Abstract: In a numerical experiment based on Gross-Pitaevskii formalism, we demonstrate unique topological quantum coherence in optically trapped Bose-Einstein condensates (BECs). Exploring the fact that vortices in a rotating BEC can be pinned by a geometric arrangement of laser beams, we show the parameter range in which vortex-antivortex molecules or multiquantum vortices are formed as a consequence of the optically imposed symmetry. Being low-energy states, we discuss the conditions for spontaneous nucleation of these unique molecules and their direct experimental observation, and provoke the potential use of the phase print of an antivortex or a multiquantum vortex when realized in unconventional circumstances.

Abstract: Digital disconnection has emerged as a concept describing the actions people take to limit their digital connectivity to enhance their well-being. To date, evidence on its effectiveness is mixed, leading to calls for greater consideration of why, how, when, and for whom digital disconnection works. This article responds to these calls, presenting a framework that differentiates four key harms that contribute to experiences of digital ill-being (time displacement, interference, role blurring, and exposure effects). Using these four harms as a starting point, the framework explains: (1) why people are motivated to digitally disconnect; (2) how specific disconnection strategies (i.e., placing limits on time, access, channels, and contents, interactions and features) may help them; and for whom (3) and under which conditions (when) these strategies can be effective.

Abstract: The incorporation of nanoscaled pinning centers in superconducting YBa2Cu3O7-d (YBCO) films is one of the core topics to enhance the critical current density Jc(B, Q) of coated conductors. The mixed double-perovskite Ba2Y(Nb/Ta)O6 (BYNTO) can be grown in nanosized columns parallel the YBCO c-axis and in step-like patterns, making it customizable to meet specific working conditions (T, B, Q). We compare a 1.6 μm thick film of pure YBCO and a similar film with additional 5 mol% of BYNTO, grown by pulsed laser deposition with a growth rate of 1.6 nm/s on buffered biaxially textured Ni-5at.% W tape. Our doped sample shows nanosized BYNTO columns parallel cYBCO and plates in the ab-plane containing Y, Nb and Ta. An improved homogeneity of the critical current density Jc over the sample was evaluated from trapped field profiles measured with a scanning Hall probe microscope. The mean Jc in rolling direction of the tape is 1.8 MA/cm² (77 K, self-field) and doubles the value of the undoped sample. Angular dependent measurements of the critical current density, Jc(Q), show a decreased anisotropy of the doped film for various magnetic fields at 77 K as well as 64 K.

Abstract: The current transport capability of YBa2Cu3O7-x(YBCO) based coated conductors (CCs) is mainly limited by two features: the grain boundaries of the used textured template, which are transferred into the superconducting film through the buffer layers, and the ability to pin magnetic flux lines by incorporation of defined defects in the crystal lattice. By adjusting the deposition conditions, it is possible to tailor the pinning landscape in doped YBCO in order to meet specific working conditions (T, B) for CC applications. To study these effects, we deposited YBCO layers with a thickness of about 1-2 mu m using pulsed laser deposition on buffered rolling-assisted biaxially textured Ni-W substrates as well as on metal tapes having either an ion-beam-texturedYSZbuffer or an MgO layer textured by inclined substrate deposition. BaHfO3 and the mixed double-perovskite Ba2Y(Nb/Ta)O-6 were incorporated as artificial pinning centers in these YBCO layers. X-ray diffraction confirmed the epitaxial growth of the superconductor on these templates as well as the biaxially oriented incorporation of the secondary phase additions in the YBCO matrix. A critical current density J(c) of more than 2 MA/cm(2) was achieved at 77 K in self-field for 1-2 mu m thick films. Detailed TEM (transmission electron microscopy) studies revealed that the structure of the secondary phase can be tuned, forming c-axis aligned nanocolumns, ab-oriented platelets, or a combination of both. Transport measurements show that the J(c) anisotropy in magnetic fields is reduced by doping and the peak in the J(c) (theta) curves can be correlated to the microstructural features.

Abstract: The critical current I-c(B) of YBa2Cu3O7-delta (YBCO) coated conductors can be increased by growing thicker superconductor layers as well as improving the critical current density J(c)(B) by the incorporation of artificial pinning centers. We studied the properties of pulsed laser deposited BaHfO3 (BHO)-doped YBCO films with thicknesses of up to 5 mu m on buffered rolling-assisted biaxially textured Ni-5 at % W tape and alternating beam assisted deposition textured Yttrium-stabilized ZrO2 layers on stainless steel. X-Ray diffraction confirms the epitaxial growth of the superconductor on the buffered metallic template. BHO additions reduce the film porosity and lower the probability to grow misoriented grains, hence preventing the J(c) decrease observed in undoped YBCO films with thicknesses > 2 mu m. Thereby, a continuous increase in I-c at 77 K is achieved. A mixed structure of secondary phase nanorods and platelets with different orientations increases J(c)(B) in the full angular range and simultaneously lowers the J(c) anisotropy compared to pristine YBCO.

Abstract: Transmission electron microscopy is used to evaluate different deposition techniques, which optimize the microstructure and physical properties of superconducting thin films. High-resolution electron microscopy proves that the use of an YBa2Cu2Ox buffer layer can avoid a variable interface configuration in YBa2Cu3O7-delta thin films grown on SrTiO3. The growth can also be controlled at an atomic level by, using sub-unit cell layer epitaxy, which results in films with high quality and few structural defects. Epitaxial strain in Sr0.85La0.15CuO2 infinite layer thin films influences the critical temperature of these films, as well as the microstructure. Compressive stress is released by a modulated or a twinned microstructure, which eliminates superconductivity. On the other hand, also tensile strain seems to lower the critical temperature of the infinite layer.

Abstract: A method to prepare TEM specimens from metallic microwires and based on conventional twin-jet electropolishing is introduced. The wire is embedded in an opaque epoxy resin medium and the hardened resin is mechanically polished to reveal the wire on both sides. The resin containing wire is then cut into discs of the appropriate size. The obtained embedded wire is electropolished in a conventional twin-jet electropolishing machine until electron transparency in large areas without radiation damage is achieved.

Abstract: The irradiation effects of thinning a sample of a Cu-Zn-Al shape memory alloy to electron transparency by a Ga+ focused ion beam were investigated. This thinning method was compared with conventional electropolishing and Ar+ ion milling. No implanted Ga was detected but surface FCC precipitation was found as a result of the focused ion beam sample preparation. Decreasing the irradiation dose by lowering the energy and current of the Ga+ ions did not lead to a complete disappearance of the FCC structure. The latter could only be removed after gentle Ar+ ion milling of the sample. It was further concluded that the precipitation of the FCC is independent of the crystallographic orientation of the surface.

Abstract: ITEM specimens of a LaAlO3/SrTiO3 multilayer are prepared by FIB with internal lift out. Using a Ga+1 beam of 5 kV, a final cleaning step yielding top, top-angle, side, and bottom-angle cleaning is performed. Different cleaning procedures, which can be easily implemented in a dual beam FIB system, are described and compared; all cleaning types produce thin lamellae, useful for HRTEM and HAADF-STEM work up to atomic resolution. However, the top cleaned lamellae are strongly affected by the curtain effect. Top-angle cleaned specimens show an amorphous layer of around 5 nm at the specimen surfaces, due to damage and redeposition. Furthermore, it is observed that the LaAlO3 layers are preferentially destroyed and transformed into amorphous material, during the thinning process.