Abstract: The crystal structure and the microstructure of epitaxial Sr4Fe6O13+/-delta thin films grown on a single-crystal SrTiO3 substrate by PLD have been investigated. A combination of electron diffraction and high-resolution microscopy allows us to refine the structure and to identify an incommensurate modulation in the Sr4Fe6O13+/-delta films. The incommensurate structure (q = alphaa(m)* approximate to 0.39alpha(m)*, superspace group Xmmm(alpha00)0s0) can be interpreted as an oxygen-deficient modification in the Fe2O2.5 double layers. Moreover, it is shown that the experimentally determined a component of the modulation can be used consistently to estimate the local oxygen content in the Sr4Fe6O13+/-delta films. The compound composition can therefore be described as Sr4Fe6O12+2alpha and the value alpha = 0.39 corresponds to a Sr4Fe6O12.78 composition. The misfit stress along the Sr4Fe6O13+/-delta/SrTiO3 interface is accommodated via both elastic deformation and inelastic mechanisms (misfit dislocations and 90degrees rotation twins). The present results also suggest the existence of SrFeO3 perovskite in the Sr4Fe6O13+/-delta films.

Abstract: CdSe(core)/CdS(shell) nanorods (NRs) have been extensively investigated for their unique optical properties, such as high photoluminescence (PL) quantum efficiency (QE) and polarized light emission. The incorporation of these NRs in silica (SiO2) is of high interest, since this renders them processable in polar solvents while increasing their photochemical stability, which would be beneficial for their application in LEDs and as biolabels. We report the synthesis of highly luminescent silica-coated CdSe/CdS NRs, by using the reverse micelle method. The mechanism for the encapsulation of the NRs in silica is unravelled and shown to be strongly influenced by the NR shape and its asymmetry. This is attributed to both the different morphology and the different crystallographic nature of the facets terminating the opposite tips of the NRs. These results lead to the formation of a novel class of NR architectures, whose symmetry can be controlled by tuning the degree of coverage of the silica shell. Interestingly, the encapsulation of the NRs in silica leads to a remarkable increase in their photostability, while preserving their optical properties.

Abstract: Li-ion batteries rely on the use of insertion positive electrodes with performances scaling with the redox potential of the 31) metals accompanying Liuptake/removal. Although not commonly studied, the Cu2+/Cu3+ redox potential has been predicted from theoretical calculations to possibly offer a high operating voltage redox couple. We herein report the synthesis and crystal structure of a hitherto-unknown oxysulfate phase, Li2Cu2O(SO4)(2), which contains infinite edgesharing CuO4 chains and presents attractive electrochemical redox activity with respect to Li+/Li, namely amphoteric characteristics. Li2Cu2O(SO4)(2) shows redox activity at 4.7 V vs Li+/Li corresponding to the oxidation of Cu2+ to Cu3+ enlisting ligand holes and associated with the reversible uptake-removal of 0.3 Li. Upon reduction, this compound reversibly uptakes similar to 2 Li at an average potential of about 2.5 V vs Li+/Li, associated with the Cu2+/Cu+ redox couple. The mechanism of the reactivity upon reduction is discussed in detail, with particular attention to the occasional appearance of an oscillation wave in the discharge profile. Our work demonstrates that Cu-based compounds can indeed be fertile scientific ground in the search for new high-energy-density electrodes.

Abstract: Intercalation of lithium in the ribbon structure Li4Mo5O17 has been achieved, using both electrochemistry and soft chemistry. The ab initio structure determination of the ¡°Mo−O¡± framework of Li12Mo5O17 shows that the [Mo5O17]¡Þ ribbons keep the same arrangement of edge sharing MoO6 octahedra and the same orientation as in the parent structure but that a topotactic antidistortion of the ribbons appears, as a result of the larger size of Mo4+ in ¡°Li12¡± compared to Mo6+ in ¡°Li4¡±. On the basis of bond valence calculations, it is observed that 12 octahedral sites are available for Li+ in the new structure so that an ordered hypothetical rock salt type structure can be proposed for Li12Mo5O17. After the first Li insertion, a stable reversible capacity of 100 mA¡¤h/g is maintained after 20 cycles. A complete structural reversibility leading back to the ribbon type Li4Mo5O17 structure is obtained using a very low rate of C/100. The exploration of the Li mobility in those oxides shows that Li4Mo5O17 is a cationic conductor with ¦Ò = 10−3.5 S/cm at 500 ¡ãC and Ea = 0.35 eV.

Abstract: The Fe-vacancy ordering patterns in the superconducting KxFe2ySe2 and nonsuperconducting Kx(Fe,Co)2ySe2 samples have been investigated by electron diffraction and high angle annular dark field scanning transmission electron microscopy. The Fe-vacancy ordering occurs in the ab plane of the parent ThCr2Si2-type structure, demonstrating two types of patterns. Superstructure I retains the tetragonal symmetry and can be described with the aI = bI = as√5 (as is the unit cell parameter of the parent ThCr2Si2-type structure) supercell and I4/m space group. Superstructure II reduces the symmetry to orthorhombic with the aII = as√2, bII = 2as√2 supercell and the Ibam space group. This type of superstructure is observed for the first time in KxFe2ySe2. The Fe-vacancy ordering is inhomogeneous: the disordered areas interleave with the superstructures I and II in the same crystallite. The observed superstructures represent the compositionally dependent uniform ordering patterns of two species (the Fe atoms and vacancies) on a square lattice. More complex uniform ordered configurations, including compositional stripes, can be predicted for different chemical compositions of the KxFe2ySe2 (0 < y < 0.5) solid solutions.

Abstract: One primary goal of self-assembly in nanoscale regime is to implement multifunctional binary nanoparticle superlattices into practical use. In the last decade, considerable effort has been put into the fabrication of binary nanoparticle superlattices with controllable structure and stoichiometry. However, limited effort has been made in order to improve the stability of these binary nanoparticle superlattices, which is a prerequisite for their potential application. In this work, we demonstrate that the carbon deposition from specimen contamination can play an auxiliary role during the heat treatment of binary nanoparticle superlattices. With the in-situ carbon matrix formation, the thermal stability of CoAu 13 binary nanoparticle superlattices is unambiguously enhanced.

Abstract: The recent revival of the Na-ion battery concept has prompted intense activities in the search for new Na-based layered oxide positive electrodes. The largest capacity to date was obtained for a Na-deficient layered oxide that relies on cationic redox processes only. To go beyond this limit, we decided to chemically manipulate these Na-based layered compounds in a way to trigger the participation of the anionic network. We herein report the electrochemical properties of a Na-rich phase Na2IrO3, which can reversibly cycle 1.5 Na+ per formula unit while not suffering from oxygen release nor cationic migrations. Such large capacities, as deduced by complementary XPS, X-ray/neutron diffraction and transmission electron microscopy measurements, arise from cumulative cationic and anionic redox processes occurring simultaneously at potentials as low as 3.0 V. The inability to remove more than 1.5 Na+ is rooted in the formation of an O1-type phase having highly stabilized Na sites as confirmed by DFT calculations, which could rationalize as well the competing metal/oxygen redox processes in Na2IrO3. This work will help to define the most fertile directions in the search for novel high energy Na-rich materials based on more sustainable elements than Ir.

Abstract: Searching for novel high-capacity electrode materials combining cationic and anionic redox processes is an ever-growing activity within the field of Li-ion batteries. In this respect, we report on the exploration of the Li3RuyNb1-yO4 (O <= y <= 1) system with an O/M ratio of 4 to maximize the number of oxygen lone pairs, responsible for the anionic redox. We show that this system presents a very rich crystal chemistry with the existence of four structural types, which derive from the rocksalt structure but differ in their cationic arrangement, creating either zigzag, helical, jagged chains or clusters. From an electrochemical standpoint, these compounds are active on reduction via a classical cationic insertion process. The oxidation process is more complex, because of the instability of the delithiated phase. Our results promote the use of the rich Li3MO4 family as a viable platform for a better understanding of the relationships between structure and anionic redox activity.

Abstract: Deactivation was investigated in Fe2O3-CeO2 oxygen storage materials during repeated H-2-reduction and CO2-reoxidation. In situ XRD, XAS, and TEM were used to identify phases, crystallite sizes, and morphological changes upon cycling operation. The effect of redox cycling was investigated both in Fe-rich (80 wt % Fe2O3-CeO2) and Ce-rich (10 wt %Fe2O3-CeO2) materials. The former consisted of 100 nm Fe2O3 particles decorated with 5-10 nm Ce1-xFexO2-x. The latter presented CeO2 with incorporated Fe, i.e. a solid solution of Ce1-xFexO2-x, as the main oxygen carrier. By modeling the EXAFS Ce-K signal for as-prepared 10 wt %Fe2O3-CeO2, the amount of Fe in CeO2 was determined as 21 mol %, corresponding to 86% of the total iron content. Sintering and solid solid transformations, the latter including both new phase formation and element segregation, were identified as deactivation pathways upon redox cycling. In Ce-rich material, perovskite (CeFeO3) was identified by XRD. This phase remained inert during reduction and reoxidation, resulting in an overall lower oxygen storage capacity. Further, Fe segregated from the solid solution, thereby decreasing its reducibility. In addition, an increase in crystallite size occurred for all phases. In Fe-rich material, sintering is the main deactivation pathway, although Fe segregation from the solid solution and perovskite formation cannot be excluded.

Abstract: Nanocrystalline titanium dioxide was prepared via aerosol pyrolysis of titanium alkoxide precursor at 200-580 degrees C in air and in nitrogen atmospheres. Powders were characterized by x-ray diffraction, thermogravimetric analysis, Brunauer-Emmett-Teller analysis, scanning electron microscopy, transmission electron microscopy, energy dispersive spectroscopy, x-ray fluorescence, Raman and infrared spectroscopy, and Berner-type low-pressure impactor. The anatase phase transition was initiated at 500 degrees C in nitrogen and at 580 degrees C in air. Under other conditions amorphous powders were observed and transformed to nanocrystalline TiO2 via thermal postannealing. In air, smooth and spherical particles with 2-4-mu m diameter were formed with an as-expected tendency to convert to rutile in the thermal postannealings. In nitrogen, a fraction of the titanium tetrabutoxide precursor evaporated and formed ultrafine particles via the gas-to-particle conversion. At 500 degrees C thermally stable anatase phase was formed in nitrogen. A specific surface area as high as 280 m(2) g(-1) was observed for an as-prepared powder.