Abstract: In this article, surface processes occurring during the etching of Si with a Cl2/O2/Ar plasma are investigated by means of experiments and modeling. Cl2-based plasmas are commonly used to etch silicon, while a small fraction of O2 is added to protect the sidewalls from lateral etching during the shallow trench isolation process. When the oxygen fraction exceeds a critical value, the wafer surface process changes from an etching regime to a deposition regime, drastically reducing the etch rate. This effect is commonly referred to as the etch stop phenomenon. To gain better understanding of this mechanism, the oxygen fraction is varied in the gas mixture and special attention is paid to the effects of oxygen and of the redeposition of non-volatile etched species on the overall etch/deposition process. It is found that, when the O2 flow is increased, the etch process changes from successful etching to the formation of a rough surface, and eventually to the actual growth of an oxide layer which completely blocks the etching of the underlying Si. The size of this etch stop island was found to increase as a function of oxygen flow, while its thickness was dependent on the amount of Si etched. This suggests that the growth of the oxide layer mainly depends on the redeposition of non-volatile etch products. The abrupt change in the etch rate as a function of oxygen fraction was not found back in the oxygen content of the plasma, suggesting the competitive nature between oxidation and chlorination at the wafer. Finally, the wafer and reactor wall compositions were investigated by modeling and it was found that the surface rapidly consisted mainly of SiO2 when the O2 flow was increased above about 15 sccm.

Abstract: Plasma, the fourth and most pervasive state of matter in the visible universe, is a fascinating medium that is connected to the beginning of our universe itself. Man-made plasmas are at the core of many technological advances that include the fabrication of semiconductor devices, which enabled the modern computer and communication revolutions. The introduction of low temperature, atmospheric pressure plasmas to the biomedical field has ushered a new revolution in the healthcare arena that promises to introduce plasma-based therapies to combat some thorny and long-standing medical challenges. This article presents an overview of where research is at today and discusses innovative concepts and approaches to overcome present challenges and take the field to the next level. It is written by a team of experts who took an in-depth look at the various applications of plasma in hygiene, decontamination, and medicine, made critical analysis, and proposed ideas and concepts that should help the research community focus their efforts on clear and practical steps necessary to keep the field advancing for decades to come.

Abstract: Cold atmospheric plasma (CAP) has shown its potential in biomedical applications, such as wound healing, cancer treatment and bacterial disinfection. Recent experiments have provided evidence that CAP can also enhance the intracellular uptake of glucose molecules which is important in diabetes therapy. In this respect, it is essential to understand the underlying mechanisms of intracellular glucose uptake induced by CAP, which is still unclear. Hence, in this study we try to elucidate the possible mechanism of glucose uptake by cells by performing computer simulations. Specifically, we study the transport of glucose molecules through native and oxidized membranes. Our simulation results show that the free energy barrier for the permeation of glucose molecules across the membrane decreases upon increasing the degree of oxidized lipids in the membrane. This indicates that the glucose permeation rate into cells increases when the CAP oxidation level in the cell membrane is increased.

Abstract: The CO and CO2 Dielectric Barrier Discharges (DBD) and their solid products were analyzed keeping similar energy input regimes. Gas chromatography analysis revealed the presence of CO2, CO and O-2 mixture in the exhaust of the CO2 DBD, while no O-2 was found when CO was used as a feed gas. It was shown that the C-2 Swan lines observed with optical emission spectroscopy were distinct in the CO plasma while they were not observed in the CO2 emission spectrum. Also the solid products of the plasmas exhibited remarkable differences. Nanoparticles with a diameter between10 and 300 nm, composed of Fe, O and C (Fe: O: C similar to 13: 50: 30) were produced by the CO2 DBD, while microscopic dendrite-like carbon structure (C: O similar to 73: 27) were formed in the CO plasma. The growth rate in the CO2 and CO DBDs was evaluated to be on the level of 0.15 mg/min and 15 mg/min, respectively. The difference of the CO and CO2 discharges and their products might be attributed to the oxygen content in the latter (6.4 mol.% O-2 in the exhaust) and subsequent etching of the carbonaceous film.