.1 x 10(13) cm(-2)) is achieved reproducibly. This provides a unique and effective way to tailor oxide interfaces for designing on-demand electronic and spintronic devices.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 19.791
Times cited: 31
DOI: 10.1002/ADMA.201805970
|
|
|
“Etching induced formation of interfacial FeMn in IrMn/CoFe bilayers”. O'Donnell D, Hassan S, Du Y, Gauquelin N, Krishnan D, Verbeeck J, Fan R, Steadman P, Bencok P, Dobrynin AN, Journal of physics: D: applied physics 52, 165002 (2019). http://doi.org/10.1088/1361-6463/AB03BD
Abstract: The effect of ion etching on exchange bias in IrMn3/Co70Fe30 bilayers is investigated. In spite of the reduction of saturation magnetization caused by the embedding of Tr from the capping layer into the Co70Fe30 layer during the etching process, the exchange bias in samples with the same thickness of the Co70Fe30 layer is reducing in proportion to the etching power. X-ray magnetic circular dichroism measurements revealed the emergence of an uncompensated Mn magnetization after etching, which is antiferromagnetically coupled to the ferromagnetic layer. This suggests etching induced formation of small interfacial FeMn regions which leads to the decrease of effective exchange coupling between ferromagnetic and antiferromagnetic layers.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.588
DOI: 10.1088/1361-6463/AB03BD
|
|
|
“Evidence for exchange bias coupling at the perovskite/brownmillerite interface in spontaneously stabilized SrCoO3-\delta/SrCoO2.5 bilayers”. Behera BC, Jana S, Bhat SG, Gauquelin N, Tripathy G, Kumar PSA, Samal D, Physical review B 99, 024425 (2019). http://doi.org/10.1103/PHYSREVB.99.024425
Abstract: Interface effect in complex oxide thin-film heterostructures lies at the vanguard of current research to design technologically relevant functionality and explore emergent physical phenomena. While most of the previous works focus on the perovskite/perovskite heterostructures, the study of perovskite/brownmillerite interfaces remains in its infancy. Here, we investigate spontaneously stabilized perovskite-ferromagnet (SrCoO3-delta)/brownmillerite-antiferromagnet (SrCoO2.5) bilayer with T-N > T-C and discover an unconventional interfacial magnetic exchange bias effect. From magnetometry investigations, it is rationalized that the observed effect stems from the interfacial ferromagnet/antiferromagnet coupling. The possibility for coupled ferromagnet/spin-glass interface engendering such effect is ruled out. Strikingly, a finite coercive field persists in the paramagnetic state of SrCoO3-delta,whereas the exchange bias field vanishes at T-C . We conjecture the observed effect to be due to the effective external quenched staggered field provided by the antiferromagnetic layer for the ferromagnetic spins at the interface. Our results not only unveil a paradigm to tailor the interfacial magnetic properties in oxide heterostructures without altering the cations at the interface, but also provide a purview to delve into the fundamental aspects of exchange bias in such unusual systems, paving a big step forward in thin-film magnetism.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 2
DOI: 10.1103/PHYSREVB.99.024425
|
|
|
“Low-field switching of noncollinear spin texture at La0.7Sr0.3MnO3-SrRuO3interfaces”. Das S, Rata AD, Maznichenko I V, Agrestini IS, Pippel E, Gauquelin N, Verbeeck J, Chen K, Valvidares SM, Vasili HB, Herrero-Martin J, Pellegrin E, Nenkov K, Herklotz A, Ernst A, Mertig I, Hu Z, Doerr K, Physical review B 99, 024416 (2019). http://doi.org/10.1103/PHYSREVB.99.024416
Abstract: Interfaces of ferroic oxides can show complex magnetic textures which have strong impact on spintronics devices. This has been demonstrated recently for interfaces with insulating antiferromagnets such as BiFeO3. Here, noncollinear spin textures which can be switched in very low magnetic field are reported for conducting ferromagnetic bilayers of La0.7Sr0.3MnO3-SrRuO3 (LSMO-SRO). The magnetic order and switching are fundamentally different for bilayers coherently grown in reversed stacking sequence. The SRO top layer forms a persistent exchange spring which is antiferromagnetically coupled to LSMO and drives switching in low fields of a few milliteslas. Density functional theory reveals the crucial impact of the interface termination on the strength of Mn-Ru exchange coupling across the interface. The observation of an exchange spring agrees with ultrastrong coupling for the MnO2/SrO termination. Our results demonstrate low-field switching of noncollinear spin textures at an interface between conducting oxides, opening a pathway for manipulating and utilizing electron transport phenomena in controlled spin textures at oxide interfaces.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 19
DOI: 10.1103/PHYSREVB.99.024416
|
|
|
“Physical properties of epitaxial SrMnO2.5−δFγoxyfluoride films”. Wang J, Shin Y, Gauquelin N, Yang Y, Lee C, Jannis D, Verbeeck J, Rondinelli JM, May SJ, Journal of physics : condensed matter 31, 365602 (2019). http://doi.org/10.1088/1361-648X/ab2414
Abstract: Recently, topotactic fluorination has become an alternative way of doping epitaxial perovskite oxides through anion substitution to engineer their electronic properties instead of the more commonly used cation substitution. In this work, epitaxial oxyfluoride SrMnO2.5−δ F γ films were synthesized via topotactic fluorination of SrMnO2.5 films using polytetrafluoroethylene as the fluorine source. Oxidized SrMnO3 films were also prepared for comparison with the fluorinated samples. The F content, probed by x-ray photoemission spectroscopy, was systematically controlled by adjusting fluorination conditions. Electronic transport measurements reveal that increased F content (up to γ = 0.14) systematically increases the electrical resistivity, despite the nominal electron-doping induced by F substitution for O in these films. In contrast, oxidized SrMnO3 exhibits a decreased resistivity and conduction activation energy. A blue-shift of optical absorption features occurs with increasing F content. Density functional theory calculations indicate that F acts as a scattering center for electronic transport, controls the observed weak ferromagnetic behavior of the films, and reduces the inter-band optical transitions in the manganite films. These results stand in contrast to bulk electron-doped La1−x Ce x MnO3, illustrating how aliovalent anionic substitutions can yield physical behavior distinct from A-site substituted perovskites with the same nominal B-site oxidation states.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.649
Times cited: 5
DOI: 10.1088/1361-648X/ab2414
|
|
|
“High-TCInterfacial Ferromagnetism in SrMnO3/LaMnO3Superlattices”. Keunecke M, Lyzwa F, Schwarzbach D, Roddatis V, Gauquelin N, Müller-Caspary K, Verbeeck J, Callori SJ, Klose F, Jungbauer M, Moshnyaga V, Advanced functional materials , 1808270 (2019). http://doi.org/10.1002/adfm.201808270
Abstract: Heterostructures of strongly correlated oxides demonstrate various intriguing and potentially useful interfacial phenomena. LaMnO3/SrMnO3 superlattices are presented showcasing a new high‐temperature ferromagnetic phase with Curie temperature, TC ≈360 K, caused by electron transfer from the surface of the LaMnO3 donor layer into the neighboring SrMnO3 acceptor layer. As a result, the SrMnO3 (top)/LaMnO3 (bottom) interface shows an enhancement of the magnetization as depth‐profiled by polarized neutron reflectometry. The length scale of charge transfer, λTF ≈2 unit cells, is obtained from in situ growth monitoring by optical ellipsometry, supported by optical simulations, and further confirmed by high resolution electron microscopy and spectroscopy. A model of the inhomogeneous distribution of electron density in LaMnO3/SrMnO3 layers along the growth direction is concluded to account for a complex interplay between ferromagnetic and antiferromagnetic layers in superlattices.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 15.621
Times cited: 26
DOI: 10.1002/adfm.201808270
|
|
|
“Self‐Assembly of Atomically Thin Chiral Copper Heterostructures Templated by Black Phosphorus”. Nerl HC, Pokle A, Jones L, Müller‐Caspary K, Bos KHW, Downing C, McCarthy EK, Gauquelin N, Ramasse QM, Lobato I, Daly D, Idrobo JC, Van Aert S, Van Tendeloo G, Sanvito S, Coleman JN, Cucinotta CS, Nicolosi V, Advanced functional materials 29, 1903120 (2019). http://doi.org/10.1002/adfm.201903120
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.124
Times cited: 1
DOI: 10.1002/adfm.201903120
|
|
|
“Depth-resolved resonant inelastic x-ray scattering at a superconductor/half-metallic-ferromagnet interface through standing wave excitation”. Kuo C-T, Lin S-C, Ghiringhelli G, Peng Y, De Luca GM, Di Castro D, Betto D, Gehlmann M, Wijnands T, Huijben M, Meyer-Ilse J, Gullikson E, Kortright JB, Vailionis A, Gauquelin N, Verbeeck J, Gerber T, Balestrino G, Brookes NB, Braicovich L, Fadley CS, Physical review B 98, 235146 (2018). http://doi.org/10.1103/PHYSREVB.98.235146
Abstract: We demonstrate that combining standing wave (SW) excitation with resonant inelastic x-ray scattering (RIXS) can lead to depth resolution and interface sensitivity for studying orbital and magnetic excitations in correlated oxide heterostructures. SW-RIXS has been applied to multilayer heterostructures consisting of a superconductor La1.85Sr0.15CuO4 (LSCO) and a half-metallic ferromagnet La0.67Sr0.33MnO3 (LSMO). Easily observable SW effects on the RIXS excitations were found in these LSCO/LSMO multilayers. In addition, we observe different depth distribution of the RIXS excitations. The magnetic excitations are found to arise from the LSCO/LSMO interfaces, and there is also a suggestion that one of the dd excitations comes from the interfaces. SW-RIXS measurements of correlated-oxide and other multilayer heterostructures should provide unique layer-resolved insights concerning their orbital and magnetic excitations, as well as a challenge for RIXS theory to specifically deal with interface effects.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 5
DOI: 10.1103/PHYSREVB.98.235146
|
|
|
“Getting rid of anti-solvents: gas quenching for high performance perovskite solar cells”. Conings B, Babayigit A, Klug M, Bai S, Gauquelin N, Sakai N, Wang JT-W, Verbeeck J, Boyen H-G, Snaith H, 2018 Ieee 7th World Conference On Photovoltaic Energy Conversion (wcpec)(a Joint Conference Of 45th Ieee Pvsc, 28th Pvsec &, 34th Eu Pvsec) (2018). http://doi.org/10.1109/PVSC.2018.8547987
Abstract: As the field of perovskite optoelectronics developed, a plethora of strategies has arisen to control their electronic and morphological characteristics for the purpose of producing high efficiency devices. Unfortunately, despite this wealth of deposition approaches, the community experiences a great deal of irreproducibility between different laboratories, batches and preparation methods. Aiming to address this issue, we developed a simple deposition method based on gas quenching that yields smooth films for a wide range of perovskite compositions, in single, double, triple and quadruple cation varieties, and produces planar heterojunction devices with competitive efficiencies, so far up to 20%.
Keywords: P1 Proceeding; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
DOI: 10.1109/PVSC.2018.8547987
|
|
|
“Thickness dependent properties in oxide heterostructures driven by structurally induced metal-oxygen hybridization variations”. Liao Z, Gauquelin N, Green RJ, Macke S, Gonnissen J, Thomas S, Zhong Z, Li L, Si L, Van Aert S, Hansmann P, Held K, Xia J, Verbeeck J, Van Tendeloo G, Sawatzky GA, Koster G, Huijben M, Rijnders G, Advanced functional materials 27, 1606717 (2017). http://doi.org/10.1002/ADFM.201606717
Abstract: Thickness-driven electronic phase transitions are broadly observed in different types of functional perovskite heterostructures. However, uncertainty remains whether these effects are solely due to spatial confinement, broken symmetry, or rather to a change of structure with varying film thickness. Here, this study presents direct evidence for the relaxation of oxygen-2p and Mn-3d orbital (p-d) hybridization coupled to the layer-dependent octahedral tilts within a La2/3Sr1/3MnO3 film driven by interfacial octahedral coupling. An enhanced Curie temperature is achieved by reducing the octahedral tilting via interface structure engineering. Atomically resolved lattice, electronic, and magnetic structures together with X-ray absorption spectroscopy demonstrate the central role of thickness-dependent p-d hybridization in the widely observed dimensionality effects present in correlated oxide heterostructures.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.124
Times cited: 55
DOI: 10.1002/ADFM.201606717
|
|
|
“On the importance of the work function and electron carrier density of oxide electrodes for the functional properties of ferroelectric capacitors”. Wang J, Nguyen MD, Gauquelin N, Verbeeck J, Do MT, Koster G, Rijnders G, Houwman E, Physica Status Solidi-Rapid Research Letters 14, 1900520 (2020). http://doi.org/10.1002/PSSR.201900520
Abstract: It is important to understand the effect of the interfaces between the oxide electrode layers and the ferroelectric layer on the polarization response for optimizing the device performance of all-oxide ferroelectric devices. Herein, the effects of the oxide La0.07Ba0.93SnO3 (LBSO) as an electrode material in an PbZr0.52Ti0.48O3 (PZT) ferroelectric capacitor are compared with those of the more commonly used SrRuO3 (SRO) electrode. SRO (top)/PZT/SRO (bottom), SRO/PZT/LBSO, and SRO/PZT/2 nm SRO/LBSO devices are fabricated. Only marginal differences in crystalline properties, determined by X-ray diffraction and scanning transmission electron microscopy, are found. High-quality polarization loops are obtained, but with a much larger coercive field for the SRO/PZT/LBSO device. In contrast to the SRO/PZT/SRO device, the polarization decreases strongly with increasing field cycling. This fatigue problem can be remedied by inserting a 2 nm SRO layer between PZT and LBSO. It is argued that strongly increased charge injection into the PZT occurs at the bottom interface, because of the low PZT/LBSO interfacial barrier and the much lower carrier density in LBSO, as compared with that in SRO, causing a low dielectric constant, depleted layer in LBSO. The charge injection creates a trapped space charge in the PZT, causing the difference in fatigue behavior.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.8
Times cited: 6
DOI: 10.1002/PSSR.201900520
|
|
|
“Tailoring vanadium dioxide film orientation using nanosheets : a combined microscopy, diffraction, transport, and soft X-ray in transmission study”. Tran Phong Le P, Hofhuis K, Rana A, Huijben M, Hilgenkamp H, Rijnders GAJHM, ten Elshof JE, Koster G, Gauquelin N, Lumbeeck G, Schuessler-Langeheine C, Popescu H, Fortuna F, Smit S, Verbeek XH, Araizi-Kanoutas G, Mishra S, Vaskivskyi I, Duerr HA, Golden MS, Advanced Functional Materials 30, 1900028 (2020). http://doi.org/10.1002/ADFM.201900028
Abstract: Vanadium dioxide (VO2) is a much-discussed material for oxide electronics and neuromorphic computing applications. Here, heteroepitaxy of VO2 is realized on top of oxide nanosheets that cover either the amorphous silicon dioxide surfaces of Si substrates or X-ray transparent silicon nitride membranes. The out-of-plane orientation of the VO2 thin films is controlled at will between (011)(M1)/(110)(R) and (-402)(M1)/(002)(R) by coating the bulk substrates with Ti0.87O2 and NbWO6 nanosheets, respectively, prior to VO2 growth. Temperature-dependent X-ray diffraction and automated crystal orientation mapping in microprobe transmission electron microscope mode (ACOM-TEM) characterize the high phase purity, the crystallographic and orientational properties of the VO2 films. Transport measurements and soft X-ray absorption in transmission are used to probe the VO2 metal-insulator transition, showing results of a quality equal to those from epitaxial films on bulk single-crystal substrates. Successful local manipulation of two different VO2 orientations on a single substrate is demonstrated using VO2 grown on lithographically patterned lines of Ti0.87O2 and NbWO6 nanosheets investigated by electron backscatter diffraction. Finally, the excellent suitability of these nanosheet-templated VO2 films for advanced lensless imaging of the metal-insulator transition using coherent soft X-rays is discussed.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 19
Times cited: 1
DOI: 10.1002/ADFM.201900028
|
|
|
“Interfacial dielectric layer as an origin of polarization fatigue in ferroelectric capacitors”. Do MT, Gauquelin N, Nguyen MD, Wang J, Verbeeck J, Blom F, Koster G, Houwman EP, Rijnders G, Scientific Reports 10, 7310 (2020). http://doi.org/10.1038/s41598-020-64451-0
Abstract: Origins of polarization fatigue in ferroelectric capacitors under electric field cycling still remain unclear. Here, we experimentally identify origins of polarization fatigue in ferroelectric PbZr0.52Ti0.48O3 (PZT) thin-film capacitors by investigating their fatigue behaviours and interface structures. The PZT layers are epitaxially grown on SrRuO3-buffered SrTiO3 substrates by a pulsed laser deposition (PLD), and the capacitor top-electrodes are various, including SrRuO3 (SRO) made by in-situ PLD, Pt by in-situ PLD (Pt-inPLD) and ex-situ sputtering (Pt-sputtered). We found that fatigue behaviour of the capacitor is directly related to the top-electrode/PZT interface structure. The Pt-sputtered/PZT/SRO capacitor has a thin defective layer at the top interface and shows early fatigue while the Pt-inPLD/PZT/SRO and SRO/PZT/SRO capacitor have clean top-interfaces and show much more fatigue resistance. The defective dielectric layer at the Pt-sputtered/PZT interface mainly contains carbon contaminants, which form during the capacitor ex-situ fabrication. Removal of this dielectric layer significantly delays the fatigue onset. Our results clearly indicate that dielectric layer at ferroelectric capacitor interfaces is the main origin of polarization fatigue, as previously proposed in the charge injection model.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.6
Times cited: 18
DOI: 10.1038/s41598-020-64451-0
|
|
|
“Atom column detection from simultaneously acquired ABF and ADF STEM images”. Fatermans J, den Dekker Aj, Müller-Caspary K, Gauquelin N, Verbeeck J, Van Aert S, Ultramicroscopy 219, 113046 (2020). http://doi.org/10.1016/j.ultramic.2020.113046
Abstract: In electron microscopy, the maximum a posteriori (MAP) probability rule has been introduced as a tool to determine the most probable atomic structure from high-resolution annular dark-field (ADF) scanning transmission electron microscopy (STEM) images exhibiting low contrast-to-noise ratio (CNR). Besides ADF imaging, STEM can also be applied in the annular bright-field (ABF) regime. The ABF STEM mode allows to directly visualize light-element atomic columns in the presence of heavy columns. Typically, light-element nanomaterials are sensitive to the electron beam, limiting the incoming electron dose in order to avoid beam damage and leading to images exhibiting low CNR. Therefore, it is of interest to apply the MAP probability rule not only to ADF STEM images, but to ABF STEM images as well. In this work, the methodology of the MAP rule, which combines statistical parameter estimation theory and model-order selection, is extended to be applied to simultaneously acquired ABF and ADF STEM images. For this, an extension of the commonly used parametric models in STEM is proposed. Hereby, the effect of specimen tilt has been taken into account, since small tilts from the crystal zone axis affect, especially, ABF STEM intensities. Using simulations as well as experimental data, it is shown that the proposed methodology can be successfully used to detect light elements in the presence of heavy elements.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 2.2
Times cited: 9
DOI: 10.1016/j.ultramic.2020.113046
|
|