“Synthesis, crystal structure and physico-chemical properties of the new quaternary oxide Sr5BiNi2O9.6”. Novitskaya M, Makhnach L, Ivashkevich L, Pankov V, Klein H, Regeau A, David J, Gemmi M, Hadermann J, Strobel P, Journal of solid state chemistry 184, 3262 (2011). http://doi.org/10.1016/j.jssc.2011.10.020
Abstract: A new black quaternary oxide Sr5BiNi2O9.6 was synthesized by solid state reaction at 1200 °C. Its structure was solved by electron crystallography and X-ray powder refinement, yielding a tetragonal structure with space group I4/mmm, a=5.3637 (2) Å, c=17.5541(5) Å, Z=4. The structure can be described as a stacking of (Bi,Sr)O rocksalt slabs and SrNiO3−δ perovskite slabs. The initial nickel valence is close to +3.1. Thermogravimetry and high-temperature oxygen coulometry showed that this compound has variable oxygen content as a function of temperature and oxygen pressure, and ultimately decomposes when heated in low oxygen pressure above 800 °C. It is a metallic conductor with n-type conduction. Its thermoelectric power was determined and found to be −20 and −38 μV/K at 300 and 650 °C, respectively. Magnetic measurements confirm the nickel valence close to +3 and show evidence of magnetic ordering at 20 K.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 4
DOI: 10.1016/j.jssc.2011.10.020
|
|
|
“Nanocrystals of lead chalcohalides : a series of kinetically trapped metastable nanostructures”. Toso S, Akkerman QA, Martin-Garcia B, Prato M, Zito J, Infante I, Dang Z, Moliterni A, Giannini C, Bladt E, Lobato I, Ramade J, Bals S, Buha J, Spirito D, Mugnaioli E, Gemmi M, Manna L, Journal Of The American Chemical Society 142, 10198 (2020). http://doi.org/10.1021/JACS.0C03577
Abstract: We report the colloidal synthesis of a series of surfactant-stabilized lead chalcohalide nanocrystals. Our work is mainly focused on Pb4S3Br2, a chalcohalide phase unknown to date that does not belong to the ambient-pressure PbS-PbBr2 phase diagram. The Pb4S3Br2 nanocrystals herein feature a remarkably narrow size distribution (with a size dispersion as low as 5%), a good size tunability (from 7 to similar to 30 nm), an indirect bandgap, photoconductivity (responsivity = 4 +/- 1 mA/W), and stability for months in air. A crystal structure is proposed for this new material by combining the information from 3D electron diffraction and electron tomography of a single nanocrystal, X-ray powder diffraction, and density functional theory calculations. Such a structure is closely related to that of the recently discovered high-pressure chalcohalide Pb4S3I2 phase, and indeed we were able to extend our synthesis scheme to Pb4S3I2 colloidal nanocrystals, whose structure matches the one that has been published for the bulk. Finally, we could also prepare nanocrystals of Pb3S2Cl2, which proved to be a structural analogue of the recently reported bulk Pb3Se2Br2 phase. It is remarkable that one high-pressure structure (for Pb4S3I2) and two metastable structures that had not yet been reported (for Pb4S3Br2 and Pb3S2Cl2) can be prepared on the nanoscale by wet-chemical approaches. This highlights the important role of colloidal chemistry in the discovery of new materials and motivates further exploration into metal chalcohalide nanocrystals.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 15
Times cited: 32
DOI: 10.1021/JACS.0C03577
|
|
|
“Direct space structure solution from precession electron diffraction data: resolving heavy and light scatterers in Pb13Mn9O25”. Hadermann J, Abakumov AM, Tsirlin AA, Filonenko VP, Gonnissen J, Tan H, Verbeeck J, Gemmi M, Antipov EV, Rosner H, Ultramicroscopy 110, 881 (2010). http://doi.org/10.1016/j.ultramic.2010.03.012
Abstract: The crystal structure of a novel compound Pb13Mn9O25 has been determined through a direct space structure solution with a Monte-Carlo-based global optimization using precession electron diffraction data (a=14.177(3) Å, c=3.9320(7) Å, SG P4/m, RF=0.239) and compositional information obtained from energy dispersive X-ray analysis and electron energy loss spectroscopy. This allowed to obtain a reliable structural model even despite the simultaneous presence of both heavy (Pb) and light (O) scattering elements and to validate the accuracy of the electron diffraction-based structure refinement. This provides an important benchmark for further studies of complex structural problems with electron diffraction techniques. Pb13Mn9O25 has an anion- and cation-deficient perovskite-based structure with the A-positions filled by the Pb atoms and 9/13 of the B positions filled by the Mn atoms in an ordered manner. MnO6 octahedra and MnO5 tetragonal pyramids form a network by sharing common corners. Tunnels are formed in the network due to an ordered arrangement of vacancies at the B-sublattice. These tunnels provide sufficient space for localization of the lone 6s2 electron pairs of the Pb2+ cations, suggested as the driving force for the structural difference between Pb13Mn9O25 and the manganites of alkali-earth elements with similar compositions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.843
Times cited: 24
DOI: 10.1016/j.ultramic.2010.03.012
|
|
|
“Halide perovskites as disposable epitaxial templates for the phase-selective synthesis of lead sulfochloride nanocrystals”. Toso S, Imran M, Mugnaioli E, Moliterni A, Caliandro R, Schrenker NJ, Pianetti A, Zito J, Zaccaria F, Wu Y, Gemmi M, Giannini C, Brovelli S, Infante I, Bals S, Manna L, Nature communications 13, 3976 (2022). http://doi.org/10.1038/S41467-022-31699-1
Abstract: Colloidal chemistry grants access to a wealth of materials through simple and mild reactions. However, even few elements can combine in a variety of stoichiometries and structures, potentially resulting in impurities or even wrong products. Similar issues have been long addressed in organic chemistry by using reaction-directing groups, that are added to a substrate to promote a specific product and are later removed. Inspired by such approach, we demonstrate the use of CsPbCl3 perovskite nanocrystals to drive the phase-selective synthesis of two yet unexplored lead sulfochlorides: Pb3S2Cl2 and Pb4S3Cl2. When homogeneously nucleated in solution, lead sulfochlorides form Pb3S2Cl2 nanocrystals. Conversely, the presence of CsPbCl3 triggers the formation of Pb4S3Cl2/CsPbCl3 epitaxial heterostructures. The phase selectivity is guaranteed by the continuity of the cationic subnetwork across the interface, a condition not met in a hypothetical Pb3S2Cl2/CsPbCl3 heterostructure. The perovskite domain is then etched, delivering phase-pure Pb4S3Cl2 nanocrystals that could not be synthesized directly. Phase-selective approaches, such using reaction-directing groups, are often seen in traditional organic chemistry and catalysis. Here authors use perovskite nanocrystals as disposable templates to drive the phase-selective synthesis of two colloidal nanomaterials, the lead sulfohalides Pb3S2Cl2 and Pb4S3Cl2.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 16.6
Times cited: 15
DOI: 10.1038/S41467-022-31699-1
|
|