“Ba2Y(Nb/Ta)O6–Doped YBCO Films on Biaxially Textured Ni–5at.% W Substrates”. Sieger M, Pahlke P, Hanisch J, Sparing M, Bianchetti M, MacManus-Driscoll J, Lao M, Eisterer M, Meledin A, Van Tendeloo G, Nast R, Schultz L, Holzapfel B, Huhne R, IEEE transactions on applied superconductivity 26, 1 (2016). http://doi.org/10.1109/TASC.2016.2539254
Abstract: The incorporation of nanoscaled pinning centers in superconducting YBa2Cu3O7-d (YBCO) films is one of the core topics to enhance the critical current density Jc(B, Q) of coated conductors. The mixed double-perovskite Ba2Y(Nb/Ta)O6 (BYNTO) can be grown in nanosized columns parallel the YBCO c-axis and in step-like patterns, making it customizable to meet specific working conditions (T, B, Q). We compare a 1.6 μm thick film of pure YBCO and a similar film with additional 5 mol% of BYNTO, grown by pulsed laser deposition with a growth rate of 1.6 nm/s on buffered biaxially textured Ni-5at.% W tape. Our doped sample shows nanosized BYNTO columns parallel cYBCO and plates in the ab-plane containing Y, Nb and Ta. An improved homogeneity of the critical current density Jc over the sample was evaluated from trapped field profiles measured with a scanning Hall probe microscope. The mean Jc in rolling direction of the tape is 1.8 MA/cm² (77 K, self-field) and doubles the value of the undoped sample. Angular dependent measurements of the critical current density, Jc(Q), show a decreased anisotropy of the doped film for various magnetic fields at 77 K as well as 64 K.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 6
DOI: 10.1109/TASC.2016.2539254
|
|
|
“Self-Assembly of Pluronic F127—Silica Spherical Core–Shell Nanoparticles in Cubic Close-Packed Structures”. Kerkhofs S, Willhammar T, Van Den Noortgate H, Kirschhock CEA, Breynaert E, Van Tendeloo G, Bals S, Martens JA, Chemistry of materials 27, 5161 (2015). http://doi.org/10.1021/acs.chemmater.5b01772
Abstract: A new ordered mesoporous silica material (COK-19) with cubic symmetry is synthesized by silicate polycondensation in a citric acid/citrate buffered micellar solution of Pluronic F127 triblock copolymer near neutral pH. SAXS, nitrogen adsorption, TEM, and electron tomography reveal the final material has a cubic close packed symmetry (Fm3̅m) with isolated spherical mesopores interconnected through micropores. Heating of the synthesis medium from room temperature to 70 °C results in a mesopore size increase from 7.0 to 11.2 nm. Stepwise addition of the silicate source allows isolation of a sequence of intermediates that upon characterization with small-angle X-ray scattering uncovers the formation process via formation and aggregation of individual silica-covered Pluronic micelles.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 39
DOI: 10.1021/acs.chemmater.5b01772
|
|
|
“New insights in the formation of combined zeolitic/mesoporous materials by using a one-pot templating synthesis”. Vernimmen J, Meynen V, Herregods SJF, Mertens M, Lebedev OI, Van Tendeloo G, Cool P, European journal of inorganic chemistry , 4234 (2011). http://doi.org/10.1002/ejic.201100268
Abstract: Zeolitic growth is often absent or occurs in separate phases when synthetic strategies based on the combination of zeolite templates and mesopore templating agents are applied. In this work, zeolitic growth and mesopore formation have been investigated at different temperatures by applying a one-pot templating approach, based on a TS-1 zeolite synthesis whereby part of the microtemplate (tetrapropylammonium hydroxide, TPAOH) is replaced by a mesotemplate (hexadecyltrimethylammonium bromide, CTMABr). Moreover, the synthesis duration and the molar ratio of the microtemplate/mesotemplate have also been studied. The different syntheses clearly show the inherent competitive mechanism between zeolitic growth and mesopore formation. These insights have led to the conclusion that by following a one-pot templating strategy with standard, nonexotic commercial templates, i.e. CTMABr and TPAOH, it is not possible to develop a true hierarchical mesoporous zeolite, meaning a mesoporous siliceous material with highly crystalline zeolitic walls. The resultant materials are instead combined zeolitic/mesoporous composite structures with, however, highly tuneable and controllable porosity characteristics.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 2.444
Times cited: 7
DOI: 10.1002/ejic.201100268
|
|
|
“Novel complex stacking of fully-ordered transition metal layers in Li4FeSbO6 materials”. McCalla E, Abakumov A, Rousse G, Reynaud M, Sougrati MT, Budic B, Mahmoud A, Dominko R, Van Tendeloo G, Hermann RP, Tarascon JM;, Chemistry of materials 27, 1699 (2015). http://doi.org/10.1021/cm504500a
Abstract: As part of a broad project to explore Li4MM'O-6 materials (with M and M' being selected from a wide variety of metals) as positive electrode materials for Li-ion batteries, the structures of Li4FeSbO6 materials with both stoichiometric and slightly deficient lithium contents are studied here. For lithium content varying from 3.8 to 4.0, the color changes from yellow to black and extra superstructure peaks are seen in the XRD patterns. These extra peaks appear as satellites around the four superstructure peaks affected by the stacking of the transition metal atoms. Refinements of both XRD and neutron scattering patterns show a nearly perfect ordering of Li, Fe, and Sb in the transition metal layers of all samples, although these refinements must take the stacking faults into account in order to extract information about the structure of the TM layers. The structure of the most lithium rich sample, where the satellite superstructure peaks are seen, was determined with the help of HRTEM, XRD, and neutron scattering. The satellites arise due to a new stacking sequence where not all transition metal layers are identical but instead two slightly different compositions stack in an AABB sequence giving a unit cell that is four times larger than normal for such monoclinic layered materials. The more lithium deficient samples are found to contain metal site vacancies based on elemental analysis and Mossbauer spectroscopy results. The significant changes in physical properties are attributed to the presence of these vacancies. This study illustrates the great importance of carefully determining the final compositions in these materials, as very small differences in compositions may have large impacts on structures and properties.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 22
DOI: 10.1021/cm504500a
|
|
|
“3D Magnetic Induction Maps of Nanoscale Materials Revealed by Electron Holographic Tomography”. Wolf D, Rodriguez LA, Béché, A, Javon E, Serrano L, Magen C, Gatel C, Lubk A, Lichte H, Bals S, Van Tendeloo G, Fernández-Pacheco A, De Teresa JM, Snoeck E, Chemistry of materials 27, 6771 (2015). http://doi.org/10.1021/acs.chemmater.5b02723
Abstract: The investigation of three-dimensional (3D) ferromagnetic nanoscale materials constitutes one of the key research areas of the current magnetism roadmap, and carries great potential to impact areas such as data storage, sensing and biomagnetism. The properties of such nanostructures are closely connected with their 3D magnetic nanostructure, making their determination highly valuable. Up to now, quantitative 3D maps providing both the internal magnetic and electric configuration of the same specimen with high spatial resolution are missing. Here, we demonstrate the quantitative 3D reconstruction of the dominant axial component of the magnetic induction and electrostatic potential within a cobalt nanowire (NW) of 100 nm in diameter with spatial resolution below 10 nanometers by applying electron holographic tomography. The tomogram was obtained using a dedicated TEM sample holder for acquisition, in combination with advanced alignment and tomographic reconstruction routines. The powerful approach presented here is widely applicable to a broad range of 3D magnetic nanostructures and may trigger the progress of novel spintronic non-planar nanodevices.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 50
DOI: 10.1021/acs.chemmater.5b02723
|
|
|
“Li2Cu2O(SO4)2: a possible electrode for sustainable Li-based batteries showing a 4.7 V redox activity vs Li+/Li0”. Sun M, Rousse G, Abakumov AM, Saubanere M, Doublet M-L, Rodriguez-Carvajal J, Van Tendeloo G, Tarascon J-M, Chemistry of materials 27, 3077 (2015). http://doi.org/10.1021/acs.chemmater.5b00588
Abstract: Li-ion batteries rely on the use of insertion positive electrodes with performances scaling with the redox potential of the 31) metals accompanying Liuptake/removal. Although not commonly studied, the Cu2+/Cu3+ redox potential has been predicted from theoretical calculations to possibly offer a high operating voltage redox couple. We herein report the synthesis and crystal structure of a hitherto-unknown oxysulfate phase, Li2Cu2O(SO4)(2), which contains infinite edgesharing CuO4 chains and presents attractive electrochemical redox activity with respect to Li+/Li, namely amphoteric characteristics. Li2Cu2O(SO4)(2) shows redox activity at 4.7 V vs Li+/Li corresponding to the oxidation of Cu2+ to Cu3+ enlisting ligand holes and associated with the reversible uptake-removal of 0.3 Li. Upon reduction, this compound reversibly uptakes similar to 2 Li at an average potential of about 2.5 V vs Li+/Li, associated with the Cu2+/Cu+ redox couple. The mechanism of the reactivity upon reduction is discussed in detail, with particular attention to the occasional appearance of an oscillation wave in the discharge profile. Our work demonstrates that Cu-based compounds can indeed be fertile scientific ground in the search for new high-energy-density electrodes.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 20
DOI: 10.1021/acs.chemmater.5b00588
|
|
|
“Influence of defect distribution on the reducibility of CeO2-x nanoparticles”. Spadaro MC, Luches P, Bertoni G, Grillo V, Turner S, Van Tendeloo G, Valeri S, D'Addato S, Nanotechnology 27, 425705 (2016). http://doi.org/10.1088/0957-4484/27/42/425705
Abstract: Ceria nanoparticles (NPs) are fundamental in heterogeneous catalysis because of their ability to store or release oxygen depending on the ambient conditions. Their oxygen storage capacity is strictly related to the exposed planes, crystallinity, density and distribution of defects. In this work a study of ceria NPs produced with a ligand-free, physical synthesis method is presented. The NP films were grown by a magnetron sputtering based gas aggregation source and studied by high resolution- and scanning-transmission electron microscopy and x-ray photoelectron spectroscopy. In particular, the influence of the oxidation procedure on the NP reducibility has been investigated. The different reducibility has been correlated to the exposed planes, crystallinity and density and distribution of structural defects. The results obtained in this work represent a basis to obtain cerium oxide NP with desired oxygen transport properties.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.44
Times cited: 11
DOI: 10.1088/0957-4484/27/42/425705
|
|
|
“Influence of substrate tilt angle on the incorporation of BaHfO3 in thick YBa2Cu3O7-&delta, films”. Sieger M, Pahlke P, Ottolinger R, Stafford BH, Lao M, Meledin A, Bauer M, Eisterer M, Van Tendeloo G, Schultz L, Nielsch K, Hühne R, IEEE transactions on applied superconductivity 27, 1 (2016). http://doi.org/10.1109/Tasc.2016.2631587
Abstract: High critical current densities can be realized in high-temperature superconductors such as YBa2Cu3O7-δ (YBCO) by controlling density, shape, size and direction of a secondary phase. Whereas the dependence on the growth rate and deposition temperature has been widely studied as key parameters for nano-engineering the pinning landscape, the vicinal tilt of the substrate surface might have an additional influence. Therefore, we deposited 6 mol% BaHfO3 (BHO) doped YBCO on SrTiO3 (STO) substrates with vicinal angles α between 0° and 40° to identify the influence of the tilt on the growth mode of BHO. An undisturbed epitaxial growth of the superconductor as well as an epitaxial integration of the BHO phase in the YBCO matrix is observed for all vicinal angles investigated. The critical temperature is constant up to α = 20°, whereas the self-field critical current density at 77 K starts to decrease above 10°. A detailed structural analysis of the film cross sections showed that the growth mode of BHO changes already for a vicinal tilt of 2° from a pure c-axis oriented growth to a layered structure with BHO aligned parallel to the YBCO ab-plane. We identified a strong influence of such a microstructure on the current flow in BHO doped YBCO films on STO substrates as well as on MgO based coated conductors prepared by inclined substrate deposition
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 3
DOI: 10.1109/Tasc.2016.2631587
|
|
|
“Epitaxial YBa2Cu3O7−xnanocomposite thin films from colloidal solutions”. Cayado P, De Keukeleere K, Garzón A, Perez-Mirabet L, Meledin A, De Roo J, Vallés F, Mundet B, Rijckaert H, Pollefeyt G, Coll M, Ricart S, Palau A, Gázquez J, Ros J, Van Tendeloo G, Van Driessche I, Puig T, Obradors X, Superconductor science and technology 28, 124007 (2015). http://doi.org/10.1088/0953-2048/28/12/124007
Abstract: A methodology of general validity to prepare epitaxial nanocomposite films based on the use of colloidal solutions containing different crystalline preformed oxide nanoparticles ( ex situ nanocomposites) is reported. The trifluoroacetate (TFA) metal–organic chemical solution deposition route is used with alcoholic solvents to grow epitaxial YBa 2 Cu 3 O 7 (YBCO) films. For this reason stabilizing oxide nanoparticles in polar solvents is a challenging goal. We have used scalable nanoparticle synthetic methodologies such as thermal and microwave-assisted solvothermal techniques to prepare CeO 2 and ZrO 2 nanoparticles. We show that stable and homogeneous colloidal solutions with these nanoparticles can be reached using benzyl alcohol, triethyleneglycol, nonanoic acid, trifluoroacetic acid or decanoic acid as protecting ligands, thereby allowing subsequent mixing with alcoholic TFA solutions. An elaborate YBCO film growth analysis of these nanocomposites allows the identification of the different relevant growth phenomena, e.g. nanoparticles pushing towards the film surface, nanoparticle reactivity, coarsening and nanoparticle accumulation at the substrate interface. Upon mitigation of these effects, YBCO nanocomposite films with high self-field critical currents ( J c ∼ 3–4 MA cm −2 at 77 K) were reached, indicating no current limitation effects associated with epitaxy perturbation, while smoothed magnetic field dependences of the critical currents at high magnetic fields and decreased effective anisotropic pinning behavior confirm the effectiveness of the novel developed approach to enhance vortex pinning. In conclusion, a novel low cost solution-derived route to high current nanocomposite superconducting films and coated conductors has been developed with very promising features.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.878
Times cited: 32
DOI: 10.1088/0953-2048/28/12/124007
|
|
|
“Plasmon mapping in Au@Ag nanocube assemblies”. Goris B, Guzzinati G, Fernández-López C, Pérez-Juste J, Liz-Marzán LM, Trügler A, Hohenester U, Verbeeck J, Bals S, Van Tendeloo G, The journal of physical chemistry: C : nanomaterials and interfaces 118, 15356 (2014). http://doi.org/10.1021/jp502584t
Abstract: Surface plasmon modes in metallic nanostructures largely determine their optoelectronic properties. Such plasmon modes can be manipulated by changing the morphology of the nanoparticles or by bringing plasmonic nanoparticle building blocks close to each other within organized assemblies. We report the EELS mapping of such plasmon modes in pure Ag nanocubes, Au@Ag coreshell nanocubes, and arrays of Au@Ag nanocubes. We show that these arrays enable the creation of interesting plasmonic structures starting from elementary building blocks. Special attention will be dedicated to the plasmon modes in a triangular array formed by three nanocubes. Because of hybridization, a combination of such nanotriangles is shown to provide an antenna effect, resulting in strong electrical field enhancement at the narrow gap between the nanotriangles.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.536
Times cited: 41
DOI: 10.1021/jp502584t
|
|
|
“Synthesis of highly stable pure-silica thin-walled hexagonally ordered mesoporous material”. Verlooy P, Aerts A, Lebedev OI, Van Tendeloo G, Kirschhock C, Martens JA, Chemical communications , 4287 (2009). http://doi.org/10.1039/b901796h
Abstract: Hexagonally ordered mesoporous silica with a very narrow mesopore size distribution and exceptionally high stability paired with unusually thin pore walls was prepared using piperidine and cetyltrimethylammonium bromide.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.319
Times cited: 17
DOI: 10.1039/b901796h
|
|
|
“Atomic and electronic structures of BaHfO3-doped TFA-MOD-derived YBa2Cu3O7−δthin films”. Molina-Luna L, Duerrschnabel M, Turner S, Erbe M, Martinez GT, Van Aert S, Holzapfel B, Van Tendeloo G, Superconductor science and technology 28, 115009 (2015). http://doi.org/10.1088/0953-2048/28/11/115009
Abstract: Tailoring the properties of oxide-based nanocomposites is of great importance for a wide range of materials relevant for energy technology. YBa2Cu3O7−δ (YBCO) superconducting thin films containing nanosized BaHfO3 (BHO) particles yield a significant improvement of the magnetic flux pinning properties and a reduced anisotropy of the critical current density. These films were prepared by chemical solution deposition (CSD) on (100) SrTiO3 (STO) substrates yielding critical current densities up to 3.6 MA cm−2 at 77 K and self-field. Transport in-field J c measurements demonstrated a high pinning force maximum of around 6 GN/m3 for a sample annealed at T = 760 °C that has a doping of 12 mol% of BHO. This sample was investigated by scanning transmission electron microscopy (STEM) in combination with electron energy-loss spectroscopy (EELS) yielding strain and spectral maps. Spherical BHO nanoparticles of 15 nm in size were found in the matrix, whereas the particles at the interface were flat. A 2 nm diffusion layer containing Ti was found at the YBCO (BHO)/STO interface. Local lattice deformation mapping at the atomic scale revealed crystal defects induced by the presence of both sorts of BHO nanoparticles, which can act as pinning centers for magnetic flux lines. Two types of local lattice defects were identified and imaged: (i) misfit edge dislocations and (ii) Ba-Cu-Cu-Ba stacking faults (Y-248 intergrowths). The local electronic structure and charge transfer were probed by high energy resolution monochromated electron energy-loss spectroscopy. This technique made it possible to distinguish superconducting from non-superconducting areas in nanocomposite samples with atomic resolution in real space, allowing the identification of local pinning sites on the order of the coherence length of YBCO (~1.5 nm) and the determination of 0.25 nm dislocation cores.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.878
Times cited: 4
DOI: 10.1088/0953-2048/28/11/115009
|
|
|
“BaHfO3artificial pinning centres in TFA-MOD-derived YBCO and GdBCO thin films”. Erbe M, Hänisch J, Hühne R, Freudenberg T, Kirchner A, Molina-Luna L, Damm C, Van Tendeloo G, Kaskel S, Schultz L, Holzapfel B, Superconductor science and technology 28, 114002 (2015). http://doi.org/10.1088/0953-2048/28/11/114002
Abstract: Chemical solution deposition (CSD) is a promising way to realize REBa2Cu3O7−x (REBCO;RE = rare earth (here Y, Gd))-coated conductors with high performance in applied magnetic fields. However, the preparation process contains numerous parameters which need to be tuned to achieve high-quality films. Therefore, we investigated the growth of REBCO thin films containing nanometre-scale BaHfO3 (BHO) particles as pinning centres for magnetic flux lines, with emphasis on the influence of crystallization temperature and substrate on the microstructure and superconductivity. Conductivity, microscopy and x-ray investigations show an enhanced performance of BHO nano-composites in comparison to pristine REBCO. Further, those measurements reveal the superiority of GdBCO to YBCO—e.g. by inductive critical current densities, Jc, at self-field and 77 K. YBCO is outperformed by more than 1 MA cm−2 with Jc values of up to 5.0 MA cm−2 for 265 nm thick layers of GdBCO(BHO) on lanthanum aluminate. Transport in-field Jc measurements demonstrate high pinning force maxima of around 4 GN m−3 for YBCO(BHO) and GdBCO(BHO). However, the irreversibility fields are appreciably higher for GdBCO. The critical temperature was not significantly reduced upon BHO addition to both YBCO and GdBCO, indicating a low tendency for Hf diffusion into the REBCO matrix. Angular-dependent Jc measurements show a reduction of the anisotropy in the same order of magnitude for both REBCO compounds. Theoretical models suggest that more than one sort of pinning centre is active in all CSD films.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.878
Times cited: 36
DOI: 10.1088/0953-2048/28/11/114002
|
|
|
“Thermal Stability of CoAu13Binary Nanoparticle Superlattices under the Electron Beam”. Altantzis T, Yang Z, Bals S, Van Tendeloo G, Pileni M-P, Chemistry of materials 28, 716 (2016). http://doi.org/10.1021/acs.chemmater.5b04898
Abstract: One primary goal of self-assembly in nanoscale regime is to implement multifunctional binary nanoparticle superlattices into practical use. In the last decade, considerable effort has been put into the fabrication of binary nanoparticle superlattices with controllable structure and stoichiometry. However, limited effort has been made in order to improve the stability of these binary nanoparticle superlattices, which is a prerequisite for their potential application. In this work, we demonstrate that the carbon deposition from specimen contamination can play an auxiliary role during the heat treatment of binary nanoparticle superlattices. With the in-situ carbon matrix formation, the thermal stability of CoAu 13 binary nanoparticle superlattices is unambiguously enhanced.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 10
DOI: 10.1021/acs.chemmater.5b04898
|
|
|
“Strongly Exchange Coupled Core|Shell Nanoparticles with High Magnetic Anisotropy: A Strategy toward Rare-Earth-Free Permanent Magnets”. Lottini E, López-Ortega A, Bertoni G, Turner S, Meledina M, Van Tendeloo G, de Julián Fernández C, Sangregorio C, Chemistry of materials 28, 4214 (2016). http://doi.org/10.1021/acs.chemmater.6b00623
Abstract: Antiferromagnetic(AFM)|ferrimagnetic(FiM) core|shell (CS) nanoparticles (NPs) of formula Co0.3Fe0.7O|Co0.6Fe2.4O4 with mean diameter from 6 to 18 nm have been synthesized through a one-pot thermal decomposition process. The CS structure has been generated by topotaxial oxidation of the core region, leading to the formation of a highly monodisperse single inverted AFM|FiM CS system with variable AFM-core diameter and constant FiM-shell thickness (~2 nm). The sharp interface, the high structural matching between both phases and the good crystallinity of the AFM material have been structurally demonstrated and are corroborated by the robust exchange-coupling between AFM and FiM phases, which gives rise to one among the largest exchange bias (HE) values ever reported for CS NPs (8.6 kOe) and to a strongly enhanced coercive field (HC). In addition, the investigation of the magnetic properties as a function of the AFM-core size (dAFM), revealed a non-monotonous trend of both HC and HE, which display a maximum value for dAFM = 5 nm (19.3 and 8.6 kOe, respectively). These properties induce a huge improvement of the capability of storing energy of the material, a result which suggests that the combination of highly anisotropic AFM|FiM materials can be an efficient strategy towards the realization of novel Rare Earth-free permanent magnets.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 48
DOI: 10.1021/acs.chemmater.6b00623
|
|
|
“Strong oxygen participation in the redox governing the structural and electrochemical properties of Na-rich layered oxide Na2IrO3”. Perez AJ, Batuk D, Saubanère M, Rousse G, Foix D, Mc Calla E, J Berg E, Dugas R, van den Bos K H W, Doublet M-L, Gonbeau D, Abakumov AM, Van Tendeloo G, Tarascon J-M, Chemistry of materials 28, 8278 (2016). http://doi.org/10.1021/acs.chemmater.6b03338
Abstract: The recent revival of the Na-ion battery concept has prompted intense activities in the search for new Na-based layered oxide positive electrodes. The largest capacity to date was obtained for a Na-deficient layered oxide that relies on cationic redox processes only. To go beyond this limit, we decided to chemically manipulate these Na-based layered compounds in a way to trigger the participation of the anionic network. We herein report the electrochemical properties of a Na-rich phase Na2IrO3, which can reversibly cycle 1.5 Na+ per formula unit while not suffering from oxygen release nor cationic migrations. Such large capacities, as deduced by complementary XPS, X-ray/neutron diffraction and transmission electron microscopy measurements, arise from cumulative cationic and anionic redox processes occurring simultaneously at potentials as low as 3.0 V. The inability to remove more than 1.5 Na+ is rooted in the formation of an O1-type phase having highly stabilized Na sites as confirmed by DFT calculations, which could rationalize as well the competing metal/oxygen redox processes in Na2IrO3. This work will help to define the most fertile directions in the search for novel high energy Na-rich materials based on more sustainable elements than Ir.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 45
DOI: 10.1021/acs.chemmater.6b03338
|
|
|
“Direct visualization of atomic-scale heterogeneous structure dynamics in MnO₂, nanowires”. Peng X, Peng H, Zhao K, Zhang Y, Xia F, Lyu J, Van Tendeloo G, Sun C, Wu J, Acs Applied Materials &, Interfaces 13, 33644 (2021). http://doi.org/10.1021/ACSAMI.1C07929
Abstract: Manganese oxides are attracting great interest owing to their rich polymorphism and multiple valent states, which give rise to a wide range of applications in catalysis, capacitors, ion batteries, and so forth. Most of their functionalities are connected to transitions among the various polymorphisms and Mn valences. However, their atomic-scale dynamics is still a great challenge. Herein, we discovered a strong heterogeneity in the crystalline structure and defects, as well as in the Mn valence state. The transitions are studied by in situ transmission electron microscopy (TEM), and they involve a complex ordering of [MnO6] octahedra as the basic building tunnels. MnO2 nanowires synthesized using solution-based hydrothermal methods usually exhibit a large number of multiple polymorphism impurities with different tunnel sizes. Upon heating, MnO2 nanowires undergo a series of stoichiometric polymorphism changes, followed by oxygen release toward an oxygen-deficient spinel and rock-salt phase. The impurity polymorphism exhibits an abnormally high stability with interesting small-large-small tunnel size transition, which is attributed to a preferential stabilizer (K+) concentration, as well as a strong competition of kinetics and thermodynamics. Our results unveil the complicated intergrowth of polymorphism impurities in MnO2, which provide insights into the heterogeneous kinetics, thermodynamics, and transport properties of the tunnel-based building blocks.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 7.504
DOI: 10.1021/ACSAMI.1C07929
|
|
|
“Enhancing total conductivity of La2NiO4+\delta epitaxial thin films by reducing thickness”. Burriel M, Santiso J, Rossell MD, Van Tendeloo G, Figueras A, Garcia G, The journal of physical chemistry: C : nanomaterials and interfaces 112, 10982 (2008). http://doi.org/10.1021/jp7101622
Abstract: High quality epitaxial c axis oriented La2NiO4+ä thin films have been prepared by the pulsed injection metal organic chemical vapor deposition technique on different substrates. High-resolution electron microscopy/transmission electron microscopy has been used to confirm the high crystalline quality of the deposited films. The c-parameter evolution has been studied by XRD as a function of time and gas atmosphere. The high temperature transport properties along the basal a−b plane of epitaxial La2NiO4+ä films have been measured, and the total conductivity of the layers has been found to increase as the thickness is reduced. Layers of 50 nm and thinner have shown a maximum conductivity larger than that measured for single-crystals, in particular, the 33 nm thick films with a conductivity of 475 S/cm in oxygen correspond to the highest value measured to date for this material.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.536
Times cited: 35
DOI: 10.1021/jp7101622
|
|
|
“Influence of strain, specimen orientation and background estimation on composition evaluation of InAs/GaAs by TEM”. Rossi EHM, Van Tendeloo G, Rosenauer A, Philosophical magazine 87, 4461 (2007). http://doi.org/10.1080/14786430701551905
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.505
Times cited: 1
DOI: 10.1080/14786430701551905
|
|
|
“Nitrogen control in nanodiamond produced by detonation shock-wave-assisted synthesis”. Shenderova OA, Vlasov II, Turner S, Van Tendeloo G, Orlinskii SB, Shiryaev AA, Khomich AA, Sulyanov SN, Jelezko F, Wrachtrup J, The journal of physical chemistry: C : nanomaterials and interfaces 115, 14014 (2011). http://doi.org/10.1021/jp202057q
Abstract: Development of efficient production methods of nanodiamond (ND) particles containing substitutional nitrogen and nitrogen-vacancy (NV) complexes remains an important goal in the nanodiamond community. ND synthesized from explosives is generally not among the preferred candidates for imaging applications owing to lack of optically active particles containing NV centers. In this paper, we have systematically studied representative classes of NDs produced by detonation shock wave conversion of different carbon precursor materials, namely, graphite and a graphite/hexogen mixture into ND, as well as ND produced from different combinations of explosives using different cooling methods (wet or dry cooling). We demonstrate that (i) the N content in nanodiamond particles can be controlled through a correct selection of the carbon precursor material (addition of graphite, explosives composition); (ii) particles larger than approximately 20 nm may contain in situ produced optically active NV centers, and (iii) in ND produced from explosives, NV centers are detected only in ND produced by wet synthesis. ND synthesized from a mixture of graphite/explosive contains the largest amount of NV centers formed during synthesis and thus deserves special attention.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.536
Times cited: 54
DOI: 10.1021/jp202057q
|
|
|
“Nonlinear optical properties of Ag nanoclusters and nanoparticles dispersed in a glass host”. Mai HH, Kaydashev VE, Tikhomirov VK, Janssens E, Shestakov MV, Meledina M, Turner S, Van Tendeloo G, Moshchalkov VV, Lievens P, The journal of physical chemistry: C : nanomaterials and interfaces 118, 15995 (2014). http://doi.org/10.1021/jp502294u
Abstract: The nonlinear absorption of Ag atomic clusters and nanoparticles dispersed in a transparent oxyfluoride glass host has been studied. The as-prepared glass, containing 0.15 atom % Ag, shows an absorption band in the UV/violet attributed to the presence of amorphous Ag atomic nanoclusters with an average size of 1.2 nm. Upon heat treatment the Ag nanoclusters coalesce into larger nanoparticles that show a surface plasmon absorption band in the visible. Open aperture z-scan experiments using 480 nm nanosecond laser pulses demonstrated nonsaturated and saturated nonlinear absorption with large nonlinear absorption indices for the Ag nanoclusters and nanoparticles, respectively. These properties are promising, e.g., for applications in optical limiting and objects contrast enhancement.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.536
Times cited: 43
DOI: 10.1021/jp502294u
|
|
|
“Surfactant effects on the structural and magnetic properties of iron oxide nanoparticles”. Filippousi M, Angelakeris M, Katsikini M, Paloura E, Efthimiopoulos I, Wang Y, Zamboulis D, Van Tendeloo G, The journal of physical chemistry: C : nanomaterials and interfaces 118, 16209 (2014). http://doi.org/10.1021/jp5037266
Abstract: Iron oxide nanoparticles were prepared using the simplest and most efficient chemical route, the coprecipitation, in the absence and the presence of three different and widely used surfactants. The purpose of this study is to investigate the possible influence of the different surfactants on the structure and therefore on the magnetic properties of the iron oxide nanoparticles. Thus, different techniques were employed in order to elucidate the composition and structure of the magnetic iron oxide nanoparticles. By combining transmission electron microscopy with X-ray powder diffraction and X-ray absorption fine structure measurements, we were able to determine and confirm the crystal structure of the constituent iron oxides. The magnetic properties were investigated by measuring the hysteresis loops where the surfactant influence on their collective magnetic behavior and subsequent AC magnetic hyperthermia response is apparent. The results indicate that the produced iron oxide nanoparticles may be considered as good candidates for biomedical applications in hyperthermia treatments because of their high heating capacity exhibited under an alternating magnetic field, which is sufficient to provoke damage to the cancer cells.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.536
Times cited: 47
DOI: 10.1021/jp5037266
|
|
|
“Unique nanostructural features in Fe, Mn-doped YBCO thin films”. Meledin A, Turner S, Cayado P, Mundet B, Solano E, Ricart S, Ros J, Puig T, Obradors X, Van Tendeloo G, Superconductor science and technology 29, 125009 (2016). http://doi.org/10.1088/0953-2048/29/12/125009
Abstract: An attempt to grow a thin epitaxial composite film of YBa2Cu3O7−δ (YBCO) with spinel MnFe2O4 (MFO) nanoparticles on a LAO substrate using the CSD approach resulted in a decomposition of the spinel and various doping modes of YBCO with the Fe and Mn cations. These nanostructural effects lead to a lowering of T c and a slight J c increase in field. Using a combination of advanced transmission electron microscopy (TEM) techniques such as atomic resolution high-angle annular dark field scanning TEM, energy dispersive x-ray spectroscopy and electron energy-loss spectroscopy we have been able to decipher and characterize the effects of the Fe and Mn doping on the film architecture. The YBaCuFeO5 anion-deficient double perovskite phase was detected in the form of 3D inclusions as well as epitaxially grown lamellas within the YBCO matrix. These nano-inclusions play a positive role as pinning centers responsible for the J c/J sf (H) dependency smoothening at high magnetic fields in the YBCO-MFO films with respect to the pristine YBCO films.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.878
Times cited: 6
DOI: 10.1088/0953-2048/29/12/125009
|
|
|
“Transmission electron microscopy on interface engineered superconducting thin films”. Bals S, Van Tendeloo G, Rijnders G, Huijben M, Leca V, Blank DHA, IEEE transactions on applied superconductivity 13, 2834 (2003). http://doi.org/10.1109/TASC.2003.812023
Abstract: Transmission electron microscopy is used to evaluate different deposition techniques, which optimize the microstructure and physical properties of superconducting thin films. High-resolution electron microscopy proves that the use of an YBa2Cu2Ox buffer layer can avoid a variable interface configuration in YBa2Cu3O7-delta thin films grown on SrTiO3. The growth can also be controlled at an atomic level by, using sub-unit cell layer epitaxy, which results in films with high quality and few structural defects. Epitaxial strain in Sr0.85La0.15CuO2 infinite layer thin films influences the critical temperature of these films, as well as the microstructure. Compressive stress is released by a modulated or a twinned microstructure, which eliminates superconductivity. On the other hand, also tensile strain seems to lower the critical temperature of the infinite layer.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 13
DOI: 10.1109/TASC.2003.812023
|
|
|
“Addition of yttrium into HfO2 films: microstructure and electrical properties”. Dubourdieu C, Rauwel E, Roussel H, Ducroquet F, Hollaender B, Rossell M, Van Tendeloo G, Lhostis S, Rushworth S, Journal of vacuum science and technology: A: vacuum surfaces and films 27, 503 (2009). http://doi.org/10.1116/1.3106627
Abstract: The cubic phase of HfO2 was stabilized by addition of yttrium in thin films grown on Si/SiO2 by metal-organic chemical vapor deposition. The cubic phase was obtained for contents of 6.5 at. % Y or higher at a temperature as low as 470 °C. The complete compositional range (from 1.5 to 99.5 at. % Y) was investigated. The crystalline structure of HfO2 was determined from x-ray diffraction, electron diffraction, and attenuated total-reflection infrared spectroscopy. For cubic films, the continuous increase in the lattice parameter indicates the formation of a solid-solution HfO2Y2O3. As shown by x-ray photoelectron spectroscopy, yttrium silicate is formed at the interface with silicon; the interfacial layer thickness increases with increasing yttrium content and increasing film thickness. The dependence of the intrinsic relative permittivity r as a function of Y content was determined. It exhibits a maximum of ~30 for ~8.8 at. % Y. The cubic phase is stable upon postdeposition high-temperature annealing at 900 °C under NH3.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.374
Times cited: 29
DOI: 10.1116/1.3106627
|
|
|
“Annular dark-field transmission electron microscopy for low contrast materials”. Leroux F, Bladt E, Timmermans J-P, Van Tendeloo G, Bals S, Microscopy and microanalysis 19, 629 (2013). http://doi.org/10.1017/S1431927613000020
Abstract: Imaging soft matter by transmission electron microscopy (TEM) is anything but straightforward. Recently, interest has grown in developing alternative imaging modes that generate contrast without additional staining. Here, we present a dark-field TEM technique based on the use of an annular objective aperture. Our experiments demonstrate an increase in both contrast and signal-to-noise ratio in comparison to conventional bright-field TEM. The proposed technique is easy to implement and offers an alternative imaging mode to investigate soft matter.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.891
Times cited: 5
DOI: 10.1017/S1431927613000020
|
|
|
“CFD modelling of small particle dispersion: the influence of the turbulence kinetic energy in the atmospheric boundary layer”. Gorlé, C, van Beeck J, Rambaud P, Van Tendeloo G, Atmospheric environment : an international journal 43, 673 (2009). http://doi.org/10.1016/j.atmosenv.2008.09.060
Abstract: When considering the modelling of small particle dispersion in the lower part of the Atmospheric Boundary Layer (ABL) using Reynolds Averaged Navier Stokes simulations, the particle paths depend on the velocity profile and on the turbulence kinetic energy, from which the fluctuating velocity components are derived to predict turbulent dispersion. It is therefore important to correctly reproduce the ABL, both for the velocity profile and the turbulence kinetic energy profile. For RANS simulations with the standard kå model, Richards and Hoxey (1993. Appropriate boundary conditions for computational wind engineering models using the kå turbulence model. Journal of Wind Engineering and Industrial Aerodynamics 4647, 145153.) proposed a set of boundary conditions which result in horizontally homogeneous profiles. The drawback of this method is that it assumes a constant profile of turbulence kinetic energy, which is not always consistent with field or wind tunnel measurements. Therefore, a method was developed which allows the modelling of a horizontally homogeneous turbulence kinetic energy profile that is varying with height. By comparing simulations performed with the proposed method to simulations performed with the boundary conditions described by Richards and Hoxey (1993. Appropriate boundary conditions for computational wind engineering models using the kå turbulence model. Journal of Wind Engineering and Industrial Aerodynamics 4647, 145153.), the influence of the turbulence kinetic energy on the dispersion of small particles over flat terrain is quantified.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.629
Times cited: 79
DOI: 10.1016/j.atmosenv.2008.09.060
|
|
|
“The chirality of carbon nanotubules determined by dark-field electron microscopy”. Bernaerts D, op de Beeck M, Amelinckx S, van Landuyt J, Van Tendeloo G, Philosophical magazine: A: physics of condensed matter: defects and mechanical properties 74, 723 (1996). http://doi.org/10.1080/01418619608243538
Abstract: Multishell carbon nanotubules are studied by means of diffraction contrast dark field images. This results in an electron microscopy method for the determination of the sign of the chiral angles in carbon nanotubes. The method is justified by a reasoning either in direct space or in diffraction space. We also investigate a carbon nanotubule exhibiting a bend and we confront the observations with the heptagon-pentagon pair model.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 20
DOI: 10.1080/01418619608243538
|
|
|
“Classification and control of the origin of photoluminescence from Si nanocrystals”. Godefroo S, Hayne M, Jivanescu M, Stesmans A, Zacharias M, Lebedev OI, Van Tendeloo G, Moshchalkov VV, Nature nanotechnology 3, 174 (2008). http://doi.org/10.1038/nnano.2008.7
Abstract: Silicon dominates the electronics industry, but its poor optical properties mean that III-V compound semiconductors are preferred for photonics applications. Photoluminescence at visible wavelengths was observed from porous Si at room temperature in 1990, but the origin of these photons (do they arise from highly localized defect states or quantum confinement effects?) has been the subject of intense debate ever since. Attention has subsequently shifted from porous Si to Si nanocrystals, but the same fundamental question about the origin of the photoluminescence has remained. Here we show, based on measurements in high magnetic fields, that defects are the dominant source of light from Si nanocrystals. Moreover, we show that it is possible to control the origin of the photoluminescence in a single sample: passivation with hydrogen removes the defects, resulting in photoluminescence from quantum-confined states, but subsequent ultraviolet illumination reintroduces the defects, making them the origin of the light again.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 38.986
Times cited: 426
DOI: 10.1038/nnano.2008.7
|
|
|
“Direct observation of nanometer-scale pinning sites in (Nd0.33Eu0.20Gd0.47)Ba2Cu3O7-\delta single crystals”. Das P, Koblischka MR, Turner S, Van Tendeloo G, Wolf T, Jirsa M, Hartmann U, Europhysics letters 83, 37005 (2008). http://doi.org/10.1209/0295-5075/83/37005
Abstract: We report on the observation of self-organized stripe-like structures on the as-grown surface and in the bulk of (Nd,Eu,Gd)Ba2Cu3Oy single crystals. The periodicity of the stripes on the surface lies between 500800 nm. These are possibly the growth steps of the crystal. Transmission electron microscopy investigations revealed stripes of periodicity in the range of 2040 nm in the bulk. From electron back scattered diffraction investigations, no crystallographic misorientation due to the nanostripes has been found. Scanning tunneling spectroscopic experiments revealed nonsuperconducting regions, running along twin directions, which presumably constitute strong pinning sites.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.957
Times cited: 5
DOI: 10.1209/0295-5075/83/37005
|
|