“Substitutional phosphorus incorporation in nanocrystalline CVD diamond thin films”. Janssen W, Turner S, Sakr G, Jomard F, Barjon J, Degutis G, Lu YG, D'Haen J, Hardy A, Bael MV, Verbeeck J, Van Tendeloo G, Haenen K, Physica status solidi: rapid research letters 8, 705 (2014). http://doi.org/10.1002/pssr.201409235
Abstract: Nanocrystalline diamond (NCD) thin films were produced by chemical vapor deposition (CVD) and doped by the addition of phosphine to the gas mixture. The characterization of the films focused on probing the incorporation and distribution of the phosphorus (P) dopants. Electron microscopy evaluated the overall film morphology and revealed the interior structure of the nanosized grains. The homogeneous films with distinct diamond grains featured a notably low sp(2):sp(3)-ratio as confirmed by Raman spectroscopy. High resolution spectroscopy methods demonstrated a homogeneous P-incorporation, both in-depth and in-plane. The P concentration in the films was determined to be in the order of 10(19) cm(-3) with a significant fraction integrated at substitutional donor sites. (C) 2014 WILEY-VCH Verlag GmbH Co. KGaA, Weinheim
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.032
Times cited: 20
DOI: 10.1002/pssr.201409235
|
“Homopolymers as nanocarriers for the loading of block copolymer micelles with metal salts : a facile way to large-scale ordered arrays of transition-metal nanoparticles”. Shan L, Punniyakoti S, Van Bael MJ, Temst K, Van Bael MK, Ke X, Bals S, Van Tendeloo G, D'Olieslaeger M, Wagner P, Haenen K, Boyen HG;, Journal of materials chemistry C : materials for optical and electronic devices 2, 701 (2014). http://doi.org/10.1039/c3tc31333f
Abstract: A new and facile approach is presented for generating quasi-regular patterns of transition metal-based nanoparticles on flat substrates exploiting polystyrene-block-poly2vinyl pyridine (PS-b-P2VP) micelles as intermediate templates. Direct loading of such micellar nanoreactors by polar transition metal salts in solution usually results in nanoparticle ensembles exhibiting only short range order accompanied by broad distributions of particle size and inter-particle distance. Here, we demonstrate that the use of P2VP homopolymers of appropriate length as molecular carriers to transport precursor salts into the micellar cores can significantly increase the degree of lateral order within the final nanoparticle arrays combined with a decrease in spreading in particle size. Thus, a significantly extended range of materials is now available which can be exploited to study fundamental properties at the transition from clusters to solids by means of well-organized, well-separated, size-selected metal and metal oxide nanostructures.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.256
Times cited: 5
DOI: 10.1039/c3tc31333f
|
“Oscillations of the superconducting temperature induced by quantum well states in thin metallic films: numerical solution of the Bogoliubov-de Gennes equations”. Shanenko AA, Croitoru MD, Peeters FM, Physical review : B : condensed matter and materials physics 75, 014519 (2007). http://doi.org/10.1103/PhysRevB.75.014519
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Condensed Matter Theory (CMT)
Impact Factor: 3.836
Times cited: 85
DOI: 10.1103/PhysRevB.75.014519
|
“Dependence of superconducting properties on the size and shape of a nanoscale superconductor: from nanowire to film”. Croitoru MD, Shanenko AA, Peeters FM, Physical review : B : condensed matter and materials physics 76, 024511 (2007). http://doi.org/10.1103/PhysRevB.76.024511
Keywords: A1 Journal article; Condensed Matter Theory (CMT); Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 54
DOI: 10.1103/PhysRevB.76.024511
|
“First-principles study of CO and OH adsorption on in-doped ZnO surfaces”. Saniz R, Sarmadian N, Partoens B, Batuk M, Hadermann J, Marikutsa A, Rumyantseva M, Gaskov A, Lamoen D, The journal of physics and chemistry of solids 132, 172 (2019). http://doi.org/10.1016/j.jpcs.2019.04.023
Abstract: We present a first-principles computational study of CO and OH adsorption on non-polar ZnO (10¯10) surfaces doped with indium. The calculations were performed using a model ZnO slab. The position of the In dopants was varied from deep bulk-like layers to
the surface layers. It was established that the preferential location of the In atoms is at the surface by examining the dependence of
the defect formation energy as well as the surface energy on In location. The adsorption sites on the surface of ZnO and the energy
of adsorption of CO molecules and OH-species were determined in connection to In doping. It was found that OH has higher
bonding energy to the surface than CO. The presence of In atoms at the surface of ZnO is favorable for CO adsorption, resulting
in an elongation of the C-O bond and in charge transfer to the surface. The effect of CO and OH adsorption on the electronic
and conduction properties of surfaces was assessed. We conclude that In-doped ZnO surfaces should present a higher electronic
response upon adsorption of CO.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Condensed Matter Theory (CMT)
Impact Factor: 2.059
Times cited: 7
DOI: 10.1016/j.jpcs.2019.04.023
|
“Porous nanostructured metal oxides synthesized through atomic layer deposition on a carbonaceous template followed by calcination”. Deng S, Kurttepeli M, Cott DJ, Bals S, Detavernier C, Journal of materials chemistry A : materials for energy and sustainability 3, 2642 (2015). http://doi.org/10.1039/C4TA05165C
Abstract: Porous metal oxides with nano-sized features attracted intensive interest in recent decades due to their high surface area which is essential for many applications, e.g. Li ion batteries, photocatalysts, fuel cells and dye-sensitized solar cells. Various approaches have so far been investigated to synthesize porous nanostructured metal oxides, including self-assembly and template-assisted synthesis. For the latter approach, forests of carbon nanotubes are considered as particularly promising templates, with respect to their one-dimensional nature and the resulting high surface area. In this work, we systematically investigate the formation of porous metal oxides (Al2O3, TiO2, V2O5 and ZnO) with different morphologies using atomic layer deposition on multi-walled carbon nanotubes followed by post-deposition calcination. X-ray diffraction, scanning electron microscopy accompanied by X-ray energy dispersive spectroscopy and transmission electron microscopy were used for the investigation of morphological and structural transitions at the micro- and nano-scale during the calcination process. The crystallization temperature and the surface coverage of the metal oxides and the oxidation temperature of the carbon nanotubes were found to produce significant influence on the final morphology.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 8.867
Times cited: 23
DOI: 10.1039/C4TA05165C
|
“Three-dimensional elemental mapping at the atomic scale in bimetallic nanocrystals”. Goris B, de Backer A, Van Aert S, Gómez-Graña S, Liz-Marzán LM, Van Tendeloo G, Bals S, Nano letters 13, 4236 (2013). http://doi.org/10.1021/nl401945b
Abstract: A thorough understanding of the three-dimensional (3D) atomic structure and composition of coreshell nanostructures is indispensable to obtain a deeper insight on their physical behavior. Such 3D information can be reconstructed from two-dimensional (2D) projection images using electron tomography. Recently, different electron tomography techniques have enabled the 3D characterization of a variety of nanostructures down to the atomic level. However, these methods have all focused on the investigation of nanomaterials containing only one type of chemical element. Here, we combine statistical parameter estimation theory with compressive sensing based tomography to determine the positions and atom type of each atom in heteronanostructures. The approach is applied here to investigate the interface in coreshell Au@Ag nanorods but it is of great interest in the investigation of a broad range of nanostructures.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.712
Times cited: 90
DOI: 10.1021/nl401945b
|
“Plasmon mapping in Au@Ag nanocube assemblies”. Goris B, Guzzinati G, Fernández-López C, Pérez-Juste J, Liz-Marzán LM, Trügler A, Hohenester U, Verbeeck J, Bals S, Van Tendeloo G, The journal of physical chemistry: C : nanomaterials and interfaces 118, 15356 (2014). http://doi.org/10.1021/jp502584t
Abstract: Surface plasmon modes in metallic nanostructures largely determine their optoelectronic properties. Such plasmon modes can be manipulated by changing the morphology of the nanoparticles or by bringing plasmonic nanoparticle building blocks close to each other within organized assemblies. We report the EELS mapping of such plasmon modes in pure Ag nanocubes, Au@Ag coreshell nanocubes, and arrays of Au@Ag nanocubes. We show that these arrays enable the creation of interesting plasmonic structures starting from elementary building blocks. Special attention will be dedicated to the plasmon modes in a triangular array formed by three nanocubes. Because of hybridization, a combination of such nanotriangles is shown to provide an antenna effect, resulting in strong electrical field enhancement at the narrow gap between the nanotriangles.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.536
Times cited: 41
DOI: 10.1021/jp502584t
|
“Long-range orientation and atomic attachment of nanocrystals in 2D honeycomb superlattices”. Boneschanscher MP, Evers WH, Geuchies JJ, Altantzis T, Goris B, Rabouw FT, van Rossum SAP, van der Zant HSJ, Siebbeles LDA, Van Tendeloo G, Swart I, Hilhorst J, Petukhov AV, Bals S, Vanmaekelbergh D;, Science 344, 1377 (2014). http://doi.org/10.1126/science.1252642
Abstract: Oriented attachment of synthetic semiconductor nanocrystals is emerging as a route for obtaining new semiconductors that can have Dirac-type electronic bands like graphene, but also strong spin-orbit coupling. The two-dimensional assembly geometry will require both atomic coherence and long-range periodicity of the superlattices. We show how the interfacial self-assembly and oriented attachment of nanocrystals results in two-dimensional (2D) metal chalcogenide semiconductors with a honeycomb superlattice. We present an extensive atomic and nanoscale characterization of these systems using direct imaging and wave scattering methods. The honeycomb superlattices are atomically coherent, and have an octahedral symmetry that is buckled; the nanocrystals occupy two parallel planes. Considerable necking and large-scale atomic motion occurred during the attachment process.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 37.205
Times cited: 304
DOI: 10.1126/science.1252642
|
“Single-step alcohol-free synthesis of coreshell nanoparticles of \gamma-casein micelles and silica”. Kerkhofs S, Leroux F, Allouche L, Mellaerts R, Jammaer J, Aerts A, Kirschhock CEA, Magusin PCMM, Taulelle F, Bals S, Van Tendeloo G, Martens JA;, RSC advances 4, 25650 (2014). http://doi.org/10.1039/C4RA03252G
Abstract: A new, single-step protocol for wrapping individual nanosized β-casein micelles with silica is presented. This biomolecule-friendly synthesis proceeds at low protein concentration at almost neutral pH, and makes use of sodium silicate instead of the common silicon alkoxides. This way, formation of potentially protein-denaturizing alcohols can be avoided. The pH of the citrate-buffered synthesis medium is close to the isoelectric point of β-casein, which favours micelle formation. A limited amount of sodium silicate is added to the protein micelle suspension, to form a thin silica coating around the β-casein micelles. The size distribution of the resulting proteinsilica structures was characterized using DLS and SAXS, as well as 1H NMR DOSY with a dedicated pulsed-field gradient cryo-probehead to cope with the low protein concentration. The degree of silica-condensation was investigated by 29Si MAS NMR, and the nanostructure was revealed by advanced electron microscopy techniques such as ESEM and HAADF-STEM. As indicated by the combined characterization results, a silica shell of 2 nm is formed around individual β-casein micelles giving rise to separate protein coresilica shell nanoparticles of 17 nm diameter. This alcohol-free method at mild temperature and pH is potentially suited for packing protein molecules into bio-compatible silica nanocapsules for a variety of applications in biosensing, therapeutic protein delivery and biocatalysis.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.108
Times cited: 3
DOI: 10.1039/C4RA03252G
|
“Using electron vortex beams to determine chirality of crystals in transmission electron microscopy”. Juchtmans R, Béché, A, Abakumov A, Batuk M, Verbeeck J, Physical review : B : condensed matter and materials physics 91, 094112 (2015). http://doi.org/10.1103/PhysRevB.91.094112
Abstract: We investigate electron vortex beams elastically scattered on chiral crystals. After deriving a general expression for the scattering amplitude of a vortex electron, we study its diffraction on point scatterers arranged on a helix. We derive a relation between the handedness of the helix and the topological charge of the electron vortex on one hand and the symmetry of the higher-order Laue zones in the diffraction pattern on the other for kinematically and dynamically scattered electrons. We then extend this to atoms arranged on a helix as found in crystals which belong to chiral space groups and propose a method to determine the handedness of such crystals by looking at the symmetry of the diffraction pattern. In contrast to alternative methods, our technique does not require multiple scattering, which makes it possible to also investigate extremely thin samples in which multiple scattering is suppressed. In order to verify the model, elastic scattering simulations are performed, and an experimental demonstration on Mn2Sb2O7 is given in which we find the sample to belong to the right-handed variant of its enantiomorphic pair. This demonstrates the usefulness of electron vortex beams to reveal the chirality of crystals in a transmission electron microscope and provides the required theoretical basis for further developments in this field.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 54
DOI: 10.1103/PhysRevB.91.094112
|
“Measuring lattice strain in three dimensions through electron microscopy”. Goris B, de Beenhouwer J, de Backer A, Zanaga D, Batenburg KJ, Sánchez-Iglesias A, Liz-Marzán LM, Van Aert S, Bals S, Sijbers J, Van Tendeloo G, Nano letters 15, 6996 (2015). http://doi.org/10.1021/acs.nanolett.5b03008
Abstract: The three-dimensional (3D) atomic structure of nanomaterials, including strain, is crucial to understand their properties. Here, we investigate lattice strain in Au nanodecahedra using electron tomography. Although different electron tomography techniques enabled 3D characterizations of nanostructures at the atomic level, a reliable determination of lattice strain is not straightforward. We therefore propose a novel model-based approach from which atomic coordinates are measured. Our findings demonstrate the importance of investigating lattice strain in 3D.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 12.712
Times cited: 87
DOI: 10.1021/acs.nanolett.5b03008
|
“Solving the structure of Li ion battery materials with precession electron diffraction : application to Li2CoPo4F”. Hadermann J, Abakumov AM, Turner S, Hafideddine Z, Khasanova NR, Antipov EV, Van Tendeloo G, Chemistry of materials 23, 3540 (2011). http://doi.org/10.1021/cm201257b
Abstract: The crystal structure of the Li2CoPO4F high-voltage cathode for Li ion rechargeable batteries has been completely solved from precession electron diffraction (PED) data, including the location of the Li atoms. The crystal structure consists of infinite chains of CoO4F2 octahedra sharing common edges and linked into a 3D framework by PO4 tetrahedra. The chains and phosphate anions together delimit tunnels filled with the Li atoms. This investigation demonstrates that PED can be successfully applied for obtaining structural information on a variety of Li-containing electrode materials even from single micrometer-sized crystallites.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 46
DOI: 10.1021/cm201257b
|
“A simplified approach to the band gap correction of defect formation energies : Al, Ga, and In-doped ZnO”. Saniz R, Xu Y, Matsubara M, Amini MN, Dixit H, Lamoen D, Partoens B, The journal of physics and chemistry of solids 74, 45 (2013). http://doi.org/10.1016/j.jpcs.2012.07.017
Abstract: The calculation of defect levels in semiconductors within a density functional theory approach suffers greatly from the band gap problem. We propose a band gap correction scheme that is based on the separation of energy differences in electron addition and relaxation energies. We show that it can predict defect levels with a reasonable accuracy, particularly in the case of defects with conduction band character, and yet is simple and computationally economical. We apply this method to ZnO doped with group III elements (Al, Ga, In). As expected from experiment, the results indicate that Zn substitutional doping is preferred over interstitial doping in Al, Ga, and In-doped ZnO, under both zinc-rich and oxygen-rich conditions. Further, all three dopants act as shallow donors, with the +1 charge state having the most advantageous formation energy. Also, doping effects on the electronic structure of ZnO are sufficiently mild so as to affect little the fundamental band gap and lowest conduction bands dispersion, which secures their n-type transparent conducting behavior. A comparison with the extrapolation method based on LDA+U calculations and with the HeydScuseriaErnzerhof hybrid functional (HSE) shows the reliability of the proposed scheme in predicting the thermodynamic transition levels in shallow donor systems.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Condensed Matter Theory (CMT)
Impact Factor: 2.059
Times cited: 36
DOI: 10.1016/j.jpcs.2012.07.017
|
“Direct space structure solution from precession electron diffraction data: resolving heavy and light scatterers in Pb13Mn9O25”. Hadermann J, Abakumov AM, Tsirlin AA, Filonenko VP, Gonnissen J, Tan H, Verbeeck J, Gemmi M, Antipov EV, Rosner H, Ultramicroscopy 110, 881 (2010). http://doi.org/10.1016/j.ultramic.2010.03.012
Abstract: The crystal structure of a novel compound Pb13Mn9O25 has been determined through a direct space structure solution with a Monte-Carlo-based global optimization using precession electron diffraction data (a=14.177(3) Å, c=3.9320(7) Å, SG P4/m, RF=0.239) and compositional information obtained from energy dispersive X-ray analysis and electron energy loss spectroscopy. This allowed to obtain a reliable structural model even despite the simultaneous presence of both heavy (Pb) and light (O) scattering elements and to validate the accuracy of the electron diffraction-based structure refinement. This provides an important benchmark for further studies of complex structural problems with electron diffraction techniques. Pb13Mn9O25 has an anion- and cation-deficient perovskite-based structure with the A-positions filled by the Pb atoms and 9/13 of the B positions filled by the Mn atoms in an ordered manner. MnO6 octahedra and MnO5 tetragonal pyramids form a network by sharing common corners. Tunnels are formed in the network due to an ordered arrangement of vacancies at the B-sublattice. These tunnels provide sufficient space for localization of the lone 6s2 electron pairs of the Pb2+ cations, suggested as the driving force for the structural difference between Pb13Mn9O25 and the manganites of alkali-earth elements with similar compositions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.843
Times cited: 24
DOI: 10.1016/j.ultramic.2010.03.012
|
“New perovskite-based manganite Pb2Mn2O5”. Hadermann J, Abakumov AM, Perkisas T, d' Hondt H, Tan H, Verbeeck J, Filonenko VP, Antipov EV, Van Tendeloo G, Journal of solid state chemistry 183, 2190 (2010). http://doi.org/10.1016/j.jssc.2010.07.032
Abstract: A new perovskite based compound Pb2Mn2O5 has been synthesized using a high pressure high temperature technique. The structure model of Pb2Mn2O5 is proposed based on electron diffraction, high angle annular dark field scanning transmission electron microscopy and high resolution transmission electron microscopy. The compound crystallizes in an orthorhombic unit cell with parameters a=5.736(1)Å≈√2a p p p (a p the parameter of the perovskite subcell) and space group Pnma. The Pb2Mn2O5 structure consists of quasi two-dimensional perovskite blocks separated by 1/2[110] p (1̄01) p crystallographic shear planes. The blocks are connected to each other by chains of edge-sharing MnO5 distorted tetragonal pyramids. The chains of MnO5 pyramids and the MnO6 octahedra of the perovskite blocks delimit six-sided tunnels accommodating double chains of Pb atoms. The tunnels and pyramidal chains adopt two mirror-related configurations (left L and right R) and layers consisting of chains and tunnels of the same configuration alternate in the structure according to an -LRLR-sequence. The sequence is sometimes locally violated by the appearance of -LL- or -RR-fragments. A scheme is proposed with a JahnTeller distortion of the MnO6 octahedra with two long and two short bonds lying in the ac plane, along two perpendicular orientations within this plane, forming a d-type pattern.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 8
DOI: 10.1016/j.jssc.2010.07.032
|
“Effect of high temperature deposition on CoSi2 phase formation”. Comrie CM, Ahmed A, Smeets D, Demeulemeester J, Turner S, Van Tendeloo G, Detavernier C, Vantomme A, Journal of applied physics 113, 234902 (2013). http://doi.org/10.1063/1.4811352
Abstract: This paper discusses the nucleation behaviour of the CoSi to CoSi2 transformation from cobalt silicide thin films grown by deposition at elevated substrate temperatures ranging from 375 °C to 600 °C. A combination of channelling, real-time Rutherford backscattering spectrometry, real-time x-ray diffraction, and transmission electron microscopy was used to investigate the effect of the deposition temperature on the subsequent formation temperature of CoSi2, its growth behaviour, and the epitaxial quality of the CoSi2 thus formed. The temperature at which deposition took place was observed to exert a significant and systematic influence on both the formation temperature of CoSi2 and its growth mechanism. CoSi films grown at the lowest temperatures were found to increase the CoSi2 nucleation temperature above that of CoSi2 grown by conventional solid phase reaction, whereas the higher deposition temperatures reduced the nucleation temperature significantly. In addition, a systematic change in growth mechanism of the subsequent CoSi2 growth occurs as a function of deposition temperature. First, the CoSi2 growth rate from films grown at the lower reactive deposition temperatures is substantially lower than that grown at higher reactive deposition temperatures, even though the onset of growth occurs at a higher temperature, Second, for deposition temperatures below 450 °C, the growth appears columnar, indicating nucleation controlled growth. Elevated deposition temperatures, on the other hand, render the CoSi2 formation process layer-by-layer which indicates enhanced nucleation of the CoSi2 and diffusion controlled growth. Our results further indicate that this observed trend is most likely related to stress and changes in microstructure introduced during reactive deposition of the CoSi film. The deposition temperature therefore provides a handle to tune the CoSi2 growth mechanism.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.068
Times cited: 2
DOI: 10.1063/1.4811352
|
“Site-specific mapping of transition metal oxygen coordination in complex oxides”. Turner S, Egoavil R, Batuk M, Abakumov AA, Hadermann J, Verbeeck J, Van Tendeloo G, Applied physics letters 101, 241910 (2012). http://doi.org/10.1063/1.4770512
Abstract: We demonstrate site-specific mapping of the oxygen coordination number for transition metals in complex oxides using atomically resolved electron energy-loss spectroscopy in an aberration-corrected scanning transmission electron microscope. Pb2Sr2Bi2Fe6O16 contains iron with a constant Fe3+ valency in both octahedral and tetragonal pyramidal coordination and is selected to demonstrate the principle of site-specific coordination mapping. Analysis of the site-specific Fe-L2,3 data reveals distinct variations in the fine structure that are attributed to Fe in a six-fold (octahedron) or five-fold (distorted tetragonal pyramid) oxygen coordination. Using these variations, atomic resolution coordination maps are generated that are in excellent agreement with simulations.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 12
DOI: 10.1063/1.4770512
|
“Development of photocatalytic efficient Ti-based nanotubes and nanoribbons by conventional and microwave assisted synthesis strategies”. Ribbens S, Meynen V, Van Tendeloo G, Ke X, Mertens M, Maes BUW, Cool P, Vansant EF, Microporous and mesoporous materials: zeolites, clays, carbons and related materials 114, 401 (2008). http://doi.org/10.1016/j.micromeso.2008.01.028
Abstract: Titanate nanotubes were prepared via a hydrothermal treatment of TiO2 powders (Riedel De Haen) in a basic solution. Morphology and structure of the prepared samples were characterized by high resolution transmission electron microscopy (HRTEM), selected area electron diffraction (SAED), XRD, FT-Raman spectroscopy, nitrogen sorption and DSC. The photocatalytic activity was evaluated by photocatalytic oxidation of rhodamine 6G. Trititanate nanotubes (TTNT) with inner pore diameters between 4 and 4.2 nm and surface areas up till 360 m(2)/g could be synthesized. The synthesis route was modified by introduction of a calcination step, by applying a lower hydrothermal temperature and microwave irradiation in order to increase the photocatalytic activity of the porous photoactive nanotubular materials. Calcination and a softer hydrothermal treatment led to the formation of anatase without affecting the surface area and nanotubular shape of the samples. In this way, the photocatalytic activity of the original trititanate nanotubes could be significantly increased. By making use of microwave assisted synthesis, the photocatalytic activity call also be increased due to the presence of anatase. However, by applying microwave synthesis, a different structure was obtained, nanoribbons (NR) instead of nanotubcs, resulting in a decrease in surface area and porosity.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA); Organic synthesis (ORSY)
Impact Factor: 3.615
Times cited: 47
DOI: 10.1016/j.micromeso.2008.01.028
|
“Artificial construction of the layered Ruddlesden-Popper manganite La2Sr2Mn3O10 by reflection high energy electron diffraction monitored pulsed laser deposition”. Palgrave RG, Borisov P, Dyer MS, McMitchell SRC, Darling GR, Claridge JB, Batuk M, Tan H, Tian H, Verbeeck J, Hadermann J, Rosseinsky MJ;, Journal of the American Chemical Society 134, 7700 (2012). http://doi.org/10.1021/ja211138x
Abstract: Pulsed laser deposition has been used to artificially construct the n = 3 Ruddlesden Popper structure La2Sr2Mn3O10 in epitaxial thin film form by sequentially layering La1-xSrxMnO3 and SrO unit cells aided by in situ reflection high energy electron diffraction monitoring. The interval deposition technique was used to promote two-dimensional SrO growth. X-ray diffraction and cross-sectional transmission electron microscopy indicated that the trilayer structure had been formed. A site ordering was found to differ from that expected thermodynamically, with the smaller Sr2+ predominantly on the R site due to kinetic trapping of the deposited cation sequence. A dependence of the out-of-plane lattice parameter on growth pressure was interpreted as changing the oxygen content of the films. Magnetic and transport measurements on fully oxygenated films indicated a frustrated magnetic ground state characterized as a spin glass-like magnetic phase with the glass temperature T-g approximate to 34 K. The magnetic frustration has a clear in-plane (ab) magnetic anisotropy, which is maintained up to temperatures of 150 K. Density functional theory calculations suggest competing antiferromagnetic and ferromagnetic long-range orders, which are proposed as the origin of the low-temperature glassy state.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 13.858
Times cited: 27
DOI: 10.1021/ja211138x
|
“Au@MOF-5 and Au/Mox@MOF-5 (M = Zn, Ti, x = 1, 2) : preparation and microstructural characterisation”. Müller M, Turner S, Lebedev OI, Wang Y, Van Tendeloo G, Fischer RA, European journal of inorganic chemistry , 1876 (2011). http://doi.org/10.1002/ejic.201001297
Abstract: The Zn-carboxylate-based porous coordination polymer MOF-5 [Zn4O(bdc)3] and the metal oxide loaded materials ZnO@MOF-5 and TiO2@MOF-5 were loaded in a second step with the precursor [ClAuCO] to yield intermediate materials denoted as [ClAuCO]@MOF-5, [ClAuCO]/ZnO@MOF-5 and [ClAuCO]/TiO2@MOF-5. These composites were decomposed to Au@MOF-5, Au/ZnO@MOF-5 and Au/TiO2@MOF-5 under hydrogen at 100 °C. The nanoparticle-loaded hybrid materials were characterised by powder X-ray diffraction (PXRD), IR spectroscopy, X-ray photoelectron spectroscopy (XPS) and N2 sorption measurements, which reveal an intact MOF-5 structure that maintains a high specific surface area. For Au@MOF-5, crystalline Au nanoparticles were distributed over the MOF matrix in a homogeneous fashion with a size of ca. 13 nm, evidenced by high resolution transmission electron microscopy. In the case of Au/ZnO@MOF-5, the Au and metal oxide particles of a few nm in size were coexistent in a given volume of the MOF-5 matrix and were not separated in different crystalline MOF particles. For the TiO2 loaded materials the oxide is preferentially located near the outer surface of the MOF particles, leading to an increase of larger exterior Au particles in comparison to very small interior Au particles as observed for the other materials. Au@MOF-5, Au/ZnO@MOF-5 and Au/TiO2@MOF-5 were tested in liquid-phase oxidation of alcohols. Preliminary results show a high activity for the Au loaded materials in this reaction. This observation is attributed to the microstructure of the composites with very small Au particles distributed homogeneously over the MOF matrix.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.444
Times cited: 75
DOI: 10.1002/ejic.201001297
|
“Exit wave reconstruction from focal series of HRTEM images, single crystal XRD and total energy studies on SbxWO3+y (x\sim0.11)”. Klingstedt M, Sundberg M, Eriksson L, Haigh S, Kirkland A, Grüner D, de Backer A, Van Aert S, Tarasaki O, Zeitschrift für Kristallographie 227, 341 (2012). http://doi.org/10.1524/zkri.2012.1517
Abstract: A new tungsten bronze in the SbWO system has been prepared in a solid state reaction from Sb2O3, WO3 and W metal powder. The average structure was determined by single crystal X-ray diffraction. SbxWO3+y (x ∼ 0.11) crystallizes in the orthorhombic space group Pm21n (no. 31), a = 27.8135(9) Å, b = 7.3659(2) Å and c = 3.8672(1) Å. The structure belongs to the (n)-ITB class of intergrowth tungsten bronzes. It contains slabs of hexagonal channels formed by six WO6 octahedra. These slabs are separated by three layers of WO6 octahedra that are arranged in a WO3-type fashion. The WO6 octahedra share all vertices to build up a three-dimensional framework. The hexagonal channels are filled with Sb atoms to ∼80% and additional O atoms. The atoms are shifted out of the center of the channels. Exit-wave reconstruction of focal series of high resolution-transmission-electron-microscope (HRTEM) images combined with statistical paramäeter estimation techniques allowed to study local ordering in the channels. Sb atoms in neighbouring channels tend to be displaced in the same direction, which is in agreement with total energy calculations on ordered structure models, but the ratio of the occupation of the two possible Sb sites varies from channel to channel. The structure of SbxWO3+y exhibits pronounced local modulations.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.179
Times cited: 4
DOI: 10.1524/zkri.2012.1517
|
“Influence of the microstructure on the high-temperature transport properties of GdBaCo2O5.5+\delta epitaxial films”. Burriel M, Casa-Cabanas M, Zapata J, Tan H, Verbeeck J, Solis C, Roqueta J, Skinner SJ, Kilner JA, Van Tendeloo G, Santiso J, Chemistry of materials 22, 5512 (2010). http://doi.org/10.1021/cm101423z
Abstract: Epitaxial thin films of GdBaCo2O5.5+δ (GBCO) grown by pulsed laser deposition have been studied as a function of deposition conditions. The variation in film structure, domain orientation, and microstructure upon deviations in the cation composition have been correlated with the charge transport properties of the films. The epitaxial GBCO films mainly consist of single- and double-perovskite regions that are oriented in different directions depending on the deposition temperature. Additionally, cobalt depletion induces the formation of a high density of stacking defects in the films, consisting of supplementary GdO planes along the c-axis of the material. The presence of such defects progressively reduces the electrical conductivity. The films closer to the stoichiometric composition have shown p-type electronic conductivity at high pO2 with values as high as 800 S/cm at 330 °C in 1 atm O2, and with a pO2 power dependence with an exponent as low as 1/25, consistent with the behavior reported for bulk GBCO. These values place GBCO thin films as a very promising material to be applied as cathodes in intermediate temperature solid oxide fuel cells.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 17
DOI: 10.1021/cm101423z
|
“Quantitative atomic resolution mapping using high-angle annular dark field scanning transmission electron microscopy”. Van Aert S, Verbeeck J, Erni R, Bals S, Luysberg M, van Dyck D, Van Tendeloo G, Ultramicroscopy 109, 1236 (2009). http://doi.org/10.1016/j.ultramic.2009.05.010
Abstract: A model-based method is proposed to relatively quantify the chemical composition of atomic columns using high angle annular dark field (HAADF) scanning transmission electron microscopy (STEM) images. The method is based on a quantification of the total intensity of the scattered electrons for the individual atomic columns using statistical parameter estimation theory. In order to apply this theory, a model is required describing the image contrast of the HAADF STEM images. Therefore, a simple, effective incoherent model has been assumed which takes the probe intensity profile into account. The scattered intensities can then be estimated by fitting this model to an experimental HAADF STEM image. These estimates are used as a performance measure to distinguish between different atomic column types and to identify the nature of unknown columns with good accuracy and precision using statistical hypothesis testing. The reliability of the method is supported by means of simulated HAADF STEM images as well as a combination of experimental images and electron energy-loss spectra. It is experimentally shown that statistically meaningful information on the composition of individual columns can be obtained even if the difference in averaged atomic number Z is only 3. Using this method, quantitative mapping at atomic resolution using HAADF STEM images only has become possible without the need of simultaneously recorded electron energy loss spectra.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 2.843
Times cited: 166
DOI: 10.1016/j.ultramic.2009.05.010
|
“Thermally induced structural and morphological changes of CdSe/CdS octapods”. Goris B, van Huis MA, Bals S, Zandbergen HW, Manna L, Van Tendeloo G, Small 8, 937 (2012). http://doi.org/10.1002/smll.201101897
Abstract: Branched nanostructures are of great interest because of their promising optical and electronic properties. For successful and reliable integration in applications such as photovoltaic devices, the thermal stability of the nanostructures is of major importance. Here the different domains (CdSe cores, CdS pods) of the heterogeneous octapods are shown to have different thermal stabilities, and heating is shown to induce specific shape changes. The octapods are heated from room temperature to 700 °C, and investigated using (analytical and tomographic) transmission electron microscopy (TEM). At low annealing temperatures, pure Cd segregates in droplets at the outside of the octapods, indicating non-stochiometric composition of the octapods. Furthermore, the tips of the pods lose their faceting and become rounded. Further heating to temperatures just below the sublimation temperature induces growth of the zinc blende core at the expense of the wurtzite pods. At higher temperatures, (500700 °C), sublimation of the octapods is observed in real time in the TEM. Three-dimensional tomographic reconstructions reveal that the four pods pointing into the vacuum have a lower thermal stability than the four pods that are in contact with the support.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 8.643
Times cited: 20
DOI: 10.1002/smll.201101897
|
“An efficient way of including thermal diffuse scattering in simulation of scanning transmission electron microscopic images”. Croitoru MD, van Dyck D, Van Aert S, Bals S, Verbeeck J, Ultramicroscopy 106, 933 (2006). http://doi.org/10.1016/j.ultramic.2006.04.006
Abstract: We propose an improved image simulation procedure for atomic-resolution annular dark-field scanning transmission electron microscopy (STEM) based on the multislice formulation, which takes thermal diffuse scattering fully into account. The improvement with regard to the classical frozen phonon approach is realized by separating the lattice configuration statistics from the dynamical scattering so as to avoid repetitive calculations. As an example, the influence of phonon scattering on the image contrast is calculated and investigated. STEM image simulation of crystals can be applied with reasonable computing times to problems involving a large number of atoms and thick or large supercells.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Condensed Matter Theory (CMT); Vision lab
Impact Factor: 2.843
Times cited: 18
DOI: 10.1016/j.ultramic.2006.04.006
|
“Refinement of the 200 structure factor for GaAs using parallel and convergent beam electron nanodiffraction data”. Müller K, Schowalter M, Jansen J, Tsuda K, Titantah J, Lamoen D, Rosenauer A, Ultramicroscopy 109, 802 (2009). http://doi.org/10.1016/j.ultramic.2009.03.029
Abstract: We present a new method to measure structure factors from electron spot diffraction patterns recorded under almost parallel illumination in transmission electron microscopes. Bloch wave refinement routines have been developed to refine the crystal thickness, its orientation and structure factors by comparison of experimentally recorded and calculated intensities. Our method requires a modicum of computational effort, making it suitable for contemporary personal computers. Frozen lattice and Bloch wave simulations of GaAs diffraction patterns are used to derive optimised experimental conditions. Systematic errors are estimated from the application of the method to simulated diffraction patterns and rules for the recognition of physically reasonable initial refinement conditions are derived. The method is applied to the measurement of the 200 structure factor for GaAs. We found that the influence of inelastically scattered electrons is negligible. Additionally, we measured the 200 structure factor from zero loss filtered two-dimensional convergent beam electron diffraction patterns. The precision of both methods is found to be comparable and the results agree well with each other. A deviation of more than 20% from isolated atom scattering data is observed, whereas close agreement is found with structure factors obtained from density functional theory [A. Rosenauer, M. Schowalter, F. Glas, D. Lamoen, Phys. Rev. B 72 (2005), 085326-1], which account for the redistribution of electrons due to chemical bonding via modified atomic scattering amplitudes.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.843
Times cited: 8
DOI: 10.1016/j.ultramic.2009.03.029
|
“Formation of a Ti-siliceous trimodal material with macroholes, mesopores and zeolitic features via a one-pot templating synthesis”. Vernimmen J, Meynen V, Mertens M, Lebedev OI, Van Tendeloo G, Cool P, Journal of porous materials 19, 153 (2012). http://doi.org/10.1007/s10934-011-9470-0
Abstract: Based on a facile one-pot templating synthesis, using a TS-1 zeolite recipe whereby part of the zeolite structure directing agent is replaced by a mesopore templating agent, a trimodal material is formed. The resulting meso-TSM material combines mesoporosity (Ti-MCM-41) with zeolitic features (TS-1) and a unique sheet-like morphology with uniform macroporous voids (macroholes). Moreover, the macrohole formation, mesoporosity and zeolitic properties of the meso-TSM material can be controlled in a straightforward way by adjusting the length of the hydrothermal treatment. This newly developed material may imply great potential for catalytic redox applications and diffusion limitated processes because of its highly tunable character in all three dimensions (micro-, meso- and macroporous scale).
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 1.624
Times cited: 2
DOI: 10.1007/s10934-011-9470-0
|
“The merging of silica-surfactant microspheres under hydrothermal conditions”. Liu S, Lebedev OI, Mertens M, Meynen V, Cool P, Van Tendeloo G, Vansant EF, Microporous and mesoporous materials: zeolites, clays, carbons and related materials 116, 141 (2008). http://doi.org/10.1016/j.micromeso.2008.03.034
Abstract: Post-synthesis hydrothermal treatments have been used to improve the quality of MCM-41 materials. In our latest work, merging of surfactant-containing silica microspheres during the hydrothermal treatments was observed. Mechanistic insights and the different stages that are involved in the merging process can be summarized as follows. First, the surfaces of the starting microspheres open up due to the dissolution of silica. Then the dissolved silica species provide mass source for the formation of particle necks connecting two neighboring microspheres. Gradually, surfaces of the starting microspheres are flattened to meet the needs of further growth of the necks. Finally, some chain-like highly-ordered mesoporous structures up to several micrometers are formed. The observed merging of the surfactant-containing microspheres is a re-assembling process, which is under the control of electrostatic force between the dissolved silica species and the surfactant cations. The occluded surfactant cations in the precursor spheres play important roles in the merging process.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 3.615
Times cited: 5
DOI: 10.1016/j.micromeso.2008.03.034
|
“Smart heating profiles for the synthesis of benzene bridged periodic mesoporous organosilicas”. Smeulders G, van Oers C, Van Havenbergh K, Houthoofd K, Mertens M, Martens JA, Bals S, Maes BUW, Meynen V, Cool P, Chemical engineering journal 175, 585 (2011). http://doi.org/10.1016/j.cej.2011.09.116
Abstract: In this study the effects of the heating rate and heating time on the formation of crystal-like benzene bridged periodic mesoporous organosilicas (PMOs) are investigated. The time needed to heat up an autoclave during the hydrothermal treatment has shown to be crucial in the synthesis of PMOs, while the total duration of heating gave rise to only minor differences. By choosing a smart heating profile, superior PMO materials can be obtained in a short time. Different heating profiles in a range from one minute to one hour are adopted by microwave equipment and compared with conventional heating methods. The heating rate has a large influence on the porosity characteristics and the uniformity of the obtained particles. Moreover, two new alternative synthetic strategies to adopt the smart heating profile are presented, in order to give some possible solutions for the expensive microwave equipment.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA); Organic synthesis (ORSY)
Impact Factor: 6.216
Times cited: 7
DOI: 10.1016/j.cej.2011.09.116
|