Abstract: The morphology and structure of diamond films, deposited on cubic boron nitride (c-BN) crystals by microwave-plasma-enhanced chemical vapor deposition, is studied by high-resolution scanning electron microscopy and micro-Raman spectroscopy. The c-BN crystals, with sizes of 200 to 350 mu m and grown by a high-temperature/high-pressure technique, were embedded in a copper holder, and used as substrates in deposition runs of 15 min to 5 h. The nucleation centers for diamond appear as well-shaped cuboctahedral crystallites, having diameters of approximately 100 nm. With increasing deposition time the diamond crystallites grew larger, forming islands on the c-BN faces. In some cases, epitaxial growth was observed on the (111) c-BN faces where coalesced particles gave rise to very smooth regions. A number of diamond crystals with peculiar shapes are observed, such as a pseudo five-fold symmetry due to multiple twinning. Moreover, both randomly distributed carbon tubes, about 100 nn in diameter and 1 mu m in length, and spherically shaped features are observed in samples prepared under the typical conditions of diamond deposition, this effect being ascribed to the influence of plasma-sputtered copper contamination. Quite unusual diamond crystals with a deep, pyramidal-shaped hole in the middle grew on the copper substrate between the c-BN crystals. (C) 2000 Elsevier Science S.A. All rights reserved.

Abstract: A Ti target was submitted to laser ablation in low ambient pressure N-2. Electron microscopy examination of the cross-section of the crater zone forming on the Ti target, and XPS analyses, indicate that there is a small effect on the nitridation processes taking place on and in the vicinity of the target. The studies show a zone influenced by the multipulse laser treatment extending beneath the crater down to a depth of the same order of magnitude as the crater depth (i.e. similar to 10 mu m). In this zone, TiN could be identified as being present only in traces, while the whole zone exhibited a layer structure with differences in morphology and mechanical wear.

Abstract: A survey is given of the application of different electron microscopic techniques to the study of structural features of high T(c)-superconducting materials. Emphasis is laid in this contribution on those structural aspects for the study of which electron microscopy has been essential or has contributed to a significant extent.

Abstract: Results are presented on the photoluminescence (PL) characterization of heavily doped p(+) Czochralski silicon, which has been subjected to a two-step, oxygen precipitation heat treatment. It will be shown that the presence of oxygen precipitates gives rise to the D1, D2 and D5 lines, where the energy of the D1 line shifts to lower values for a stronger degree of precipitation. The occurrence of these PL features is also a function of the boron concentration in the p(+) material. The PL results are compared with Fourier transform infrared absorption data and with transmission electron microscope, results. From this, it is concluded that PL has a good potential for use in the assessment of oxygen precipitation in heavily doped silicon.

Abstract: Infrared absorption spectra of oxygen precipitates in boron doped silicon with a boron concentration between 10(17) and 10(19) cm(-3) are analyzed, applying the spectral function theory of the composite precipitates. The aspect ratio of the platelet precipitates has been determined by transmission electron microscopy measurements. Our analysis shows that in samples with moderate doping levels (<10(18) B cm(-3)) SiOgamma precipitates are formed with stoichiometry as in the lightly doped case. In the heavily (>10(18) cm(-3)) boron doped samples, however, the measured spectra of the precipitates are consistent with a mixture of SiO2 and B2O3. with a volume fraction of B2O3 as high as 0.41 in the most heavily doped case.

Abstract: Shallow trench isolation (STI) is a promising technology for the isolation structures of the new generation of ULSI devices with dimensions below 0.18 mum. The various processing steps cause stress fields in STI structures, which can lead to defect formation in the silicon substrate. In their turn, stress fields affect the electrical parameters and the reliability of devices. Convergent beam electron diffraction (CBED) is used in this study to examine the influence of a wet and a dry pre-gate oxidation on the stress distribution around STI structures. The measurements are performed on STI structures with different width and spacing. CBED analysis is compared with bright-field TEM images. Defects are observed in high-strain areas of small isolated structures. (C) 2001 Elsevier Science Ltd. All rights reserved.

Abstract: An alternative pathway to assemble mesoporous molecular sieve silicas is developed using nonionic alkylamines and N,N-dimethylalkylamines (SO) as structure-directing agents in acidic conditions. The synthesized mesostructures possess wormhole-like frameworks with pore sizes and pore volumes in the range of 20-90 Angstrom and 0.5-1.3 cm(3)/g, respectively. The formation of the mesophase is controlled by a counterion-mediated mechanism of the type (S(0)H(+))(X(-)I(+)), where S(0)H(+) are protonated water molecules that are hydrogen bonded to the lone electron pairs on the amine surfactant headgroups (S(0)H(+)), X(-) is the counteranion originating from the acid, and I(+) are the positively charged (protonated) silicate species. We found that the stronger the ion X(-) is bonded to S(0)H(+), the more it catalyzes the silica condensation into (S(0)H(+))(X(-)I(+)). Br(-) is shown to be a strong binding anion and therefore a fast silica polymerization promoter compared to Cl(-) resulting in the formation of a higher quality mesophase for the Br(-) syntheses. We also showed that the polymerization rate of the silica, dictated by the counterion, controls the morphology of the mesostructures from nonuniform agglomerated blocks in the case of Br(-) syntheses to spherical particles for the Cl(-) syntheses. Next to many benefits such as low temperature, short synthesis time, and the use of inexpensive, nontoxic, and easily extractable amine templates, the developed materials have a remarkable higher thermal and hydrothermal stability compared to hexagonal mesoporous silica, which is also prepared with nonionic amines but formed through the S(0)I(0) mechanism.

Abstract: It is known that the neutral image tone of a developed photographic film becomes brownish when the thickness of the original silver halide tabular crystals is reduced. We investigate by electron microscopy to what extent the silver filament structure has changed and how it induces the shift in image tone. Therefore, two samples of AgBr {111} tabular crystals with average thicknesses of 160 nm and 90 nm respectively, are compared. It is shown that the dimensions and defect structure of the filaments are comparable, but that the 90 nm crystals result in a more widely spaced structure, which explains the shift in image tone on a qualitative level. The influence of the addition of an image toner, i.e., phenylmercaptotetrazole, on the filament structure is also investigated. An even more open filament structure of longer, but smaller filaments was observed.