Abstract: The irradiation effects of thinning a sample of a Cu-Zn-Al shape memory alloy to electron transparency by a Ga+ focused ion beam were investigated. This thinning method was compared with conventional electropolishing and Ar+ ion milling. No implanted Ga was detected but surface FCC precipitation was found as a result of the focused ion beam sample preparation. Decreasing the irradiation dose by lowering the energy and current of the Ga+ ions did not lead to a complete disappearance of the FCC structure. The latter could only be removed after gentle Ar+ ion milling of the sample. It was further concluded that the precipitation of the FCC is independent of the crystallographic orientation of the surface.

Abstract: A method to prepare TEM specimens from metallic microwires and based on conventional twin-jet electropolishing is introduced. The wire is embedded in an opaque epoxy resin medium and the hardened resin is mechanically polished to reveal the wire on both sides. The resin containing wire is then cut into discs of the appropriate size. The obtained embedded wire is electropolished in a conventional twin-jet electropolishing machine until electron transparency in large areas without radiation damage is achieved.

Abstract: The mechanical properties of olivine-rich rocks are key to determining the mechanical coupling between Earth's lithosphere and asthenosphere. In crystalline materials, the motion of crystal defects is fundamental to plastic flow(1-4.) However, because the main constituent of olivine-rich rocks does not have enough slip systems, additional deformation mechanisms are needed to satisfy strain conditions. Experimental studies have suggested a non-Newtonian, grain-size-sensitive mechanism in olivine involving grain-boundary sliding(5,6). However, very few microstructural investigations have been conducted on grain-boundary sliding, and there is no consensus on whether a single or multiple physical mechanisms are at play. Most importantly, there are no theoretical frameworks for incorporating the mechanics of grain boundaries in polycrystalline plasticity models. Here we identify a mechanism for deformation at grain boundaries in olivine-rich rocks. We show that, in forsterite, amorphization takes place at grain boundaries under stress and that the onset of ductility of olivine-rich rocks is due to the activation of grain-boundary mobility in these amorphous layers. This mechanism could trigger plastic processes in the deep Earth, where high-stress conditions are encountered (for example, at the brittle-plastic transition). Our proposed mechanism is especially relevant at the lithosphere-asthenosphere boundary, where olivine reaches the glass transition temperature, triggering a decrease in its viscosity and thus promoting grain-boundary sliding.

Abstract: Stacking faults are known as defective structures in crystalline materials that typically lower the structural quality of the material. Here, we show that a particular type of defects, i.e., stacking fault tetrahedra (SFTs), exhibits quantized, particle-in-a-box electronic behaviour, revealing a potential synthetic route to decoupled nanoparticles in metal films. We report on the electronic properties of SFTs that exist in Au(111) films, as evidenced by scanning tunnelling microscopy and confirmed by transmission electron microscopy. We find that the SFTs reveal a remarkable decoupling from their metal surroundings, leading to pronounced energy level quantization effects within the SFTs. The electronic behaviour of the SFTs can be described well by the particle-in-a-box model. Our findings demonstrate that controlled preparation of SFTs may offer an alternative way to achieve well decoupled nanoparticles of high crystalline quality in metal thin films without the need of thin insulating layers.

Abstract: NiTi is one of the most popular shape-memory alloys, a phenomenon resulting from a martensitic transformation. Commercial NiTi-based alloys are often thermally treated to contain Ni4Ti3 precipitates. The presence of these precipitates can introduce an extra transformation step related to the so-called R-phase. It is believed that the strain field surrounding the precipitates, caused by the matrixprecipitate lattice mismatch, lies at the origin of this intermediate transformation step. Atomic-resolution transmission electron microscopy in combination with geometrical phase analysis is used to measure the elastic strain field surrounding these precipitates. By combining measurements from two different crystallographic directions, the three-dimensional strain matrix is determined from two-dimensional measurements. Comparison of the measured strain matrix to the eigenstrain of the R-phase shows that both are very similar and that the introduction of the R-phase might indeed compensate the elastic strain introduced by the precipitate.

Abstract: Functional interfaces are at the core of research in the emerging field of domain boundary engineering where polar, conducting, chiral, and other interfaces and twin boundaries have been discovered. Ferroelectricity was found in twin walls of paraelectric CaTiO3. We show that the effect of functional interfaces can be optimized if the number of twin boundaries is increased in densely twinned materials. Such materials can be produced by shear in the ferroelastic phase rather than by rapid quench from the paraelastic phase.

Abstract: Recent findings have linked low hysteresis in shape memory alloys with phase compatibility between austenite and martensite. To investigate the evolution of microstructure as phase compatibility increases and hysteresis is reduced, transmission electron microscopy was used to study the alloy system Ti50Ni50xPdx, where the composition is systemically tuned to approach perfect compatibility. Changes in morphology, twinning density and twinning modes are reported, along with special microstructures occurring when compatibility is achieved. In addition, the interface between austenite and a single variant of martensite was studied by high-resolution and conventional electron microscopy. The low energy configuration of the interface detailed in this article suggests that it plays an important role in the lowering of hysteresis compared to classical habit plane interfaces.

Abstract: The structure of the metastable Ni2Al phase, which has long been a matter of controversy, has been carefully re-examined by means of high-resolution transmission electron microscopy (HREM) and electron microdiffraction. First, it is concluded that theas-quenched NixAl100-x(60 less-than-or-equal-to x less-than-or-equal-to 65) material already exhibits a partial omega-type collapse in a one-dimensional fashion which and is consistent with the anomalous dip in the phonon dispersion curve. Ni2Al precipitates are formed on annealing by thermal decomposition of the high-temperature NixAl100-xB2 phase and still retain the small omega-type shuffle. The amount of displacement in the well developed Ni2Al phase was estimated to be between 20 and 50% of the ideal omega collapse; this was determined by means of a combined technique of HREM and microdiffraction together with dynamical calculations of HREM images and diffraction intensities.

Abstract: Advanced transmission electron microscopy and statistical parameter estimated quantification procedures were applied to study the room temperature quasi-dynamical strain glass state in NiTi alloys. Nanosized strain pockets are visualised and the displacements of the atom columns are quantified. A comparison is made with conventional high-resolution transmission electron microscopy images of point defect induced strains in NiAl alloys.

Abstract: A large number of materials have a highly degenerate ground state and therefore a complex microstructure. Because of this degenerate state, phase transitions between the different phases play an important role. High resolution techniques in electron microscopy and nano-scale chemical analysis allow to study not only the microstructure but also the interfaces down to an atomic scale. We focus particularly on the ambiguity of alloys oil approaching the phase transition. The short range order (SRO) in ''1 1/20'' type alloys and the microstructure of ''tweed'' and needle formation in martensite like alloys with composition Ni5Al3 are considered in more detail.