“Oxidation barrier of Cu and Fe powder by Atomic Layer Deposition”. Cremers V, Rampelberg G, Barhoum A, Walters P, Claes N, Oliveira TM de, Assche GV, Bals S, Dendooven J, Detavernier C, Surface and coatings technology 349, 1032 (2018). http://doi.org/10.1016/j.surfcoat.2018.06.048
Abstract: Atomic layer deposition (ALD) is a vapor based technique which allows to deposit uniform, conformal films with a thickness control at the atomic scale. In this research, Al 2 O 3 coatings were deposited on micrometer-sized Fe and Cu powder (particles) using the thermal trimethylaluminum (TMA)/ water (H 2 O) process in a rotary pump-type ALD reactor. Rotation of the powder during deposition was required to obtain a pinhole-free ALD coating. The protective nature of the coating was evaluated by quantifying its effectiveness in protecting the metal particles during oxidative annealing treatments. The Al 2 O 3 coated powders were annealed in ambient air while in-situ thermogravimetric analysis (TGA) and in-situ x-ray diffraction (XRD) data were acquired. The thermal stability of a series of Cu and Fe powder with different Al 2 O 3 thicknesses were determined with TGA. In both samples a clear shift in oxidation temperature is visible. For Cu and Fe powder coated with 25 nm Al 2 O 3 , we observed an increase of the oxidation temperature with 300-400°C. For the Cu powder a thin film of only 8 nm is required to obtain an initial increase in oxidation temperature of 200°C. In contrast, for Fe powder a thicker coating of 25 nm is required. In both cases, the oxidation temperature increases with increasing thickness of the Al 2 O 3 coating. These results illustrate that the Al 2 O 3 thin film, deposited by the thermal ALD process (TMA/H 2 O) can be an efficient and pinhole-free barrier layer for micrometer-sized powder particles, provided that the powder is properly agitated during the process to ensure sufficient vapour-solid interaction.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.589
Times cited: 10
DOI: 10.1016/j.surfcoat.2018.06.048
|
|
|
“β-Na1.7IrO3: A Tridimensional Na-Ion Insertion Material with a Redox Active Oxygen Network”. Pearce PE, Rousse G, Karakulina OM, Hadermann J, Van Tendeloo G, Foix D, Fauth F, Abakumov AM, Tarascon J-M, Chemistry of materials 30, 3285 (2018). http://doi.org/10.1021/acs.chemmater.8b00320
Abstract: The revival of the Na-ion battery concept has prompted an intense search for new high capacity Na-based positive electrodes. Recently, emphasis has been placed on manipulating Na-based layered compounds to trigger the participation of the anionic network. We further explored this direction and show the feasibility of achieving anionic-redox activity in three-dimensional Na-based compounds. A new 3D β-Na1.7IrO3 phase was synthesized in a two-step process, which involves first the electrochemical removal of Li from β-Li2IrO3 to produce β-IrO3, which is subsequently reduced by electrochemical Na insertion. We show that β-Na1.7IrO3 can reversibly uptake nearly 1.3 Na+ per formula unit through an uneven voltage profile characterized by the presence of four plateaus related to structural transitions. Surprisingly, the β-Na1.7IrO3 phase was found to be stable up to 600 °C, while it could not be directly synthesized via conventional synthetic methods. Although these Na-based iridate phases are of limited practical interest, they help to understand how introducing highly polarizable guest ions (Na+) into host rocksalt-derived oxide structures affects the anionic redox mechanism.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 6
DOI: 10.1021/acs.chemmater.8b00320
|
|
|
“Recent breakthroughs in scanning transmission electron microscopy of small species”. van den Bos KHW, Altantzis T, De Backer A, Van Aert S, Bals S, Advances in Physics: X 3, 1480420 (2018). http://doi.org/10.1080/23746149.2018.1480420
Abstract: Over the last decade, scanning transmission electron microscopy has become one of the most powerful tools to characterise nanomaterials at the atomic scale. Often, the ultimate goal is to retrieve the three-dimensional structure, which is very challenging since small species are typically sensitive to electron irradiation. Nevertheless, measuring individual atomic positions is crucial to understand the relation between the structure and physicochemical properties of these (nano)materials. In this review, we highlight the latest approaches that are available to reveal the 3D atomic structure of small species. Finally, we will provide an outlook and will describe future challenges where the limits of electron microscopy will be pushed even further.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 8
DOI: 10.1080/23746149.2018.1480420
|
|
|
“Mono- and Multilayer Silicene-Type Honeycomb Lattices by Oriented Attachment of PbSe Nanocrystals: Synthesis, Structural Characterization, and Analysis of the Disorder”. Peters JL, Altantzis T, Lobato I, Jazi MA, van Overbeek C, Bals S, Vanmaekelbergh D, Sinai SB, Chemistry of materials 30, 4831 (2018). http://doi.org/10.1021/acs.chemmater.8b02178
Abstract: Nanocrystal (NC) solids are commonly prepared from nonpolar organic NC suspensions. In many cases, the capping on the NC surface is preserved and forms a barrier between the NCs. More recently, superstructures with crystalline connections between the NCs, implying the removal of the capping, have been reported, too. Here, we present large-scale uniform superstructures of attached PbSe NCs with a silicene-type honeycomb geometry, resulting from solvent evaporation under nearly reversible conditions. We also prepared multilayered silicene honeycomb structures by using larger amounts of PbSe NCs. We show that the two-dimensional silicene superstructures can be seen as a crystallographic slice from a 3-D simple cubic structure. We describe the disorder in the silicene lattices in terms of the nanocrystals position and their atomic alignment. The silicene honeycomb sheets are large enough to be used in transistors and optoelectronic devices.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 33
DOI: 10.1021/acs.chemmater.8b02178
|
|
|
“Chemical activity of the peroxide/oxide redox couple : case study of Ba5Ru2O11 in aqueous and organic solvents”. Grimaud A, Iadecola A, Batuk D, Saubanere M, Abakumov AM, Freeland JW, Cabana J, Li H, Doublet M-L, Rousse G, Tarascon J-M, Chemistry of materials 30, 3882 (2018). http://doi.org/10.1021/ACS.CHEMMATER.8B01372
Abstract: The finding that triggering the redox activity of oxygen ions within the lattice of transition metal oxides can boost the performances of materials used in energy storage and conversion devices such as Li-ion batteries or oxygen evolution electrocatalysts has recently spurred intensive and innovative research in the field of energy. While experimental and theoretical efforts have been critical in understanding the role of oxygen nonbonding states in the redox activity of oxygen ions, a clear picture of the redox chemistry of the oxygen species formed upon this oxidation process is still missing. This can be, in part, explained by the complexity in stabilizing and studying these species once electrochemically formed. In this work, we alleviate this difficulty by studying the phase Ba5Ru2O11, which contains peroxide O-2(2-) groups, as oxygen evolution reaction electrocatalyst and Li-ion battery material. Combining physical characterization and electrochemical measurements, we demonstrate that peroxide groups can easily be oxidized at relatively low potential, leading to the formation of gaseous dioxygen and to the instability of the oxide. Furthermore, we demonstrate that, owing to the stabilization at high energy of peroxide, the high-lying energy of the empty sigma* antibonding O-O states limits the reversibility of the electrochemical reactions when the O-2(2-)/O2- redox couple is used as redox center for Li-ion battery materials or as OER redox active sites. Overall, this work suggests that the formation of true peroxide O-2(2-) states are detrimental for transition metal oxides used as OER catalysts and Li-ion battery materials. Rather, oxygen species with O-O bond order lower than 1 would be preferred for these applications.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 2
DOI: 10.1021/ACS.CHEMMATER.8B01372
|
|
|
“Control of the interfacial wettability to synthesize highly dispersed PtPd nanocrystals for efficient oxygen reduction reaction”. Wei H, Hu Z-Y, Xiao Y-X, Tian G, Ying J, Van Tendeloo G, Janiak C, Yang X-Y, Su B-L, Chemistry: an Asian journal 13, 1119 (2018). http://doi.org/10.1002/ASIA.201800191
Abstract: Highly dispersed PtPd bimetallic nanocrystals with enhanced catalytic activity and stability were prepared by adjusting the interfacial wettability of the reaction solution on a commercial carbon support. This approach holds great promise for the development of high-performance and low-cost catalysts for practical applications.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.083
Times cited: 3
DOI: 10.1002/ASIA.201800191
|
|
|
“Local probing of the enhanced field electron emission of vertically aligned nitrogen-doped diamond nanorods and their plasma illumination properties”. Deshmukh S, Sankaran KJ, Srinivasu K, Korneychuk S, Banerjee D, Barman A, Bhattacharya G, Phase DM, Gupta M, Verbeeck J, Leou KC, Lin IN, Haenen K, Roy SS, Diamond and related materials 83, 118 (2018). http://doi.org/10.1016/J.DIAMOND.2018.02.005
Abstract: A detailed conductive atomic force microscopic investigation is carried out to directly image the electron emission behavior for nitrogen-doped diamond nanorods (N-DNRs). Localized emission measurements illustrate uniform distribution of high-density electron emission sites from N-DNRs. Emission sites coupled to nano graphitic phases at the grain boundaries facilitate electron transport and thereby enhance field electron emission from N-DNRs, resulting in a device operation at low turn-on fields of 6.23 V/mu m, a high current density of 1.94 mA/cm(2) (at an applied field of 11.8 V/mu m) and a large field enhancement factor of 3320 with a long lifetime stability of 980 min. Moreover, using N-DNRs as cathodes, a microplasma device that can ignite a plasma at a low threshold field of 390 V/mm achieving a high plasma illumination current density of 3.95 mA/cm2 at an applied voltage of 550 V and a plasma life-time stability for a duration of 433 min was demonstrated.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.561
Times cited: 9
DOI: 10.1016/J.DIAMOND.2018.02.005
|
|
|
“Orthorhombic vs. hexagonal epitaxial SrIrO3 thin films : structural stability and related electrical transport properties”. Bhat SG, Gauquelin N, Sebastian NK, Sil A, Béché, A, Verbeeck J, Samal D, Kumar PSA, Europhysics letters 122, 28003 (2018). http://doi.org/10.1209/0295-5075/122/28003
Abstract: Metastable orthorhombic SrIrO3 (SIO) is an arch-type spin-orbit coupled material. We demonstrate here a controlled growth of relatively thick (200 nm) SIO films that transform from bulk “6H-type” structure with monoclinic distortion to an orthorhombic lattice by controlling growth temperature. Extensive studies based on high-resolution X-ray diffraction and transmission electron microscopy infer a two distinct structural phases of SIO. Electrical transport reveals a weak temperature-dependent semi-metallic character for both phases. However, the temperature-dependent Hall-coefficient for the orthorhombic SIO exhibits a prominent sign change, suggesting a multiband character in the vicinity of E-F. Our findings thus unravel the subtle structure-property relation in SIO epitaxial thin films. Copyright (C) EPLA, 2018
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.957
Times cited: 4
DOI: 10.1209/0295-5075/122/28003
|
|
|
“Strain analysis from nano-beam electron diffraction : influence of specimen tilt and beam convergence”. Grieb T, Krause FF, Schowalter M, Zillmann D, Sellin R, Müller-Caspary K, Mahr C, Mehrtens T, Bimberg D, Rosenauer A, Ultramicroscopy 190, 45 (2018). http://doi.org/10.1016/J.ULTRAMIC.2018.03.013
Abstract: Strain analyses from experimental series of nano-beam electron diffraction (NBED) patterns in scanning transmission electron microscopy are performed for different specimen tilts. Simulations of NBED series are presented for which strain analysis gives results that are in accordance with experiment. This consequently allows to study the relation between measured strain and actual underlying strain. A two-tilt method which can be seen as lowest-order electron beam precession is suggested and experimentally implemented. Strain determination from NBED series with increasing beam convergence is performed in combination with the experimental realization of a probe-forming aperture with a cross inside. It is shown that using standard evaluation techniques, the influence of beam convergence on spatial resolution is lower than the influence of sharp rings around the diffraction disc which occur at interfaces and which are caused by the tails of the intensity distribution of the electron probe. (C) 2018 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.843
Times cited: 1
DOI: 10.1016/J.ULTRAMIC.2018.03.013
|
|
|
“Subtissue plasmonic heating monitored with CaF2:Nd3+,Y3+ nanothermometers in the second biological window”. Quintanilla M, Zhang Y, Liz-Marzan LM, Chemistry of materials 30, 2819 (2018). http://doi.org/10.1021/ACS.CHEMMATER.8B00806
Abstract: Measuring temperature in biological environments is an ambitious goal toward supporting medical treatment and diagnosis. Minimally invasive techniques based on optical probes require very specific properties that are difficult to combine within a single material. These include high chemical stability in aqueous environments, optical signal stability, low toxicity, high emission intensity, and, essential, working at wavelengths within the biological transparency windows so as to minimize invasiveness while maximizing penetration depth. We propose CaF2:Nd3+,Y3+ as a candidate for thermometry based on an intraband ratiometric approach, fully working within the biological windows (excitation at 808 nm; emission around 1050 nm). We optimized the thermal probes through the addition of Y3+ as a dopant to improve both emission intensity and thermal sensitivity. To define the conditions under which the proposed technique can be applied, gold nanorods were used to optically generate subtissue hot areas, while the resulting temperature variation was monitored with the new nanothermometers.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 28
DOI: 10.1021/ACS.CHEMMATER.8B00806
|
|
|
“Influence of 4H-SiC substrate miscut on the epitaxy and microstructure of AlGaN/GaN heterostructures”. Gkanatsiou A, Lioutas CB, Frangis N, Polychroniadis EK, Prystawko P, Leszczynski M, Altantzis T, Van Tendeloo G, Materials science in semiconductor processing 91, 159 (2019). http://doi.org/10.1016/j.mssp.2018.11.008
Abstract: AlGaN/GaN heterostructures were grown on “on-axis” and 2° off (0001) 4H-SiC substrates by metalorganic vapor phase epitaxy (MOVPE). Structural characterization was performed by transmission electron microscopy. The dislocation density, being greater in the on-axis case, is gradually reduced in the GaN layer and is forming
dislocation loops in the lower region. Steps aligned along [11̅00] in the off-axis case give rise to simultaneous defect formation. In the on-axis case, an almost zero density of steps is observed, with the main origin of defects probably being the orientation mismatch at the grain boundaries between the small not fully coalesced AlN grains. V-shaped formations are observed in the AlN nucleation layer, but are more frequent in the off-axis case, probably enhanced by the presence of steps. These V-shaped formations are completely overgrown by the GaN layer, during the subsequent deposition, presenting AlGaN areas in the walls of the defect, indicating an interdiffusion between the layers. Finally, at the AlGaN/GaN heterostructure surface in the on-axis case, V-shapes are observed, with the AlN spacer and AlGaN (21% Al) thickness on relaxed GaN exceeding the critical thickness for relaxation. On the other hand, no relaxation in the form of V-shape creation is observed in the off-axis case, probably due to the smaller AlGaN thickness (less than 21% Al). The AlN spacer layer, grown in between the heterostructure, presents a uniform thickness and clear interfaces.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.359
Times cited: 1
DOI: 10.1016/j.mssp.2018.11.008
|
|
|
“Postsynthetic high-alumina zeolite crystal engineering in organic free hyper-alkaline media”. Van Tendeloo L, Wangermez W, Vandekerkhove A, Willhammar T, Bals S, Maes A, Martens JA, Kirschhock CEA, Breynaert E, Chemistry of materials 29, 629 (2017). http://doi.org/10.1021/ACS.CHEMMATER.6B04052
Abstract: Postsynthetic modification of high -alumina zeolites in hyper alkaline media can be tailored toward alteration of framework topology, crystal size and morphology, or desired Si/A1 ratio. FAU, EMT, MAZ, KFI, HEU, and LTA starting materials were treated with 1.2 M MOH (M = Na, K, RE, or Cs), leading to systematic ordered porosity or fully transformed frameworks with new topology and adjustable Si/Al ratio. In addition to the versatility of this tool for zeolite crystal engineering, these alterations improve understanding of the crystal chemistry. Such knowledge can guide further development in zeolite crystal engineering. Postsynthetic alteration also provides insight on the long-term stability of aluminosilicate zeolites that are used as a sorption sink in concrete -based waste disposal facilities in harsh alkaline conditions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 16
DOI: 10.1021/ACS.CHEMMATER.6B04052
|
|
|
“Gel-based morphological design of zirconium metal-organic frameworks”. Bueken B, Van Velthoven N, Willhammar T, Stassin T, Stassen I, Keen DA, Baron GV, Denayer JFM, Ameloot R, Bals S, De Vos D, Bennett TD, Chemical science 8, 3939 (2017). http://doi.org/10.1039/C6SC05602D
Abstract: The ability of metal-organic frameworks (MOFs) to gelate under specific synthetic conditions opens up new opportunities in the preparation and shaping of hierarchically porous MOF monoliths, which could be directly implemented for catalytic and adsorptive applications. In this work, we present the first examples of xero-or aerogel monoliths consisting solely of nanoparticles of several prototypical Zr4+-based MOFs: UiO-66-X (X – H, NH2, NO2, (OH)(2)), UiO-67, MOF-801, MOF-808 and NU-1000. High reactant and water concentrations during synthesis were observed to induce the formation of gels, which were converted to monolithic materials by drying in air or supercritical CO2. Electron microscopy, combined with N-2 physisorption experiments, was used to show that irregular nanoparticle packing leads to pure MOF monoliths with hierarchical pore systems, featuring both intraparticle micropores and interparticle mesopores. Finally, UiO-66 gels were shaped into monolithic spheres of 600 mm diameter using an oil-drop method, creating promising candidates for packed-bed catalytic or adsorptive applications, where hierarchical pore systems can greatly mitigate mass transfer limitations.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 8.668
Times cited: 168
DOI: 10.1039/C6SC05602D
|
|
|
“Measurement of the Indirect Band Gap of Diamond with EELS in STEM”. Korneychuk S, Guzzinati G, Verbeeck J, Physica status solidi : A : applications and materials science 215, 1800318 (2018). http://doi.org/10.1002/pssa.201800318
Abstract: In this work, a simple method to measure the indirect band gap of diamond with electron energy loss spectroscopy (EELS) in transmission electron microscopy (TEM) is showed. The authors discuss the momentum space resolution achievable with EELS and the possibility of deliberately selecting specific transitions of interest. Based on a simple 2 parabolic band model of the band structure, the authors extend our predictions from the direct band gap case discussed in previous work, to the case of an indirect band gap. Finally, the authors point out the emerging possibility to partly reconstruct the band structure with EELS exploiting our simplified model of inelastic scattering and support it with experiments on diamond.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.775
Times cited: 6
DOI: 10.1002/pssa.201800318
|
|
|
“Small-moment paramagnetism and extensive twinning in the topochemically reduced phase Sr2ReLiO5.5”. Hasanli N, Gauquelin N, Verbeeck J, Hadermann J, Hayward MA, Journal of the Chemical Society : Dalton transactions 47, 15783 (2018). http://doi.org/10.1039/C8DT03463J
Abstract: Reaction of the cation-ordered double perovskite Sr2ReLiO6 with dilute hydrogen at 475 degrees C leads to the topochemical deintercalation of oxide ions from the host lattice and the formation of a phase of composition Sr2ReLiO5.5, as confirmed by thermogravimetric and EELS data. A combination of neutron and electron diffraction data reveals the reduction process converts the -Sr2O2-ReLiO4-Sr2O2-ReLiO4- stacking sequence of the parent phase into a -Sr2O2-ReLiO3-Sr2O2-ReLiO4-, partially anion-vacant ordered sequence. Furthermore a combination of electron diffraction and imaging reveals Sr2ReLiO5.5 exhibits extensive twinning – a feature which can be attributed to the large, anisotropic volume expansion of the material on reduction. Magnetisation data reveal a strongly reduced moment of (eff) = 0.505(B) for the d(1) Re6+ centres in the phase, suggesting there remains a large orbital component to the magnetism of the rhenium centres, despite their location in low symmetry coordination environments.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.029
DOI: 10.1039/C8DT03463J
|
|
|
“The role of MOFs in Thin-Film Nanocomposite (TFN) membranes”. Van Goethem C, Verbeke R, Pfanmoeller M, Koschine T, Dickmann M, Timpel-Lindner T, Egger W, Bals S, Vankelecom IFJ, Journal of membrane science 563, 938 (2018). http://doi.org/10.1016/J.MEMSCI.2018.06.040
Abstract: Incorporation of MOFs in interfacially polymerized Thin-Film Nanocomposite (TFN) membranes has widely been shown to result in increased membrane performance. However, the exact functioning of these membranes is poorly understood as large variability in permeance increase, filler incorporation and rejection changes can be observed in literature. The synthesis and functioning of TFN membranes (herein exemplified by ZIF-8 filled polyamide (PA) membranes prepared via the EFP method) was investigated via targeted membrane synthesis and thorough characterization via STEM-EDX, XRD and PALS. It is hypothesized that the acid generated during the interfacial polymerization (IP) at least partially degrades the crystalline, acid-sensitive ZIF-8 and that this influences the membrane formation (through so-called secondary effects, i.e. not strictly linked to the pore morphology of the MOF). Nanoscale HAADF-STEM imaging and STEM-EDX Zn-mapping revealed no ZIF-8 particles but rather the presence of randomly shaped regions with elevated Zn-content. Also XRD failed to show the presence of crystalline areas in the composite PA films. As the addition of the acid-quenching TEA led to an increase in the diffraction signal observed in XRD, the role of the acid was confirmed. The separate addition of dissolved Zn2+ to the synthesis of regular TFC membranes showed an increase in permeance while losing some salt retention, similar to observations regularly made for TFN membranes. While the addition of a porous material to a TFC membrane is a straightforward concept, all obtained results indicate that the synthesis and performance of such composite membranes is often more complex than commonly accepted.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.035
Times cited: 84
DOI: 10.1016/J.MEMSCI.2018.06.040
|
|
|
“Removal of arsenic and mercury species from water by covalent triazine framework encapsulated \gamma-Fe2O3 nanoparticles”. Leus K, Folens K, Nicomel NR, Perez JPH, Filippousi M, Meledina M, Dirtu MM, Turner S, Van Tendeloo G, Garcia Y, Du Laing G, Van Der Voort P, Journal of hazardous materials 353, 312 (2018). http://doi.org/10.1016/J.JHAZMAT.2018.04.027
Abstract: The covalent triazine framework, CTF-1, served as host material for the in situ synthesis of Fe2O3 nanoparticles. The composite material consisted of 20 +/- 2 m% iron, mainly in gamma-Fe2O3 phase. The resulting gamma-Fe2O3@CTF-1 was examined for the adsorption of As-III, As-V and H-II from synthetic solutions and real surface-, ground- and wastewater. The material shows excellent removal efficiencies, independent from the presence of Ca2+, Mg2+ or natural organic matter and only limited dependency on the presence of phosphate ions. Its adsorption capacity towards arsenite (198.0 mg g(-1)), arsenate (102.3 mg g(-1)) and divalent mercury (165.8 mg g(-1)) belongs amongst the best-known adsorbents, including many other iron-based materials. Regeneration of the adsorbent can be achieved for use over multiple cycles without a decrease in performance by elution at 70 degrees C with 0.1 M NaOH, followed by a stirring step in a 5 m% H2O2 solution for As or 0.1 M thiourea and 0.001 M HCl for Hg. In highly contaminated water (100 mu gL(-1)), the adsorbent polishes the water quality to well below the current WHO limits.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.065
Times cited: 22
DOI: 10.1016/J.JHAZMAT.2018.04.027
|
|
|
“Kinetics of lifetime changes in bimetallic nanocatalysts revealed by quick X-ray absorption spectroscopy”. Filez M, Poelman H, Redekop EA, Galvita VV, Alexopoulos K, Meledina M, Ramachandran RK, Dendooven J, Detavernier C, Van Tendeloo G, Safonova OV, Nachtegaal M, Weckhuysen BM, Marin GB, Angewandte Chemie: international edition in English 57, 12430 (2018). http://doi.org/10.1002/ANIE.201806447
Abstract: Alloyed metal nanocatalysts are of environmental and economic importance in a plethora of chemical technologies. During the catalyst lifetime, supported alloy nanoparticles undergo dynamic changes which are well-recognized but still poorly understood. High-temperature O-2-H-2 redox cycling was applied to mimic the lifetime changes in model Pt13In9 nanocatalysts, while monitoring the induced changes by insitu quick X-ray absorption spectroscopy with one-second resolution. The different reaction steps involved in repeated Pt13In9 segregation-alloying are identified and kinetically characterized at the single-cycle level. Over longer time scales, sintering phenomena are substantiated and the intraparticle structure is revealed throughout the catalyst lifetime. The insitu time-resolved observation of the dynamic habits of alloyed nanoparticles and their kinetic description can impact catalysis and other fields involving (bi)metallic nanoalloys.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 11.994
Times cited: 4
DOI: 10.1002/ANIE.201806447
|
|
|
“Interfacial oxidation and photoluminescence of InP-Based core/shell quantum dots”. Tessier MD, Baquero EA, Dupont D, Grigel V, Bladt E, Bals S, Coppel Y, Hens Z, Nayral C, Delpech F, Chemistry of materials 30, 6877 (2018). http://doi.org/10.1021/ACS.CHEMMATER.8B03117
Abstract: Indium phosphide colloidal quantum dots (QDs) are emerging as an efficient cadmium-free alternative for optoelectronic applications. Recently, syntheses based on easy-to-implement aminophosphine precursors have been developed. We show by solid-state nuclear magnetic resonance spectroscopy that this new approach allows oxide-free indium phosphide core or core/shell quantum dots to be made. Importantly, the oxide-free core/shell interface does not help in achieving higher luminescence efficiencies. We demonstrate that in the case of InP/ZnS and InP/ZnSe QDs, a more pronounced oxidation concurs with a higher photoluminescence efficiency. This study suggests that a II-VI shell on a III-V core generates an interface prone to defects. The most efficient InP/ZnS or InP/ZnSe QDs are therefore made with an oxide buffer layer between the core and the shell: it passivates these interface defects but also results in a somewhat broader emission line width.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 74
DOI: 10.1021/ACS.CHEMMATER.8B03117
|
|
|
“Influence of artificial pinning centers on structural and superconducting properties of thick YBCO films on ABAD-YSZ templates”. Pahlke P, Sieger M, Ottolinger R, Lao M, Eisterer M, Meledin A, Van Tendeloo G, Haenisch J, Holzapfel B, Schultz L, Nielsch K, Huehne R, Superconductor science and technology 31, 044007 (2018). http://doi.org/10.1088/1361-6668/AAAFBE
Abstract: Recent efforts in the development of YBa2Cu3O7-x (YBCO) coated conductors are devoted to the increase of the critical current I-c in magnetic fields. This is typically realized by growing thicker YBCO layers as well as by the incorporation of artificial pinning centers. We studied the growth of doped YBCO layers with a thickness of up to 7 mu m using pulsed laser deposition with a growth rate of about 1.2 nm s(-1). Industrially fabricated ion-beam textured YSZ templates based on metal tapes were used as substrates for this study. The incorporation of BaHfO3 (BHO) or Ba2Y(Nb0.5Ta0.5)O-6 (BYNTO) secondary phase additions leads to a denser microstructure compared to undoped films. A purely c-axis-oriented YBCO growth is preserved up to a thickness of about 4 mu m, whereas misoriented texture components were observed in thicker films. The critical temperature is slightly reduced compared to undoped films and independent of film thickness. The critical current density J(c) of the BHO- and BYNTO-doped YBCO layers is lower at 77 K and self-field compared to pure YBCO layers; however, I-c increases up to a thickness of 5 mu m. A comparison between films with a thickness of 1.3 mu m revealed that the anisotropy of the critical current density J(c)(theta) strongly depends on the incorporated pinning centers. Whereas BHO nanorods lead to a strong B vertical bar vertical bar c-axis peak, the overall anisotropy is significantly reduced by the incorporation of BYNTO forming a mixture of short c-axis-oriented nanorods and small (a-b)-oriented platelets. As a result, the J(c) values of the doped films outperform the undoped samples at higher fields and lower temperatures for most magnetic field directions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.878
Times cited: 9
DOI: 10.1088/1361-6668/AAAFBE
|
|
|
“Incommensurately modulated structures and luminescence properties of the AgxSm(2-x)/3WO4 (x=0.286, 0.2) scheelites as thermographic phosphors”. Morozov V, Deyneko D, Basoyich O, Khaikina EG, Spassky D, Morozov A, Chernyshev V, Abakumov A, Hadermann J, Chemistry of materials 30, 4788 (2018). http://doi.org/10.1021/ACS.CHEMMATER.8B02029
Abstract: Ag+ for Sm3+ substitution in the scheelite-type AgxSm(2-x)/3 square(1-2x)/3WO4 tungstates has been investigated for its influence on the cation-vacancy ordering and luminescence properties. A solid state method was used to synthesize the x = 0.286 and x = 0.2 compounds, which exhibited (3 + 1)D incommensurately modulated structures in the transmission electron microscopy study. Their structures were refined using high resolution synchrotron powder X-ray diffraction data. Under near-ultraviolet light, both compounds show the characteristic emission lines for (4)G(5/2) -> H-6(J) (J = 5/2, 7/2, 9/2, and 11/2) transitions of the Sm3+ ions in the range 550-720 nm, with the J = 9/2 transition at the similar to 648 nm region being dominant for all photoluminescence spectra. The intensities of the (4)G(5/2) -> H-6(9/2) and (4)G(5/2) -> H-6(7/2) bands have different temperature dependencies. The emission intensity ratios (R) for these bands vary reproducibly with temperature, allowing the use of these materials as thermographic phosphors.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 2
DOI: 10.1021/ACS.CHEMMATER.8B02029
|
|
|
“Ferrimagnetism as a consequence of unusual cation ordering in the Perovskite SrLa2FeCoSbO9”. Tang Y, Hunter EC, Battle PD, Hendrickx M, Hadermann J, Cadogan JM, Inorganic chemistry 57, 7438 (2018). http://doi.org/10.1021/ACS.INORGCHEM.8B01012
Abstract: A polycrystalline sample of SrLa2FeCoSbO9 has been prepared in a solid-state reaction and studied by a combination of electron microscopy, magnetometry, Mossbauer spectroscopy, X-ray diffraction, and neutron diffraction. The compound adopts a monoclinic (space group P2(1)/n; a = 5.6218(6), b = 5.6221(6), c = 7.9440(8) angstrom, beta = 90.050(7)degrees at 300 K) perovskite-like crystal structure with two crystallographically distinct six-coordinate sites. One of these sites is occupied by 2/3 Co-2(+),1/3 Fe3+ and the other by 2/3 Sb5+, 1/3 Fe3+. This pattern of cation ordering results in a transition to a ferrimagnetic phase at 215 K. The magnetic moments on nearest-neighbor, six-coordinate cations align in an antiparallel manner, and the presence of diamagnetic Sb5+ on only one of the two sites results in a nonzero remanent magnetization of similar to 1 mu(B) per formula unit at 5 K.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 6
DOI: 10.1021/ACS.INORGCHEM.8B01012
|
|
|
“Fe-containing magnesium aluminate support for stability and carbon control during methane reforming”. Theofanidis SA, Galvita VV, Poelman H, Dharanipragada NVRA, Longo A, Meledina M, Van Tendeloo G, Detavernier C, Marin GB, ACS catalysis 8, 5983 (2018). http://doi.org/10.1021/ACSCATAL.8B01039
Abstract: We report a MgFexAl2-xO4 synthetic spinel, where x varies from 0 to 0.26, as support for Ni-based catalysts, offering stability and carbon control under various conditions of methane reforming. By incorporation of Fe into a magnesium aluminate spine!, a support is created with redox functionality and high thermal stability, as concluded from temporal analysis of products (TAP) experiments and redox cycling, respectively. A diffusion coefficient of 3 x 10(-17) m(2) s(-1) was estimated for lattice oxygen at 993 K from TAP experiments. X-ray diffraction (XRD) and extended X-ray absorption fine structure (EXAFS) modeling identified that the incorporation of iron occurs as Fe3+ in the octahedral sites of the spinel lattice, replacing aluminum. Simulation of the X-ray absorption near edge structure (XANES) spectrum of the reduced support showed that 60 +/- 10% of iron was reduced from 3+ to 2+ at 1073 K, while there was no formation of metallic iron. A series of Ni/MgFexAl2-xO4 catalysts, where x varies from 0 to 0.26, was synthesized and reduced, yielding a supported Ni-Fe alloy. The evolution of the catalyst structure during H-2 temperature-programmed reduction (TPR) and CO2 temperature-programmed oxidation (TPO) was examined using time-resolved in situ XRD and XANES. During reforming, iron in both the support and alloy keeps control of carbon accumulation, as confirmed by O-2-TPO on the spent catalysts. By fine tuning the amount of Fe in MgFexAl2-xO4, a supported alloy was obtained with a Ni/Fe molar ratio of similar to 10, which was active for reforming and stable. By comparison of the performance of Ni-based catalysts with Fe either incorporated into or deposited onto the support, the location of Fe within the support proved crucial for the stability and carbon mitigation under reforming conditions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 10.614
Times cited: 18
DOI: 10.1021/ACSCATAL.8B01039
|
|
|
“Effect of Bimetallic Pd/Pt Clusters on the Sensing Properties of Nanocrystalline SnO2 in the Detection of CO”. Malkov I V, Krivetskii VV, Potemkin D I, Zadesenets A V, Batuk MM, Hadermann J, Marikutsa A V, Rumyantseva MN, Gas'kov AM, Russian journal of inorganic chemistry 63, 1007 (2018). http://doi.org/10.1134/S0036023618080168
Abstract: Nanocrystalline tin dioxide modified by Pd and Pt clusters or by bimetallic PdPt nanoparticles was synthesized. Distribution of the modifers on the SnO2 surface was studied by high-resolution transmission electron microscopy and energy dispersive X-ray microanalysis with element distribution mapping. It was shown that the Pd/Pt ratio in bimetallic particles varies over a broad range and does not depend on the particle diameter. The effect of platinum metals on the reducibility of nanocrystalline SnO2 by hydrogen was determined. The sensing properties of the resulting materials towards 6.7 ppm CO in air were estimated in situ by electrical conductivity measurements. The sensor response of SnO2 modified with bimetallic PdPt particles was a superposition of the signals of samples with Pt and Pd clusters.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.787
Times cited: 3
DOI: 10.1134/S0036023618080168
|
|
|
“Dopant-induced electron localization drives CO2 reduction to C2 hydrocarbons”. Zhou Y, Che F, Liu M, Zou C, Liang Z, De Luna P, Yuan H, Li J, Wang Z, Xie H, Li H, Chen P, Bladt E, Quintero-Bermudez R, Sham T-K, Bals S, Hofkens J, Sinton D, Chen G, Sargent EH, Nature chemistry 10, 974 (2018). http://doi.org/10.1038/S41557-018-0092-X
Abstract: The electrochemical reduction of CO2 to multi-carbon products has attracted much attention because it provides an avenue to the synthesis of value-added carbon-based fuels and feedstocks using renewable electricity. Unfortunately, the efficiency of CO2 conversion to C-2 products remains below that necessary for its implementation at scale. Modifying the local electronic structure of copper with positive valence sites has been predicted to boost conversion to C-2 products. Here, we use boron to tune the ratio of Cu delta+ to Cu-0 active sites and improve both stability and C-2-product generation. Simulations show that the ability to tune the average oxidation state of copper enables control over CO adsorption and dimerization, and makes it possible to implement a preference for the electrosynthesis of C-2 products. We report experimentally a C-2 Faradaic efficiency of 79 +/- 2% on boron-doped copper catalysts and further show that boron doping leads to catalysts that are stable for in excess of similar to 40 hours while electrochemically reducing CO2 to multi-carbon hydrocarbons.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 25.87
Times cited: 700
DOI: 10.1038/S41557-018-0092-X
|
|
|
“Deactivation of Sn-Beta during carbohydrate conversion”. van der Graaf WNP, Tempelman CHL, Hendriks FC, Ruiz-Martinez J, Bals S, Weckhuysen BM, Pidko EA, Hensen EJM, Applied catalysis : A : general 564, 113 (2018). http://doi.org/10.1016/J.APCATA.2018.07.023
Abstract: The deactivation of Sn-Beta zeolite catalyst during retro-aldolization and isomerization of glucose is investigated. Confocal fluorescence microscopy reveals that retro-aldolization of glucose in CH3OH at 160 degrees C is accompanied with the build-up of insoluble oligomeric deposits in the micropores, resulting in a rapid catalyst deactivation. These deposits accumulate predominantly in the outer regions of the zeolite crystals, which points to mass transport limitations. Glucose isomerization in water is not only accompanied by the formation of insoluble deposits in the micropores, but also by the structural degradation of the zeolite due to desilication and destannation. Enhanced and sustained catalytic performance can be achieved by using ethanol/water mixtures as the reaction solvent instead of water.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.339
Times cited: 25
DOI: 10.1016/J.APCATA.2018.07.023
|
|
|
“Complex Magnetic Ordering in the Oxide Selenide Sr2Fe3Se2O3”. Cassidy SJ, Orlandi F, Manuel P, Hadermann J, Scrimshire A, Bingham PA, Clarke SJ, Inorganic chemistry 57, 10312 (2018). http://doi.org/10.1021/ACS.INORGCHEM.8B01542
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 2
DOI: 10.1021/ACS.INORGCHEM.8B01542
|
|
|
“Can surface reactivity of mixed crystals be predicted from their counterparts? A case study of (Bi1-xSbx)2Te3 topological insulators”. Volykhov AA, Sanchez-Barriga J, Batuk M, Callaert C, Hadermann J, Sirotina AP, Neudachina VS, Belova AI, Vladimirova NV, Tamm ME, Khmelevsky NO, Escudero C, Perez-Dieste V, Knop-Gericke A, Yashina LV, Journal of materials chemistry C : materials for optical and electronic devices 6, 8941 (2018). http://doi.org/10.1039/C8TC02235F
Abstract: The behavior of ternary mixed crystals or solid solutions and its correlation with the properties of their binary constituents is of fundamental interest. Due to their unique potential for application in future information technology, mixed crystals of topological insulators with the spin-locked, gapless states on their surfaces attract huge attention of physicists, chemists and material scientists. (Bi1-xSbx)(2)Te-3 solid solutions are among the best candidates for spintronic applications since the bulk carrier concentration can be tuned by varying x to obtain truly bulk-insulating samples, where the topological surface states largely contribute to the transport and the realization of the surface quantum Hall effect. As this ternary compound will be evidently used in the form of thin-film devices its chemical stability is an important practical issue. Based on the atomic resolution HAADF-TEM and EDX data together with the XPS results obtained both ex situ and in situ, we propose an atomistic picture of the mixed crystal reactivity compared to that of its binary constituents. We find that the surface reactivity is determined by the probability of oxygen attack on the Te-Sb bonds, which is directly proportional to the number of Te atoms bonded to at least one Sb atom. The oxidation mechanism includes formation of an amorphous antimony oxide at the very surface due to Sb diffusion from the first two quintuple layers, electron tunneling from the Fermi level of the crystal to oxygen, oxygen ion diffusion to the crystal, and finally, slow Te oxidation to the +4 oxidation state. The oxide layer thickness is limited by the electron transport, and the overall process resembles the Cabrera-Mott mechanism in metals. These observations are critical not only for current understanding of the chemical reactivity of complex crystals, but also to improve the performance of future spintronic devices based on topological materials.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.256
Times cited: 3
DOI: 10.1039/C8TC02235F
|
|
|
“Atomic-scale quantification of charge densities in two-dimensional materials”. Müller-Caspary K, Duchamp M, Roesner M, Migunov V, Winkler F, Yang H, Huth M, Ritz R, Simson M, Ihle S, Soltau H, Wehling T, Dunin-Borkowski RE, Van Aert S, Rosenauer A, Physical review B 98, 121408 (2018). http://doi.org/10.1103/PHYSREVB.98.121408
Abstract: The charge density is among the most fundamental solid state properties determining bonding, electrical characteristics, and adsorption or catalysis at surfaces. While atomic-scale charge densities have as yet been retrieved by solid state theory, we demonstrate both charge density and electric field mapping across a mono-/bilayer boundary in 2D MoS2 by momentum-resolved scanning transmission electron microscopy. Based on consistency of the four-dimensional experimental data, statistical parameter estimation and dynamical electron scattering simulations using strain-relaxed supercells, we are able to identify an AA-type bilayer stacking and charge depletion at the Mo-terminated layer edge.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 10
DOI: 10.1103/PHYSREVB.98.121408
|
|
|
“The atomic lensing model: new opportunities for atom-by-atom metrology of heterogeneous nanomaterials”. van den Bos KHW, Janssens L, De Backer A, Nellist PD, Van Aert S, Ultramicroscopy 203, 155 (2019). http://doi.org/10.1016/j.ultramic.2018.12.004
Abstract: The atomic lensing model has been proposed as a promising method facilitating atom-counting in heterogeneous nanocrystals [1]. Here, image simulations will validate the model, which describes dynamical diffraction as a superposition of individual atoms focussing the incident electrons. It will be demonstrated that the model is reliable in the annular dark field regime for crystals having columns containing dozens of atoms. By using the principles of statistical detection theory, it will be shown that this model gives new opportunities for detecting compositional differences.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.843
Times cited: 4
DOI: 10.1016/j.ultramic.2018.12.004
|
|