Abstract: Semiconductor heterostructures are used for the fabrication of optoelectronic devices. Performance of such devices is governed by their chemical morphology. The composition distribution of quantum wells and dots is influenced by kinetic growth processes which are not understood completely at present. To obtain more information about these effects, methods for composition determination with a spatial resolution at a near atomic scale are necessary. In this paper we focus on the present state of the composition evaluation by the lattice fringe analysis (CELFA) technique and explain the basic ideas, optimum imaging conditions, precision and accuracy.

Abstract: An alternative pathway to assemble mesoporous molecular sieve silicas is developed using nonionic alkylamines and N,N-dimethylalkylamines (SO) as structure-directing agents in acidic conditions. The synthesized mesostructures possess wormhole-like frameworks with pore sizes and pore volumes in the range of 20-90 Angstrom and 0.5-1.3 cm(3)/g, respectively. The formation of the mesophase is controlled by a counterion-mediated mechanism of the type (S(0)H(+))(X(-)I(+)), where S(0)H(+) are protonated water molecules that are hydrogen bonded to the lone electron pairs on the amine surfactant headgroups (S(0)H(+)), X(-) is the counteranion originating from the acid, and I(+) are the positively charged (protonated) silicate species. We found that the stronger the ion X(-) is bonded to S(0)H(+), the more it catalyzes the silica condensation into (S(0)H(+))(X(-)I(+)). Br(-) is shown to be a strong binding anion and therefore a fast silica polymerization promoter compared to Cl(-) resulting in the formation of a higher quality mesophase for the Br(-) syntheses. We also showed that the polymerization rate of the silica, dictated by the counterion, controls the morphology of the mesostructures from nonuniform agglomerated blocks in the case of Br(-) syntheses to spherical particles for the Cl(-) syntheses. Next to many benefits such as low temperature, short synthesis time, and the use of inexpensive, nontoxic, and easily extractable amine templates, the developed materials have a remarkable higher thermal and hydrothermal stability compared to hexagonal mesoporous silica, which is also prepared with nonionic amines but formed through the S(0)I(0) mechanism.

Abstract: A thorough investigation was performed on the physical (mechanical, thermal, and hydrothermal stability) and chemical (ion exchange capacity and silanol number) characteristics of aluminosilicate FSMs, synthesized via a new successful short-time synthesis route using leached saponite and a low concentration of CTAB. Moreover, the influence of an additional Al incorporation, utilizing different aluminum sources, on the structure of the FSM derived from saponite is studied. A mesoporous aluminosilicate with a low Si/Al ratio of 12.8 is synthesized, and still has a very large surface area of 1130 m(2)/g and pore volume of 0.92 cm(3)/g. The aluminum-containing samples all have a high cation exchange capacity of around 1 mmol/9 while they still have a silanol number of about 0.9 OH/nm(2); both characteristics being interesting for high-yield postsynthesis modification reactions. Finally, a study is performed on the transformation of the aluminosilicates into their Bronsted acid form via the exchange with ammonium ions and a consecutive heat treatment.

Abstract: Infrared absorption spectra of composite precipitates are analysed with a modified Day-Thorpe algorithm, assuming a precipitated phase consisting of a mixture of two components with known optical properties. Additional constraints are introduced when solving the model equations by using a priori knowledge making the algorithm more reliable. It is shown that this novel approach allows determining both morphology and composition of precipitates. The method is applied to characterise oxide precipitates in boron-doped silicon. The results indicate that for the resistivity range above 60 mOmegacm, the precipitated phase is most probably SiO1.17+/-0.14, while for resistivities below 20 mOmega cm, precipitates consist of a SiO2/B2O3 composite with a large volume fraction of B(2)0(3) (up to 40% for 8 mOmegacm material). (C) 2003 Elsevier B.V. All rights reserved.

Abstract: The dissociation of 60degrees and screw dislocations in diamond is modeled in an approach combining isotropic elasticity theory with ab initio-based tight-binding total-energy calculations. Both dislocations are found to dissociate with a substantial lowering of their line energies. For the 60degrees dislocation, however, an energy barrier to dissociation is found. We investigate the core structure of a screw dislocation distinguishing “shuffle,” “mixed,” and “glide” cores. The latter is found to be the most stable undissociated screw dislocation. Further, the glide motion of 90degrees and 30degrees partials is discussed in terms of a process involving the thermal formation and subsequent migration of kinks along the dislocation line. The calculated activation barriers to dislocation motion show that the 30degrees partial is less mobile than the 90degrees partial. Finally, high-resolution electron microscopy is performed on high-temperature, high-pressure annealed natural brown diamond, allowing the core regions of 60degrees dislocations to be imaged. The majority of dislocations are found to be dissociated. However, in some cases, undissociated 60degrees dislocations were also observed.

Abstract: Structural, chemical, and physical properties of whitlockite-type Ca9Bi(VO4)(7) were studied by X-ray powder diffraction (XRD), electron diffraction (ED), second-harmonic generation (SHG), thermogravimetry, differential scanning calorimetry, dielectric, and electrical-conductivity measurements. A new phase-transition of the ferroelectric type was found in Ca9Bi(VO4)(7) with a transition temperature, T-c of 1053 +/- 3 K. The polar phase, beta-Ca9Bi(VO4)(7), is stable below T-c down to at least 160 K. The centrosymmetric beta'-phase is stable above T-c up to 1273 +/- 5 K. Above 1273 K, it decomposes to give BiVO4 and whitlockite-type solid solutions of Ca9+1.5xBi1-x(VO4)(7). The beta<---->beta' phase transition is reversible and of second order. Electrical conductivity of beta'-Ca9Bi(VO4)(7) is rather high (sigma = 0.6 x 10(-3) S/cm at 1200 K) and obeys the Arrhenius law with an activation energy of 1.0 eV. Structure parameters of Ca9Bi(VO4)(7) are refined by the Rietveld method from XRD data measured at room temperature (space group R3c; Z = 6; a = 10.8992(1) Angstrom, c = 38.1192(4) Angstrom, and V = 3921.6(1) Angstrom(3); R-wp = 3.06% and R-p = 2.36%). Bi3+ ions together with Ca2+ ions are statistically distributed among the M1, M2, M3, and M5 sites. Ca9Bi(VO4)(7) has a SHG efficiency of about 140 times that of quartz. Through the powder SHG measurements, we estimated the nonlinear optical susceptibility, Digital, at about 6.1-7.2 pm/V. This value for Ca9Bi(VO4)(7) is comparable with that for known nonlinear optical materials such as LiNbO3 and LiTaO3.

Abstract: We measured the electrical resistivity R(T) and specific heat C-p(T) between room temperature (RT) and 4.2 K as well as the microstructure by transmission electron microscopy (TEM) of a Ni-52 Ti-48 SMA quenched from 1000degreesC (B2-Phase range) to RT and then annealed for 1h at T=380degreesC, 550degreesC and 650degreesC. In the “as quenched” and the “650degreesC annealed” state no martensitic transformations (MT's) occur. The diffraction patterns show faint reflections originating from coherent Ni4Ti3 precipitates in an early state of formation. Additional reflections of the type 1/2 <110>, 1/2 <111> and 1/3 <110> result from various lattice displacement waves, which are precursors of the MT's to the B19' and R-phase, respectively. Indeed, high resolution TEM micrographs of the [001] zone of the “as quenched” sample reveal transverse 1/2 <110> <110> lattice displacement waves, precursors of the B19' martensite. The coherent Ni4Ti3 precipitates, homogeneously distributed on a small length scale, binder the MT's in the “as quenched” and the “650degreesC annealed” state, and thus only the precursors appear. When annealed at T=380degreesC, however, coherent Ni4Ti3 precipitates with a length of 10nm are clearly visible in TEM. These precipitates trigger the NIT from the B2 to the R-phase on cooling, as evidenced also by anomalies in R(T) and C-p(T). Annealing at T-550degreesC leads to the well known two step MT's from the B2 to the R-phase and then into the B19'-phase. These martensitic transitions are clearly seen as additional peaks in the specific heat and anomalies in the resistance, while the “as quenched” and 650degreesC annealed samples show weak features in R(T) and C-p(T).

Abstract: High-resolution transmission electron microscopy was performed on compacted Ni(3)Al nanostructured material prepared by the inert gas condensation technique. From electron diffraction data an incomplete L1(2) ordering of the crystallites is observed in the free particles as well as in the room temperature compacted samples. However, a completely ordered L1(2) structure with much bigger and well-defined crystallites exhibiting several defects is observed in material compacted and annealed at 773 K. Sharp crystallite boundaries as well as amorphous material and voids are observed in between crystallites in all samples, the former being dominant in the annealed material, the latter in the as-prepared one.

Abstract: Complex [(La0.7Sr0.3MnO3)(m)(SrTiO3)(n)] [(LSMO)(m)/(STO)(8)](15) superlattices with different layer thicknesses (m=5, 8, 12, 16, 32) have been prepared using pulsed liquid injection metalorganic chemical vapor deposition. Transmission electron microscopy and electron diffraction reveal a very clear and well-separated layer sequence. The remarkable microstructure, as well as the ferromagnetic transition temperature, depends on the LSMO layer thickness. Apart from a very clear layer sequence, electron microscopy shows evidence of a self-assembled nanostructure formation: SrMnO3 nanoinclusions and associated SrTiO3-SrMnO3 thin walls. A formation model and growth mechanism for the self-assembled structure is proposed, based on high resolution and energy filtered elemental imaging. (C) 2003 American Institute of Physics.