“Stable Rh particles in hydrotalcite-derived catalysts coated on FeCrAlloy foams by electrosynthesis”. Benito P, Nuyts G, Monti M, de Nolf W, Fornasari G, Janssens K, Scavetta E, Vaccari A, Applied catalysis : B : environmental 179, 321 (2015). http://doi.org/10.1016/J.APCATB.2015.05.035
Abstract: Rh-based structured catalysts for the Catalytic Partial Oxidation of CH4 to syngas were prepared by electrosynthesis of Rh/Mg/Al hydrotalcite-type compounds on FeCrAlloy foams and calcination. The effects of Rh content, total metal concentration, and partial replacement of Mg2+ by Ni2+ in the electrolytic solution on coating thickness, Rh speciation, metallic particle size, and catalytic activity were investigated by SEM/EDS, mu-XRF/XANES and tests under diluted and concentrated reaction conditions. The amount of Rh species, present as Mg (RhxAl1-x)(2)O-4, depended on the thickness of the electrosynthesised layer as well as the Rh particle size and dispersion. Smaller and more dispersed particles were obtained by decreasing the Rh concentration in the electrolytic solution from Rh/Mg/Al=11/70/19 to 5/70/25 and 2/70/28 atomic ratio% (a.r.%) and in thinner rather than thicker layers. Despite the improvement in metallic particles features, the CH4 conversion was negatively affected by the low amount of active sites in the coating, the high metal support interaction and possibly the oxidation of metallic particles and carbon formation. A larger amount of solid containing well dispersed Rh particles was deposited by increasing the total metal concentration from 0.03 M to 0.06 M with the Rh/Mg/Al=5/70/25 a.r.%, and the catalytic performances were enhanced. The partial replacement of Mg2+ by Ni2+ gave rise to a very active bimetallic Rh/Ni catalyst, CH4 conversion and selectivity to syngas were above 90%, however, it slightly deactivated with time-on-stream. (C) 2015 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 9.446
Times cited: 14
DOI: 10.1016/J.APCATB.2015.05.035
|
|
|
“Combined use of synchrotron-radiation-based imaging techniques for the characterization of structured catalysts”. Basile F, Benito P, Bugani S, de Nolf W, Fornasari G, Janssens K, Morselli L, Scavetta E, Tonelli D, Vaccari A, Advanced functional materials 20, 4117 (2010). http://doi.org/10.1002/ADFM.201001004
Abstract: Active-phase-coated metallic supports as structured catalysts are gaining attention in endothermic and exothermic processes because they improve heat transfer. The deposition of a well-adhered and stable catalyst layer on the metallic support constitutes an important feature for the successful application of the final material. In this work, coating of FeCrAlY foams is performed by a one-step electrosynthesis-deposition of hydrotalcite-type compounds, precursors of catalysts active in endothermic steam methane reforming. The catalysts are studied at different length scales by using, for the first time, a combination of several techniques: SEM/EDS and X-ray fluorescence, X-ray powder diffraction and absorption-tomography experiments on the micro- and nanoscales at a synchrotron facility. The results show that the morphology of the coating depends on the synthesis conditions and that the catalyst may be described as Ni metal crystallites dispersed on γ-Al2O3, homogeneously coating the FeCrAlY foam.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 12.124
Times cited: 24
DOI: 10.1002/ADFM.201001004
|
|
|
“The use of microscopic X-ray diffraction for the study of HgS and its degradation products corderoite (\alpha-Hg3S2Cl2), kenhsuite (\gamma-Hg3S2Cl2) and calomel (Hg2Cl2) in historical paintings”. Radepont M, de Nolf W, Janssens K, van der Snickt G, Coquinot Y, Klaassen L, Cotte M, Journal of analytical atomic spectrometry 26, 959 (2011). http://doi.org/10.1039/C0JA00260G
Abstract: Since antiquity, the red pigment mercury sulfide (α-HgS), called cinnabar in its natural form or vermilion red when synthetic, was very often used in frescoes and paintings, even if it was known to suffer occasionally from degradation. The paint hereby acquires a black or silver-grey aspect. The chemical characterization of these alteration products is rather challenging mainly because of the micrometric size and heterogeneity of the surface layers that develop and that are responsible for the color change. Methods such as electron microscopy, synchrotron-based microscopic X-ray fluorescence, microscopic X-ray absorption near edge spectroscopy, Raman microscopy and secondary ion microscopy have been previously employed to identify the (Hg- and S-) compounds present and to study their co-localization. Next to these, also microscopic X-ray diffraction (XRD) (either by making use of laboratory X-ray sources or when used at a synchrotron facility) allows the identification of the crystal phases that are present in degraded HgS paint layers. In this paper we employ these various forms of micro-XRD to analyze degraded red paint in different paintings and compare the results with other X-ray based methods. Whereas the elemental analyses of the degradation products revealed, next to mercury and sulfur, the presence of chlorine, X-ray diffraction allowed the identification, next to α-HgS, of the Hg and S-containing compound calomel (Hg2Cl2) but also of the Hg, S and Cl-containing minerals corderoite (α-Hg3S2Cl2) and kenhsuite (γ-Hg3S2Cl2). These observations are consistent with X-ray absorption spectroscopy measurements performed at the S- and Cl-edges.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 3.379
Times cited: 40
DOI: 10.1039/C0JA00260G
|
|
|
“Thermodynamic and experimental study of the degradation of the red pigment mercury sulfide”. Radepont M, Coquinot Y, Janssens K, Ezrati J-J, de Nolf W, Cotte M, Journal of analytical atomic spectrometry 30, 599 (2015). http://doi.org/10.1039/C4JA00372A
Abstract: The red pigment mercury sulfide, called cinnabar or vermilion, is well known to suffer from an alteration giving rise to a grey, grey-white or black color at the surface of degraded works of art. This phenomenon can dramatically affect the esthetical value of artworks. This work aims at assessing the factors (light, halides) influencing the instability of red mercury sulfide and understanding (by combining thermodynamic and experimental approaches) the chemical equilibria governing the formation and evolution of the different degradation compounds. From the thermodynamic study of the Hg-S-Cl-H2O system, it was concluded that Hg(0), Hg3S2Cl2, and Hg2Cl2 can be formed from the reaction of alpha-HgS with ClO(g). In the second part, the artificial ageing experiments presented were carried out on model samples following the conditions assessed in the first part, in order to reproduce natural ageing observed on red mercury sulfide. Similarly to degradation compounds detected on original works of art, mercury chlorine compounds such as calomel (Hg2Cl2) and corderoite (alpha-Hg3S2Cl2) were identified on the surface of alpha-HgS model samples, when exposed to light and a sodium hypochlorite solution. Sulfates were detected as well, and more particularly gypsum (CaSO4 center dot 2H(2)O) when Ca was originally present in the model sample. The relationship between color and composition is discussed as well.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 3.379
Times cited: 26
DOI: 10.1039/C4JA00372A
|
|
|
“Macroscopic X-ray powder diffraction scanning : possibilities for quantitative and depth-selective parchment analysis”. Vanmeert F, de Nolf W, Dik J, Janssens K, Analytical chemistry 90, 6445 (2018). http://doi.org/10.1021/ACS.ANALCHEM.8B00241
Abstract: At or below the surface of painted works of art, valuable information is present that provides insights into an objects past, such as the artists technique and the creative process that was followed or its conservation history but also on its current state of preservation. Various noninvasive techniques have been developed over the past 2 decades that can probe this information either locally (via point analysis) or on a macroscopic scale (e.g., full-field imaging and raster scanning). Recently macroscopic X-ray powder diffraction (MA-XRPD) mapping using laboratory X-ray sources was developed. This method can visualize highly specific chemical distributions at the macroscale (dm(2)). In this work we demonstrate the synergy between the quantitative aspects of powder diffraction and the noninvasive scanning capability of MA-XRPD highlighting the potential of the method to reveal new types of information. Quantitative data derived from a 15th/16th century illuminated sheet of parchment revealed three lead white pigments with different hydrocerussite-cerussite compositions in specific pictorial elements, while quantification analysis of impurities in the blue azurite pigment revealed two distinct azurite types: one rich in barite and one in quartz. Furthermore, on the same artifact, the depth-selective possibilities of the method that stem from an exploitation of the shift of the measured diffraction peaks with respect to reference data are highlighted. The influence of different experimental parameters on the depth-selective analysis results is briefly discussed. Promising stratigraphic information could be obtained, even though the analysis is hampered by not completely understood variations in the unit cell dimensions of the crystalline pigment phases.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 6.32
Times cited: 6
DOI: 10.1021/ACS.ANALCHEM.8B00241
|
|
|
“Macroscopic X-ray powder diffraction scanning, a new method for highly selective chemical imaging of works of art : instrument optimization”. Vanmeert F, de Nolf W, De Meyer S, Dik J, Janssens K, Analytical chemistry 90, 6436 (2018). http://doi.org/10.1021/ACS.ANALCHEM.8B00240
Abstract: In the past decade macroscopic X-ray fluorescence imaging (MA-XRF) has become established as a method for the noninvasive investigation of flat painted surfaces, yielding large scale elemental maps. MA-XRF is limited by a lack of specificity, only allowing for indirect pigment identification based on the simultaneous presence of chemical elements. The high specificity of X-ray powder diffraction (XRPD) mapping is already being exploited at synchrotron facilities for investigations at the (sub)microscopic scale, but the technique has not yet been employed using lab sources. In this paper we present the development of a novel MA-XRPD/XRF instrument based on a laboratory X-ray source. Several combinations of X-ray sources and area detectors are evaluated in terms of their spatial and angular resolution and their sensitivity. The highly specific imaging capability of the combined MA-XRPD/XRF instrument is demonstrated on a 15th/16th century illuminated manuscript directly revealing the distribution of a large number of inorganic pigments, including the uncommon yellow pigment massicot (o-PbO). The case study illustrates the wealth of new mapping information that can be obtained in a noninvasive manner using the laboratory MA-XRPD/XRF instrument.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 6.32
Times cited: 11
DOI: 10.1021/ACS.ANALCHEM.8B00240
|
|
|
“Role of coating-metallic support interaction in the properties of electrosynthesized Rh-based structured catalysts”. Benito P, de Nolf W, Nuyts G, Janssens K, et al, ACS catalysis 4, 3779 (2014). http://doi.org/10.1021/CS501079K
Abstract: Rh-structured catalysts for the catalytic partial oxidation of CH4 to syngas were prepared by electrosynthesis of Rh-containing hydrotalcite-type (HT) compounds on FeCrAlloy foams followed by calcination at 900 degrees C. During the calcination the simultaneous decomposition of the layered HT structure and formation of the protective FeCrAlloy outer shell in alumina occurred. Here, we studied the role of the coating-metallic support interaction in the properties of the catalysts after calcination, H-2 reduction, and catalytic tests, by a combination of electron (FEG-SEM/EDS) and synchrotron X-ray (XRF/XRPD and XRF/XANES) microscopic techniques. The characterization of crystalline phases in the metallic support and coating and distribution of Rh active species was carried out on several samples prepared by modifying the Rh content in the electrolytic solution (Rh/Mg/Al = 11.0/70.0/19.0, 5.0/70.0/25.0, 0/70.0/30.0 atomic ratio). A sample was also prepared with no aluminum in the electrolytic solution (Rh/Mg/Al = 13.6/86.4/0.0 atomic ratio) and calcined at 550 and 900 degrees C. The interaction between the elements of the metallic support and the catalytic coating increased the film adhesion during the thermal treatment and catalytic tests and modified the catalyst crystalline phases. A chemical reaction between Al corning from the foam and Mg in the coating occurred during calcination at high temperature leading to the formation of spinel phases in which rhodium is solved, together with some Rh2O3 and Rh. The metallic support was oxidized forming the corundum scale and chromium oxides, moreover t-Al2O3 was identified. For the Rh11.0Mg70.0Al19.0 catalyst the inclusion of Rh in the spinel phase decreased its reducibility in the H-2 pretreatment. The reduction continued during catalytic tests by feeding diluted CH4/O-2/He gas mixtures, evidenced by the catalyst activation. While under concentrated gas mixtures the deactivation occurred, probably by oxidation.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 10.614
Times cited: 13
DOI: 10.1021/CS501079K
|
|
|
“XRDUA : crystalline phase distribution maps by two-dimensional scanning and tomographic (micro) X-ray powder diffraction”. de Nolf W, Vanmeert F, Janssens K, Journal of applied crystallography 47, 1107 (2014). http://doi.org/10.1107/S1600576714008218
Abstract: Imaging of crystalline phase distributions in heterogeneous materials, either plane projected or in virtual cross sections of the object under investigation, can be achieved by scanning X-ray powder diffraction employing X-ray micro beams and X-ray-sensitive area detectors. Software exists to convert the two-dimensional powder diffraction patterns that are recorded by these detectors to one-dimensional diffractograms, which may be analysed by the broad variety of powder diffraction software developed by the crystallography community. However, employing these tools for the construction of crystalline phase distribution maps proves to be very difficult, especially when employing micro-focused X-ray beams, as most diffraction software tools have mainly been developed having structure solution in mind and are not suitable for phase imaging purposes. XRDUA has been developed to facilitate the execution of the complete sequence of data reduction and interpretation steps required to convert large sequences of powder diffraction patterns into a limited set of crystalline phase maps in an integrated fashion.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Times cited: 62
DOI: 10.1107/S1600576714008218
|
|
|
“Improvement in the coating homogeneity in electrosynthesized Rh structured catalysts for the partial oxidation of methane”. Benito P, Monti M, de Nolf W, Nuyts G, Janssens K, et al, Catalysis today 246, 154 (2015). http://doi.org/10.1016/J.CATTOD.2014.10.003
Abstract: The precipitation of Rh/Mg/Al and Rh/Al hydroxides on the surface of FeCrAlloy foams by a base electrogeneration method was investigated to improve the properties of the deposited film (homogeneity and composition) and therefore the performances of the structured catalysts, obtained by calcination, in the Catalytic Partial Oxidation of CH4 to syngas. The work focussed on decreasing current gradients within open-cell foam cylinders by increasing the number of electrical contacts from 1 to 3 points to promote a more homogeneous precipitation of the hydroxides. Electrochemical and catalytic tests as well as SEM/EDS and mu-XRFIXRD analyses allowed to correlate the effect of the number of electrical contact points with materials properties. Lastly, syntheses were performed on Pt plates to study the effect of the electrical behaviour and shape of the support on the composition of the film. A more homogeneous coating of the foam surface was achieved by adopting a configuration with 3 contact points since the reduction of nitrates and water molecules that generates the basic media in the vicinity of the support was enhanced. Layer thicknesses up to 5-15 mu m were deposited; however, the sequential precipitation of a film with composition closer to the expected one and a layer enriched in Al and Rh (outer layer) was not avoided. The improvement in the coating gave rise to enhanced performances for a sample prepared at -1.1 V for 3000 s. Contrarily, the low adherence of the outer layer in a sample prepared at -1.2 V for 2000 s during both calcination and catalytic tests may be responsible of the unexpected decrease in catalytic performances. The same sequential precipitation was observed by performing the syntheses on Pt plates, showing that the electrical nature the support did not play a key role on this phenomenon. (C) 2014 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 4.636
Times cited: 14
DOI: 10.1016/J.CATTOD.2014.10.003
|
|
|
“Optimization of mobile scanning macro-XRF systems for the in situ investigation of historical paintings”. Alfeld M, Janssens K, Dik J, de Nolf W, van der Snickt G, Journal of analytical atomic spectrometry 26, 899 (2011). http://doi.org/10.1039/C0JA00257G
Abstract: Elemental distribution maps are of great interest in the study of historical paintings, as they allow to investigate the pigment use of the artist, to image changes made in the painting during or after its creation and in some cases to reveal discarded paintings that were later over painted. Yet a method that allows to record such maps of a broad range of elements in a fast, non-destructive and in situ manner is not yet commonly available; a dedicated mobile scanning XRF instrument might fill this gap. In this paper we present three self-built scanning macro-XRF instruments, each based on the experience gained with its precursor. These instruments are compared in terms of sensitivity and limits of detection, which includes a discussion of the use of polycapillary optics and pinhole collimators as beam defining devices. Furthermore, the imaging capabilities of the instruments are demonstrated in three exemplary cases: (parts of) historical paintings from the 15th to the 19th century are examined. These cases illustrate the value of element specific distribution maps in the study of historical paintings and allow in the case of Vincent van Gogh's Patch of Grass a direct comparison between in situ and synchrotron based scanning macro-XRF.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 3.379
Times cited: 107
DOI: 10.1039/C0JA00257G
|
|
|
“Role of the relative humidity and the Cd/Zn stoichiometry in the photooxidation process of cadmium yellows (CdS/Cd1-xZnxS) in oil paintings”. Monico L, Chieli A, De Meyer S, Cotte M, de Nolf W, Falkenberg G, Janssens K, Romani A, Miliani C, Chemistry: a European journal 24, 11584 (2018). http://doi.org/10.1002/CHEM.201801503
Abstract: Cadmium yellows (CdYs) refer to a family of cadmium sulfide pigments, which have been widely used by artists since the late 19th century. Despite being considered stable, they are suffering from discoloration in iconic paintings, such as Joy of Life by Matisse, Flowers in a blue vase by Van Gogh, and The Scream by Munch, most likely due to the formation of CdSO4 center dot nH(2)O. The driving factors of the CdYs degradation and how these affect the overall process are still unknown. Here, we study a series of oil mock-up paints made of CdYs of different stoichiometry (CdS/Cd0.76Zn0.24S) and crystalline structure (hexagonal/ cubic) before and after aging at variable relative humidity under exposure to light and in darkness. Synchrotron radiation-based X-ray methods combined with UV-Vis and FTIR spectroscopy show that: 1) Cd0.76Zn0.24S is more susceptible to photooxidation than CdS; both compounds can act as photocatalysts for the oil oxidation. 2) The photooxidation of CdS/Cd0.76Zn0.24S to CdSO4 center dot nH(2)O is triggered by moisture. 3) The nature of alteration products depends on the aging conditions and the Cd/Zn stoichiometry. Based on our findings, we propose a scheme for the mechanism of the photocorrosion process and the photocatalytic activity of CdY pigments in the oil binder. Overall, our results form a reliable basis for understanding the degradation of CdS-based paints in artworks and contribute towards developing better ways of preserving them for future generations.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 5.317
Times cited: 5
DOI: 10.1002/CHEM.201801503
|
|
|
“Disclosing the binding medium effects and the pigment solubility in the (photo)reduction process of chrome yellows (PbCrO4/PbCr1-xSxO4)”. Monico L, Sorace L, Cotte M, de Nolf W, Janssens K, Romani A, Miliani C, ACS Omega 4, 6607 (2019). http://doi.org/10.1021/ACSOMEGA.8B03669
Abstract: The darkening due to chemical alteration of chrome yellows (PbCrO4/PbCr1-xSxO4) is a phenomenon threatening a large number of 19th-20th century paintings, including the Amsterdam Sunflowers by Vincent van Gogh. Our earlier studies have proven that the alteration is due to a Cr(VI) -> Cr(III) reduction with Cr(V)-species that are formed as long-lived intermediates and that bCr(1-x)S(x)O(4) (0 < x <= 0.8) types undergo reduction more readily than monoclinic, S-free, PbCrO4. In this context, there is still lack of knowledge about the effects of the chemical properties of the binding medium (i.e., chemical composition and drying process) and the solubility of chrome yellows on the overall reduction pathways. Here, we study a series of naturally and photochemically aged mock-up paints prepared by mixing chrome yellow powders (PbCrO4/PbCr0.2S0.8O4) with either linseed oil or a water-based acrylic emulsion as the binding medium. Equivalent paints made up of the highly soluble K2CrO4 were also investigated and used as benchmarks to provide a more in-depth understanding of the influence of the solubility on the chromate reduction pathways in the two different binders. A combination of synchrotron radiation-based Cr K-edge X-ray absorption near edge structure (XANES), electron paramagnetic resonance (EPR), and UV-Visible spectroscopy measurements shows that: (1) the Cr(VI) reduction results from the interaction between the pigment and the binder; (2) the process is more significant in oil, giving rise to Cr(V)- and Cr(III)-species as well as oxidized organic compounds; (3) the lightfastness of the chrome yellow pigment is enhanced in the acrylic binder; and (4) the tendency toward chromium reduction increases with increasing solubility of the pigment. Based on our findings, we propose a scheme for the mechanism of the (photo)reduction process of chrome yellows in the oil and acrylic binder. Overall, our results provide new insights into the factors driving the degradation of lead chromate-based paints in artworks and contribute to the development of strategies for preserving them over time.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Times cited: 4
DOI: 10.1021/ACSOMEGA.8B03669
|
|
|
“Probing the chemistry of CdS paints in The Scream by in situ noninvasive spectroscopies and synchrotron radiation x-ray techniques”. Monico L, Cartechini L, Rosi F, Chieli A, Grazia C, De Meyer S, Nuyts G, Vanmeert F, Janssens K, Cotte M, De Nolf W, Falkenberg G, Sandu ICA, Tveit ES, Mass J, De Freitas RP, Romani A, Miliani C, Science Advances 6, eaay3514 (2020). http://doi.org/10.1126/SCIADV.AAY3514
Abstract: The degradation of cadmium sulfide (CdS)-based oil paints is a phenomenon potentially threatening the iconic painting The Scream (ca. 1910) by Edvard Munch (Munch Museum, Oslo) that is still poorly understood. Here, we provide evidence for the presence of cadmium sulfate and sulfites as alteration products of the original CdS-based paint and explore the external circumstances and internal factors causing this transformation. Macroscale in situ noninvasive spectroscopy studies of the painting in combination with synchrotron-radiation x-ray microspectroscopy investigations of a microsample and artificially aged mock-ups show that moisture and mobile chlorine compounds are key factors for promoting the oxidation of CdS, while light (photodegradation) plays a less important role. Furthermore, under exposure to humidity, parallel/secondary reactions involving dissolution, migration through the paint, and recrystallization of water-soluble phases of the paint are associated with the formation of cadmium sulfates.
Keywords: A1 Journal article; Engineering sciences. Technology; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 13.6
Times cited: 4
DOI: 10.1126/SCIADV.AAY3514
|
|
|
“Degradation process of lead chromate in paintings by Vincent van Gogh studied by means of synchrotron X-ray spectromicroscopy and related methods : 2 : original paint layer samples”. Monico L, van der Snickt G, Janssens K, de Nolf W, Miliani C, Dik J, Radepont M, Hendriks E, Geldof M, Cotte M, Analytical chemistry 83, 1224 (2011). http://doi.org/10.1021/AC1025122
Abstract: The darkening of the original yellow areas painted with the chrome yellow pigment (PbCrO4, PbCrO4·xPbSO4, or PbCrO4·xPbO) is a phenomenon widely observed on several paintings by Vincent van Gogh, such as the famous different versions of Sunflowers. During our previous investigations on artificially aged model samples of lead chromate, we established for the first time that darkening of chrome yellow is caused by reduction of PbCrO4 to Cr2O3·2H2O (viridian green), likely accompanied by the presence of another Cr(III) compound, such as either Cr2(SO4)3·H2O or (CH3CO2)7Cr3(OH)2 [chromium(III) acetate hydroxide]. In the second part of this work, in order to demonstrate that this reduction phenomenon effectively takes place in real paintings, we study original paint samples from two paintings of V. van Gogh. As with the model samples, in view of the thin superficial alteration layers that are present, high lateral resolution spectroscopic methods that make use of synchrotron radiation (SR), such as microscopic X-ray absorption near edge (μ-XANES) and X-ray fluorescence spectrometry (μ-XRF) were employed. Additionally, μ-Raman and mid-FTIR analyses were carried out to completely characterize the samples. On both paint microsamples, the local presence of reduced Cr was demonstrated by means of μ-XANES point measurements. The presence of Cr(III) was revealed in specific areas, in some cases correlated to the presence of Ba(sulfate) and/or to that of aluminum silicate compounds.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 6.32
Times cited: 84
DOI: 10.1021/AC1025122
|
|
|
“Combined use of synchrotron radiation based micro-X-ray fluorescence, micro-X-ray diffraction, micro-X-ray absorption near-edge, and micro-fourier transform infrared spectroscopies for revealing an alternative degradation pathway of the pigment cadmium yellow in a painting by Van Gogh”. van der Snickt G, Janssens K, Dik J, de Nolf W, Vanmeert F, Jaroszewicz J, Cotte M, Falkenberg G, Van der Loeff L, Analytical chemistry 84, 10221 (2012). http://doi.org/10.1021/AC3015627
Abstract: Over the past years a number of studies have described the instability of the pigment cadmium yellow (CdS). In a previous paper we have shown how cadmium sulfide on paintings by James Ensor oxidizes to CdSO4 center dot H2O. The degradation process gives rise to the fading of the bright yellow color and the formation of disfiguring white crystals that are present on the paint surface in approximately 50 mu m sized globular agglomerations. Here, we study cadmium yellow in the painting “Flowers in a blue vase” by Vincent van Gogh. This painting differs from the Ensor case in the fact that (a) a varnish was superimposed onto the degraded paint surface and (b) the CdS paint area is entirely covered with an opaque crust. The latter obscures the yellow color completely and thus presents a seemingly more advanced state of degradation. Analysis of a cross-sectioned and a crushed sample by combining scanning microscopic X-ray diffraction (mu-XRD), microscopic X-ray absorption near-edge spectroscopy (mu-XANES), microscopic X-ray fluorescence (mu-XRF) based chemical state mapping and scanning microscopic Fourier transform infrared (mu-FT-IR) spectrometry allowed unravelling the complex alteration pathway. Although no crystalline CdSO4 compounds were identified on the Van Gogh paint samples, we conclude that the observed degradation was initially caused by oxidation of the original CdS pigment, similar as for the previous Ensor case. However, due to the presence of an overlying varnish containing lead-based driers and oxalate ions, secondary reactions took place. In particular, it appears that upon the photoinduced oxidation of its sulfidic counterion, the Cd2+ ions reprecipitated at the paint/varnish interface after having formed a complex with oxalate ions that themselves are considered to be degradation products of the resin and/or oil in the varnish. The SO42- anions, for their part, found a suitable reaction partner in Pb2+ ions stemming from a dissolved lead-based siccative that was added to the varnish to promote its drying. The resulting opaque anglesite compound in the varnish, in combination with the underlying CdC2O4 layer at the paint/varnish interface, account for the orange-gray crust that is disfiguring the painting on a macroscopic level. In this way, the results presented in this paper demonstrate how, through a judicious combined use of several microanalytical methods with speciation capabilities, many new insights can be obtained from two minute, but highly complex and heterogeneous paint samples.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 6.32
Times cited: 59
DOI: 10.1021/AC3015627
|
|
|
“Room-temperature study of iron gall ink impregnated paper degradation under various oxygen and humidity conditions : time-dependent monitoring by viscosity and X-ray absorption near-edge spectrometry measurements”. Rouchon V, Duranton M, Burgaud C, Pellizzi E, Lavédrine B, Janssens K, de Nolf W, Nuyts G, Vanmeert F, Hellemans K, Analytical chemistry 83, 2589 (2011). http://doi.org/10.1021/AC1029242
Abstract: Many western manuscripts were written using iron gall inks. These inks can damage the paper via two major mechanisms: (a) acid hydrolysis, enhanced by humidity, and (b) oxidative depolymerization provoked by the presence of oxygen and free iron(II) ions. The degradation of unsized Whatman paper impregnated with different combinations of iron sulfate, gallic acid, and gum arabic was studied at room temperature in order to assess the relative importance of each mechanism. The samples were stored in various environments including a dry and/or an oxygen-free atmosphere. The cellulose depolymerization was monitored by viscometry and related to changes in the oxidation state of iron, determined by X-ray absorption near-edge spectrometry. The results indicate that residual amounts of oxygen (less than 0.1%) promote cellulose depolymerization, whereas the level of relative humidity has no impact. The cellulose depolymerization also appears closely correlated to oxidative mechanisms. Regarding the oxidation of iron, it only occurs in the simultaneous presence of oxygen and moisture, suggesting the occurrence of rustlike oxidative mechanisms. Finally, the presence of gallic acid has a strong influence, which is only partially explained by its capacity to reduce iron(III) to iron(II).
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 6.32
Times cited: 28
DOI: 10.1021/AC1029242
|
|
|
“Material analyses of “Christ with singing and music-making Angels”, a late 15th-C panel painting attributed to Hans Memling and assistants : part 1 : non-invasive in situ investigations”. van der Snickt G, Miliani C, Janssens K, Brunetti BG, Romani A, Rosi F, Walter P, Castaing J, de Nolf W, Klaassen L, Labarque I, Wittermann R, Journal of analytical atomic spectrometry 26, 2216 (2011). http://doi.org/10.1039/C1JA10073D
Abstract: In cultural heritage science, compositional data is traditionally obtained from works of art through the analysis of samples by means of various bench-top instruments (scanning electron microscope, Raman spectrometer, etc.). Alternatively, the object can be transported to a laboratory where it may be examined, usually by spectroscopic methods working in reflection mode. However, this paper describes how a complementary set of mobile and portable instruments was deployed in situ to gain a comprehensive view on the materials and related ageing compounds of an (almost) unmovable 15th-C polyptych, prior to and in preparation of the extraction of a limited number of samples. In line with the methodological approach discussed, PXRF was first employed as an efficient screening tool. The ensuing elemental data was supplemented by more specific information on both organic as inorganic materials supplied by reflection near- and mid-FTIR spectroscopy and fluorimetry. In completion, a limited number of diffraction patterns were collected with a mobile XRD instrument in order to identify the constituent crystalline phases in pigments, grounding materials and degradation products. In this way, it could be demonstrated how a rich array of colours was obtained by means of a limited palette of pigments: lead white, lead tin yellow, azurite, natural ultramarine, bone black, vermillion, madder lake, and a green copper-organo complex were detected and situated on the panels. Remarkably, next to chalk also gypsum was found in the ground layer(s) of this Western European easel painting. The relatively large surface of the background was covered with gold leaf; the analyses seem to point towards the labour-intensive water gilding technique. The versatility of this combination of analytical techniques was further illustrated by the accurate characterisation of degradation products affecting the readability and conservation of the painting: the overall presence of a calcium oxalate-based film of variable thickness was established. Nevertheless, further analysis of cross-sectioned samples was considered desirable in order to study the stratigraphy, to gain direct access to altered and sub-imposed layers and to allow highly detailed analysis of micrometric degradation products by state-of-the art techniques (i.e. synchrotron radiation).
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 3.379
Times cited: 32
DOI: 10.1039/C1JA10073D
|
|
|
“Revealing hidden paint layers in oil paintings by means of scanning macro-XRF : a mock-up study based on Rembrandt's “An old man in military costume””. Alfeld M, de Nolf W, Cagno S, Janssens K, et al, Journal of analytical atomic spectrometry 28, 40 (2013). http://doi.org/10.1039/C2JA30119A
Abstract: Over the past several decades the oeuvre of Rembrandt has been the subject of extensive art historical and scientific investigations. One of the most striking features to emerge is his frequent re-use of canvases and panels. The painting An Old Man in Military Costume (78.PB.246), in the collection of the J. Paul Getty Museum, is an example of such a re-used panel. Conventional imaging techniques revealed the presence of a second portrait under the surface portrait, but the details of this hidden portrait have not yet been revealed. Vermilion (HgS) has been identified to have been used nearly exclusively in the flesh tones of the lower painting, suggesting that element-specific XRF imaging might successfully image the hidden portrait. To test this hypothesis, a full-scale mock-up of the painting was created, including a “free impression” of the hidden portrait, reproducing as closely as possible the pigments and paint stratigraphy of the original painting. XRF imaging of the mock-up painting was conducted using three different XRF imaging systems: a mobile X-ray tube based system and two synchrotron-based setups (one equipped with multiple SDDs and one equipped with a Maia detector). The sensitivity, limits of detection and imaging capabilities of each system under the chosen experimental conditions are evaluated and compared. The results indicate that an investigation of the original painting by this method would have an excellent chance of success.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 3.379
DOI: 10.1039/C2JA30119A
|
|
|
“Micro X-ray diffraction and fluorescence tomography for the study of multilayered automotive paints”. de Nolf W, Janssens K, Surface and interface analysis 42, 411 (2010). http://doi.org/10.1002/SIA.3125
Abstract: Combined microscopic X-ray fluorescence/microscopic X-ray diffraction (µ-XRF/µ-XRD) tomography is a recently developed method that allows the visualization of the distribution of chemical elements and the associated crystalline phases inside complex, heterogeneous materials of extended thickness (millimeter range) in a nondestructive fashion. In this paper, the accuracy and resolution with which the individual layers in a multilayer stack of automotive paints can be distinguished is evaluated, and some of their properties measured. A paint layer system of eight layers was investigated, in which eight different crystalline substances were identified, each layer consisting of an organic, synthetic resin doped with finely milled inorganic compounds that serve as pigments or to strengthen the layer. In the XRD tomograms, all paint layers could be straightforwardly distinguished and their average thickness calculated. In case the filtered back projection method was used for tomogram reconstruction, a spatial resolution comparable to the microbeam size was obtained indicating no significant reconstruction blurring. When a more robust reconstruction method, such as the maximum-likelihood expectation maximization method, was employed, tomograms showing fewer artifacts were obtained, but with a spatial resolution that was two times worse. In the corresponding XRF tomograms, significant self-absorption distorted the element-specific tomograms corresponding to the low-energy (<7 keV) characteristic radiation and limited their usefulness. It can be concluded that microbeam XRD tomography allows the accurate visualization of the distribution of crystalline phases in multilayered automotive paint materials of millimeter dimensions with sufficient resolution to allow separate characterization of each layer in terms of its crystal-phase composition and thickness.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 1.132
Times cited: 70
DOI: 10.1002/SIA.3125
|
|
|
“Recent trends in quantitative aspects of microscopic X-ray fluorescence analysis”. Janssens K, de Nolf W, van der Snickt G, Vincze L, Vekemans B, Terzano R, Brenker FE, Trends in analytical chemistry 29, 464 (2010). http://doi.org/10.1016/J.TRAC.2010.03.003
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 8.442
Times cited: 48
DOI: 10.1016/J.TRAC.2010.03.003
|
|
|
“Lead soaps in paintings : friends or foes?”.Cotte M, Checroun E, De Nolf W, Taniguchi Y, De Viguerie L, Burghammer M, Walter P, Rivard C, Salome M, Janssens K, Susini J, Studies in conservation 62, 2 (2017). http://doi.org/10.1080/00393630.2016.1232529
Abstract: The origin(s) and role(s) of metal soaps in paints are a worldwide concern today. These hybrid compounds, containing both fatty acid chains and metals associated with a carboxylate function, are increasingly identified in paints. As reviewed in the first part of this work, the presence of metal soaps in paints is differently interpreted in scientific publications: metal soaps are sometimes considered to play a positive role as anchor points, during paint drying processes; they can also be considered as responsible for many degradation processes (protrusions, efflorescences, darkening, etc.). Their origins are also interpreted in various ways. In some paintings (in particular from the twentieth century), they have sometimes introduced on purpose, as additives, to modify the physical properties of the painting materials. In older paintings, metal soaps are usually thought to result from an uncontrolled reaction of oil with lead-based pigments, in particular lead white, red lead, and lead tin yellow. In the second part of this work, the review of historical recipes of lead-based paint shows an important number of recipes based on controlled mixing of oil with lead driers. In the third part, the experimental reproduction of such traditional recipes using walnut oil and litharge (PbO) shows that lead soaps can be formed, both in about one hour at approximate to 100 degrees C, or in about one month at room temperature. It shows as well that after a few years, litharge is no longer detected in the paint medium, while different lead carbonates are. Finally, the micro-infrared spectroscopy and micro-X-ray diffraction re-analysis of protrusions from a nine-year model painting shows together with lead soaps, the presence of Pb-5(CO3)(3)(OH)(2)O ('synthetic plumbonacrite'), an unusual phase recently observed in a protrusion from a painting by Vincent Van Gogh. This work highlights (i) the multiple origins and roles of metal soaps in paints and (ii) the importance of combining the analysis of fragments from historical paintings with the analysis and reproduction of historical recipes. In particular, we show that the components detected today in historical paintings may severely differ from those originally used or prepared by the painter, complicating the assessment of the painter's intentions. More than the presence of metal soaps, the key questions to be tackled should be about their origins and (re)mobilization.
Keywords: A1 Journal article; Art; History; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 0.578
Times cited: 26
DOI: 10.1080/00393630.2016.1232529
|
|
|
“Micro-analytical characterisation of radioactive heterogeneities in samples from Central Asian TENORM sites”. Lind OC, de Nolf W, Janssens K, Salbu B, Journal of environmental radioactivity 123, 63 (2013). http://doi.org/10.1016/J.JENVRAD.2012.02.012
Abstract: The present work focuses on the use of micro-analytical techniques to demonstrate the heterogeneous distribution of radionuclides and metals in soils collected at Former Soviet Union mining sites in Central Asia. Based on digital autoradiography, radionuclides were heterogeneously distributed in soil samples collected at the abandoned uranium mining sites Kurday, Kazakhstan, Kadji Sai, Kyrgyzstan and Taboshar, Tajikistan. Using electron microscopy interfaced with X-ray microanalysis submicron – mm-sized radioactive particles and rock fragments with U, As, Se and toxic metals on the surfaces were identified in Kurday and Kadji Sai samples. Employing scanning and tomographic (3D) synchrotron radiation based micro-X-ray fluorescence (mu-SRXRF) and synchrotron radiation based micro-X-ray diffraction (mu-SRXRD) allowed us to observe the inner structure of the particles without physical sectioning. The distribution of elements in virtual crosssections demonstrated that U and a series of toxic elements were rather heterogeneously distributed also within individual radioactive TENORM particles. Compared to archived data, U in Kadji Sai particles was present as uraninite (U4O9+y or UO2+x) or Na-zippeite aNa(4)(UO2)(6)[(OH)(10)(SO4)(3)]center dot 4H(2)O), i.e. U minerals with very low solubility. The results suggested that TENORM particles can carry substantial amount of radioactivity, which can be subject to re-suspension, atmospheric transport and water transport. Thus, the potential radioecological and radioanalytical impact of radioactive particles at NORM and TENORM sites worldwide should be taken into account. The present work also demonstrates that radioecological studies should benefit from the use of advanced methods such as synchrotron radiation based techniques. (C) 2012 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 2.31
Times cited: 16
DOI: 10.1016/J.JENVRAD.2012.02.012
|
|
|
“Non-invasive and non-destructive examination of artistic pigments, paints, and paintings by means of X-Ray methods”. Janssens K, van der Snickt G, Vanmeert F, Legrand S, Nuyts G, Alfeld M, Monico L, Anaf W, de Nolf W, Vermeulen M, Verbeeck J, De Wael K, Topics in Current Chemistry 374, 81 (2016). http://doi.org/10.1007/S41061-016-0079-2
Abstract: Recent studies are concisely reviewed, in which X-ray beams of (sub)micrometre to millimetre dimensions have been used for non-destructive analysis and characterization of pigments, minute paint samples, and/or entire paintings from the seventeenth to the early twentieth century painters. The overview presented encompasses the use of laboratory and synchrotron radiation-based instrumentation and deals with the use of several variants of X-ray fluorescence (XRF) as a method of elemental analysis and imaging, as well as with the combined use of X-ray diffraction (XRD) and X-ray absorption spectroscopy (XAS). Microscopic XRF is a variant of the method that is well suited to visualize the elemental distribution of key elements, mostly metals, present in paint multi-layers, on the length scale from 1 to 100 μm inside micro-samples taken from paintings. In the context of the characterization of artists pigments subjected to natural degradation, the use of methods limited to elemental analysis or imaging usually is not sufficient to elucidate the chemical transformations that have taken place. However, at synchrotron facilities, combinations of μ-XRF with related methods such as μ-XAS and μ-XRD have proven themselves to be very suitable for such studies. Their use is often combined with microscopic Fourier transform infra-red spectroscopy and/or Raman microscopy since these methods deliver complementary information of high molecular specificity at more or less the same length scale as the X-ray microprobe techniques. Since microscopic investigation of a relatively limited number of minute paint samples, taken from a given work of art, may not yield representative information about the entire artefact, several methods for macroscopic, non-invasive imaging have recently been developed. Those based on XRF scanning and full-field hyperspectral imaging appear very promising; some recent published results are discussed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 4.033
Times cited: 50
DOI: 10.1007/S41061-016-0079-2
|
|
|
“High energy X-ray powder diffraction for the imaging of (hidden) paintings”. de Nolf W, Dik J, van der Snickt G, Wallert A, Janssens K, Journal of analytical atomic spectrometry 26, 910 (2011). http://doi.org/10.1039/C0JA00255K
Abstract: Over the past few years a number of innovative imaging techniques have been introduced for the visualization of hidden paint layers in Old Master Paintings. These include X-ray fluorescence scanning, TeraHertz imaging, optical coherence tomography and other acoustics-based forms of visualization. All of these techniques are usually a trade-off between their penetrative capability on the one side and their analytical precision in terms of spatial resolution and material identification on the other. Here, we present the first-time use of High-Energy X-ray Powder Diffraction imaging (HE-XRPD) in the study of hidden layers in paintings. As an imaging tool, it combines high-depth sensitivity with fingerprint identification of most inorganic painting materials. The potential as well as some limitations of this technique are demonstrated using model paintings as well as an authentic 16th century painting.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 3.379
Times cited: 34
DOI: 10.1039/C0JA00255K
|
|
|
“Macroscopic Fourier transform infrared scanning in reflection mode (MA-rFTIR), a new tool for chemical imaging of cultural heritage artefacts in the mid-infrared range”. Legrand S, Alfeld M, Vanmeert F, de Nolf W, Janssens K, The analyst 139, 2489 (2014). http://doi.org/10.1039/C3AN02094K
Abstract: In this paper we demonstrate that by means of scanning reflection FTIR spectroscopy, it is possible to record highly specific distribution maps of organic and inorganic compounds from flat, macroscopic objects with cultural heritage value in a non-invasive manner. Our previous work involved the recording of macroscopic distributions of chemical elements or crystal phases from painted works of art based on respectively macroscopic X-ray fluorescence or X-ray powder diffraction analysis. The use of infrared radiation instead of X-rays has the advantage that more specific information about the nature and distribution of the chemical compounds present can be gathered. This higher imaging specificity represents a clear advantage for the characterization of painting and artist materials. It allows the distribution of metallo-organic compounds to be visualized and permits distinguishing between pigmented materials containing the same key metal. The prototype instrument allows the recording of hyperspectral datacubes by scanning the surface of the artefact in a contactless and sequential single-point measuring mode, while recording the spectrum of reflected infrared radiation. After the acquisition, spectral line intensities of individual bands and chemical distribution maps can be extracted from the datacube to identify the compounds present and/or to highlight their spatial distribution. Not only is information gained on the surface of the investigated artefacts, but also images of overpainted paint layers and, if present, the underdrawing may be revealed in this manner. A current major limitation is the long scanning times required to record these maps.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 3.885
Times cited: 25
DOI: 10.1039/C3AN02094K
|
|
|
“The ID21 X-ray and infrared microscopy beamline at the ESRF: status and recent applications to artistic materials”. Cotte M, Pouyet E, Salome M, Rivard C, De Nolf W, Castillo-Michel H, Fabris T, Monico L, Janssens K, Wang T, Sciau P, Verger L, Cormier L, Dargaud O, Brun E, Bugnazet D, Fayard B, Hesse B, del Real AEP, Veronesi G, Langlois J, Balcar N, Vandenberghe Y, Sole VA, Kieffer J, Barrett R, Cohen C, Cornu C, Baker R, Gagliardini E, Papillon E, Susini J, Journal of analytical atomic spectrometry 32, 477 (2017). http://doi.org/10.1039/C6JA00356G
Abstract: The ID21 beamline (European Synchrotron Radiation facility, France) is a multi micro-analytical platform combining X-ray and infrared micro-probes, for characterization of elements, species, molecular groups and crystalline structures in complex materials. Applications are mainly in the fields of cultural heritage, life science, environmental and earth sciences, materials sciences. Here, we first present the status of instruments: (i) the scanning micro-spectroscopy end-station, operating from 2.0 to 9.2 keV, under vacuum and offering cryo conditions, for the acquisition of 2D micro X-ray fluorescence (mu XRF) maps, single point micro X-ray Absorption Near Edge Structure (mu XANES) spectra and speciation maps with sub-micrometric resolution; (ii) the XANES full-field end-station, operating in the same vacuum and energy conditions, for the acquisition of hyper-spectral radiographs of thin concentrated samples, resulting in speciation maps with micrometric resolution and millimetric field of view; (iii) the scanning micro-X-ray diffraction (mu XRD)/mu XRF end-station, operating at 8.5 keV, in air, for the acquisition of 2D crystalline phase maps, with micrometric resolution; and (iv) the scanning infrared microscope, operating in the mid-infrared range for the acquisition of molecular maps and some structural maps with micrometric resolution. Recent hardware and software developments are presented, as well as new protocols for improved sample preparation of thin sections. Secondly, a review of recent applications for the study of cultural heritage is presented, illustrated by various examples: determination of the origin of the color in blue Chinese porcelains and in brown Sevres porcelains; detection of lead in ink on Herculaneum papyri; identification and degradation of modeling materials used by Auguste Rodin and of chrome yellow pigments used by Vincent van Gogh. Cryo capabilities are illustrated by the analysis of plants exposed to chromate solutions. These examples show the variety of materials analyzed, of questions tackled, and particularly the multiple advantages of the ID21 analytical platform for the analysis of ancient and artistic materials.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 3.379
Times cited: 39
DOI: 10.1039/C6JA00356G
|
|
|
“The use of synchrotron radiation for the characterization of artists' pigments and paintings”. Janssens K, Alfeld M, van der Snickt G, de Nolf W, Vanmeert F, Radepont M, Monico L, et al, Annual review of analytical chemistry 6, 399 (2013). http://doi.org/10.1146/ANNUREV-ANCHEM-062012-092702
Abstract: We review methods and recent studies in which macroscopic to (sub)microscopic X-ray beams were used for nondestructive analysis and characterization of pigments, paint microsamples, and/or entire paintings. We discuss the use of portable laboratory- and synchrotron-based instrumentation and describe several variants of X-ray fluorescence (XRF) analysis used for elemental analysis and imaging and combined with X-ray diffraction (XRD) and X-ray absorption spectroscopy (XAS). Macroscopic and microscopic (μ-)XRF variants of this method are suitable for visualizing the elemental distribution of key elements in paint multilayers. Technical innovations such as multielement, large-area XRF detectors have enabled such developments. The use of methods limited to elemental analysis or imaging usually is not sufficient to elucidate the chemical transformations that take place during natural pigment alteration processes. However, synchrotron-based combinations of μ-XRF, μ-XAS, and μ-XRD are suitable for such studies.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 7.435
Times cited: 46
DOI: 10.1146/ANNUREV-ANCHEM-062012-092702
|
|
|
“Degradation process of lead chromate in paintings by Vincent van Gogh studied by means of synchrotron X-ray spectromicroscopy and related methods : 1 : artificially aged model samples”. Monico L, van der Snickt G, Janssens K, de Nolf W, Miliani C, Verbeeck J, Tian H, Tan H, Dik J, Radepont M, Cotte M, Analytical chemistry 83, 1214 (2011). http://doi.org/10.1021/ac102424h
Abstract: On several paintings by artists of the end of the 19th century and the beginning of the 20th Century a darkening of the original yellow areas, painted with the chrome yellow pigment (PbCrO4, PbCrO4·xPbSO4, or PbCrO4·xPbO) is observed. The most famous of these are the various Sunflowers paintings Vincent van Gogh made during his career. In the first part of this work, we attempt to elucidate the degradation process of chrome yellow by studying artificially aged model samples. In view of the very thin (1−3 μm) alteration layers that are formed, high lateral resolution spectroscopic methods such as microscopic X-ray absorption near edge (μ-XANES), X-ray fluorescence spectrometry (μ-XRF), and electron energy loss spectrometry (EELS) were employed. Some of these use synchrotron radiation (SR). Additionally, microscopic SR X-ray diffraction (SR μ-XRD), μ-Raman, and mid-FTIR spectroscopy were employed to completely characterize the samples. The formation of Cr(III) compounds at the surface of the chrome yellow paint layers is particularly observed in one aged model sample taken from a historic paint tube (ca. 1914). About two-thirds of the chromium that is present at the surface has reduced from the hexavalent to the trivalent state. The EELS and μ-XANES spectra are consistent with the presence of Cr2O3·2H2O (viridian). Moreover, as demonstrated by μ-XANES, the presence of another Cr(III) compound, such as either Cr2(SO4)3·H2O or (CH3CO2)7Cr3(OH)2 [chromium(III) acetate hydroxide], is likely.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 6.32
Times cited: 113
DOI: 10.1021/ac102424h
|
|