Basile, F.; Benito, P.; Bugani, S.; de Nolf, W.; Fornasari, G.; Janssens, K.; Morselli, L.; Scavetta, E.; Tonelli, D.; Vaccari, A. |
Title |
Combined use of synchrotron-radiation-based imaging techniques for the characterization of structured catalysts |
Type |
A1 Journal article |
Year |
2010 |
Publication |
Advanced functional materials |
Abbreviated Journal |
Adv Funct Mater |
Volume |
20 |
Issue |
23 |
Pages |
4117-4126 |
Keywords |
A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation) |
Abstract |
Active-phase-coated metallic supports as structured catalysts are gaining attention in endothermic and exothermic processes because they improve heat transfer. The deposition of a well-adhered and stable catalyst layer on the metallic support constitutes an important feature for the successful application of the final material. In this work, coating of FeCrAlY foams is performed by a one-step electrosynthesis-deposition of hydrotalcite-type compounds, precursors of catalysts active in endothermic steam methane reforming. The catalysts are studied at different length scales by using, for the first time, a combination of several techniques: SEM/EDS and X-ray fluorescence, X-ray powder diffraction and absorption-tomography experiments on the micro- and nanoscales at a synchrotron facility. The results show that the morphology of the coating depends on the synthesis conditions and that the catalyst may be described as Ni metal crystallites dispersed on γ-Al2O3, homogeneously coating the FeCrAlY foam. |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
|
Editor |
|
Language |
|
Wos |
000285392900010 |
Publication Date |
2010-09-23 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue ![sorted by Series Issue field, descending order (down)](img/sort_desc.gif) |
|
Edition |
|
ISSN |
1616-301x |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
12.124 |
Times cited |
24 |
Open Access |
|
Notes |
; The authors give thanks to Dr. Cloetens, for helping during the absorption tomography experiments, performed at ID19 of the ESRF; and P. Blauet and R. Toucolou, for helping during the mu-XRF/XRPD and nano-XRF experiments at ID22 and ID22-NI of the ESRF. The financial support from the Ministero per l'Istruzione, l'Universita e la Ricerca (MIUR, Roma, Italy) is gratefully acknowledged. ; |
Approved |
Most recent IF: 12.124; 2010 IF: 8.508 |
Call Number |
UA @ admin @ c:irua:85834 |
Serial |
5525 |
Permanent link to this record |
|
|
|
Author |
Benito, P.; Monti, M.; de Nolf, W.; Nuyts, G.; Janssens, K.; et al. |
Title |
Improvement in the coating homogeneity in electrosynthesized Rh structured catalysts for the partial oxidation of methane |
Type |
A1 Journal article |
Year |
2015 |
Publication |
Catalysis today |
Abbreviated Journal |
Catal Today |
Volume |
246 |
Issue |
|
Pages |
154-164 |
Keywords |
A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation) |
Abstract |
The precipitation of Rh/Mg/Al and Rh/Al hydroxides on the surface of FeCrAlloy foams by a base electrogeneration method was investigated to improve the properties of the deposited film (homogeneity and composition) and therefore the performances of the structured catalysts, obtained by calcination, in the Catalytic Partial Oxidation of CH4 to syngas. The work focussed on decreasing current gradients within open-cell foam cylinders by increasing the number of electrical contacts from 1 to 3 points to promote a more homogeneous precipitation of the hydroxides. Electrochemical and catalytic tests as well as SEM/EDS and mu-XRFIXRD analyses allowed to correlate the effect of the number of electrical contact points with materials properties. Lastly, syntheses were performed on Pt plates to study the effect of the electrical behaviour and shape of the support on the composition of the film. A more homogeneous coating of the foam surface was achieved by adopting a configuration with 3 contact points since the reduction of nitrates and water molecules that generates the basic media in the vicinity of the support was enhanced. Layer thicknesses up to 5-15 mu m were deposited; however, the sequential precipitation of a film with composition closer to the expected one and a layer enriched in Al and Rh (outer layer) was not avoided. The improvement in the coating gave rise to enhanced performances for a sample prepared at -1.1 V for 3000 s. Contrarily, the low adherence of the outer layer in a sample prepared at -1.2 V for 2000 s during both calcination and catalytic tests may be responsible of the unexpected decrease in catalytic performances. The same sequential precipitation was observed by performing the syntheses on Pt plates, showing that the electrical nature the support did not play a key role on this phenomenon. (C) 2014 Elsevier B.V. All rights reserved. |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
|
Editor |
|
Language |
|
Wos |
000349998300020 |
Publication Date |
2014-10-31 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue ![sorted by Series Issue field, descending order (down)](img/sort_desc.gif) |
|
Edition |
|
ISSN |
0920-5861 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
4.636 |
Times cited |
14 |
Open Access |
|
Notes |
; The financial support from the Ministero per l'Istruzione, l'Universita e la Ricerca (MIUR, Roma, I) is gratefully acknowledged. The authors thank D. Grolimund and C.N. Borca for assisting the mu XRF/XRD conducted experiments at MicroXAS Beamline of SLS Thanks are due to Porvair for supplying FeCrAlloy foams. ; |
Approved |
Most recent IF: 4.636; 2015 IF: 3.893 |
Call Number |
UA @ admin @ c:irua:124616 |
Serial |
5656 |
Permanent link to this record |
|
|
|
Author |
Benito, P.; de Nolf, W.; Nuyts, G.; Janssens, K.; et al. |
Title |
Role of coating-metallic support interaction in the properties of electrosynthesized Rh-based structured catalysts |
Type |
A1 Journal article |
Year |
2014 |
Publication |
ACS catalysis |
Abbreviated Journal |
Acs Catal |
Volume |
4 |
Issue |
10 |
Pages |
3779-3790 |
Keywords |
A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation) |
Abstract |
Rh-structured catalysts for the catalytic partial oxidation of CH4 to syngas were prepared by electrosynthesis of Rh-containing hydrotalcite-type (HT) compounds on FeCrAlloy foams followed by calcination at 900 degrees C. During the calcination the simultaneous decomposition of the layered HT structure and formation of the protective FeCrAlloy outer shell in alumina occurred. Here, we studied the role of the coating-metallic support interaction in the properties of the catalysts after calcination, H-2 reduction, and catalytic tests, by a combination of electron (FEG-SEM/EDS) and synchrotron X-ray (XRF/XRPD and XRF/XANES) microscopic techniques. The characterization of crystalline phases in the metallic support and coating and distribution of Rh active species was carried out on several samples prepared by modifying the Rh content in the electrolytic solution (Rh/Mg/Al = 11.0/70.0/19.0, 5.0/70.0/25.0, 0/70.0/30.0 atomic ratio). A sample was also prepared with no aluminum in the electrolytic solution (Rh/Mg/Al = 13.6/86.4/0.0 atomic ratio) and calcined at 550 and 900 degrees C. The interaction between the elements of the metallic support and the catalytic coating increased the film adhesion during the thermal treatment and catalytic tests and modified the catalyst crystalline phases. A chemical reaction between Al corning from the foam and Mg in the coating occurred during calcination at high temperature leading to the formation of spinel phases in which rhodium is solved, together with some Rh2O3 and Rh. The metallic support was oxidized forming the corundum scale and chromium oxides, moreover t-Al2O3 was identified. For the Rh11.0Mg70.0Al19.0 catalyst the inclusion of Rh in the spinel phase decreased its reducibility in the H-2 pretreatment. The reduction continued during catalytic tests by feeding diluted CH4/O-2/He gas mixtures, evidenced by the catalyst activation. While under concentrated gas mixtures the deactivation occurred, probably by oxidation. |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
|
Editor |
|
Language |
|
Wos |
000345735200053 |
Publication Date |
2014-09-24 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue ![sorted by Series Issue field, descending order (down)](img/sort_desc.gif) |
|
Edition |
|
ISSN |
2155-5435 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
10.614 |
Times cited |
13 |
Open Access |
|
Notes |
; The authors thank the scientists who assisted during the conducted experiments: D. Grolimund and C. N. Borca for the mu XRF/XRPD experiments performed at MicroXAS Beamline of SLS, M. Janousch for the mu XRF/XANES experiments at Phoenix Beamline of the SLS, M. Salome for the mu XRE/XANES experiments at ID21 Beamline of the ESRF, and I. Guerra for the FEG-SEM/EDS experiments at Granada University. Thanks must go to Porvair for supplying FeCrAlloy foams. The financial support from the Ministero per l'Istruzione, l'Universita e la Ricerca (MIUR, Roma, I) is gratefully acknowledged. ; |
Approved |
Most recent IF: 10.614; 2014 IF: 9.312 |
Call Number |
UA @ admin @ c:irua:122215 |
Serial |
5820 |
Permanent link to this record |
|
|
|
Author |
Benito, P.; Nuyts, G.; Monti, M.; de Nolf, W.; Fornasari, G.; Janssens, K.; Scavetta, E.; Vaccari, A. |
Title |
Stable Rh particles in hydrotalcite-derived catalysts coated on FeCrAlloy foams by electrosynthesis |
Type |
A1 Journal article |
Year |
2015 |
Publication |
Applied catalysis : B : environmental |
Abbreviated Journal |
Appl Catal B-Environ |
Volume |
179 |
Issue |
|
Pages |
321-332 |
Keywords |
A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation) |
Abstract |
Rh-based structured catalysts for the Catalytic Partial Oxidation of CH4 to syngas were prepared by electrosynthesis of Rh/Mg/Al hydrotalcite-type compounds on FeCrAlloy foams and calcination. The effects of Rh content, total metal concentration, and partial replacement of Mg2+ by Ni2+ in the electrolytic solution on coating thickness, Rh speciation, metallic particle size, and catalytic activity were investigated by SEM/EDS, mu-XRF/XANES and tests under diluted and concentrated reaction conditions. The amount of Rh species, present as Mg (RhxAl1-x)(2)O-4, depended on the thickness of the electrosynthesised layer as well as the Rh particle size and dispersion. Smaller and more dispersed particles were obtained by decreasing the Rh concentration in the electrolytic solution from Rh/Mg/Al=11/70/19 to 5/70/25 and 2/70/28 atomic ratio% (a.r.%) and in thinner rather than thicker layers. Despite the improvement in metallic particles features, the CH4 conversion was negatively affected by the low amount of active sites in the coating, the high metal support interaction and possibly the oxidation of metallic particles and carbon formation. A larger amount of solid containing well dispersed Rh particles was deposited by increasing the total metal concentration from 0.03 M to 0.06 M with the Rh/Mg/Al=5/70/25 a.r.%, and the catalytic performances were enhanced. The partial replacement of Mg2+ by Ni2+ gave rise to a very active bimetallic Rh/Ni catalyst, CH4 conversion and selectivity to syngas were above 90%, however, it slightly deactivated with time-on-stream. (C) 2015 Elsevier B.V. All rights reserved. |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
|
Editor |
|
Language |
|
Wos |
000359873800036 |
Publication Date |
2015-05-19 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue ![sorted by Series Issue field, descending order (down)](img/sort_desc.gif) |
|
Edition |
|
ISSN |
0926-3373 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
9.446 |
Times cited |
14 |
Open Access |
|
Notes |
; The Authors acknowledge M. Salome for helping during the mu XRF/XANES experiments at ID21 Beamline of the ESRF, the Department of Structural Characterisation of CNR-IMM of Bologna for the access to the FEG-SEM facility and Dr F. Ospitali for the scientific support. Thanks are due to Farrel Lytle database for providing the necessary Rh metal spectrum (rhfoil.a99 in http:// ixs.iit.edu/data/FarrelLytledata/). The financial support from the Ministero per l'Istruzione, l'Universita e la Ricerca (MIUR, Roma, Italy) and the University of Bologna (FARB program) is gratefully acknowledged. ; |
Approved |
Most recent IF: 9.446; 2015 IF: 7.435 |
Call Number |
UA @ admin @ c:irua:127777 |
Serial |
5846 |
Permanent link to this record |